JPH05263302A - Underwear for adjusting body - Google Patents
Underwear for adjusting bodyInfo
- Publication number
- JPH05263302A JPH05263302A JP21733491A JP21733491A JPH05263302A JP H05263302 A JPH05263302 A JP H05263302A JP 21733491 A JP21733491 A JP 21733491A JP 21733491 A JP21733491 A JP 21733491A JP H05263302 A JPH05263302 A JP H05263302A
- Authority
- JP
- Japan
- Prior art keywords
- underwear
- shape
- manipulative
- shape memory
- niti
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【0001】[0001]
【産業上の利用分野】この発明は、整体用下着に関する
ものである。さらに詳しくは、この発明は、形状記憶合
金の形状記憶性能、超弾性性能および低弾性率を利用し
て、下着の一部の形状を保持し、着心地とともに、着用
者の体型を補整する整体機能を向上させることのできる
整体用下着に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an underwear for manipulative treatment. More specifically, the present invention utilizes the shape memory performance, superelasticity, and low elastic modulus of shape memory alloys to hold a part of the shape of underwear and to provide comfort and to adjust the body shape of the wearer. The present invention relates to an underwear for manipulative treatment which can improve the function.
【0002】[0002]
【従来の技術】従来より、着用者の体型を補整する整体
用下着として、ガードル、ボディスーツ、ボディシェイ
パー、ウェストニッパー等が広く用いられてきている。
これらのうちで、ガードルやボディスーツについては、
たとえば図5および図6に示したように、下腹部
(ア)、ウェスト部(イ)および臀部(ウ)の体型の補
整のために、ナイロンやポリウレタンなどの太い線を用
いた強力なネット生地を型を用いて成形し、これを下着
の一部の所定部位に縫製して、整体機能を持たせたもの
が知られている。また、ボディシェイパーには、図7に
示したように、下腹部(ア)およびウェスト部(イ)の
体型補整のために、上記したようなガードルやボディス
ーツ同様な方式で整体機能を付与しているものがある。
さらに、ウェストニッパーについては、図8に示したよ
うに、ボーン(エ)と呼ばれる金属性の補強部材を通常
6〜8本縦に取り付け、ウェスト部(イ)の体型を補整
するようにしている。2. Description of the Related Art Conventionally, girdles, body suits, body shapers, waist nippers, etc. have been widely used as underwear for manipulating the body of a wearer.
Of these, for girdles and bodysuits,
For example, as shown in FIGS. 5 and 6, a strong net cloth using a thick wire such as nylon or polyurethane for adjusting the body shapes of the lower abdomen (A), waist (I) and buttocks (U). It is known that a mold is molded using a mold, and this is sewn to a predetermined part of a piece of underwear to have a manipulative function. In addition, as shown in FIG. 7, the body shaper is provided with a manipulative function in the same manner as the girdle or bodysuit as described above for body shape correction of the lower abdomen (a) and waist (a). There is something.
Further, as for the waist nipper, as shown in FIG. 8, normally 6 to 8 metallic reinforcing members called bones (d) are vertically attached to adjust the body shape of the waist portion (a). .
【0003】[0003]
【発明が解決しようとする課題】しかしながら、たとえ
ばこれらの図5〜図7に示されるガードル、ボディスー
ツおよびボディシェイパーの場合には、生地の強度を利
用して肉体の一部を抑え込むようにしているため、ナイ
ロンやポリウレタンなどのような繊維を用いている限
り、引張強度は強いが、生地自体で三次元的な形状を保
持するにはその力が弱く不十分であり、美しい体型に補
整しにくいという欠点がある。However, for example, in the case of the girdle, body suit and body shaper shown in FIGS. 5 to 7, the strength of the dough is used to hold down a part of the body. Therefore, as long as fibers such as nylon and polyurethane are used, the tensile strength is strong, but the strength is weak and insufficient to retain the three-dimensional shape of the fabric itself, and it is difficult to adjust to a beautiful figure. There is a drawback.
【0004】また、図8に例示したようなウェストニッ
パーの場合には、生地の引張強度を利用してウェスト部
(イ)を円周方向に締め付け、ボーン(エ)で抑え込む
構造であるため、三次元的な美しい体型に整える整体機
能に乏しいという問題があった。この発明は、以上の通
りの事情に鑑みてなされたものであり、従来の整体用下
着の欠点を解消し、着心地をとともに、着用者の体型を
補整する整体機能をも向上させることのできる、形状記
憶合金を利用した新しい整体用下着を提供することを目
的としている。Further, in the case of the waist nipper as illustrated in FIG. 8, the waist portion (a) is clamped in the circumferential direction by utilizing the tensile strength of the cloth, and is restrained by the bone (d). There was a problem that it lacked the manipulative function to prepare a beautiful three-dimensional figure. The present invention has been made in view of the circumstances as described above, and it is possible to eliminate the drawbacks of the conventional underwear for manipulative treatment, improve the comfort, and also improve the manipulative treatment function for adjusting the wearer's body shape. , An object is to provide a new underwear for manipulative treatment using a shape memory alloy.
【0005】[0005]
【課題を解決するための手段】この発明は、上記の課題
を解決するものとして、NiTi系形状記憶合金線の織
物または編物を下着の一部の形状に形状記憶熱処理し、
着用時の温度でオーステナイト相がでるように変態温度
を調整し、下着に取り付けて下着の一部の形状を保持し
てなることを特徴とする整体用下着を提供する。Means for Solving the Problems The present invention is to solve the above problems by subjecting a woven or knitted NiTi-based shape memory alloy wire to a shape of a part of underwear by shape memory heat treatment,
Provided is an underwear for manipulative treatment, which is characterized in that a transformation temperature is adjusted so that an austenite phase appears at a temperature at the time of wearing and is attached to the underwear to hold a part of the shape of the underwear.
【0006】また、この発明は、NiTi系形状記憶合
金線で網状または布状の織物または編物を作る際に、ス
テンレス鋼、チタン、タン合金、あるいはアモルファス
合金の金属線、もしくは融点が250 ℃以上のポリエステ
ル、アクリル、ナイロン等の合成繊維糸を1種以上組み
合わせることも包含している。このように、NiTi系
形状記憶合金線を単独で、あるいは他の金属線や合成繊
維の糸と組み合わせて製造した織物または編物を下着の
一部の形状、すなわち、たとえばガードルおよびボディ
スーツの場合には、図1および図2に各々例示したよう
に、下腹部(1)、ウェスト部(2)および臀部
(3)、また、ボディシェイパーの場合には、図3に例
示したように、下腹部(1)およびウェスト部(2)、
さらに、ウェストニッパーの場合には、図4に例示した
ように、ウェスト部(2)と従来のウェストニッパーの
ボーンに相当する部位(4)の各々の部位に相当する形
状に形状記憶熱処理し、着用時の温度でオーステナイト
相がでるように変態温度を調整して、下着に取り付け
る。Further, according to the present invention, when a net-like or cloth-like woven or knitted material is made of NiTi-based shape memory alloy wire, a metal wire of stainless steel, titanium, tan alloy, or amorphous alloy, or a melting point of 250 ° C. or more. It also includes a combination of one or more types of synthetic fiber yarns such as polyester, acrylic and nylon. Thus, a woven or knitted fabric produced by NiTi-based shape memory alloy wire alone or in combination with other metal wires or yarns of synthetic fiber is used in a part of the shape of underwear, that is, in the case of girdle and body suit, for example. Is a lower abdomen (1), a waist (2) and a buttocks (3) as illustrated in FIGS. 1 and 2, and in the case of a body shaper, a lower abdomen is illustrated as illustrated in FIG. (1) and waist (2),
Further, in the case of a waist nipper, as illustrated in FIG. 4, shape memory heat treatment is performed to a shape corresponding to each of the waist portion (2) and the portion (4) corresponding to the bone of the conventional waist nipper, Adjust the transformation temperature so that the austenite phase appears at the temperature of wearing, and attach it to underwear.
【0007】NiTi系合金のオーステナイト相は、超
弾性状態であり、鋼などの他の金属線材に比べると低弾
性率で、しかも弾性を保つ変形の範囲が広く、しなやか
であるという特性を有している。このNiTi系合金線
を熱処理により予めたとえば上記したような整体用下着
の一部の形状に対応するように形状記憶させることによ
り、型くずれすることなく、着用者の体型を美しく整え
ることができるとともに、着用時の着心地を向上させる
ことができる。特に、図4に例示したウェストニッパー
の場合には、従来取り付けていた硬いボーンという金属
製の補強部材が不要となり、ウェスト部(2)の圧迫感
がなくなる。また、ウェスト部(2)のラインがきれい
になる。The austenite phase of the NiTi alloy is in a superelastic state, has a low elastic modulus as compared with other metal wire rods such as steel, and has a wide range of deformation that maintains elasticity and is supple. ing. This NiTi-based alloy wire is heat-treated in advance so that the shape of the body is memorized so as to correspond to the shape of a part of the body shaping underwear as described above, and the wearer's body shape can be beautifully adjusted without losing the shape, The wearing comfort can be improved. In particular, in the case of the waist nipper illustrated in FIG. 4, the hard reinforcing member made of metal, which is conventionally attached, such as a hard bone, is unnecessary, and the waist portion (2) does not have a feeling of pressure. Also, the line of the waist part (2) becomes clean.
【0008】[0008]
【作用】この発明の整体用下着においては、NiTi系
形状記憶合金の網状または布状の織物または編物を整体
用下着の一部に使用することにより、三次元的形状と強
度を保持し、かつしなやかであるという特性を生かしつ
つ、装着時の違和感をなくし、スムーズに着用者の体型
を整えることが可能となる。In the manipulative undergarment of the present invention, the net-like or cloth-like woven or knitted material of NiTi-based shape memory alloy is used as a part of the manipulative undergarment to maintain the three-dimensional shape and strength, and While taking advantage of the suppleness, it is possible to eliminate the discomfort at the time of wearing and smoothly adjust the wearer's body shape.
【0009】[0009]
【実施例】以下、実施例を示し、この発明の整体用下着
についてさらに詳しく説明する。 実施例1 形状記憶熱処理により、オーステナイト終了温度(Af
点)が約25℃以下となるようにNiTi形状記憶合金
の化学組成を調整し、直径50μmの円形断面を有する
線材に加工して、これをメリヤス網に編み、編物を作成
した。この編物を図1〜図4に示したガードル、ボディ
スーツ、ボディシェイパーおよびウェストニッパーにお
いて、下腹部、ウェスト部および臀部の体型を整えるよ
うな所定の形状に形状記憶熱処理し、取り付けて、種々
のサイズの整体用下着を作成した。EXAMPLES Hereinafter, the underwear for manipulative treatment of the present invention will be described in more detail with reference to examples. Example 1 Austenite finish temperature (Af
The chemical composition of the NiTi shape memory alloy was adjusted so that the point) was about 25 ° C. or less, processed into a wire having a circular cross section with a diameter of 50 μm, and knitted into a knitted mesh to form a knit. In the girdle, body suit, body shaper, and waist nippers shown in FIGS. 1 to 4, the knitted fabric is shape-memory heat-treated into a predetermined shape for adjusting the body shapes of the lower abdomen, waist and buttocks, and attached to various shapes. I made an underwear for size adjustment.
【0010】この下着を様々な体型の女性30人に試着
してもらい、着心地の検定を行った。被験者の着用前
後、また、従来の下着との比較から、この発明の整体用
下着は、身体への圧迫感が少なく、着心地も良好であ
り、しかも身体のラインを美しくすることができること
が確認された。 実施例2 実施例1と同一化学組成のNiTi系形状記憶合金を直
径60μmの細い線材に加工し、この線材と直径125 μ
mのCo−Fe−Cr−Si−B系アモルファス合金線
材とを、各々、縦糸および横糸として布を織り、実施例
1と同様の形状記憶熱処理を行い、様々なサイズのガー
ドル、ボディスーツ、ボディシェイパーおよびウェスト
ニッパーを作成した。Thirty women of various body types tried on this underwear to test the comfort. Before and after wearing by the subject, and from comparison with conventional underwear, it was confirmed that the manipulative underwear of the present invention has less pressure on the body, is comfortable to wear, and can make the body line beautiful. Was done. Example 2 A NiTi-based shape memory alloy having the same chemical composition as in Example 1 was processed into a thin wire rod having a diameter of 60 μm.
m-Co-Fe-Cr-Si-B based amorphous alloy wire rods were woven as warp threads and weft threads, respectively, and subjected to the same shape memory heat treatment as in Example 1 to obtain girdles, body suits and bodies of various sizes. Created shapers and waist nippers.
【0011】この下着について、様々な体型の30人の
女性を対象とした装着テストを行った。その結果、実施
例1と同様に、この発明の整体用下着は、着心地がよ
く、しかも整体性が良好であることが確認された。 実施例3 実施例1と同一のNiTi系形状記憶合金線材とナイロ
ン糸とを、各々、縦糸および横糸として布を織り、かつ
実施例1と同様の形状記憶熱処理を行い、整体用下着を
作成した。With respect to this underwear, a wearing test was conducted on 30 women of various body types. As a result, it was confirmed that the manipulative underwear of the present invention was comfortable to wear and good in manipulative property, as in Example 1. Example 3 The same NiTi-based shape memory alloy wire and nylon yarn as in Example 1 were woven as warp yarns and weft yarns, respectively, and the same shape memory heat treatment as in Example 1 was performed to prepare an underwear for body preparation. .
【0012】この下着についても様々な体型の女性30
人を対象として装着テストを行った。実施例1および2
と同様に、着心地と整体性の良好さが確認された。もち
ろんこの発明は、以上の例によって限定されるものでは
ない。NiTi形状記憶合金線、アモルファス合金線の
組成および太さ、合成繊維糸の種類、また、整体用下着
の種類等の細部については様々な態様が可能であること
はいうまでもない。Women of various body types 30
A wearing test was conducted on humans. Examples 1 and 2
Similar to the above, it was confirmed that the wearability and manipulability were good. Of course, the present invention is not limited to the above examples. It goes without saying that various aspects are possible in details such as the composition and thickness of the NiTi shape memory alloy wire, the amorphous alloy wire, the kind of synthetic fiber yarn, and the kind of underwear for body preparation.
【0013】[0013]
【発明の効果】以上詳しく説明した通り、この発明によ
って、着心地がよく、三次元的に美しいボディラインを
実現することのできる整体性の向上した整体用下着が提
供される。As described in detail above, according to the present invention, an underwear for manipulative treatment is provided, which is comfortable to wear and can realize a beautiful three-dimensional body line with improved manipulative properties.
【図1】<a><b>は、各々、この発明の整体用下着
の一実施例としてのガードルを示した正面図および背面
斜視図である。1A and 1B are a front view and a rear perspective view, respectively, showing a girdle as an example of an underbody for manipulative treatment of the present invention.
【図2】<a><b>は、各々、この発明の整体用下着
の別の例としてのボディスーツを示した正面斜視図およ
び背面図である。2A and 2B are a front perspective view and a rear view, respectively, showing a bodysuit as another example of the manipulative undergarment of the present invention.
【図3】<a><b>は、各々、この発明の整体用下着
のまた別の例としてのボディシェイパーを示した正面斜
視図および背面図である。3A and 3B are a front perspective view and a rear view, respectively, showing a body shaper as another example of the manipulative treatment undergarment of the present invention.
【図4】<a><b>は、各々、この発明の整体用下着
のさらにまた別の例としてのウェストニッパーを示した
正面図および背面図である。4A and 4B are a front view and a rear view, respectively, showing a waist nipper as still another example of the manipulative treatment undergarment of the present invention.
【図5】(a)(b)は、各々、従来のガードルを示し
た正面図および背面斜視図である。5A and 5B are respectively a front view and a rear perspective view showing a conventional girdle.
【図6】(a)(b)は、各々、従来のボディスーツを
示した正面斜視図および背面図である。6 (a) and 6 (b) are respectively a front perspective view and a rear view showing a conventional bodysuit.
【図7】(a)(b)は、各々、従来のボディシェイパ
ーを示した正面斜視図および背面図である。7A and 7B are respectively a front perspective view and a rear view showing a conventional body shaper.
【図8】(a)(b)は、各々、従来のウェストニッパ
ーを示した正面図および背面図である。8A and 8B are respectively a front view and a rear view showing a conventional waist nipper.
1 下腹部 2 ウェスト部 3 臀部 4 ボーン相当部 1 Lower abdomen 2 West part 3 Gluteal part 4 Bone equivalent part
フロントページの続き (51)Int.Cl.5 識別記号 庁内整理番号 FI 技術表示箇所 // C22C 19/03 A (72)発明者 海江田 悠美子 千葉県船橋市上山町1の55,5−106 (72)発明者 大森 譲 三重県桑名市大字東方1601の18Continuation of front page (51) Int.Cl. 5 Identification number Reference number within the agency FI technical display location // C22C 19/03 A (72) Inventor Yumiko Kaieda 55, 5-106 (1) Kamiyamacho, Funabashi, Chiba ( 72) Inventor Yu Omori 18 181-1601 Touhou, Kuwana City, Mie Prefecture
Claims (2)
編物を下着の一部の形状に形状記憶熱処理し、着用時の
温度でオーステナイト相がでるように変態温度を調整
し、下着に取り付けて下着の一部の形状を保持してなる
ことを特徴とする整体用下着。1. A woven or knitted NiTi-based shape memory alloy wire is subjected to shape memory heat treatment in a part of the shape of underwear, the transformation temperature is adjusted so that an austenite phase is formed at the temperature at the time of wearing, and the underwear is attached to the underwear. An underwear for manipulative treatment, which is characterized by retaining a part of the shape of the.
編物に、ステンレス鋼、チタン、チタン合金、あるいは
アモルファス合金の金属線、もしくは融点が250 ℃以上
の合成繊維糸を1種以上組み合わせてなる請求項1の整
体用下着。2. A combination of a woven or knitted NiTi-based shape memory alloy wire and a metal wire of stainless steel, titanium, titanium alloy, or amorphous alloy, or one or more kinds of synthetic fiber yarn having a melting point of 250 ° C. or more. Item 1 underwear for manipulative treatment.