JPH05254632A - Flexible screw for conveyor - Google Patents

Abstract

PURPOSE:To prolong the life of a shaft and reduce the maintenance cost by using the resin which possesses a specific physical property value for at least one, preferably for the former of the resin layer installed on a steel cable and the resin which constitutes a cord. CONSTITUTION:On a flexible rod 1 having a resin layer 12 at least at a part of a steel cable11, a flexible screw for conveyor is constituted by winding a cord 2 having a resin layer 22 at least on the surface layer. In this case, at least the surface layer of at least one between the resin layer 12 which constitutes the flexible rod 1 and the resin 22 which constitutes the cord 2 is made of the resin having a bending modulus of 3,000kgf/cm<2> or less, frictional coefficient of 2.0 or less and an abrasion quantity of 25mg or less. Accordingly, the excellent flexibility is provided, and since the abrasion resistance is excellent and the frictional coefficient is small, the abrasion of the resin layer due to the sliding with a container during transport can be reduced, and the container can be prevented from being broken.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【産業上の利用分野】本発明は、ガラス製やプラスチッ
ク製瓶などの容器を搬送する装置、或いは石炭、鉱石、
穀物、木材チップ、プラスチックチップ、セメント、樹
脂ペレットなどの粉粒体を運搬する装置に使用するコン
ベヤ用フレキシブルスクリューに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a device for transporting containers such as glass and plastic bottles, coal, ore,
The present invention relates to a flexible screw for a conveyor used in an apparatus for transporting powdered or granular materials such as grains, wood chips, plastic chips, cement and resin pellets.

【０００２】[0002]

【従来の技術】液体などの充填物を入れたガラス製、プ
ラスチック製瓶などの容器（以下、これらを単に容器と
称する）の搬送に、鋼索（ワイヤロープ）に鋼などの金
属製ワイヤを螺旋状に巻付けたスクリューが使用されて
いる。この種の構造を有するスクリューを用いる容器搬
送装置は、スクリューを一定間隔を置いて並列配置し、
スクリュー間に容器を懸架し（通常は容器の首にある鍔
をスクリューに引っ掛ける）、スクリューを回転させる
ことにより容器を搬送するように構成される。2. Description of the Related Art For transporting containers such as glass and plastic bottles (hereinafter, simply referred to as containers) filled with a liquid or the like, a steel wire (wire rope) is spirally wound with a metal wire such as steel. A screw wound into a shape is used. Container transporting device using a screw having this kind of structure, the screws are arranged in parallel at regular intervals,
It is configured to suspend the container between the screws (usually hook the collar at the neck of the container onto the screw) and rotate the screw to convey the container.

【０００３】当該装置は、容器輸送に用いられる通常の
ベルトコンベヤやローラコンベヤなどとは全く異なる搬
送原理、即ちスクリューと容器の首との接触摩擦によっ
て容器を移動させるものであり、通常のコンベヤよりも
容器の位置決めが精確で、製造工程ラインを自動化でき
ると共に、装置自体の構造も単純小型で、設備費用も安
い。This device moves a container by a conveying principle which is completely different from that of a usual belt conveyor or roller conveyor used for container transportation, that is, by moving the screw by the contact friction between the screw and the neck of the container. The positioning of the container is accurate, the manufacturing process line can be automated, the structure of the device itself is simple and small, and the equipment cost is low.

【０００４】上述の装置では、スクリューの高速回転に
より容器を搬送することから、スクリューに懸架した容
器、特にスクリューに接触する容器の首（鍔も含む）が
磨滅や損傷を受けやすい。特に、炭酸飲料を充填する容
器では安全性の点からこの損傷を出来るだけ少なくする
ことが必要である。In the above-mentioned apparatus, since the container is conveyed by the high-speed rotation of the screw, the container suspended by the screw, especially the neck (including the collar) of the container that comes into contact with the screw, is easily worn or damaged. Particularly, in the case of a container filled with a carbonated beverage, it is necessary to reduce this damage as much as possible in terms of safety.

【０００５】一方、石炭、鉱石、穀物、木材チップ、プ
ラスチックチップ、セメント、樹脂ペレットなどの粉粒
体の運搬法の一つに、多くは鋼からなるコイル状ワイヤ
を金属製又は樹脂製チューブ内に挿入・配置し、鋼製ワ
イヤを回転させてチューブ一端に設けた投入口から入れ
た粉粒体を他端に設けた排出口まで運搬する方法があ
る。しかし、コイル状ワイヤでは、ワイヤの金属材質故
にこれと接触するチューブ内壁の磨滅が著しいため、維
持費用が高くなるという問題があるだけでなく、粉粒体
の運搬がスムーズでないため、チューブ内に粉粒体が滞
留したり、或いはチューブ他端からの粉粒体吐出量が不
安定になるなどの欠点がある。更に、かかるコイル状ワ
イヤによる輸送では、搬送路線を傾斜させてチューブの
下端から上端に粉粒体を輸送することもあるが、粉粒体
を上方に運ぶ揚力が小さいという不都合な面も有する。On the other hand, one of the methods for transporting powder particles such as coal, ore, grain, wood chips, plastic chips, cement and resin pellets is to use a coiled wire made of steel in a metal or resin tube. There is a method of transporting the powder or granules inserted into and placed in a tube and rotating the steel wire from the inlet provided at one end of the tube to the outlet provided at the other end. However, in the case of coiled wire, the inner wall of the tube that comes into contact with it is significantly worn out due to the metal material of the wire, which not only has the problem of high maintenance costs, but also the transportation of powder particles is not smooth, so There are drawbacks such as accumulation of powder or granules, or instability of the discharge amount of powder or granules from the other end of the tube. Further, in the transportation by the coiled wire, although the transportation route may be inclined to transport the particles from the lower end to the upper end of the tube, there is also an inconvenience that the lifting force for conveying the particles upward is small.

【０００６】そこで本発明者らは、先に、樹脂層を鋼索
上に設けた可撓性ロッドと、このロッド上に螺旋状に巻
き付けた樹脂製コードとからなるコンベヤ用フレキシブ
ルスクリューを提案し、従来の容器搬送装置及び粉粒体
運搬装置における上記の問題点を解消した。Therefore, the present inventors previously proposed a flexible screw for a conveyor, which comprises a flexible rod having a resin layer provided on a steel rope and a resin cord spirally wound on the rod, The above-mentioned problems in the conventional container conveying device and powdery substance conveying device have been solved.

【０００７】[0007]

【発明が解決しようとする課題】ところで、このような
装置で容器の搬送を行うとき、容器は螺旋状に巻き付け
られた樹脂製コードだけでなく、ロッドの樹脂層とも摺
動するので、やがてはコードのみならず、容器が接触す
る部分の樹脂層も損耗する。そのため、スクリューは定
期的に交換しなければならないが、メンテナンス費用を
削減するにはスクリューを長寿命化することが肝要であ
る。従って、上記コードおよび鋼索上に設ける樹脂層
は、耐摩耗性に優れ、摩擦抵抗が小さいものであること
が必要である。また、湾曲した搬送路線を含む装置にお
いては、湾曲部における敷設を容易にするためにスクリ
ューには充分な可撓性が要求されるので、これに用いら
れる樹脂は上記特性だけでなく、可撓性をも備えていな
ければならない。By the way, when the container is conveyed by such a device, the container slides not only on the resin cord wound in a spiral shape but also on the resin layer of the rod, so that the container eventually comes out. Not only the cord, but also the resin layer at the portion where the container comes into contact is damaged. Therefore, the screw must be replaced regularly, but it is important to extend the life of the screw to reduce the maintenance cost. Therefore, it is necessary that the resin layer provided on the cord and the steel rope has excellent wear resistance and low frictional resistance. Further, in a device including a curved conveyance route, the screw is required to have sufficient flexibility in order to facilitate the laying in the curved portion. Therefore, the resin used for this has not only the above-mentioned characteristics but also the flexibility. Must also have sex.

【０００８】本発明者は、このような要求を満たすコン
ベヤ用フレキシブルスクリューを提供せんがため、検討
を重ねた結果、鋼索上に設けられる樹脂層およびコード
を構成する樹脂の少なくとも一方、特に好ましくは前者
に、特定の物性値を有する樹脂を用いるとよいことを見
出し、本発明を完成した。Since the inventor of the present invention does not provide a flexible screw for a conveyor satisfying such requirements, as a result of repeated studies, at least one of the resin layer provided on the steel rope and the resin constituting the cord, particularly preferably, The former found that it is preferable to use a resin having a specific physical property value, and completed the present invention.

【０００９】[0009]

【課題を解決するための手段】即ち、本発明は、鋼索上
の少なくとも一部に樹脂層を有する可撓性ロッドと該ロ
ッド上に螺旋上に設けられた少なくとも表層が樹脂から
なるコードとを備えてなるコンベヤ用フレキシブルスク
リューにおいて、可撓性ロッドの樹脂層およびコードを
構成する樹脂の少なくとも一方の少なくとも表層が、曲
げ弾性率が３０００kgf/cm² 以下、摩擦係数が２．０以
下且つ摩耗量が２５ｍｇ以下である樹脂からなることを
特徴とするコンベヤ用フレキシブルスクリューに係るも
のである。That is, according to the present invention, there is provided a flexible rod having a resin layer on at least a part of a steel rope, and a cord provided on a spiral of the rod and at least a surface layer of which is made of resin. In a conveyor flexible screw provided, at least one of the resin layer of the flexible rod and the resin constituting the cord has a bending elastic modulus of 3000 kgf / cm ² or less, a friction coefficient of 2.0 or less, and an abrasion amount. Is a resin of 25 mg or less.

【００１０】曲げ弾性率が小さいことと、摩擦係数が小
さく且つ摩耗量が少ないということとは、樹脂の特性と
して相矛盾するもののようであるが、フレキシブルスク
リューの樹脂層を構成する樹脂には前述のごとく、可撓
性と耐久性が同時に要求されるので、充分な可撓性を確
保するために曲げ弾性率が３０００ｋｇｆ／ｃｍ² 以
下、好ましくは２０００ｋｇｆ／ｃｍ² 以下であること
が必要であり、それと同時に耐久性の確保のために摩擦
係数が２．０以下、好ましくは１．５以下で且つ摩耗量
が２５ｍｇ以下、好ましくは１０ｍｇ以下であることが
必要となる。The fact that the flexural modulus is small and the friction coefficient is small and the amount of wear is small seems to contradict each other as the characteristics of the resin. as the so flexibility and durability are simultaneously required, the flexural modulus in order to ensure sufficient flexibility 3000 kgf / cm ² or less, preferably required to be 2,000 kgf / cm ² or less At the same time, in order to ensure durability, it is necessary that the friction coefficient is 2.0 or less, preferably 1.5 or less and the amount of wear is 25 mg or less, preferably 10 mg or less.

【００１１】曲げ弾性率が上記値より大きい樹脂では、
硬すぎて充分な可撓性が得られないので好ましくない
が、この値が余りにも小さくなりすぎる（つまり軟らか
くなりすぎる）と、摩擦係数が大きくなる結果、被搬送
容器のスムーズな搬送が出来にくくなったり、摩耗しや
すくなって耐久性を確保できない。そこで本発明におい
ては、摩擦係数及び摩耗量の上限を定めることによって
耐久性の確保を企っている。For a resin having a flexural modulus higher than the above value,
It is not preferable because it is too hard to obtain sufficient flexibility, but if this value is too small (that is, too soft), the coefficient of friction becomes large, which makes it difficult to smoothly transfer the container to be transferred. It becomes easy to wear and wear, and durability cannot be secured. Therefore, in the present invention, the upper limit of the friction coefficient and the wear amount is set to ensure the durability.

【００１２】上記各物性値で特定された本発明の樹脂
は、良好な可撓性と耐久性とを兼備しているので、これ
を用いた本発明のフレキシブルスクリューは、容器搬送
時の容器との摺動による損耗が少ないため、寿命が長
く、従って本発明によれば、メンテナンス費用を削減す
ることが可能である。Since the resin of the present invention specified by the above-mentioned physical property values has both good flexibility and durability, the flexible screw of the present invention using this resin can be used as a container during container transportation. Since there is little wear due to sliding, the life is long, and according to the present invention, maintenance costs can be reduced.

【００１３】なお、本発明における摩擦係数とは、鈴木
式摩擦係数試験法に従い、相手の素材がＳ−４５Ｃ、面
圧が５kgf/cm² 、滑り速度が０．２ｍ／秒の条件下で測
定して得られた値である。また、摩耗量は、テーバー摩
耗試験機を用い、摩耗輪がＨ−２２、荷重１ｋｇの条件
下で１０００回転させたときの摩耗量である。The friction coefficient in the present invention is measured according to the Suzuki type friction coefficient test method under the conditions that the other material is S-45C, the surface pressure is 5 kgf / cm ² , and the sliding speed is 0.2 m / sec. This is the value obtained by The amount of wear is the amount of wear when using a Taber wear tester and rotating the wear wheel 1000 times under the conditions of H-22 and a load of 1 kg.

【００１４】上記の各要件を満足する樹脂としては、例
えば、軟質フッ素樹脂、中密度ポリエチレン、低密度ポ
リエチレン、ポリアミドエラストマー（例えば市販品と
しては、宇部興産株式会社製、商品名ＰＡＥ１２０
０）、熱可塑性ウレタン（例えば市販品としては、株式
会社クラレ製、商品名クラミロン９１９８）、熱可塑性
ポリエステル（例えば市販品としては、東洋紡績株式会
社製ペルプレンＳ１００１−０４）等が挙げられるが、
中でも軟質フッ素樹脂が好ましく用いられる。Resins satisfying the above requirements include, for example, soft fluororesin, medium density polyethylene, low density polyethylene, polyamide elastomer (for example, commercially available products, Ube Industries, Ltd., trade name PAE120).
0), thermoplastic urethane (for example, as a commercial product, manufactured by Kuraray Co., Ltd., trade name: Clamiron 9198), thermoplastic polyester (for example, as a commercial product, Toyo Boseki Co., Ltd., Perprene S1001-04), and the like.
Of these, soft fluororesins are preferably used.

【００１５】ここに軟質フッ素樹脂とは、フッ素ゴムに
フッ素樹脂をグラフトしたもの、ハードセグメントとし
てのフッ素樹脂とソフトセグメントとしてのフッ素エラ
ストマー（ゴム）とからなる熱可塑性フッ素エラストマ
ーおよびフッ素系共重合体をいい、例えば、フッ化ビニ
リデン−ヘキサフルオロプロピレン共重合体またはフッ
化ビニリデン−ヘキサフルオロプロピレン−テトラフル
オロエチレン共重合体をフッ素ゴム主鎖とし、フッ化ビ
ニリデンをグラフトしたもの（市販品としては、セント
ラル硝子株式会社製、商品名セフラルソフト１５０）、
フッ化ビニリデン−ヘキサフルオロプロピレン−テトラ
フルオロエチレン共重合体（モル比５０：３０：２０）
のソフトセグメント８５重量％とエチレン−テトラフル
オロエチレン−ヘキサフルオロプロピレン共重合体（モ
ル比４３：４９：８）のハードセグメント１５重量％と
からなる熱可塑性フッ素エラストマー（市販品として
は、ダイキン工業株式会社製、商品名ダイエルサーモプ
ラスチックＴ−５３０）、四フッ化エチレン−プロピレ
ン共重合体、四フッ化エチレン−エチレン共重合体等が
挙げられ、中でもセフラルソフト１５０が特に好ましく
用いられる。The term "soft fluororesin" as used herein means a fluororubber grafted with a fluororesin, a thermoplastic fluoroelastomer comprising a fluororesin as a hard segment and a fluoroelastomer (rubber) as a soft segment, and a fluorocopolymer. , Vinylidene fluoride-hexafluoropropylene copolymer or vinylidene fluoride-hexafluoropropylene-tetrafluoroethylene copolymer as a fluororubber main chain, grafted with vinylidene fluoride (as a commercial product, Made by Central Glass Co., Ltd., trade name Sefral Soft 150),
Vinylidene fluoride-hexafluoropropylene-tetrafluoroethylene copolymer (molar ratio 50:30:20)
Of 85% by weight of a soft segment and 15% by weight of a hard segment of an ethylene-tetrafluoroethylene-hexafluoropropylene copolymer (molar ratio 43: 49: 8), a thermoplastic fluoroelastomer (commercially available from Daikin Industries, Ltd. Company name, trade name DAIEL THERMOPLASTIC T-530), tetrafluoroethylene-propylene copolymer, tetrafluoroethylene-ethylene copolymer and the like can be mentioned, of which Cefral Soft 150 is particularly preferably used.

【００１６】なお、上記樹脂には、動摩擦係数低減の目
的で四フッ化系樹脂潤滑剤（例えばダイキン工業株式会
社製、商品名ルブロン）を、耐摩耗性向上の目的でグラ
ファイト、炭化珪素、窒化ホウ素、モリブデン、トリア
ジンビスマレイミド粉体等を添加してもよい。A tetrafluoride resin lubricant (for example, Lubron, manufactured by Daikin Industries, Ltd., trade name: Lubron) is used for the above-mentioned resin for the purpose of reducing the dynamic friction coefficient, and graphite, silicon carbide, nitriding is used for the purpose of improving wear resistance. Boron, molybdenum, triazine bismaleimide powder or the like may be added.

【００１７】これら添加物の配合量は、樹脂１００重量
部に対して通常、１〜２０重量部、好ましくは１〜５重
量部である。The amount of these additives to be added is usually 1 to 20 parts by weight, preferably 1 to 5 parts by weight, based on 100 parts by weight of the resin.

【００１８】本発明においては、上記の樹脂を可撓性ロ
ッドの樹脂層およびコードを構成する樹脂の少なくとも
一方に用いるが、本発明の好ましい態様としては、可撓
性ロッドの樹脂層に上記樹脂を使用したものが挙げられ
る。本発明の目的達成のためには、被搬送容器と摺動す
る部分が上記樹脂で構成されていればよいので、可撓性
ロッドの樹脂層は、必ずしも鋼索上の全面に亘って設け
られていなくてもよく、容器と摺動する部分だけに設け
られていてもよい。また、この樹脂層は、全体が上記樹
脂からなるものでも或いは表層のみが上記樹脂で構成さ
れていてもよい。In the present invention, the above-mentioned resin is used for at least one of the resin layer of the flexible rod and the resin forming the cord. In a preferred embodiment of the present invention, the resin is used for the resin layer of the flexible rod. The thing which used is mentioned. In order to achieve the object of the present invention, since the portion that slides on the transported container may be made of the above resin, the resin layer of the flexible rod is not necessarily provided over the entire surface of the steel rope. It does not have to be provided, and may be provided only in the portion that slides on the container. The resin layer may be entirely made of the above resin, or only the surface layer may be made of the above resin.

【００１９】鋼索上に樹脂層を設ける方法としては、例
えば通常の押出被覆技術を用いて鋼索を被覆する方法、
上記の樹脂からなるテープを鋼索上に全面またはギャッ
プ巻きすることによって鋼索上に樹脂層を全面もしくは
部分的に設ける方法などが挙げられる。押出被覆を行う
には、例えば鋼索を一定の張力下で一方向に送り出しな
がら、鋼索の進行方向軸上に配置したダイスから樹脂材
を溶融押出しすると同時に鋼索上に被覆する如き方法が
示される。As a method of providing a resin layer on the steel rope, for example, a method of coating the steel rope using a usual extrusion coating technique,
Examples include a method in which a resin layer is entirely or partially provided on the steel rope by winding the tape made of the above resin on the steel rope over the entire surface or gap. To carry out extrusion coating, for example, a method is shown in which the resin material is melt-extruded from a die arranged on the traveling direction axis of the steel rope while being fed in one direction under constant tension, and at the same time the steel rope is coated.

【００２０】このときの樹脂層の肉厚はスクリューの用
途やサイズにもよるが、通常は２．０mm以下、好適には
１．０mm以下である。この肉厚はスクリューの同心度を
高めるために可及的に均一であることが望ましい。The thickness of the resin layer at this time is usually 2.0 mm or less, preferably 1.0 mm or less, although it depends on the use and size of the screw. It is desirable that this wall thickness be as uniform as possible in order to increase the concentricity of the screw.

【００２１】本発明のフレキシブルスクリューの用途で
ある容器搬送装置ではスクリューの回転により容器を搬
送することから、可撓性ロッドに螺旋状に巻付けられた
コードと直接接触する容器の首（鍔も含む）が摩滅や損
傷を受けないことが製品上また安全上重要である。特
に、炭酸飲料を充填する容器では容器の傷に一層注意し
なければならない。従って、コードの材質としては耐摩
耗性、可撓性、ころがり性、滑り性などが良好で、且つ
動摩擦（滑り摩擦ところがり摩擦）係数が小さいことが
好ましい。Since the container is conveyed by the rotation of the screw in the container conveying device which is the application of the flexible screw of the present invention, the neck of the container (also the collar) which comes into direct contact with the cord spirally wound around the flexible rod. It is important for the product and safety that the (including) is not worn or damaged. Particularly, in a container filled with a carbonated beverage, more attention must be paid to the damage of the container. Therefore, it is preferable that the material of the cord has good wear resistance, flexibility, rolling property, slidability and the like and has a small coefficient of dynamic friction (sliding friction and rolling friction).

【００２２】また、別途の粉粒体運搬装置においては、
粉粒体（例えば砂利、砕石、石炭、コークス、鉄鉱石、
土、石灰石、穀物、セメント、木材や樹脂などのチップ
やペレットなどのいわゆるばら物）をシャフトの回転に
より運搬するので、コードはそれに見合うだけの十分な
耐摩耗性や強度を有していることが望まれる。In addition, in the separate powder and granular material conveying device,
Granules (eg gravel, crushed stone, coal, coke, iron ore,
Since the shaft rotates to convey soil, limestone, grain, cement, chips and pellets such as wood and resin, etc., the cord must have sufficient wear resistance and strength to meet it. Is desired.

【００２３】上記の要求を満たすコードの樹脂材として
は、前記可撓性ロッドの樹脂層と同じ樹脂が挙げられる
が、その他の樹脂が好ましく用いられる場合もあり、例
えばポリオレフィン〔例えば各種ポリエチレン、特に超
高分子量ポリエチレンまたはそれをベースとする射出成
形性の改善されたもの（例えば、市販品としては、三井
石油化学工業株式会社製リュブマー）、ポリプロピレン
など〕、ポリエーテル（例えばポリアセタール、ポリフ
ェニレンエーテルなど）、ポリアミド（例えば６−ナイ
ロン、６，６ナイロン、11−ナイロンなど）、フッ素樹
脂（例えばポリテトラフルオロエチレン、テトラフルオ
ロエチレン−パーフルオロアルキルビニルエーテル共重
合体など）、ポリエステル（例えばポリエチレンテレフ
タレート、ポリブチレンテレフタレートなど）などをコ
ードの樹脂材として用いることができる。中でもリュブ
マーは、摺動性や耐久性の点から好ましく用いられる。As the resin material of the cord satisfying the above requirements, the same resin as the resin layer of the flexible rod may be mentioned, but other resins may be preferably used. For example, polyolefin [eg various polyethylene, particularly Ultra-high-molecular-weight polyethylene or those based on it with improved injection moldability (for example, commercially available products include Mitsui Petrochemical Co., Ltd., Lübmer), polypropylene, etc.), polyethers (for example, polyacetal, polyphenylene ether, etc.) , Polyamide (eg 6-nylon, 6,6 nylon, 11-nylon etc.), fluororesin (eg polytetrafluoroethylene, tetrafluoroethylene-perfluoroalkyl vinyl ether copolymer etc.), polyester (eg polyethylene terephthalate, polybrene) And the like can be used terephthalate, etc.) as the resin material of the cord. Among them, the lubmer is preferably used in terms of slidability and durability.

【００２４】コードは、全体が上記樹脂製でもよいが、
ケブラー（アラミド繊維）、ガラス、カーボンファイバ
などの繊維束からなる芯体を有していてもよい。芯体の
あるコードは、摩擦熱による温度上昇や容器搬送時にか
かる荷重などに起因するコード伸びの抑制が可能であ
り、結果として螺旋状巻きしたコードピッチの乱れを防
止できる点で好都合である。The cord may be entirely made of the above resin,
You may have the core body which consists of fiber bundles, such as Kevlar (aramid fiber), glass, and carbon fiber. The cord with a core is advantageous in that the cord elongation can be suppressed due to the temperature rise due to frictional heat and the load applied during container transportation, and as a result, the disorder of the spirally wound cord pitch can be prevented.

【００２５】なお、可撓性ロッド上に螺旋状巻きするコ
ードの巻付けピッチは、容器搬送装置では容器の搬送速
度を考慮した上で容器の大きさ、容器の搬送数量、スク
リュー回転数などに基づいて、又粉粒体運搬装置では粉
粒体の種類や大きさなどに基づいて適宜決定される。
又、ピッチはスクリューの全長にわたって一定である必
要はなく、例えばスクリューの任意部分において変化さ
せてもよい。The winding pitch of the cord spirally wound on the flexible rod depends on the size of the container, the number of containers to be conveyed, the number of rotations of the screw, etc. in consideration of the conveying speed of the container in the container conveying device. On the basis of the type and size of the granular material, it is appropriately determined in the granular material conveying device.
Also, the pitch need not be constant over the entire length of the screw, and may vary, for example, in any part of the screw.

【００２６】[0026]

【実施例】以下、本発明のコンベヤ用フレキシブルスク
リューを実施例に基づいて詳細に説明する。図１はフレ
キシブルスクリューの一例を、図２はその横断面を示
す。当スクリューは、可撓性ロッド１とロッド１上に螺
旋状に巻付けた樹脂製コード２とからなる。ロッド１は
鋼索１１上に前記特定値の曲げ弾性率、摩擦係数および
摩耗量を有する樹脂層１２が設けられ、コード２は樹脂
層２２の中心に芯体２１を有する。EXAMPLES A flexible screw for a conveyor according to the present invention will be described in detail below based on examples. FIG. 1 shows an example of a flexible screw, and FIG. 2 shows a cross section thereof. The screw comprises a flexible rod 1 and a resin cord 2 wound around the rod 1 in a spiral shape. The rod 1 is provided with a resin layer 12 having a bending elastic modulus, a friction coefficient and a wear amount having the above-mentioned specific values on a steel rope 11, and the cord 2 has a core body 21 at the center of the resin layer 22.

【００２７】実施例１ ロッドの樹脂層にセフラルソフト（前出、曲げ弾性率：
１１００kgf/cm² 、摩擦係数：１．２、摩耗量：５．１
ｍｇ）を、コードの樹脂材としてリュブマー（前出、）
を、コードの芯体としてケブラー（前出、）を用い、下
記のサイズのフレキシブルスクリューを作製した。サイ
ズは、ロッドの径６．８mm、鋼索の径６．０mm、ロッド
の樹脂層の肉厚０．４mm、コードの径４．５mm、芯体の
径１．０mm、コードの樹脂層の肉厚１．７５mm、スクリ
ューのフライト径１５．５mm、コードの巻付ピッチ４０
mmである。 実施例２ ロッドの樹脂層に、ルブロン（前出、）を１５重量％、
窒化ホウ素を３重量％配合した以外は実施例１と同様に
してフレキシブルスクリューを作製した。 実施例３ セフラルソフトに替えてダイエルサーモプラスチック
（前出、曲げ弾性率：１５００kgf/cm² 、摩擦係数：
０．６、摩耗量：１０ｍｇ）を使用した以外は実施例１
と同様にしてフレキシブルスクリューを作製した。Example 1 A resin layer of a rod was provided with a sepral soft material (described above, flexural modulus:
1100kgf / cm ² , friction coefficient: 1.2, wear amount: 5.1
mg) as the resin material for the cord, Lübmer (see above)
Using a Kevlar (as described above) as the core of the cord, a flexible screw having the following size was produced. The size is rod diameter 6.8 mm, steel rope diameter 6.0 mm, rod resin layer thickness 0.4 mm, cord diameter 4.5 mm, core body diameter 1.0 mm, cord resin layer thickness 1.75mm, screw flight diameter 15.5mm, cord winding pitch 40
mm. Example 2 15 wt% of Lubron (supra) was added to the resin layer of the rod,
A flexible screw was produced in the same manner as in Example 1 except that 3% by weight of boron nitride was added. Example 3 In place of Cefralsoft, DAIEL THERMOPLASTIC (described above, flexural modulus: 1500 kgf / cm ² , friction coefficient:
0.6, wear amount: 10 mg)
A flexible screw was produced in the same manner as in.

【００２８】比較例１ セフラルソフトに替えてレザミン（ポリウレタンエラス
トマー、大日精化株式会社製）（曲げ弾性率：約２００
kgf/cm² 、摩擦係数：約３．０、摩耗量：３４ｍｇ）を
使用した以外は実施例１と同様にしてフレキシブルスク
リューを作製した。Comparative Example 1 Resamine (polyurethane elastomer, manufactured by Dainichiseika Co., Ltd.) was used instead of Cefralsoft (flexural modulus: about 200).
A flexible screw was produced in the same manner as in Example 1 except that kgf / cm ² , friction coefficient: about 3.0, and wear amount: 34 mg) were used.

【００２９】このようにして得られた実施例および比較
例のフレキシブルスクリューを容器搬送装置に用い、下
記ｉ）およびii）の試験方法にてスクリューの耐久性
（摩耗程度）および容器の首の損傷（又は損耗度合）を
調べた。また、スクリューの可撓性についての評価は、
３０ｃｍ長のスクリューの片端を水平に保持し、他端を
自由に垂れ下がらせたときの、その垂下量が３ｃｍ以上
のものを良、それ以下を不良と判定する方法で行った。
その結果を表１に示した。なお、容器はポリエチレンテ
レフタレート製で、その大きさは、首の径２６．０mm、
鍔の径４１．２mm、その肉厚３．３５mmである。The flexible screws of Examples and Comparative Examples thus obtained were used in a container conveying device and the durability (degree of wear) of the screw and damage to the neck of the container were measured by the following test methods i) and ii). (Or degree of wear) was examined. Also, the evaluation of the flexibility of the screw,
When one end of a screw having a length of 30 cm was held horizontally and the other end was allowed to hang freely, a hanging amount of 3 cm or more was judged as good, and a value less than that was judged as defective.
The results are shown in Table 1. In addition, the container is made of polyethylene terephthalate, the size of the neck is 26.0 mm,
The diameter of the brim is 41.2 mm and its wall thickness is 3.35 mm.

【００３０】ｉ）スクリューの耐久性試験方法 スクリュー回転数６００rpm 、容器搬送速度２４ｍ／
分、容器搬送ピッチ１２０ｍｍ、容器重量５００ｇの条
件下で１５時間稼働した後、ロッドおよびコードの重量
変化を求め、スクリュー長１２０ｍｍ当たりのロッドお
よびコードの重量変化がそれぞれ１×１０^-2ｇ以下であ
れば実用上の耐久性は「良」、それよりも大きい値であ
れば「不良」と判定した。 ii）容器の首の損傷程度を調べる試験方法 稼働時間を９０秒とし、他の条件は上記耐久性試験と同
一にて稼働した後、目視にてポリエチレンテレフタレー
ト容器の首部に商品価値を損ねる程度の傷が生ずるかど
うかを調べた。I) Screw durability test method Screw rotation speed 600 rpm, container transport speed 24 m /
After operating for 15 hours under the conditions of a container conveyance pitch of 120 mm and a container weight of 500 g, the weight change of the rod and the cord was determined, and the weight change of the rod and the cord per screw length of 120 mm was 1 × 10 ^-2 g or less, respectively. The practical durability was judged to be “good”, and a value larger than that was judged to be “poor”. ii) Test method for checking the degree of damage to the neck of the container After operating for 90 seconds and operating under the same conditions as the above durability test under other conditions, the neck of the polyethylene terephthalate container can be visually inspected to such an extent that the commercial value is damaged. I checked to see if it would hurt.

【００３１】[0031]

【表１】 [Table 1]

【００３２】[0032]

【発明の効果】本発明のコンベヤ用フレキシブルシャフ
トは、以上説明したように特定の曲げ弾性率、摩擦係数
および摩耗量を有する樹脂を鋼索上の樹脂層および／ま
たはコードの材料として用いたものであるから、良好な
可撓性を有すると共に、耐摩耗性に優れ、且つ摩擦係数
が小さいので、搬送時の容器との摺動による樹脂層の損
耗が少なく、且つ容器を損傷することも少ない。INDUSTRIAL APPLICABILITY As described above, the flexible shaft for a conveyor of the present invention uses a resin having a specific bending elastic modulus, friction coefficient and wear amount as a material for a resin layer and / or cord on a steel rope. Therefore, it has good flexibility, excellent wear resistance, and a small coefficient of friction, so that the resin layer is less likely to be worn due to sliding with the container during transportation, and the container is less likely to be damaged.

【図面の簡単な説明】[Brief description of drawings]

【図１】本発明のシャフトの一例を示す一部切取斜視図
である。FIG. 1 is a partially cutaway perspective view showing an example of a shaft of the present invention.

【図２】図１に示したシャフトの横断面図である。2 is a cross-sectional view of the shaft shown in FIG.

【符号の説明】[Explanation of symbols]

１ ：可撓性ロッド ２ ：樹脂製コード １１ ：鋼索 １２ ：ロッドの樹脂層 ２１ ：芯体 ２２ ：コードの樹脂層 1: Flexible Rod 2: Resin Cord 11: Steel Cord 12: Rod Resin Layer 21: Core 22: Cord Resin Layer

Claims (2)

【特許請求の範囲】[Claims] 【請求項１】 鋼索上の少なくとも一部に樹脂層を有す
る可撓性ロッドと該ロッド上に螺旋上に設けられた少な
くとも表層が樹脂からなるコードとを備えてなるコンベ
ヤ用フレキシブルスクリューにおいて、可撓性ロッドの
樹脂層およびコードを構成する樹脂の少なくとも一方の
少なくとも表層が、曲げ弾性率が３０００kgf/cm² 以
下、摩擦係数が２．０以下且つ摩耗量が２５ｍｇ以下で
ある樹脂からなることを特徴とするコンベヤ用フレキシ
ブルスクリュー。1. A flexible screw for a conveyor, comprising: a flexible rod having a resin layer on at least a part of a steel rope; and a cord provided on the rod in a spiral shape and at least a surface layer made of resin. At least the surface layer of at least one of the resin layer of the flexible rod and the resin constituting the cord is made of a resin having a bending elastic modulus of 3000 kgf / cm ² or less, a friction coefficient of 2.0 or less, and an abrasion amount of 25 mg or less. Characteristic flexible screw for conveyor. 【請求項２】 可撓性ロッドの樹脂層が、軟質フッ素樹
脂からなることを特徴とする請求項１に記載のコンベヤ
用フレキシブルスクリュー。2. The flexible screw for a conveyor according to claim 1, wherein the resin layer of the flexible rod is made of a soft fluororesin.