JPH05205940A - Superconducting device - Google Patents
Superconducting deviceInfo
- Publication number
- JPH05205940A JPH05205940A JP3297945A JP29794591A JPH05205940A JP H05205940 A JPH05205940 A JP H05205940A JP 3297945 A JP3297945 A JP 3297945A JP 29794591 A JP29794591 A JP 29794591A JP H05205940 A JPH05205940 A JP H05205940A
- Authority
- JP
- Japan
- Prior art keywords
- pipe
- superconducting
- ceramic
- hollow
- ceramics
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の利用分野】本発明はセラミック系超電導材料を
応用した電力蓄積装置に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a power storage device using a ceramic superconducting material.
【０００２】[0002]
【従来の技術】従来、超電導材料はＮｂ−Ｇｅ（例えば
Ｎｂ3 Ｇｅ）等の金属材料が用いられている。この材料
は金属であるため、延性、展性または曲げ性を高く有
し、超電導マグネット用コイル、また電力蓄積用コイル
として用いることが可能である。2. Description of the Related Art Conventionally, a metal material such as Nb-Ge (for example, Nb 3 Ge) has been used as a superconducting material. Since this material is a metal, it has high ductility, malleability or bendability, and can be used as a coil for a superconducting magnet or a coil for power storage.
【０００３】しかし、この金属の超電導材料はＴｃ（超
電導臨界温度を以下Ｔｃという）オンセットが小さく、
２３Ｋまたはそれ以下でしかなかった。しかしその工業
的応用を考えるならば、このＴｃが１００Ｋまたはそれ
以上を有し、Ｔｃｏ（電気抵抗が零となる温度）が液体
窒素温度である７７Ｋまたはそれ以上であることがきわ
めて重要である。However, this metallic superconducting material has a small Tc (superconducting critical temperature hereafter referred to as Tc) onset,
It was only 23K or less. However, considering its industrial application, it is extremely important that this Tc has a value of 100K or higher and that Tco (the temperature at which the electric resistance becomes zero) is 77K or higher, which is the liquid nitrogen temperature.
【０００４】最近、かかる超電導材料として、銅の酸化
物セラミック材料が注目されている。しかしこの銅の酸
化物セラミックスは延性、展性および曲げ性に乏しい。
加えて成型した後の加工がきわめて困難であるという他
の欠点を有する。Recently, copper oxide ceramic materials have attracted attention as such superconducting materials. However, this copper oxide ceramic is poor in ductility, malleability and bendability.
In addition, it has another drawback that it is extremely difficult to process after molding.
【０００５】[0005]
【従来の問題点】このため、銅の酸化物セラミックスを
用いて、リング状またはコイル状に設けるとともに、そ
の始点と終点とを同時に超電導セラミックスで連結し、
電力蓄積装置とする試みはまったくない。加えて、コイ
ル構造を有しつつ、同時にセラミックスを機械的に金属
で補強する手段も、また自らに冷媒を有し冷却する構造
もまったく知られていない。Therefore, copper oxide ceramics are used to form a ring shape or a coil shape, and the start point and the end point thereof are simultaneously connected by superconducting ceramics,
There have been no attempts to use it as a power storage device. In addition, neither a means for mechanically reinforcing ceramics with a metal while having a coil structure, nor a structure for cooling itself by having a cooling medium are known at all.
【０００６】[0006]
【問題を解決すべき手段】本発明は超電導セラミックス
をリング状またはコイル状に設け、その始点と終点とを
超電導セラミックスで連結する電力蓄積装置である。さ
らに本発明はこのセラミックスに金属または金属化合物
の支持体を添わしめ、機械的補強に加えて、このセラミ
ックスが非超電導状態となった時も電流を流し得る手段
としている。さらにこの中空の支持体の内部に超電導セ
ラミック材料となるべき材料を混合または溶かした、ま
たはゲル状にした溶液を中空パイプの一方を一次的に塞
いで他方より注入する。The present invention is a power storage device in which superconducting ceramics are provided in a ring shape or a coil shape, and the start point and the end point thereof are connected by the superconducting ceramics. Further, in the present invention, a support made of a metal or a metal compound is added to this ceramic, and in addition to mechanical reinforcement, a means for allowing an electric current to flow even when this ceramic is in a non-superconducting state. Further, a solution in which a material to be a superconducting ceramic material is mixed or melted or gelled is temporarily closed in one of the hollow pipes and injected into the hollow support from the other.
【０００７】次にこの中空パイプ全体を加熱し、液体成
分である溶媒全体を気化して除去する。するとこの超電
導セラミック材料は中空パイプの内壁にコーティングさ
れる。これを加熱し、焼成させるとともに、酸化または
還元を繰り返し行うことにより、超電導性を有するセラ
ミック材料、例えば銅の酸化物セラミックスである（Ａ
1-x Ｂｘ）ｙＣｕＯｚ ｘ＝０．０１〜０．３，ｙ＝
１．３〜２．２，ｚ＝２．０〜４．５で示される分子構
造を有し、ＡがＹ（イットリューム），Ｇａ（ガリュー
ム），Ｚｒ（ジルコニューム），Ｎｂ（ニオブ），Ｇｅ
（ゲルマニューム），Ｙｂ（イッテルビューム）または
その他のランタノイドより１つまたは複数種選ばれ、Ｂ
はＲａ（ラジューム），Ｂａ（バリューム）またはＳｒ
（ストロンチューム），Ｃａ（カルシューム），Ｍｇ
（マグネシューム），Ｂｅ（ベリリューム）より１つま
たは複数種選ばれ、セラミックスを形成する。Next, the entire hollow pipe is heated to vaporize and remove the entire solvent which is a liquid component. Then, the superconducting ceramic material is coated on the inner wall of the hollow pipe. A ceramic material having superconductivity, for example, a copper oxide ceramic, is obtained by repeating heating and firing and oxidation or reduction (A
1-x Bx) yCuOz x = 0.01 to 0.3, y =
It has a molecular structure represented by 1.3 to 2.2, z = 2.0 to 4.5, and A is Y (yttrium), Ga (gallum), Zr (zirconium), Nb (niobium), Ge.
(Germanium), Yb (ytterbume) or one or more kinds selected from other lanthanoids, B
Is Ra (radium), Ba (value) or Sr
(Strontium), Ca (calcium), Mg
One or more kinds are selected from (Magnesium) and Be (Berylium) to form ceramics.
【０００８】本発明で用いられるセラミックスは上記以
外の元素をＡ，Ｂまたは添加不純物として加えることが
可能である。The ceramics used in the present invention may contain elements other than those mentioned above as A, B or added impurities.
【０００９】本発明において、中空金属支持体の内壁に
第１の層として超電導セラミック材料がコーティングさ
れるが、さらにその上側にこの第１の層のセラミック材
料を十分固化した後、第２層のセラミック材料をコーテ
ィングすべく、同一工程を繰り返しすることは有効であ
る。またその場合、それぞれのコーティング層でＡまた
はＢの種類、Ｘ，Ｙ，Ｚの値の一部を変更してもよい。In the present invention, the inner wall of the hollow metal support is coated with the superconducting ceramic material as the first layer, and the ceramic material of the first layer is sufficiently solidified on the upper side of the superconducting ceramic material. It is useful to repeat the same process to coat the ceramic material. In that case, the type of A or B and a part of the values of X, Y, and Z may be changed in each coating layer.
【００１０】本発明において、さらにこれを繰り返して
多層構造としてもよいことはいうまでもない。Needless to say, in the present invention, this may be repeated to form a multilayer structure.
【００１１】[0011]
【作用】本発明の超電導電力蓄積装置により、初めて安
価な大電力用バッテリを作ることが可能となった。特に
その応用として、太陽電池等の光電変換装置で発電した
電気エネルギを蓄積させ得る。さらにこの蓄積装置が需
要地と数百〜数千Kmも離れている場合、この蓄積装置に
電気エネルギを充電して、それをトラック、船等により
輸送することにより、電気エネルギという目に見えない
エネルギを移送し得る。かつ本発明の蓄積装置は化学反
応を用いないため、長期使用においても何らの化学的な
劣化もない。The superconducting power storage device of the present invention makes it possible for the first time to manufacture an inexpensive battery for high power. In particular, as an application thereof, electric energy generated by a photoelectric conversion device such as a solar cell can be stored. Furthermore, if this storage device is several hundred to several thousand Km away from the demanded place, the storage device is charged with electric energy and transported by a truck, ship, etc. Energy can be transferred. Moreover, since the storage device of the present invention does not use a chemical reaction, there is no chemical deterioration even in long-term use.
【００１２】また本発明のコイル状の始点と終点を互い
に電気的に抵抗が零であるセラミックスで連結すること
により、エンドレスコイルとし得る。このコイルは電流
損失のないコイル、即ち電気エネルギの蓄積用装置とし
て用いることが可能となる。以下図面に従って本発明の
実施例を示す。Further, an endless coil can be obtained by connecting the starting point and the ending point of the coil shape of the present invention to each other with ceramics having an electrical resistance of zero. This coil can be used as a coil without current loss, that is, as a device for storing electric energy. Embodiments of the present invention will be described below with reference to the drawings.
【００１３】[0013]
〔実施例〕この実施例では（Ａ1-x Ｂｘ）ｙＣｕＯｚに
おいてＡとしてＹをＹ2 Ｏ3 ，ＢとしてＢａをＢａＣＯ
3 またＣｕとしてＣｕＯを用いた。それぞれ高純度化学
社製の９９．９５％以上のものを用いた。これらをｘ＝
０．０５，ｘ＝０．０７５及びｘ＝０．１，ｙ＝１．
８，ｙ＝２．０，ｙ＝２．２とした。これらを混合して
９種類の混合物を作った。これらを一度３Ｋｇ／ｃｍ2
の圧力で加圧しタブレットとし７００℃、3 時間さらに
１０００℃、１０時間で大気中で仮焼成した。さらにこ
れらを再び粉砕した。そしてその平均粒径が１００μｍ
以下、例えば１０μｍ程度となるようにした。この混合
物をカプセル内に封入し、再びこれを５Ｋｇ／ｃｍ2 の
圧力でプレスし、タブレット状とした。そしてこれを１
０００℃、１０時間酸化性雰囲気例えば大気中で本焼成
した。するとこの構造はペルプスカイト構造もみられる
が、変形K2NiF4型がＸ線解析像から観察された。[Embodiment] In this embodiment, in (A 1-x Bx) yCuOz, Y is Y 2 O 3 as A, and Ba is BaCO as B.
3 CuO was used as Cu. 99.95% or more manufactured by Kojundo Chemical Co., Ltd. was used. X =
0.05, x = 0.075 and x = 0.1, y = 1.
8, y = 2.0 and y = 2.2. These were mixed to make 9 kinds of mixtures. Once these 3Kg / cm 2
Then, the mixture was pressed at 700 ° C. for 3 hours, then at 1000 ° C. for 10 hours, and temporarily calcined in the atmosphere. Further, they were ground again. And the average particle size is 100 μm
Hereinafter, for example, the thickness is set to about 10 μm. This mixture was enclosed in a capsule and pressed again at a pressure of 5 Kg / cm 2 to give a tablet. And this one
Main firing was performed in an oxidizing atmosphere such as air at 000 ° C. for 10 hours. Then, although this structure had a perovskite structure, the modified K 2 NiF 4 type was observed from the X-ray analysis image.
【００１４】次にこの本焼成したＴｃオンセットが４０
Ｋ以上好ましくは９０Ｋ，Ｔｃｏが好ましくは７７Ｋ以
上あることを電圧−電流−温度特性より確認する。Next, this main-baked Tc onset is 40
It is confirmed from the voltage-current-temperature characteristics that K or more is preferably 90K and Tco is preferably 77K or more.
【００１５】再びこのタブレットを微粉末とした。そし
てこの平均粒径が１００μｍ以下〜５μｍ例えば３０μ
ｍになるようにした。この工程において、この粉砕の
際、その結晶構造が基本的に破壊しないように努めた。This tablet was again made into a fine powder. The average particle size is 100 μm or less to 5 μm, for example, 30 μm.
It was set to m. In this process, an effort was made so that the crystal structure was not basically destroyed during the pulverization.
【００１６】この粉末を液体、例えばフロン液またはア
ルコール例えばエタノールその他の液体中に混合、また
は溶かした。This powder was mixed or dissolved in a liquid such as Freon liquid or an alcohol such as ethanol or other liquid.
【００１７】この溶液を中空の支持体である図１に示し
た金属パイプ（２）、例えば銅または銅の化合物（例え
ばＮｉＣｕ化合物）の内部に他方を塞いで注いだ。この
パイプをセラミック粒子が内壁に均一な厚さに付着すべ
く、回転、上下振動をしつつ全体を１００〜４００℃の
温度に加熱した。This solution was poured into the metal pipe (2) shown in FIG. 1 which is a hollow support, for example, copper or a compound of copper (for example, NiCu compound) with the other closed. The whole of this pipe was heated to a temperature of 100 to 400 ° C. while rotating and vertically vibrating so that the ceramic particles adhered to the inner wall with a uniform thickness.
【００１８】かくしてこの中空パイプの内部の溶媒を除
去することができ、その内壁にセラミック粒をコーティ
ング（３）した。Thus, the solvent inside the hollow pipe could be removed, and the inner wall of the hollow pipe was coated with ceramic particles (3).
【００１９】この時内壁とより密着させやすくするた
め、エポキシ系、アクリル系の樹脂をとかした溶媒、例
えばトルエン等を用いてもよい。At this time, in order to make the inner wall more adherent, it is possible to use a solvent such as toluene in which an epoxy resin or an acrylic resin is dissolved.
【００２０】この後この内壁に付着し乾燥させたセラミ
ックスに対して、その中空部に酸素または酸素とアルゴ
ンの混合気体を導入して、酸化させつつ５００〜１１０
０℃、例えば６００℃３時間さらに８００℃５時間の加
熱焼成を行った。After that, oxygen or a mixed gas of oxygen and argon is introduced into the hollow portion of the ceramic which is adhered to the inner wall and dried, and is oxidized to 500 to 110.
Heating and baking was performed at 0 ° C., for example, 600 ° C. for 3 hours and 800 ° C. for 5 hours.
【００２１】かかる工程をさらに１〜５回繰り返すこと
により、このセラミック材を５０μｍ〜１cm（代表的に
は０．５〜５ｍｍ）の平均厚さにパイプ内に付着させる
ことが可能となった。かくして図１に示す如き中空支持
体（２）の内側に超電導セラミックス（３）を中空
（４）を有して本発明の超電導セラミックスを用いたパ
イプ（１）を作ることができた。By repeating the above steps 1 to 5 times, it becomes possible to deposit the ceramic material in the pipe with an average thickness of 50 μm to 1 cm (typically 0.5 to 5 mm). Thus, as shown in FIG. 1, a pipe (1) using the superconducting ceramics of the present invention could be made by having a hollow (4) of the superconducting ceramics (3) inside the hollow support (2).
【００２２】この実施例において、パイプは円環型中空
支持体を用いた。しかしその形状は角型中空支持体を用
いてもよい。また他の形とすることも可能である。In this example, the pipe used was an annular hollow support. However, a rectangular hollow support may be used for the shape. Other shapes are also possible.
【００２３】かかる超電導セラミックパイプにおいて、
Ｔｃはタブレット等で作られた時のＴｃよりは５〜２０
Ｋ低い値となってしまった。しかしこれは初期のタブレ
ットでのＴｃを向上させるとともにより改良が可能であ
る。In such a superconducting ceramic pipe,
Tc is 5-20 than Tc when made with tablets etc.
K is low. However, this improves the Tc of early tablets and can be further improved.
【００２４】本発明はかかるセラミックスを用いてエン
ドレスコイル構造の電力蓄積装置を作った。According to the present invention, an electric power storage device having an endless coil structure is made by using such ceramics.
【００２５】図２にその縦断面図を示す。このエンドレ
スコイルは太陽電池等で発電した電気エネルギのバッテ
リとして用いることができる。FIG. 2 shows a vertical sectional view thereof. This endless coil can be used as a battery of electric energy generated by a solar cell or the like.
【００２６】図面より明らかなごとく、予め中空を実施
例１と同様に有するパイプをコイル（７）形状に作る。
さらにこの始点（５），終点（６）も同様に中空パイプ
（４）で連結する。このエンドレスコイルは注入口
（８）を有する。この注入口は電気エネルギの入力およ
び出力端子として用いることができる。As is clear from the drawings, a pipe having a hollow in advance is formed in the coil (7) shape as in the first embodiment.
Further, the start point (5) and the end point (6) are similarly connected by the hollow pipe (4). This endless coil has an inlet (8). This inlet can be used as an input and output terminal for electrical energy.
【００２７】ここに実施例１と同様の方法で超電導セラ
ミックスを混合またはとかした溶液を注ぎ込む。A solution in which the superconducting ceramics are mixed or melted is poured in the same manner as in Example 1.
【００２８】これを乾燥し、不要溶媒を気体として
（８），（８’）より放出し、パイプの内部を乾燥させ
る。さらに実施例１と同様に酸化物気体を導入し、セラ
ミックスを乾燥させる。This is dried, and the unnecessary solvent is released as gas from (8) and (8 ') to dry the inside of the pipe. Further, an oxide gas is introduced in the same manner as in Example 1 to dry the ceramics.
【００２９】かくして内部が中空、かつその内壁に超電
導セラミックスがコーティングされたパイプ（１）を用
いたエンドレスコイル（７）を作ることができた。この
Ｔｃｏは実験では４５Ｋであった。しかし超電導材料の
選択によりＴｃｏを向上させ得る。また、この中空部に
液体水素を導入することにより、このエンドレスコイル
をして抵抗零の閉回路を作る例とし得たため、電気エネ
ルギ蓄積装置として用いることができた。この実施例に
おいて、電気エネルギの入力、出力部には失電力用ダイ
オードを設け、充電、放電させた時に無限大の電流が流
れないようにした。Thus, an endless coil (7) using a pipe (1) having a hollow interior and an inner wall coated with superconducting ceramics could be manufactured. This Tco was 45K in the experiment. However, Tco can be improved by selecting a superconducting material. Further, by introducing liquid hydrogen into the hollow portion, the endless coil can be used as an example of forming a closed circuit with zero resistance, so that it can be used as an electric energy storage device. In this embodiment, diodes for power loss are provided at the input and output parts of electric energy so that infinite current does not flow when charged and discharged.
【００３０】〔実施例２〕この実施例は（Ａ1-X Ｂｘ）
ｙＣｕＯｚ・（Ａ1-X ' Ｂ’ｘ’）ｙ’Ｃｕｚ’におい
て、ＡとしてＹｂ、Ｂ，Ｂ’としてＢａおよびＳｒを用
いた。ｘ，ｘ’として０．０７５，ｙ，ｙ’として２．
０を調整した。するとパイプ形状とした後もＴｃｏを７
４Ｋに保つことができた。その他は実施例１と同様であ
る。Example 2 This example is (A 1-X Bx)
In yCuOz · (A 1- X'B'x ') y'Cuz', Yb was used as A, and Ba and Sr were used as B and B '. x, x'is 0.075, y, y'is 2.
0 was adjusted. Then, even after making it into a pipe shape, Tco is 7
I was able to keep it at 4K. Others are the same as in the first embodiment.
【００３１】〔実施例３〕この実施例は実施例１と同じ
成分を用い、仮焼成をした。材料を粉砕し、微粉末とし
た後、型に入れ、ドーナツ型または指輪型のリッグ構造
として再プレスし、本焼成を行った。Example 3 In this example, the same components as in Example 1 were used and pre-baking was performed. The material was pulverized into a fine powder, put into a mold, re-pressed into a donut-shaped or ring-shaped rig structure, and fired.
【００３２】ここに外部より磁場を用いてエネルギを加
えた。 するとこのリング内を電流が無限時間流れ、電
力蓄積をさせ得る磁場を発生する。このエネルギの取り
出しは、このリングの磁場を切るようにして取り出すこ
とができる。Energy was applied from the outside by using a magnetic field. Then, an electric current flows in this ring for an infinite time, generating a magnetic field capable of accumulating electric power. This energy can be extracted by cutting off the magnetic field of this ring.
【００３３】[0033]
【発明の効果】本実施例はかかるパイプ形状とした後、
これらをその内部の中空部に冷却材である液体、例えば
液体窒素または液体水素を封入し、連続的にこのパイプ
を内部より最も温度が重要なセラミックスを直接冷やす
手段と同時になり得る。According to the present embodiment, after the pipe shape is formed,
These can serve as a means for directly enclosing a liquid, which is a coolant, such as liquid nitrogen or liquid hydrogen, in the hollow portion of the inside thereof and continuously cooling the ceramics whose temperature is the most important than the inside of the pipe continuously.
【００３４】また、この外側の金属を銅または銅の化合
物とすることにより、外部との溶接も可能であり、電気
装置の一部として用いることが可能である。この金属ま
たは金属化合物として銅または銅化合物とすることによ
り、特にその部品としての用途をひろげることができ
る。Further, by using copper or a compound of copper as the metal on the outside, welding with the outside is possible and it can be used as a part of an electric device. By using copper or a copper compound as the metal or the metal compound, the use as a component thereof can be particularly widened.
【図１】本発明の超電導セラミックパイプ。FIG. 1 is a superconducting ceramic pipe of the present invention.
【図２】本発明のパイプを用いた電気蓄積装置のー例。FIG. 2 is an example of an electric storage device using the pipe of the present invention.
─────────────────────────────────────────────────────
─────────────────────────────────────────────────── ───
【手続補正書】[Procedure amendment]
【提出日】平成５年１月１９日[Submission date] January 19, 1993
【手続補正１】[Procedure Amendment 1]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】全文[Name of item to be corrected] Full text
【補正方法】変更[Correction method] Change
【補正内容】[Correction content]
【書類名】明細書[Document name] Statement
【発明の名称】 超電導装置 Title : Superconducting device
【特許請求の範囲】[Claims]
【発明の詳細な説明】Detailed Description of the Invention
【０００１】[0001]
【発明の利用分野】本発明はセラミック系超電導材料を
利用した超伝導装置に関する。The present invention relates to a ceramic superconducting material.
The superconducting device used .
【０００２】[0002]
【従来の技術】従来、超電導材料はＮｂ−Ｇｅ（例えば
Ｎｂ３Ｇｅ）等の金属材料が用いられている。この材料
は金属であるため、延性、展性または曲げ性を高く有
し、超電導マグネット用コイル、また電力蓄積用コイル
として用いることが可能である。2. Description of the Related Art Conventionally, a metal material such as Nb-Ge (for example, Nb 3 Ge) has been used as a superconducting material. Since this material is a metal, it has high ductility, malleability or bendability, and can be used as a coil for a superconducting magnet or a coil for power storage.
【０００３】しかし、この金属の超電導材料はＴｃ（超
電導臨界温度を以下Ｔｃという）オンセットが小さく、
２３Ｋまたはそれ以下でしかなかった。しかしその工業
的応用を考えるならば、このＴｃが１００Ｋまたはそれ
以上を有し、Ｔｃｏ（電気抵抗が零となる温度）が液体
窒素温度である７７Ｋまたはそれ以上であることがきわ
めて重要である。However, this metallic superconducting material has a small Tc (superconducting critical temperature hereafter referred to as Tc) onset,
It was only 23K or less. However, considering its industrial application, it is extremely important that this Tc has a value of 100K or higher and that Tco (the temperature at which the electric resistance becomes zero) is 77K or higher, which is the liquid nitrogen temperature.
【０００４】最近、かかる超電導材料として、銅の酸化
物セラミック材料が注目されている。しかしこの銅の酸
化物セラミックスは延性、展性および曲げ性に乏しい。
加えて成型した後の加工がきわめて困難であるという他
の欠点を有する。Recently, copper oxide ceramic materials have attracted attention as such superconducting materials. However, this copper oxide ceramic is poor in ductility, malleability and bendability.
In addition, it has another drawback that it is extremely difficult to process after molding.
【０００５】[0005]
【従来の問題点】このため、銅の酸化物セラミックスよ
りなる超電導セラミックスを用いて、任意の形状の超電
導装置を作成することは、従来は困難であった。加え
て、超電導セラミックスを機械的に金属で補強する手段
も構造もまったく知られていない。[Problems with the prior art] For this reason, copper oxide ceramics
Of superconducting ceramics
Creating a guiding device has heretofore been difficult. In addition
To mechanically reinforce superconducting ceramics with metal
Neither the structure nor the structure is known at all.
【０００６】[0006]
【問題を解決すべき手段】本発明は超電導セラミックス
を任意の形状に設けた超電導装置であって、前記超電導
装置は金属の支持体の外側または内側に銅の酸化物セラ
ミックスよりなる超電導セラミックスがコーティングさ
れて設けられたことを特徴とする超電導装置である。さ
らに本発明においては、このセラミックスに金属または
金属化合物の支持体を添わしめ、機械的補強に加えて、
このセラミックスが非超電導状態となった時も電流を流
し得る手段としている。The present invention provides a superconducting device in which superconducting ceramics are provided in an arbitrary shape.
The device consists of a copper oxide ceramic on the outside or inside of a metal support.
Mixed superconducting ceramics coated
It is a superconducting device characterized by being provided separately. It
Furthermore, in the present invention, a support of a metal or a metal compound is added to this ceramic, in addition to mechanical reinforcement,
This ceramic is used as a means for allowing a current to flow even when it is in a non-superconducting state.
【０００７】もし、前記支持体が中空パイプ形状を有し
ていた場合、超電導セラミックス材料の粉末を有機溶媒
と混合した原料等を前記パイプ内部に注ぎ込み、内部に
均一に超電導セラミックス材料からなる膜を均一に形成
する。次にこの中空パイプ全体を加熱し、液体成分であ
る溶媒全体を気化して除去する。するとこの超電導セラ
ミック材料は中空パイプの内壁にコーティングされる。
これを加熱し、焼成させるとともに、酸化または還元を
繰り返し行うことにより、超電導性を有するセラミック
材料、例えば銅の酸化物セラミックスである（Ａ１−ｘ
Ｂｘ）ｙＣｕＯｚ ｘ＝０．０１〜０．３，ｙ＝１．３
〜２．２，ｚ＝２．０〜４．５で示される分子構造を有
し、ＡがＹ（イットリューム），Ｇａ（ガリューム），
Ｚｒ（ジルコニューム），Ｎｂ（ニオブ），Ｇｅ（ゲル
マニューム），Ｙｂ（イッテルビューム）またはその他
のランタノイドより１つまたは複数種選ばれ、ＢはＲａ
（ラジューム），Ｂａ（バリューム）またはＳｒ（スト
ロンチューム），Ｃａ（カルシューム），Ｍｇ（マグネ
シューム），Ｂｅ（ベリリューム）より１つまたは複数
種選ばれ、セラミックスを形成する。 If the support has a hollow pipe shape
If it is, the powder of superconducting ceramic material is
Pour the raw materials mixed with the above into the pipe,
Uniformly forming a film made of superconducting ceramic material
To do . Next, the entire hollow pipe is heated to vaporize and remove the entire solvent that is a liquid component. Then, the superconducting ceramic material is coated on the inner wall of the hollow pipe.
A ceramic material having superconductivity, for example, an oxide ceramic of copper (A 1-x) is obtained by heating and firing this and repeating oxidation or reduction.
Bx) yCuOz x = 0.01 to 0.3, y = 1.3
, 2.2, z = 2.0 to 4.5, A is Y (yttrium), Ga (gallum),
One or more species selected from Zr (zirconium), Nb (niobium), Ge (germanium), Yb (ytterbume) or other lanthanoid, and B is Ra
One or more kinds are selected from (radium), Ba (value) or Sr (strontium), Ca (calcium), Mg (magnesium), and Be (berium) to form ceramics.
【０００８】本発明で用いられるセラミックスは上記以
外の元素をＡ，Ｂまたは添加不純物として加えることが
可能である。The ceramics used in the present invention may contain elements other than those mentioned above as A, B or added impurities.
【０００９】本発明において、中空金属支持体の内壁に
第１の層として超電導セラミック材料がコーティングさ
れるが、さらにその上側にこの第１の層のセラミック材
料を十分固化した後、第２層のセラミック材料をコーテ
ィングすべく、同一工程を繰り返しすることは有効であ
る。またその場合、それぞれのコーティング層でＡまた
はＢの種類、Ｘ，Ｙ，Ｚの値の一部を変更してもよい。In the present invention, the inner wall of the hollow metal support is coated with the superconducting ceramic material as the first layer, and the ceramic material of the first layer is sufficiently solidified on the upper side of the superconducting ceramic material. It is useful to repeat the same process to coat the ceramic material. In that case, the type of A or B and a part of the values of X, Y, and Z may be changed in each coating layer.
【００１０】本発明において、さらにこれを繰り返して
多層構造としてもよいことはいうまでもない。Needless to say, in the present invention, this may be repeated to form a multilayer structure.
【００１１】[0011]
【作用】本発明によって、延性、展性および曲げ性に乏
しく、加えて成型した後の加工がきわめて困難であると
いう欠点を有する超電導セラミックス材料を用いて、任
意の形状を有する超電導装置を作成することが可能にな
った。本装置は形状が任意なだけではなく、金属支持体
を有するため、超電導性が破壊された際にも電流のパス
が確保されており、信頼性の非常に高いものである。 [Function] According to the present invention, ductility, malleability and bendability are poor.
In addition, it is extremely difficult to process after molding
Using a superconducting ceramic material that has the drawback
It is now possible to create superconducting devices that have the desired shape.
It was. This device is not only of arbitrary shape, but also a metal support
Has a current path even when the superconductivity is destroyed.
Has been secured and is highly reliable.
【００１２】また本発明の装置の形状を線状とした場
合、抵抗ゼロの超電導線が作成可能であり、これは従来
以上の大電流を流すことが可能となるし、コイル状とし
て始点と終点を互いに電気的に抵抗が零であるセラミッ
クスで連結することにより、エンドレスコイルとし得
る。このコイルは電流損失のないコイル、即ち電気エネ
ルギの蓄積用装置として用いることが可能となる。以下
図面に従って本発明の実施例を示す。If the device of the present invention has a linear shape,
In this case, it is possible to create a superconducting wire with zero resistance.
It becomes possible to pass the above large current, and a coil is used.
By connecting the starting point and the ending point with ceramics having an electrical resistance of zero, an endless coil can be obtained. This coil can be used as a coil without current loss, that is, as a device for storing electric energy. Embodiments of the present invention will be described below with reference to the drawings.
【００１３】[0013]
【実施例】 〔実施例１〕この実施例では（Ａ１−ｘＢｘ）ｙＣｕＯ
ｚにおいてＡとしてＹをＹ２Ｏ３，ＢとしてＢａをＢａ
ＣＯ３またＣｕとしてＣｕＯを用いた。それぞれ高純度
化学社製の９９．９５％以上のものを用いた。これらを
ｘ＝０．０５，ｘ＝０．０７５及びｘ＝０．１，ｙ＝
１．８，ｙ＝２．０，ｙ＝２．２とした。これらを混合
して９種類の混合物を作った。これらを一度３Ｋｇ／ｃ
ｍ２の圧力で加圧しタブレットとし７００℃、３時間さ
らに１０００℃、１０時間で大気中で仮焼成した。さら
にこれらを再び粉砕した。そしてその平均粒径が１００
μｍ以下、例えば１０μｍ程度となるようにした。この
混合物をカプセル内に封入し、再びこれを５Ｋｇ／ｃｍ
２の圧力でプレスし、タブレット状とした。そしてこれ
を１０００℃、１０時間酸化性雰囲気例えば大気中で本
焼成した。するとこの構造はペロブスカイト構造もみら
れるが、変形Ｋ２ＮｉＦ４型がＸ線解析像から観察され
た。EXAMPLES Example 1 In this example, (A 1-x Bx) yCuO is used.
In z, Y is Y 2 O 3 as A , and B is Ba as Ba.
Cu 3 was used as CO 3 and Cu. 99.95% or more manufactured by Kojundo Chemical Co., Ltd. was used. These are x = 0.05, x = 0.075 and x = 0.1, y =
It was set to 1.8, y = 2.0, and y = 2.2. These were mixed to make 9 kinds of mixtures. Once these 3Kg / c
The mixture was pressed at a pressure of m 2 to form a tablet, which was calcinated at 700 ° C. for 3 hours and further at 1000 ° C. for 10 hours in the atmosphere. Further, they were ground again. And the average particle size is 100
It is set to be not more than μm, for example, about 10 μm. Encapsulate this mixture in a capsule and re-add it to 5 Kg / cm
It was pressed at a pressure of 2 to form a tablet. Then, this was fired at 1000 ° C. for 10 hours in an oxidizing atmosphere such as air. Then, although this structure had a perovskite structure, the modified K 2 NiF 4 type was observed from the X-ray analysis image.
【００１４】次にこの本焼成したＴｃオンセットが４０
Ｋ以上好ましくは９０Ｋ，Ｔｃｏが好ましくは７７Ｋ以
上あることを電圧−電流−温度特性より確認する。Next, this main-baked Tc onset is 40
It is confirmed from the voltage-current-temperature characteristics that K or more is preferably 90K and Tco is preferably 77K or more.
【００１５】再びこのタブレットを微粉末とした。そし
てこの平均粒径が１００μｍ以下〜５μｍ例えば３０μ
ｍになるようにした。この工程において、この粉砕の
際、その結晶構造が基本的に破壊しないように努めた。This tablet was again made into a fine powder. The average particle size is 100 μm or less to 5 μm, for example, 30 μm.
It was set to m. In this process, an effort was made so that the crystal structure was not basically destroyed during the pulverization.
【００１６】この粉末を液体、例えばフロン液またはア
ルコール例えばエタノールその他の液体中に混合、また
は溶かした。This powder was mixed or dissolved in a liquid such as Freon liquid or an alcohol such as ethanol or other liquid.
【００１７】この溶液を中空の支持体である図１に示し
た金属パイプ（２）、例えば銅または銅の化合物（例え
ばＮｉＣｕ化合物）の内部に他方を塞いで注いだ。この
パイプをセラミック粒子が内壁に均一な厚さに付着すべ
く、回転、上下振動をしつつ全体を１００〜４００℃の
温度に加熱した。This solution was poured into the metal pipe (2) shown in FIG. 1 which is a hollow support, for example, copper or a compound of copper (for example, NiCu compound) with the other closed. The whole of this pipe was heated to a temperature of 100 to 400 ° C. while rotating and vertically vibrating so that the ceramic particles adhered to the inner wall with a uniform thickness.
【００１８】かくしてこの中空パイプの内部の溶媒を除
去することができ、その内壁にセラミック粒をコーティ
ング（３）した。Thus, the solvent inside the hollow pipe could be removed, and the inner wall of the hollow pipe was coated with ceramic particles (3).
【００１９】この時内壁とより密着させやすくするた
め、エポキシ系、アクリル系の樹脂をとかした溶媒、例
えばトルエン等を用いてもよい。At this time, in order to make the inner wall more adherent, it is possible to use a solvent such as toluene in which an epoxy resin or an acrylic resin is dissolved.
【００２０】この後この内壁に付着し乾燥させたセラミ
ックスに対して、その中空部に酸素または酸素とアルゴ
ンの混合気体を導入して、酸化させつつ５００〜１１０
０℃、例えば６００℃３時間さらに８００℃５時間の加
熱焼成を行った。After that, oxygen or a mixed gas of oxygen and argon is introduced into the hollow portion of the ceramic which is adhered to the inner wall and dried, and is oxidized to 500 to 110.
Heating and baking was performed at 0 ° C., for example, 600 ° C. for 3 hours and 800 ° C. for 5 hours.
【００２１】かかる工程をさらに１〜５回繰り返すこと
により、このセラミック材を５０μｍ〜１ｃｍ（代表的
には０．５〜５ｍｍ）の平均厚さにパイプ内に付着させ
ることが可能となった。かくして図１に示す如き中空支
持体（２）の内側に超電導セラミックス（３）を中空
（４）を有して本発明の超電導セラミックスを用いたパ
イプ（１）を作ることができた。By repeating the above steps 1 to 5 times, it becomes possible to deposit the ceramic material in the pipe with an average thickness of 50 μm to 1 cm (typically 0.5 to 5 mm). Thus, as shown in FIG. 1, a pipe (1) using the superconducting ceramics of the present invention could be made by having a hollow (4) of the superconducting ceramics (3) inside the hollow support (2).
【００２２】この実施例において、パイプは円環型中空
支持体を用いた。しかしその形状は角型中空支持体を用
いてもよい。また他の形とすることも可能である。In this example, the pipe used was an annular hollow support. However, a rectangular hollow support may be used for the shape. Other shapes are also possible.
【００２３】かかる超電導セラミックパイプにおいて、
Ｔｃはタブレット等で作られた時のＴｃよりは５〜２０
Ｋ低い値となってしまった。しかしこれは初期のタブレ
ットでのＴｃを向上させるとともにより改良が可能であ
る。In such a superconducting ceramic pipe,
Tc is 5-20 than Tc when made with tablets etc.
K is low. However, this improves the Tc of early tablets and can be further improved.
【００２４】本発明はかかるセラミックスを用いてエン
ドレスコイル構造の電力蓄積装置を作った。According to the present invention, an electric power storage device having an endless coil structure is made by using such ceramics.
【００２５】図２にその縦断面図を示す。このエンドレ
スコイルは太陽電池等で発電した電気エネルギのバッテ
リとして用いることができる。FIG. 2 shows a vertical sectional view thereof. This endless coil can be used as a battery of electric energy generated by a solar cell or the like.
【００２６】図面より明らかなごとく、予め中空を実施
例１と同様に有するパイプをコイル（７）形状に作る。
さらにこの始点（５），終点（６）も同様に中空パイプ
（４）で連結する。このエンドレスコイルは注入口
（８）を有する。この注入口は電気エネルギの入力およ
び出力端子として用いることができる。As is clear from the drawings, a pipe having a hollow in advance is formed in the coil (7) shape as in the first embodiment.
Further, the start point (5) and the end point (6) are similarly connected by the hollow pipe (4). This endless coil has an inlet (8). This inlet can be used as an input and output terminal for electrical energy.
【００２７】ここに実施例１と同様の方法で超電導セラ
ミックスを混合またはとかした溶液を注ぎ込む。A solution in which the superconducting ceramics are mixed or melted is poured in the same manner as in Example 1.
【００２８】これを乾燥し、不要溶媒を気体として
（８），（８’）より放出し、パイプの内部を乾燥させ
る。さらに実施例１と同様に酸化物気体を導入し、セラ
ミックスを乾燥させる。This is dried, and the unnecessary solvent is released as gas from (8) and (8 ') to dry the inside of the pipe. Further, an oxide gas is introduced in the same manner as in Example 1 to dry the ceramics.
【００２９】かくして内部が中空、かつその内壁に超電
導セラミックスがコーティングされたパイプ（１）を用
いたエンドレスコイル（７）を作ることができた。この
Ｔｃｏは実験では４５Ｋであった。しかし超電導材料の
選択によりＴｃｏを向上させ得る。また、この中空部に
液体水素を導入することにより、このエンドレスコイル
をして抵抗零の閉回路を作る例とし得たため、電気エネ
ルギ蓄積装置として用いることができた。この実施例に
おいて、電気エネルギの入力、出力部には失電力用ダイ
オードを設け、充電、放電させた時に無限大の電流が流
れないようにした。Thus, an endless coil (7) using a pipe (1) having a hollow interior and an inner wall coated with superconducting ceramics could be manufactured. This Tco was 45K in the experiment. However, Tco can be improved by selecting a superconducting material. Further, by introducing liquid hydrogen into the hollow portion, the endless coil can be used as an example of forming a closed circuit with zero resistance, so that it can be used as an electric energy storage device. In this embodiment, diodes for power loss are provided at the input and output parts of electric energy so that infinite current does not flow when charged and discharged.
【００３０】〔実施例２〕この実施例は（Ａ１−ｘＢ
ｘ）ｙＣｕＯｚ・（Ａ１−ｘ’Ｂ’ｘ’）ｙ’Ｃｕｚ’
において、ＡとしてＹｂ、Ｂ，Ｂ’としてＢａおよびＳ
ｒを用いた。ｘ，ｘ’として０．０７５，ｙ，ｙ’とし
て２．０を調整した。するとパイプ形状とした後もＴｃ
ｏを７４Ｋに保つことができた。その他は実施例１と同
様である。[Embodiment 2] In this embodiment, (A 1-x B)
x) yCuOz ・ (A 1- x'B'x ') y'Cuz'
, Yb as A, B and B ′ as Ba and S
r was used. 0.075 was adjusted as x, x ', and 2.0 was adjusted as y, y'. Then, even after making it into a pipe shape, Tc
I was able to keep o at 74K. Others are the same as in the first embodiment.
【００３１】〔実施例３〕この実施例は実施例１と同じ
成分を用い、仮焼成をした。材料を粉砕し、微粉末とし
た後、型に入れ、ドーナツ型または指輪型のリッグ構造
として再プレスし、本焼成を行った。Example 3 In this example, the same components as in Example 1 were used and pre-baking was performed. The material was pulverized into a fine powder, put into a mold, re-pressed into a donut-shaped or ring-shaped rig structure, and fired.
【００３２】ここに外部より磁場を用いてエネルギを加
えた。するとこのリング内を電流が無限時間流れ、電力
蓄積をさせ得る磁場を発生する。このエネルギの取り出
しは、このリングの磁場を切るようにして取り出すこと
ができる。Energy was applied from the outside by using a magnetic field. Then, an electric current flows in this ring for an infinite time, generating a magnetic field capable of accumulating electric power. This energy can be extracted by cutting off the magnetic field of this ring.
【００３３】[0033]
【発明の効果】本発明により延性、展性および曲げ性に
乏しく、加えて成型した後の加工がきわめて困難である
という欠点を有する超電導セラミックス材料を用いて、
任意の形状を有する超電導装置を作成することが可能に
なった。本装置は形状が任意なだけではなく、金属支持
体を有するため、超電導性が破壊された際にも電流のパ
スが確保されており、信頼性の非常に高いものである。 According to the present invention, ductility, malleability and bendability are improved.
Poor and extremely difficult to process after molding
Using a superconducting ceramic material that has the drawback
It is possible to create superconducting devices with arbitrary shapes
became. This device is not only of arbitrary shape, but also metal support
Since it has a body, it can carry out current flow even when the superconductivity is destroyed.
The security is high and the reliability is very high.
【００３４】また、その構成も金属支持体の内側または
外側に超電導セラミックスからなる材料が膜状に１層以
上望ましくは複数層重ねて設けられたものあり、比較的
簡便な構成で達成しているものである。 The structure is also the inside of the metal support or
At least one layer of superconducting ceramic material is formed on the outside in the form of a film.
Above all, it is desirable to have multiple layers,
This is achieved with a simple structure.
【００３５】本発明によって、超電導セラミックス材料
を用いて、従来の金属超電導材料と同程度に自由な形状
に設けることが可能となった。 According to the present invention, a superconducting ceramic material
Free shape as high as conventional metal superconducting materials
It has become possible to install in.
【図面の簡単な説明】[Brief description of drawings]
【図１】本発明の超電導セラミックパイプ。FIG. 1 is a superconducting ceramic pipe of the present invention.
【図２】本発明のパイプを用いた電気蓄積装置の一例。FIG. 2 is an example of an electric storage device using the pipe of the present invention.
Claims (3)
状またはコイル状に設け、かつ始点と終点とを互いに連
結して設けられたことを特徴とする超電導セラミック材
料を用いた電力蓄積装置。1. A power storage device using a superconducting ceramic material, characterized in that superconducting ceramics of copper oxide is provided in a ring shape or a coil shape, and a start point and an end point are connected to each other.
外側または内側に金属の支持体を設けたことを特徴とす
る超電導セラミック材料を用いた電力蓄積装置。2. A power storage device using a superconducting ceramic material according to claim 1, wherein a metal support is provided outside or inside the superconducting ceramic.
（Ａ1-x ＢX ）ｙＣｕＯｚ ｘ＝０．０１〜０．３，ｙ
＝１．３〜２．２，ｚ＝２．０〜４．５で示される分子
構造を有し、ＡはＹ（イットリュ−ム），Ｇａ（ガリュ
ーム），Ｚｒ（ジルコニューム），Ｎｂ（ニオブ），Ｇ
ｅ（ゲルマニューム），Ｙｂ（イッテルビューム）また
はその他ランタノイドより１つまたは複数の元素が選ば
れ、ＢはＲａ（ラジューム），Ｂａ（バリューム）また
はＳｒ（ストロンチューム），Ｃａ（カルシューム），
Ｍａ（マグネシューム）またはＢｅ（ベリリューム）よ
り１つまたは複数の元素が選ばれた超電導性セラミック
材料であることを特徴とする超電導セラミック材料を用
いたパイプ。3. The oxide ceramics according to claim 1, wherein (A 1-x B x ) yCuOz x = 0.01 to 0.3, y.
= 1.3-2.2, z = 2.0-4.5, A is Y (yttrium), Ga (gallum), Zr (zirconium), Nb (niobium). , G
One or more elements are selected from e (germanium), Yb (ytterbium) or other lanthanoids, and B is Ra (radium), Ba (valuem) or Sr (strontium), Ca (calcium),
A pipe using a superconducting ceramic material, which is a superconducting ceramic material in which one or more elements are selected from Ma (magnesium) or Be (beryllium).