JPH05194134A - 歯科用陶材 - Google Patents
歯科用陶材Info
- Publication number
- JPH05194134A JPH05194134A JP4313111A JP31311192A JPH05194134A JP H05194134 A JPH05194134 A JP H05194134A JP 4313111 A JP4313111 A JP 4313111A JP 31311192 A JP31311192 A JP 31311192A JP H05194134 A JPH05194134 A JP H05194134A
- Authority
- JP
- Japan
- Prior art keywords
- weight
- porcelain
- dental
- bao
- ceramic material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
11重量%、K2O 8〜12重量%、Na2O 10.5〜12重量%、
CaO 0.7〜2重量%、BaO 0.6〜2重量%、B2O30.5〜2.5
重量%、Sb2O3 0.1〜0.6重量%、CeO2 0〜0.5重量
%、TiO2 1.2〜3.8重量%、Li2O 0.8〜1.4重量%及び
F2 1.2〜3.8重量%を有する。
Description
温度及び20〜500℃での熱膨張率α13〜14・1
0-6・K-1を有する金属陶製及び完全陶製義歯を製造及
び修理するための歯科用陶材に関する。
造、金属陶製及び完全陶製義歯の変形のための矯正、損
傷部分の修理又は金属製義歯への陶材層の前装が可能で
ある。
を得るために、エナメル化の方法により、陶材層を前装
として金属フレームワーク(冠、ブリッジ)上に施し
た。その際、陶器粉末を水性スラリとして金属フレーム
ワーク上に施与し、高温で焼く。その際、その陶器物質
の燃焼温度(加工温度)は、金属フレームワーク材料の
固相化温度より下で、少なくとも100℃であり、陶器
物質の20〜500℃の範囲での熱膨張率は、金属材料
のよりも僅かに少ないことが重要であり、従って、燃焼
及び冷却の際に、前装層中に亀裂は生じない。
陶材を用いて耐熱性陶材塑型物質上に、完全陶製義歯部
品、例えば全部冠、部分冠、インレー充填物及び前装介
殻を、焼結法で製造することができる。
ク材料のせいで、前装の際に、20〜500℃で、13
〜14・10-6・K-1である一般に高い熱膨張率を必要
とする。通例、これらの陶材は、950±30℃で加工
されるが、これは、幾つかの歯科用合金に関しては高す
ぎる。歯科用陶材の組成を変えることにより、その際、
熱膨張率及び耐蝕性をマイナスに変化させずに加工温度
を実質的に降下させることは、非常に困難である。その
際、生物学的に問題のある成分、例えば酸化鉛は、回避
されねばならない。
10-6・K-1は、一般に、歯科用陶材物質がアルカリ金
属酸化物25〜30重量%を含有する場合にのみ得られ
る。しかしながら、そのために、酸性環境では、例えば
歯垢のある口腔内では、これらの陶材の耐蝕性の限度が
得られる。
号明細書から、SiO2の他に残分として、Al2O3
5〜15%、B2O3 0.5〜2.5%、Sb2O3
0.5〜2.5%、CaO 0.1〜0.5%、BaO
0.5〜2.5%、Na2O5〜10%、K2O 10
〜15%、Li2O 0.1〜0.5%及びF2 0.1
〜0.5%を含有する、金属陶製及び完全陶製の義歯の
製造、矯正及び修理のための歯科用陶材が公知である。
これらは、20〜500℃での熱膨張率13.5(±
1)・10-6・K-1を有するが、その加工温度730±
30℃は、幾つかの歯科用合金にとって、前装の際にま
だ高すぎる。
1168.6号明細書中に、熱膨張率16〜17.5・
10-6・K-1及び加工温度770±70℃を有する、金
属製義歯の前装のための陶材が記載されている。これら
は、SiO2 60〜68%、Al2O3 10〜15
%、B2O3 0.7〜1.5%、Sb2O3 0〜0.5
%、CeO2 0〜0.5%、BaO 0〜0.5%、
CaO 0.1〜0.5%、K2O 9〜12%、Na2
O 9〜11%、Li2O 0.8〜1.4%及びF2
0.2〜0.4%からなる。
は、20〜500℃での熱膨張率13〜14・10-6・
K-1及び700℃より下の加工温度を有する金属陶製及
び完全陶製義歯を製造及び修理するための歯科用陶材を
発明することであった。更に、これは、生物学的に問題
のない成分を含有し、かつ口腔内で耐蝕性であるべきで
ある。
りSiO2 60〜65重量%、Al2O3 8.5〜1
1重量%、K2O 8〜12重量%、Na2O 10.5
〜12重量%、CaO0.7〜2重量%、BaO 0.
6〜2重量%、B2O3 0.5〜2.5重量%、Sb2
O3 0.1〜0.6重量%、CeO2 0〜0.5重量
%、TiO21.2〜3.8重量%、Li2O 0.8〜
1.4重量%及びF2 1.2〜3.8重量%からなる
材料により解決される。
%、Al2O3 8.5〜9.5重量%、K2O 10〜
11.5重量%、Na2O 10.5〜11.5重量
%、CaO 0.7〜1.5重量%、BaO 0.6〜
1.2重量%、B2O3 0.7〜1.5重量%、Sb2
O3 0.2〜0.4重量%、CeO2 0.1〜0.4
重量%、TiO2 1.5〜3重量%、Li2O 0.8
〜1.2重量%及びF21.2〜2.4重量%を含有す
るのが、有利である。
0±30℃を有する。その際、ガラス点は、約450℃
であり、軟化点は、約510℃である。これらは、非常
に高い物質均一性及び非常に高い透明度(70%より高
い光透過率)を有する。DIN13925による曲げ抵
抗は、110N・mm-2であり、従って最小必要値50
N・mm-2をはるかに超えている。
酢酸中16時間)の際の質量損失は、約0.028重量
%である。その際、曲げ抵抗は、意想外にも50%まで
上昇し、一方、公知の歯科用陶材では、30%まで減少
する。
記載する: ──────────────────────────────────── 材料 1 2 3 ──────────────────────────────────── SiO2 61.3% 60.9 62.3 Al2O3 9.0% 8.6 9.3 K2O 10.7% 11.2 10.2 Na2O 10.9% 10.7 12.0 CaO 1.0% 0.9 0.8 BaO 0.9% 0.7 0.8 B2O3 1.0% 1.8 0.5 Sb2O3 0.3% 0.2 0.1 CeO2 0.2% 0.3 0.1 TiO2 2.1% 1.2 1.3 Li2O 1.0% 0.8 1.4 F2 1.6% 2.7 1.2
Claims (2)
- 【請求項1】 700℃より下の加工温度及び20〜5
00℃での熱膨張率α13〜14・10-6・K-1を有す
る金属陶製及び完全陶製義歯を製造及び修理するための
歯科用陶材において、その組成が、SiO2 60〜6
5重量%、Al2O3 8.5〜11重量%、K2O 8
〜12重量%、Na2O 10.5〜12重量%、Ca
O 0.7〜2重量%、BaO 0.6〜2重量%、B
2O3 0.5〜2.5重量%、Sb2O3 0.1〜0.
6重量%、CeO2 0〜0.5重量%、TiO2 1.
2〜3.8重量%、Li2O 0.8〜1.4重量%及
びF2 1.2〜3.8重量%であることを特徴とす
る、歯科用陶材。 - 【請求項2】 SiO2 60〜63重量%、Al2O3
8.5〜9.5重量%、K2O 10〜11.5重量
%、Na2O 10.5〜11.5重量%、CaO
0.7〜1.5重量%、BaO 0.6〜1.2重量
%、B2O3 0.7〜1.5重量%、Sb2O3 0.2
〜0.4重量%、CeO2 0.1〜0.4重量%、T
iO2 1.5〜3重量%、Li2O 0.8〜1.2重
量%及びF21.2〜2.4重量%を含有する、請求項
1記載の歯科用陶材。