JPH05171512A - Production of highly strong polyamide monofilament having excellent transparency - Google Patents
Production of highly strong polyamide monofilament having excellent transparencyInfo
- Publication number
- JPH05171512A JPH05171512A JP34489491A JP34489491A JPH05171512A JP H05171512 A JPH05171512 A JP H05171512A JP 34489491 A JP34489491 A JP 34489491A JP 34489491 A JP34489491 A JP 34489491A JP H05171512 A JPH05171512 A JP H05171512A
- Authority
- JP
- Japan
- Prior art keywords
- liquid
- polyamide monofilament
- spinneret
- monofilament
- cooled
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、透明性に優れ、かつ高
い引張強度を有するポリアミドモノフィラメントの製造
方法に関するものであり、詳しくは主として釣糸や漁網
などの漁獲用途に適した透明性かつ高強度のポリアミド
モノフィラメントの製造方法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for producing a polyamide monofilament having excellent transparency and high tensile strength. More specifically, the invention relates to a transparent and high strength material suitable mainly for fishing applications such as fishing line and fishing net. The present invention relates to a method for producing a polyamide monofilament.
【０００２】[0002]
【従来の技術】従来、ポリアミドモノフィラメントを紡
糸するには、口金より吐出された溶融状態の糸条を、冷
却媒体すなわち冷水に通して急冷する方法が一般的に用
いられている。2. Description of the Related Art Conventionally, in order to spin a polyamide monofilament, a method in which a molten yarn discharged from a spinneret is rapidly cooled by passing it through a cooling medium, that is, cold water is generally used.
【０００３】しかしながら、前記の吐出ポリマーを冷水
で急冷する方法においては、得られるモノフィラメント
の強力は向上するものの、表層に球晶が生成するため、
モノフィラメントが不透明となり、釣糸などの漁獲用途
に使用するには好ましくないという不具合があった。However, in the method of quenching the discharged polymer with cold water, the strength of the obtained monofilament is improved, but since spherulites are formed in the surface layer,
The monofilament becomes opaque, which is not preferable for use in fishing applications such as fishing line.
【０００４】ところで、冷却液体として無極性または極
性の小さい液体を用いることにより、前記糸条の表層に
おける球晶の発生を防ぎ、透明性を向上させる方法が、
特公昭３３−１６３９号公報および特公昭３１−３５５
９号公報に記載されている。By the way, a method of preventing the generation of spherulites in the surface layer of the yarn and improving the transparency by using a non-polar or small-polarity liquid as the cooling liquid is known.
JP-B-33-1639 and JP-B-31-355
No. 9 publication.
【０００５】しかしながら、前記の特公昭３３−１６３
９号公報および特公昭３１−３５５５９号公報に記載さ
れる無極性または極性の小さい液体を用いて吐出ポリマ
ーを冷却する方法では、吐出ポリマー表層の球晶生成は
抑制されるものの、冷却液体の比熱が水に比べて小さい
ため、吐出ポリマーの冷却速度が遅くなり、得られるモ
ノフィラメントの内部に球晶が発生し、この球晶によっ
てモノフィラメントの透明性が阻害されるという問題が
あった。However, the above Japanese Patent Publication No. 33-163.
In the method described in JP-B No. 9 and JP-B No. 31-35559, in which the discharged polymer is cooled by using a non-polar or small-polarity liquid, spherocrystal formation in the surface layer of the discharged polymer is suppressed, but the specific heat of the cooling liquid is reduced. Since it is smaller than water, the cooling rate of the discharged polymer is slowed down, spherulites are generated inside the obtained monofilament, and the spherulite hinders the transparency of the monofilament.
【０００６】また、ポリアミドに脂肪族モノアミンを添
加することによって、吐出ポリマーを水で冷却において
も透明性を保持する方法が、特開昭４７−３３１３９号
公報に開示されている。Further, Japanese Patent Application Laid-Open No. 47-33139 discloses a method in which an aliphatic monoamine is added to polyamide to maintain transparency even when the discharged polymer is cooled with water.
【０００７】すなわち、前記特開昭４７−３３１３９号
公報で示されている方法は、ポリアミドモノフィラメン
トの透明性を改善するための結晶化抑制剤として、脂肪
族モノアミンを添加することを特徴としている。しか
し、この方法では得られるポリアミドモノフィラメント
の引張強度が低く、高強度化が達成できないという問題
があった。That is, the method disclosed in JP-A-47-33139 is characterized in that an aliphatic monoamine is added as a crystallization inhibitor for improving the transparency of the polyamide monofilament. However, this method has a problem in that the obtained polyamide monofilament has a low tensile strength and cannot achieve high strength.
【０００８】さらに、ポリアミドモノフィラメントを水
蒸気で処理することによって、モノフィラメントの表層
部を低配向化する方法が、特公昭４７−４３７６８号公
報、特開昭５２−１１０９０８号公報および特開昭５２
−１１０９１８号公報に開示されている。Further, a method of lowering the orientation of the surface layer portion of the monofilament by treating the polyamide monofilament with steam is disclosed in JP-B-47-43768, JP-A-52-110908 and JP-A-52.
No. 110918.
【０００９】これら特公昭４７−４３７６８号公報、特
開昭５２−１１０９０８号公報および特開昭５２−１１
０９１８号公報に示されている方法は、ポリアミドモノ
フィラメントに対する水蒸気処理の作用を有効に利用す
ることによって、ポリアミドモノフィラメントの結節強
度を向上させる方法として相当に優れた技術である。Japanese Patent Publication No. 47-43768, Japanese Patent Publication No. 52-110908 and Japanese Patent Publication No. 52-11.
The method disclosed in Japanese Patent No. 0918 is a considerably excellent technique as a method for improving the knot strength of a polyamide monofilament by effectively utilizing the action of steam treatment on the polyamide monofilament.
【００１０】すなわち、前記特公昭４７−４３７６８号
公報に記載の方法は、一旦延伸されたポリアミドモノフ
ィラメントを水蒸気中で処理することによって、モノフ
ィラメントの表層部の配向を低くしようとするものであ
り、また特開昭５２−１１０９１８号公報に記載の方法
は、水蒸気中で延伸を行うことにより、ポリアミドモノ
フィラメントの内層部の配向を高めると共に、表層部の
低配向化を図ろうとするものである。That is, the method described in Japanese Patent Publication No. 47-43768 is intended to lower the orientation of the surface layer portion of the monofilament by treating the once stretched polyamide monofilament in steam. The method described in Japanese Patent Application Laid-Open No. 52-110918 aims to increase the orientation of the inner layer portion of the polyamide monofilament and lower the orientation of the surface layer portion by stretching in steam.
【００１１】しかるに、これらの従来技術においては、
いずれもすでに配向および結晶化の進んだポリアミドモ
ノフィラメントを、水蒸気中で処理するものであり、内
層部高配向および表層部低配向の形成に限度があるた
め、内層部をより高い配向、表層部をより低い配向とす
ることは困難であった。However, in these conventional techniques,
In both cases, polyamide monofilaments that have already been oriented and crystallized are treated in water vapor, and there is a limit to the formation of high orientation of the inner layer portion and low orientation of the surface layer portion. It was difficult to obtain a lower orientation.
【００１２】したがって、これらの従来技術では、さら
に高い結節強度を有するポリアミドモノフィラメントを
製造することができず、その実施例によると、最高のも
ので引張強度が６．７８ｇ／ｄ程度、結節強度が５．４
９ｇ／ｄ程度の値にすぎない。Therefore, these conventional techniques cannot produce polyamide monofilaments having higher knot strength, and according to the examples, the highest tensile strength is about 6.78 g / d and the knot strength is high. 5.4
The value is only about 9 g / d.
【００１３】また、前記特開昭５２−１１０９１８号公
報記載のポリアミドモノフィラメントの場合には、結節
強度はすべて無視し、引張強度を高くしたものであるに
もかかわらず、その引張強度の最高値は、高々７．０〜
９．５ｇ／ｄにすぎない。Further, in the case of the polyamide monofilament described in the above-mentioned Japanese Patent Laid-Open No. 52-110918, although the knot strength is all ignored and the tensile strength is increased, the maximum value of the tensile strength is , At most 7.0
Only 9.5 g / d.
【００１４】[0014]
【発明が解決しようとする課題】本発明の目的は、上述
した従来技術で得られるポリアミドモノフィラメントに
比較して、高い引張強度および結節強度を有すると共
に、透明性がきわめて優れたポリアミドモノフィラメン
トを製造可能な方法を提供することにある。An object of the present invention is to produce a polyamide monofilament which has high tensile strength and knot strength and is extremely excellent in transparency as compared with the polyamide monofilament obtained by the above-mentioned prior art. To provide a simple method.
【００１５】[0015]
【課題を解決するための手段】上記の目的を達成するた
めに、本発明の透明性の優れたポリアミドモノフィラメ
ントの製造方法は、紡糸口金から吐出されたポリアミド
からなる吐出ポリマーを、紡糸口金の直下に設けられた
液体浴中で冷却した後引取り、引続き熱延伸する際、前
記液体浴における液体を二層となし、下層の液体として
水を、また上層の液体として前記水よりも比重が小さ
く、無極性または極性の小さい液体を用い、前記上層お
よび下層の液体の温度を２〜１０℃の範囲内となした二
段階で冷却を施すと共に、吐出ポリマーが上層の液体を
通過する距離Ｌ（cm）、紡糸口金の単孔当たりの吐出量
Ｑ（ｇ／分）および引取速度Ｖ（ｍ／分）が、式２×Ｖ
×Ｑ0.5 ≦Ｌ≦１０×Ｖ×Ｑ0.5 の関係を満たすことを
特徴とする。In order to achieve the above object, a method for producing a polyamide monofilament having excellent transparency according to the present invention is such that a discharge polymer composed of polyamide discharged from a spinneret is directly under the spinneret. When the liquid is cooled in a liquid bath provided in, and subsequently subjected to hot stretching, the liquid in the liquid bath is formed into two layers, water as a lower layer liquid and specific gravity smaller than that of the upper layer liquid. , A non-polar or low-polarity liquid is used, the upper layer liquid and the lower layer liquid are cooled in two stages in which the temperature is within the range of 2 to 10 ° C., and the distance L ( cm), the discharge amount Q (g / min) per single hole of the spinneret and the take-up speed V (m / min) are calculated by the formula 2 × V
It is characterized in that the relationship of × Q 0.5 ≦ L ≦ 10 × V × Q 0.5 is satisfied.
【００１６】また、本発明の透明性の優れた高強度ポリ
アミドモノフィラメントの製造方法は、吐出ポリマーを
冷却媒体中から引出した後、温度６０〜１５０℃、圧力
２０〜３００mmＨ2 Ｏの水蒸気で満たされた加熱処理装
置に導入し、０．０１〜１．０秒間加熱処理し、この加
熱処理装置から導き出し、引続いて４．５倍以上に熱延
伸することをさらなる特徴とする。Further, according to the method for producing a high-strength polyamide monofilament having excellent transparency of the present invention, the discharged polymer is drawn out from the cooling medium and then filled with water vapor at a temperature of 60 to 150 ° C. and a pressure of 20 to 300 mmH 2 O. It is further characterized in that it is introduced into the above heat treatment apparatus, subjected to heat treatment for 0.01 to 1.0 seconds, led out from this heat treatment apparatus, and subsequently subjected to hot stretching at a ratio of 4.5 or more.
【００１７】[0017]
【実施態様】本発明に係る方法は、ポリアミドすべてに
適用することができるが、特にナイロン６、ナイロン６
・６に好ましく適応され、またこれらを主体とした共重
合物あるいはブレンド物であっても適応することができ
る。BEST MODE FOR CARRYING OUT THE INVENTION The method according to the present invention can be applied to all polyamides, but especially nylon 6 and nylon 6
6 is preferably applied, and a copolymer or a blend containing these as the main components can also be applied.
【００１８】本発明の方法について具体的に説明する。The method of the present invention will be specifically described.
【００１９】まず、乾燥されたポリアミドチップを溶融
し、紡糸口金から液体浴に吐出する。First, the dried polyamide chips are melted and discharged from the spinneret into a liquid bath.
【００２０】液体浴は紡糸口金の直下に設けられてお
り、液体浴の中には上層および下層からなる二層の液体
が用いられている。The liquid bath is provided directly below the spinneret, and a two-layer liquid consisting of an upper layer and a lower layer is used in the liquid bath.
【００２１】前記の上層の液体は、水と相溶性がなく水
より比重の小さい無極性または極性の小さい液体であ
り、この液体は２〜１０℃、好ましくは４〜１０℃の温
度に調整されている。The liquid in the upper layer is a non-polar or small-polarity liquid that is incompatible with water and has a smaller specific gravity than water. The liquid is adjusted to a temperature of 2 to 10 ° C, preferably 4 to 10 ° C. ing.
【００２２】前記の上層の液体としては、ベンゾール、
トリオール、キシロール、テトラリン等の芳香族炭化水
素、ヘキサン、オクタン、シクロヘキサン、ケロシン、
エーテル、石油ベンジン、リグロイン、低粘度流動パラ
フィン等の脂肪族炭化水素およびその誘導体等が用いら
れる。更には上記物質を主体とした混合物を用いてもよ
い。As the upper layer liquid, benzene,
Aromatic hydrocarbons such as triol, xylol, tetralin, hexane, octane, cyclohexane, kerosene,
Aliphatic hydrocarbons such as ether, petroleum benzine, ligroin, low-viscosity liquid paraffin, and their derivatives are used. Further, a mixture mainly containing the above substances may be used.
【００２３】前記の下層の液体は水であり、この水は２
〜１０℃、好ましくは４〜１０℃の温度に調整されてい
る。The lower layer liquid is water, and this water is 2
The temperature is adjusted to -10 ° C, preferably 4 to 10 ° C.
【００２４】前記のように、紡糸口金の直下に設けた液
体浴として二層の液体を用いたことから、吐出直後のポ
リアミドポリマーは、上層の液体において無極性または
極性の小さい液体で表層が冷却され、この表層部分に球
晶が発生するのが抑制される。As described above, since the two-layer liquid is used as the liquid bath provided immediately below the spinneret, the polyamide polymer immediately after discharge is a non-polar or small-polar liquid in the upper liquid, and the surface layer is cooled. The generation of spherulites in this surface layer portion is suppressed.
【００２５】上記液体浴の上層を吐出ポリマーが通過す
る距離Ｌ（cm）、単孔当たりの吐出量Ｑ（ｇ／分）およ
び引取速度Ｖ（ｍ／分）の関係は、式２×Ｖ×Ｑ0.5 ≦
Ｌ≦１０×Ｖ×Ｑ0.5 とすることが好ましい。The relationship between the distance L (cm) that the discharged polymer passes through the upper layer of the liquid bath, the discharge amount Q (g / min) per single hole, and the take-up speed V (m / min) is expressed by the formula 2 × V × Q 0.5 ≤
It is preferable that L ≦ 10 × V × Q 0.5 .
【００２６】前記液体浴において、上層の液体を吐出ポ
リマーが通過する距離Ｌが上記の範囲より短いと、吐出
ポリマーは表層が十分冷却されない状態で下層の水に至
り冷却されるため、表層に球晶の層が形成され、得られ
るモノフィラメントの透明性が劣る場合がある。In the liquid bath, if the distance L through which the discharge polymer passes through the liquid in the upper layer is shorter than the above range, the discharge polymer is cooled down to the water in the lower layer in a state where the surface layer is not sufficiently cooled. In some cases, a crystal layer is formed and the transparency of the obtained monofilament is poor.
【００２７】一方、前記液体浴において、上層の液体を
通過する距離Ｌが上記範囲より長いと、比熱の小さい液
体で長時間冷却されることになるため、冷却が遅延し、
得られるモノフィラメントの内層に球晶が形成されるこ
とから、この場合にも透明性が劣る場合がある。On the other hand, in the liquid bath, if the distance L through which the upper layer liquid passes is longer than the above range, the liquid having a low specific heat is cooled for a long time, so that the cooling is delayed,
Since spherulites are formed in the inner layer of the obtained monofilament, the transparency may be poor in this case as well.
【００２８】すなわち、前記の液体浴の上層を吐出ポリ
マーが通過する距離Ｌ（cm）と単孔当たりの吐出量Ｑ
（ｇ／分）と引取速度Ｖ（ｍ／分）との関係を、式２×
Ｖ×Ｑ0.5 ≦Ｌ≦１０×Ｖ×Ｑ0.5 とすることによっ
て、確実に透明性の優れた高強度ポリアミドモノフィラ
メントを得ることができる。That is, the distance L (cm) that the discharge polymer passes through the upper layer of the liquid bath and the discharge amount Q per single hole.
The relationship between (g / min) and the take-up speed V (m / min) can be calculated by the formula 2 ×
By setting V × Q 0.5 ≦ L ≦ 10 × V × Q 0.5 , it is possible to reliably obtain a high-strength polyamide monofilament having excellent transparency.
【００２９】上層の液体で表層が冷却された吐出ポリマ
ーは、次いで下層の液体である水に至り、この水によっ
て更に冷却される。すなわち、上層の液体で表層が十分
冷却され、内層部分の冷却が不十分な状態の吐出ポリマ
ーは、下層の液体である水の層に入り、さらに内層部分
が冷却されることになる。この場合に、内層部分の溶融
状態のポリマーが、直接水に触れることなく、比熱の大
きな水で急冷されるため、内層部分における球晶の発生
が効果的に抑制される。The discharged polymer, the surface layer of which has been cooled by the liquid of the upper layer, reaches water which is the liquid of the lower layer, and is further cooled by this water. That is, the discharged polymer in a state where the surface layer is sufficiently cooled by the upper layer liquid and the inner layer portion is not sufficiently cooled enters the water layer which is the lower layer liquid, and the inner layer portion is further cooled. In this case, the molten polymer in the inner layer portion is rapidly cooled with water having a large specific heat without directly contacting with water, so that the generation of spherulites in the inner layer portion is effectively suppressed.
【００３０】上記のように、吐出ポリマーを冷却する口
金直下の液体浴として、上層に無極性あるいは極性の小
さい液体を、また下層に水を用いた二層構造の冷却媒体
を用いて、二段階で冷却することにより、吐出ポリマー
の内外層ともに球晶の発生を抑制することができ、透明
性の良好な未延伸モノフィラメントが得られる。また、
冷却された後の内外層におけるポリマーの構造差も少な
くなる。As described above, as a liquid bath just below the mouthpiece for cooling the discharged polymer, a two-stage cooling medium using a non-polar or small-polarity liquid in the upper layer and water in the lower layer is used, and two-stage cooling is performed. By cooling with, the generation of spherulites can be suppressed in both the inner and outer layers of the discharged polymer, and an unstretched monofilament having good transparency can be obtained. Also,
The structural difference of the polymer in the inner and outer layers after cooling is also reduced.
【００３１】上記のように冷却固化されたポリアミドモ
ノフィラメントは、冷却浴から導出された後、低圧の水
蒸気が充満された水蒸気処理装置に導入される。The polyamide monofilament cooled and solidified as described above is discharged from the cooling bath and then introduced into a steam treatment apparatus filled with low-pressure steam.
【００３２】水蒸気処理装置で使用する水蒸気は、飽和
水蒸気であっても、また５０重量％以上の水分を含む加
熱蒸気であってもよいが、圧力としては２０〜３００mm
Ｈ2 Ｏの低圧であり、水蒸気処理装置内の雰囲気温度は
６０〜１６０℃、水蒸気処理装置内のにおけるポリアミ
ドモノフィラメントの滞留時間は０．０１〜１．０秒間
の条件とする。The steam used in the steam treatment apparatus may be saturated steam or heated steam containing 50% by weight or more of water, but the pressure is 20 to 300 mm.
The pressure is H 2 O at a low pressure, the atmospheric temperature in the steam treatment apparatus is 60 to 160 ° C., and the residence time of the polyamide monofilament in the steam treatment apparatus is 0.01 to 1.0 seconds.
【００３３】前記の水蒸気処理条件を満足しない場合、
例えば水蒸気圧力が２０mmＨ2 Ｏ未満の低圧、水蒸気処
理温度が６０℃未満の低温、あるいは未延伸ポリアミド
モノフィラメントが水蒸気にさらされる時間が０．０１
秒間未満の短時間のいずれかの条件となった場合には、
未延伸ポリアミドモノフィラメントの急冷された表層部
の複屈折が内層部分の複屈折よりも高くなり、この高く
なった複屈折の緩和が一定に行われないため好ましくな
い。When the above steam treatment conditions are not satisfied,
For example, the steam pressure is lower than 20 mmH 2 O, the steam treatment temperature is lower than 60 ° C., or the unstretched polyamide monofilament is exposed to steam for 0.01 time.
If any of the conditions for a short time less than 2 seconds,
The birefringence of the rapidly cooled surface layer portion of the unstretched polyamide monofilament becomes higher than the birefringence of the inner layer portion, and this increased birefringence is not alleviated uniformly, which is not preferable.
【００３４】一方、例えば水蒸気圧力が３００mmＨ2 Ｏ
を越える高圧、水蒸気処理温度が１６０℃を越える高
温、あるいは未延伸ポリアミドモノフィラメントが水蒸
気にさらされる時間が１．０秒間を越える長時間のいず
れかの条件となった場合には、未延伸ポリアミドモノフ
ィラメントは水蒸気による影響が表層部分のみではなく
内層部分まで浸透し過ぎたものとなり、次いで延伸され
た後のポリアミドモノフィラメントは、高配向部分が少
なくなり、高強度にならないため好ましくない。On the other hand, for example, when the water vapor pressure is 300 mmH 2 O
Unexpanded polyamide monofilament, under the conditions of high pressure exceeding 1.0 ° C., steam treatment temperature exceeding 160 ° C., or exposure time of unexpanded polyamide monofilament to steam for a long time exceeding 1.0 second. Is not preferable because the effect of water vapor has penetrated too much not only in the surface layer portion but also in the inner layer portion, and the polyamide monofilament after being stretched has less highly oriented portions and does not have high strength, which is not preferable.
【００３５】また、この場合に得られるポリアミドモノ
フィラメントは、透明性が劣り、釣糸や漁網などの水産
資材用としては適さないものとなる。Further, the polyamide monofilament obtained in this case is inferior in transparency and is not suitable for marine products such as fishing line and fishing net.
【００３６】本発明のポリアミドモノフィラメントの製
造方法における最大の特徴は、延伸に先立って、冷却浴
の中に形成された二層の特定条件を満足する液体で吐出
ポリマを冷却することにあり、さらにこのように冷却さ
れた未延伸ポリアミドモノフィラメントを水蒸気処理す
ることにある。The greatest feature of the method for producing a polyamide monofilament of the present invention is that prior to stretching, the discharged polymer is cooled with a liquid satisfying the specific conditions of the two layers formed in the cooling bath. The unstretched polyamide monofilament thus cooled is subjected to steam treatment.
【００３７】前記ポリアミドモノフィラメントの水蒸気
処理は、前記のように未延伸ポリアミドモノフィラメン
トを６０〜１６０℃の温度、２０〜３００mmＨ2 Ｏの低
圧の水蒸気で処理することにより、次の延伸工程で延伸
を施す際に、高倍率で延伸することが可能となり、この
高倍率延伸によって高強度のポリアミドモノフィラメン
トを得ることが可能となる。In the steam treatment of the polyamide monofilament, as described above, the unstretched polyamide monofilament is treated with a steam at a temperature of 60 to 160 ° C. and a low pressure of 20 to 300 mmH 2 O so as to be stretched in the next stretching step. At this time, it becomes possible to draw at a high draw ratio, and it becomes possible to obtain a high-strength polyamide monofilament by this high draw ratio.
【００３８】前記の高倍率延伸には、熱延伸法を用い、
さらに高倍率延伸を施してより高強度とするためには、
多段熱延伸法が用いられる。A hot stretching method is used for the above-mentioned high-magnification stretching,
In order to further increase the strength by applying a high-strength drawing,
A multi-stage hot drawing method is used.
【００３９】前記の多段熱延伸法は例えば、一段目延伸
を１５０〜２１０℃で、４．０〜５．５倍の熱延伸と
し、次いで１８０〜２１５℃の温度で、０．９０〜１．
０３倍の緊張熱処理とし、更に引続いて二段目延伸を１
９０〜２２０℃の温度で、総合延伸倍率が５．５〜７．
２倍の範囲となるごとく条件を設定する。In the multi-stage hot stretching method, for example, the first stage stretching is carried out at 150 to 210 ° C. to 4.0 to 5.5 times the hot stretching, and then at a temperature of 180 to 215 ° C. for 0.90 to 1.
A tension heat treatment of 03 times was performed, and then the second stage drawing was continued to 1
At a temperature of 90 to 220 ° C., the total draw ratio is 5.5 to 7.
Set the conditions so that the range is doubled.
【００４０】前記のように本発明に係る方法によって得
られた未延伸モノフィラメントは、熱延伸を施した後も
透明性に優れ、しかも高倍率延伸を可能とし、高強度の
ポリアミドモノフィラメントを与える。As described above, the unstretched monofilament obtained by the method according to the present invention is excellent in transparency even after being subjected to hot stretching, and enables high-strength stretching, and gives a high-strength polyamide monofilament.
【００４１】以下実施例によって説明するが、ポリアミ
ドモノフィラメントの物性測定法は以下のとおりであ
る。The method of measuring the physical properties of the polyamide monofilament will be described below with reference to examples.
【００４２】硫酸相対粘度（ηｒ）：試料１ｇを９８％
硫酸１００ｍｌに溶解し、オストワルド粘度計で２５℃
で測定した。Sulfuric acid relative viscosity (ηr): 98% of 1 g of sample
Dissolve in 100 ml of sulfuric acid and use an Ostwald viscometer at 25 ° C.
It was measured at.
【００４３】引張強度、引張伸度、結節強度、および結
節伸度：ＪＩＳ−Ｌ１０１７の定義によった。試料を綛
状にとり、２０℃、６５％ＲＨの温湿度調節室で２４時
間放置した後、（株）オリエンテック社製“テンシロ
ン”ＵＴＭ−４−１００型引張試験機を用い、試長２５
cm、引張速度３０cm／分の条件で測定した。Tensile strength, tensile elongation, knot strength, and knot elongation: defined according to JIS-L1017. After taking a sample in the shape of a slab and leaving it in a temperature / humidity control room at 20 ° C. and 65% RH for 24 hours, using a “Tensilon” UTM-4-100 tensile tester manufactured by Orientec Co., Ltd., a test length of 25
The measurement was performed under the conditions of cm and tensile speed of 30 cm / min.
【００４４】[0044]
【実施例】実施例１ナイロン−６（相対粘度６．５０）
チップを１５mmφエクストルダー型紡糸機に供給し、溶
融紡糸温度：２９０℃、押込み圧力：１００Kg／cm2 の
条件で１．０mmφの紡糸口金より吐出した。この吐出さ
れた吐出ポリマーを紡糸口金の直下に設けられた液体浴
を用いて冷却した。EXAMPLES Example 1 Nylon-6 (relative viscosity 6.50)
The chips were supplied to a 15 mmφ extruder type spinning machine and discharged from a 1.0 mmφ spinneret under the conditions of melt spinning temperature: 290 ° C. and indentation pressure: 100 kg / cm 2 . The discharged discharged polymer was cooled using a liquid bath provided immediately below the spinneret.
【００４５】液体浴における液体は、上層に７℃に調整
されたケロシン（冷却長３０cm）、下層に７℃に調整さ
れた水（冷却長５０cm）を用いた二層とした。The liquid used in the liquid bath was a two-layer structure using kerosene (cooling length 30 cm) adjusted to 7 ° C. for the upper layer and water (cooling length 50 cm) adjusted to 7 ° C. for the lower layer.
【００４６】前記液体浴によって冷却された未延伸モノ
フィラメントを、長さ２．５cmの水蒸気処理装置を通過
させ、水蒸気処理を施した。この水蒸気処理装置内の水
蒸気圧力は６０mmＨ2 Ｏ、温度は９０℃とした。The unstretched monofilament cooled by the liquid bath was passed through a steam treatment device having a length of 2.5 cm to be subjected to steam treatment. The steam pressure in the steam treatment apparatus was 60 mmH 2 O and the temperature was 90 ° C.
【００４７】前記液体浴および水蒸気処理装置で処理さ
れた未延伸ポリアミドモノフィラメントを、引続いて５
ｍ／分の速度で引取りロールによって引取った後、連続
して１６０℃に加熱した長さ１５cmのポリエチレングリ
コール浴中で４．５倍に熱延伸し一段延伸モノフィラメ
ントを得た。The unstretched polyamide monofilaments treated in the liquid bath and steam treatment device are subsequently treated with 5
After being drawn by a take-up roll at a speed of m / min, it was continuously drawn 4.5 times in a polyethylene glycol bath having a length of 15 cm and heated to 160 ° C. to obtain a single-stage drawn monofilament.
【００４８】次に得られた一段延伸モノフィラメント
を、連続して２００℃、長さ２cmのポリエチレングリコ
ール浴中で０．９５倍の延伸比で弛緩処理し、更に連続
して２００℃、長さ５０cmのポリエチレングリコール浴
中で二段目の熱延伸を行なった。この二段目の延伸倍率
は１．５倍とした。Next, the obtained single-stage drawn monofilament was continuously subjected to relaxation treatment in a polyethylene glycol bath having a length of 2 cm at 200 ° C. at a draw ratio of 0.95 times, and further continuously at 200 ° C. and a length of 50 cm. The second thermal drawing was performed in the polyethylene glycol bath. The draw ratio of the second stage was 1.5 times.
【００４９】延伸を終ったポリアミドモノフィラメント
は、次いで浴温９０℃、長さ１００cmの温水浴中を定長
で通過させた後、仕上剤を付与して巻取った。The stretched polyamide monofilament was then passed through a hot water bath having a bath temperature of 90 ° C. and a length of 100 cm at a fixed length, and then a finishing agent was applied thereto and wound.
【００５０】得られたポリアミドモノフィラメントは透
明性に優れ、力学特性は次のとおりであった。The polyamide monofilament obtained was excellent in transparency and had the following mechanical characteristics.
【００５１】引張強度 ： １０．５ｇ／ｄ引張伸度
： ２２．３％結節強度： ９．５ｇ／ｄ結節伸度
： １８．０％比較例１紡糸口金の直下に設けた液体
浴を二層とすることなく、すべて７℃に調整された水を
用いた以外は、実施例１と同様の条件でポリアミドモノ
フィラメントを紡糸および延伸した。その結果延伸工程
において糸切れが多発し高倍率延伸はできなかった。Tensile Strength: 10.5 g / d Tensile Elongation: 22.3% Knot Strength: 9.5 g / d Knot Elongation: 18.0% Comparative Example 1 Two layers of liquid bath provided directly under the spinneret. The polyamide monofilament was spun and stretched under the same conditions as in Example 1, except that water adjusted to 7 ° C. was used. As a result, yarn breakage occurred frequently in the drawing step, and high-magnification drawing was not possible.
【００５２】比較例２実施例１において、水蒸気処理装
置を除いた以外はすべて同じ方法で紡糸、延伸を行った
結果、得られたポリアミドモノフィラメントの力学特性
は次の通りであった。Comparative Example 2 As a result of spinning and drawing in the same manner as in Example 1 except that the steam treatment apparatus was omitted, the obtained polyamide monofilament had the following mechanical characteristics.
【００５３】引張強度 ： １０．０ｇ／ｄ引張伸度
： ２２．３％結節強度： ８．８ｇ／ｄ結節伸度
： １８．０％比較例３紡糸口金の直下に設けた液体
浴を二層とすることなく、すべて７℃に調整された水を
用い、延伸工程における第二段目の延伸倍率を１．３５
倍とした以外は実施例１と同様の条件でポリアミドモノ
フィラメントを紡糸および延伸した。Tensile Strength: 10.0 g / d Tensile Elongation: 22.3% Knot Strength: 8.8 g / d Knot Elongation: 18.0% Comparative Example 3 Two layers of liquid bath provided directly under the spinneret. Without using the water, the second draw ratio in the drawing process was 1.35.
A polyamide monofilament was spun and stretched under the same conditions as in Example 1 except that the number was doubled.
【００５４】その結果、得られたポリアミドモノフィラ
メントは表層に球晶が発生し、著しく透明性が阻害され
ており、力学特性も次に示すとおり、実施例１に比較し
て著しく低い値を示すものであった。As a result, the obtained polyamide monofilament was found to have spherulites in the surface layer, which markedly hindered the transparency, and the mechanical properties of the polyamide monofilament showed a significantly lower value than that of Example 1, as shown below. Met.
【００５５】引張強度 ： ８．８ｇ／ｄ引張伸度
： ２３．０％結節強度： ７．０ｇ／ｄ結節伸度
： １６．５％比較例４紡糸口金の直下に設けた液体
浴の液体を二層とすることなく、すべてケロシンを用い
た以外はすべて実施例１と同様の条件で紡糸、延伸を用
い、ポリアミドモノフィラメントを得た。Tensile Strength: 8.8 g / d Tensile Elongation: 23.0% Knot Strength: 7.0 g / d Knot Elongation: 16.5% Comparative Example 4 The liquid in the liquid bath provided immediately below the spinneret was used. A polyamide monofilament was obtained by spinning and drawing under the same conditions as in Example 1 except that kerosene was used instead of using two layers.
【００５６】得られたポリアミドモノフィラメントは、
内層に球晶が発生し、著しく透明性が阻害されており、
力学特性も次に示すとおり、実施例１に比較して著しく
低い値を示すものであった。The polyamide monofilament obtained is
Spherulites occur in the inner layer, which significantly hinders transparency,
As shown below, the mechanical properties were also significantly lower than those of Example 1.
【００５７】引張強度 ： ９．４ｇ／ｄ引張伸度
： １９．５％結節強度： ８．３ｇ／ｄ結節伸度
： １７．１％Tensile Strength: 9.4 g / d Tensile Elongation: 19.5% Knot Strength: 8.3 g / d Nodule Elongation: 17.1%
【００５８】[0058]
【発明の効果】本発明の方法によって得られるポリアミ
ドモノフィラメントは、内外層ともに球晶の発生が抑制
されるため、優れた透明性を有し、釣糸、および漁網用
糸として最適である。EFFECT OF THE INVENTION The polyamide monofilament obtained by the method of the present invention is excellent in transparency because it suppresses the formation of spherulites in both the inner and outer layers, and is optimal as a fishing line and a fishing line.
【００５９】さらに、未延伸糸が均一であるため延伸工
程における糸切れもなく、極めて高倍率延伸を可能と
し、製糸性が向上すると共に、得られたポリアミドモノ
フィラメントは、引張強度、結節強度が高く、釣糸、お
よび漁網用糸として最適である。Furthermore, since the undrawn yarn is uniform, there is no yarn breakage in the drawing process, and it is possible to carry out extremely high-magnification drawing, the yarn-forming property is improved, and the obtained polyamide monofilament has high tensile strength and knot strength. Most suitable for fishing line, fishing line, and fishing line.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.5 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｄ０１Ｆ 6/60 Ｆ 7199−3Ｂ Ｋ 7199−3Ｂ ３４１ Ｃ 7199−3Ｂ Ｄ０２Ｊ 1/22 ３０１ Ｂ Ｄ０６Ｍ 11/05 7199−3Ｂ Ｄ０６Ｍ 3/12 ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 5 Identification code Internal reference number FI Technical display location D01F 6/60 F 7199-3B K 7199-3B 341 C 7199-3B D02J 1/22 301 B D06M 11 / 05 7199-3B D06M 3/12
Claims (2)
フィラメントの製造方法において、紡糸口金から吐出さ
れたポリアミドからなる吐出ポリマーを、紡糸口金の直
下に設けられた液体浴中で冷却した後引取り、引続き熱
延伸する際、前記液体浴における液体を二層となし、下
層の液体として水を、また上層の液体として前記水より
も比重が小さく、無極性または極性の小さい液体を用
い、前記上層および下層の液体の温度を２〜１０℃の範
囲内となした二段階で冷却を施すと共に、吐出ポリマー
が上層の液体を通過する距離Ｌ（cm）、紡糸口金の単孔
当たりの吐出量Ｑ（ｇ／分）および引取速度Ｖ（ｍ／
分）が、式２×Ｖ×Ｑ0.5 ≦Ｌ≦１０×Ｖ×Ｑ0.5 の関
係を満たすことを特徴とする透明性に優れた高強度ポリ
アミドモノフィラメントの製造方法。1. A method for producing a high-strength polyamide monofilament having excellent transparency, wherein a discharged polymer composed of polyamide discharged from a spinneret is cooled in a liquid bath provided directly below the spinneret, and then collected. During the subsequent hot drawing, the liquid in the liquid bath is formed into two layers, water is used as the lower layer liquid, and specific gravity smaller than that of the water is used as the upper layer liquid, and a nonpolar or small polar liquid is used, and the upper layer and The lower layer liquid is cooled in two steps within a temperature range of 2 to 10 ° C., the distance L (cm) at which the discharged polymer passes through the upper layer liquid, and the discharge amount Q per single hole of the spinneret. g / min) and the take-up speed V (m /
Min) satisfies the formula 2 × V × Q 0.5 ≦ L ≦ 10 × V × Q 0.5 . A method for producing a high-strength polyamide monofilament having excellent transparency.
た後、温度６０〜１５０℃、圧力２０〜３００mmＨ2 Ｏ
の水蒸気で満たされた加熱処理装置に導入し、０．０１
〜１．０秒間加熱処理し、この加熱処理装置から導き出
し、引続いて４．５倍以上に熱延伸することを特徴とす
る請求項１記載の透明性に優れた高強度ポリアミドモノ
フィラメントの製造方法。2. A temperature of 60 to 150 ° C. and a pressure of 20 to 300 mmH 2 O after the discharged polymer is drawn out from the cooling medium.
Was introduced into a heat treatment apparatus filled with
The method for producing a high-strength polyamide monofilament excellent in transparency according to claim 1, wherein the heat treatment is conducted for ~ 1.0 second, the heat treatment is conducted from the heat treatment apparatus, and then the material is heat-stretched 4.5 times or more. ..