JPH04502646A - Polymer blend of polycarbonate, styrene terpolymer and glass fiber - Google Patents

Abstract

(57)【要約】本公報は電子出願前の出願データであるため要約のデータは記録されません。 (57) [Summary] This bulletin contains application data before electronic filing, so abstract data is not recorded.

Description

【発明の詳細な説明】 ポリカーボネート、スチレンターポリマー及びガラス繊維のポリマーブレンド 関　連　出　願 本願は、１９８８年３月８日付で提出した同時継続中の米国特許出願第１６５， ４６２号の一部継続出願である。[Detailed description of the invention] Polymer blend of polycarbonate, styrene terpolymer and glass fiber Related application This application is filed under co-pending U.S. Patent Application No. 165, filed March 8, 1988, This is a continuation in part of No. 462.

発　明　の　分　野 本発明は、ポリカーボネート；スチレン、アクリロニトリル及び無水マレイン酸 のスチレンターポリマー、及びガラス繊維を含むポリマーブレンド組成物に関す る。更に詳しくは、本発明はモジュラス及び熱変形温度を含む優れた物理的性質 の組合せを発揮する前記ポリマーブレンド組成物に関する。Branch of development The present invention uses polycarbonate; styrene, acrylonitrile and maleic anhydride. styrene terpolymer and glass fibers. Ru. More specifically, the present invention provides superior physical properties including modulus and heat distortion temperature. The present invention relates to the above polymer blend composition exhibiting a combination of:

発　明　の　背　景 エンジニアリング用途に使用するポリマーブレンド組成物は、耐熱性、良好な強 さ及び良好なモジュラスの組合せを発揮する必要がある。更に、ブレンド組成物 は、加工及び成形を促す良好なメルトフロー特性を発揮する必要がある。ポリカ ーボネートは、タフネス及び比較的高い軟化温度により人気の高いブレンド成分 である。しかし、メルトフロー特性が比較的劣り、そのメルトフロー特性を改良 するために、ポリカーボネートはしばしば１種又はそれ以上の他のポリマーとブ レンドされる。得られるブレンドは通常改良されたメルトフロー特性を示すが、 耐熱性、衝撃強さ等の他の性質が劣化する。Background of the invention Polymer blend compositions used in engineering applications have high heat resistance, good strength, It is necessary to exhibit a combination of strength and good modulus. Furthermore, the blend composition must exhibit good melt flow properties to facilitate processing and molding. polycarbonate Carbonate is a popular blending ingredient due to its toughness and relatively high softening temperature. It is. However, the melt flow characteristics are relatively poor, and the melt flow characteristics can be improved. To achieve this, polycarbonate is often combined with one or more other polymers. Rend. The resulting blends usually exhibit improved melt flow properties, but Other properties such as heat resistance and impact strength deteriorate.

この種のブレンド組成物の例が知られている。例えば、グラボウスキの米国特許 第３，１３０，１７７号明細書に、ポリカーボネ−１・とポリブタジェン、スチ レン、アクリロニトリルグラフトポリマーとのブレンドが開示され、グラボウス キの米国特許第３，１６２．６９５号明細書に、ポリカーボネートとブタジェン −スチレン、メタクリル酸メチル、スチレングラフト共重合体とのブレンドが開 示されている。リービクらの米国特許第４，２０５．１．４０号明細書に、ポリ カーボネート、ＡＢＳ等のジエンゴムグラフトポリマー及びスチレンポリマーの ブレンドから成る熱可塑性成形組成物が開示されている。ポリカーボネートと、 スチレン−無水マレイン酸共重合体、ＡＢＳ樹脂及びスチレン−アクリロニトリ ルランダム共重合体との類似のブレンドが、ヘントンの米国特許第４，２１８． ５４４号明細書に開示されている。グリゴらの米国特許第４，４７２゜５５４号 明細書に、ポリカーボネート、ＡＢＳ等のグラフトポリマー及びポリマー性酸性 化剤のブレンドから成る熱可塑性成形組成物が開示されている。ジョーンズらの 米国特許束４，５６９，９６９号及び同４，６６３．３８９号、並びに欧州特許 出願第１３５．４９３号各明細書にも、ポリカーボネート、ＡＢＳポリマー及び スチレンポリマーのポリマーブレンドが開示されている。これらのブレンドは、 含まれる成分の種類及び比率に応じて様々な物理的性質を発揮する。Examples of blend compositions of this type are known. For example, Grabowski's US patent No. 3,130,177 discloses that polycarbonate-1 and polybutadiene, Blends with acrylonitrile grafted polymers are disclosed and Grabous In U.S. Pat. -Blends with styrene, methyl methacrylate, and styrene graft copolymers have been developed. It is shown. No. 4,205.1.40 to Liebik et al. of diene rubber graft polymers and styrene polymers such as carbonate and ABS. A thermoplastic molding composition comprising a blend is disclosed. polycarbonate and Styrene-maleic anhydride copolymer, ABS resin and styrene-acrylonitrile Similar blends with Lurandom copolymers are described in Henton U.S. Pat. No. 4,218. No. 544. U.S. Pat. No. 4,472°554 to Grigo et al. In the specification, graft polymers such as polycarbonate and ABS, and polymer acidic A thermoplastic molding composition comprising a blend of curing agents is disclosed. Jones et al. U.S. patent bundles 4,569,969 and 4,663.389, and European patents Application No. 135.493 also describes polycarbonate, ABS polymer and Polymer blends of styrene polymers are disclosed. These blends are It exhibits various physical properties depending on the types and ratios of the components included.

パーソンズの同時継続中の米国特許出願第１６５．４６２号明細書に、ポリカー ボネート、スチレン−アクリロニトリル−無水マレイン酸ターポリマー、及び前 記ポリカーボネートとスチレンターポリマーとの間のブレンド相容化剤の役割を 果たす少量のＡＢＳ樹脂から成るブレンド組成物が開示されている。この組成物 は、優れた衝撃強さ、耐熱性及びモジュラスの組合せを発揮する。Parsons co-pending U.S. patent application Ser. carbonate, styrene-acrylonitrile-maleic anhydride terpolymer, and The role of blend compatibilizer between polycarbonate and styrene terpolymer A blend composition comprising a small amount of ABS resin is disclosed. This composition exhibits an excellent combination of impact strength, heat resistance and modulus.

更に、高い引張、圧縮及び曲げ強さを必要とする用途用の熱可塑性組成物にガラ ス繊維を添加することも知られている。スチレン−無水マレイン酸共重合体、及 びポリカーボネートと組合せたスチレン−無水マレイン酸共重合体を含むガラス 充填組成物が、登録商標ディラーク及び登録商標アーロイの商品名でアーコ社か ら、そして登録商標力ドンとしてモンサンド社から現在市販されている。また、 英国特許第１．３６５，３２９号明細書にガラス繊維含有スチレン樹脂組成物が 開示されており、そしてローリングらの米国特許第４．４８７．８８１号明細書 にポリカーボネート、グラフトエラストマー、ポリ無水物及びガラス繊維のブレ ンドが開示されている。これらの組成物も、様々な物理的性質の組合せを発揮す る。Additionally, glass can be added to thermoplastic compositions for applications requiring high tensile, compressive and flexural strength. It is also known to add fibers. Styrene-maleic anhydride copolymer, and glass containing styrene-maleic anhydride copolymer in combination with polycarbonate and polycarbonate The filling composition is manufactured by Arco under the trade name Dirag (registered trademark) and Alloy (registered trademark). and is currently commercially available from Monsando under the registered trademark Rikidon. Also, British Patent No. 1,365,329 describes a glass fiber-containing styrene resin composition. No. 4,487,881 to Loring et al. Polycarbonate, grafted elastomer, polyanhydride and glass fiber blends is disclosed. These compositions also exhibit various combinations of physical properties. Ru.

発　明　の　概　要 即ち、本発明の目的は、耐熱性、良好な強さ及び良好なモジュラスを含む優れた 物理的性質の組合せを発揮するポリマーブレンド組成物を提供することにある。Outline of the invention That is, the object of the present invention is to provide excellent heat resistance, good strength and good modulus. The objective is to provide polymer blend compositions that exhibit a combination of physical properties.

本発明のもう１つの目的は、ブレンドを様々なエンジニアリング熱可塑性ブレン ド用途に使用可能とする優れた耐熱性、強さ及びモジュラスの組合せを発揮する ポリマーブレンド組成物を提供することにある。本発明の更にもう１つの目的は 、改良された性質、特に組成物の個々の成分と比較して改良された性質を発揮す る前記組成物を提供することにある。Another object of the invention is to blend various engineering thermoplastic blends. Demonstrates an excellent combination of heat resistance, strength and modulus that allows it to be used in hard applications. An object of the present invention is to provide a polymer blend composition. Yet another object of the invention is , exhibiting improved properties, especially compared to the individual components of the composition. An object of the present invention is to provide the above-mentioned composition.

これらの及びその他の目的は、ポリカーボネート、スチレン−アクリロニトリル −無水マレイン酸ターポリマー及びガラス繊維を含む本発明のブレンド組成物に より達成される。更に詳しくは、ガラス繊維はポリカーボネート、ターポリマー 及びガラス繊維を基準として約５乃至約４０重量％の量で含まれる。好ましくは 、ポリカーボネートは約１５乃至約６５重量％、更に好ましくは約２０乃至約３ ５重量％の量で含まれ、そしてターポリマーは約１０乃至約８０重量％、更に好 ましくは約３５乃至約７５重量％の量で含まれる。この組成物は、良好な強さ、 モジュラス及び耐熱性を含む優れた物理的性質の組合せを発揮する。このブレン ドは、ブレンド組成物の他の優れた性質に重大な悪影響を及ぼすことなく、例え ば表面外観及び衝撃強さ等における他の改良をも得るために、必要に応じて少量 のＡＢＳ樹脂を含むことができる。For these and other purposes, polycarbonate, styrene-acrylonitrile - a blend composition of the invention comprising a maleic anhydride terpolymer and glass fibers; more achieved. More specifically, glass fibers are polycarbonate, terpolymer and about 5 to about 40% by weight based on glass fiber. Preferably , about 15 to about 65% by weight polycarbonate, more preferably about 20 to about 3% by weight. 5% by weight, and the terpolymer is present in an amount of about 10 to about 80% by weight, more preferably Preferably, it is included in an amount of about 35 to about 75% by weight. This composition has good strength, Exhibits an excellent combination of physical properties including modulus and heat resistance. This brain without significantly adversely affecting the other good properties of the blend composition. small amounts as necessary to obtain other improvements in surface appearance and impact strength, etc. ABS resin may be included.

これらの及びその他の目的、及び本発明のブレンド組成物により得られる利点が 、以下の詳細な説明により更に明確になる。These and other objects and advantages obtained by the blend compositions of the present invention , will become more clear from the detailed description below.

詳　細　な　説　明 本発明のポリマーブレンド組成物は、ポリカーボネート：スチレン−アクリロニ トリル−無水マレイン酸ターポリマー；及びポリカーボネート、ターポリマー及 びガラス繊維を基準として約５乃至約４０重量％の量のガラス繊維を含む。この ブレンド組成物は、優れた強さ、モジュラス及び耐熱性の組合せを発揮する。Detailed explanation The polymer blend composition of the present invention comprises polycarbonate:styrene-acryloni. tolyl-maleic anhydride terpolymers; and polycarbonates, terpolymers and and glass fibers in an amount of about 5% to about 40% by weight, based on glass fibers. this The blend composition exhibits an excellent combination of strength, modulus and heat resistance.

このブレンド組成物に含まれるポリカーボネート成分は、当業界で公知の芳香族 ホモポリカーボネート又はコポリカーボネートの何れであってもよい。ポリカー ボネート成分は、例えば界面重縮合法、均質相中での重縮合又はエステル交換反 応によるなど、当業界で通常知られている方法の何れに従っても製造することが できる。これらの方法及びそれらに係わる反応物質、触媒、溶媒及び条件は当業 界で周知であり、そして例えば、参照として、米国特許第２゜９６４．９７４号 、同２，９７０，１３７号、同２，９９９．８３５号、同２．９９９，８４６号 、同３，０２８゜３６５号、同３，１５３，００８号、同３，１８７，０６５号 、同３，２１５，６６８号及び同３，２５８，４１４号各明細書に記載されてい る。適切なポリカーボネートは、例えば１種又はそれ以上の下記ビスフェノール に基づく。The polycarbonate component included in this blend composition is an aromatic polycarbonate component known in the art. It may be either homopolycarbonate or copolycarbonate. polycar The carbonate component can be used, for example, in an interfacial polycondensation process, in a homogeneous phase polycondensation process or in a transesterification reaction. It can be manufactured according to any method commonly known in the art, such as by can. These methods and their associated reactants, catalysts, solvents, and conditions are within the skill of the art. Well known in the art and see, for example, U.S. Pat. No. 2,964,974. , No. 2,970,137, No. 2,999.835, No. 2.999,846 , No. 3,028゜365, No. 3,153,008, No. 3,187,065 , No. 3,215,668 and No. 3,258,414. Ru. Suitable polycarbonates include, for example, one or more of the following bisphenols: based on.

ジヒドロキシジフェニル、ビス−（ヒドロキシフェニル）アルカン、ビス＝（ヒ ドロキシフェニル）シクロアルカン、ビス−（ヒドロキシフェニル）スルフィド 、ビス＝（ヒドロキシフェニル）エーテル、ビス−（ヒドロキシフェニル）ケト ン、ビス−（ヒドロキシフェニル）スルホキシド、ビス−（ヒドロキシフェニル ）スルホン、α、α−ビス−（ヒドロキシフェニル）ジイソプロピルベンゼン、 及びこれらの核−アルキル化及び核−ハロゲン化誘導体、並びにこれらの混合物 。Dihydroxydiphenyl, bis(hydroxyphenyl)alkane, bis=(hydrogen) Droxyphenyl) cycloalkane, bis-(hydroxyphenyl) sulfide , bis(hydroxyphenyl)ether, bis(hydroxyphenyl)keto bis-(hydroxyphenyl) sulfoxide, bis-(hydroxyphenyl) ) sulfone, α, α-bis-(hydroxyphenyl)diisopropylbenzene, and nuclear-alkylated and nuclear-halogenated derivatives thereof, and mixtures thereof. .

これらのビスフェノールの具体例は、４．４＝−ジヒドロキシジフェニル、２． ２−ビス＝（４−ヒドロキシフェニル）プロパン、２．４−ビス−（４−ヒドロ キシフェニル）−２−メチルブタン、１．１−ビス−（４−ヒドロキシフェニル ）シクロヘキサン、α、α−ビス−（４−ヒドロキシフェニル）−ｐ−ジイソプ ロピルベンゼン、２，２−ビス（３−メチル−４−ヒドロキシフェニル）プロパ ン、２．２−ビス（３−クロロ−４−ヒドロキシフェニル）プロパン、ビス−（ ３，５−ジメチル−４−ヒドロキシフェニル）メタン、２．２−ビス（３，５− ジメチル−４−ヒドロキシフェニル）プロパン、ビス−（３，５−ジメチル−４ −ヒドロキシフェニル）スルホン、２，４−ビス−（３，５−ジメチル−４−ヒ ドロキシフェニル）−２−メチルブタン、１，１−ビス−（３，５−ジメチル− ４−ヒ５−ジメチルー４−ヒドロキシフェニル）−ｐ−ジイソプロピルベンゼン 、２，２−ビス＝（３，５−ジクロロ−４＝ヒドロキシフエニル）プロパン及び ２．２−ビス（３゜５−ジブロモ−４−ヒドロキシフェニル）プロパンである。Specific examples of these bisphenols include 4.4=-dihydroxydiphenyl, 2. 2-bis=(4-hydroxyphenyl)propane, 2.4-bis-(4-hydro xyphenyl)-2-methylbutane, 1,1-bis-(4-hydroxyphenyl) ) cyclohexane, α, α-bis-(4-hydroxyphenyl)-p-diisopropylene Lopylbenzene, 2,2-bis(3-methyl-4-hydroxyphenyl)propyl 2,2-bis(3-chloro-4-hydroxyphenyl)propane, bis-( 3,5-dimethyl-4-hydroxyphenyl)methane, 2,2-bis(3,5- dimethyl-4-hydroxyphenyl)propane, bis-(3,5-dimethyl-4 -Hydroxyphenyl)sulfone, 2,4-bis-(3,5-dimethyl-4-hydroxyphenyl) Droxyphenyl)-2-methylbutane, 1,1-bis-(3,5-dimethyl- 4-hy5-dimethyl-4-hydroxyphenyl)-p-diisopropylbenzene , 2,2-bis=(3,5-dichloro-4=hydroxyphenyl)propane and 2.2-bis(3°5-dibromo-4-hydroxyphenyl)propane.

特に好適なビスフェノールは、ビスフェノールＡとして一層普通に知られている ２、２−ビス−（４−ヒドロキシフェニル）プロパンである。A particularly preferred bisphenol is more commonly known as bisphenol A. 2,2-bis-(4-hydroxyphenyl)propane.

ポリカーボネート成分は、ブレンド組成物に良好な引張及び曲げ強さ、並びに良 好な耐熱性を付与するのに十分な量でブレンド組成物中に含まれる。好ましくは 、ポリカーボネート成分は、ポリカーボネート、ターポリマー及びガラス繊維の 総重量を基準として約１５乃至約６５重量％の量で含まれる。更に好ましくは、 ポリカーボネートは、ポリカーボネート、ターポリマー及びガラス繊維を基準と して約２０乃至約３５重量％の量で含まれる。本発明者らは、２０重量％以上の ポリカーボネートが、組成物に、ターポリマー及びガラス繊維を含む組成物より 大きな、そしてポリカーボネート及びガラス繊維を含む組成物と比べて大きな、 引張及び曲げ強さを付与することを見い出した。更に、本発明者らは、ポリカー ボネートが約３５重量％を超えると、組成物の引張及び曲げモジュラスを低下さ せ始めることを見い出した。The polycarbonate component provides the blend composition with good tensile and flexural strength, as well as It is included in the blend composition in an amount sufficient to impart good heat resistance. Preferably , the polycarbonate component is made of polycarbonate, terpolymer and glass fiber. It is included in an amount of about 15 to about 65% by weight based on the total weight. More preferably, Polycarbonate is based on polycarbonate, terpolymer and glass fiber. It is contained in an amount of about 20 to about 35% by weight. The present inventors found that 20% by weight or more The polycarbonate is better than a composition containing a terpolymer and glass fibers in the composition. large, and compared to compositions containing polycarbonate and glass fibers, It has been found that it imparts tensile and bending strength. Furthermore, the present inventors have discovered that polycarbonate More than about 35% by weight of bonate reduces the tensile and flexural modulus of the composition. I found that it started to change.

ブレンド組成物に含まれる第２の成分は、スチレン−アクリロニトリル−無水マ レイン酸ターポリマーから成る。The second component included in the blend composition is a styrene-acrylonitrile-anhydrous polymer. Consisting of leic acid terpolymer.

好ましくは、スチレンはターポリマー組成物の過半量を構成し、これによりター ポリマーは得られるブレンド組成物に剛性、良好なモジュラス及び耐熱性を付与 する。無水マレイン酸は、スチレン成分の性質を高めるのに十分な量でターポリ マー中に含まれる。好ましくは、無水マレイン酸はターポリマーの約４乃至約２ ５重量％を構成する。更に、ブレンド組成物が良好な溶融体安定性を発揮し、そ してそれにより良好な加工及び成形性を発揮するために、ターポリマーのアクリ ロニトリル成分を好ましくは約２０重量％以下の量で使用する。更に好ましくは 、約５乃至約２０重量％のアクリロニトリルをターポリマー中に含ませる。Preferably, styrene constitutes the majority of the terpolymer composition, thereby The polymer imparts stiffness, good modulus and heat resistance to the resulting blend composition do. Maleic anhydride is added to the terpolymer in sufficient amounts to enhance the properties of the styrene component. Contained in the market. Preferably, maleic anhydride accounts for about 4 to about 2 of the terpolymer. It constitutes 5% by weight. Additionally, the blend composition exhibits good melt stability and The terpolymer acrylic The lonitrile component is preferably used in an amount up to about 20% by weight. More preferably , about 5 to about 20 weight percent acrylonitrile is included in the terpolymer.

ターポリマーは、好ましくは当業界で周知である様な連続式重合法で形成される 。実際的には、スチレン−アクリロニトリル−無水マレイン酸ターポリマーの製 造を、該ターポリマーとスチレン−アクリロニトリル共重合体との混合物から成 る生成物を形成する様に調節することができる。Terpolymers are preferably formed by continuous polymerization methods such as are well known in the art. . In practice, the production of styrene-acrylonitrile-maleic anhydride terpolymer The structure is made of a mixture of the terpolymer and a styrene-acrylonitrile copolymer. can be adjusted to form a product that

ターポリマーの製造の間に得られる可能性のある、このターポリマーと共重合体 との混合物も又、下記実施例で示す様に本発明のブレンド成分組成物中に使用す ることができる。This terpolymer and copolymers that may be obtained during the production of the terpolymer Mixtures of can be done.

スチレン−アクリロニトリル−無水マレイン酸ターポリマーは、ブレンドに良好 な剛性、良好なモジュラス、及び特に熱変形温度で示される様な高い耐熱性を付 与するのに十分な量で使用する。好ましくは、ターポリマーはポリカーボネート 、ターポリマー及びガラス繊維の総重量を基準として約１０乃至約８０重量％の 量で使用する。更に好ましくは、ターポリマーはポリカーボネート、ターポリマ ー及びガラス繊維を基準として約３５乃至約７５重量％の量で含まれる。Styrene-acrylonitrile-maleic anhydride terpolymer is good for blending high stiffness, good modulus, and high heat resistance, especially as indicated by the heat distortion temperature. Use in sufficient quantity to provide Preferably the terpolymer is polycarbonate , about 10 to about 80% by weight based on the total weight of the terpolymer and glass fibers. Use in quantity. More preferably, the terpolymer is polycarbonate, terpolymer from about 35% to about 75% by weight, based on fiber and glass fibers.

ポリマーブレンド組成物の第３の成分は、ポリカーボネート、ターポリマー及び ガラス繊維を基準として約５乃至約４０重量％の量で使用されるガラス繊維から 成る。ガラス繊維は、ブレンド組成物に改良された強さ及びモジュラスを付与す る。様々なガラス繊維が市販されており、そして本発明組成物中に使用するのに 適している。本発明組成物中では様々なサイズのガラス繊維を使用することがで きるが、ガラス繊維が約０．０５乃至約０．５インチの平均長さを有することが 好ましい。下記実施例中で示す様に、本発明で使用するのに適したガラス繊維は オーエンスーフーニング・ファイバーガラス社から市販されている。好ましくは 、ガラス繊維はポリカーボネート、ターポリマー及びガラス繊維を基準として約 １０乃至約３０重量％の量で本発明組成物中に含まれる。The third component of the polymer blend composition comprises polycarbonate, terpolymer and From glass fibers used in an amount of about 5 to about 40% by weight based on glass fibers Become. Glass fibers impart improved strength and modulus to blend compositions. Ru. A variety of glass fibers are commercially available and suitable for use in the compositions of the present invention. Are suitable. Glass fibers of various sizes can be used in the compositions of the invention. However, the glass fibers can have an average length of about 0.05 to about 0.5 inches. preferable. As shown in the examples below, glass fibers suitable for use in the present invention include It is commercially available from Owens-Hooning Fiberglass Company. Preferably , glass fiber is approximately based on polycarbonate, terpolymer and glass fiber. It is included in the compositions of the present invention in amounts of 10 to about 30% by weight.

更に、本発明のブレンド組成物は、必要に応じてＡＢＳ樹脂を含むことができる 。含ませる場合、ＡＢＳ樹脂は、ポリカーボネート成分とスチレンターポリマー 成分との間の相容性を改良し、それにより、得られるブレンド組成物はポリカー ボネート成分の衝撃強さ、スチレンターポリマー成分の剛性及び良好なモジュラ ス、並びにポリカーボネート成分及びターポリマー成分双方の耐熱性を維持する のに十分な量で使用する。ブレンド成分の性質に悪影響を及ぼすことなくポリカ ーボネート成分とターポリマー成分との相容性を高めるためには、ＡＢＳ樹脂は 組成物の総重量を基準として２０重量％未満の量で使用すべきである。また、改 善をもたらすためには、ＡＢＳ樹脂は少なくとも約４重量％の量で使用すべきで ある。好適な態様においては、ＡＢＳ樹脂を約４乃至約１９重量％の量で使用す る。Furthermore, the blend composition of the present invention can optionally contain ABS resin. . If included, ABS resin is a polycarbonate component and a styrene terpolymer. improves the compatibility between the components, so that the resulting blend composition Impact strength of the bonate component, stiffness and good modularity of the styrene terpolymer component maintains heat resistance of both polycarbonate and terpolymer components. Use in sufficient quantity. polycarbonate without adversely affecting the properties of the blend ingredients. - In order to increase the compatibility between the carbonate component and the terpolymer component, ABS resin It should be used in an amount of less than 20% by weight based on the total weight of the composition. Also, the revision To provide good results, ABS resin should be used in an amount of at least about 4% by weight. be. In a preferred embodiment, ABS resin is used in an amount of about 4 to about 19% by weight. Ru.

ＡＢＳ樹脂は、ジエンゴム基体に剛性グラフトポリマーをグラフトさせて成る。ABS resins consist of a diene rubber substrate grafted with a rigid graft polymer.

好適な態様においては、剛性グラフトポリマーはスチレンとアクリロニトリルと から形成され、そしてジエンゴム基体はポリブタジェンから成る。しかし、当業 界で周知である様に、剛性ポリマーを、スチレンに代るモノビニリデン芳香族単 量体及びアクリロニトリルに代るアクリル酸エステル又はメタクリル酸エステル 単量体から形成したＡＢＳ樹脂を使用することも、十分に本発明の範囲内である 。更に、ＡＢＳ樹脂は、当業界で周知である様に、ポリブタジェン以外のジエン ゴムを含むことができる。本発明において、ＡＢＳ樹脂成分に言及するときは、 こうした等価のポリマーも包含する。しかし、ポリブタジェンにスチレンとアク リロニトリルとから成る剛性グラフトポリマーをグラフトさせたＡＢＳ樹脂が好 適なＡＢＳ樹脂であることに留意されたい。この好適な態様において、更に、グ ラフト部分に含まれるスチレンの量がアクリロニトリルの量以上となる様にＡＢ Ｓ樹脂の剛性グラフト部分のスチレンのアクリロニトリルに対する重量比が約１ ．１乃至約５：１の範囲内であることが好ましい。ＡＢＳ樹脂成分は、同様に当 業界で周知の方法により製造することができる。当業界で公知である様に、ＡＢ Ｓの製造方法により、ＡＢＳのグラフト共重合体と非グラフトスチレン−アクリ ロニトリル共重合体との混合物から成る生成物を得る可能性がある。これらの混 合物も、本発明において使用するのに適切である。In a preferred embodiment, the rigid graft polymer comprises styrene and acrylonitrile. and the diene rubber substrate consists of polybutadiene. However, those skilled in the art As is well known in the art, rigid polymers can be used to replace styrene with monovinylidene aromatic monomers. acrylic acid ester or methacrylic acid ester in place of polymer and acrylonitrile It is also well within the scope of this invention to use ABS resins formed from monomers. . Additionally, ABS resins may contain dienes other than polybutadiene, as is well known in the art. May contain rubber. In the present invention, when referring to the ABS resin component, Such equivalent polymers are also included. However, polybutadiene and styrene ABS resin grafted with a rigid graft polymer consisting of rylonitrile is preferred. Note that ABS resin is suitable. In this preferred embodiment, the group further includes: AB so that the amount of styrene contained in the raft part is greater than the amount of acrylonitrile. The weight ratio of styrene to acrylonitrile in the rigid graft portion of S resin is approximately 1. ．． Preferably, the ratio is within the range of 1 to about 5:1. The ABS resin component is also the same. It can be manufactured by methods well known in the industry. As is known in the art, AB According to the manufacturing method of S, a graft copolymer of ABS and a non-grafted styrene-acrylic It is possible to obtain products consisting of mixtures with lonitrile copolymers. These mixtures Compounds are also suitable for use in the present invention.

ＡＢＳ樹脂は、ポリカーボネート成分とターポリマー成分との間のブレンド相客 化を成し遂げるために、少なくとも３０重量％、好ましくは少なくとも５０重量 ％のジエンゴム基体を含有する必要がある。好適な態様においては、ＡＢＳ樹脂 は約５０乃至約７５重量％、更に好ましくは約６０乃至約７０重量％のジエンゴ ム基体を含む。ABS resin is a blend between a polycarbonate component and a terpolymer component. at least 30% by weight, preferably at least 50% by weight to achieve % of diene rubber substrate. In a preferred embodiment, ABS resin is about 50 to about 75% by weight, more preferably about 60 to about 70% by weight of diengo. including the base material.

本発明のブレンド組成物は、例えば単軸及び二軸押出機、混合ロール及び内部ミ キサー等を包含する従来からの混合及び配合装置において製造することができる 。ブレンド組成物には、そのほかに、例えば配合剤、のり剤、安定剤、潤滑剤、 流動促進剤、防炎剤、離型剤、帯電防止剤等を包含する様々な従来からの添加剤 を含ませることができる。The blend compositions of the invention can be used, for example, in single and twin screw extruders, mixing rolls and internal mills. Can be manufactured on conventional mixing and compounding equipment including mixers etc. . In addition, the blend composition may include, for example, compounding agents, adhesives, stabilizers, lubricants, A variety of conventional additives including glidants, flame retardants, mold release agents, antistatic agents, etc. can be included.

この種の添加剤の例が、米国特許第４．２８９．６６８号及び同４，４１４，３ ４２号各明細書に示されている。Examples of additives of this type are U.S. Pat. No. 4,289,668 and U.S. Pat. No. 42, each specification.

下記実施例により、本発明の具体的態様を説明する。特に断わらない限り、実施 例を通して示された百分率は重量百分率である。実施例において使用したポリカ ーボネート（ＰＣ）、スチレン−アクリロニトリル−無水マレイン酸ターポリマ ー（ＳＡＭＡ）　、ガラス繊維（ＧＦ）及びＡＢＳ樹脂を以下に説明する。The following examples illustrate specific embodiments of the present invention. Implemented unless otherwise specified The percentages given throughout the examples are weight percentages. Polycarbonate used in the example carbonate (PC), styrene-acrylonitrile-maleic anhydride terpolymer - (SAMA), glass fiber (GF) and ABS resin will be explained below.

ＰＣ−１＋　モーベイ・ケミカル・カンバニイからＭ−５０の表示で入手したポ リカーボネート、ＰＣ−２：　ゼネラル・エレクトリック・カンパニイから登録 商標レキサンの商品名で入手したポリカーボネート、 ＳＡＭＡ−１：　このターポリマーは、約２１乃至２２重量％の無水マＬツイン 酸を含み、４そして単一反応器内で定常状態条件下で製造された。使用した供給 ％は、スチレン８１重量％、アクリロニトリル約９％、そして無水マレイン酸約 １０乃至１１％であった。単量体のポリマーへの転化率が約５０％であり、その 時点で得られた湯境を真空押出機に連続的にポンプ送給し、そこで未反応スチレ ン及びアクリロニトリルを除去し反応器に再循環させた。ターポリマーは、示差 走査熱量測定（Ｄ　Ｓ　Ｃ）分析法を用いて１０４乃至１０８℃でのＴｇが不在 であることで示された様に、スチレン−アクリロニトリル共重合体を殆ど又は全 く含まなかった、 ＳＡＭＡ−２：　このターポリマーは、約１０乃至１１重量％の無水マレイン酸 を含み、そして二反応器系内でＳＡＭＡ−１の製造法で説明した生成湯境を第２ の反応器に導き、そこで未反応スチレン及びアクリロニトリルを更に重合させて 製造した。このターポリマーは、ＤＳＣ分析により現われた２つのＴｇで示され た様に、約５０重量％までのスチレン−アクリロニトリル共重合体を含んでいた 、 ＧＦ−１：　オーインゲス−コーニング・ファイバーガラス社から０ＣＦ４０８ の表示で入手した、３／１６インチの平均長さを有するガラス繊維（切断ストラ ンド）、ＧＦ−２ニ　オーインゲス−コーニング・ファイノ（−ガラス社から０ ＣＦ４９７の表示で入手した、１／８インチの平均長さを有するガラス繊維（切 断ストランド）、ＡＢＳ：　このＡＢＳ樹脂は、５０重量％のポリブタジェン基 体と該基体にグラフトした５０重量％のスチレン−アクリロニトリル共重合体と から成っていた。グラフト共重合体中でのスチレンのアクリロニトリルに対する 重量比は３：１であった。PC-1+ A port obtained from Mobay Chemical Company with the designation M-50. Recarbonate, PC-2: Registered from General Electric Company Polycarbonate obtained under the trademark Lexan trade name, SAMA-1: This terpolymer contains about 21 to 22% by weight of anhydrous polymer. 4 and was produced under steady-state conditions in a single reactor. supply used % is 81% by weight of styrene, approximately 9% of acrylonitrile, and approximately 9% of maleic anhydride. It was 10 to 11%. The conversion rate of monomer to polymer is about 50%; The resulting hot water was continuously pumped into a vacuum extruder where unreacted styrene was removed. and acrylonitrile were removed and recycled to the reactor. Terpolymer is a differential Absence of Tg at 104-108°C using scanning calorimetry (DSC) analysis method As shown, most or all of the styrene-acrylonitrile copolymer It didn't include much, SAMA-2: This terpolymer contains approximately 10-11% by weight maleic anhydride. and in a two-reactor system, the production bath described in the SAMA-1 production process was added to the second reactor system. reactor, where unreacted styrene and acrylonitrile are further polymerized. Manufactured. This terpolymer was shown to have two Tg's revealed by DSC analysis. contained up to about 50% by weight of styrene-acrylonitrile copolymer. , GF-1: 0CF408 from Ohinges-Corning Fiberglass Company Glass fibers (cut struts) with an average length of 3/16 inch obtained under the designation ), GF-2 Ni Oinges-Corning Faino (-0 from Glass Company) Glass fiber (cut) having an average length of 1/8 inch obtained under the designation CF497. ABS: This ABS resin contains 50% by weight of polybutadiene groups. 50% by weight of styrene-acrylonitrile copolymer grafted onto the substrate; It consisted of Styrene versus acrylonitrile in graft copolymers The weight ratio was 3:1.

実施例１ 本実施例において、３０重量％のＰＣ−１，４０重量％のＳＡＭＡ−１及び３０ 重量％のＧＦ−１から成る本発明の組成物を製造した。本実施例及び以下の実施 例において、低圧縮スクリュウを備えた単軸押出機を用いてブレンド操作を行な い、そして得られたブレンドをペレット化し、そして試験片へと成形した。更に 、本実施例及び以下の実施例において、ＡＳＴＭ−Ｄ−２５６（方法Ｅに準拠し た逆ノツチ付衝撃強さ）に準拠して衝撃強さを測定し、ＡＳＴＭ−Ｄ６４８に準 拠し、アニールしてない射出成形試料を用いて２６５ｐｓ　ｉで熱変形を測定し 、そしてＡＳＴＭ−Ｄ６３８に準拠して強さ及びモジュラスを測定した。本実施 例の組成物は、室温で３，７フート・ボンド／インチの逆ノツチ衝撃強さ、２７ ７″Ｆの熱変形温度（１／８インチ試料）、２６，４００ｐｓｉの曲げ強さ及び １６．０Ｘ１０５ｐｓｉの曲げモジュラスを示した。この様に、組成物は良好な 物理的性質の組合せを発揮した。Example 1 In this example, 30% by weight of PC-1, 40% by weight of SAMA-1 and 30% by weight of A composition of the invention was prepared consisting of % GF-1 by weight. This example and the following implementation In the example, the blending operation is performed using a single screw extruder with a low compression screw. The resulting blend was then pelletized and formed into test specimens. Furthermore , in this and the following examples, according to ASTM-D-256 (Method E). Impact strength was measured in accordance with ASTM-D648. Accordingly, thermal deformation was measured at 265 ps i using an unannealed injection molded sample. , and strength and modulus were measured according to ASTM-D638. Main implementation The example composition has a reverse notched impact strength of 3.7 foot bonds/inch at room temperature, 27 7″F heat distortion temperature (1/8″ sample), 26,400 psi bending strength and It exhibited a flexural modulus of 16.0 x 105 psi. In this way, the composition has a good Exhibited a combination of physical properties.

実施例２ 本実施例において、ＰＣ−１、ＳＡＭＡ−２、及びＧＦ−１又はＧＦ−２から成 る組成物を製造した。これら成分の重量％を、下記表１に示した様に変動させた 。これらの組成物を、同様に逆ノツチ衝撃強さ、熱変形温度、引張強さ及びモジ ュラス、並びに曲げ強さ及びモジュラスの測定に付し、その結果を同様に表１に 示した。Example 2 In this example, the PC-1, SAMA-2, and GF-1 or GF-2 are A composition was prepared. The weight percentages of these components were varied as shown in Table 1 below. . These compositions were similarly tested for reverse notch impact strength, heat distortion temperature, tensile strength and modulus. The results are also shown in Table 1. Indicated.

表　１ ＰＣ−１６５５５２２，５９−−− ３ＡＭＡ−２２５３５６７，５８１９０衝撃強さ、室温、　６．０５゜３　２， ４　２．４　２．３１／８インチ　２６６　２５５　２４１　２３６　２３５１ ／４インチ　２５９　２５５　２４２　２４２　２３６引張強さ、ｐｓｊ　１２ ７００　１２７００　１０６００　９１００　９９００引張モジユラス、　６． ４　６．８　８．３　８．２　８．５ｐｓｉｘｌｏ５ 曲げ強さ、ｐａｔ　１９８００　１９７００　１６７００　１４６００　１３８ ００曲げモジュラス、　６．７　７．０　７．９　８．１　８．１．５ ｐａｔＸ１０ 表１から明らかな様に、組成物２Ａ乃至２Ｄは本発明によるものであり、一方組 成物２Ｅはポリカーボネートを含まない比較組成物である。表１に示した本発明 組成物の物理的性質により、２２．５重量％のポリカーボネート、６７．５重量 ％のターポリマー及び１０重量％のガラス繊維を含む組成物２Ｃが、とりわけ優 れた物理的性質測定値の組合せ、とりわけ熱変形温度、並びに引張及び曲げの強 さ更に本実施例により、ＰＣ−１，ＳＡＭＡ−２、及びＧＦ−１又はＧＦ−２か ら成る本発明組成物を例示する。成分の重量％を表２に示した様に変動させた。Table 1 PC-1655522,59--- 3AMA-2253567, 58190 impact strength, room temperature, 6.05°3 2, 4 2.4 2.31/8 inch 266 255 241 236 2351 /4 inch 259 255 242 242 236 Tensile strength, psj 12 700　12700　10600　9100　9900 Tensile modulus, 6. 4 6.8 8.3 8.2 8.5psixlo5 Bending strength, pat 19800 19700 16700 14600 138 00 bending modulus, 6.7 7.0 7.9 8.1 8.1.5 patX10 As is clear from Table 1, compositions 2A to 2D are according to the present invention; Composition 2E is a comparative composition that does not contain polycarbonate. The present invention shown in Table 1 Due to the physical properties of the composition, 22.5% polycarbonate by weight, 67.5% by weight Composition 2C containing 10% terpolymer and 10% glass fibers is particularly advantageous. combination of measured physical properties, in particular heat distortion temperature, and tensile and bending strength. Furthermore, according to this embodiment, PC-1, SAMA-2, and GF-1 or GF-2 The following is an example of a composition of the present invention consisting of: The weight percentages of the ingredients were varied as shown in Table 2.

得られた組成物を、逆ノツチ衝撃強さ、熱変形温度、並びに引張及び曲げの強さ 及びモジュラスの測定に付し、それらの結果を同様に表２に示した。The resulting composition was tested for reverse notch impact strength, heat distortion temperature, and tensile and bending strength. The results were also shown in Table 2.

表　２ ＰＣ−１６５５５４５２０８−−− ８ＡＭＡ−２１５２５３５６０７２８０衝撃強さ、室温、　５．７　５．９　５ ．１　４．０　２．９３，７フ一トｌｉノド／インチ 脚へＪ【万５醒、１： １／８インチ　２８０　２７０　２５７　２５２　２４４　２３９１／４インチ 　２７３　２６６　２５４　２５０　２４２　２４０引張強さ、ｐｓｉ　１３４ ００　１５２００　１４９００　１４７００　１３８００　１３８００引張モジ ユラス、　８，５　１０．２　９，７　１１．７　１１．６　１１．５ｐｓｉＸ １０５ 曲げ強さ、ｐｓｉ　２００００　２１９００　２２０００　２０８００　１９６ ００　１９３００曲げモジュラス、　８．７　９．５　９，４　１２．０　１２ ．０　１２．０ｐｓｉＸ１０ 表２中に記載した組成から明らかな様に、組成物３Ａ乃至３Ｅは本発明によるも のであり、そして優れた性質を示し、一方組成物３Ｆはポリカーボネートを含ま ない比較組成物である。また、本発明組成物３Ｄが熱変形温度、並びに引張及び 曲げの強さ及びモジュラスを含む格別に優れた物理的性質の組合せを発揮した。Table 2 PC-1655545208--- 8AMA-2152535607280 Impact strength, room temperature, 5.7 5.9 5 ．． 1 4.0 2.93,7 feet / inch J to leg [man5 awakening, 1: 1/8 inch 280 270 257 252 244 239 1/4 inch 273 266 254 250 242 240 Tensile strength, psi 134 00 15200 14900 14700 13800 13800 Tensile Moji Yuras, 8,5 10.2 9,7 11.7 11.6 11.5psiX 105 Bending strength, psi 20000 21900 22000 20800 196 00 19300 bending modulus, 8.7 9.5 9,4 12.0 12 ．． 0 12.0psiX10 As is clear from the compositions listed in Table 2, compositions 3A to 3E are according to the present invention. and exhibits excellent properties, while Composition 3F contains polycarbonate. There is no comparative composition. In addition, the composition 3D of the present invention has a heat deformation temperature, tensile strength and It exhibited an exceptional combination of physical properties including flexural strength and modulus.

実施例４ 本実施例により、更にＡＢＳをも含む本発明組成物を説明する。詳しくは、これ らの組成物は表３に示した量のＰＣ−１、ＳＡＭＡ−２、ＧＦ−１及びＡＢＳか ら成っていた。得られた組成物を、逆ノツチ衝撃強さ、熱変形温度、並びに引張 及び曲げの強さ及びモジュラスの測定に付し、それらの結果を同様に表３に示し た。Example 4 This example illustrates a composition of the invention that also includes ABS. For details, see this Their composition contains PC-1, SAMA-2, GF-1 and ABS in the amounts shown in Table 3. It consisted of The resulting composition was tested for reverse notch impact strength, heat distortion temperature, and tensile strength. And the bending strength and modulus were measured, and the results are also shown in Table 3. Ta.

表　３ ＰＣ−１４，５１３，５１８４１２１６ＳＡＭＡ−２７６，５７２，０６３６８ ６４５６ＧＦ−１１０１０１０２０２０２０ ＡＢＳ　９．０４．５　９　８　４　８衝撃強さ、室温、　３．４　２．８　４ ．３　３．９　３．８　４．１熱変形温度、丁 １／８インチ　２３７　２３７　２３９　２４３　２４４　２４４１／４インチ 　２３４　２４０　２４０　２４１　２４７　２４１引張強さ、ｐｓｊ　１１０ ００　１０５００　１２９００　１５０００　１５２００　１６２００引張モジ ユラス、　７．８　７．７　７，５　１１．０　１１．３　１０．８ｐｓｉＸ１ ０５ 曲げ強さ、Ｉ）ｓｉ　１７９００　１６６００　１９５００　２３８００　２３ ２００　２４４００曲げモジュラス、　７．５　７．７　？、０　１０．０　１ ２．０　１１．０ｐｓｉｘ１０５ 概して、２０重量％のガラス繊維を含む組成物４Ｄ乃至４Ｆが１０重量％のガラ ス繊維を含む組成物４Ａ乃至４Ｃと比べて改良された性質を示した。また、組成 物４Ｃ及び４Ｆが好適な量のポリカーボネート成分を含んでいた。Table 3 PC-14,513,51841216SAMA-276,572,06368 6456GF-1101010202020 ABS 9.04.5 9 8 4 8 Impact strength, room temperature, 3.4 2.8 4 ．． 3 3.9 3.8 4.1 Heat distortion temperature, 1/8 inch 237 237 239 243 244 244 1/4 inch 234 240 240 241 247 241 Tensile strength, psj 110 00 10500 12900 15000 15200 16200 Tensile Moji Yuras, 7.8 7.7 7.5 11.0 11.3 10.8psiX1 05 Bending strength, I) si 17900 16600 19500 23800 23 200 24400 bending modulus, 7.5 7.7? , 0 10.0 1 2.0 11.0psix105 Generally, compositions 4D to 4F containing 20% by weight glass fibers contain 10% by weight glass fibers. It showed improved properties compared to compositions 4A to 4C containing fibers. Also, the composition Products 4C and 4F contained suitable amounts of polycarbonate components.

実施例５ 本実施例により、前記の好適な範囲のポリカーボネート、ターポリマー及びガラ ス繊維を含む本発明のブレンド組成物を例示する。これらの組成物のいくつかは 、他に必要に応じてＡＢＳ樹脂成分をも含んでいた。組成の重量％を表４に示し た。これらの組成物を、逆ノツチ付及びノツチなし衝撃強さ、熱変形温度、並び に引張及び曲げの強さ及びモジュラスの測定に付し、それらの結果を同様に表４ に示した。Example 5 According to this example, the preferred ranges of polycarbonate, terpolymer and glass 1 illustrates a blend composition of the present invention containing fibers. Some of these compositions are In addition, it also contained an ABS resin component as required. The weight percent of the composition is shown in Table 4. Ta. These compositions were tested for reverse notched and unnotched impact strength, heat distortion temperature, and were subjected to tensile and bending strength and modulus measurements, and the results are also shown in Table 4. It was shown to.

表　４ ＰＣ−２１５３０１５２０１０ ＳＡ１０５Ａ　５７．５　６５　５５　５５７７．５ＧＦ−１１７，５１５１５ １５１２，５ＡＢＳ　１０−１５　１０− 衝撃強さ、室温、 フートポンＦ／イ／チ 逆ノツチ付　４．３　４．６　５．０　４．８　２．０ノツチなし　６．　７　 ５．　１　６．　７　７．　４　１．　９熱変形温度、Ｔ １／８インチ　２３６　２３９　２３２　２３８　２３６引張強さ、ｐｓｉ　１ ３６００　１１６００　１２９００　１３６００　７９００引張モジユラス、　 ９．１　８．２　７．５　７．９　８．０、５ ５ｌｘｌＯ 曲げ強さ、ｐｓｉ　１９３６０　１５８００　１７９５０　１９４００　１０９ ００曲げモジュラス、　８．８　８．７　７．７　Ｂ、２　８．３ｐｓｉｘ１０ 組成物５Ｂ及び５Ｅにより、ブレンド中のポリカーボネート含量の増加により引 張及び曲げ強さが増大することが示された。組成物５Ｃ及び５Ｄにより、ＡＢＳ 樹脂量変動の影響が示された。最後に、組成物５Ａ及び５Ｅにより、ガラス量増 加の組成物のモジュラス及び強さへの影響が示本実施例により多量のガラス繊維 を含む本発明のブレンド組成物を例示する。詳しくは、これらの組成物はＰＣ− ２、ＳＡＭＡ−２、ＧＦ−１及び必要に応じてＡＢＳから成っていた。これらの 組成物に含まれる成分の重量％を表５に示した。これらの組成物を、逆ノツチ及 びノツチなし衝撃強さ、熱変形温度、並びに引張及び曲げの強さ及びモジュラス の測定に付し、それらの結果を同様に表５に示した。Table 4 PC-21530152010 SA105A 57.5 65 55 5577.5GF-117, 51515 1512,5ABS 10-15 10- impact strength, room temperature, Footpon F/I/C With reverse notch 4.3 4.6 5.0 4.8 2.0 without notch 6. 7 5. 1 6. 7 7. 4 1. 9 Heat distortion temperature, T 1/8 inch 236 239 232 238 236 Tensile strength, psi 1 3600　11600　12900　13600　7900 Tensile modulus, 9.1 8.2 7.5 7.9 8.0, 5 5lxlO Bending strength, psi 19360 15800 17950 19400 109 00 bending modulus, 8.8 8.7 7.7 B, 2 8.3 psi x 10 Compositions 5B and 5E showed increased polycarbonate content in the blend. It was shown that the tensile and flexural strength increased. With compositions 5C and 5D, ABS The influence of resin amount variation was shown. Finally, compositions 5A and 5E increase the amount of glass. This example shows the effect of addition on the modulus and strength of the composition. The blend composition of the present invention comprising: Specifically, these compositions are PC- 2, SAMA-2, GF-1 and optionally ABS. these Table 5 shows the weight percent of the components contained in the composition. These compositions are Unnotched impact strength, heat distortion temperature, and tensile and bending strength and modulus The results are also shown in Table 5.

表５に示した結果により、これらの組成物が非常に良好な強さ及びモジュラス特 性、並びに良好な熱変形温度及び衝撃強さを示したことが分る。The results shown in Table 5 demonstrate that these compositions have very good strength and modulus properties. It can be seen that the material exhibited good properties, as well as good heat distortion temperature and impact strength.

以上の実施例は本発明の特定の態様を例証するために示したものであり、本発明 組成物の範囲を減縮することを意図したものではない。当業者には、本発明範囲 内の他の態様及び利点が明らかである。The foregoing examples are presented to illustrate specific embodiments of the invention and are It is not intended to limit the scope of the composition. Those skilled in the art will understand the scope of the invention Other aspects and advantages within are apparent.

国際調査報告international search report

Claims (16)

【特許請求の範囲】[Claims] １．（ａ）ポリカーボネート、 （ｂ）スチレン−アクリロニトリル−無水マレイン酸ターポリマー及び （ｃ）ポリカーボネート、ターポリマー及びガラス繊維を基準として約５乃至約 ４０重量％の量のガラス繊維を含むポリマーブレンド組成物。1. (a) polycarbonate, (b) styrene-acrylonitrile-maleic anhydride terpolymer and (c) from about 5 to about 50% based on polycarbonate, terpolymers, and glass fibers; Polymer blend composition containing glass fibers in an amount of 40% by weight. ２．ポリカーボネート、ターポリマー及びガラス繊維を基準として約１５乃至約 ６５重量％のポリカーボネートを含む請求項１記載のポリマーブレンド組成物。2. Based on polycarbonate, terpolymers and glass fibers from about 15 to about The polymer blend composition of claim 1 comprising 65% by weight polycarbonate. ３．ポリカーボネート、ターポリマー及びガラス繊維を基準として約２０乃至約 ３５重量％のポリカーボネートを含む請求項２記載のポリマーブレンド組成物。3. Based on polycarbonate, terpolymers and glass fibers, from about 20 to about 3. The polymer blend composition of claim 2 comprising 35% by weight polycarbonate. ４．ポリカーボネート、ターポリマー及びガラス繊維を基準として約１０乃至約 ８０重量％のターポリマーを含む請求項１記載のポリマーブレンド組成物。4. Based on polycarbonate, terpolymers and glass fibers, from about 10 to about The polymer blend composition of claim 1 comprising 80% by weight terpolymer. ５．ポリカーボネート、ターポリマー及びガラス繊維を基準として約３５乃至約 ７５重量％のターポリマーを含む請求項４記載のポリマーブレンド組成物。5. Based on polycarbonate, terpolymers and glass fibers from about 35 to about 5. The polymer blend composition of claim 4 comprising 75% by weight terpolymer. ６．ポリカーボネートが芳香族ホモポリカーボネート又は芳香族コポリカーボネ ートから成る請求項１記載のポリマーブレンド組成物。6. Polycarbonate is aromatic homopolycarbonate or aromatic copolycarbonate 2. The polymer blend composition of claim 1, comprising: ７．ポリカーボネートがビスフェノールＡの誘導体である請求項６記載のポリマ ーブレンド組成物。7. 7. The polymer according to claim 6, wherein the polycarbonate is a derivative of bisphenol A. -Blend composition. ８．ターポリマーが約４乃至約２５重量％の無水マレイン酸を含む請求項１記載 のポリマーブレンド組成物。8. Claim 1, wherein the terpolymer contains from about 4 to about 25 weight percent maleic anhydride. polymer blend composition. ９．ターポリマーが約５乃至約２０重量％のアクリロニトリルを含む請求項８記 載のポリマーブレンド組成物。9. 9. The terpolymer comprises from about 5 to about 20% by weight acrylonitrile. The polymer blend compositions described above. １０．ターポリマーがスチレン−アクリロニトリル共重合体を含む請求項１記載 のポリマーブレンド組成物。10. Claim 1, wherein the terpolymer comprises a styrene-acrylonitrile copolymer. polymer blend composition. １１．ガラス繊維が約０．０５乃至約０．５インチの平均長さを有する請求項１ 記載のポリマーブレンド組成物。11. Claim 1: The glass fibers have an average length of about 0.05 to about 0.5 inches. Polymer blend compositions as described. １２．更に、ポリカーボネートとターポリマーとの相容性を改良するのに十分な 量のＡＢＳ樹脂を含む請求項１記載のポリマーブレンド組成物。12. In addition, sufficient The polymer blend composition of claim 1, comprising an amount of ABS resin. １３．ＡＢＳ樹脂が組成物の２０重量％未満の量で含まれる請求項１２記載のポ リマーブレンド組成物。13. 13. The polymer according to claim 12, wherein the ABS resin is present in an amount less than 20% by weight of the composition. Rimmer blend composition. １４．ＡＢＳ樹脂が約４乃至約１９重量％の量で含まれる請求項１３記載のポリ マーブレンド組成物。14. 14. The polyester of claim 13, wherein the ABS resin is present in an amount of about 4 to about 19% by weight. Merblend composition. １５．ＡＢＳ樹脂が少なくとも約３０重量％のジエンゴム基体を含む請求項１２ 記載のポリマーブレンド組成物。15. 12. The ABS resin comprises at least about 30% by weight diene rubber substrate. Polymer blend compositions as described. １６．ＡＢＳ樹脂が約５０乃至約７５重量％のジエンゴム基体を含む請求項１５ 記載のポリマーブレンド組成物。16. Claim 15 wherein the ABS resin comprises about 50 to about 75 weight percent diene rubber substrate. Polymer blend compositions as described.