JPH0441833A - Joint material - Google Patents
Joint materialInfo
- Publication number
- JPH0441833A JPH0441833A JP14953590A JP14953590A JPH0441833A JP H0441833 A JPH0441833 A JP H0441833A JP 14953590 A JP14953590 A JP 14953590A JP 14953590 A JP14953590 A JP 14953590A JP H0441833 A JPH0441833 A JP H0441833A
- Authority
- JP
- Japan
- Prior art keywords
- joint
- joint material
- weight
- calcium carbonate
- cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【発明の詳細な説明】
［産業上の利用分野コ
本発明はタイルの目地間隙に充填される目地材料に係り
、特にカビ等の汚れを簡単に除去できる目地材料に関す
る。DETAILED DESCRIPTION OF THE INVENTION [Field of Industrial Application] The present invention relates to a joint material that is filled into the joint gaps of tiles, and more particularly to a joint material that can easily remove stains such as mold.
［従来の技術〕
内装タイル同志の間隙に充填された目地には、カビが発
生し易い。特に浴室、洗面所等の湿度の高い雰囲気にさ
らされるタイル壁面の目地では、短期間でカビが発生し
、不衛生となるだけでなく、壁面の美観を著しく損ねる
。[Prior Art] Mold is likely to grow in the joints filled in the gaps between interior tiles. Particularly in the joints of tile walls that are exposed to a high humidity atmosphere, such as in bathrooms and washrooms, mold grows in a short period of time, which not only becomes unsanitary, but also significantly impairs the aesthetic appearance of the walls.
従来、このような目地のカビ対策としては、■ 目地材
に防カビ剤を入れて、カビ発生を防止する。Conventionally, measures against mold in such joints include: (1) Adding a fungicide to the joint material to prevent mold growth.
■ 目地材を着色してカラー目地材として、カビ゛を目
立たなくする。■ Color the joint material and use it as a colored joint material to make mold less noticeable.
などの方法が採用されている。methods have been adopted.
［発明が解決しようとするｔ！０１
上記従来の方法のうち、■のカラー目地材では、カビの
根本的な防止はできず、カビ発生の問題は解決されない
。■の防カビ剤を入れた目地材であれば、防カビ剤の防
カビ効果によりカビ発生を防止することができるが、目
地材中に混入された防カビ剤は経時的に失効し、通常２
年位で防カビ効果が失われる。このため、それ以降は防
カビ剤を含有しない目−地材と同様にカビが発生し易く
なるという欠点がある。[The invention attempts to solve the problem! 01 Among the conventional methods described above, the colored joint material (3) cannot fundamentally prevent mold and does not solve the problem of mold growth. If the joint material contains a moldproofing agent, it is possible to prevent mold growth due to the moldproofing effect of the moldproofing agent, but the moldproofing agent mixed in the jointing material expires over time, and usually 2
The antifungal effect is lost over the years. For this reason, there is a drawback that mold is likely to grow thereafter, similar to joint materials that do not contain a fungicide.
［課題を解決するための手段］
本発明の目地材料は、タイルの目地間隙に充填される目
地材料において、炭酸カルシウムを内割りで１０〜４０
重量％含有することを特徴とするものである。[Means for Solving the Problems] The joint material of the present invention is a joint material that is filled into the joint gaps of tiles, and contains calcium carbonate in an amount of 10 to 40%.
It is characterized by containing % by weight.
以下に本発明の詳細な説明する。The present invention will be explained in detail below.
本発明において、目地材料はセメント特に白色セメント
を硬化成分として含み、ケイ砂と炭酸カルシウムを加え
た細骨材をセメント１００重量部に対し３０〜７０重量
部含むものが好ましい。カラー目地材料とするには、更
に、適宜の顔料を含有させる。In the present invention, the joint material preferably contains cement, particularly white cement, as a hardening component, and 30 to 70 parts by weight of fine aggregate to which silica sand and calcium carbonate are added per 100 parts by weight of cement. In order to make it into a colored joint material, an appropriate pigment is further included.
本発明において、目地材料中の炭酸カルシウムの含有量
は内割りで１０〜４０重量％であるが、好ましくは３０
重量％以下、とりわけ２０〜２５重量％程度であること
が望ましい。炭酸カルシウム含有量は少な過ぎると本発
明による十分な改善効果が得られず、多過ぎると表面が
削りとられすぎて目地がなくなってしまう、また、炭酸
カルシウムは２５μｍ以下、とりわけ５μｍ以下の粉末
として配合するのが良い。In the present invention, the content of calcium carbonate in the joint material is 10 to 40% by weight, preferably 30% by weight.
It is desirable that the amount is less than 20% by weight, particularly about 20 to 25% by weight. If the calcium carbonate content is too low, the sufficient improvement effect of the present invention cannot be obtained, and if it is too high, the surface will be scraped off too much and the joints will disappear. It is good to mix.
なお、従来より目地に防カビ剤を含有させておくことに
より目地のカビ発生を防止することが行なわれているが
、本発明においても目地材料に防カビ剤を含有させても
良い。Incidentally, although it has been conventionally done to prevent the growth of mold in the joints by containing a moldproofing agent in the joints, the joint material may also contain a moldproofing agent in the present invention.
［作用］
かかる本発明の目地材料を目地間隙に充填して施工され
たタイル壁において、目地にカビが発生したときには薄
い酸溶液（塩酸など可溶性炭酸塩を生じさせる酸の溶液
）で目地を洗う。そうすると、目地の表面が少量だけ溶
解し、即ち、目地中の炭酸カルシウムが可溶性炭酸塩と
なフて溶出し、それに伴なって、表面に付着したカビ等
の汚れ成分が除去される。[Function] When mold occurs in the joints of a tile wall constructed by filling the joint gaps of the present invention with the joint material of the present invention, the joints are washed with a dilute acid solution (a solution of an acid that produces soluble carbonates, such as hydrochloric acid). . As a result, only a small amount of the surface of the joint is dissolved, that is, the calcium carbonate in the joint becomes soluble carbonate and is eluted, and accordingly, stain components such as mold attached to the surface are removed.
なお、本発明において、目地の洗浄に用い゛る酸溶液と
しては、１〜３％程度の塩酸等の弱酸水溶液が好適であ
る。In the present invention, as the acid solution used for cleaning the joints, a weak acid aqueous solution such as about 1 to 3% hydrochloric acid is suitable.
［実施例］
以下に実施例を挙げて、本発明をより具体的に説明する
。[Example] The present invention will be described in more detail with reference to Examples below.
実施例１
下記配合物を混合することにより本発明の目地材料を製
造した。Example 1 A joint material of the present invention was produced by mixing the following formulations.
白色セメント；１００重量部
炭酸カルシウム：３５重量部
ケイ砂＝８重量部
なお、炭酸カルシウムは粒径２５μｍ以下の粉末であり
、ケイ砂は１．２ｍｍ以下の細粒を用いた。White cement: 100 parts by weight Calcium carbonate: 35 parts by weight Silica sand = 8 parts by weight Calcium carbonate was a powder with a particle size of 25 μm or less, and fine silica sand with a particle size of 1.2 mm or less was used.
この目地材料１００重量部に水を４０重量部添加して混
練した後、浴室内装タイル壁の目地に充填した。約１８
ケ月経過すると目地表面にカビが発生したので、雑布に
希塩酸（濃度１．５％）を浸し、目地を拭いた。軽く２
〜３回程度拭くことによりカビがほぼ完全に除去された
。After adding 40 parts by weight of water to 100 parts by weight of this joint material and kneading, the mixture was filled into the joints of a tile wall in a bathroom interior. about 18
After several months, mold had grown on the joint surface, so I soaked a cloth in dilute hydrochloric acid (concentration 1.5%) and wiped the joint. Lightly 2
The mold was almost completely removed by wiping it about three times.
［効果］
以上の通り、本発明の目地材料により形成された目地は
、弱酸溶液で拭くことにより極めて簡単にカビを除去で
き、目地を長期間、衛生的かつ美麗に保つことが可能と
される。[Effects] As described above, mold can be removed extremely easily from the joints formed using the joint material of the present invention by wiping with a weak acid solution, making it possible to keep the joints hygienic and beautiful for a long period of time. .
特許出願人 株式会社イナックスPatent applicant: Inax Co., Ltd.
Claims (1)
、炭酸カルシウムを１０〜４０重量％含有することを特
徴とする目地材料。(1) A joint material that is filled into the joint gaps of tiles and is characterized by containing 10 to 40% by weight of calcium carbonate.