JPH04328318A - 磁気記録媒体 - Google Patents
磁気記録媒体Info
- Publication number
- JPH04328318A JPH04328318A JP3099029A JP9902991A JPH04328318A JP H04328318 A JPH04328318 A JP H04328318A JP 3099029 A JP3099029 A JP 3099029A JP 9902991 A JP9902991 A JP 9902991A JP H04328318 A JPH04328318 A JP H04328318A
- Authority
- JP
- Japan
- Prior art keywords
- recording medium
- magnetic
- magnetic recording
- carbon black
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【0001】
【産業上の利用分野】本発明は磁気記録媒体に関する。
特に耐久性に優れた磁気記録媒体に関する。
【0002】
【従来の技術及び発明が解決しようとする課題】磁気記
録媒体の磁性層中には通常、カーボンブラックが含まれ
ている。カーボンブラックを用いる目的は、遮光性の付
与と帯電防止性能の付与である。また、粒径の異なる2
種類のカーボンブラックを併用してより良い潤滑性を付
与するという考え方もある。
録媒体の磁性層中には通常、カーボンブラックが含まれ
ている。カーボンブラックを用いる目的は、遮光性の付
与と帯電防止性能の付与である。また、粒径の異なる2
種類のカーボンブラックを併用してより良い潤滑性を付
与するという考え方もある。
【0003】しかしながら、カーボンブラックの選択と
磁気記録媒体の耐久性についての検討は充分になされて
いるとは言いがたい。そこで、本発明の目的はこの観点
からの検討を進め、耐久性に優れた磁気記録媒体を提供
することにある。
磁気記録媒体の耐久性についての検討は充分になされて
いるとは言いがたい。そこで、本発明の目的はこの観点
からの検討を進め、耐久性に優れた磁気記録媒体を提供
することにある。
【0004】
【課題を解決するための手段】本発明者らは上記の目的
を達成するために鋭意研究した結果、磁性塗料中に平均
粒径25〜130 nm、BET 比表面積30〜80
m2/g、且つ吸油量 300〜550 ml/100
gのカーボンブラックを配合することによって、磁性層
中にある程度磁性粉が集合するような構造が形成され、
そこに潤滑剤が適切に保持され、磁気記録媒体の耐久性
が向上することを見出し、本発明を完成するに至った。
を達成するために鋭意研究した結果、磁性塗料中に平均
粒径25〜130 nm、BET 比表面積30〜80
m2/g、且つ吸油量 300〜550 ml/100
gのカーボンブラックを配合することによって、磁性層
中にある程度磁性粉が集合するような構造が形成され、
そこに潤滑剤が適切に保持され、磁気記録媒体の耐久性
が向上することを見出し、本発明を完成するに至った。
【0005】すなわち本発明は、非磁性支持体上に磁性
粉と結合剤を主成分とする磁性層が設けられた磁気記録
媒体において、当該磁性層が平均粒径が25〜130
nm、BET 比表面積が30〜80m2/g、且つ吸
油量が 300〜550 ml/100 gであるカー
ボンブラックを含有することを特徴とする磁気記録媒体
を提供するものである。
粉と結合剤を主成分とする磁性層が設けられた磁気記録
媒体において、当該磁性層が平均粒径が25〜130
nm、BET 比表面積が30〜80m2/g、且つ吸
油量が 300〜550 ml/100 gであるカー
ボンブラックを含有することを特徴とする磁気記録媒体
を提供するものである。
【0006】本発明に係わるカーボンブラックを用いる
と、磁性層中にある程度磁性粉が集合するような構造が
形成され、そこに潤滑剤が適切に保持され、適度な表面
の粗さができて、低温でも高温でも磁気記録媒体の耐久
性の向上がみられるようになる。この場合、磁性粉が集
合するような構造が形成されるといってもそれによる電
磁変換特性の低下はない。通常磁気記録媒体に用いられ
るカーボンブラックは吸油量が50〜150 ml/1
00 g程度、多くても250ml /100 g程度
であるのに対し、本発明に係わるカーボンブラックは吸
油量が 300〜550 ml/100 gと非常に多
いのが特徴である。
と、磁性層中にある程度磁性粉が集合するような構造が
形成され、そこに潤滑剤が適切に保持され、適度な表面
の粗さができて、低温でも高温でも磁気記録媒体の耐久
性の向上がみられるようになる。この場合、磁性粉が集
合するような構造が形成されるといってもそれによる電
磁変換特性の低下はない。通常磁気記録媒体に用いられ
るカーボンブラックは吸油量が50〜150 ml/1
00 g程度、多くても250ml /100 g程度
であるのに対し、本発明に係わるカーボンブラックは吸
油量が 300〜550 ml/100 gと非常に多
いのが特徴である。
【0007】本発明に用いられるカーボンブラックは上
記物性を有するものであり、その使用量は磁性粉100
重量部に対して5〜12重量部が好ましい。
記物性を有するものであり、その使用量は磁性粉100
重量部に対して5〜12重量部が好ましい。
【0008】また、本発明に係わるカーボンブラック以
外に、遮光性、帯電防止性能、或いは潤滑性等の付与の
ために別のカーボンブラックを併用してもよい。
外に、遮光性、帯電防止性能、或いは潤滑性等の付与の
ために別のカーボンブラックを併用してもよい。
【0009】本発明に用いられる結合剤としては、極性
基を有するポリウレタン樹脂が好ましく、極性基として
はスルホン酸のアルカリ金属塩が好ましい。また、極性
基の濃度は 0.1〜1000当量/106 g、好ま
しくは1〜100 当量/106 gである。その他の
結合剤としては、ポリ塩化ビニル、塩化ビニル酢酸ビニ
ル共重合体、ポリアクリルニトリル、ニトリルゴム、エ
ポキシ樹脂、アルキッド樹脂、ポリアミド、ポリアクリ
ル酸エステル、ポリメタクリル酸エステル、ポリ酢酸ビ
ニル、ポリビニルブチラール、塩化ビニリデン、硝化綿
、マレイン酸変性塩化ビニル・酢酸ビニル共重合体、エ
チルセルロースなどが挙げられる。これらは単独で用い
ても、2種以上を混合して用いてもよい。結合剤の総使
用量は対磁性粉で15〜30重量%とするのが好ましい
。
基を有するポリウレタン樹脂が好ましく、極性基として
はスルホン酸のアルカリ金属塩が好ましい。また、極性
基の濃度は 0.1〜1000当量/106 g、好ま
しくは1〜100 当量/106 gである。その他の
結合剤としては、ポリ塩化ビニル、塩化ビニル酢酸ビニ
ル共重合体、ポリアクリルニトリル、ニトリルゴム、エ
ポキシ樹脂、アルキッド樹脂、ポリアミド、ポリアクリ
ル酸エステル、ポリメタクリル酸エステル、ポリ酢酸ビ
ニル、ポリビニルブチラール、塩化ビニリデン、硝化綿
、マレイン酸変性塩化ビニル・酢酸ビニル共重合体、エ
チルセルロースなどが挙げられる。これらは単独で用い
ても、2種以上を混合して用いてもよい。結合剤の総使
用量は対磁性粉で15〜30重量%とするのが好ましい
。
【0010】本発明に用いられる磁性粉としては針状形
の微細なγ−Fe2O3, Fe3O4, CrO2の
ような金属酸化物、またCo被着γ−Fe2O3, C
o ドープγ−Fe2O3 のような加工処理を施した
γ−Fe2O3 、鉄メタル粉等が挙げられる。これら
のうち鉄メタル粉、微小板状のバリウムフェライト及び
そのFe原子の一部がTi, Co, Zn, V,
Nb 等の1種又は2種以上で置換された磁性粉、Co
, Fe−Co, Fe−Ni等の金属又は合金の超微
粉は特に化学安定性が悪いから、この改良のためニッケ
ル、コバルト、チタン、ケイ素、アルミニウムなどを金
属原子、塩及び酸化物の形で少量加えたり表面処理され
たりすることがあるが、これらを用いることもできる。 鉄メタル粉は、またその安定化のため弱い酸化性雰囲気
の中で表面に薄い酸化被膜を作らせることがあるが、こ
のように処理されたメタル粉を用いることもできる。
の微細なγ−Fe2O3, Fe3O4, CrO2の
ような金属酸化物、またCo被着γ−Fe2O3, C
o ドープγ−Fe2O3 のような加工処理を施した
γ−Fe2O3 、鉄メタル粉等が挙げられる。これら
のうち鉄メタル粉、微小板状のバリウムフェライト及び
そのFe原子の一部がTi, Co, Zn, V,
Nb 等の1種又は2種以上で置換された磁性粉、Co
, Fe−Co, Fe−Ni等の金属又は合金の超微
粉は特に化学安定性が悪いから、この改良のためニッケ
ル、コバルト、チタン、ケイ素、アルミニウムなどを金
属原子、塩及び酸化物の形で少量加えたり表面処理され
たりすることがあるが、これらを用いることもできる。 鉄メタル粉は、またその安定化のため弱い酸化性雰囲気
の中で表面に薄い酸化被膜を作らせることがあるが、こ
のように処理されたメタル粉を用いることもできる。
【0011】また、本発明の磁気記録媒体を製造する際
に用いられる非磁性支持体としては、ポリエチレンテレ
フタレートのようなポリエステル;ポリエチレン、ポリ
プロピレン等のポリオレフィン; セルローストリアセ
テート、セルロースジアセテート等のセルロース誘導体
;ポリカーボネート;ポリ塩化ビニル;ポリイミド;芳
香族ポリアミド等のプラスチック;Al,Cu等の金属
;紙等が使用される。形態はフィルム、テープ、シート
、ディスク、カード、ドラム等いずれでもよい。また支
持体表面はコロナ放電、放射線、紫外線等で処理されて
いても、あるいは適当な樹脂でプレコートされていても
よい。
に用いられる非磁性支持体としては、ポリエチレンテレ
フタレートのようなポリエステル;ポリエチレン、ポリ
プロピレン等のポリオレフィン; セルローストリアセ
テート、セルロースジアセテート等のセルロース誘導体
;ポリカーボネート;ポリ塩化ビニル;ポリイミド;芳
香族ポリアミド等のプラスチック;Al,Cu等の金属
;紙等が使用される。形態はフィルム、テープ、シート
、ディスク、カード、ドラム等いずれでもよい。また支
持体表面はコロナ放電、放射線、紫外線等で処理されて
いても、あるいは適当な樹脂でプレコートされていても
よい。
【0012】本発明の磁気記録媒体の磁性層には上記の
成分の他、この分野で通常使用される添加剤として分散
剤、潤滑剤、研磨剤、防錆剤、防黴剤等が加えられても
良い。更に磁性層の硬度を調整するためにポリイソシア
ナート化合物等の硬化剤を用いることもできる。
成分の他、この分野で通常使用される添加剤として分散
剤、潤滑剤、研磨剤、防錆剤、防黴剤等が加えられても
良い。更に磁性層の硬度を調整するためにポリイソシア
ナート化合物等の硬化剤を用いることもできる。
【0013】
【実施例】以下実施例にて本発明を説明するが、本発明
はこれらの実施例に限定されるものではない。尚、例中
「部」「%」は特記しない限り重量基準である。
はこれらの実施例に限定されるものではない。尚、例中
「部」「%」は特記しない限り重量基準である。
【0014】実施例1
下記配合物を用いてフロッピーディスクを作製した。
【0015】
注)
1) 平均粒径38nm, BET 比表面積40m
2/g, 吸油量 500ml DBP/100 g(
ここで DBPはジブチルフタレートである。以下同様
。) 2) 平均粒径80nm, BET 比表面積35m
2/g, 吸油量 27ml DBP/100 g 上記配合物をボールミルで72時間混練後、硬化剤(日
本ポリウレタン工業製のコロネートL )6部を添加し
、磁性塗料を得て、これを厚さ75μm のポリエチレ
ンテレフタレートフィルム上に乾燥膜厚が 2.5μm
となるように塗布した。乾燥後カレンダー処理をし、
円盤状に打抜き、磁気ディスクを得た。これをケースに
入れてフロッピーディスクとした。
2/g, 吸油量 500ml DBP/100 g(
ここで DBPはジブチルフタレートである。以下同様
。) 2) 平均粒径80nm, BET 比表面積35m
2/g, 吸油量 27ml DBP/100 g 上記配合物をボールミルで72時間混練後、硬化剤(日
本ポリウレタン工業製のコロネートL )6部を添加し
、磁性塗料を得て、これを厚さ75μm のポリエチレ
ンテレフタレートフィルム上に乾燥膜厚が 2.5μm
となるように塗布した。乾燥後カレンダー処理をし、
円盤状に打抜き、磁気ディスクを得た。これをケースに
入れてフロッピーディスクとした。
【0016】このフロッピーディスクを駆動装置に入れ
、耐久性試験を行った。試験の環境は、5℃/20%→
25℃/80%→60℃/20%を24時間かけてサイ
クル的に変化させた。その結果、3000万パス(初期
出力の70%となるパス回数)以上の結果を得た。
、耐久性試験を行った。試験の環境は、5℃/20%→
25℃/80%→60℃/20%を24時間かけてサイ
クル的に変化させた。その結果、3000万パス(初期
出力の70%となるパス回数)以上の結果を得た。
【0017】比較例1
実施例1の塗料配合において、カーボンブラックaは配
合せず、代わりにカーボンブラックbを10部又は20
部としてフロッピーディスクを作製し、実施例1と同様
の試験を行った。結果はいずれも500 万パスであっ
た。
合せず、代わりにカーボンブラックbを10部又は20
部としてフロッピーディスクを作製し、実施例1と同様
の試験を行った。結果はいずれも500 万パスであっ
た。
【0018】比較例2
実施例1の塗料配合において、カーボンブラックaの代
わりに平均粒径 30nm,BET 比表面積65m2
/g, 吸油量50ml DBP/100 gのカーボ
ンブラックを10部用いてフロッピーディスクを作製し
、実施例1と同様の試験を行った。結果は500 万パ
スであった。
わりに平均粒径 30nm,BET 比表面積65m2
/g, 吸油量50ml DBP/100 gのカーボ
ンブラックを10部用いてフロッピーディスクを作製し
、実施例1と同様の試験を行った。結果は500 万パ
スであった。
Claims (2)
- 【請求項1】 非磁性支持体上に磁性粉と結合剤を主
成分とする磁性層が設けられた磁気記録媒体において、
当該磁性層が平均粒径が25〜130 nm、BET
比表面積が30〜80m2/g、且つ吸油量が 300
〜550 ml/100 gであるカーボンブラックを
含有することを特徴とする磁気記録媒体。 - 【請求項2】 結合剤が極性基を有するポリウレタン
樹脂を含有する請求項1記載の磁気記録媒体。