JPH04190876A - Coating method for flat sheet roofing material - Google Patents

Abstract

PURPOSE:To eliminate the possibility of coating material being collected on a demarcation part between coated and uncoated surfaces by a method wherein a trough is provided on the uncoated surface of a flat sheet roofing material in such a manner as to match the edge of the trough in position with the coating demarcation part and a dropping coat is applied to a predetermined coating surface thereof while the dropping coating material is being recovered by this trough. CONSTITUTION:A trough 6 is provided on the uncoated surface of a flat sheet roofing material 1 in such a manner as to match the edge 5 of the trough in position with a coating demarcation part 9. A dropping coat is applied to a predetermined coating surface while the dropping coating material is being recovered by this trough. As a result, in coating the flat sheet roofing material, there is no collection of the coating material taking place on the demarcation part between the coated and uncoated surfaces and the coating surface can be made even with the other coating surfaces.

Description

【発明の詳細な説明】 （産業上の利用分野） この発明は、平板屋根材の塗装方法に関するものである
。さらに詳しくは、この発明は、塗装面境界部での塗料
集塊の生成を防止し、他の塗装面の塗布量と平均化する
ことのできる改善された平板屋根材の塗装方法に関する
ものである。DETAILED DESCRIPTION OF THE INVENTION (Field of Industrial Application) The present invention relates to a method for coating flat roofing materials. More specifically, the present invention relates to an improved method for painting flat roofing materials that can prevent the formation of paint agglomerates at the boundaries of painted surfaces and can even out the amount of paint applied to other painted surfaces. .

（従来の技術） 従来より、住宅等の屋根部の施工には、セメント系無機
質板等からなる平板屋根材が広（用いられている。(Prior Art) Conventionally, flat plate roofing materials made of cement-based inorganic plates and the like have been widely used in the construction of roofs of houses and the like.

このような平板屋根材を用いて屋根葺きをする場合には
、たとえば第３図にその斜視図を示したように、軒先側
から平板屋根材（ア）の一部を互いに重ね合わせながら
配置固定している。When roofing is done using such flat roofing materials, for example, as shown in the perspective view in Figure 3, parts of the flat roofing materials (A) are overlapped and fixed in place from the eaves side. are doing.

一般に、これら従来の平板屋根材（ア）の表面には、基
材の保護や外観修飾を目的として、樹脂等による塗装が
施されているが、第３図に例示したように、曝露部（イ
）と非曝露部（つ）とに区分される平板屋根材（ア）の
曝露部（イ）にのみ塗装を施したものが普及しつつある
。Generally, the surface of these conventional flat roofing materials (A) is coated with resin or the like for the purpose of protecting the base material or modifying its appearance. Flat plate roofing materials (A) that are divided into (A) and non-exposed areas (B) are becoming popular, with coating applied only to the exposed areas (B).

第４図は、このような塗料使用量の低減と、塗　　　　
−装作業の合理化等を図るための平板屋根材（ア）の塗
装方法の一例を示したものである。この従来法の場合に
は、平板屋根材（ア）の基材（１）をフローコーターヘ
ッド（オ）の下方で一定方向に進行させ、フローコータ
ーヘッド（オ）から塗料膜（力）を曝露部（イ）に滴下
させて塗料（キ）を塗布している。また、フローコータ
ーヘッド（オ）の下部には針金等のヒケ部材（り）を配
設し、これによって塗料膜（力）を曝露部（イ）と非曝
露部（つ）の境界部（ケ）上で遮断するようにしている
。Figure 4 shows this reduction in the amount of paint used and
- This shows an example of a method of painting flat roofing materials (A) to streamline the installation work. In the case of this conventional method, the base material (1) of the flat roofing material (a) is advanced in a fixed direction below the flow coater head (e), and the paint film (force) is exposed from the flow coater head (e). The paint (g) is applied by dripping it onto the area (a). In addition, a sink member such as a wire is installed at the bottom of the flow coater head (O), and this allows the paint film to be applied to the boundary between the exposed area (A) and the non-exposed area (T). ).

（発明が解決しようとする課題） しかしながら、このような従来法の場合には、第４図に
も示した通り、ヒゲ部材（り）によって塗料膜（力）を
遮断するようにしているため、他の曝露部（イ）に比較
して多量の塗料（キ）かヒゲ部材（り）に沿って境界部
（ケ）に滴下され、塗料の集塊か生じてしまうという問
題かあった。(Problem to be Solved by the Invention) However, in the case of such a conventional method, as shown in FIG. 4, the paint film (force) is blocked by the barb member. There was a problem in that a larger amount of paint (x) was dripped onto the boundary area (x) along the whisker member (ri) compared to the other exposed areas (a), resulting in agglomeration of the paint.

また、この塗料集塊の生成によって塗装置後のエアブロ
−による境界線のはかしが効果的に行なえず、仕上がり
外観か好ましいものとはならなかった。In addition, due to the formation of this paint agglomerate, the boundary line could not be effectively marked out by air blowing after painting, and the finished appearance was not desirable.

さらにまた、フローコーターヘッド（オ）からの塗料膜
（力）の滴下か一部分に限定されるため、タンクからの
塗料の流量か制限され、塗料膜（力）に膜切れが生じ、
均一な塗装が困難であるという欠点も有していた。Furthermore, since the paint film (force) drips from the flow coater head (O) only in a portion, the flow rate of the paint from the tank is restricted, causing breaks in the paint film (force).
Another drawback was that uniform coating was difficult.

この発明は、以上の通りの事情に鑑みてなされたもので
あり、従来の平板屋根材の塗装方法の欠点を解消し、平
板屋根材を塗装する際に、塗装面と非塗装面の境界部に
塗料の集塊を生じることなく、他の塗装面と平均化する
ことのできる新しい平板屋根材の塗装方法を提供するこ
とを目的としている。This invention was made in view of the above circumstances, and it solves the drawbacks of the conventional coating method for flat roofing materials, and when painting flat roofing materials, it is possible to eliminate the The object of the present invention is to provide a new method for painting flat roofing materials that can be evened out with other painted surfaces without causing paint agglomerations.

（課題を解決するための手段） この発明は、上記の課題を解決するものとして、平板屋
根材の非塗装面の上方に、そのエッソか塗装面境界部上
に位置するように樋を配設し、この樋により滴下塗料を
回収しつつ、所定の表面に塗料を滴下して塗装すること
を特徴とする平板屋根材の塗装方法を提供する。(Means for Solving the Problems) This invention solves the above problems by disposing a gutter above the non-painted surface of a flat roofing material so as to be located above the boundary between the esso and the painted surface. The present invention also provides a method for painting a flat plate roofing material, which is characterized in that the dripping paint is collected by the gutter and the paint is dripped onto a predetermined surface for painting.

またこの発明は、樋のエッジが先端部鋭角状であること
を好ましい態様としもている。Further, in the present invention, it is preferable that the edge of the gutter has an acute-angled tip.

（作　用） この発明の平板屋根材の塗装方法においては、平板屋根
材の上方に、エツジを有する樋を、そのエツジが塗装面
境界部上に位置するように配設するため、非塗装面に滴
下される塗料膜はこの樋により遮断、回収され、境界部
に多量の塗料か滴下することがない。このため、境界部
に塗料の集塊か生成することはなく、エアブロ−による
境界線のぼかしも容易となる。また、フローコーター等
の全面に塗料膜を張ることかできるため、タンク流量が
多くなり、膜切れがな（、均一な塗装かでき、仕上がり
外観も向上する。(Function) In the method for painting flat roofing materials of the present invention, a gutter having an edge is disposed above the flat roofing material so that the edge is located on the boundary of the painted surface. The paint film that is dripped onto the wall is blocked and collected by this gutter, preventing a large amount of paint from dripping onto the boundary area. Therefore, no paint agglomerates are formed at the boundary, and the boundary line can be easily blurred by air blowing. In addition, since a paint film can be applied to the entire surface of the flow coater, the flow rate in the tank is increased, there is no breakage of the film, uniform coating is possible, and the finished appearance is improved.

さらにまた、樋によって回収した塗料は再利用できるた
め、資材のムダを省略することかでき、全体の製造コス
トの低下を図ることができる。Furthermore, since the paint collected by the gutter can be reused, waste of materials can be omitted and the overall manufacturing cost can be reduced.

（実施例） 以下、添付した図面に沿って実施例を示し、この発明の
構成についてさらに詳しく説明する。(Example) Hereinafter, an example will be shown along with the attached drawings, and the structure of the present invention will be explained in more detail.

第１図は、この発明の平板屋根材の塗装方法の一実施例
を示した要部正面図である。FIG. 1 is a front view of essential parts showing an embodiment of the method for coating flat roofing materials of the present invention.

たとえばこの第１図に示したように、この発明の塗装方
法では、平板屋根材（１）の基材（２）をフローコータ
ーヘット（３）の下方で一定方向に進行させ、フローコ
ーターヘッド（３）の全面から塗料膜（４）を滴下させ
る。基材（２）の直上方、たとえば　２０〜８０ｍｍ上
方には、先端部鋭角状のエツジ（５）を有する樋（６）
を配設し、平板屋根材（１）の非曝露部（７）上に滴下
する塗料膜（４）を遮断し、塗料を回収するようにして
いる。また、樋（６）のエツジ（５）は、平板屋根材（
１）の非曝露部部 （７）と曝露部（８）との境界部（９）の真上に位置し
、滴下する塗料膜（４）を基材（２）表面と樋（６）へ
と分断するため、境界部（９）に多量の塗料が滴下する
ことはない。For example, as shown in FIG. 1, in the coating method of the present invention, the base material (2) of the flat roofing material (1) is advanced in a fixed direction below the flow coater head (3). Drop the paint film (4) from the entire surface of 3). Immediately above the base material (2), for example, 20 to 80 mm above, there is a gutter (6) having an acute-angled edge (5).
is arranged to block the paint film (4) dripping onto the non-exposed part (7) of the flat roofing material (1) and collect the paint. In addition, the edge (5) of the gutter (6) is connected to the flat roofing material (
Located directly above the boundary (9) between the non-exposed area (7) and the exposed area (8) in 1), the dripping paint film (4) is directed onto the surface of the substrate (2) and the gutter (6). Therefore, a large amount of paint will not drip onto the boundary (9).

このようにして、境界部（９）を含めた曝露部（８）に
塗料（１０）を均一に塗布することができる。境界部（
９）への塗料集塊の生成はない。In this way, the paint (10) can be uniformly applied to the exposed area (8) including the boundary area (9). Boundary (
9) There is no formation of paint agglomerates.

第２図は、この発明の塗装方法を用いた平板屋根材の塗
装工程の一例を示した斜視図である。２枚の平板屋根材
（１）となる基材（２）を図中矢印方向へ直進させて、
フローコーターヘッド（３）より滴下した塗料膜（４）
により、曝露部（８）の塗装を行っている。塗装後に基
材（２）を分割して平板屋根材（１）としている。FIG. 2 is a perspective view showing an example of a coating process for a flat roofing material using the coating method of the present invention. Move the base material (2) that will become the two flat roofing materials (1) straight in the direction of the arrow in the figure,
Paint film (4) dripping from the flow coater head (3)
The exposed area (8) is being painted. After painting, the base material (2) is divided into flat roofing materials (1).

このような塗装置後に、曝露部（８）の側から非曝露部
（９）の側へエアーブローを行なえば、境界部（９）上
の塗料（１０）をぼかすことができ、仕上がり外観の良
好な平板屋根材（１）を効率よく製造することができる
。After applying the paint, blowing air from the exposed area (8) to the non-exposed area (9) will blur the paint (10) on the boundary area (9) and improve the finished appearance. A good flat plate roofing material (1) can be efficiently manufactured.

もちろんこの発明は、以上の例によって限定されるもの
ではなく、樋の大きさや、その設置位置、あるいはフロ
ーコーター等からの塗料の排出量等の細部については、
様々な態様が可能であることは言うまでもない。Of course, this invention is not limited to the above examples, and details such as the size of the gutter, its installation position, and the amount of paint discharged from the flow coater etc.
It goes without saying that various embodiments are possible.

（発明の効果） 以上詳しく説明した通り、この発明によって、効率よく
、しかも低コストで平板屋根材の仕上がり外観の良好な
部分塗装を行なうことができる。(Effects of the Invention) As described above in detail, according to the present invention, it is possible to perform partial painting of a flat plate roofing material with a good finished appearance efficiently and at low cost.

【図面の簡単な説明】[Brief explanation of drawings]

第１図は、この発明の平板屋根材の塗装方法の一実施例
を示した要部正面図である。 第２図は、この発明の塗装方法を用いた平板屋根材の塗
装工程の一例を示した斜視図である。 第３図は、平板屋根材を用いた一般的な屋根施工例を示
した斜視図である。 第４図は、従来の平板屋根材の部分塗装方法を例示した
要部正面図である。 ■・・・平板屋根材 ２・・・基　　材 ３・・・フローコーターヘッド ４・・・塗料膜 ５・・・エツジ ６・・・樋 ７・・・非曝露部 ８・・・曝　露　部− ９・・・境界部 １０・・・塗　　料 代理人　弁理士　　西　澤　　利　末 弟　　１　　図 第２図 第　　４　　図 オFIG. 1 is a front view of essential parts showing an embodiment of the method for coating flat roofing materials of the present invention. FIG. 2 is a perspective view showing an example of a coating process for a flat roofing material using the coating method of the present invention. FIG. 3 is a perspective view showing an example of general roof construction using flat roofing materials. FIG. 4 is a front view of main parts illustrating a conventional partial coating method for flat plate roofing materials. ■...Flat roofing material 2...Base material 3...Flow coater head 4...Paint film 5...Edge 6...Gutter 7...Non-exposed area 8...Exposed area - 9...Boundary part 10...Paint agent Patent attorney Toshi Nishizawa, youngest brother 1 Figure 2 Figure 4 Figure O

Claims (2)

【特許請求の範囲】[Claims] （１）平板屋根材の非塗装面の上方に、そのエッジが塗
装面境界部上に位置するように樋を配設し、この樋によ
り滴下塗料を回収しつつ、所定の表面を滴下塗装するこ
とを特徴とする平板屋根材の塗装方法。(1) A gutter is installed above the non-painted surface of the flat roofing material so that its edge is located above the boundary of the painted surface, and the dripping paint is collected by this gutter while drip-painting is applied to the predetermined surface. A method of painting flat roofing materials characterized by: （２）樋のエッジが先端部鋭角状である請求項（１）記
載の塗装方法。(2) The coating method according to claim (1), wherein the edge of the gutter has an acute-angled tip.