JPH0346572B2 - - Google Patents
Info
- Publication number
- JPH0346572B2 JPH0346572B2 JP60033197A JP3319785A JPH0346572B2 JP H0346572 B2 JPH0346572 B2 JP H0346572B2 JP 60033197 A JP60033197 A JP 60033197A JP 3319785 A JP3319785 A JP 3319785A JP H0346572 B2 JPH0346572 B2 JP H0346572B2
- Authority
- JP
- Japan
- Prior art keywords
- metal wire
- fabric
- yarn
- wire
- metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【発明の詳細な説明】
（産業上の利用分野）
本発明は、金属線を含有してなる伸縮性布帛物
に関する。DETAILED DESCRIPTION OF THE INVENTION (Industrial Field of Application) The present invention relates to a stretchable fabric containing metal wire.
（従来技術）
従来、金属線を含有してなる布帛物としては、
長繊維状または短繊維状の金属を糸や繊維束状に
して布帛物にしてなるものや、あるいは適宜の繊
維束に金属線を捲回させてなる複合糸を用いてな
る布帛物が知られている。(Prior art) Conventionally, fabrics containing metal wires include:
Fabric products are known, such as fabrics made from long or short fiber metal in the form of threads or fiber bundles, or composite yarns made by winding metal wires around appropriate fiber bundles. ing.
これらは一般に以下に記載する欠点があるもの
であつた。 These generally had the following drawbacks.
すなわち、前者は硬くて曲がりにくく柔軟性に
乏しいばかりか、一般に糸や束状にすると直径が
太くなりかつ重いものであり、布帛物にすること
自体にも問題があるものであつた。また、後者は
複合糸であるために、箔状の金属なども比較的簡
単に使用でき、この点からは直径の増加や重量の
増加は、普通の丸断面金属線を用いる場合よりも
改善できるものであるが、やはり布帛物としては
柔軟性に乏しくまた伸びがないために用途が限ら
れるものであつた。 That is, the former is not only hard and difficult to bend and lacks flexibility, but also generally has a thick diameter and is heavy when made into threads or bundles, and there are problems in making it into fabrics. In addition, since the latter is a composite thread, it is relatively easy to use foil-like metal, and from this point of view, the increase in diameter and weight can be improved compared to when using ordinary round-section metal wire. However, as a fabric, it has limited flexibility and lacks stretch, so its uses are limited.
一般に、これらの布帛物は、そのままの状態で
は使用されることが少なく、その用途に応じた成
型加工等の各種の加工を受けるものであるが、上
記従来の布帛物では、該加工に際しては、曲がり
にくく、また折れ目が入つたりすることなどが多
く、加工性も取扱い性も悪いものであつた。 In general, these fabrics are rarely used as they are, and are subjected to various processing such as molding depending on their purpose. It was difficult to bend, often had creases, and had poor workability and handling.
たとえば、モールド成型等の成型加工の場合、
合成樹脂と該布帛との合体ハウジング成型など
は、該布帛物にほとんど伸びがないため実際上不
可能な場合も多いものであつた。 For example, in the case of mold processing such as molding,
In many cases, it is actually impossible to mold a synthetic resin and the fabric into a housing because the fabric has almost no elongation.
このような布帛物において、用途を広げるに
は、むろん単に伸びるだけでなく、伸縮伸長性と
回復性を該布帛に付与することが有効である。 In order to widen the range of uses of such fabrics, it is of course effective to impart not only stretchability but also stretchability and recovery properties to the fabrics.
（発明が解決しようとする問題点）
本発明の目的は、上記したような点に鑑み、従
来では得られなかつた優れた伸縮伸長性と回復性
および柔軟性を有し、たとえば成型に際して各種
複雑な形状にも適用が可能という成型加工性に優
れた、金属線を含有してなる伸縮性布帛物を提供
せんとするものである。(Problems to be Solved by the Invention) In view of the above-mentioned points, it is an object of the present invention to have excellent stretchability, recovery properties, and flexibility that have not been available in the past, and to solve various complex problems during molding. It is an object of the present invention to provide a stretchable fabric containing metal wire, which has excellent moldability and can be applied to various shapes.
（問題点を解決するための手段）
上記目的を達成する本発明の金属線を含有して
なる伸縮性布帛物は、以下の構成からなる。(Means for Solving the Problems) A stretchable fabric containing a metal wire of the present invention that achieves the above object has the following configuration.
すなわち、弾性繊維フイラメント糸と繊維束と
からなる芯部に金属線がらせん状に捲回されてな
る複合糸を用いてなる布帛物であり、タテ方向、
またはヨコ方向に10％以上の伸縮伸長率を有する
ことを特徴とする金属線を含有してなる伸縮性布
帛物である。 In other words, it is a fabric made of a composite yarn in which a metal wire is spirally wound around a core made of an elastic fiber filament yarn and a fiber bundle.
Alternatively, it is a stretchable fabric containing a metal wire characterized by having a stretch rate of 10% or more in the horizontal direction.
（作用）
以下、さらに詳しく本発明の金属線を含有して
なる伸縮性布帛物について説明をする。(Function) The stretchable fabric containing the metal wire of the present invention will be explained in more detail below.
上記した構成を有する本発明の布帛物におい
て、金属線の素材は特に限定されず、該布帛物の
用途等に応じて適宜選択できるものであり、場合
によつては金属メツキされてなるものでもよい。
また、本発明において金属線とは、少なくとも１
本以上の長繊維状あるいは短繊維状の金属からな
る糸状もしくは束状等の線状物、あるいは、長繊
維状あるいは短繊維状もしくは金属粉を含んでな
る糸状もしくは束状等の線状物を言い、要は金属
的な性質や特徴が部分的であれ主体的に発揮され
ることを前提としてなる線状物を言うものであ
る。 In the fabric article of the present invention having the above-mentioned configuration, the material of the metal wire is not particularly limited, and can be selected as appropriate depending on the use of the fabric article, and may be metal-plated in some cases. good.
Furthermore, in the present invention, the metal wire refers to at least one
Linear objects such as threads or bundles made of metal in the form of long fibers or short fibers, or linear objects such as threads or bundles made of long fibers or short fibers or metal powder. In short, it refers to a linear object that exhibits metallic properties and characteristics, even if only partially.
本発明の布帛物は、このような金属線が弾性フ
イラメント糸と繊維束とからなる芯部にらせん状
に捲回されてなる金属線複合弾性糸を用いてなる
ものであり、布帛物の態様は織物あるいは編物あ
るいは網状物等であり、さらにそれに樹脂等の他
素材の含浸あるいはコーテイング等、任意の高次
加工がなされていても構わない。また、該金属線
複合弾性糸と他の糸との組合せで交織、交編等さ
れていてもよいものである。 The fabric article of the present invention is made using a metal wire composite elastic yarn in which such a metal wire is spirally wound around a core consisting of an elastic filament yarn and a fiber bundle, and the embodiments of the fabric article are as follows: is a woven fabric, knitted fabric, net-like fabric, etc., and may be further subjected to arbitrary high-order processing such as impregnation or coating with other materials such as resin. Further, the metal wire composite elastic yarn may be interwoven, interwoven, etc. in combination with other yarns.
本発明の布帛物は、このような構成により伸縮
伸長性を付与される。 The fabric of the present invention is given stretchability by such a structure.
該伸縮伸長性は、タテ方向、またはヨコ方向に
少なくとも10％以上の伸縮伸長率を有することが
必要である。該値が10％未満では、本発明の所期
の目的である好ましい伸縮伸長性の付与が到底達
成されない。また、本発明の布帛においてタテ方
向とヨコ方向の双方に10％以上の伸縮伸長率を有
するものが好ましいものである。 The stretchability is required to have a stretchability of at least 10% in the vertical direction or the horizontal direction. If the value is less than 10%, the desired purpose of the present invention, which is to provide preferable stretchability, cannot be achieved at all. In addition, it is preferable that the fabric of the present invention has an elongation rate of 10% or more in both the vertical and horizontal directions.
本発明者らの知見によれば、一般に前記モール
ド成型等に際しては、伸縮伸長率でタテ方向、ヨ
コ方向共に100％程度の値を示す布帛を使用する
のが好ましく、本発明の布帛物はそのような伸縮
伸長性を十分に達することが可能である。 According to the findings of the present inventors, it is generally preferable to use a fabric that exhibits an expansion/contraction rate of about 100% in both the vertical and horizontal directions during the molding, etc., and the fabric of the present invention It is possible to achieve sufficient stretchability.
複合糸の芯部に、弾性繊維フイラメント糸とと
もに用いられる繊維束は、該布帛物の伸長時にお
ける金属線の切断を防止することが主たる目的で
用いられるものであり、合成繊維や天然繊維のフ
イラメント糸や紡績糸などが使用され得、特に高
強力のポリエステル系フイラメント糸それも仮ヨ
リ加工等によりケン縮を付与されているケン縮加
工糸や、または、やはり高強力のポリアラミド系
フイラメント糸などを好ましく用いることができ
る。また、該繊維束を場合によつては炭素繊維も
しくは炭素繊維糸で構成することもでき、この場
合には高強力という特徴に加えて該繊維束が導電
性をも有しているという特徴があるものである。
また該繊維束は、布帛伸長時における伸縮伸長特
性をある定レベルにコントロールする等の効果も
もたらしめ得るものである。 The fiber bundle used in the core of the composite yarn together with the elastic fiber filament yarn is used primarily to prevent the metal wire from breaking when the fabric is stretched. Threads or spun yarns can be used, and in particular, high-strength polyester filament yarns, such as curled yarns that have been given crimp by temporary twisting or the like, or polyaramid filament yarns, which are also high-strength filament yarns. It can be preferably used. In addition, the fiber bundle may be composed of carbon fiber or carbon fiber yarn depending on the case, and in this case, in addition to the high strength, the fiber bundle also has electrical conductivity. It is something.
Furthermore, the fiber bundle can also bring about effects such as controlling the stretching/elongation characteristics to a certain level when the fabric is stretched.
該繊維束は、弾性フイラメント糸に捲回されて
芯部を構成してなる場合が好ましく、その場合、
上記金属線と該繊維束とは互いに逆方向のらせん
状捲回とするのが望ましい。 Preferably, the fiber bundle is wound around an elastic filament yarn to form a core; in that case,
It is desirable that the metal wire and the fiber bundle are spirally wound in opposite directions.
このようにすることにより、好ましい伸縮性を
発揮でき布帛物に伸長作用が加わつたとき、該布
帛物の構成複合糸の伸縮伸長率をほぼ一定にし
て、伸長状態における金属線の切断を効果的に防
止することができるものである。なお、一方、該
繊維束は、弾性フイラメント糸にらせん状に捲回
されていないで、単に引揃えられてなるものでも
よい。ただし、その場合には、伸縮性をある程度
有する仮ヨリ加工糸等のケン縮加工糸などを用い
ることが肝要である。 By doing so, it is possible to exhibit preferable stretchability, and when a stretching action is applied to the fabric, the stretching/elongation rate of the composite yarns constituting the fabric is kept almost constant, and the cutting of the metal wire in the stretched state is effectively prevented. This is something that can be prevented. On the other hand, the fiber bundle may not be spirally wound around the elastic filament yarn, but may simply be aligned. However, in that case, it is important to use a curled yarn such as a temporarily twisted yarn that has some degree of elasticity.
また、弾性繊維フイラメント糸は、伸縮伸長率
が少なくとも100％以上の値を示すもの、好まし
くは400％程度以上の値を示すものであればよく、
ポリマー等特には限定されないが、例えば、ポリ
ウレタン系エラストマー、ポリエステル系エラス
トマー、ポリウレタン系エラストマー、天然ゴ
ム、合成ゴムなどの弾性特性を有する各種繊維フ
イラメント糸を用いることができ、耐久性、ぜい
化なども考慮すれば、ポリウレタン系あるいはポ
リエステル系あるいはポリアミド系の各エラスト
マーが好ましいものである。 In addition, the elastic fiber filament yarn may be one that exhibits a stretching/elongation ratio of at least 100% or more, preferably about 400% or more,
Although the polymer is not particularly limited, for example, various fiber filament yarns having elastic properties such as polyurethane elastomer, polyester elastomer, polyurethane elastomer, natural rubber, and synthetic rubber can be used to improve durability, embrittlement, etc. Taking this into account, polyurethane-based, polyester-based, or polyamide-based elastomers are preferred.
該弾性フイラメント糸は、モノフイラメント糸
あるいはマルチフイラメント糸のいずれでもよい
が、伸長後の回復力という点からすれば、モノフ
イラメント糸よりはマルチフイラメント糸の方が
回復パワーが一般に強いと言え、好ましいもので
ある。 The elastic filament yarn may be either a monofilament yarn or a multifilament yarn, but from the point of view of recovery power after elongation, multifilament yarn is preferable because it can be said that the recovery power is generally stronger than that of monofilament yarn. It is something.
金属線の形態については、金属箔の線状物ある
いは長手方向に垂直な断面形状が円形状のもの
等、特にその形態は限定されず、適宜使用目的に
応じて定められればよいものである。特に箔状の
線状物を使用する場合には、複合糸表面が極めて
滑らかでかつ該金属の被覆性が良好なものを得る
ことが可能であり、表面の滑らかな布帛物となる
ものである。一方、円形断面形状のものを用いる
場合には、箔状のものを用いる場合と比較して伸
縮性がやや低下する傾向にあり、布帛物の表面は
やや凹凸が生じるものであり、網状物や目の粗い
編物や織物に適していると言えるものである。ま
た、金属線は、多重に捲回されていてもよく、こ
のようにすることにより金属の被覆性が一層向上
されるものである。多重に捲回させる場合、伸縮
伸長性を損うことのないように、各金属線のらせ
ん方向は同一のものとするのがよい。 The form of the metal wire is not particularly limited, such as a linear metal foil or a circular cross-section perpendicular to the longitudinal direction, and may be determined as appropriate depending on the purpose of use. In particular, when using a foil-like linear material, it is possible to obtain a composite yarn with an extremely smooth surface and good coverage with the metal, resulting in a fabric with a smooth surface. . On the other hand, when using a fabric with a circular cross-section, the elasticity tends to be slightly lower than when using a foil-like fabric, and the surface of the fabric is slightly uneven, and the fabric has a slightly uneven surface. It can be said that it is suitable for coarse knitting and woven fabrics. Further, the metal wire may be wound multiple times, and by doing so, the metal coverage is further improved. When winding the metal wire multiple times, it is preferable that the helical direction of each metal wire be the same so as not to impair the stretchability.
かかる本発明の布帛物に用いられる金属線複合
弾性糸の概略モデル図を、第１図、第２図、第３
図に示した。 Schematic model diagrams of the metal wire composite elastic yarn used in the fabric of the present invention are shown in FIGS. 1, 2, and 3.
Shown in the figure.
これらの図において、１は弾性繊維フイラメン
ト糸であり、２は繊維束、３は金属線である。い
ずれの図においても繊維束２が弾性繊維フイラメ
ント糸１に対してらせん状に捲回されてなる例、
それも金属線３の捲回方向とは逆方向に捲回され
てなる例を示している。また、第１図が円形断面
の金属線を用いてなる場合、第２図が箔状の金属
線を用いてなる場合、第３図が金属線を２重に捲
回させてなる複合糸の例をそれぞれ示している。 In these figures, 1 is an elastic fiber filament yarn, 2 is a fiber bundle, and 3 is a metal wire. In each figure, an example in which the fiber bundle 2 is spirally wound around the elastic fiber filament yarn 1,
It also shows an example in which the metal wire 3 is wound in the opposite direction to the winding direction. In addition, when Fig. 1 uses a metal wire with a circular cross section, Fig. 2 uses a foil-shaped metal wire, and Fig. 3 shows a composite yarn made by doubly winding the metal wire. An example is provided for each.
本発明の布帛物は、上記したような金属線複合
弾性糸を用いて、通常の織機や編機あるいは布帛
物の態様に応じたその他の布帛製造機械により布
帛物となし得、しかして柔軟性に富み優れた伸縮
伸長性と回復性を有する伸縮性布帛物が得られる
ものである。 The fabric of the present invention can be made into a fabric by using a metal wire composite elastic yarn as described above using a normal loom, knitting machine, or other fabric manufacturing machine depending on the mode of the fabric, and has flexibility. The result is a stretchable fabric that is rich in elasticity and has excellent stretchability and recovery properties.
該布帛物の伸縮伸長性は、複合糸の各構成素材
等の選定により任意に適宜設定できるものである
が、この他にたとえば、金属線の太さや厚さに対
する弾性繊維フイラメント糸の太さとの組合せに
よつても任意に設定することができるものであ
る。すなわち、一例を挙げると、金属線が細いあ
るいは箔状のときは薄いものに対して弾性繊維フ
イラメント糸が太い組合せの場合には該布帛物の
伸縮伸長性が高く、タテ方向、ヨコ方向共に概し
て200％以上の高伸縮伸長率を得ることができる。
一方、これと逆の組合せの場合には布帛物の伸縮
伸長性が低くなる傾向にある。本発明者らの各種
検討によれば、本発明の布帛物に用いられる金属
線弾性複合糸は、弾性繊維フイラメント糸の径と
金属線の径とが、下記(a)式、(b)式の関係を満足す
ることが望ましい。 The stretchability of the fabric can be set arbitrarily and appropriately by selecting each constituent material of the composite yarn, but in addition, for example, it can be determined by the thickness of the elastic fiber filament yarn with respect to the thickness and thickness of the metal wire. They can also be set arbitrarily by combination. That is, to give an example, when the metal wire is thin or foil-like, it is thin, but when the elastic fiber filament yarn is thick, the fabric has high elasticity and extensibility in both the vertical and horizontal directions. High elasticity and elongation of over 200% can be obtained.
On the other hand, in the case of the opposite combination, the stretchability of the fabric tends to be low. According to various studies by the present inventors, the metal wire elastic composite yarn used in the fabric of the present invention has a diameter of the elastic fiber filament yarn and a diameter of the metal wire according to the following formulas (a) and (b). It is desirable to satisfy the following relationship.
すなわち、 Ｄ／ｄ≧3.0 ……(a) ｄ≦1.0 ……(b) である。ただし、ここで、 Ｄ：弾性フイラメント糸の換算直径（mm） ｄ：金属線の換算直径（mm） である。 That is, D/d≧3.0……(a) d≦1.0...(b) It is. However, here, D: Converted diameter of elastic filament yarn (mm) d: Converted diameter of metal wire (mm) It is.
また、金属線の捲回に関しては、第１図、第２
図に示すらせん角θが30度以上であるようにする
のが好ましい。また、上記(b)式の通り、金属線は
その換算直径が１mm以下であることが望ましく、
該値が１mmを越えるもののときには、一般に好ま
しい複合状態を得ることが難しいものである。金
属線を多重に捲回させるときには、各金属線が上
記の関係を満足するものを用いるのがやはり望ま
しいものである。 Regarding the winding of metal wire, see Figure 1 and Figure 2.
It is preferable that the helical angle θ shown in the figure is 30 degrees or more. Also, as shown in equation (b) above, it is desirable that the converted diameter of the metal wire is 1 mm or less,
When the value exceeds 1 mm, it is generally difficult to obtain a desirable composite state. When winding metal wires in multiple layers, it is desirable to use metal wires that satisfy the above relationship.
複合糸を上記した通りの構成にすることによ
り、良好な表面品位や伸縮伸長性を有する金属線
複合弾性糸となるものであり、かかる糸を用いれ
ば、むろん布帛物としても良好な表面品位と伸縮
伸長性を達成することができる。 By configuring the composite yarn as described above, a metal wire composite elastic yarn with good surface quality and stretchability can be obtained.If such a yarn is used, of course, it can also be made into a fabric with good surface quality. Stretchability can be achieved.
なお、ここで、弾性繊維フイラメント糸の換算
直径Ｄ（mm）とは、次式(c)で求めるものである。 In addition, here, the converted diameter D (mm) of the elastic fiber filament yarn is determined by the following equation (c).
Ｄ＝10×√4（mm） ……(c)
ここで、
Ｗ：弾性繊維フイラメント糸のデニール（重さ）
（ｇ／９×105cm）
Ｌ：弾性繊維フイラメント糸の長さ（ここでは、
Ｌ＝９×105cm）
ρ：弾性繊維フイラメント糸の比重（ｇ／cm3）
であり、デニール値は、糸長さ9000ｍにおける重
さ（単位ｇ）で表わすものである。また、デニー
ル、長さ等の測定に際しては、複合糸を分解し、
弛緩状態で25℃×65％RHの雰囲気中に24時間放
置して、該自由放縮後の値を測定してなるもので
ある。 D=10×√4(mm) ……(c) Here, W: Denier (weight) of elastic fiber filament yarn
(g/9×10 5 cm) L: Length of elastic fiber filament yarn (here,
L=9×10 5 cm) ρ: Specific gravity (g/cm 3 ) of the elastic fiber filament yarn, and the denier value is expressed in weight (unit: g) at a yarn length of 9000 m. In addition, when measuring denier, length, etc., we disassemble the composite yarn and
The sample was left in a relaxed state in an atmosphere of 25°C x 65% RH for 24 hours, and the value after free contraction was measured.
また、金属線の換算直径ｄ（mm）は、該金属線
が丸断面のもののときはそのままの直径ｄ（mm）
で求め、箔状等の非円形のもののときは該金属箔
等の断面積Ｓを元にして、これを同断面積の丸断
面糸に換算して直径ｄ（mm）を求めるものである。
すなわち、この場合、
ｄ＝√4（mm）
となるものである。なお、このとき箔状のものの
断面積を求めるに際しては、厚さをミクロン単位
まで求めるものである。 In addition, the converted diameter d (mm) of the metal wire is the same diameter d (mm) when the metal wire has a round cross section.
In the case of a non-circular item such as a foil, the diameter d (mm) is determined by converting this to a round cross-section thread having the same cross-sectional area based on the cross-sectional area S of the metal foil.
That is, in this case, d=√4 (mm). At this time, when determining the cross-sectional area of the foil-like material, the thickness is determined to the micron level.
本発明の布帛物に用いられる金属線複合弾性糸
は、中空スピンドルを用いた公知のカバリング糸
製造機を用いて簡単に製造することができるもの
である。繊維束を弾性繊維フイラメント糸にらせ
ん状に捲回させてなる芯部を有する複合糸を用い
るときには、まず、弾性繊維フイラメント糸に該
繊維束を上記カバリング糸製造機によりらせん状
に捲回させ、さらに、それに金属線を上記カバリ
ング糸製造機によりらせん状に捲回させるとい
う、二段階のカバリング工程を行なえばよい。金
属線を多重に捲回させるときもこれと同様であ
る。なお、また弾性繊維フイラメント糸に繊維束
を捲回させるに際しては、合ネン法を用いること
もできる。 The metal wire composite elastic yarn used in the fabric of the present invention can be easily manufactured using a known covering yarn manufacturing machine using a hollow spindle. When using a composite yarn having a core formed by spirally winding a fiber bundle around an elastic fiber filament yarn, first, the fiber bundle is spirally wound around an elastic fiber filament yarn using the covering yarn manufacturing machine; Furthermore, a two-step covering process may be performed in which the metal wire is wound spirally by the covering thread manufacturing machine. The same applies when winding the metal wire multiple times. Furthermore, when winding the fiber bundle around the elastic fiber filament yarn, a spinning method can also be used.
本発明の金属線を含有してなる伸縮性布帛物
は、金属線の有する特徴を生かして各種の分野に
使用することができ、その実用的価値は高い。 The stretchable fabric containing the metal wire of the present invention can be used in various fields by taking advantage of the characteristics of the metal wire, and has high practical value.
たとえば、金属線として銅線を用いれば、電界
シールド材（ノイズ防止）として、強電、弱電、
電子材料等の各種の分野（電線ケーブル、電子レ
ンジ、コンピユーター等のシールド材等）におい
て成型性のよい伸縮性布帛物として利用できるも
のである。また、銅には、抗細菌作用があるの
で、細菌防止用フイルターや各種衣料用生地もし
くは布帛、あるいはさらに抗細菌性を有する生理
帯や靴下等にも好ましい布帛物として利用するこ
とができるものである。 For example, if copper wire is used as the metal wire, it can be used as an electric field shield material (noise prevention) for strong electric current, low electric current,
It can be used as a stretchable fabric with good moldability in various fields such as electronic materials (wire cables, shielding materials for microwave ovens, computers, etc.). In addition, copper has an antibacterial effect, so it can be used as a preferred fabric for antibacterial filters, various clothing fabrics, and even sanitary belts and socks that have antibacterial properties. be.
また、金属線として、アルミニウム線を用いれ
ば、該アルミニウムの軽くてかつ熱反射性を有す
るという特性を利用して防寒衣料や防寒資材、あ
るいはさらに消防服等にも伸縮性や加工性の良い
布帛もしくは生地として利用できるものである。 In addition, if aluminum wire is used as the metal wire, the light and heat-reflecting characteristics of aluminum can be used to make fabrics with good stretch and workability for use in cold-weather clothing, materials, and even firefighting clothing. Or it can be used as fabric.
また、金属線として、鉛線を用いれば、Ｘ線遮
蔽効果を利用してＸ線防護衣料やＸ線遮蔽資材等
に使用でき、また、その重さを利用して波浪衝撃
吸収漁網等にも利用できるものである。 Furthermore, if lead wire is used as the metal wire, it can be used for X-ray protective clothing, X-ray shielding materials, etc. by taking advantage of its X-ray shielding effect, and its weight can also be used for wave impact-absorbing fishing nets, etc. It is available.
むろん、金属含有シート状物として一般的耐
火、耐炎材としてなども使用できるものである。 Of course, it can also be used as a general fireproof or flameproof material as a metal-containing sheet material.
なお、本発明において、布帛物の伸縮伸長率と
は以下の方法で測定してなるものである。 In addition, in the present invention, the expansion/contraction elongation rate of a fabric is measured by the following method.
すなわち、織物状布帛物については、JIS Ｌ
1096の6.14.1 Ｂ法（定荷重法）を用いて、垂直
荷重のみ変更して用いるものである。すなわち、
金属線の換算直径が0.05mm以下の複合糸を用いた
織物状布帛物においては1.5Kgの垂直荷重を、金
属線の換算直径が0.05mmより大きいものを用いた
織物状布帛物には５Kgの垂直荷重をそれぞれ使用
するものである。 In other words, for woven fabrics, JIS L
1096 6.14.1 Method B (constant load method) is used with only the vertical load changed. That is,
A vertical load of 1.5 kg is applied to woven fabrics using composite yarns with a metal wire equivalent diameter of 0.05 mm or less, and a 5 kg vertical load is applied to woven fabrics using metal wires with an equivalent diameter larger than 0.05 mm. Each uses a vertical load.
編物状布帛物あるいはその他の布帛物の場合に
は、JIS Ｌ 1081の6.18.2（定荷重伸長率）のグ
ラブ法を用いて、前記織物状布帛物と同様の垂直
荷重をそれぞれ使用して測定するものである。 In the case of knitted fabrics or other fabrics, measure using the Grab method of JIS L 1081 6.18.2 (constant load elongation rate) using the same vertical load as for the woven fabrics. It is something to do.
（実施例）
以下、実施例により具体的に本発明の構成、効
果について説明する。(Example) Hereinafter, the configuration and effects of the present invention will be specifically explained using examples.
実施例 １
ポリウレタン弾性フイラメント糸（560デニー
ル、42フイラメント）にカバリングマシンを用い
てポリエステル仮ヨリ加工糸（50デニール）を捲
回させ、さらにカバリングマシンにより直径0.03
mmの銅線を捲回させて、３層同心構造の金属線複
合弾性糸を製造した。この糸を用いて横編機を用
いて平編組織の編地を編成した。こうして得られ
た編地は、タテ方向に100％、ヨコ方向に250％の
伸縮伸長率を有するものであつた。これをタテ方
向、ヨコ方向同時に引張つたところ、布帛面積比
で4.0倍程度の伸縮伸長率を有することが確認で
きた。Example 1 A polyester pre-twisted yarn (50 denier) was wound around a polyurethane elastic filament yarn (560 denier, 42 filaments) using a covering machine, and a diameter of 0.03 was further wound using a covering machine.
A metal wire composite elastic yarn with a three-layer concentric structure was manufactured by winding copper wire with a thickness of 1 mm. Using this yarn, a knitted fabric with a plain knit structure was knitted using a flat knitting machine. The thus obtained knitted fabric had an elongation rate of 100% in the vertical direction and 250% in the horizontal direction. When this was stretched simultaneously in the vertical and horizontal directions, it was confirmed that the fabric had a stretch ratio of about 4.0 times in area ratio.
かかる編地をABS樹脂を用いてサンドイツチ
状に箱型に成型加工したところ、編地の伸縮伸長
性が十分に生かされて、加工性が極めて良好なも
のであつた。 When such a knitted fabric was molded into a sandwich box shape using ABS resin, the stretchability of the knitted fabric was fully utilized and the workability was extremely good.
この成型加工品について、入力500W、300MHz
での電解強度の変化を調べたところ、40dBに減
衰するものであり、シールド効果が十分にあると
判断されるものであつた。 Regarding this molded product, input 500W, 300MHz
When we investigated the change in the electrolytic strength, we found that it was attenuated to 40 dB, and it was judged that the shielding effect was sufficient.
実施例 ２
ポリウレタンフイラメント糸（1680デニール、
112フイラメント）にカバリングマシンを用いて
ポリエステル仮ヨリ加工糸（50デニール）を捲回
させ、さらにカバリングマシンにより厚さ0.035
mmの銅箔を捲回させて、３層同心構造の金属線複
合弾性糸を製造した。この糸に再度カバリングマ
シンにより厚さ0.035mmの銅箔を捲回させて、４
層同心構造（金属線が二重らせん）の金属線複合
弾性糸を製造した。この糸をタテ糸、ヨコ糸に用
いて通常の織機にて平織し、２軸伸縮性織物を製
造した。かかる織物は、タテ方向80％、ヨコ方向
100％の伸縮伸長率を有するものであつた。この
織物は、柔軟性に富み曲がりやすくかつ伸縮伸長
性および回復性に優れ、成型加工性に優れている
と判断されるものであつた。Example 2 Polyurethane filament yarn (1680 denier,
112 filament) using a covering machine to wind polyester pre-twisted yarn (50 denier), and then using a covering machine to wind it to a thickness of 0.035.
A metal wire composite elastic yarn with a three-layer concentric structure was manufactured by winding a copper foil of mm in diameter. This thread is again wrapped with 0.035mm thick copper foil using a covering machine.
A metal wire composite elastic yarn with a layer concentric structure (metal wire double helix) was manufactured. This yarn was used as a warp yarn and a weft yarn, and was plain woven using an ordinary loom to produce a biaxially stretchable fabric. Such a fabric is 80% in the vertical direction and 80% in the horizontal direction.
It had a stretching/elongation rate of 100%. This woven fabric was judged to be highly flexible, easy to bend, excellent in stretchability and recovery properties, and excellent in moldability.
実施例 ３
ポリウレタンフイラメント糸（210デニール、
20フイラメント）にカバリングマシンを用いてポ
リエステル仮ヨリ加工糸（30デニール）を捲回さ
せ、さらにカバリングマシンにより厚さ0.015mm
のアルミニウム箔を捲回させて、３層同心構造の
金属線複合弾性糸を製造した。Example 3 Polyurethane filament yarn (210 denier,
20 filament) using a covering machine to wind polyester pre-twisted yarn (30 denier), and then using a covering machine to wind it to a thickness of 0.015 mm.
A metal wire composite elastic yarn with a three-layer concentric structure was manufactured by winding aluminum foil.
この糸をヨコ糸に用い、タテ糸にはポリエステ
ル仮ヨリ加工糸150デニールを用いて通常の織機
にて平織し、ヨコ方向に主たる伸縮性を有する織
物を得た。かかる織物は、ヨコ方向に20％の伸縮
伸長率を有するものであつた。 This yarn was used as the weft yarn, and a 150 denier polyester tentatively twisted yarn was used as the warp yarn, and plain weaved on a normal loom to obtain a fabric having primary elasticity in the weft direction. This woven fabric had a stretch rate of 20% in the horizontal direction.
一方、上記の複合糸を、タテ糸およびヨコ糸に
用いて上記と同様に通常の織機にて平織し、伸縮
性を有する織物を得た。かかる織物は、タテ方向
20％、ヨコ方向50％の伸縮伸長率を有するもので
あつた。 On the other hand, the above-mentioned composite yarn was used as the warp yarn and the weft yarn, and was plain woven using an ordinary loom in the same manner as above to obtain a stretchable fabric. Such a fabric is
It had an elongation ratio of 20% and 50% in the horizontal direction.
上記の織物はいずれのものも、衣料用として好
ましい伸縮性と柔軟性を有していると言え、アル
ミニウムの特徴を生かして防寒着の裏地用途に最
適であると判断されるものであつた。 All of the above-mentioned fabrics can be said to have stretchability and flexibility suitable for clothing, and were judged to be optimal for use as linings for cold-weather clothing, taking advantage of the characteristics of aluminum.
（発明の効果） 本発明の効果を以下に述べる。(Effect of the invention) The effects of the present invention will be described below.
本発明の金属線を含有してなる布帛物は、金属
線を含むものでありながら、従来の類似のもので
は得られなかつた、優れた柔軟性と伸縮伸長性お
よび伸縮回復性を有するものである。簡単に言う
と、この布帛物は金属を含んでいながら、曲がり
に強く、かつよく伸びそして伸ばされてもフリー
になるとよく縮む。 Although the fabric containing the metal wire of the present invention contains the metal wire, it has excellent flexibility, stretchability, and recovery properties that were not available with conventional similar products. be. Simply put, although this fabric contains metal, it is resistant to bending, stretches well, and shrinks well when released even when stretched.
これらの特性を生かして、合成樹脂との一体型
成型等に際しては、複雑な３次元形状のものでも
比較的簡単に可能となるものである。また、むろ
んその柔軟性、伸縮性等により、一般的に布帛と
しても取扱い性や加工性が容易であり、衣料用途
等にも適用しやすいものである。 By taking advantage of these characteristics, even complex three-dimensional shapes can be relatively easily formed when integrally molded with synthetic resin. Furthermore, due to its flexibility, stretchability, etc., it is generally easy to handle and process as a fabric, making it easy to apply to clothing and the like.
本発明の布帛物に用いられる金属線複合弾性糸
では、繊維束を補助的に使用しているので、布帛
伸長時における金属線の切断が良好に防止され
得、かつ伸縮伸長特性をある定レベルにコントロ
ールすることが可能なものでもある。 Since the metal wire composite elastic yarn used in the fabric article of the present invention uses fiber bundles as an auxiliary material, it is possible to effectively prevent the metal wires from being cut when the fabric is stretched, and the elastic elongation characteristics can be maintained at a certain level. It is also something that can be controlled.
本発明の布帛物においては、金属線、弾性繊維
フイラメント糸、繊維束の３者の組合せから構成
糸がなるものであり、これら各素材の適宜な組合
せにより、広範囲に布帛物としての伸縮伸長特性
の設定が可能なものである。 In the fabric of the present invention, the constituent threads are a combination of metal wires, elastic fiber filament yarns, and fiber bundles, and by appropriately combining these materials, the fabric has a wide range of elasticity and elongation characteristics. can be set.
本発明の布帛物は、特に金属線の素材について
実際上特に限定されることがないので、その用途
に応じた金属線素材の選定が可能であり、その利
用分野は広いものである。 Since the fabric of the present invention is not particularly limited in practice with respect to the material of the metal wire, it is possible to select the material of the metal wire according to the application, and the field of use thereof is wide.
第１図、第２図、第３図は、本発明の布帛物に
用いられる金属線複合弾性糸の例を示す概略モデ
ル図である。
図面中の符号の説明、１：弾性繊維マルチフイ
ラメント糸、２：繊維束、３：金属線、θ：らせ
ん角。
FIG. 1, FIG. 2, and FIG. 3 are schematic model diagrams showing examples of metal wire composite elastic yarns used in the fabric article of the present invention. Explanation of symbols in the drawings: 1: Elastic fiber multifilament yarn, 2: Fiber bundle, 3: Metal wire, θ: Helix angle.
Claims (1)
芯部に金属線がらせん状に捲回されてなる複合糸
を用いてなる布帛物であり、タテ方向、またはヨ
コ方向に10％以上の伸縮伸長率を有することを特
徴とする金属線を含有してなる伸縮性布帛物。 ２ 金属線が、金属箔の線状物であることを特徴
とする特許請求の範囲第１項記載の金属線を含有
してなる伸縮性布帛物。 ３ 金属線が、長手方向に垂直な断面形状が円形
のものであることを特徴とする特許請求の範囲第
１項記載の金属線を含有してなる伸縮性布帛物。 ４ 金属線が、複数らせんの多重に捲回されてな
る複合糸を用いてなることを特徴とする特許請求
の範囲第１項、第２項または第３項記載の金属線
を含有してなる伸縮性布帛物。 ５ 金属線として銅線が用いられ、電界シールド
用途に用いられることを特徴とする特許請求の範
囲第１項、第２項、第３項または第４項記載の金
属線を含有してなる伸縮性布帛物。 ６ 金属線として銅線が用いられ、抗細菌材用途
に用いられることを特徴とする特許請求の範囲第
１項、第２項、第３項または第４項記載の金属線
を含有してなる伸縮性布帛物。 ７ 金属線としてアルミニウム線が用いられ、熱
反射性布帛用途に用いられることを特徴とする特
許請求の範囲第１項、第２項、第３項または第４
項記載の金属線を含有してなる伸縮性布帛物。 ８ 金属線として鉛線が用いられ、Ｘ線遮蔽材用
途に用いられることを特徴とする特許請求の範囲
第１項、第２項、第３項または第４項記載の金属
線を含有してなる伸縮性布帛物。 ９ 金属線として鉛線が用いられ、波浪衝撃吸収
漁網用途に用いられることを特徴とする特許請求
の範囲第１項、第２項、第３項または第４項記載
の金属線を含有してなる伸縮性布帛物。[Scope of Claims] 1. A fabric made of a composite yarn in which a metal wire is spirally wound around a core made of an elastic fiber filament yarn and a fiber bundle, and the fabric is made of a composite yarn made of a core made of an elastic fiber filament yarn and a fiber bundle, and has a diameter of 10 mm in the vertical direction or in the horizontal direction. 1. A stretchable fabric containing metal wire, characterized by having a stretch rate of % or more. 2. A stretchable fabric containing a metal wire according to claim 1, wherein the metal wire is a linear metal foil. 3. A stretchable fabric containing a metal wire according to claim 1, wherein the metal wire has a circular cross-sectional shape perpendicular to the longitudinal direction. 4. A metal wire containing the metal wire according to claim 1, 2, or 3, characterized in that the metal wire is made of a composite thread formed by multiple windings of multiple spirals. Stretch fabric. 5. A stretchable product containing a metal wire according to claim 1, 2, 3, or 4, wherein a copper wire is used as the metal wire and is used for electric field shielding. Sex fabric. 6. A copper wire is used as the metal wire and contains the metal wire according to claim 1, 2, 3, or 4, which is used for antibacterial material applications. Stretch fabric. 7 Claims 1, 2, 3, or 4, characterized in that aluminum wire is used as the metal wire and is used for heat-reflective fabric applications.
A stretchable fabric comprising the metal wire as described in 1. 8. A lead wire is used as the metal wire, and the metal wire is used as an X-ray shielding material. A stretchable fabric. 9. A lead wire is used as the metal wire, and the metal wire is used as a fishing net for absorbing wave shock, and contains the metal wire according to claim 1, 2, 3, or 4. A stretchable fabric.