JPH0327200A - Inorganic board - Google Patents
Inorganic boardInfo
- Publication number
- JPH0327200A JPH0327200A JP16208989A JP16208989A JPH0327200A JP H0327200 A JPH0327200 A JP H0327200A JP 16208989 A JP16208989 A JP 16208989A JP 16208989 A JP16208989 A JP 16208989A JP H0327200 A JPH0327200 A JP H0327200A
- Authority
- JP
- Japan
- Prior art keywords
- inorganic board
- cement
- acrylic emulsion
- mortar layer
- resin mortar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
（産業上の利用分野〉
この発明は、無機質板に関するものである。さらに詳し
くは、この発明は、表面の乾燥によって発生し易い反り
を抑止することのできる表面化粧無機質板に関するもの
である．
（従来の技術）
建築用の外装材等として、セメントにアスベスト、ロッ
クウール、バルプ等を配合して成形した無機質板が広く
使用されており、これらの無機質板については、その表
面に塗料を塗布して化粧することも行われてきている。Detailed Description of the Invention (Industrial Field of Application) The present invention relates to an inorganic board. This relates to boards. (Prior art) Inorganic boards made by blending cement with asbestos, rock wool, bulp, etc. are widely used as exterior materials for buildings. Paints have also been applied to the surface to create makeup.
これらの無機質板の成形法としては、抄造法、押出し法
、あるいは注型法などが知られており、たとえば抄造法
による場合には、第３図に示したように、ボルトランド
セメント（ＰＣ）、アスベスト、バルプ等からなる原料
スラリ−（ア）から抄造ドラム（イ）によって、シート
（ウ）を抄造し、プレスロール（工）で加圧脱水した後
に、養土槽（オ）において養生し、その後、表面に塗Ｉ
１（力）を塗布し、焼付装置（キ〉によって焼イ・１硬
化させて、表面に化粧塗膜（ク）を右ずる無機質板（ゲ
）を製造している。As methods for forming these inorganic plates, there are known methods such as paper making, extrusion, and casting. For example, when using the paper making method, as shown in Fig. 3, Bolt Land Cement (PC) is used. A sheet (C) is made from a raw material slurry (A) consisting of asbestos, bulp, etc. using a paper-making drum (B), dehydrated under pressure with a press roll (D), and then cured in a soil nurturing tank (E). , then apply I on the surface
The inorganic board is manufactured by applying 1 (force) and baking and hardening it with a baking device (ki) to form a decorative coating film (ku) on the surface.
（発明が解決しようとする課題）
たとえばこの第３図に示した抄造法等によって製造する
ことのできる無機質板は、表面化粧によって、様々な意
匠の建築材として用いられるが、これらの無機質板を屋
根材等として使用する場合には、その表面への日射によ
る加熱等によって表面が乾燥し、無Ｒ質板に反りが発生
し易いという問題があった。(Problems to be Solved by the Invention) For example, inorganic boards that can be manufactured by the paper making method shown in Fig. 3 are used as building materials with various designs depending on the surface decoration. When used as a roofing material, etc., there is a problem in that the surface becomes dry due to heating due to solar radiation, and the non-R material board tends to warp.
この反りは、表面の加熱、乾燥によって烈機質板（ゲ）
の表面層の透湿抵抗が低下して、不均一に変形すること
によるものであり、この反り変形によって建築材として
の機能が損なわれ、また、表面に形成した化粧塗Ｖ＜ク
）が剥離するという欠点が避けられなかった．
この発明は、以上の通りの事情に鑑みてなされたもので
あり、従来の無機質板の欠点を解消し、表面乾燥による
反り変形を抑止し、化粧塗膜の密着性を向上させること
のできる新しい熟機質板を提０（することを目的として
いる。This warping is caused by heating and drying the surface.
This is because the moisture permeability resistance of the surface layer of the material decreases and it deforms unevenly.This warping deformation impairs its function as a building material, and also causes the decorative coating formed on the surface to peel off. The disadvantage of doing so was unavoidable. This invention was made in view of the above circumstances, and is a new product that can eliminate the drawbacks of conventional inorganic boards, prevent warping and deformation due to surface drying, and improve the adhesion of decorative coatings. The purpose is to present a matured quality board.
（課題を解決するための手段）
この発明は、上記の′ａＢを解決するものとして、アク
リルエマルジョンとセメン１・どの混合物からなるレジ
ンモルタル層を烈機質板表面に配設してなることを特徴
とする熟機質板を提供する．この無機質板としては、抄
造法、押出し成形法等の適宜な方法によって製造したも
のであってよく、その配合も、ボルトランドセメント（
ＰＣ）搾のセメントと、アスベスト、ロックウール、パ
ルプなどの繊維成分に、シリカ粉、その他の添加材を適
宜に加えたスラリー組或物、あるいは混合物とすること
ができる．これらの配合には従来公知の配合成分を用い
ることができる。(Means for Solving the Problems) The present invention solves the above problem 'aB' by disposing a resin mortar layer made of a mixture of acrylic emulsion and cement 1 on the surface of a ceramic board. We offer mature quality boards with special characteristics. This inorganic board may be manufactured by an appropriate method such as a paper forming method or an extrusion molding method, and its composition may also be made of boltland cement (
It can be a slurry composition or a mixture of compressed cement (PC) and fiber components such as asbestos, rock wool, and pulp, with silica powder and other additives added as appropriate. Conventionally known ingredients can be used in these formulations.
表面に形成するレジンモルタル層は、アクリルエマルジ
ョンとセメントとの混合物からなるものとするが、この
場合のアクリルエマルジゴンのアクリル系樹脂としては
、アクリル酸アルキルエステル樹脂、アクリル酸・アク
リル酸アルキルエステル共重合物、メタクリル酸・アク
リル酸アルキルエステル共重合物、エチレン・アクリル
酸アルキルエステル共重合物、塩化ビニル・アクリル酸
アルキルエステル共重合物、メタクリル酸アルキルエス
テル樹脂、アクリル酸アルキルエステル・エボキシ共重
合物等の適宜なものを使用するこができる。，Ｖ機質板
の使用環境等を考慮して適宜に選択することができる．
これらのアクリル系樹脂と水との配合は広い範囲で可能
であり、たとえば樹脂：水の重量比で、２０〜７ ０
： １００程度とすることができ、必要に応じて乳化剤
の所要量を使用することができる．レジンモルタル層を
形戒するためのアクリルエマルジョンとセメントとの配
合比は、アクリルエマルジョン固形分とセメントとの混
合物に対して、固形分の１Ｉｔ．量比を１０〜７０％程
度とするのが好ましい。より好適には３０〜５０％程度
とする。The resin mortar layer formed on the surface shall be made of a mixture of acrylic emulsion and cement. In this case, the acrylic resin of the acrylic emulsion may include acrylic acid alkyl ester resin, acrylic acid/acrylic acid alkyl ester resin, etc. Polymers, methacrylic acid/acrylic acid alkyl ester copolymer, ethylene/acrylic acid alkyl ester copolymer, vinyl chloride/acrylic acid alkyl ester copolymer, methacrylic acid alkyl ester resin, acrylic acid alkyl ester/epoxy copolymer You can use any appropriate one such as , can be selected appropriately considering the environment in which the V-organic plate will be used. These acrylic resins and water can be mixed in a wide range, for example, the weight ratio of resin:water is 20 to 70.
: It can be about 100, and the required amount of emulsifier can be used as needed. The mixing ratio of the acrylic emulsion and cement for forming the resin mortar layer is 1 It. It is preferable that the quantitative ratio is about 10 to 70%. More preferably, it is about 30 to 50%.
７０％以上の場合にはコストが上昇し、また成形しにく
くなる。固形分が１０％以下では効果にムラが生じる。When it is 70% or more, the cost increases and it becomes difficult to mold. If the solid content is less than 10%, the effect will be uneven.
この発明の燕機質板は、たとえば第１図に示したように
、抄造法算によって製造した無機質シート（１）の表面
に、上記の通りのアクリルエマルジョンとセメントとの
混合物からなるレジンモルタル層（２）を形成し、これ
を湿ｐ！！．養生および／またはオートクレープ芥生す
ることにより製遣ずることができる。For example, as shown in FIG. 1, the swallow matrix board of the present invention has a resin mortar layer made of a mixture of acrylic emulsion and cement as described above on the surface of an inorganic sheet (1) manufactured by a papermaking process. (2) and wet p! ! ．． It can be manufactured by curing and/or autoclaving.
その後、表面化粧のための塗月、たとえばアクリルエマ
ルジョン塗料を塗布することができる。Thereafter, a surface cosmetic coating, for example an acrylic emulsion paint, can be applied.
塗膜の密着性は良好なものとなる。The adhesion of the coating film becomes good.
（作 用）
この発明においては、レジンモルタル層によって表面披
覆ずるため、表面層の透湿抵抗を向上させ、表面乾燥に
よる無機質板の反り変形を仰止することができる．
また、このレジンモルタルの存在によって、塗膜の密着
性は著しく向上ずる。塗膜の剥離を抑止することができ
る。(Function) In this invention, since the surface is covered with a resin mortar layer, the moisture permeation resistance of the surface layer can be improved and the warping deformation of the inorganic board due to surface drying can be prevented. Furthermore, the presence of this resin mortar significantly improves the adhesion of the coating film. Peeling of the paint film can be suppressed.
（実施例｝
以下、実施例を示し、さらに詳しくこの発明の熟機質仮
について説明する。(Example) Hereinafter, examples will be shown and the ripening material of the present invention will be explained in more detail.
まず、次の配合からなる混合物スラリーより、ハチェッ
クマシンでシート製造する。First, a sheet is manufactured using a Hacheck machine from a mixture slurry having the following composition.
ボルトランドセメント ６０（重量部）シリカ６）
４ ０
アスベスト ２ｏ
パルプ １
このシートの表面にボルトランドセメントとアクリルエ
マルジョンとの混合物を吹付け塗布する。Boltland Cement 60 (parts by weight) Silica 6)
4 0 Asbestos 2o Pulp 1 A mixture of Bortland cement and acrylic emulsion is spray applied to the surface of this sheet.
この時の混合物の配合割合は表１に示した通りの種々の
ものとした。また、エマルジョンとしては、アクロナー
ル３０３２ （油化バーディッシュ社製）を用いた。こ
れをプレス脱水して成形した。この時の圧力は８ ０
１ｑｒ ／ ｄとした。The blending proportions of the mixture at this time were varied as shown in Table 1. Moreover, Acronal 3032 (manufactured by Yuka Bardish Co., Ltd.) was used as the emulsion. This was press dehydrated and molded. The pressure at this time is 80
It was set as 1qr/d.
次いで、湿熟養生とオートクレープ養生の２種の養生を
区分して行った。湿熟養生は８０″Ｃ、１００％Ｒ Ｈ
ｉ生槽で、またオートクレープ養生は１６５゜Ｃ、６
時間の条件で行った。Next, two types of curing were carried out: moist curing and autoclave curing. Humid aging at 80″C, 100%RH
i in a storage tank, and autoclave curing at 165°C, 6
It was done under the time constraints.
このシートにアクリルエマルジョンｆｆｌ ？−１を塗
商した。塗布量は５０ｔ／ｎ−ｒ（固形分）とし、焼付
は、１４０℃１０分間で行った．
この無機質板の反り変形と塗膜の密着性を評価した。評
価試験は、表面温度が８０゜Ｃになるように、第２図に
示したように、アスファルトーフィング（３）上に置い
た試料（４）の表面を赤外線ランプ（５）により加熱す
ることにより行った。Acrylic emulsion ffl on this sheet? -1 was printed. The coating amount was 50t/nr (solid content), and baking was performed at 140°C for 10 minutes. The warping deformation of this inorganic board and the adhesion of the coating film were evaluated. In the evaluation test, the surface of the sample (4) placed on the asphalt topping (3) was heated with an infrared lamp (5), as shown in Figure 2, so that the surface temperature reached 80°C. This was done by
試料（４）の大きさは、９００ ｘ４００ （關）と
し、両端の変位量と中央の変位量との差を測定して反り
の大きさとした。The size of sample (4) was 900 x 400 (square), and the difference between the amount of displacement at both ends and the amount of displacement at the center was measured and determined as the amount of warpage.
塗膜の密着性については、試ｖｌｌ４（４）を凍結融解
（ＡＳＴＭ Ａ法）し、塗膜の状態について評価する
こととした．
これらの結果を示したものが表１である。Regarding the adhesion of the coating film, sample vll4 (4) was freeze-thawed (ASTM A method) and the condition of the coating film was evaluated. Table 1 shows these results.
比較例は、アクリルエマルジョンとセメントとの配合比
が好ましくない例を示している。The comparative example shows an example in which the blending ratio of acrylic emulsion and cement is unfavorable.
表１の結果から明らかなように、この発明の実施例の場
合には、いずれも反りの大きさが１．０ｍｓｎ以下程度
と極めて小さく、密着性にも優れていることがわかる。As is clear from the results in Table 1, in all the examples of the present invention, the magnitude of warpage was extremely small, about 1.0 msn or less, and it was found that the adhesiveness was also excellent.
表１
（発明の効果）
この発明により、以上詳しく説明した通り、表面乾燥に
よる反り変形が抑止され、また塗膜の審着性の向上した
ｊ！′！機質板が提供される。Table 1 (Effects of the Invention) As explained in detail above, this invention suppresses warping and deformation due to surface drying, and improves the adhesion of the coating film. ′! A texture board is provided.
第１図は、この発明のｊ無機質板を例示した斜視口であ
る。第２図は、その↑、！性評価の方法を示した開面図
である．
第３図は、抄造法による製造を例示した工程断面図であ
る。
１・・・無機質シート
２・・・レジンモルタル層
（注）１）全体厚み ５間
２）密着竹 Ａ・・・剥離なしFIG. 1 is a perspective view illustrating the inorganic plate of the present invention. Figure 2 shows that ↑! FIG. FIG. 3 is a process cross-sectional view illustrating manufacturing by a papermaking method. 1... Inorganic sheet 2... Resin mortar layer (Note) 1) Overall thickness 5 spaces 2) Adhesive bamboo A... No peeling
Claims (3)
なるレジンモルタル層を無機質板表面に配設してなるこ
とを特徴とする無機質板。(1) An inorganic board characterized by having a resin mortar layer made of a mixture of acrylic emulsion and cement disposed on the surface of the inorganic board.
合物重量に対して１０〜７０％である請求項（１）記載
の無機質板。(2) The inorganic board according to claim 1, wherein the solid content of the acrylic emulsion is 10 to 70% based on the weight of the mixture with cement.
る請求項（１）記載の無機質板。(3) The inorganic board according to claim (1), wherein a paint film is formed on the resin mortar layer.