JPH03146701A - Stocking - Google Patents
StockingInfo
- Publication number
- JPH03146701A JPH03146701A JP28070689A JP28070689A JPH03146701A JP H03146701 A JPH03146701 A JP H03146701A JP 28070689 A JP28070689 A JP 28070689A JP 28070689 A JP28070689 A JP 28070689A JP H03146701 A JPH03146701 A JP H03146701A
- Authority
- JP
- Japan
- Prior art keywords
- yarn
- polyurethane elastic
- filaments
- stockings
- core
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は、伸縮性に優れ、心地良い締付は力が柔らかく
作用する着用感を提供し、且つ透明感のある美しい外観
を備えるストッキングに関するものである。DETAILED DESCRIPTION OF THE INVENTION [Field of Industrial Application] The present invention relates to stockings with excellent elasticity, comfortable tightening that provides a feeling of wearing with soft force, and a transparent and beautiful appearance. It is something.
従来より、ストッキング用の原糸としては、伸縮性の良
好な熱可塑性合成繊維の嵩高捲縮加工糸強撚トルク糸等
が用いられてきた。BACKGROUND ART Hitherto, bulky crimped yarns of thermoplastic synthetic fibers with good elasticity, high-twist torque yarns, and the like have been used as yarns for stockings.
また、近年では、シングルカバード・ヤーン（ＳＣＹ）
、あるいはダブルカバード・ヤーン（ＤＣＹＩ と呼
ばれるストッキング用原糸が多用されている。これは、
ポリウレタン弾性糸（スパンデックス）のモノフィラメ
ント糸を芯にし、その上にナイロン糸をカバリングした
ものであって、伸長弾性回復力に極めて優れ、このよう
な糸を用いたストッキングは一般に６サポートタイプ”
と呼ばれて市場に多く出回っている。In recent years, single covered yarn (SCY)
, or double covered yarn (DCYI) is often used for stockings.
Stockings made of polyurethane elastic yarn (spandex) monofilament yarn as a core and covered with nylon yarn have excellent elongation elastic recovery ability, and stockings using this type of yarn are generally 6-support type.
It is called and sold in large numbers on the market.
そして、最近は特に締付は力の大なるスト、キングが、
脚を美しく見せ、且つ脚の疲れを緩和する効果を奏する
ものとして流行してきている。これは、７０デニール、
極端なものは１４０デニルの太いポリウレタン弾性糸に
ナイロンヲカハリングしたものであって、従来にない締
付は強力を発揮せしめたものである。And recently, especially tightening is a powerful strike, the king,
It has become popular because it makes the legs look beautiful and has the effect of relieving leg fatigue. This is 70 denier,
The most extreme type is a 140 denier thick polyurethane elastic thread wrapped with nylon wrapper, which has an unprecedented tightening force.
しかしながら、上述の如くポリウレタン弾性糸を芯糸と
するカバリング糸を用いたストッキングは、締付は効果
のみを狙ったものであって、風合が硬く、極端にきつい
感じを与えるものであった。However, as described above, stockings using covering yarns with polyurethane elastic yarns as core yarns are tightened only for effect, and have a hard feel and an extremely tight feel.
また、締付は強力を強くしようとしてポリウレタン弾性
糸を太くすればするほど透明感が劣り、やぼったいイメ
ージとなることを免れなかった。In addition, the thicker the polyurethane elastic thread was made in order to increase the tightening force, the less transparent it became, resulting in a dull image.
更に、ポリウレタン弾性糸の使用量が堆えるとその分だ
け耐摩耗強度が弱くなり、ポリウレタンが表面に目をむ
いたり、洗濯により編地が伸びきって復帰しなくなった
りというような問題も引き起こされた。Furthermore, as the amount of polyurethane elastic yarn used increases, the abrasion resistance weakens accordingly, causing problems such as the polyurethane peeling on the surface or the knitted fabric stretching out after washing and not returning to its original shape. Ta.
本発明は、このような事情に鑑みなされたものであって
、充分な伸縮性と締付は強力を有するとともに着用時の
風合が柔らかく、且つ透明感に優れたストッキングの提
供を目的とするものである。The present invention was made in view of the above circumstances, and aims to provide stockings that have sufficient elasticity and strong tightening properties, are soft to the touch when worn, and have excellent transparency. It is something.
〔課題を解決するための手段〕
上記目的を達成するために、本発明のスト・２キングは
、収縮率の異なる２成分以上のポリマーで構成された複
合糸と、ポリウレタン弾性糸を芯糸とするカバリング糸
を１本交互に配列せしめて少なくともレッグ部を編成し
てなるという構成をとる。[Means for Solving the Problems] In order to achieve the above object, the striker/two-king of the present invention uses a composite yarn composed of two or more polymers having different shrinkage rates and a polyurethane elastic yarn as a core yarn. At least the leg portions are knitted by alternately arranging one covering yarn.
また、上記複合糸としては、ポリウレタン弾性体とポリ
カブラミドとを並列または偏心芯鞘型に接合してなり、
総繊度が５〜５０ｄ、フィラメント構成本数が１〜１０
本の範囲内の捲！Ｉｉｆ複合糸を用いることが好ましい
。Moreover, the above-mentioned composite yarn is made by joining polyurethane elastic body and polycabramide in parallel or eccentric core-sheath type,
Total fineness is 5-50d, number of filaments is 1-10
Turn within the scope of the book! Preferably, Iif composite yarns are used.
このような構成において、複合糸はその特徴である自己
捲縮の発現によって柔らかいタッチの優れた伸縮性能を
発揮し、ポリウレタン弾性糸を芯糸とするカバリング糸
による締付は力を柔軟に作用せしめる。In this structure, the composite yarn exhibits excellent stretchability with a soft touch due to its characteristic self-crimping, and the tightening by the covering yarn with polyurethane elastic yarn as the core yarn allows the force to be applied flexibly. .
また、複合糸とカバリング糸とを交編することにより、
充分な伸縮性を奏するのみならず、着用時における透明
感の優れたものが得られる。In addition, by inter-knitting the composite yarn and covering yarn,
Not only does it have sufficient elasticity, but it also provides excellent transparency when worn.
更に、洗濯後も複合糸の自己捲縮特性が作用し、復帰力
に優れ、編地が伸びきってしまうというようなことがな
い。Furthermore, even after washing, the self-crimping properties of the composite yarn remain in effect, providing excellent return power and preventing the knitted fabric from becoming completely stretched.
以下、本発明に係るストッキングの実施例を図面に基づ
き説明する０本発明でいうストッキングとは、膝上まで
のオーバーニー・ストッキング、大腿部付根までのフル
・レングス・ストッキング、及びパンティ部とストッキ
ング部とを一体にしたパンティストッキングのすべてを
含むものである。Below, embodiments of stockings according to the present invention will be explained based on the drawings. Stockings in the present invention include over-knee stockings that reach above the knee, full-length stockings that extend to the base of the thigh, and panty and stockings. This includes all pantyhose that combine the parts.
第１図は、本発明をパンティストッキングに適用した例
を示している。このパンティストッキング（Ｐ） は
、通常の如く、パンティ部（ｌ〉、レッグ部（２）、及
びフート部（３）の３部位より構成され、パンティ部（
１） はウーリーナイロンやポリウレタン系カバリン
グ糸等から適宜選択された原糸で、伸縮性を有する編組
織に編成されている。FIG. 1 shows an example in which the present invention is applied to pantyhose. This pantyhose (P), as usual, is composed of three parts: a panty part (l), a leg part (2), and a foot part (3).
1) is a raw yarn appropriately selected from woolly nylon, polyurethane covering yarn, etc., and is knitted into a stretchable knitted structure.
そして、レッグ部（２）及びフート部（３）は、第２図
に示すように、複合糸（４）とポリウレタン弾性糸を芯
糸とするカバリング糸（５）とを１本交互に用いて＆［
されている。The leg portion (2) and foot portion (3) are made by alternately using one composite yarn (4) and one covering yarn (5) having a polyurethane elastic yarn as the core yarn, as shown in Fig. 2. &[
has been done.
本発明でいう複合糸（４）とは、収縮の異なる２威分以
上のポリマーを別々に供給し、紡出時に両者を貼り合わ
せてなる、いわゆるコンジュゲート・ヤーンである。本
実施例では、特に伸縮性並びに耐久性に優れ、且つ高速
条件下で安定した編立の可能な、ポリウレタン弾性体と
ポリカブラミドとを並列型又は偏心芯鞘型に接合した拷
縮腹合糸を用いている。The composite yarn (4) referred to in the present invention is a so-called conjugate yarn in which two or more polymers with different contraction rates are separately supplied and the two are bonded together during spinning. In this example, we used a crimped diagonal yarn in which polyurethane elastic material and polycabramide are joined in a parallel type or eccentric core-sheath type, which has particularly excellent elasticity and durability, and can be knitted stably under high-speed conditions. I am using it.
この捲１１複金糸は、捲縮数が５コ／ｃｍ以上であって
、捲縮振巾が繊維直径の５倍以下、放縮後の捲縮伸長率
が５０％以下であることを特徴とするものである。即ち
、捲縮数が５コ／ ｃ ｍ以上、捲縮振巾が繊維直径の
５倍以下であること、好ましくは捲縮数が８コ／ ｃ
ｍ以上、捲縮振巾が２〜４倍であることが、第３図に示
すようなゆるやかな波状捲縮を発現することを意味して
いる。そして、このような波状捲縮を有する状態でコン
ブ又はチーズに捲かれており、放縮後の捲縮伸張率が５
０％以下、好ましくは４０％以下であることが、コンブ
又はチーズからの解舒後も捲縮型態変化が極めて少ない
安定した複合糸であることを意味するものである。これ
ら捲縮数、捲縮振巾、及び放縮後の捲縮伸張率が上記の
範囲を外れると、編立時の解舒張力変動が大きくなり、
編地に繞設が発生するのみならず、糸切れや目飛びが発
生することにもなり好ましくない。This 11-wound double gold thread has the number of crimps of 5 crimps/cm or more, a crimp width of 5 times or less of the fiber diameter, and a crimp elongation rate of 50% or less after release. It is something to do. That is, the number of crimps is 5 crimps/cm or more, the crimp width is 5 times or less the fiber diameter, and preferably the number of crimps is 8 crimps/cm.
m or more and the crimp width is 2 to 4 times as large, which means that gentle wavy crimp as shown in FIG. 3 is produced. Then, it is rolled up into kelp or cheese with such wavy crimp, and the crimp elongation rate after release is 5.
A content of 0% or less, preferably 40% or less, means that the composite yarn is stable and shows very little change in crimp form even after unraveling from kelp or cheese. If the number of crimp, crimp width, and crimp elongation rate after unwrapping are out of the above range, the unwinding tension fluctuation during knitting will become large.
This is undesirable because it not only causes stringiness in the knitted fabric, but also causes yarn breakage and skipped stitches.
また、湧水収縮率は７〜１７％の範囲内であることが好
ましい。即ち、これが７％未満では編立後の軌処理によ
っても充分に捲縮が発現せず、方１７％より大であると
、過度の収縮により製品として寸法不足になるという問
題を有し、いずれも不適である。Moreover, it is preferable that the shrinkage rate of spring water is within the range of 7 to 17%. That is, if it is less than 7%, sufficient crimp will not occur even during track processing after knitting, and if it is more than 17%, there will be a problem that the product will be insufficient in size due to excessive shrinkage. is also inappropriate.
ここで、上述の４つの測定値について簡単に説明すると
、随縮数、捲縮振巾及び放縮後の捲縮伸張率とは、糸を
コツプ又はチーズから解舒後２５二１°Ｃ５６５±３％
ＲＨの瓜湿度下で１時間ｈ１縮させ、これを試料として
下記の測定を行うものである。Here, to briefly explain the four measurement values mentioned above, the number of contractions, the crimp width, and the crimp elongation rate after unwinding are 2521°C565± 3%
The sample was subjected to h1 shrinkage for 1 hour under RH humid conditions, and the following measurements were performed using this as a sample.
捲縮数は、試料に０．２ ｇ ／ ｄの荷重を掛けて試
料長５ｃｍを取り出し、次いで取り出した試料５ｃｍ間
の捲縮数を測定して１ｃｍ当りにＩ臭算する。The number of crimps is determined by applying a load of 0.2 g/d to the sample, taking out a sample length of 5 cm, then measuring the number of crimps between the 5 cm of the sample, and calculating the number of crimp per 1 cm.
捲！Ｉｉｉ振巾及び繊維直径は、試料を２枚のプレパラ
ートガラスで挟み顕微鏡下で測定するか、あるいは写真
を取って写真の実測から算出する。本発明ではｌ！縮振
巾とは第３図のＬであり、繊維直径とはｄである。Roll! III. The amplitude and fiber diameter are measured by sandwiching the sample between two slide glasses under a microscope, or by taking a photograph and calculating it from the actual measurement of the photograph. In the present invention, l! The contraction width is L in FIG. 3, and the fiber diameter is d.
また、放！！ｉ！後の捲縮伸張率とは、コツプあるいは
チーズから直接１０００ｄ相当のカセを取り、放縮させ
て無荷重下で捲縮を発現させた後、２００ｇの荷重を１
分間掛け、次いで２００ｇ荷重を２．５０ ｍ ｇ荷重
に変更して２時間放置した後のカセ長さ１０を測定し、
次いで２００ｇの荷重を１分間１１）けた１女のカセ長
さｅ、を測定し下式で算出した埴である。Release again! ! i! The subsequent crimp elongation rate is calculated by taking a skein equivalent to 1000 d directly from a cot or cheese, letting it shrink to develop crimp under no load, and then applying a load of 200 g to 1
The skein length 10 was measured after applying for a minute, then changing the 200 g load to a 2.50 m g load and leaving it for 2 hours,
Next, the length e of the first girl's skein was measured under a load of 200 g for 1 minute (11), and the length e was calculated using the following formula.
そして、湧水収縮率は、コツプあるいはチーズから直を
妾（工数したｌ０００ｄ＋目当のカセに２００ｇの荷重
を掛け１分後のカセ長さ１２を測定する。The shrinkage rate of spring water is determined by measuring the length of the skein after 1 minute by applying a load of 200 g to the skein (1000 d of man-hours + the desired skein) and measuring the length of the skein 1 minute later.
次いで２５０ｍｇの荷重を掛けた状態で湧水中に１５分
間浸漬し１時間風乾した後、再度２００ｇの荷重下でカ
セ長さｌ、を測定し下式で算出する。Next, the sample was immersed in spring water for 15 minutes with a load of 250 mg applied thereto, air-dried for 1 hour, and then the length l of the skein was measured again under a load of 200 g and calculated using the formula below.
尚、ポリウレタン弾性体としては、ソフトセグメントを
ポリへキサメチレンカーボネートを主成分とするものが
好ましく、ポリカブラミドとの接合重量比率は７／３〜
３／７の範囲とする。The polyurethane elastic body is preferably one whose main component is polyhexamethylene carbonate, and the weight ratio of the soft segment to polycabramide is 7/3 to 7/3.
The range is 3/7.
以上、本発明に係るストッキングに用いる複合糸として
好適なものの一例を挙げて説明したが、本発明の構成の
上ではこの複合糸に限定されることなく、異威分間の収
縮率差により自己捲縮性を有するものであれば適用する
ことができる。The above description has given an example of a compound yarn suitable for use in the stockings according to the present invention, but the structure of the present invention is not limited to this compound yarn. Any material can be used as long as it has shrinkability.
そして、この複合糸は、単糸フィラメントの繊度を３〜
３Ｑｄ、フィラメント構成本数を１〜ＩＯ本とし、総繊
度を５〜５０ｄとするが、本発明で（，１特に透明感を
求めることから、総繊度を５〜３０ｄ、フィラメント構
成本数を１〜６本の範囲内とすることが好ましい。即ち
、この範囲を外れると、耐久性が不充分となるか、或は
透明感及び風合がひどく劣るかのいずれかの欠点を有す
るものとなり不適である。The fineness of the single filament of this composite yarn is 3 to 3.
3Qd, the number of constituting filaments is 1 to IO, and the total fineness is 5 to 50d. However, in the present invention (1), since transparency is particularly sought, the total fineness is 5 to 30d, and the number of filaments is 1 to 6. It is preferable to keep it within the range specified in this book.In other words, if it falls outside of this range, it will be unsuitable because it will have either insufficient durability or extremely poor transparency and texture. .
そして、もう一方のカバリング糸（５）は、２０〜１４
０ｄのポリウレタン弾性糸に、ナイロン糸をカバリング
したものである。このナイロン糸は、繊度を１０〜２０
ｄ、フィラメント構成本数を１〜７本、好ましくは１３
〜１５ｄ、２〜３本とするウーリー糸、ケンネル糸等か
ら適宜遣択される。And the other covering thread (5) is 20 to 14
0d polyurethane elastic thread covered with nylon thread. This nylon thread has a fineness of 10 to 20
d. The number of filaments is 1 to 7, preferably 13.
-15d, 2 to 3 woolly yarns, kennel yarns, etc., as appropriate.
そして、カバリングをシングルにするかダブルにするか
は、上記ポリウレタン弾性糸の太さと求める締付しナパ
ヮーとから選定することができる。Whether the covering should be single or double can be selected based on the thickness of the polyurethane elastic thread and the desired tightening napa.
本発明に係るストッキングにおいては、上記カバリン糸
（５）と前述した複合糸（４）とを１本ずつ交互に交編
するが、これは、編地面の美しさを考慮したものである
。即ち、交ｉｍｍを１：２或は２：１等のような組織に
すると、両原糸（４） 、 （５）の特性がアンバラン
スに編地面に現出することとなり、外観上好ましくない
。In the stockings according to the present invention, the Kavalin yarn (5) and the composite yarn (4) described above are alternately knitted one by one, but this is done in consideration of the beauty of the knitted surface. In other words, if the cross-imm ratio is 1:2 or 2:1, the characteristics of both yarns (4) and (5) will appear unbalanced on the knitted surface, which is unfavorable in terms of appearance. .
〈具体例）
複合糸として、以下に述べる方法で捲縮複合糸を製造し
た。<Specific Example> As a composite yarn, a crimped composite yarn was manufactured by the method described below.
まず、ソフトセグメント成分が数平均分子量２０００の
ポリへキサメチレンカーボネート７０部とポリへキサメ
チレンアジペート３０部、ジイソンアネート化合物が４
，４′−ジフェニルメタンジイソシアネト、鎖伸張剤が
１．４−ブタンジオールからなるショアー硬度９５の熱
可塑性ポリウレタン弾性体とポリカブラミドとを別々に
溶融し、しかる後、両成分の接合重量比率５１５で並列
型に接合して単糸３０ｄの未延伸糸を捲取った。First, the soft segment components were 70 parts of polyhexamethylene carbonate with a number average molecular weight of 2000, 30 parts of polyhexamethylene adipate, and 4 parts of a diisonanate compound.
, 4'-diphenylmethane diisocyanate, and polycabramide and a thermoplastic polyurethane elastomer with a Shore hardness of 95 consisting of 1.4-butanediol as a chain extender are separately melted, and then the weight ratio of both components is 515. The undrawn yarns of 30 d of single yarns were joined in parallel and wound up.
そして、この未延伸糸を、２個のローラー（第１０−ラ
ーが加熱ローラー）の間に長さ２０ｃｍの熱板プレート
を設けた延伸機を用いて下記の条件のもとに延伸し、２
０ｄ／２ｆのフィラメント糸を得た。Then, this undrawn yarn was drawn under the following conditions using a drawing machine equipped with a 20 cm long hot plate between two rollers (the 10th roller is a heating roller).
A filament yarn of 0d/2f was obtained.
延伸速度・・・６００ｍ／分
延伸倍率・・・３．５０倍
加熱ローラー温度・・・２５°Ｃ
熟仮プレート温度・・・２５°Ｃ
次いで、２つのローラー間に４０ｃｍの熱板プレートを
設置した弛緩熱処理装置を用い、送り出しローラー速度
４００ｍ／分、熱板プレート温度を１２０℃に固定し、
引き出しローラー速度を２２０ｍ／分として弛緩熱処理
した後コツプに捲取り、熱処理時の弛緩率を４５％とす
る複合糸を完成した。Stretching speed: 600 m/min Stretching ratio: 3.50 times Heating roller temperature: 25°C Temporary aging plate temperature: 25°C Next, a 40cm hot plate was installed between the two rollers. Using a relaxation heat treatment device, the delivery roller speed was set at 400 m/min and the hot plate temperature was fixed at 120°C.
After the yarn was subjected to relaxation heat treatment at a drawing roller speed of 220 m/min, it was wound into a coppice to complete a composite yarn with a relaxation rate of 45% during heat treatment.
この複合糸の捲縮数は２５コ／ ｃ ｍ 、捲縮振巾／
繊維直径は２．７、放縮後の捲縮伸張率及び湧水収縮率
は夫々１０％とｌ０１５％であった。The number of crimp of this composite yarn is 25/cm, the crimp width/
The fiber diameter was 2.7, and the crimp elongation rate and spring shrinkage rate after release were 10% and 1015%, respectively.
また、カバリング糸として、２０ｄのポリウレタン弾性
糸に１３ ｄ１５ ｆのウーリーナイロンをダブルカバ
リングしたものを用い、４０のシームレススト、キング
ｋＪＡ機（回転数６００ｒｐｍ）により前記複合糸と交
編した田地でレッグ部及びフート部を形成したストッキ
ングを得た。In addition, as a covering yarn, a 20 d polyurethane elastic yarn double-covered with 13 d 15 ft woolly nylon was used, and the leg was interknitted with the composite yarn using a 40 seamless strike, King kJA machine (rotation speed 600 rpm). A stocking having a section and a foot section was obtained.
そして、比較例として、実施例の複合糸１００％で編成
したもの（比較例Ａ）、実施例のカバリング糸１００％
で編成したもの（比較例Ｂ）、及び同し複合糸とカバリ
ング糸をｌ：３で交編したもの（比較例Ｃ）を作り、上
記の実施別品とともに３０名による着用テストを行った
。その評価をまた、これらのストッキングを洗濯用ネッ
トに入れて洗濯機で洗濯した後、約６時間着用し、再度
洗濯するというサイクルを３サイクル繰り返したところ
、比較例Ｂのものは復帰力が劣り元の寸法よりも伸びて
しまいがちであったが、実施例のものは洗４１も元寸法
を確保しうるものであった。As a comparative example, one knitted with 100% of the composite yarn of the example (Comparative example A), and one knitted with 100% of the covering yarn of the example.
(Comparative Example B) and one in which the same composite yarn and covering yarn were interknitted at a l:3 ratio (Comparative Example C) were made, and a wear test was conducted by 30 people along with the above-mentioned separate products. In addition, when these stockings were placed in a laundry net, washed in a washing machine, worn for about 6 hours, and washed again for 3 cycles, the results showed that the stockings in Comparative Example B had poor recovery power. Although it had a tendency to expand beyond its original dimensions, in the example, the wash 41 was also able to maintain its original dimensions.
以上述べた通り、本発明のストッキングは、複合糸がそ
の自己捲縮特性によって柔らかい夕、チの優れた伸縮性
を発揮し、ポリウレタン弾性糸を芯糸とするカバリング
糸による締付は力を硬い締付は感でなく心地良く作用せ
しめるものである。As described above, the stockings of the present invention exhibit excellent elasticity with soft elasticity due to the self-crimping property of the composite yarn, and the tightness of the covering yarn with polyurethane elastic yarn as the core yarn makes the force hard. Tightening is not about feeling, but about feeling.
また、充分な伸縮力を備えていながら透明感に（２れ、
且つ編地表面の外観も美麗である。In addition, it has sufficient elasticity and transparency (2).
Moreover, the appearance of the surface of the knitted fabric is beautiful.
更に、洗濯後等の復帰力にも優れており、洗濯と着用と
の繰り返しによっても元寸法がくずれるというようなこ
とがない。Furthermore, it has excellent recovery ability after washing, and does not lose its original dimensions even after repeated washing and wearing.
第１図は本発明のストッキングの一実施例を示す正面図
、第２図はその編組織説明図、第３図は同実施例に用い
た複合糸の説明図である。
（１）・・・パンティ部、 （２） ・・・レノク
部（３）・・・フート部、（４）・・・複合糸。
（５）・・・カバリング糸
（Ｐ） ・・・パンティストッキング。
第
図
第
図
第
図FIG. 1 is a front view showing an embodiment of the stocking of the present invention, FIG. 2 is an explanatory diagram of its knitting structure, and FIG. 3 is an explanatory diagram of the composite yarn used in the same embodiment. (1)...Panty part, (2)...Length part (3)...Foot part, (4)...Composite yarn. (5)...Covering thread (P)...Pantyhose. Figure Figure Figure
Claims (2)
た複合糸（４）と、ポリウレタン弾性糸を芯糸とするカ
バリング糸（５）とを１本交互に配列せしめて少なくと
もレッグ部（２）を編成してなるストッキング。(1) One composite yarn (4) composed of two or more polymer components having different shrinkage rates and one covering yarn (5) having a polyurethane elastic yarn as the core yarn are alternately arranged so that at least the leg portion (2 ) are knitted into stockings.
性体とポリカプラミドとを並列または偏心芯鞘型に接合
してなり、総繊度が５〜５０ｄ，フィラメント構成本数
が１〜１０本の範囲内の捲縮複合糸であるストッキング
。(2) The composite yarn (4) according to claim 1 is formed by joining a polyurethane elastic body and a polycapramide in a parallel or eccentric core-sheath type, has a total fineness of 5 to 50 d, and has a filament composition of 1 to 10. Stockings that are crimped composite yarns within the range.