JPH0290412A - Electric cable - Google Patents
Electric cableInfo
- Publication number
- JPH0290412A JPH0290412A JP63242821A JP24282188A JPH0290412A JP H0290412 A JPH0290412 A JP H0290412A JP 63242821 A JP63242821 A JP 63242821A JP 24282188 A JP24282188 A JP 24282188A JP H0290412 A JPH0290412 A JP H0290412A
- Authority
- JP
- Japan
- Prior art keywords
- sheath
- boric acid
- electric cable
- rubber composition
- ant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
〔産業上の利用分野〕
この発明は、優れた防蟻性を有する電気ケーブルに関す
る。DETAILED DESCRIPTION OF THE INVENTION [Industrial Field of Application] The present invention relates to an electric cable having excellent termite resistance.
従来よりシロアリなどによる電気ケーブルの食害を防止
するために種々の防蟻電気ケーブルが用いられている。Various types of termite-proof electrical cables have been used to prevent damage to electrical cables caused by termites and the like.
これら防蟻ケーブルとしては、例えばケーブル絶縁線心
上に金属シースあるいは金属テープを形成したものや、
ケーブルシースの上にナイロンジャケットを形成したも
の、あるいはケーブル絶縁線心上に高密度ポリエチレン
などの硬質プラスチック製のシースを設けたものなどが
用いられている。These termite-proof cables include, for example, cables with a metal sheath or metal tape formed on the insulated cable core,
A cable with a nylon jacket formed on top of the cable sheath, or a cable with a sheath made of hard plastic such as high-density polyethylene over an insulated cable core are used.
しかし、金属シースや金属テープを形成したケーブルは
、ケーブル自体が硬くて曲げに＜＜、布設工事等の工事
の際、取り扱い作業性が悪く、ケーブルの価格が上昇す
る。また、この種の電気ケーブルでは、金属シースある
いは金属テープ自体はシロアリによって食害されないが
、金属テープあるいは金属シースの外被のコム、プラス
チック防食層が食害された場合に、金属シースあるいは
金属テープが腐食作用によって侵されてしまうと言う欠
点もある。また、ナイロンジャケットを形成した電気ケ
ーブルは、やはりケーブル自体が硬くて曲げにくく取扱
い作業性が悪い。また、ナイロンジャケットを形成する
ために特別の技術および設備が必要であり、価格が高く
なるという欠点もある。さらに、硬質プラスチック製シ
ースを設けた電気ケーブルも、やはりケーブル自体力上
硬くて取扱いが不便であり、硬質プラスチック製シース
を形成するために大型の押出機を用いて高温で押出被覆
せねばならず、実用工種々の制約を受けるなどの欠点が
ある。However, a cable formed with a metal sheath or metal tape is hard and bends easily, and is difficult to handle during construction such as installation work, resulting in an increase in the price of the cable. In addition, in this type of electrical cable, the metal sheath or metal tape itself is not damaged by termites, but if the comb or plastic corrosion protection layer of the metal tape or metal sheath's outer sheath is damaged, the metal sheath or metal tape will corrode. It also has the disadvantage of being eroded by the action. Further, the electric cable formed with a nylon jacket is hard and difficult to bend, and has poor handling efficiency. Another disadvantage is that special techniques and equipment are required to form the nylon jacket, which increases the price. Furthermore, electrical cables with hard plastic sheaths are hard and inconvenient to handle, and must be extruded at high temperatures using a large extruder to form the hard plastic sheath. However, there are drawbacks such as being subject to various practical limitations.
この発明では、硼酸もしくは、硼酸を吸着含浸させた無
定形シリカとこれらの化合物の熱分解温度以下の成形温
度を有するゴム組成物あるいは合成樹脂組成物とからな
る防蟻層を設けることをその解決手段とした。In this invention, the solution is to provide an anti-termite layer made of boric acid or amorphous silica adsorbed and impregnated with boric acid, and a rubber composition or synthetic resin composition having a molding temperature below the thermal decomposition temperature of these compounds. It was used as a means.
以下、図面を参照してこの□発明の詳細な説明する。Hereinafter, this invention will be described in detail with reference to the drawings.
まず、請求項１記載に係る電気ケーブルについて述べる
。First, an electric cable according to claim 1 will be described.
第１図は、この電気ケーブルの一例を示すもので、図中
符号１は電気ケーブルである。この電気ケーブル１は、
中心層の銅、アルミニウムなどの金属導体２と、この導
体２を絶縁するエチレンプロピレンゴム、ポリエチレン
、ポリ塩化ビニルなどで形成された絶縁体３と、この絶
縁体３を被覆するクロロプレンゴム、クロロスルフォン
化ホリエチレン、ポリ塩化ビニル、ポリエチレンなどの
成形温度が２８０°Ｃ以下であるゴム組成物あるいは合
成樹脂組成物で形成された防蟻層となるシース４とから
構成されている。そして、このシース４には硼酸か含有
されている。この硼酸には、オルトホウ酸、メタホウ酸
、四ホウ酸などが用いられる。FIG. 1 shows an example of this electric cable, and reference numeral 1 in the figure indicates the electric cable. This electric cable 1 is
A metal conductor 2 such as copper or aluminum in the center layer, an insulator 3 made of ethylene propylene rubber, polyethylene, polyvinyl chloride, etc. that insulates the conductor 2, and a chloroprene rubber or chlorosulfone that covers the insulator 3. The sheath 4 is made of a rubber composition or a synthetic resin composition having a molding temperature of 280° C. or lower, such as polyethylene chloride, polyvinyl chloride, or polyethylene, and serves as an anti-termite layer. The sheath 4 contains boric acid. Orthoboric acid, metaboric acid, tetraboric acid, etc. are used as the boric acid.
ここでゴム組成物あるいは合成樹脂組成物の成形温度を
２８０ ’Ｃ以下に規定したのは硼酸の熱分解温度か約
３００°Ｃであり、シース４の押出被覆加工時に硼酸が
加熱されて熱分解を起し、防蟻性か低下することを防止
するためである。Here, the molding temperature of the rubber composition or synthetic resin composition is specified to be 280'C or less, which is the thermal decomposition temperature of boric acid, which is approximately 300°C. This is to prevent the anti-termite properties from decreasing.
そして硼酸のシース４における配合量は１〜３０重量％
か好ましく、１重量％未満では目的とする防蟻作用が得
られず、また３０重量％を越えるとシース４を形成して
いるコム組成物あるいは合成樹脂組成物の機械的、電気
的特性が低下して不都合となる。The amount of boric acid in the sheath 4 is 1 to 30% by weight.
Preferably, if it is less than 1% by weight, the desired anti-termite effect cannot be obtained, and if it exceeds 30% by weight, the mechanical and electrical properties of the comb composition or synthetic resin composition forming the sheath 4 will deteriorate. This is inconvenient.
このように硼酸を含む防蟻層となるシース４を設けたこ
の電気ケーブル１は、シース４に含まれた上記化合物に
よって持続性のある優れた防蟻作用を発揮し、シロアリ
なとの昆虫類による食害を受けることがない。This electric cable 1, which is provided with the sheath 4 which serves as a termite-proof layer containing boric acid, exhibits a long-lasting and excellent termite-proofing effect due to the compound contained in the sheath 4, and is effective against termites and other insects. There is no feeding damage due to
次に、この電気ケーブル１の製造方法について説明する
。まず、導体２の表面に通常の押出被覆によって絶縁体
３を形成する。次にシース４を形成するゴム、プラスチ
ック材料に硼酸を所要量添加し、混合する。ついで硼酸
を含むゴム、プラスチック材料をクロスへラドダイを有
する押出機に供給し、上記絶縁体３表面に押出被覆法に
よってシース４を形成する。Next, a method of manufacturing this electric cable 1 will be explained. First, the insulator 3 is formed on the surface of the conductor 2 by ordinary extrusion coating. Next, a required amount of boric acid is added to the rubber or plastic material forming the sheath 4 and mixed. Next, a rubber or plastic material containing boric acid is fed to an extruder equipped with a rad die, and a sheath 4 is formed on the surface of the insulator 3 by an extrusion coating method.
第２図はこの電気ケーブルの第２の実施例を示すもので
、この例では３本の絶縁線心を硼酸を含む防蟻層となる
シース４で外被したものである。FIG. 2 shows a second embodiment of this electric cable, in which three insulated wire cores are covered with a sheath 4 which serves as a termite-proof layer containing boric acid.
また、第３図はこの第３の実施例を示すもので、この例
では３本の絶縁線心をまず金属テープなどの金属被覆層
５で被覆し、ついで硼酸を含む防蟻層となるシース４で
外被したものである。これらの実施例に示された防蟻ケ
ーブルｌにあっても、シース４に含まれる硼酸によって
長期にわたり防蟻作用が発現し、白蟻などによる食★を
受けることがない。FIG. 3 shows this third embodiment. In this example, three insulated wire cores are first covered with a metal coating layer 5 such as a metal tape, and then a sheath containing boric acid to serve as an anti-termite layer is coated. 4 is covered with outer cover. Even in the termite-proof cables 1 shown in these examples, the boric acid contained in the sheath 4 exhibits a termite-proofing effect over a long period of time, and the cables are not eaten by termites or the like.
次に、請求項２に記載の電気ケーブルについて第１図な
いし、第３図を利用して説明する。Next, the electric cable according to claim 2 will be explained using FIGS. 1 to 3.
この電気ケーブル１では、防蟻層となるシース４には、
硼酸を吸着含浸させた無定形シリカが防蟻剤として含有
されている。この硼酸としては、オルトホウ酸、メタホ
ウ酸、四ホウ酸があり、これらを無定形シリカに吸着含
浸させたもので通常は硼酸分として５〜５０％吸着含浸
させたものである。In this electric cable 1, the sheath 4, which serves as an anti-termite layer, includes:
Amorphous silica adsorbed and impregnated with boric acid is contained as a termiticide. Examples of this boric acid include orthoboric acid, metaboric acid, and tetraboric acid, which are adsorbed and impregnated into amorphous silica, and usually 5 to 50% boric acid content is adsorbed and impregnated.
この硼酸を吸着含浸させた無定形シリカのシース４にお
ける配合量は、１〜３０重量％とされる。The amount of the amorphous silica adsorbed and impregnated with boric acid in the sheath 4 is 1 to 30% by weight.
１重量％未満では目的とする防蟻効果が十分に得られず
、また３０重量％を越えるとシース４を形成しているゴ
ム組成物あるいは合成樹脂組成物の機械的、電気的特性
が低下して不都合となる。If it is less than 1% by weight, the desired anti-termite effect cannot be obtained sufficiently, and if it exceeds 30% by weight, the mechanical and electrical properties of the rubber composition or synthetic resin composition forming the sheath 4 will deteriorate. This is inconvenient.
また防蟻層となるシース４を構成するゴム組成物あるい
は合成樹脂組成物としては、その成形温度が２８０°Ｃ
以下のものか用いられる。ここで、成形温度を２８０℃
以下と規定しているのは、硼酸の熱分解温度が約３００
°Ｃであり、無定形シリカの熱分解温度が約１０００°
Ｃ以上であるので、シース４の押出被覆加工時にこれら
化合物が加熱されて熱分解を起し、防蟻効果が低下する
ことを防止するためである。Furthermore, the molding temperature of the rubber composition or synthetic resin composition constituting the sheath 4, which serves as an anti-termite layer, is 280°C.
The following may be used: Here, the molding temperature is 280℃
The following specifies that the thermal decomposition temperature of boric acid is approximately 300
°C, and the thermal decomposition temperature of amorphous silica is approximately 1000 °C.
C or more, this is to prevent these compounds from being heated and thermally decomposed during the extrusion coating process of the sheath 4, thereby preventing the anti-termite effect from decreasing.
この電気ケーブル１では、上記２種の化合物を併用する
ことにより、単独で使用するよりも少量の添加で防蟻効
果が得られ、硼酸単独添加のものよりも長期間防蟻効果
が持続する。In this electric cable 1, by using the above two types of compounds in combination, a termite-proofing effect can be obtained with a smaller amount of addition than when using them alone, and the termite-proofing effect lasts for a longer period of time than when boric acid is added alone.
この電気ケーブル１の製造は、先のものと同様に行われ
る。The manufacture of this electrical cable 1 is carried out similarly to the previous one.
なお、この発明では、シース４を防蟻層とするものには
限定されず、例えば、通常のシースの外側に」二記化合
物を含有するゴム組成物あるいは樹脂組成物からなる被
覆層を設けたものであってもよい。Note that the present invention is not limited to using the sheath 4 as an anti-termite layer; for example, a coating layer made of a rubber composition or a resin composition containing the compound described in "2" may be provided on the outside of a normal sheath. It may be something.
第１表に示す配合の合成樹脂組成物を用いて、シース厚
さ１ 、５ ｍｍのビニルシースケーブル（６００Ｖ
＋ ＣＶ ＋ ３ ×８ ｍｍ”）を作成し、そのシ
ースの防蟻性を検討した。防蟻性の評価は、両端末を封
止した約Ｌｏａｍの試料ケーブルを松材と共に金属容器
内に収容し、この金属製容器にイエシロアリの巣を入れ
て３ケ月間放置し、試料ケーブルのイエシロアリによる
食害状況を観察することによって行った。A vinyl sheathed cable (600 V
+ CV + 3 A nest of Japanese termites was placed in this metal container and left for three months, and the damage caused by the termites to the sample cable was observed.
結果を第１表に示した。The results are shown in Table 1.
食害判定方法は試料ケーブルのシースに食害を受けてい
れば×とし、受けていなければ○とした。The feeding damage evaluation method was: If the sheath of the sample cable suffered from feeding damage, it was marked as ×, and if it was not, it was marked as ○.
（以下余白）
第 １ 表
（配合量は重量部）
＊１ 押出被覆温度・１７０°Ｃ
＊２ オルト硼酸
＊３ オルト硼酸を１５％吸着含浸させた無定形シリカ
また、試料Ｎｏ、２．３，５．６のケーブルについては
、更に容器内での放置期間を１２ケ月まで延長したが、
イエシロアリによる食害は認められなかった。(Leaving space below) Table 1 (Blend amounts are parts by weight) *1 Extrusion coating temperature 170°C *2 Orthoboric acid *3 Amorphous silica adsorbed and impregnated with 15% orthoboric acid Also, sample No. 2.3, Regarding the cables listed in Section 5.6, the period of storage in the container was further extended to 12 months.
No feeding damage by domestic termites was observed.
以上説明したように、この発明の電気ケーブルは、硼酸
もしくは硼酸を吸着含浸させた無定形シリカと、これら
化合物の熱分解温度以下の成形温度を有するゴム組成物
あるいは樹脂組成物とからなる防蟻層を有してなるもの
であるので、これら化合物による防蟻作用が長期間持続
し、シロアリなどによる食害を受けることがない。また
、シースなどを構成するゴム組成物あるいは樹脂組成物
に上記化合物を含有させただけのものであるので、電気
ケーブルの曲げ易さや電気特性などを損うことがない。As explained above, the electric cable of the present invention is an anti-termite comprising boric acid or amorphous silica adsorbed and impregnated with boric acid, and a rubber composition or resin composition having a molding temperature below the thermal decomposition temperature of these compounds. Since it has a layer, the termite-preventing effect of these compounds lasts for a long period of time, and there is no damage caused by termites or the like. Further, since the above-mentioned compound is simply added to the rubber composition or resin composition constituting the sheath, etc., the bendability and electrical properties of the electric cable are not impaired.
さらに特別の製造設備や製造技術などを必須とせず、製
造コストの上昇が微がですむなどの効果を有する。Furthermore, it does not require any special manufacturing equipment or technology, and has the advantage of minimizing the increase in manufacturing costs.
第１図ないし第３図はいずれもこの発明の電気ケーブル
の例を示す断面図である。
１・・・・・電気ケーブル、２・・・・・金属導体、３
・絶縁体、４・・・・シース、５・・・・金属被覆層。1 to 3 are sectional views showing examples of the electric cable of the present invention. 1...Electric cable, 2...Metal conductor, 3
- Insulator, 4... sheath, 5... metal coating layer.
Claims (2)
有するゴム組成物あるいは合成樹脂組成物とからなる防
蟻層を有する電気ケーブル。(1) An electric cable having an anti-termite layer made of boric acid and a rubber composition or synthetic resin composition having a molding temperature below the thermal decomposition temperature of this compound.
合物の熱分解温度以下の成形温度を有するゴム組成物あ
るいは合成樹脂組成物とからなる防蟻層を有する電気ケ
ーブル。(2) An electric cable having an anti-termite layer made of amorphous silica adsorbed and impregnated with boric acid and a rubber composition or synthetic resin composition having a molding temperature below the thermal decomposition temperature of these compounds.