JPH0268817A - Slot ribbon cable of run water prevention type - Google Patents
Slot ribbon cable of run water prevention typeInfo
- Publication number
- JPH0268817A JPH0268817A JP63221955A JP22195588A JPH0268817A JP H0268817 A JPH0268817 A JP H0268817A JP 63221955 A JP63221955 A JP 63221955A JP 22195588 A JP22195588 A JP 22195588A JP H0268817 A JPH0268817 A JP H0268817A
- Authority
- JP
- Japan
- Prior art keywords
- water
- absorbing
- tape
- core
- cable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
〔発明の背景〕
技術分野
本発明は、光フアイバー芯線や導電体芯線を有するケー
ブルの改良に関する。さらに具体的には、本発明は、ケ
ーブル外被の破損によってケーブル内に侵入した水がケ
ーブル長手方向に浸透する所謂「水走り」を防止した走
水防止ケーブルに、特にその改良に、関する。BACKGROUND OF THE INVENTION Technical Field The present invention relates to improvements in cables having optical fiber cores or conductor cores. More specifically, the present invention relates to a water running prevention cable that prevents so-called "water running" in which water that has entered the cable due to damage to the cable jacket permeates in the longitudinal direction of the cable, and particularly to improvements thereof.
光フアイバー芯線を有するケーブルあるいは導電体芯線
を有するケーブルは周知のものであり、特に前者は光通
信技術の進歩によってその将来性が注目されている。BACKGROUND ART Cables having optical fiber core wires and cables having conductor core wires are well known, and the former is particularly attracting attention for its future potential due to advances in optical communication technology.
このようなケーブルの具体例の一つとして、スロットリ
ボン型ケーブルがある。これは、複数本の芯線を平行に
並べてその全体を扁平状にプラスチック被覆してなる芯
線リボンを複数枚重積してなる重積体を、芯材外周の長
手方向に設けた複数本の溝(スロット)の内部に収容し
、その全体を外被で被覆した構造のものである。One specific example of such a cable is a slotted ribbon cable. This is a stacked body made by stacking multiple core wire ribbons, each of which is made by arranging multiple core wires in parallel and covering the entire core wire in a flat shape with plastic. (slot) and is entirely covered with an outer cover.
このようなケーブルには上記のものの外に種々の構造の
ものがあるが、これは一般に外被を有していて、内部の
芯線を外界から保護するようになっている。しかし、経
年劣化あるいは破損事故等による外被の損傷は避は難い
。外被が損傷した場合の被害の一つは水分の浸入による
芯線への悪影響であるが、いったん水がケーブル内に浸
入するとそれがケーブル長手方向に浸透して被害が広範
囲に及ぶというケーブルの構造に生得的な問題がある。Although such cables have various constructions in addition to those described above, they generally have an outer sheath to protect the inner core wire from the outside world. However, damage to the outer cover due to aging or breakage accidents is inevitable. One of the damages when the outer sheath is damaged is the adverse effect on the core wire due to the infiltration of moisture, but once water infiltrates into the cable, it permeates in the longitudinal direction of the cable, causing damage over a wide range of cables. has an inherent problem.
従来の技術
このような浸入水の被害は既に認識されていて、所謂「
走水防止ケーブル」がいくつか提案されている。それら
は、いずれも、浸入水の通路となるケーブル内の隙間を
埋めるべく考案されたものである。そのような方法の一
つは、撥水性ゼリー(具体的には石油精製後のペトロラ
タムやポリブテンを基材とし、石油ワックス、低分子量
ポリエチレン、酸化防止剤等を加えた混和物)をスロッ
トリボン型ケーブルの場合は芯材の溝の内部の重積体を
除く空間に圧入する方法が知られている。Conventional technology The damage caused by such infiltration water has already been recognized, and the so-called
Several "water running prevention cables" have been proposed. All of these are designed to fill gaps in the cable that allow water to enter. One such method is to use a water-repellent jelly (specifically, a mixture made from refined petrolatum or polybutene as a base material, with petroleum wax, low molecular weight polyethylene, antioxidants, etc.) in a slotted ribbon shape. In the case of cables, a method is known in which the cable is press-fitted into the space inside the groove of the core material excluding the stacked body.
しかし、この方法は、ケーブルの末端までのゼリーの均
一充填が困難であって、未充填部分ができがちである。However, with this method, it is difficult to uniformly fill the jelly to the end of the cable, and unfilled areas tend to occur.
また、その点に対する配慮から、ゼリーの流動性を増す
べく加熱状態で圧入が行なわれるが、圧入後はゼリーの
熱収縮によって空隙が発生して、水の通路が形成されて
しまうという問題点がある。一方、圧入圧力を高めれば
、芯線が光ファイバーの場合はファイバー特性が低下す
る危険がある。In addition, in consideration of this point, press-fitting is performed in a heated state to increase the fluidity of the jelly, but after press-fitting, there is a problem that voids are generated due to thermal contraction of the jelly, and water passages are formed. be. On the other hand, if the press-fitting pressure is increased, there is a risk that the fiber properties will deteriorate if the core wire is an optical fiber.
撥水性ゼリー圧入法に生得的なこの問題に対しては、ゼ
リーに高吸水性樹脂を添加することが提案されている。To solve this problem inherent in the water-repellent jelly injection method, it has been proposed to add a super absorbent resin to the jelly.
この方法は防止効果向上からは有益であるが、親水性の
高吸水性樹脂が油性のゼリーに分散しているところから
油分が吸水性の障害になって、高吸水性樹脂の能力が十
分発揮されないので、完全な解決には到っていない。This method is beneficial in terms of improving the prevention effect, but since the hydrophilic superabsorbent resin is dispersed in an oily jelly, the oil becomes an obstacle to water absorption, and the superabsorbent resin's ability is not fully utilized. Therefore, a complete solution has not been reached.
一方、高吸水性樹脂をフィルム、不織布等の基材にバイ
ンダーで固定してなるシートで芯線のリボン重積体の外
側をテーピングして、高吸水性樹脂が水浸入時に膨潤す
ることによって浸水の拡大を防止するようにする方法が
知られている。しかし、この方法にもいくつかの問題点
がある。すなわち基材の高吸水性樹脂保持力が弱いので
、ケーブル製作時に樹脂の脱落が多く、また小径の芯線
には薄いシートが必要であるところ、このようなシート
の薄型化は容易ではない、というように加工性に難があ
るからである。On the other hand, by taping the outside of the ribbon stack of core wires with a sheet made by fixing a superabsorbent resin to a base material such as a film or nonwoven fabric with a binder, the superabsorbent resin swells when water enters, resulting in water leakage. Methods are known to prevent expansion. However, this method also has some problems. In other words, the superabsorbent resin holding power of the base material is weak, so the resin often falls off during cable production, and thin sheets are required for small-diameter core wires, and it is not easy to make such sheets thinner. This is because the processability is difficult.
要旨
本発明は上記の点に解決を与えることを目的とし、スロ
ットリボン型ケーブルの芯線リボン重積体の吸水性樹脂
複合体(詳細後記)のテープによる囲繞、重積体収容芯
材溝内の空隙の該複合体の線状体による充填およびこの
芯材の該複合体のテープによる囲繞によってこの目的を
達成しようとするものである。Summary The present invention aims to solve the above-mentioned problems by surrounding the core ribbon stack of a slotted ribbon cable with a tape of a water-absorbing resin composite (details will be described later), and by surrounding the core ribbon stack of the slot ribbon cable with a tape in the core material groove for storing the stack. This objective is achieved by filling the void with a linear body of the composite and by surrounding the core with a tape of the composite.
すなわち、本発明による走水防止スロットリボン型ケー
ブルは、複数本の芯線を平行に並べてその全体をプラス
チック被覆してなる芯線リボンを複数枚重ねて重積体と
し、その複数本を、芯材外周の長手方向に設けた複数本
の溝内に収容し、それを外被で被覆してなるスロットリ
ボン型ケーブルにおいて、該重積体の少なくとも1本が
吸水性テープで巻いたものであること、芯材溝内の該重
積体との間の隙間の少なくとも一部に吸水性線状体が介
在していること、ならびに芯材が吸水性テープで巻いた
ものであること、のいずれかもしくは組み合わせよりな
ること、ならびに該吸水性テープおよび吸水性線状体が
それぞれテープ状または線状のあるいはテープ状または
線状に加工しつる支持体に含浸または塗布した水溶性エ
チレン性不飽和モノマーを重合させて得た吸水性高分子
複合体からなるものであること、を特徴とするものであ
る。That is, the water running prevention slot ribbon type cable according to the present invention has a plurality of core ribbons arranged in parallel and covered entirely with plastic to form a stacked body, and the plurality of core ribbons are stacked around the outer periphery of the core material. A slotted ribbon cable that is housed in a plurality of grooves provided in the longitudinal direction of the cable and covered with an outer sheath, at least one of the stacked bodies being wrapped with water-absorbing tape; Either a water-absorbing linear body is interposed in at least a part of the gap between the core material groove and the stacked body, and the core material is wrapped with water-absorbing tape; or and the water-absorbing tape and the water-absorbing linear body are polymerized with a water-soluble ethylenically unsaturated monomer impregnated or coated on a tape-shaped or linear support, or a tape-shaped or linear support, respectively. It is characterized in that it is made of a water-absorbing polymer composite obtained by
効果
本発明によれば、撥水性ゼリーの代りに「乾燥した」走
水防止材を使用ししかもケーブル形成時に走水防止材を
配することになるから、前記した従来技術の内包する間
厘点とは無縁である。Effects According to the present invention, a "dry" water running prevention material is used instead of the water-repellent jelly, and the water running prevention material is disposed during cable formation, thereby eliminating the disadvantages inherent in the prior art described above. It has nothing to do with it.
そして、本発明で使用する走水防止材である吸水性高分
子複合体(詳細後記)は吸水によって速やかに膨潤する
ものであるから、ケーブル外被破損による浸水発生時に
は膨潤による体積増大によって発生する圧力によって、
浸水の拡大を効果的に阻止することができる。Furthermore, since the water-absorbing polymer composite (details will be described later), which is the water running prevention material used in the present invention, quickly swells due to water absorption, when water intrusion occurs due to damage to the cable sheath, it will occur due to volume increase due to swelling. By pressure,
The spread of flooding can be effectively prevented.
I、ケーブルの基本構成
本発明で、対象とするケーブルは、スロットリボン型ケ
ーブルであって、前記したように、複数本の芯線を平行
に並べてその全体を偏平状にプラスチック被覆してなる
芯線リボンの重積体を、芯材の外周に長手方向に設けた
溝(スロット)に収容し、それを外被で被覆してなるも
のである。I. Basic Structure of Cable The cable targeted by the present invention is a slot ribbon type cable, which, as mentioned above, is a core ribbon made by arranging a plurality of core wires in parallel and covering the entire core wire in a flat shape with plastic. The stacked body is housed in a groove (slot) provided in the longitudinal direction on the outer periphery of the core material, and the slot is covered with an outer cover.
このような基本構成のケーブルは周知のものである。Cables with this basic configuration are well known.
すなわち、「芯線」は、このケーブルが電線であれば銅
、アルミニウム等の金属線であり、またこのケーブルが
光通信用のものであれば先ファイバーである。スロット
リボン型ケーブルは、光フアイバー用のケーブルの形態
としては特に適したものである。また、特に光ファイバ
ーの場合は、その保護のために光ファイバーを緩衝層(
たとえば、軟質紫外線架橋プラスチック層)で覆い、さ
らにナイロン等のプラスチックからなる被覆が設けられ
ていることがあるが、本発明ではこのような構造を持つ
ものをも「芯線」と呼ぶものである。That is, the "core wire" is a metal wire such as copper or aluminum if the cable is an electric wire, and is a fiber end if the cable is for optical communication. Slotted ribbon cables are particularly suitable as fiber optic cables. In addition, especially in the case of optical fibers, the optical fibers are covered with a buffer layer (
For example, the wire may be covered with a soft ultraviolet crosslinked plastic layer) and further provided with a coating made of plastic such as nylon, and in the present invention, wires with such a structure are also referred to as "core wires."
また、芯線は単一線からなるものの外に、複数本からな
るもの、特に撚線、であワてもよく、いずれも本発明の
「芯線」として定義されるものである。その場合の複数
本の芯線は、その種類、太さ等において異なるものであ
ってもよい。Further, the core wire may be not only a single wire but also a plurality of wires, especially twisted wires, and both are defined as the "core wire" of the present invention. In that case, the plurality of core wires may be different in type, thickness, etc.
このような芯線は、複数本を平行に並べて、その全体を
扁平状にプラスチック被覆して芯線リボン(または芯線
テープ)とし、複数枚を重積して重積体とし、それを芯
材の溝すなわちスロットに収容して、スロットリボン型
ケーブルとする。Such core wires are made by arranging multiple core wires in parallel, covering the entire core wire in a flat shape with plastic to make a core wire ribbon (or core wire tape), stacking multiple core wires on top of each other to make a stack, and then inserting it into the groove of the core material. That is, it is housed in a slot to form a slot ribbon type cable.
光ファイバーは、これをリボンにしてもまたそれを重積
体の形態にしても、引張りに対して弱いことがふつうで
あるから、これを芯材の溝に収容してケーブルとするこ
とは合理的であるが、それでもなお引張りに弱いことが
ふつうである。Optical fibers, whether in the form of ribbons or stacks, are generally weak against tension, so it is reasonable to accommodate them in the grooves of the core material and make them into cables. However, it is usually still weak against tension.
ケーブルとして必要な抗張力を持たせるために金属線そ
の他からなる線状抗張力体を芯材内に配することがふつ
うである。線状抗張力体は、金属線そのものである場合
の外に、適当な被覆(たとえば緩衝性の被81)を有す
るものであってもよい。In order to provide the cable with the necessary tensile strength, a linear tensile strength body made of metal wire or the like is usually placed within the core material. The linear tensile strength member may be a metal wire itself or may have a suitable covering (for example, a cushioning covering 81).
なお、ケーブルとして必要な抗張力は、線状抗張力体を
芯材の溝内に配しであるいは外被中に配して担保するこ
ともできる。Note that the tensile strength required for the cable can also be ensured by placing linear tensile strength members in the grooves of the core material or in the outer sheath.
いずれの構成のものであれ、ケーブルの外周を被覆して
芯線リボンを保護すべき外被は、ゴム、プラスチック、
ゴムないしプラスチック含浸布、その他の素材からなっ
ており、すべて周知のものである。Regardless of the configuration, the sheath that covers the outer circumference of the cable to protect the core ribbon is rubber, plastic,
It may be made of rubber or plastic impregnated cloth or other materials, all of which are well known.
このような基本構成からなるスロットリボン型ケーブル
の製造法もまた周知であって、基本的には芯線リボンの
重積体の形成、その芯材溝への導入およびそれに対する
外被の施用からなる。A method for producing slotted ribbon cables having this basic configuration is also well known and basically consists of forming a stack of core ribbons, introducing them into the core grooves and applying an outer sheath to them. .
■0本発明による走水防止スロットリボン型ケーブル
本発明による走水防止スロットリボン型ケーブルは、上
記の基本構成のスロットリボン型ケーブルの芯線リボン
重積体の少なくとも1本が吸水性テープで巻いたもので
あること、芯材溝内の該重積体との間の隙間の少なくと
も一部に吸水性線状体が介在していること、ならびに芯
材が吸水性テープで巻いたものであること、のいずれか
もしくは組み合わせによって特徴づけられる。■0 Water running prevention slotted ribbon cable according to the present invention The water running preventing slotted ribbon cable according to the present invention is such that at least one of the core ribbon stacks of the slotted ribbon cable having the above-mentioned basic configuration is wrapped with water-absorbing tape. A water-absorbing linear body is interposed in at least a part of the gap between the core material groove and the stacked body, and the core material is wrapped with water-absorbing tape. , or a combination thereof.
ケーブル芯材内の溝すなわち線状空隙を充填すべき吸水
性線状体は、これを溝内に配するには溝内に形成される
空隙を考慮して必要本数(1本または複数本)の吸水性
線状体をケーブル製造時に使用すればよい。The number of water-absorbing linear bodies that should fill the grooves, that is, the linear voids in the cable core material, is required (one or more) in order to arrange them in the grooves, taking into consideration the voids formed within the grooves. The water-absorbing linear body may be used when manufacturing the cable.
添付の図面は本発明による走水防止スロットリボン型ケ
ーブルの一具体例の断面図であって、第1図は芯線リボ
ン重積体、第2図はリボン重積体を芯材溝内に収容して
なる本発明走水防止スロットリボン型ケーブル、である
。この第2図の具体例は、吸水性テープによる芯線リボ
ン重積体の被覆および吸水性線状体によるケーブル内空
隙の充填を最大限に行なったものであって、本発明の典
型的な姿を示すものである(本発明がこのような構造に
限定されないことは前記したところである)。The attached drawings are cross-sectional views of a specific example of the water running prevention slot ribbon type cable according to the present invention, in which FIG. 1 shows a stack of core ribbons, and FIG. 2 shows a stack of ribbons accommodated in a core groove. The present invention is a slotted ribbon type cable to prevent water running. The specific example shown in FIG. 2 is a typical example of the present invention, in which the core ribbon stack is covered with a water-absorbing tape and the voids in the cable are filled to the maximum with a water-absorbing linear body. (It has been mentioned above that the present invention is not limited to such a structure).
本発明による走水防止スロットリボン型ケーブルは、前
記基本構成のケーブルの周知の製造法において、芯線リ
ボン重積体および芯材の吸水性テープ巻き(テープ巻き
は、ケーブル製造での単位工程として周知のものである
)および芯線リボン重積体の芯材溝への収容を吸水性線
状体と共に行なうこと、によって製造することができる
。The water running prevention slot ribbon type cable according to the present invention is produced by winding a core ribbon stack and a core material with a water-absorbing tape (tape winding is well known as a unit process in cable manufacturing) in the well-known manufacturing method of the cable with the above-mentioned basic structure. ) and a stack of core ribbons is accommodated in the core groove together with the water-absorbing linear body.
■、吸水性テープおよび吸水性線状体
本発明で走水防止材として使用するのは、テープ状また
は線状のあるいはテープ状または線状に加工しうる支持
体に含浸または塗布した水溶性エチレン性不飽和モノマ
ーを重合させて得た吸水性高分子複合体からなるもので
ある。■Water-absorbing tape and water-absorbing linear material In the present invention, water-soluble ethylene impregnated or coated on a tape-like, linear, or processable support It consists of a water-absorbing polymer composite obtained by polymerizing sexually unsaturated monomers.
先ず、水溶性エチレン性不飽和モノマーには、アクリル
酸またはメタクリル酸(以下、アクリルないしメタクリ
ル部分を「(メタ)アクリル」という)またはその部分
ないし全中和物(たとえば、アルカリ金属塩またはアン
モニウム塩)、(メタ)アクリルアミド、N−メチロー
ル(メタ)アクリルアミド、エチレングリコールモノ(
メタ)アクリル酸エステル、ビニルスルホン酸、その他
がある。(メタ)アクリル酸またはその中和物(特に、
20%以上のカルボキシル基中和物)が特に好ましい。First, water-soluble ethylenically unsaturated monomers include acrylic acid or methacrylic acid (hereinafter, the acrylic or methacrylic moiety is referred to as "(meth)acrylic") or partially or fully neutralized products thereof (for example, alkali metal salts or ammonium salts). ), (meth)acrylamide, N-methylol (meth)acrylamide, ethylene glycol mono(
There are meth)acrylic acid esters, vinyl sulfonic acid, and others. (meth)acrylic acid or its neutralized product (especially
20% or more carboxyl group neutralized products) are particularly preferred.
このようなモノマーの重合によって生成する親水性ポリ
マーに所望の水不溶性を与えるべく、架橋性モノマーを
共重合させることができる(架橋性モノマーは外にも、
合目的的なモノマーを共重合させることができ、従って
そのような態様も本発明でいう[水溶性モノマーを重合
させて得た吸水性高分子複合体」の節部に入るもとする
)。そのような架橋性モノマーとしてはN、N’ −
メチレンビス(メタ)アクリルアミド、ポリエチレング
リコールジ(メタ)アクリル酸エステル、グリセリンジ
ないしトリ(メタ)アクリル酸エステル、その他がある
。In order to impart the desired water insolubility to the hydrophilic polymer produced by the polymerization of such monomers, crosslinking monomers can be copolymerized (crosslinking monomers can also include
Purposeful monomers can be copolymerized, and such embodiments are also included in the term "water-absorbing polymer composite obtained by polymerizing water-soluble monomers" in the present invention. Such crosslinking monomers include N, N'-
Examples include methylene bis(meth)acrylamide, polyethylene glycol di(meth)acrylate, glycerin di- or tri(meth)acrylate, and others.
これらのようなモノマーをその上に支持して吸水性高分
子複合体を形成させるべき支持体は、繊維質、スポンジ
状その他の吸収性素材または非吸収性素材からなる、テ
ープ状または線状のものあるいはテープ状または線状に
加工しつる形体のものである。具体的には不織布、編織
物、スポンジ(狭義の海綿だけでなく、広く弾性多孔体
を意味するものとする。連続気泡のものが望ましい)、
プラスチックフィルム、その他、がある。重合工程前あ
るいは重合工程後に、必要な寸法のテープ状片または線
状片に加工する。The support on which these monomers are supported to form a water-absorbing polymer composite may be a tape-like or linear support made of fibrous, sponge-like or other absorbent material or non-absorbent material. It is a tape-like or linear-shaped object. Specifically, non-woven fabrics, knitted fabrics, sponges (not just sponges in the narrow sense, but broadly elastic porous materials. Open-celled materials are preferable),
There are plastic films and others. Before or after the polymerization process, it is processed into tape-like pieces or linear pieces of required dimensions.
このような支持体上での前記のモノマーの重合は、合目
的的な任意の方法によって行なうことができる。典型的
な方法は、モノマー水溶液を支持体に含浸させ、塗布し
、あるいは噴霧し、適当な重合開始手段たとえば七ツマ
ー水溶液に溶存させておいたラジカル重合開始剤の分解
によるラジカル発生(たとえば加熱により、あるいは溶
存重合開始剤がレドックス系の酸化剤成分である場合は
還元剤成分の添加による)、あるいは高エネルギー放射
線の照射、その他によって重合を開始させることからな
る。なお、ラジカル重合開始剤の添加方法は任意である
。たとえば、モノマー溶液に溶存させてもよいし、また
モノマー溶液を塗布した支持体にラジカル重合開始剤溶
液を噴霧するか、逆にラジカル重合開始剤を塗布した支
持体にモノマー溶液を噴霧してもよい。重合終了後は、
乾燥、細断、その他の処理を行なって、テープまたは線
状体を得る。支持体に対する吸水性ポリマーの含量は、
支持体の1〜1000重量%、好ましくは10〜100
重量%程度、がふつうである。Polymerization of the monomers mentioned above on such a support can be carried out by any convenient method. A typical method involves impregnating, coating, or spraying an aqueous monomer solution onto a support, and generating radicals using an appropriate polymerization initiator, such as decomposition of a radical polymerization initiator dissolved in an aqueous solution of monomer (e.g., by heating). (or by adding a reducing agent component when the dissolved polymerization initiator is a redox-based oxidizing agent component), irradiation with high-energy radiation, or other means. Note that the method of adding the radical polymerization initiator is arbitrary. For example, the radical polymerization initiator solution may be dissolved in a monomer solution, or the radical polymerization initiator solution may be sprayed onto a support coated with a monomer solution, or conversely, the monomer solution may be sprayed onto a support coated with a radical polymerization initiator. good. After polymerization,
A tape or linear body is obtained by drying, shredding, and other treatments. The content of water-absorbing polymer to the support is
1 to 1000% by weight of the support, preferably 10 to 100%
It is usually about % by weight.
テープと線状体とは所与のケーブルについて同一素材の
ものである必要はない。たとえば、テープは不織布を支
持体とす゛るものとし、線状体はスポンダを支持体とす
るものとすることができる。The tape and wire need not be of the same material for a given cable. For example, the tape may use a nonwoven fabric as a support, and the linear body may use a sponder as a support.
■、実施例
固形分63重量%の70モル%中和されたアクリル酸カ
リウム水溶液を調製した。この溶液に、アクリル酸カリ
ウムモノマーに対して、0.4ffl量%のN−N’
メチレンビスアクリルアミド及び0.3重量%の過硫酸
カリウムを溶解し、その後、坪量が40g/rrIl′
のポリエステル繊維不織布(ユニチカ(株)製マリック
ス90403WSO)の上にこの水溶液を、ポリマー目
付量が50g/rr?となるように均一に含浸させた。(2) Example A 70 mol% neutralized potassium acrylate aqueous solution with a solid content of 63% by weight was prepared. To this solution, 0.4 ffl amount % of N-N' was added to the potassium acrylate monomer.
Methylenebisacrylamide and 0.3% by weight of potassium persulfate were dissolved, and then the basis weight was 40g/rrIl'
This aqueous solution was applied onto a polyester fiber nonwoven fabric (Marix 90403WSO manufactured by Unitika Co., Ltd.) with a polymer basis weight of 50 g/rr? It was impregnated uniformly so that
一方、ポリエステル繊維をベースとするひも状品太さl
ll11M×100mを前記モノマー溶液をポリマー目
付量が0.5g/g基材となる様に含浸させ、テフロン
製のメツシュ芯に巻き取った。On the other hand, a string-like product based on polyester fiber has a thickness of 1
11M x 100m was impregnated with the monomer solution so that the polymer basis weight was 0.5 g/g base material, and wound around a Teflon mesh core.
これらのモノマー含浸材を窒素で置換されたオーブンに
1時装置いてモノマーを重合させ、その後100℃にて
減圧乾燥して、吸水性高分子複合体からなる吸水性シー
ト及び線状体を得た。この吸水性シートはその後2cm
幅にスリットして吸水性テープを得た。These monomer-impregnated materials were placed in an oven purged with nitrogen for one hour to polymerize the monomers, and then dried under reduced pressure at 100°C to obtain water-absorbing sheets and linear bodies made of water-absorbing polymer composites. . This water-absorbing sheet is then 2cm long.
A water-absorbent tape was obtained by slitting the tape widthwise.
モデル実験として、低密度ポリエチレンのロッド(径8
IIIIn×約7m)を用意し、これに前記2C11幅
の吸水性テープを一定ピッチで巻き付け、1mずつに切
断して、7本の芯線相当品を用意した。As a model experiment, a low-density polyethylene rod (diameter 8
IIIIn×approximately 7 m) was prepared, the 2C11 width water absorbent tape was wound at a constant pitch, and the tape was cut into 1 m pieces to prepare products equivalent to seven core wires.
これを、中心に1本、まわりに6本を前記吸水性線状体
を内部の間隙に同一方向にそろえてはさんで結束し、固
定後さらに吸水性線状体を外部の凹部に同一方向にそろ
えて埋めながら、そのまわりを吸水性テープで巻いて固
定した。作成した集合体に、21Ill厚となるように
ポリエチレン被覆を行った。This is bundled by sandwiching one water-absorbing linear body in the center and six around it in the same direction in the internal gap, and after fixing, the water-absorbing linear body is placed in the external recess in the same direction. I lined it up and buried it, wrapping it with absorbent tape and fixing it in place. The produced assembly was coated with polyethylene to a thickness of 21 Ill.
得られたケーブル相当品を水平にして、一端に0.1K
g/rrfの水圧をかけて常温で水密試験を実施したが
、6Hr経過しても他端からの水の滴下はなかった。The obtained cable equivalent product is laid horizontally and 0.1K is applied to one end.
A watertight test was conducted at room temperature by applying a water pressure of g/rrf, but no water dripped from the other end even after 6 hours.
以上のモデル実験より、本発明による走水防止スロット
リボン型ケーブルは、外被損傷による水の浸入があって
も、浸透の拡大を防ぐ効果のあることが確認された。ま
た、従来の撥水性ゼリーのようなべとつきがなく、製作
作業、良好であった。From the above model experiments, it was confirmed that the water running prevention slot ribbon type cable according to the present invention is effective in preventing the expansion of water penetration even if water intrusion occurs due to damage to the jacket. In addition, it was not sticky like conventional water-repellent jelly and was easy to manufacture.
第1図は、本発明の走水防止スロットリボン型ケーブル
の光フアイバーリボンの重積体についての一実施例を示
す断面図である。
第2図は、本発明による走水防止スロットリボン型ケー
ブルの一実施例を示す断面図である。
1・・・芯線、2・・・芯線リボン、3・・・リボン重
積体、4・・・吸水性テープ、5・・・吸水性線状体、
6・・・吸水性テープ、7・・・抗張力材、8・・・溝
付き芯材、9・・・外被、10・・・走水防止スロット
リボン型ケーブル。FIG. 1 is a sectional view showing an embodiment of a stacked optical fiber ribbon of the anti-water run slotted ribbon cable of the present invention. FIG. 2 is a sectional view showing an embodiment of the anti-water running slotted ribbon cable according to the present invention. DESCRIPTION OF SYMBOLS 1... Core wire, 2... Core wire ribbon, 3... Ribbon stack, 4... Water-absorbing tape, 5... Water-absorbing linear body,
6... Water-absorbing tape, 7... Tensile strength material, 8... Grooved core material, 9... Outer cover, 10... Water running prevention slot ribbon type cable.
Claims (1)
覆してなる芯線リボンを複数枚重ねて重積体とし、その
複数本を、芯材外周の長手方向に設けた複数本の溝内に
収容し、それを外被で被覆してなるスロットリボン型ケ
ーブルにおいて、該重積体の少なくとも1本が吸水性テ
ープで巻いたものであること、芯材溝内の該重積体との
間の隙間の少なくとも一部に吸水性線状体が介在してい
ること、ならびに芯材が吸水性テープで巻いたものであ
ること、のいずれかもしくは組み合わせよりなること、
ならびに該吸水性テープおよび吸水性線状体がそれぞれ
テープ状または線状のあるいはテープ状または線状に加
工しうる支持体に含浸または塗布した水溶性エチレン性
不飽和モノマーを重合させて得た吸水性高分子複合体か
らなるものであること、を特徴とする、走水防止スロッ
トリボン型ケーブル。A plurality of core wire ribbons made by arranging a plurality of core wires in parallel and covering the whole with plastic are stacked to form a stacked body, and the plurality of core wires are housed in a plurality of grooves provided in the longitudinal direction of the outer periphery of the core material. , in a slotted ribbon type cable formed by covering it with an outer sheath, at least one of the stacked bodies is wrapped with water-absorbing tape, and a gap between the stacked bodies and the stacked body in the core groove. A water-absorbing linear body is interposed in at least a part of the core material, and the core material is wrapped with a water-absorbing tape, or a combination thereof;
and a water-absorbing material obtained by polymerizing a water-soluble ethylenically unsaturated monomer impregnated or coated on a tape-shaped or linear support, or a support that can be processed into a tape-shaped or linear shape, for the water-absorbing tape and water-absorbing linear body, respectively. 1. A slotted ribbon type cable to prevent running water, characterized in that the cable is made of a synthetic polymer composite.