JPH0248991A - 光学記録媒体 - Google Patents
光学記録媒体Info
- Publication number
- JPH0248991A JPH0248991A JP63180076A JP18007688A JPH0248991A JP H0248991 A JPH0248991 A JP H0248991A JP 63180076 A JP63180076 A JP 63180076A JP 18007688 A JP18007688 A JP 18007688A JP H0248991 A JPH0248991 A JP H0248991A
- Authority
- JP
- Japan
- Prior art keywords
- group
- formula
- carbon atoms
- recording medium
- optical recording
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
（産業上の利用分野）
本発明は光記録媒体、特に近赤外域に吸収を持つ半導体
レーザー用の有機系記録層を有する光記録媒体に関する
。
レーザー用の有機系記録層を有する光記録媒体に関する
。
（従来の技術）
近年、゛ト導体レーザーの発展は目覚ましく小型で安定
した発振器が安価に入手可能になり、各種記録装置の光
源として用いられはじめた。しかしながらこれら半導体
レーデ−の波長は比較的長波長のものに限定されており
短波長光の発振が可能な半導体レーザーは寿命、出力な
どに問題がある。
した発振器が安価に入手可能になり、各種記録装置の光
源として用いられはじめた。しかしながらこれら半導体
レーデ−の波長は比較的長波長のものに限定されており
短波長光の発振が可能な半導体レーザーは寿命、出力な
どに問題がある。
従って半導体レーザー用記録媒体としては近赤外域に吸
収を持つ素材を薄膜層として用いることが必須となり、
最大吸収波長が７５０ｐ以ドの素材では不適当である。
収を持つ素材を薄膜層として用いることが必須となり、
最大吸収波長が７５０ｐ以ドの素材では不適当である。
従来この種の記録媒体とじては基板上に形成せしめた薄
膜にレーザー光を照射し、ピットを形成せしめ、ピット
とピットでない部位の反射率の差で記録情報を読みだす
ものがある。この記録および再生（読み出し）のための
記録層の構成は、記録用薄膜形成層と反射膜からなる２
層以−Ｌのものもあるが、記録用薄膜層のみで前記両機
能を有するものが４Ｔ利である。この記録用薄膜層の単
層膜の場合は該記録用薄膜層の素材はそれ自身で高い反
射率を有することが高いＣＺＮ比を得るために必堡であ
る。この種の記録媒体としては、無機ではＴｏまたはそ
の合金の低融点金属を用いたものが知られ、有機系では
シアニン系色素を用いたもの、フタロシアニン系化合物
を用いたものが知られている。
膜にレーザー光を照射し、ピットを形成せしめ、ピット
とピットでない部位の反射率の差で記録情報を読みだす
ものがある。この記録および再生（読み出し）のための
記録層の構成は、記録用薄膜形成層と反射膜からなる２
層以−Ｌのものもあるが、記録用薄膜層のみで前記両機
能を有するものが４Ｔ利である。この記録用薄膜層の単
層膜の場合は該記録用薄膜層の素材はそれ自身で高い反
射率を有することが高いＣＺＮ比を得るために必堡であ
る。この種の記録媒体としては、無機ではＴｏまたはそ
の合金の低融点金属を用いたものが知られ、有機系では
シアニン系色素を用いたもの、フタロシアニン系化合物
を用いたものが知られている。
（発明が解決しようとする課Ｍ）
Ｔｅ系合金を用いた無機系光記録媒体は比較的感度も高
く優れているが、１坏性に問題があり、成膜方法もスパ
ッタリング等によるため設備コスト等が高く、生産性も
低い欠点をイｒしている。シアニン系色素を用いた有機
系の薄膜光記録媒体の場合はスピンコード法等の比較的
安価な方法で生産できる利点を有しているが性能面、例
えば保存安定性（耐久性）で膚足できる状態に達してい
ないのが現状である。またナフトキノン、アントラキノ
ン系の場合は溶剤溶解性に乏しく、また凝集構造の生成
など保存安定性に問題があった。さらにフタロシアニン
系化合物の場合にも溶剤溶解性、゛ト導体レーザーマツ
チング性、保イを中の結晶変化等で不充分であった。
く優れているが、１坏性に問題があり、成膜方法もスパ
ッタリング等によるため設備コスト等が高く、生産性も
低い欠点をイｒしている。シアニン系色素を用いた有機
系の薄膜光記録媒体の場合はスピンコード法等の比較的
安価な方法で生産できる利点を有しているが性能面、例
えば保存安定性（耐久性）で膚足できる状態に達してい
ないのが現状である。またナフトキノン、アントラキノ
ン系の場合は溶剤溶解性に乏しく、また凝集構造の生成
など保存安定性に問題があった。さらにフタロシアニン
系化合物の場合にも溶剤溶解性、゛ト導体レーザーマツ
チング性、保イを中の結晶変化等で不充分であった。
（課題を解決するための手段）
近赤外域の光に高感度であり、溶剤溶解性が大きく、高
い反射率を示し毒性がな（かつ耐久性にも優れた光記録
媒体の記録再生のための薄膜材を提供し、もって優れた
光記録媒体を提供するために、鋭意検討の結果本発明に
到達した。すなわち本発明は、下記一般式〔１〕式で示
されるナフタロシアニン化合物をＬ成分とする有機薄膜
を基板りに形成せしめてなることを特徴とする光学記録
媒体である。
い反射率を示し毒性がな（かつ耐久性にも優れた光記録
媒体の記録再生のための薄膜材を提供し、もって優れた
光記録媒体を提供するために、鋭意検討の結果本発明に
到達した。すなわち本発明は、下記一般式〔１〕式で示
されるナフタロシアニン化合物をＬ成分とする有機薄膜
を基板りに形成せしめてなることを特徴とする光学記録
媒体である。
（式中、Ｍは水素原子２個またはＩａｓＩＩａｘＩＩ［
ａｌｌＶａｘ Ｖａ１ＶＩａｘ■ａ１■、Ｉｂ、ＩＩｂ
。
ａｌｌＶａｘ Ｖａ１ＶＩａｘ■ａ１■、Ｉｂ、ＩＩｂ
。
ｍｂ、 ■ｂ１ｖｂ、ｖｘｂ、■ｂ族の元素を表し、ｙ
、 、Ｙ２はハロゲン原子、ヒドロキシ基、または酸素
を、Ｒ，、Ｒ２、Ｒ，、Ｒ，、Ｒ５、Ｒ，、Ｒ７、Ｒ８
は少なくとも一つは一般式、／ ０−Ｑ−Ｎ ＼ （式中、Ｑは炭素数１〜１８の直鎖又は分枝のアルキル
基をＮ Ｒｎ 、Ｒｔｏは同一でも相異なっていても良
く、水素原子、炭素数１からｌＯのアルキル基または炭
素数１から１０のシクロアルキル基または炭素数１から
１０のアルケニル基または炭素数Ｉから１０のシクロア
ルケニル基またはアリル基、アラアルキル基、またはＲ
９とＲＩＯが炭素原子またはへテロ原ｆで結合し、一般
式中の窒素原子と共に３〜７員環の複素環を形成してい
ることを表す） で示されるアミノアルコキシ基を表し、その他の置換基
は同一でも相異なっていても良く、ヒ記アミノアルコキ
シ基または炭素数１−１８の直鎖または分枝のアルコキ
シ基を、Ｘは水素原ｒ１ハロゲン原子、ニトロ原ｆを、
ｎは０〜４の整数を表す） 本発明の特定のナフタロシアニン化合物を薄膜として基
板１−に形成した光学記録媒体は、近赤外域における感
度、反射率、耐久性のいずれも滴定するものであり、光
ディスク、光カード、テープなどの各種の尤を用いた記
録、ｉＩＴ生のための媒体として有用である。
、 、Ｙ２はハロゲン原子、ヒドロキシ基、または酸素
を、Ｒ，、Ｒ２、Ｒ，、Ｒ，、Ｒ５、Ｒ，、Ｒ７、Ｒ８
は少なくとも一つは一般式、／ ０−Ｑ−Ｎ ＼ （式中、Ｑは炭素数１〜１８の直鎖又は分枝のアルキル
基をＮ Ｒｎ 、Ｒｔｏは同一でも相異なっていても良
く、水素原子、炭素数１からｌＯのアルキル基または炭
素数１から１０のシクロアルキル基または炭素数１から
１０のアルケニル基または炭素数Ｉから１０のシクロア
ルケニル基またはアリル基、アラアルキル基、またはＲ
９とＲＩＯが炭素原子またはへテロ原ｆで結合し、一般
式中の窒素原子と共に３〜７員環の複素環を形成してい
ることを表す） で示されるアミノアルコキシ基を表し、その他の置換基
は同一でも相異なっていても良く、ヒ記アミノアルコキ
シ基または炭素数１−１８の直鎖または分枝のアルコキ
シ基を、Ｘは水素原ｒ１ハロゲン原子、ニトロ原ｆを、
ｎは０〜４の整数を表す） 本発明の特定のナフタロシアニン化合物を薄膜として基
板１−に形成した光学記録媒体は、近赤外域における感
度、反射率、耐久性のいずれも滴定するものであり、光
ディスク、光カード、テープなどの各種の尤を用いた記
録、ｉＩＴ生のための媒体として有用である。
本発明の目的を損わないかぎりにおいて、ナフタロシア
ニン化合物に安定剤、滑剤、帯電防ＩＬ剤、バインダー
としての高分子化合物、他の染料、増感剤を併用しても
よい。本発明において使用される基板材料は、使用レー
ザー光に透明、不透明のいずれでもよいが、基板側から
のレーザー光で古きこみ記録を行なう場合はレーザー光
に対して透明でなければならない。
ニン化合物に安定剤、滑剤、帯電防ＩＬ剤、バインダー
としての高分子化合物、他の染料、増感剤を併用しても
よい。本発明において使用される基板材料は、使用レー
ザー光に透明、不透明のいずれでもよいが、基板側から
のレーザー光で古きこみ記録を行なう場合はレーザー光
に対して透明でなければならない。
これらの基板材料としてはガラス、アクリル樹脂、メタ
アクリル樹脂、ポリエステル樹脂、ニトロセルロース樹
脂、ポリアミド樹脂、ポリカーボネート樹脂、ポリメチ
ルペンテン−１樹脂、エポキシ樹脂、塩化ビニール樹脂
、ポリバラフェニレン樹脂等が挙げられる。これらの樹
脂は、シート、フィルム、円板等の形状物であり、また
これ等の形状物には必要に応じてド塗り層や、特定の金
属の蒸着を施した層をａするものであってもよい。
アクリル樹脂、ポリエステル樹脂、ニトロセルロース樹
脂、ポリアミド樹脂、ポリカーボネート樹脂、ポリメチ
ルペンテン−１樹脂、エポキシ樹脂、塩化ビニール樹脂
、ポリバラフェニレン樹脂等が挙げられる。これらの樹
脂は、シート、フィルム、円板等の形状物であり、また
これ等の形状物には必要に応じてド塗り層や、特定の金
属の蒸着を施した層をａするものであってもよい。
以Ｆ１実施例によりさらに詳しく説明する。
なお、実施例における特性の測定と評価はド記によった
。
。
スペクトル
ナフタロシアニン化合物をエタノールに１．５％に溶解
してスピンコーターにてガラス基板上に７０ｎｍの薄膜
を形成した。これをＵＶ−Ｖ Ｉ Ｓスペクトロメータ
ー（島津ＵＶ２１ ＯＡ）にて吸収および反射スペクト
ルを測定した。これより８３０ｎＴ１１の反射率（Ｒ％
）を求めた。
してスピンコーターにてガラス基板上に７０ｎｍの薄膜
を形成した。これをＵＶ−Ｖ Ｉ Ｓスペクトロメータ
ー（島津ＵＶ２１ ＯＡ）にて吸収および反射スペクト
ルを測定した。これより８３０ｎＴ１１の反射率（Ｒ％
）を求めた。
ａＥＪｋＪＬＪＬ
以ｌｔにより得られた記録媒体に８３０＋ｙｍの半導体
レーザーを光パワー ７ｍＷで、レンズ径をＩＰに絞っ
て照射し、トラックの凹部に書き込みを行った。
レーザーを光パワー ７ｍＷで、レンズ径をＩＰに絞っ
て照射し、トラックの凹部に書き込みを行った。
次いで、同じレーザー光源（０，５ｍＷ）を読み出し光
とし、反射光のＣ／Ｎ比が５０ｄＢ以Ｉ−、となる片き
込み光パルス幅を測定し、感度の逆数を算出した。
とし、反射光のＣ／Ｎ比が５０ｄＢ以Ｉ−、となる片き
込み光パルス幅を測定し、感度の逆数を算出した。
耐−つし−五一
以１ユの記録媒体にサイシャインカーボンアークフェー
ドメーターにより６３℃で３００時間照射した後の反射
率、Ｃ／Ｎ比を測定し、劣化を１１８べた。
ドメーターにより６３℃で３００時間照射した後の反射
率、Ｃ／Ｎ比を測定し、劣化を１１８べた。
１１」Ｌｌ
以」−により得られた記録媒体を７０℃、９０％ＲＨで
３ケ月間保存したときの反射率およびＣ／Ｎ比を測定し
た。
３ケ月間保存したときの反射率およびＣ／Ｎ比を測定し
た。
溶−」（−性一
栓付き試験管にナフタロシニアン化合物を１．５ｇとり
、エタノールを５−添加して、密栓後６０℃で３０分間
超音波を加えて溶解した。次いで室温にして、１時間放
置後濾過して可溶分を測定して、溶解度を求めた。
、エタノールを５−添加して、密栓後６０℃で３０分間
超音波を加えて溶解した。次いで室温にして、１時間放
置後濾過して可溶分を測定して、溶解度を求めた。
（実施例）
Ｆ記する各実験隘に対応するナフタロシアニン化合物を
エタノールに溶解しスピンコーターにより、ガラス基板
［−に７０ｎｍの固形分厚さとなるように塗布した。ｆ
Ｕられた各々の試料について、各種特性および性能を評
価した。結宋を表−■に示す。
エタノールに溶解しスピンコーターにより、ガラス基板
［−に７０ｎｍの固形分厚さとなるように塗布した。ｆ
Ｕられた各々の試料について、各種特性および性能を評
価した。結宋を表−■に示す。
Ｎｏ。
Ｎｏ。
■、 Ｏ（ＣＨ２）２Ｎ（Ｃ４Ｈ９）２Ｈ３
Ｎｏ。
■、−〇−＋ＣＨ２）２Ｎ（Ｃ２Ｈ５）２Ｎｏ。
■
一〇−＋ＣＨ２）６Ｎ（ＣＨ３）２
Ｎｏ。
Ｎｏ。
■−８Ｏ□ＮＨ−（ＣＨ２）じＯＣ２□Ｈ４５■−〇
（ＣＨ２）Ｎ（ＣＨ３）２ ■ ＮＨＣＯ ２Ｈ５ Ｎｏ。
（ＣＨ２）Ｎ（ＣＨ３）２ ■ ＮＨＣＯ ２Ｈ５ Ｎｏ。
（発明の効果）
本発明の特定のナフタロシアニン化合物を主成分とする
薄膜を基板上に形成した光学記録媒体は、をバランスよ
（備えたものであり、さらに、該媒体は耐久性において
も優れたものであることが判った。これに対して、同様
のナツタロンシアニン化合物であっても本発明の一般式
で表わされる以外のものであれば、Ｌ記、光学記録媒体
としての諸特性において、いずれかが劣るものであり実
用性にとぼしいものであることが判った。
薄膜を基板上に形成した光学記録媒体は、をバランスよ
（備えたものであり、さらに、該媒体は耐久性において
も優れたものであることが判った。これに対して、同様
のナツタロンシアニン化合物であっても本発明の一般式
で表わされる以外のものであれば、Ｌ記、光学記録媒体
としての諸特性において、いずれかが劣るものであり実
用性にとぼしいものであることが判った。
特ｊ出顧人 東洋紡績株式会社
特釘ボ瀬人 洪理薬品工１絆式食社
Claims (1)
- （１）下記一般式〔１〕式で示されるナフタロシアニン
化合物を主成分とする有機薄膜を、基板上に形成せしめ
てなることを特徴とする光学記録媒体。 〔１〕式、 ▲数式、化学式、表等があります▼ （式中、Ｍは水素原子２個または I ａ、IIａ、IIIａ、
IVａ、Ｖａ、VIａ、VIIａ、VIII、 I ｂ、IIｂ、IIIｂ
、IVｂ、Ｖｂ、VIｂ、VIIｂ族の元素を表し、Ｙ＿１、
Ｙ＿２はハロゲン原子、ヒドロキシ基、または酸素を、
Ｒ＿１、Ｒ＿２、Ｒ＿３、Ｒ＿４、Ｒ＿５、Ｒ＿６、Ｒ
＿７、Ｒ＿８は少なくとも一つは一般式、▲数式、化学
式、表等があります▼（式中、Ｑは炭素数１〜１８の直
鎖又は分枝のアルキル基を、Ｒ＿９、Ｒ＿１＿０は同一
でも相異なっていても良く、水素原子、炭素数１から１
０のアルキル基または炭素数１から１０のシクロアルキ
ル基または炭素数１から１０のアルケニル基または炭素
数１から１０のシクロアルケニル基またはアリル基、ア
ラアルキル基、またはＲ＿９とＲ＿１＿０が炭素原子ま
たはヘテロ原子で結合し、一般式中の窒素原子と共に３
〜７員環の複素環を形成していることを表す） で示されるアミノアルコキシ基を表し、その他の置換基
は同一でも相異なっていても良く、上記アミノアルコキ
シ基または炭素数１〜１８の直鎖または分枝のアルコキ
シ基を表し、Ｘは素原子、ハロゲン原子、ニトロ原子を
、ｎは０〜４の整数を表す）