JPH02221401A - Stockings - Google Patents
StockingsInfo
- Publication number
- JPH02221401A JPH02221401A JP3889389A JP3889389A JPH02221401A JP H02221401 A JPH02221401 A JP H02221401A JP 3889389 A JP3889389 A JP 3889389A JP 3889389 A JP3889389 A JP 3889389A JP H02221401 A JPH02221401 A JP H02221401A
- Authority
- JP
- Japan
- Prior art keywords
- stockings
- moisture
- polyurethane coating
- permeable polyurethane
- organic solvent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
［産業上の利用分野］
本発明は、保温性、肌荒れ防止性に優れたストッキング
類に関する。DETAILED DESCRIPTION OF THE INVENTION [Industrial Field of Application] The present invention relates to stockings that are excellent in heat retention and prevention of rough skin.
［従来の技術］
ストッキングやパンティーストッキングなどのストッン
グ類は今や女性の必需洋品となっている。これらのスト
ッキング類はファツション性（美的特性）を追及したも
のばかりであり、肌荒れを防止する機能を有するものは
存在しない。[Prior Art] Stockings such as stockings and pantyhose have now become essential clothing for women. These stockings are all designed for fashionability (aesthetic properties), and none have the function of preventing skin irritation.
［発明が解決しようとする課題］
本発明者らはこれらの従来ストッキング類の有する性質
をそのまま有する上に、さらに肌荒れ防止特性を有する
ものを提供するものである。[Problems to be Solved by the Invention] The present inventors provide stockings that not only have the properties of these conventional stockings but also have skin roughness prevention properties.
本発明によれば、特に低温低湿時、たとえば冬場や寒冷
地での肌荒れを効果的に防止することができ、さらには
シエイプアップ効果も期待できる。According to the present invention, it is possible to effectively prevent skin roughness, especially in low temperature and low humidity conditions, for example, in winter or in cold regions, and furthermore, a shape-up effect can be expected.
［課題を解決するための手段］
かかる目的を達成するために、本発明は次の構成を有す
る。すなわち、
繊度５〜５０デニールのナイロン会フィラメント糸から
なる編地と透湿性ポリウレタン被膜を一体化したことを
特徴とするストッキング類であり、特に前記編地が、該
伸縮性透湿性被膜中に埋め込まれているストッキング類
では、耐久性ならびに物理特性に優れたものが提供でき
る。[Means for Solving the Problems] In order to achieve the above object, the present invention has the following configuration. That is, the stockings are characterized by integrating a knitted fabric made of nylon filament yarn with a fineness of 5 to 50 deniers and a moisture permeable polyurethane coating, and in particular, the knitted fabric is embedded in the stretchable moisture permeable coating. We can provide stockings with excellent durability and physical properties.
ストッキング類は、ソフト感を与え、さらに脚部、特に
女性の脚部の美しさをひき出す効果を有する。Stockings give a soft feel and have the effect of bringing out the beauty of legs, especially women's legs.
本発明は通常のストッキング類のもつ効果をそのまま有
し、さらに寒冷地など低温低湿の場所での肌荒れを防止
するために、温度や湿度に依存することなく、適度の湿
度を保持する機能を付与したものである。The present invention has the same effect as ordinary stockings, but also has the ability to maintain an appropriate level of humidity without depending on temperature or humidity, in order to prevent skin roughness in low-temperature, low-humidity places such as cold regions. This is what I did.
かかる機能を有するものとして、本発明では、透湿性ポ
リウレタン被膜を選択するものである。In the present invention, a moisture permeable polyurethane coating is selected as having such a function.
すなわち、この被膜は連続気泡からなる多孔性被膜であ
り、保温性に富む性質を有する。したがって、寒冷地に
おいても肌を有効に保護し、しかも発汗された汗をスム
ーズに外部に放出する機能を発揮する特徴を有する。That is, this coating is a porous coating consisting of open cells and has excellent heat retention properties. Therefore, it has the characteristics of effectively protecting the skin even in cold regions and also exhibiting the function of smoothly releasing sweat to the outside.
かかる透湿性ポリウレタン被膜は、好ましくは１〜１０
μ、特に好ましくは５μ以下の均一な気孔で構成された
微多孔を有し、好ましくはその伸長率が２００〜５００
％のものが選択される。Such a moisture permeable polyurethane coating preferably has a molecular weight of 1 to 10
μ, particularly preferably 5 μ or less, has micropores composed of uniform pores, and preferably has an elongation rate of 200 to 500.
% are selected.
かかる透湿性ポリウレタン被膜の内、編地と一体化した
状態（弛緩状態）において、ＪＩＳ Ｘ−０２０８に準
じて測定した透湿度が好ましくは２，５００ｇ／ｆｆｌ
・２４時間以上、さらに好ましくは３，０００〜１０，
０００ ｇ／ｒｄ・２４時間の透湿性を有するものが選
択される。The moisture permeable polyurethane coating preferably has a moisture permeability of 2,500 g/ffl when it is integrated with the knitted fabric (relaxed state) as measured in accordance with JIS X-0208.
・24 hours or more, more preferably 3,000 to 10,
000 g/rd・24 hours moisture permeability is selected.
しかし、かかる被膜一体化ストッキング類は原寸のまま
着用するよりは、やや伸長して着用するものであり、た
とえば伸長率の大きいところで、約１．２〜２倍程度に
伸長して着用するのが通常である。すなわち、それだけ
透湿性は向上する。However, such stockings with integrated membranes are meant to be worn slightly stretched rather than worn as they are in their original size. Normal. In other words, the moisture permeability is improved accordingly.
本発明のストッキング類は、実際の着用時での透湿性で
、好ましくは６．０００ ｇｌｏｆ・２４時間以上、さ
らに好ましくはｓ、ｏｏｏ〜１５．０００ｇ／ｎｆ・２
４時間の透湿性を有するものであれば、本発明の前記効
果は好都合に達成される。The stockings of the present invention have moisture permeability when actually worn, preferably 6,000 g/24 hours or more, more preferably s, ooo to 15,000 g/nf/2.
The effects of the present invention can be advantageously achieved if the material has a moisture permeability of 4 hours.
かかる透湿性ポリウレタン被膜は、伸縮性ならびに透湿
性を有し、保温性と透湿性を同時に発揮する上に、さら
に物理的に脚部を締付ける作用を有するので、血行を促
進し、疲れを除去する作用ならびにシエイプアップ効果
を同時に発揮する特徴を有する。Such a moisture-permeable polyurethane coating has elasticity and moisture permeability, and not only exhibits heat retention and moisture permeability at the same time, but also has the effect of physically tightening the legs, promoting blood circulation and eliminating fatigue. It has the characteristic of exerting both action and shape-up effect at the same time.
本発明のナイロン・フィラメント糸としては、ナイロン
６、ナイロン６・６、ナイロン６・１０などのポリアミ
ド、あるいはこれらに第３成分を共重合あるいはブレン
ドしてなるポリアミド系フィラメント糸など通常ストッ
キング類に使用されるものがあげられる。これらのフィ
ラメントは本発明の効果を阻害しない範囲内で他の繊維
と混用（併用）してもよい。ここでいうフィラメント糸
としてはマルチフィラメント、モノフィラメントのいず
れでもよい。The nylon filament yarn of the present invention includes polyamide filament yarns such as nylon 6, nylon 6/6, and nylon 6/10, or polyamide filament yarns made by copolymerizing or blending these with a third component, which are usually used in stockings. What is given is given. These filaments may be mixed (combined) with other fibers within a range that does not impede the effects of the present invention. The filament thread here may be either a multifilament or a monofilament.
かかるフィラメント糸としては５〜５０デニル（モノフ
ィラメントの場合は５〜２０デニール）のものが、ウレ
タン被膜との一体化のし易さ、風合ならびに感触の上か
ら選択される。Such filament yarns are selected from 5 to 50 deniers (5 to 20 deniers in the case of monofilaments) from the viewpoint of ease of integration with the urethane coating, texture, and feel.
かかるフィラメント糸は生糸、加工糸（たとえばウーリ
ーナイロン糸）や、該フィラメントをウレタン弾性糸へ
カバーリングした糸などいずれの形状、構造のものでも
よいが、好ましくは加工糸の方が伸縮性に優れている。The filament yarn may be of any shape or structure, such as raw silk, processed yarn (for example, woolly nylon yarn), or a yarn in which the filament is covered with urethane elastic yarn, but preferably processed yarn has better elasticity. ing.
本発明でいうストッキング類とはパンティーストッキン
グまたはストッキングなどをいうが、かかるストッキン
グ類の編地としては平編組織、九編組織織、タッグ編組
織など各種の通常ストッキング類に適用されるものが適
用される。−数的には平編組織が用いられ、これには４
本給糸編機、６本給糸編機、８本給糸編機などの編機が
使用される。Stockings as used in the present invention refer to pantyhose or stockings, and the knitted fabrics for such stockings include those that are used for various ordinary stockings, such as plain knit, nine-ply weave, and tag knit. be done. - Numerically, a plain knit structure is used, which includes 4
Knitting machines such as a main yarn feed knitting machine, a 6 yarn feed knitting machine, and an 8 yarn feed knitting machine are used.
本発明のストッキング類はポリウレタン被膜と編地が一
体化したものであるが、かかる一体化には部分接着構造
、や埋め込み構造がある。The stockings of the present invention are made by integrating a polyurethane coating and a knitted fabric, and such integration includes a partially bonded structure and an embedded structure.
これらの一体化構造の中でも、好ましくは埋め込み構造
が、ストッキング類の耐久性ならびに物理特性の上から
選択される。Among these integrated structures, embedded structures are preferably selected from the viewpoint of durability and physical properties of the stockings.
すなわち、本発明の代表的な例は、たとえば第１図のよ
うに透湿性ポリウレタン被膜１が、ナイロンフィラメン
ト糸からなる編地２を埋め込んだ構造で一体化されたス
トッキング類である。他の例としては第２図のように透
湿性ポリウレタン被膜１を、接着剤３により点状にナイ
ロンフィラメント糸からなる編地２と一体化したストッ
キング類があげられる。That is, a typical example of the present invention is stockings in which a moisture-permeable polyurethane coating 1 is integrated with a knitted fabric 2 made of nylon filament yarn, as shown in FIG. 1, for example. Another example is stockings in which a moisture-permeable polyurethane coating 1 is integrated with a knitted fabric 2 made of nylon filament yarn in dots using an adhesive 3, as shown in FIG.
第１１図のストッキング類も第２図のストッキング類も
、保温性や透湿性の点では変りがないが、耐久性、物理
的特性ならびにシエイプアップ特性などの点では第１図
のものが格段に優れた性能を発揮する。The stockings in Figure 11 and the stockings in Figure 2 are the same in terms of heat retention and moisture permeability, but the ones in Figure 1 are significantly superior in terms of durability, physical properties, and shape-up properties. Demonstrates excellent performance.
次に本発明の透湿性ポリウレタン被膜の製造方法につい
て説明する。Next, a method for producing a moisture-permeable polyurethane film according to the present invention will be explained.
すなわち、透湿性ポリウレタン被膜はポリウレタンエラ
ストマーの有機溶剤溶液を乾式凝固、湿式凝固または乾
湿式凝固のいずれかの凝固方法により凝固することによ
って作られる。That is, the moisture-permeable polyurethane coating is made by coagulating a solution of a polyurethane elastomer in an organic solvent by any one of dry coagulation, wet coagulation, or wet-dry coagulation.
該ポリウレタンエラストマーとしては、たとえば、ポリ
エステル系ポリウレタンエラストマーあるいはポリエー
テル系ポリウレタンエラストマーなど任意のものが使用
できる。As the polyurethane elastomer, any one can be used, such as a polyester-based polyurethane elastomer or a polyether-based polyurethane elastomer.
また、ここで使用する有機溶剤としては有機性の高い、
たとえばジメチルホルムアミド（ＤＭＦ）、ジメチルス
ルホキサイド（ＤＭＳＯ） 、テトラヒドロフラン（Ｔ
ＨＦ）などがあげられる。In addition, the organic solvent used here is highly organic,
For example, dimethylformamide (DMF), dimethyl sulfoxide (DMSO), tetrahydrofuran (T
HF), etc.
ポリウレタン被膜を連続気孔を有する多孔性物質とする
方法としては、たとえば該有機溶剤溶液に、水や低級ア
ルコールなどの極性溶剤、界面活性剤（特に非イオン界
面活性剤）またはこれらの混用物などを混合配合し、こ
れを、前記適宜の方法により凝固（場合によって加熱を
伴いながら）するなどの方法があげられる。A method for making a polyurethane film into a porous material having continuous pores is, for example, by adding a polar solvent such as water or a lower alcohol, a surfactant (particularly a nonionic surfactant), or a mixture thereof to the organic solvent solution. Examples of methods include mixing and blending the mixture and solidifying it (with heating in some cases) using the above-mentioned appropriate method.
かかる有機溶剤溶液に、さらに撥水剤や接着性化合物を
配合することにより、さらに被膜特性を改善することが
できる。By further adding a water repellent or an adhesive compound to such an organic solvent solution, the film properties can be further improved.
上記製膜方法のさらに具体的な一例をもって以下説明す
る。A more specific example of the above film forming method will be described below.
すなわち、ポリウレタンエラストマー（使用濃度測的８
〜２５重量％）のＤＭＦ溶液に、非イオン界面活性剤、
撥水剤、ポリイソシアネートを混合した組成物を湿式凝
固する。That is, polyurethane elastomer (use density measurement 8
~25% by weight) in DMF solution, a nonionic surfactant,
A composition containing a water repellent and a polyisocyanate is wet coagulated.
この場合、ポリウレタンエラストマーの濃度が低いと気
孔径は大きくなり、濃度が高くなるにつれて気孔径は小
さくなる。したがってこの濃度は被膜物性と透湿性との
関係から適宜設定するのが好ましい。In this case, when the concentration of the polyurethane elastomer is low, the pore size becomes large, and as the concentration becomes high, the pore size becomes small. Therefore, it is preferable to set this concentration appropriately from the relationship between the physical properties of the film and the moisture permeability.
該非イオン界面活性剤としては、たとえば高級アルコー
ルにエチレンオキサイド付加物など市販のものが適用で
きるが、特にポリプロピレングリコールとポリエチレン
グリコールのブロック共重合体活性剤が好ましい。この
界面活性剤により撥水剤、ポリイソシアネートとポリウ
レタンエラストマーとの相溶性を改善し、かつ凝固速度
を調整し、さらに形成する気孔を略５μ以下に調整する
ことができる。さらに、撥水剤を均一に該気孔壁表面に
集合せしめる作用をも発揮する。この界面活性剤の使用
濃度例は前記有機溶剤溶液に対して、好ましくは約１〜
８重量％程度である。As the nonionic surfactant, commercially available surfactants such as ethylene oxide adducts to higher alcohols can be used, but block copolymer surfactants of polypropylene glycol and polyethylene glycol are particularly preferred. This surfactant can improve the compatibility between the water repellent, the polyisocyanate, and the polyurethane elastomer, adjust the coagulation rate, and further adjust the size of the pores to be approximately 5 μm or less. Furthermore, it also exhibits the effect of uniformly collecting the water repellent agent on the surface of the pore walls. The concentration of this surfactant used is preferably about 1 to
It is about 8% by weight.
撥水剤としてはフッ素系撥水剤、シリコン系撥水剤など
があげられるが、特に反応性系撥水剤が好ましい。かか
る撥水剤としては、たとえば少なくとも１個のパーフロ
ロアルキル基と少なくとも１個の官能基、たとえばアク
リル基やグリシジル基を有する撥水性化合物、たとえば
パーフロロアルキルアクリレート（グリシジル）系化合
物およびその誘導体があげられる。Examples of the water repellent include fluorine-based water repellents and silicone-based water repellents, with reactive water repellents being particularly preferred. Such water repellents include, for example, water-repellent compounds having at least one perfluoroalkyl group and at least one functional group, such as an acrylic group or a glycidyl group, such as perfluoroalkyl acrylate (glycidyl) compounds and derivatives thereof. can give.
ここで上記反応性として、乾燥または加熱処理温度（た
とえば１００℃以上）で反応する性質を有するもの（た
とえばスコッチガードＦＣ−４５３：住人スリーエムＫ
Ｋ社製）を選択するのが、処理の七易さや被膜特性の点
で好ましい。Here, as the above-mentioned reactivity, a substance having a property of reacting at a drying or heat treatment temperature (for example, 100°C or higher) (for example, Scotchgard FC-453: Jujutsu 3M K
(manufactured by Company K) is preferable in terms of ease of processing and film properties.
かかる撥水剤の使用濃度例は、前記有機溶剤溶液に対し
て好ましくは約１〜１０重量％程度である。The concentration of such a water repellent agent is preferably about 1 to 10% by weight based on the organic solvent solution.
ポリイソシアネートとしては、イソシアネート基を２個
以上有する、たとえばジイソシアネート、トリイソシア
ネートなどであって、具体的には、トリレンジイソシア
ネート、ジフェニルメタンジイソシアネートなどや、こ
れらとトリメチロールプロパンやグリセリンとから誘導
したトリイソシアネートなどがあげられる。かかるポリ
イソシアネートは反応性が高いので通常はフェノールな
どの封鎖剤で適宜の温度（前記乾燥または熱処理温度）
まで遊離しないようにして用いられる。このポリイソシ
アネートの反応温度と前記反応性撥水剤の反応温度とを
調整することにより該被膜内での撥水性被膜の耐久性を
付与することができる。Examples of polyisocyanates include diisocyanates and triisocyanates having two or more isocyanate groups, such as tolylene diisocyanate, diphenylmethane diisocyanate, and triisocyanates derived from these and trimethylolpropane or glycerin. etc. Since such polyisocyanates are highly reactive, they are usually treated with a capping agent such as phenol at an appropriate temperature (the above-mentioned drying or heat treatment temperature).
It is used in such a way that it does not become liberated. By adjusting the reaction temperature of the polyisocyanate and the reaction temperature of the reactive water repellent, the durability of the water repellent film within the film can be imparted.
かかるポリイソシアネートの使用濃度例は前記有機溶剤
溶液に対して、好ましくは０．２〜３重量％程度である
。The concentration of the polyisocyanate used is preferably about 0.2 to 3% by weight based on the organic solvent solution.
かかる組成からなるポリウレタンエラストマー有機溶剤
溶液を湿式凝固する場合の凝固浴は、該有機溶剤の水溶
液が好ましく適用される。たとえばＤＭＦの場合では、
ＤＭＦ５〜２０重量％含有する水溶液が好ましく適用さ
れる。When a polyurethane elastomer organic solvent solution having such a composition is wet-coagulated, an aqueous solution of the organic solvent is preferably used as the coagulation bath. For example, in the case of DMF,
An aqueous solution containing 5 to 20% by weight of DMF is preferably applied.
かかるポリウレタンエラストマー有機溶剤溶液を、スト
ッキングに付与して一体化させる。The polyurethane elastomer organic solvent solution is applied to the stockings to integrate them.
この場合、該ストッキングを各サイズの足型に予め嵌込
んでおくのが好ましい。In this case, it is preferable to fit the stockings into the lasts of each size in advance.
すなわち、該ストッキングを着用状態つまり伸長した状
態にしておいて、透湿性ポリウレタン被膜を形成せしめ
る。That is, the moisture-permeable polyurethane coating is formed while the stockings are kept in a worn state, that is, in a stretched state.
ポリウレタン被膜の伸長率は２〜５倍、実用的にはよい
ところ２〜３倍程度であるから、上記被膜形成時のスト
ッキングの伸長状態も実用寸法付近に調整しておくのが
、被膜耐久性ならびに透湿性の設定の上から好ましい。The elongation rate of the polyurethane coating is 2 to 5 times, and a practical value is about 2 to 3 times, so it is important to adjust the elongation state of the stockings to near the practical size when forming the above film to improve the durability of the film. It is also preferred from the viewpoint of moisture permeability.
具体的には実際の足型は実用寸法よりやや小さ目で、た
とえば着用時に１．２〜２．０倍程度に伸長する大きさ
に設定しておくのが好ましい。この倍数が設定されれば
、透湿性ならびに被膜強度などを該倍数から逆算して設
定することができる。Specifically, it is preferable that the actual last of the foot be slightly smaller than the practical size, and set to a size that will elongate by about 1.2 to 2.0 times when worn, for example. Once this multiple is set, moisture permeability, film strength, etc. can be set by calculating backwards from the multiple.
なお、該ポリウレタンエラストマー有機溶剤溶液には、
必要に応じて、フタロシアニン、スレン、群青などの顔
料、さらにグリセリン、ポリエチレングリコール、スク
ワラン、ラノリン、尿素などの化粧品原料（肌荒れ防止
剤）、芳香剤（香料）、抗菌剤、防臭（消臭）剤、制電
剤などを適宜配合することができる。その場合かかる薬
剤をメラミン樹脂やシリカあるいは有機重合体などから
なるマイクロカプセルに担持させた後、配合することも
できる。In addition, the polyurethane elastomer organic solvent solution contains:
If necessary, pigments such as phthalocyanine, threne, and ultramarine, as well as cosmetic raw materials (anti-skin irritation agents) such as glycerin, polyethylene glycol, squalane, lanolin, and urea, fragrances, antibacterial agents, and deodorizing agents. , an antistatic agent, etc. can be appropriately blended. In this case, the drug may be supported in microcapsules made of melamine resin, silica, organic polymer, etc., and then blended.
なお、前記被膜形成後に、さらに前記撥水剤を１回以上
含浸付与することにより、さらに高い撥水特性（耐水圧
）を付与することができる。この場合該撥水剤の有機溶
剤溶液や反応性撥水剤を付与することにより格段の撥水
、耐水効果を達成することができる。In addition, even higher water repellency (water pressure resistance) can be imparted by impregnating the film with the water repellent agent one or more times after forming the film. In this case, significant water repellency and water resistance effects can be achieved by applying an organic solvent solution of the water repellent or a reactive water repellent.
以下、実施例により本発明を説明する。The present invention will be explained below with reference to Examples.
（実施例）
実施例１
１２デニール、５フイラメントの６・６ナイロン・ウー
リー加工糸を４本給糸編機に供給してパンティーストッ
キング用編地を編成し、これを用いてパンティーストッ
キングを縫製した。(Example) Example 1 A knitted fabric for pantyhose was knitted by supplying four 12 denier, 5 filament 6.6 nylon woolly processed yarns to a yarn feeding knitting machine, and this was used to sew pantyhose. .
このパンティーストッキングを、予め石膏製足型に装着
した後、下記組成からなるポリウレタンエラストマー有
機溶剤溶液（粘度８００ｃｐｓ／３０℃）を均一に塗布
し、直ちにＤＭＦＩＯ重量％含有する水溶液中に浸漬し
て、３０℃、５分間ゲル化し、さらに８０℃にて３０分
間湯洗した。After the pantyhose were previously attached to a plaster last, a polyurethane elastomer organic solvent solution (viscosity 800 cps/30°C) having the following composition was uniformly applied, and immediately immersed in an aqueous solution containing % by weight of DMFIO. It was gelatinized at 30°C for 5 minutes, and then washed with hot water at 80°C for 30 minutes.
これを１００℃の熱風乾燥機にて乾燥した後、１４０℃
、３分間熱処理した。After drying this in a hot air dryer at 100℃,
, heat treated for 3 minutes.
［ポリウレタンエラストマー有機溶剤溶液組成］このパ
ンティーストッキングは第１図のようにナイロン・フィ
ラメント糸がポリウレタン被膜の中に埋め込まれた構造
を有していた。このポリウレタン被膜は微細な気孔を無
数に有するもので、該ストッキングの透湿度は８０００
ｇ／％・２４時間で、保温性にも優れていた。このパン
ティストッキングを１２月〜２月の３力月間、２０人に
着用してもらったが、肌荒れは発生せず、さらに疲れが
減少し、シエイプアップ効果があるとの回答を得た。[Composition of polyurethane elastomer organic solvent solution] These pantyhose had a structure in which nylon filament threads were embedded in a polyurethane coating as shown in FIG. This polyurethane coating has countless fine pores, and the moisture permeability of the stockings is 8000.
g/% for 24 hours, and had excellent heat retention. We asked 20 people to wear these pantyhose during the three health months from December to February, and the results showed that they did not cause skin irritation, reduced fatigue, and had a shape-up effect.
比較のために上記ナイロン・フィラメント糸からなるポ
リウレタン被膜を有さない通常のパンチイードストッキ
ングを他の２０人に同一期間着用してもらったが、１５
人が肌荒れを発生し・た。For comparison, 20 other people were asked to wear regular punched stockings made of the above nylon filament yarn without a polyurethane coating for the same period;
A person has developed rough skin.
実施例２
実施例１において、該ポリウレタンエラストマー有機溶
剤溶液１００部中に、次の各薬剤をそれぞれ別々に添加
配合して３水準の溶液を調整した。Example 2 In Example 1, the following chemicals were separately added to 100 parts of the polyurethane elastomer organic solvent solution to prepare three levels of solutions.
これらの薬剤を含有するポリウレタンエラストマー有機
溶剤溶液を実施例と同一方法により塗布した。これらの
パンティーストッキングは透湿性、保温性などについて
は、いずれも実施例１と差異はなかったが、それぞれ添
加配合された薬剤の性能が付加されたものであった。す
なわち、Ａは着色効果、Ｂは肌荒れ防止効果、Ｃは汗臭
、体臭消去効果が発揮された。A polyurethane elastomer organic solvent solution containing these chemicals was applied by the same method as in the examples. These pantyhose had no difference from Example 1 in terms of moisture permeability, heat retention, etc., but each had the added performance of the drug added thereto. That is, A exhibited a coloring effect, B an effect of preventing rough skin, and C an effect of eliminating sweat odor and body odor.
［発明の効果］
本発明は、保温性に優れ、かつ肌荒れ防止効果にも優れ
たストッキング類を提供するものであり、さらに本発明
によれば、血行促進効果とシエイプアップ効果を同時に
達成する美容と健康に優れた効果を発揮するストッキン
グ類を提供することしができる。[Effects of the Invention] The present invention provides stockings that have excellent heat retention properties and are also excellent in preventing rough skin.Furthermore, according to the present invention, the present invention simultaneously achieves a blood circulation promoting effect and a shape-up effect. We can provide stockings that have excellent beauty and health benefits.
第１図は本発明の代表的なストッキング類の断面図であ
る。第２図は本発明のストッキング類の他の例である。
図中
１：透湿性ポリウレタン被膜
２：ナイロンフィラメント糸からなる編地３：接着剤FIG. 1 is a sectional view of typical stockings of the present invention. FIG. 2 shows another example of stockings according to the present invention. In the figure 1: Moisture-permeable polyurethane coating 2: Knitted fabric made of nylon filament yarn 3: Adhesive
Claims (2)
糸からなる編地と透湿性ポリウレタン被膜を一体化した
ことを特徴とするストッキング類。(1) Stockings characterized by integrating a knitted fabric made of nylon filament yarn with a fineness of 5 to 50 deniers and a moisture-permeable polyurethane coating.
込まれている請求項（１）記載のストッキング類。(2) The stockings according to claim (1), wherein the knitted fabric is embedded in the moisture-permeable polyurethane coating.