JPH01294740A - Grinding of gelatin, resin film, resin coat and coating material - Google Patents
Grinding of gelatin, resin film, resin coat and coating materialInfo
- Publication number
- JPH01294740A JPH01294740A JP12302288A JP12302288A JPH01294740A JP H01294740 A JPH01294740 A JP H01294740A JP 12302288 A JP12302288 A JP 12302288A JP 12302288 A JP12302288 A JP 12302288A JP H01294740 A JPH01294740 A JP H01294740A
- Authority
- JP
- Japan
- Prior art keywords
- gelatin
- powder
- film
- gelatin powder
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【発明の詳細な説明】
（産業上の利用分野）
この発明は樹脂フィルム、樹脂皮膜あるいは樹脂塗料等
に混入使用されるゼラチンの粉砕方法と、この粉砕され
たゼラチン粉を用いた樹脂フィルム並びに樹脂皮膜及び
樹脂塗料の提供↓こ関する。Detailed Description of the Invention (Industrial Field of Application) This invention relates to a method for pulverizing gelatin used as a mixture in resin films, resin coatings, resin paints, etc., and a resin film and resin using the pulverized gelatin powder. Regarding the provision of films and resin paints.
（従来の技術）
ゼラチンは一種の誘導蛋白質であって有機溶媒に不溶の
特性と、冷水に膨潤し、温水に溶は出し粘性の高いゾル
となる特性並びに２〜３％またはそれ以上の濃度では室
温で弾性のあるゲルを形成する特性から合成ゴムの改質
剤等として用いられている。(Prior art) Gelatin is a type of derived protein, and has the characteristics of being insoluble in organic solvents, swelling in cold water, dissolving in hot water, and forming a highly viscous sol. It is used as a modifier for synthetic rubber because of its ability to form an elastic gel at room temperature.
又、同様の特性を活かしてストレッチ性の良好なフィル
ムを作り出したり吸放湿機能を有し、しかも耐水通気性
の良好なフィルムを作り出すために樹脂フィルム中に混
入することが試みられている。In addition, attempts have been made to incorporate them into resin films in order to make use of similar properties to create films with good stretchability, moisture absorption and desorption functions, and water resistance and air permeability.
更に、各種の製品の表面に設けられる皮膜あるいは塗布
膜に同様のストレッチ性をもたらしたり、あるいは吸放
湿機能をもたらしたり、更には撥水機能と通気特性とを
同時にもたらすために、これらの皮膜あるいは塗布膜を
作り出す樹脂溶液ないしは塗料中にゼラチンを混入する
ことが試みられている。Furthermore, in order to provide similar stretch properties to the films or coatings provided on the surfaces of various products, to provide moisture absorption and desorption functions, and furthermore to provide water repellency and breathability properties at the same time, these films are being developed. Alternatively, attempts have been made to mix gelatin into the resin solution or paint that creates the coating film.
そして多くの実験の結果、これらの合成ゴムあるいは樹
脂フィルムないしは樹脂皮膜、樹脂塗膜等に含まれるゼ
ラチンは、その粒径が微細であればある程、特有の効果
を合成ゴムあるいは樹脂フィルム、樹脂皮膜ないしは樹
脂塗膜にもたらすことが明らかとされている。As a result of many experiments, the finer the particle size of gelatin contained in these synthetic rubbers, resin films, resin films, resin coatings, etc., the more specific effects it has. It is clear that this effect can be applied to films or resin coatings.
特に、樹脂フィルムを薄くすることによって、樹脂フィ
ルムに特有の伸縮性と、吸放湿性並びに撥水性とをもた
らすためには、該樹脂フィルムに含まれるゼラチン粉の
粒径をより微細な範囲で揃える必要があった。In particular, in order to make the resin film thinner and thereby provide the elasticity, moisture absorption and desorption properties, and water repellency that are unique to the resin film, the particle size of the gelatin powder contained in the resin film should be made uniform within a finer range. There was a need.
又、製品等の表面に形成された塗布膜あるいは皮膜面に
特有の滑らかさと汗ばみ感の無い良好な肌触り感及び特
有の手触り感をもたらすためにも、この塗布膜あるいは
皮膜に含まれるゼラチン粉の粒径をより微細な範囲で揃
えることが好都合であった。In addition, in order to provide the coating film or coating surface formed on the surface of the product, etc. with smoothness, a good texture without sweaty feeling, and a unique texture, the gelatin powder contained in the coating film or film may be used. It was advantageous to arrange the particle sizes within a finer range.
そこで、粉あるいは粒状とされていたゼラチンをボール
ミル等で再粉砕し、これを分級した上で使用していた。Therefore, gelatin, which had been in the form of powder or granules, was re-pulverized using a ball mill, etc., and then used after being classified.
（発明が解決しようとする課題）
しかしながら、か−る従来のボールミルで粉砕する方法
ではゼラチンの再微粉化に難があり、均一の品質を有し
、しかも均一の微細な粒径かもなる粉砕ゼラチン粉な作
り出すことができなかった。(Problems to be Solved by the Invention) However, it is difficult to re-pulverize gelatin using the conventional method of grinding with a ball mill. I couldn't make it powdery.
又、このようにゼラチン固有の特性が損われたり、ある
いは比較的大きい粒径のゼラチン粉が混入されている粉
砕ゼラチン粉を用いて作り出された樹脂フィルムあるい
は樹脂皮膜ないしは樹脂塗膜には特有の滑らかさや肌触
り感がもたらされず、これらのフィルム、皮膜ないしは
塗膜に混入ゼラチンによる特有の吸放湿機能、伸縮機能
、撥水機能等がもたらされない欠点を有していた。In addition, the inherent properties of gelatin may be impaired in this way, or resin films, resin films, or resin coatings made using crushed gelatin powder mixed with gelatin powder of relatively large particle size may have certain characteristics. They do not provide smoothness or feel to the touch, and have the disadvantage that gelatin mixed in these films, membranes, or coatings does not provide the characteristic moisture absorbing and releasing functions, elastic functions, water repellent functions, etc.
特に従前の手法である乾式ボールミルによる単純な磨砕
粉砕による粉砕では、この粉砕に際して、磨砕に伴う多
量の熱が発生し、この発熱に伴う種々の不都合がもたら
された。In particular, in the conventional method of pulverization by simple grinding and pulverization using a dry ball mill, a large amount of heat was generated due to the grinding, and this heat generation caused various inconveniences.
先ず、このボールミルによる粉砕時の発生熱によって粉
砕中のゼラチンが部分的に粘弾性のあるゲル状態とされ
る場合があり、微粉状に効率良く粉砕できなくなること
が往々にして生じ、あるいは粉又は粒状のゼラチン相互
が融着して粘弾性の塊状となる不都合があった。特に、
かＳる不都合は、粉砕処理対象とされるゼラチンの含有
水分が高い場合、あるいはゼラチンの粉砕が過湿条件下
でなされる場合等に顕著に生じた。First, the gelatin being ground may be partially turned into a viscoelastic gel state due to the heat generated during grinding by this ball mill, which often results in the inability to efficiently grind the gelatin into fine powder. There was a problem in that the granular gelatin fused together to form a viscoelastic lump. especially,
The disadvantage of sulfur is particularly noticeable when the gelatin to be pulverized has a high moisture content or when the gelatin is pulverized under humid conditions.
次いで、このボールミルによる粉砕時の発生熱によって
粉砕中のゼラチンから急速に水分が消失された場合、粉
砕ゼラチン粉の親水性が阻害され、水分による膨潤ない
しは温水に対する溶出機能が無くなる欠点を有しており
、特に粉砕ゼラチン中の含有水分が２重量％未満となる
ような条件下での粉砕にもとづく粉砕ゼラチン粉では、
かする親水性を始めとするゼラチン粉固有の粘弾性、接
着性ないしは伸縮性等の種々の特性が損なわれる欠点を
有していた。Next, if water is rapidly lost from the gelatin being ground due to the heat generated during grinding by this ball mill, the hydrophilicity of the ground gelatin powder will be inhibited, and the gelatin powder will swell with water or lose its ability to elute with hot water. In particular, for ground gelatin powder based on grinding under conditions where the water content in the ground gelatin is less than 2% by weight,
This has the disadvantage that various properties inherent to gelatin powder, such as hydrophilicity, viscoelasticity, adhesiveness, and stretchability, are impaired.
かＳる点から従前のボールミルによる粉砕の方法によっ
て粉又は粒状のゼラチンを粉砕するためには極力粉砕時
の摩擦に伴う発生熱が蓄積されたり、あるいは、この摩
擦熱等が過度に発生しないように長い時間をかけて、ゆ
っくりと粉砕する必要があった。このため、ゼラチンの
粉砕効率が悪く、又仕上がる粉砕ゼラチン粉の粒径も比
較的大きい範囲で止める必要があり、より微細なゼラチ
ン粉を得ることができなかった。From this point of view, in order to grind powder or granular gelatin using the conventional grinding method using a ball mill, it is necessary to prevent the heat generated due to friction during grinding from accumulating or to prevent excessive generation of this frictional heat. It took a long time to grind it down slowly. For this reason, the gelatin pulverization efficiency was poor, and the particle size of the finished pulverized gelatin powder had to be kept within a relatively large range, making it impossible to obtain finer gelatin powder.
そこで、粉又は粒状をなすゼラチンを液状ポリマーある
いは各種の溶剤で希釈した樹脂溶液に混配合し、この粉
又は粒状のゼラチンが混配合された液状ポリマーあるい
は樹脂溶液を湿式粉砕機に投入して粉砕することが試み
られた。Therefore, powder or granular gelatin is mixed with a liquid polymer or a resin solution diluted with various solvents, and the liquid polymer or resin solution mixed with powder or granular gelatin is placed in a wet grinder and pulverized. An attempt was made to do so.
か＼る湿式粉砕の方法では、液状ポリマーあるいは樹脂
溶液の流動抵抗が大きく、撹拌、粉砕が円滑になされな
いと共に、混配合したゼラチンがポリマー中に均一に分
散されない欠点を有していた。特に、この種の液状ポリ
マーあるいは樹脂溶液の撹拌を続行した場合、これらの
ポリマーあるいは樹脂溶液の粘性が経時的に高められる
傾向にあり、湿式粉砕機による円滑な粉砕処理が困難と
される場合が多く、粉砕機の撹拌に伴って粉砕機中の粉
砕温度が上昇された場合には、か＼る粉砕上の不都合は
更に顕著に生ずる傾向を示した。Such wet pulverization methods have the disadvantage that the flow resistance of the liquid polymer or resin solution is large, and stirring and pulverization cannot be carried out smoothly, and the blended gelatin is not uniformly dispersed in the polymer. In particular, if this type of liquid polymer or resin solution is continued to be stirred, the viscosity of these polymers or resin solutions tends to increase over time, making it difficult to grind them smoothly using a wet grinder. In most cases, when the grinding temperature in the grinder was increased as the grinder was stirred, these problems during grinding tended to become more pronounced.
又、粉又は粒状のゼラチンを粉砕する装置自体に前記の
摩擦あるいは衝撃に伴う発生熱を取り除くための冷却な
いしは排気装置あるいはゼラチンの含有水分を一定に保
つための装置等を設ける必要があり、粉砕装置自体が大
がかりなものとなる欠点を有していた。In addition, the equipment itself for grinding powdered or granular gelatin must be equipped with a cooling or exhaust device to remove the heat generated due to friction or impact, or a device to keep the moisture content of gelatin constant. The device itself had the disadvantage of being large-scale.
更に、従前の方法によって粉又は粒状のゼラチンを粉砕
した場合、粉砕機内の温度、湿度あるいはボールの撹拌
速度等の諸条件によって作り出されるゼラチン粉の粒径
にバラつきを生じ、長時間に亘る粉砕によっても粒径の
大きいゼラチン粉が微細な粒径のゼラチン粉中に残る不
都合があった。Furthermore, when powdered or granular gelatin is crushed using conventional methods, the particle size of the gelatin powder produced varies depending on various conditions such as the temperature, humidity, and stirring speed of the ball inside the crusher, and due to long-term crushing, However, there is a problem in that gelatin powder with a large particle size remains in the gelatin powder with a fine particle size.
特に従来方法によって粉又は粒状のゼラチンを粉砕した
場合粒径が１．０ミクロン（細長状の粒の場合には短い
側で測定し、以下μｍと表示する。）から５０μｍ前後
のものとなり、極めて微細な粒径のゼラチン粉が作り出
される反面、比較的大きい粒径のゼラチン粉が相当１残
される不都合があり、か＼る不都合は長時間に亘ってボ
ールミルによる粉砕を続行した場合でも同様であった。In particular, when powdered or granular gelatin is pulverized by conventional methods, the particle size ranges from 1.0 microns (in the case of elongated grains, measured on the short side, hereinafter expressed as μm) to around 50 μm, which is extremely Although gelatin powder with a fine particle size is produced, there is an inconvenience that a considerable amount of gelatin powder with a relatively large particle size remains, and this inconvenience is the same even if grinding with a ball mill is continued for a long time. Ta.
この結果、これらのゼラチン粉をポリウレタン樹脂溶液
等の樹脂素材に含ませてシート、フィルム類を成形した
場合、シート、フィルムの面から混入ゼラチンの一部が
突き出し、これがシート、フィルムの面にザラつき感を
もたらすと共に、この大きいゼラチン粒子の周縁部分と
シートあるいはフィルムとの間に縁切れを生じ易く、こ
の大きい粒径のゼラチン粒子がシートないしはフィルム
から抜は落ちたり、あるいは核部からシート、フィルム
の面にひび割れを生ずる不都合があった。As a result, when a sheet or film is formed by incorporating gelatin powder into a resin material such as a polyurethane resin solution, some of the mixed gelatin protrudes from the surface of the sheet or film, causing roughness on the surface of the sheet or film. In addition to giving a sticky feeling, edge breakage is likely to occur between the periphery of the large gelatin particles and the sheet or film, and the large gelatin particles may fall off the sheet or film, or the core may break off from the sheet or film. This had the disadvantage of causing cracks on the surface of the film.
特に取上におけるゼラチン粉の粒子径の不揃いに伴う不
都合は、成形されるフィルムの厚さを０．０２〜０．０
０６ｍｍ＋のように極薄状とした場合、あるいはシート
、布帛、革、紙ないしは各種の成形品の表面に極薄状の
０．００２ｍｎ程度の皮膜を作り出したり、更には塗料
として、このゼラチン粉を混入して使用する場合に顕著
に生ずるものであった。In particular, the problem associated with uneven particle diameters of gelatin powder during pick-up is that the thickness of the film to be formed is 0.02 to 0.0.
This gelatin powder can be used to create an ultra-thin film such as 06 mm+, or to create an ultra-thin film of about 0.002 mm on the surface of sheets, fabrics, leather, paper, or various molded products, or even as a paint. This problem was noticeable when mixed with other substances.
又、取上の従来方法によるゼラチン粉の粉砕方法並びに
粉砕されたゼラチン粉の利用方法においては、粒又は粉
状のゼラチンを略１０〜１５重量％の含水率の状態で粉
砕し、これをそのま＼の状態で各種の樹脂素材あるいは
塗料と混ぜ合せるものである。しかしながら、か＼るゼ
ラチン粉な樹脂素材あるいは塗料と混ぜ合せる場合、混
合されるゼラチン粉が微細であればある程、樹脂素材あ
るいは塗料中に円滑に分散されない傾向を示し、特に対
象とされる樹脂素材が粘性のある溶液状であったり、あ
るいは塗料液が粘性を有している場合等では、これらの
溶液あるいは塗料液中に均一に分散されない欠点な有し
ていた。In addition, in the conventional method of pulverizing gelatin powder and the method of using the pulverized gelatin powder mentioned above, granular or powdered gelatin is pulverized with a water content of about 10 to 15% by weight, and then It is mixed with various resin materials or paints in its raw state. However, when mixing such gelatin powder with a resin material or paint, the finer the gelatin powder mixed, the more difficult it is to be smoothly dispersed into the resin material or paint. When the material is in the form of a viscous solution or when the coating liquid is viscous, it has the disadvantage that it is not uniformly dispersed in these solutions or coating liquids.
更に、塗装膜あるいは各種物品の皮膜等の組成分として
、このゼラチン粉を混合した場合、これらの塗料ないし
は皮膜の構成要素中に含まれている粒径の大きいゼラチ
ン粉が塗膜あるいは皮膜の形成に際して、これらの塗膜
ないしは皮膜の面に筋状の傷をもたらし、あるいはスプ
レーガンの目詰りをもたらす不都合があった。Furthermore, when this gelatin powder is mixed as a component of paint films or films of various articles, the gelatin powder with large particle size contained in the constituent elements of these paints or films may cause the formation of the paint film or film. In this case, there is an inconvenience that streak-like scratches are caused on the surface of these coatings or coatings, or that the spray gun is clogged.
本発明はか＼る従来例における不都合に鑑み、粉又は粒
状をなすゼラチン粉の粉砕に際して生ずる摩擦に伴う熱
によってもたらされる粉砕ゼラチンに対する悪影響を取
り除くと共に、短時間で、しかも均一の粒径からなる微
細なゼラチン粉の粉砕成形を可能とし、しかもゼラチン
特有の品質が損われず、且つ均一の粒径からなるゼラチ
ン粉をジェットミルを用いて形成し、しかもこのゼラチ
ン粉を溶剤中に懸濁状に配合して用意することによって
、各種の樹脂素材あるいは塗料と円滑に、しかも均一に
混ざり合うゼラチン粉の提供を目的としている。In view of the inconveniences in the conventional examples, the present invention eliminates the adverse effects on the crushed gelatin caused by the heat caused by the friction generated during the crushing of gelatin powder in the form of powder or granules, and also provides a method for producing gelatin in a short time and having a uniform particle size. It is possible to pulverize and mold fine gelatin powder without compromising the unique quality of gelatin, and to form gelatin powder with a uniform particle size using a jet mill. Moreover, this gelatin powder can be suspended in a solvent. The aim is to provide gelatin powder that mixes smoothly and uniformly with various resin materials or paints by preparing it by blending it with gelatin powder.
（課題を解決するための手段）
本発明に係るゼラチンの粉砕方法と、この粉砕ゼラチン
粉を用いた樹脂フィルム並びに樹脂皮膜及び塗料とは取
上の目的を達成するものとして、その請求項１の発明は
、粉又は粒状をなす固体ゼラチンを用意し、このゼラチ
ンをジェットミルで粉砕、分級して粒径が６μ哨よりも
細かいゼラチン粉を作り出すものであり、請求項２の発
明は、前記請求項１の発明でのジェットミルによる粉砕
に先立って、粉砕対象とされる粉又は粒状のゼラチンを
篩又は風量分級機等を用いて分級し、粉又は粒状のゼラ
チンが１００μｍよりも微細な範囲に属するゼラチンを
、そのゼラチン全量の少なくとも９０重量％以上のもの
として用意し、この分級により粒径の揃えられたゼラチ
ンを請求項１の発明と同一の方法で、しかも低温エアー
を用いたジェットミルで粉砕するものである。(Means for Solving the Problems) The method of pulverizing gelatin according to the present invention, the resin film, resin film, and paint using the pulverized gelatin powder are as claimed in claim 1. In the invention, solid gelatin in the form of powder or granules is prepared, and this gelatin is pulverized with a jet mill and classified to produce gelatin powder having a particle size of less than 6 μm. Prior to the pulverization by the jet mill in the invention of item 1, the powder or granular gelatin to be pulverized is classified using a sieve or an airflow classifier, so that the powder or granular gelatin is finer than 100 μm. Prepare gelatin containing at least 90% by weight of the total amount of gelatin, and gelatin whose particle size has been made uniform by this classification, by the same method as the invention of claim 1, and in a jet mill using low-temperature air. It is meant to be crushed.
又、請求項３の発明は、請求項１の発明でジェットミル
を用いて粉砕のされた６μｍよりも微細な範囲に属する
ゼラチン粉な樹脂フィルムに含ませるものであり、請求
項１の発明で粉砕されたゼラチン粉を、溶剤中に混入し
、この混入溶剤と共に樹脂素材に配合し、主として０．
０２〜０．００６ ＋ｎ＋＋＋の厚さからなるフィルム
を作り出すものであり、請求項４の発明は、請求項１の
発明にもとづいてジェットミルで粉砕した６μ請よりも
細かいゼラチン粉を、溶剤中に混入し、この混入ゼラチ
ン粉を含む溶剤と共に樹脂皮膜の成形樹脂溶液の一成分
とし、形成された樹脂皮膜に６μ閣よりも微細な範囲に
属するゼラチンを均一に混入せしめるものである。In addition, the invention of claim 3 is to include in the resin film gelatin powder, which is finer than 6 μm and is pulverized using a jet mill in the invention of claim 1. The pulverized gelatin powder is mixed into a solvent, and mixed with the mixed solvent into a resin material.
02 to 0.006 +n+++, and the invention of claim 4 is based on the invention of claim 1, in which gelatin powder finer than 6 μm, which has been ground with a jet mill, is placed in a solvent. The mixed gelatin powder is mixed with the solvent and used as a component of the molding resin solution for the resin film, and the formed resin film is uniformly mixed with gelatin in a range finer than 6 μm.
更に請求項５の発明では、ジェットミルで粉砕をした６
μＩよりも微細なゼラチン粉を、溶剤中に混入し、この
混入ゼラチン粉を含んだ溶剤と共に塗料に配合して塗料
成分としたものである。Furthermore, in the invention of claim 5, the 6
Gelatin powder finer than μI is mixed into a solvent and mixed into a paint together with a solvent containing the mixed gelatin powder to form a paint component.
（作用）
本発明に係るゼラチンの粉砕方法と、この粉砕ゼラチン
を組成分の一部とするフィルム及び皮膜と、この粉砕ゼ
ラチンを含む溶剤が塗料成分の一部とされている塗料は
取上の構成からして以下の作用を有している。(Function) The method of pulverizing gelatin according to the present invention, the films and coatings in which this pulverized gelatin is part of the composition, and the paints in which the solvent containing this pulverized gelatin is part of the paint component are described below. Considering the structure, it has the following effects.
先ず請求項１の発明においては、ジェットミルのエアー
の介在によって粉砕ゼラチン粉相互が互に密着し合った
状態で摩砕、衝撃されることが無く、常にゼラチン粉相
互がジェットエアーを介在して接触される状況とされて
いることから、ゼラチン粉相互が粉砕時に溶着し合った
り、粉砕機の面に付着することがない。First, in the invention of claim 1, the pulverized gelatin powders are not ground or impacted while being in close contact with each other due to the intervention of the air of the jet mill, and the gelatin powders are always interposed with the jet air. Since the gelatin powders are in contact with each other, the gelatin powders do not weld to each other during pulverization or adhere to the surface of the pulverizer.
又、粉砕時の摩砕、衝撃に伴う発生熱がジェットエアー
に吸収され、しかも粉砕ゼラチン粉がジェットエアーに
よって表面を覆われたような状況とされていることから
、この発生熱に伴ってゼラチンの特性が損われたり、軟
化あるいは硬化することがない。In addition, the heat generated due to the grinding and impact during crushing is absorbed by the jet air, and since the surface of the crushed gelatin powder is covered by the jet air, the gelatin is absorbed by the generated heat. It does not lose its properties, soften or harden.
請求項２の発明では、粉砕されるゼラチンの粒径を一定
の範囲に揃え、しかも低温エアーを用いたジェットミル
で粉砕したことから、粉砕がより短時間で目的とする粒
径のゼラチン粉とすることができ、しかも粉砕されたゼ
ラチン粉の粒径が概ね均一とされる。又、低温エアーを
用いることによってゼラチンの粉砕が更に効率良く、し
かも粉砕ゼラチン粉の品質の劣化が避けられた。In the invention of claim 2, the particle size of the gelatin to be crushed is made to be within a certain range, and the gelatin powder is crushed in a jet mill using low-temperature air. Moreover, the particle size of the pulverized gelatin powder is generally uniform. Furthermore, by using low-temperature air, gelatin could be crushed more efficiently, and deterioration in the quality of the crushed gelatin powder could be avoided.
請求項３〜５の発明では、６μ調よりも微細とされた微
粉状のゼラチン粉が溶剤中に懸濁状とされた状態で、フ
ィルム、皮膜が形成され、あるいは塗料成分の要素とさ
れていることから、フィルムないしは皮膜の成形樹脂及
び塗料と、この粉砕ゼラチン粉との混合が円滑、確実に
なされ、このフィルム、皮膜及び塗料中に粉砕されたゼ
ラチン粉が均一に分散される特長を有している。又、こ
のフィルム、皮膜ないしは塗料中に含まれるゼラチン粉
が６μ■よりも微細な範囲に属するものであることから
、形成されるフィルム、皮膜ないしは塗装塗膜から、こ
れらのゼラチン粉が浮き出したり、突出するように露出
することがない。In the invention according to claims 3 to 5, fine gelatin powder of finer than 6 μm fineness is suspended in a solvent to form a film or coating, or as an element of a paint component. As a result, the molding resin and paint for the film or coating can be mixed smoothly and reliably with this pulverized gelatin powder, and the pulverized gelatin powder is uniformly dispersed in the film, coating, and coating. are doing. In addition, since the gelatin powder contained in this film, coating, or paint belongs to a range finer than 6μ, these gelatin powders may stand out from the formed film, coating, or paint film. It is not exposed in a protruding manner.
（実施例）
以下、本発明に係るゼラチンの粉砕方法と、この粉砕方
法により粉砕したゼラチン粉を組成分の一部とするフィ
ルム並びに皮膜と、同様のゼラチン粉を塗料成分の一部
とする塗料の典型的な一実施例について説明する。(Example) Hereinafter, a method of pulverizing gelatin according to the present invention, a film and a coating having gelatin powder pulverized by this pulverizing method as a part of the composition, and a paint having a similar gelatin powder as a part of the paint component. A typical example will be described.
先ず請求項１及び請求項２の発明の実施例について説明
するに、通例、無味、無臭の白粉又は透明な薄片として
用意される固体ゼラチン（こ＼でゼラチンとは、主とし
て工業用ゼラチンが用いられているが各種性状及び濃度
のゼラチンのいずれでも良く、にかわをも含むものであ
る。）を基本的には気乾含水率（大気中に放置した状態
での含水率＝平衡含水率）の状態でジェットミルに投入
して粉砕する。このジェットミルによる粉砕はジェット
エアーによってゼラチン相互が接触、磨砕されない状態
で粉砕ゼラチン粉の粒径が６μ園よりも微細な範囲とな
るまで続けられる。First, to explain the embodiments of the invention of claims 1 and 2, solid gelatin (here, gelatin is mainly used is industrial gelatin), which is usually prepared as a tasteless and odorless white powder or transparent flakes. gelatin of various properties and concentrations, including glue) is basically jetted at an air-dried moisture content (moisture content when left in the air = equilibrium moisture content). Pour into a mill and grind. The pulverization by this jet mill is continued until the particle size of the pulverized gelatin powder becomes finer than 6 μm, with the gelatin particles not coming into contact with each other and being ground by jet air.
又、このジェットミルにより粉砕されるゼラチン粉の粒
径を均一とし、しかも短時間に粉砕ゼラチンを目的とす
る粒径にまで粉砕するためには、ジェットミルに用いら
れるジェットエアーを一１５℃前後のものとして粉砕機
内に噴出させ、しかもこのジェットミルに投入するゼラ
チン粉を分級し、そのゼラチン粉が１００μｌよりも細
かい範囲に属している微細ゼラチン粉をゼラチン粉全量
の９０重量％以上となるように篩又は風量分級機で分級
しておくのが良い。In addition, in order to make the particle size of the gelatin powder ground by this jet mill uniform, and to grind the gelatin to the desired particle size in a short time, the jet air used in the jet mill must be heated at around -15°C. The gelatin powder is squirted into a pulverizer as a jet mill, and the gelatin powder to be input into this jet mill is classified so that the fine gelatin powder, which is smaller than 100 μl, accounts for 90% by weight or more of the total amount of gelatin powder. It is best to classify it using a sieve or airflow classifier.
尚、このジェットミルによる粉砕は、投入された粒又は
粉状のゼラチンの粒径が６μ鋼よりも微細なものとなる
まで続行される。従って、このジェットミルによる粉砕
時間等の粉砕条件は、ジェットミルの容量と、このジェ
ットミルで用いられるエアー圧及びエアー投入量と、こ
のジェットミルに投入されるゼラチンの種別及び投入量
並びにジェットミルの粉砕温度等の諸条件によって随時
変更されるが、極力粉砕中のジェットエアーの温度が上
昇されない範囲でゼラチンの粉砕をなすことが、粉砕ゼ
ラチンの品質の劣化をもたらさないために必要である。The pulverization by this jet mill is continued until the particle size of the introduced grains or powdered gelatin becomes finer than that of 6μ steel. Therefore, the grinding conditions such as the grinding time using this jet mill are determined by the capacity of the jet mill, the air pressure and amount of air input used in this jet mill, the type and amount of gelatin charged into this jet mill, and the jet mill. This may be changed from time to time depending on conditions such as the pulverization temperature, but it is necessary to pulverize gelatin within a range that does not increase the temperature of the jet air during pulverization as much as possible in order to avoid deterioration in the quality of the pulverized gelatin.
又、請求項２の発明に係る実施例では、取上の粉砕機に
よる粉砕をより効果的になすために、粉砕されるゼラチ
ンに対し予備粉砕を施し、これを真比重による風量分級
又は嵩による篩分縁によって、その粒径を揃えるもので
あり、通例ターボミル又はジットミル等の乾式粉砕機に
よる粉砕により用意する。Further, in the embodiment according to the invention of claim 2, in order to make the crushing by the pick-up crusher more effective, the gelatin to be crushed is subjected to preliminary crushing, and the gelatin is subjected to air volume classification based on true specific gravity or air volume classification based on bulk. The particle size is made uniform by the sieve edges, and it is usually prepared by grinding with a dry grinder such as a turbo mill or a jet mill.
又、このジェットミルでの粉砕に用いるエアーを略−１
５℃に冷却して除湿したものとし、ジェットミル内で生
ずる衝撃破砕に伴う温度の上昇を極力抑制する。Also, the air used for grinding with this jet mill is approximately -1
The material is cooled to 5° C. and dehumidified to suppress the temperature rise due to impact crushing that occurs in the jet mill as much as possible.
この請求項２の発明では、ジェットミルに投入されるゼ
ラチンの平均粒径を１００μ閣とし、ジェットミル内に
噴出されるジェットエアーを６ｋｇ／ｃが〜８ｋｇ／ｃ
がとし、しかも該エアーを一１５℃に冷却して用いたと
ころ、粉砕されたゼラチンの親水性が全く損なわれずボ
ールミルによる粉砕に比し極めて短かい時間で６μｍよ
りも微細な粒径のゼラチン粉とすることができた。In the invention of claim 2, the average particle size of the gelatin charged into the jet mill is 100 μm, and the jet air ejected into the jet mill is 6 kg/c to 8 kg/c.
Moreover, when the air was cooled to -15°C and used, the hydrophilicity of the ground gelatin was not impaired at all, and gelatin powder with a particle size of less than 6 μm was produced in an extremely short time compared to grinding with a ball mill. I was able to do this.
このように、ゼラチンがジェットミルのエアーを介在し
て粉砕されたことから粉砕中のゼラチンが粉砕時の発生
熱によって溶は出したり、膨潤したり、あるいは硬くな
ったりすることが少なく、粉砕中におけるゼラチンの吸
放湿現象が少ない特長を有している。この結果、ゼラチ
ンの粉砕の過程においてゼラチンの含水率が高められて
相互に融着し合ったり、柔らかくなって磨砕あるいは衝
撃粉砕に適しな（なったりすることがない、又、ゼラチ
ンの粉砕の過程においてゼラチンの含水率が低められて
親水性を阻害されるまで品質が劣化されることもない、
このようにして粉砕されたゼラチン粉は、溶剤に配合さ
れて塗料あるいは樹脂の成形用に用いられる。In this way, since the gelatin is pulverized using the air of the jet mill, the gelatin being pulverized is less likely to melt, swell, or harden due to the heat generated during pulverization. Gelatin has the advantage of having little moisture absorption and desorption phenomenon. As a result, during the gelatin grinding process, the water content of the gelatin increases and the gelatin does not fuse together or become soft and suitable for grinding or impact grinding. During the process, the water content of gelatin is lowered and the quality does not deteriorate until its hydrophilicity is inhibited.
The thus pulverized gelatin powder is mixed with a solvent and used for molding paints or resins.
例 １
ゼラチンを気乾含水率の状態でターボミルで粉砕し、こ
れを分級して平均粒径が３４μｍとなるようにした。こ
のゼラチン粉の含有水分は１２重量％であったが、実際
のゼラチン粉の粉砕では５〜１５重量％の範囲にある含
水率のゼラチン粉の使用が可能であった。前記の平均粒
径が３４μｍのゼラチンをジェットの粉砕エアー８ ｋ
ｇ／ ｃｍ’ 、分級ローター７００Ｏｒｐｍで６０分
間粉砕し、逐次分級補正をしながら６μｍ未満のゼラチ
ン粉を作り出した。このジェットミルによって粉砕され
たゼラチンの粒度分布は以下のとおりであり、この粉砕
ゼラチン粉を真比重による風量分級機で分級して６μｍ
よりも細かい範囲のゼラチン粉とした。Example 1 Gelatin was ground in an air-dried state with a moisture content using a turbo mill, and then classified to have an average particle size of 34 μm. The moisture content of this gelatin powder was 12% by weight, but in actual pulverization of gelatin powder, it was possible to use gelatin powder with a moisture content in the range of 5 to 15% by weight. The above-mentioned gelatin with an average particle size of 34 μm was crushed with 8 k of jet air.
g/cm' and pulverized for 60 minutes with a classification rotor at 700 rpm to produce gelatin powder of less than 6 μm while sequentially correcting the classification. The particle size distribution of the gelatin crushed by this jet mill is as follows.
It was made into a finer range of gelatin powder.
１０．００μｍ以上〜 ０．０重量％９．
００ ／／ 〜ｌＯ，００μｍ未満３９．４
ＪＪ８．００ ／／ 〜９．００ ＪＪ
３６．ＯＪＪ７．００ ／／ 〜８．００
／／ ０．０ ＪＪ６．００ ｎ 〜７．
００ Ｊ） １０．６ １１５．００ ／／
〜６．００ ／／ ７．ＯＢ４．００
ｉｉ 〜５．００ ／／ ２．４ ／７
３．００ ／７ 〜４．００ ｉｔ ３．
Ｑ Ｂ２．００ ｔｔ 〜３．００ ／／
ｌ、Ｑｎｌ、００ ｔｔ 〜 ２．
ＱＯ）） ０．５ ＪｌＯ，０９／／
〜 １．００ ｔｔ Ｏ，１／／例
２
前記のターボミルで粉砕し、その粒径を１００μｌで分
級したゼラチン粉をジェットミルに投入し、６ｋｇ／ｃ
がの粉砕エアーな−１５℃に冷却してジェットミル内に
噴射してゼラチン粉の粉砕をした。このジェットミルに
よる粉砕を７００Ｏｒｐｍの分級ローターによって分級
しながら７０分間続けたところ、その大部分が６μｍよ
りも細かい範囲のゼラチン粉とされた。10.00μm or more - 0.0% by weight9.
00 // ~lO, less than 00 μm 39.4
JJ8.00 // ~9.00 JJ
36. OJJ7.00 // ~8.00
// 0.0 JJ6.00 n ~7.
00 J) 10.6 115.00 //
~6.00 // 7. OB4.00
ii ~5.00 // 2.4 /7
3.00 /7 ~4.00 it 3.
Q B2.00 tt ~3.00 //
l, Qnl, 00 tt ~ 2.
QO)) 0.5 JlO,09//
~ 1.00 tt O, 1//example
2. The gelatin powder that was crushed with the turbo mill and classified into 100 μl particles was put into a jet mill, and the gelatin powder was crushed at 6 kg/c.
The gelatin powder was pulverized by cooling air to -15°C and injecting it into a jet mill. When this jet mill pulverization was continued for 70 minutes while being classified by a 700 Orpm classification rotor, the majority of the pulverization was made into gelatin powder in a range finer than 6 μm.
８．０μｍ以上〜９．０μ−未満 ２１．０重量％７．
０〃 〜８．Ｏｉｔ １Ｂ、ｇ Ｂ６．０〃
〜７．０ ／） １５．［ｌ ／１５．０
〃 〜６．Ｑ ｉｔ １９．Ｏｉｉ４．０〃
〜５．０ ／／ １２．０ ＪＪ３．０
〃 〜４．０ ）Ｊ １０．０ １／２．０
〃 〜３．０ ／／ ３．０ ＪＪ１、
Ｏ〃 〜２．Ｏｎ ｌ、７ ｎｏ、０９
／／ 〜１．０ ／／ ０．
３ ／／この実施例では、先の例１の実施例より以
上に粉砕ゼラチン粉中の含水率の低下が避けられ、粉砕
ゼラチン粉が粉砕時の発生熱によって、その品質を損な
われることがなかった。従って、この例２の方法で粉砕
されたゼラチン粉は、粉砕処理前のゼラチン素材が有し
ていたと同様の親水性を有し、吸湿に伴う膨潤と、適度
のゾル並びにゲル化をもたらす特性を有していた。8.0 μm or more to less than 9.0 μm 21.0% by weight7.
0 ~8. Oit 1B, g B6.0〃
~7.0/) 15. [l/15.0
~6. Q it 19. Oii4.0〃
~5.0 // 12.0 JJ3.0
〃 ~4.0) J 10.0 1/2.0
〃 ~3.0 // 3.0 JJ1,
O ~2. On l, 7 no, 09
// ~1.0 // 0.
3 // In this example, a decrease in the water content in the ground gelatin powder was avoided to a greater extent than in the example of Example 1, and the quality of the ground gelatin powder was not impaired by the heat generated during grinding. Ta. Therefore, the gelatin powder pulverized by the method of Example 2 has the same hydrophilicity as the gelatin material before pulverization, and has the properties of swelling due to moisture absorption and forming a suitable sol and gel. had.
取上の方法で粉砕されたゼラチン粉は、その粉砕の過程
並びに作り出されたゼラチン粉が以下の特長を有してい
る。The gelatin powder pulverized by the above method has the following features in the pulverization process and the gelatin powder produced.
先ず、ジェットミルに投入された粒又は粉状のゼラチン
は、ジェットミルのエアーで包みこまれた状態で粉砕さ
れるため、ゼラチン相互が融着し合うことがなく、又ボ
ールないしは粉砕機の面に融着することがない、特に、
ボールの磨砕ないしは衝撃に伴って生ずる熱が、ジェッ
トミルのエアーにより分散されて直接ゼラチンに伝達さ
れることがなく、熱によるゼラチンの変質ないしはゼラ
チンの溶融着の虞れがない。First, the grained or powdered gelatin fed into the jet mill is crushed while being surrounded by the air of the jet mill, so the gelatin does not fuse together and the surface of the bowl or the crusher does not melt. In particular,
The heat generated by the grinding or impact of the balls is dispersed by the air of the jet mill and is not directly transmitted to the gelatin, so there is no risk of gelatin deterioration or gelatin melting due to heat.
又、ゼラチンが低温のジェットエアーによって覆われた
状態で粉砕された場合、このゼラチンの粉砕過程におい
て、ゼラチンが湿気を帯びて膨潤ないしはゾル状となっ
たり、この粉砕過程での水分の蒸散加熱に伴うゲル化現
象を生ずることがない、従って、このジェットミルで粉
砕されたゼラチンはゼラチン特有の膨潤機能あるいは親
水性と特有の粘弾性等の特性を損うことがない、又、ゼ
ラチンの粉砕過程においてゼラチンが湿気を帯び、且つ
加熱に伴って粘性を帯びることによって粉砕が困難とさ
れることもなく、均一の粒径からなる微細なゼラチン粉
を確実且つ容易に作り出すことができる。In addition, if gelatin is crushed while being covered with low-temperature jet air, the gelatin may become moist and swell or become sol-like during the crushing process, or the gelatin may evaporate and heat due to water evaporation during the crushing process. Therefore, the gelatin milled with this jet mill does not lose its unique swelling function or properties such as hydrophilicity and unique viscoelasticity, and the gelatin milling process Fine gelatin powder having a uniform particle size can be reliably and easily produced without making grinding difficult due to the gelatin becoming moist and viscous upon heating.
更に、粉砕分級されて得られたゼラチン粉は、取上の粉
砕方法による場合では、その粒径がいずれも６μｍより
も微細なものとされ、相互に融着し合ったり、絡み合っ
たりしていない特長を有しており、この粉砕したゼラチ
ン粉な溶剤中に混合した場合、この溶剤中に均一に分散
され、概ねゼラチン粉が懸濁様に分散される特長を有し
ている。Furthermore, when the gelatin powder obtained by pulverization and classification is used by the above-mentioned pulverization method, the particle size is finer than 6 μm, and the gelatin powder is not fused or entangled with each other. It has a characteristic that when this ground gelatin powder is mixed in a solvent, it is uniformly dispersed in the solvent, and the gelatin powder is generally dispersed in a suspension-like manner.
このようにしてジェットミルを用いて粉砕されたゼラチ
ンを溶剤に混配合する。The gelatin thus pulverized using a jet mill is mixed with a solvent.
そして、これらの溶剤に混配合されたゼラチン粉は一個
一個が夫々に独立の状態で溶剤中に浮遊しており、外気
から完全に遮断されている、このことから粉砕されたゼ
ラチン粉の管理が容易とされ、粉砕後にゼラチン粉が湿
気を帯びたり、硬化したり、あるいは相互に融着し合っ
たりすることがない。The gelatin powder mixed in these solvents is individually suspended in the solvent, and is completely isolated from the outside air. This makes it difficult to manage the crushed gelatin powder. The gelatin powder does not get wet, harden, or fuse together after being ground.
このようにして粉砕されたゼラチン粉を、このゼラチン
粉の混配合した溶液と共に成形用の樹脂あるいは塗料に
配合する。この配合の方法と配合の量は、成形される樹
脂製品、フィルムないしはシートの特性及び塗料の特性
等に合せて適宜決定される。The thus pulverized gelatin powder is blended with a solution containing the gelatin powder into a molding resin or paint. The blending method and blending amount are appropriately determined depending on the characteristics of the resin product, film or sheet to be molded, the characteristics of the coating material, etc.
尚、叙正において用いられる溶剤は有機溶剤を典型例と
するものであり、この粉砕ゼラチンを混入使用する樹脂
溶液等の樹脂素材ないしはこの粉砕ゼラチンを配合され
る塗料に適応する溶剤が用いられる。そして、この溶剤
はゼラチンが不溶であることを要し、典型的にはジメチ
ルフォルムアミド
ン
ルアルコール、ｎ−ブタノール、ベンジルアルコール、
酢酸エチル、酢酸ブチル、アセトン、メチルイソブチル
ケトン、シクロヘキサン、テトラヒドロフラン、ジオキ
サン、キジロール、２・ニトロプロパン、二塩化エタン
、トリクロールエチレン、パークロールエチレン、メチ
ルセロソルブ、エチルセロソルブ等が用いられている。Incidentally, the solvent used in the preparation is typically an organic solvent, and a solvent is used that is compatible with the resin material such as the resin solution in which the pulverized gelatin is mixed or the paint in which the pulverized gelatin is mixed. This solvent must be insoluble in gelatin and typically includes dimethylformamidon alcohol, n-butanol, benzyl alcohol,
Ethyl acetate, butyl acetate, acetone, methyl isobutyl ketone, cyclohexane, tetrahydrofuran, dioxane, quidylol, 2-nitropropane, ethane dichloride, trichlorethylene, perchlorethylene, methyl cellosolve, ethyl cellosolve, etc. are used.
か＼る溶剤はゼラチンが不溶のものであることから、こ
れにゼラチンを混入してもゼラチンが膨潤したり、溶け
だしたりすることがなく、又ゼラチン中の水分等が溶剤
に吸収されてゼラチンが硬化したりすることがない．又
，ゼラチンの保管過程において、この溶剤中に投入され
たゼラチンが、この溶剤に混入したときと同様の状態で
保管される特長を有している。Since gelatin is not soluble in these solvents, gelatin will not swell or dissolve even if gelatin is mixed with it, and the water etc. in gelatin will be absorbed by the solvent and gelatin will not dissolve. It does not harden. In addition, during the gelatin storage process, the gelatin added to the solvent is stored in the same state as when it was mixed in the solvent.
前記のゼラチン粉を有する溶剤の配合される樹脂は、作
り出されるフィルム、皮膜あるいは塗装塗膜の形成に適
する樹脂であり、前記溶剤により溶液状とされるもので
ある．即ち、通例は成形される樹脂フィルム、シート等
の樹脂素材に適する溶剤を用いて前記のゼラチン粉の混
配合をなす。The resin to which the gelatin powder-containing solvent is blended is a resin suitable for forming a film, film, or paint film, and is made into a solution by the solvent. That is, the gelatin powder is usually mixed with a solvent suitable for the resin material to be molded, such as a resin film or sheet.
従って、前記のゼラチン粉の混配合に用いる溶剤の選択
により、各種の樹脂フィルム、シート等の成形と、各種
の樹脂皮膜の形成及び各種樹脂塗料が作り出される。Therefore, by selecting the solvent used for mixing the gelatin powder, various resin films, sheets, etc. can be formed, various resin films can be formed, and various resin paints can be produced.
又、このゼラチン粉を含む溶剤に配合される樹脂及び塗
液は、ペースト状であっても粉体状ないしは液状であっ
ても良く、この溶剤の配合量を調節することによってペ
ースト状ないしは粘性の高い溶液状又は粘性の低い希釈
溶液状とされる。In addition, the resin and coating liquid mixed in the solvent containing gelatin powder may be in the form of a paste, powder, or liquid, and by adjusting the amount of the solvent, it can be made into a paste or viscous form. It is in the form of a high solution or a dilute solution with low viscosity.
このようにして溶剤の配合された樹脂又は塗液を用いて
フィルムないしはシート、あるいは皮膜と、塗料とを作
り出す、このフィルム、シートを作り出す方法はカレン
ダーロール、インフレーション成形等適宜の方法が用い
られる他、雌型紙の表面にコーティングした後に、この
離型紙を剥ぎとってフィルム、シートを作る方法等があ
る。又、各種の皮膜は布、紙、皮革あるいは木製品その
他の製品の表面に塗布形成する方法と、前記溶剤を配合
された樹脂溶液中に布、紙等を漬は込み形成する方法及
び離型紙の表面にコーティングした後、この離型紙面上
の樹脂皮膜を布、樹脂シート、紙、皮革等の面に転写接
着する方法等により作り出す、更に、塗料は、各種の用
途に合せた塗膜形成要素及び顔料に対し、塗膜形成助要
素の一部として又は改良ないしは増量要素として前記の
ゼラチン粉な有する溶剤の添加配合がなされるものであ
り、−数的な撹拌、混合で作り出される。In this way, a film or sheet, or a membrane, and a paint are created using a resin or a coating liquid mixed with a solvent.The method of creating this film or sheet is by using an appropriate method such as calendar roll molding, inflation molding, etc. There are methods such as coating the surface of a female pattern paper and then peeling off the release paper to make a film or sheet. In addition, various films can be formed by coating the surface of cloth, paper, leather, wood products, or other products, by soaking cloth, paper, etc. in a resin solution containing the above-mentioned solvent, and by using release paper. After coating the surface, the resin film on the release paper surface is transferred and adhered to the surface of cloth, resin sheet, paper, leather, etc.The paint is created by a method such as transferring and adhering it to the surface of cloth, resin sheet, paper, leather, etc.Furthermore, the paint is a film-forming element suitable for various uses. The above-mentioned gelatin powder or other solvent is added to the pigment and the gelatin powder as part of the film-forming auxiliary element or as an improving or bulking element, and is produced by numerical stirring and mixing.
このようにして作り出されるフィルム、皮膜及び塗装塗
膜は、これらの素材中に含まれるゼラチン粉の粒径が６
μｍよりも微細な範囲に属していることから、フィルム
、皮膜ないしは塗装塗膜の厚さが０．０２〜０．００２
ｍｍの範囲であっても、これらのフィルム、皮膜ないし
は塗装塗膜の面から混入ゼラチン粉が浮き出したり、突
き出したりすることがなく、平滑で良好な肌触り感のあ
るフィルム、皮膜あるいは塗膜とされた。Films, membranes, and painted coatings produced in this way are made with gelatin powder contained in these materials having a particle size of 6.
Since it belongs to a range finer than μm, the thickness of the film, coating or paint film is 0.02 to 0.002
Even in the range of mm, the mixed gelatin powder does not stand out or protrude from the surface of these films, coatings, or painted coatings, and the films, coatings, or coatings are smooth and have a good texture. Ta.
又、取上のようにして作り出されたフィルム、皮膜ある
いは塗膜等の樹脂成形品中に含まれるゼラチン粉の一部
を溶出することにより、このフィルム、皮膜あるいは塗
膜等の面に数ミクロンよりも微細な多数の孔を設けるこ
とができる。In addition, by eluting a part of the gelatin powder contained in the resin molded product such as the film, membrane, or coating produced in the above manner, a few microns of It is possible to provide a large number of holes that are finer than the above.
このように２〜３μｍよりも微細な孔をフィルム、皮膜
あるいは塗膜の面に設けることによって、これらのフィ
ルム、皮膜あるいは塗膜に通気性がもたらされること＼
なり、特にこのフィルム、皮膜あるいは塗膜にもたらさ
れる通気性は、０．０００４μ閣前後の粒径からなる水
蒸気を、 通し、水滴を通さない特長を有している。In this way, by providing pores smaller than 2 to 3 μm on the surface of a film, coating, or coating, these films, coatings, or coatings are made breathable.
In particular, the air permeability provided to this film, film, or coating has the feature of allowing water vapor with a particle size of around 0.0004 μm to pass through, but not allowing water droplets to pass through.
このことから耐水、透湿機能をフィルム、皮膜あるいは
塗膜にもたらすことができる。From this, water resistance and moisture permeability can be imparted to the film, film, or coating.
従って、各種の布地、皮革あるいは木製品等の表面に前
記のゼラチン粉を含む０．０２〜０．００２ｍｍ厚さか
らなる皮膜あるいは塗膜を形成し、ないしはフィルムを
貼り合せて、この皮膜、塗膜あるいはフィルム中のゼラ
チン粉を溶出した場合、これらの布地、皮革あるいは木
製品等に特有の耐水性と透湿性とがもたらされることＳ
なる。因みに、通例の雨滴の径は２０００μｍであり、
微細な電画においても１００μ■であって、これらのフ
ィルム等に設けられた微細な孔を通過することがない、
又、これらのフィルム面等に付着した雨滴も表面張力の
関係から前記の微細な孔を通して滲潤することがない。Therefore, a film or paint film containing the gelatin powder with a thickness of 0.02 to 0.002 mm is formed on the surface of various fabrics, leather, wooden products, etc., or a film is bonded to the surface of the product. Alternatively, when the gelatin powder in the film is eluted, the water resistance and moisture permeability characteristic of these fabrics, leather, wood products, etc. are brought about.
Become. By the way, the diameter of a normal raindrop is 2000μm,
Even minute electrical pictures have a diameter of 100μ and do not pass through the minute holes provided in these films.
Furthermore, raindrops adhering to the surface of these films do not seep through the fine pores due to surface tension.
例 ３
前記ゼラチン粉を含む溶剤を用いてポリウレタン樹脂フ
ィルムを作り、このフィルムを繊編布の面に転写した。Example 3 A polyurethane resin film was made using a solvent containing gelatin powder, and this film was transferred onto the surface of a woven fabric.
６μｍよりも微細なゼラチン粉 １ｏ重量部ト ル
エ ン ７０重量部ポリウ
レタン樹脂固形分 ３０重量部この樹脂溶液を離
型紙の面にドクターナイフコーティング法により０．０
０８ｍｍの厚さで塗着し、これを乾燥した後に該離型紙
より剥ぎとって厚さ０．００８ｍ＋ｎのフィルムを作っ
た。Gelatin powder finer than 6 μm 10 parts by weight Torr
Ene 70 parts by weight Polyurethane resin solid content 30 parts by weight This resin solution was coated on the surface of release paper with a doctor knife coating method.
The film was applied to a thickness of 0.08 mm, and after drying, it was peeled off from the release paper to form a film with a thickness of 0.008 m+n.
又、このフィルムを引き剥すことなく１．５ｍｍ厚の不
織布の面に接着しながら前記離型紙を剥ぎとって不織布
の面にフィルムスキン層を作り出した。そして、この不
織布を６０”Ｃの温水中に漬は込んで１５分間湯洗いし
たところフィルム中に含まれているゼラチン粉が、その
全量の３５重量％相当消失した。Further, the release paper was peeled off while adhering this film to the surface of a 1.5 mm thick nonwoven fabric without peeling it off, thereby creating a film skin layer on the surface of the nonwoven fabric. Then, when this nonwoven fabric was soaked in hot water at 60''C and washed in hot water for 15 minutes, gelatin powder contained in the film disappeared by an amount equivalent to 35% by weight of the total amount.
尚、前記のゼラチン粉の混入量を３重量部〜３０重量部
の間で各５重量部づつ増しながらフィルムを作ったとこ
ろ、前記例３の割合でゼラチン粉を３重量部としたとこ
ろ作り出されたフィルム面の光沢が良好で、充分な腰の
強さを有している反面、接触時のベタつき感があった。Incidentally, when films were made by increasing the amount of gelatin powder mixed in between 3 parts by weight and 30 parts by weight in increments of 5 parts by weight each, when the gelatin powder was added to 3 parts by weight at the ratio of Example 3, Although the surface of the film had good gloss and sufficient stiffness, it felt sticky upon contact.
又、３５重量部のゼラチン粉を配合したフィルム面はゼ
ラチン特有の接触抵抗と良好な肌触り感がある反面、フ
ィルム面に強い力が作用した場合に、このフィルム面に
シワよれを生じ、又前記のフィルムをラミネートした製
品では、表面がヨした状態で下地の生地面が一部露出す
ることがあった。従って、前記のゼラチン粉の配合量は
３〜３０重量部が最適である。しかしながら、フィルム
の成形樹脂の種別、使用溶剤の配合量及び成形条件等に
よって前記のゼラチン粉の配合量を更に変更することも
できる。In addition, while the film surface containing 35 parts by weight of gelatin powder has the contact resistance and good texture characteristic of gelatin, it also wrinkles when a strong force is applied to the film surface. For products laminated with this film, the surface was warped and a portion of the underlying fabric surface was sometimes exposed. Therefore, the optimum amount of the gelatin powder is 3 to 30 parts by weight. However, the amount of gelatin powder can be further changed depending on the type of film molding resin, the amount of solvent used, molding conditions, etc.
又、前記の湯洗によるゼラチン粉の溶出は、使用温水の
湯温を高くする程、短時間で多量の含有ゼラチン粉の溶
出が可能とされる反面、フィルムないしはラミネートフ
ィルムが毀損されたり、ベースとなる生地が損傷される
不都合があった。このことからフィルムのラミネートさ
れる生地の種別、素材特性とフィルム自体の素材特性並
びにフィルム中に含まれているゼラチン粉の１並びにフ
ィルムから溶出されるゼラチン粉の量等を総合的に勘案
して、このフィルム、皮膜あるいは塗膜中に含まれてい
るゼラチン粉の溶出がなされる。尚、前記実施例のポリ
ウレタン樹脂フィルムにおいては６０〜１５０℃の温水
又は熱水で含有ゼラチン粉の溶出をなすことが理想的で
あり、６０℃以下の温水では含有ゼラチン粉の溶出量が
少なく、時間も長く必要とされた。Furthermore, in the above-mentioned elution of gelatin powder by hot water washing, the higher the temperature of the hot water used, the more gelatin powder it contains can be eluted in a shorter time. There was an inconvenience that the fabric would be damaged. From this, we comprehensively take into consideration the type of fabric the film is laminated with, the material characteristics of the film itself, the amount of gelatin powder contained in the film, and the amount of gelatin powder eluted from the film. Then, the gelatin powder contained in the film, membrane or coating is eluted. In addition, in the polyurethane resin film of the above-mentioned example, it is ideal to elute the gelatin powder contained in hot water of 60 to 150 ° C., and the amount of gelatin powder contained in the film is small in hot water of 60 ° C. or less. It also required a lot of time.
例 ４
ト ル エ ン ７０重量部６μｍ
よりも微細なゼラチン粉 １０重量部ポリ塩化ビニル樹
脂 ３０重量部この例４で作り出された塩ビ
フィルムでは柔軟性が増し、通例の塩ビフィルムに比し
伸縮性が著しく増すと共に吸湿機能がもたらされた。Example 4 Toluene 70 parts by weight 6 μm
10 parts by weight of finer gelatin powder 30 parts by weight of polyvinyl chloride resin The PVC film produced in this Example 4 has increased flexibility and significantly increased stretchability compared to conventional PVC film, as well as a moisture absorbing function. Ta.
又、前記配合量によってフィルム、皮膜の形成と共に塗
料が作り出された。Also, depending on the above-mentioned blending amount, a coating material was produced along with the formation of a film and a coating.
例 ５
ト ル エ ン ７０重量部６μ鱗よ
りも微細なゼラチン粉 １０重量部アクリル樹脂
３０重量部
この例５の配合比率で作り出されたフィルムは耐候性に
優れており、耐摩耗性が良好である割に接触時のベタつ
き感がない特長を有し、フィルム面の光沢も良好であっ
た。又、この配合比率からなる樹脂溶液で皮膜を形成し
、又塗料として塗膜を形成したところ同様に耐摩耗性に
優れ、且つ吸湿機能を有する皮膜ないしは塗膜とされた
。Example 5 Toluene 70 parts by weight Gelatin powder finer than 6μ scales 10 parts by weight Acrylic resin
30 parts by weight The film produced with the blending ratio of Example 5 has excellent weather resistance, has good abrasion resistance, has no sticky feeling upon contact, and has good gloss on the film surface. there were. Furthermore, when a film was formed with a resin solution having this blending ratio and a coating film was also formed as a paint, the film or coating film was similarly excellent in abrasion resistance and had a moisture absorbing function.
例 ６
ト ル エ ン ７０
重量部６ＬＬＩＩ＋よりも微細なゼラチン粉 １０重量
部ポリ塩化ビニル樹脂 １５重量部アクリル
樹脂 １５重量部
この例６の配合比率で作り出されたフィルムは前記例５
のフィルムに比し耐摩耗性が劣る傾向を示したが肌触り
が良く、ラミネート時の接着性が良好であった。又、こ
の配合比率からなる樹脂溶液を用いて形成した皮膜及び
、この樹脂溶液を含む塗料を用いて形成した塗膜は吸湿
性と、接触抵抗とが良好で適度の肌触り感を有している
。Example 6 Toluene 70
Part by weight 6 Gelatin powder finer than LLII+ 10 parts by weight Polyvinyl chloride resin 15 parts by weight Acrylic resin 15 parts by weight The film produced with the blending ratio of Example 6 was the same as Example 5.
Although the abrasion resistance tended to be inferior to that of the above film, it felt good to the touch and had good adhesion during lamination. In addition, films formed using a resin solution having this blending ratio and coating films formed using a paint containing this resin solution have good hygroscopicity and contact resistance, and have an appropriate feel to the touch. .
例 ７
トルエン中に粉砕ゼラチン粉を混配合し、この粉砕ゼラ
チン粉を有するトルエンに二液反応タイプのウレタン塗
料のポリエステルを配合し、その後インシアネートを添
加配合してスプレーガンで膜厚０．００６＋ａｍの塗膜
を得た。Example 7 Mix ground gelatin powder in toluene, blend polyester of a two-component reaction type urethane paint into the toluene containing the ground gelatin powder, then add and blend incyanate and spray with a spray gun to a film thickness of 0.006+ am. A coating film was obtained.
この塗膜は艶消し効果に優れ１手に触れたときの風合い
はベトつき感がなく良好であった。この実施例では、二
液反応型ウレタン樹脂塗料中のポリエステルとゼラチン
粉との合計重量に対するゼラチン粉を１０〜４０重量％
の範囲で塗膜を形成した。This coating film had an excellent matte effect and had a good texture when touched with the hand without any sticky feeling. In this example, the amount of gelatin powder was 10 to 40% by weight based on the total weight of polyester and gelatin powder in the two-part reactive urethane resin paint.
A coating film was formed in the range of .
例 ８
液状ウレタン樹脂液（無黄変−波型ボリウレクン、不揮
発分３０％）をメチルエチルケトンの混合剤を用いて２
０〜５０ ｐｏｉｓｅ （２５℃）に調整し、このウレ
タン樹脂１００重量部中にゼラチン粉５０重量部をトル
エンと共に混合し、１００ ｐｏｉｓｅ （２５℃）
となるように撹拌混合した。この混合物をＰｖＣ板にス
プレーガンで吹きつけ１００℃で１分間乾燥したところ
吸湿性の良好な、しかも艶消し効果の高い塗膜が得られ
た。Example 8 A liquid urethane resin solution (non-yellowing - corrugated polyurethane, non-volatile content 30%) was mixed with a mixture of methyl ethyl ketone.
0 to 50 poise (25°C), 50 parts by weight of gelatin powder was mixed with toluene in 100 parts by weight of this urethane resin, and the temperature was adjusted to 100 poise (25°C).
The mixture was stirred and mixed. When this mixture was sprayed onto a PvC board with a spray gun and dried at 100° C. for 1 minute, a coating film with good hygroscopicity and a high matting effect was obtained.
例 ９
ウレタン樹脂１００重量部中にゼラチン粉３０重量部を
含む溶剤を配合して得られた混合液を離型紙上にコーテ
ィングし、乾燥後得られた０、００６ｍｍの厚さのフィ
ルムを繊物基材に転写して張り合せた。このようにして
作り出された織物の表面はベトつき感がなく、感触にも
優れていた。Example 9 A mixed solution obtained by blending 100 parts by weight of urethane resin with a solvent containing 30 parts by weight of gelatin powder was coated on release paper, and after drying, the obtained film with a thickness of 0,006 mm was used as a textile material. It was transferred to a base material and pasted. The surface of the fabric thus produced had no sticky feeling and had an excellent feel.
例 １０
離型紙上にゼラチン粉を含む一液型ウレタン樹脂（ゼラ
チン粉含有のメチルエチルケトンを溶剤とした不揮発分
３０重量％の混合液）をコンマロールで塗布、乾燥し、
更に、このコーティング層の上に、ゼラチン粉な含む二
液型ウレタン樹脂（ゼラチン粉含有のメチルエチルケト
ンを溶剤とした不揮発分５０重量％の混合液）を塗布、
乾燥して積層皮膜を作り、この積層皮膜を離型紙から引
き剥がすようにして不繊布の面にラミネート接着した。Example 10 A one-component urethane resin containing gelatin powder (a mixture of gelatin powder and methyl ethyl ketone as a solvent with a non-volatile content of 30% by weight) was applied onto release paper using a comma roll, dried,
Furthermore, on top of this coating layer, a two-component urethane resin containing gelatin powder (a mixture of gelatin powder and methyl ethyl ketone as a solvent with a non-volatile content of 50% by weight) is applied.
It was dried to form a laminated film, and this laminated film was peeled off from the release paper and laminated and adhered to the surface of the nonwoven fabric.
このラミネートフィルムを有する不織布の表面はベトつ
き感がなく、又ゼラチン粉を含まないラミネート接着と
同様の接着強度が得られた。The surface of the nonwoven fabric having this laminate film did not have a sticky feeling, and adhesive strength similar to that of laminate adhesion not containing gelatin powder was obtained.
（効果）
本発明に係るゼラチンの粉砕方法では、ゼラチン粉がジ
ェットミルのエアーによって夫々に分離された状態で粉
砕されることから、ゼラチン粉相互が直接々触して融着
し合うことがない。(Effects) In the method for pulverizing gelatin according to the present invention, the gelatin powders are separated and pulverized by the air of the jet mill, so that the gelatin powders do not come into direct contact with each other and fuse together. .
又、ゼラチン粉の粉砕に際して衝撃粉砕に伴う熱の発生
が無く、熱変化に伴うゼラチン粉相互の融着あるいは品
質劣化の不都合を生ずることがない。Further, when the gelatin powder is pulverized, no heat is generated due to impact pulverization, and there is no problem of gelatin powders fusing together or quality deterioration due to thermal changes.
更に、ジェットミルのエアーで包みこまれた状態でゼラ
チン粉が粉砕されることから、粉砕の過程においてゼラ
チン粉が極端に乾燥したり、膨潤したりすることがない
、このことからゼラチン粉の乾燥に伴う親水性の阻害が
少な（、又膨潤に伴ってゼラチン粉が粘性を帯びて粉砕
が阻害される不都合も少ない、これらのことから粒径が
６μｍよりも微細な範囲に属するゼラチン粉を確実に、
しかも短時間で効率良（作り出すことができた。Furthermore, since the gelatin powder is crushed while being surrounded by the air of the jet mill, the gelatin powder does not dry out or swell excessively during the crushing process. (Also, gelatin powder becomes viscous as it swells, which inhibits grinding.) For these reasons, it is recommended to use gelatin powder whose particle size is finer than 6 μm. To,
Moreover, it was possible to create it efficiently in a short time.
更に、この微細な粉状に粉砕されたゼラチンが溶剤中に
懸濁状に分散されていることからフィルム、シートある
いは皮膜等の成形樹脂との配合が円滑、容易とされ、こ
れらの樹脂混合液中にゼラチン粉が均一に分散される特
長を有している。又、か＼る特長は、粉砕されたゼラチ
ン粉を、溶剤と共に塗料成分とした場合でも同様である
。Furthermore, since this fine powdered gelatin is dispersed in a suspension in a solvent, it is said to be smooth and easy to blend with molding resins for films, sheets, membranes, etc., and these resin mixtures. It has the feature that gelatin powder is evenly dispersed inside. Moreover, the above characteristics are the same even when pulverized gelatin powder is used as a coating component together with a solvent.
従って、斜上の６μｍよりも微細な範囲に属するゼラチ
ン粉を含む樹脂混合液あるいは塗料を用いてフィルム、
皮膜あるいは塗膜を形成した場合、これらのフィルム、
皮膜あるいは塗膜中にゼラチン粉が均一に分散された状
態で、これらのフィルム等が形成される。このことから
、これらのフィルム等にゼラチン特有の吸放湿性、適度
の接触抵抗、及び伸縮性がもたらされると共に静電気の
帯電が防止される特長を有している。Therefore, using a resin mixture or paint containing gelatin powder in a range finer than 6 μm,
When a film or coating is formed, these films,
These films are formed with gelatin powder uniformly dispersed in the film or coating. As a result, these films and the like have the characteristics of gelatin-specific moisture absorption and desorption properties, appropriate contact resistance, and elasticity, as well as being prevented from being charged with static electricity.
又、これらのフィルム、シート、皮膜ないしは塗膜に含
まれるゼラチン粉の粒径が６μｍよりも微細であること
から、これらのフィルム、シート、皮膜ないしは塗膜を
薄（形成することが可能とされた。特にフィルムないし
は皮膜としては０．００６ｍｍの厚さのものが、又塗膜
としては０．００２ｍｍの厚さのものが作られ、そのい
ずれにおいても形成されたフィルム、皮膜あるいは塗膜
の面から混入ゼラチン粉が浮き出したり、突き出したり
することがなく、肌触りが良好で滑らかな面とされた。In addition, since the particle size of the gelatin powder contained in these films, sheets, films, or coatings is finer than 6 μm, it is possible to form these films, sheets, films, or coatings thinly. In particular, films or coatings with a thickness of 0.006 mm and coatings with a thickness of 0.002 mm were made, and in both cases, the surface of the formed film, coating, or coating was made. The mixed gelatin powder did not stand out or stick out, and the surface was smooth and felt good to the touch.
又、形成されるフィルム、皮膜あるいは塗膜の面にゼラ
チン粉が均一に露呈していることから、これらのフィル
ム、皮膜あるいは塗膜の面に吸湿性が効果的にもたらさ
れ、良好な肌触り感がもたらされる。In addition, since the gelatin powder is uniformly exposed on the surface of the film, film, or coating that is formed, hygroscopicity is effectively brought to the surface of the film, film, or coating, resulting in a good texture. It brings a feeling.
更に、形成されるフィルム、皮膜あるいは塗膜の面から
混入ゼラチン粉を溶出させた場合、これらのフィルム、
皮膜あるいは塗膜の面に数ミクロンの微細な孔が無数に
設けられることＳなり、形成されるフィルム等の面に特
有の吸放湿機能、特に耐水透湿機能がもたれらされる特
長を有している。Furthermore, if mixed gelatin powder is eluted from the surface of the formed film, membrane or coating, these films,
Innumerable micropores of several micrometers are provided on the surface of the film or coating, and the surface of the formed film has a unique moisture absorbing and releasing function, especially water resistance and moisture permeability. are doing.
又、取上で形成されたフィルム、皮膜あるいは塗膜の面
にサンディング処理を施した場合、フィルム等に含まれ
ているゼラチン粉の有する吸湿機能、耐水透湿機能と、
良好な肌触り感が更に助長される。In addition, when sanding is applied to the surface of the film, film, or coating formed during pick-up, the gelatin powder contained in the film etc. has a moisture absorption function, a water resistance and moisture permeability function,
Good touch feeling is further promoted.
本発明に係るゼラチンの粉砕方法と、この粉砕方法によ
って得られるゼラチン粉な用いたフィルム、皮膜並びに
塗料は取上における特長ある内容から合成皮革材として
各種の家具あるいは鞄等の身の回り用品ないしは自動車
の内装材等として用いられる他、静電気を帯びない特性
を活かして各種の電子機器と、これらのオへレーク−用
のキーボード等として用いられる。The method of pulverizing gelatin according to the present invention and the gelatin powder obtained by this pulverizing method as well as films, membranes, and paints can be used as synthetic leather materials for use in various furniture, personal items such as bags, and automobiles. In addition to being used as interior materials, it is also used in various electronic devices and keyboards for these devices due to its non-static properties.
又、取上のゼラチン粉を有するフィルム及び皮膜並びに
塗料は、ゼラチン粉な含まない通例のフィルムの成形方
法あるいは皮膜の形成方法ないしは塗膜の形成方法と同
一の方法ないしは手法で作り出したり、用いたりするこ
とができる。このことから本発明に係る粉砕ゼラチン粉
を用いたフィルム、皮膜及び塗膜は日常身の回りにある
全ての商品の成形ないしは表面化粧等の手段として用い
ることができる。In addition, the films, coatings, and coatings containing gelatin powder mentioned above may be produced or used by the same method or method as the method for forming a film, forming a film, or forming a coating film that does not contain gelatin powder. can do. From this, films, membranes and coatings using the ground gelatin powder according to the present invention can be used as means for molding or surface decoration of all the products that are around us every day.
Claims (1)
分級して、６ミクロンよりも微細な粒径のゼラチン粉と
したことを特徴とするゼラチンの粉砕方法。 ２、平均粒径が１００ミクロンとされた粉又は粒状のゼ
ラチンを低温エアーを用いたジェットミルで粉砕して分
級し、６ミクロンよりも微細な粒径のゼラチン粉とした
ことを特徴とするゼラチンの粉砕方法。 ３、粉又は粒状をなすゼラチンがジェットミルで粉砕さ
れ、且つ分級されて６ミクロンよりも微細な粒径のゼラ
チン粉とされていると共に該ゼラチン粉がジメチルフォ
ルムアミド、トルエン等の溶剤に混配合されて形成樹脂
フィルム組成分の一部とされていることを特徴とする樹
脂フィルム。 ４、粉又は粒状をなすゼラチンがジェットミルで粉砕さ
れ、且つ分級されて６ミクロンよりも微細な粒径のゼラ
チン粉とされていると共に該ゼラチン粉がジメチルフォ
ルムアミド、トルエン等の溶剤に混配合されて形成樹脂
皮膜組成分の一部とされていることを特徴とする樹脂皮
膜。 ５、粉又は粒状をなすゼラチンがジェットミルで粉砕さ
れ、且つ分級されて６ミクロンよりも微細な粒径のゼラ
チン粉とされていると共に該ゼラチン粉がジメチルフォ
ルムアミド、トルエン等の溶剤に混配合されて塗料成分
の一部とされていることを特徴とする塗料。[Claims] 1. Grinding powder or granular gelatin with a jet mill;
A method for pulverizing gelatin, characterized by classifying it into gelatin powder having a particle size finer than 6 microns. 2. Gelatin characterized by powder or granular gelatin with an average particle size of 100 microns being crushed and classified using a jet mill using low-temperature air to obtain gelatin powder with a particle size finer than 6 microns. How to grind. 3. Powder or granular gelatin is ground with a jet mill and classified into gelatin powder with a particle size finer than 6 microns, and the gelatin powder is mixed with a solvent such as dimethylformamide or toluene. A resin film characterized in that the resin film is a part of the composition of the formed resin film. 4. Powdered or granular gelatin is ground with a jet mill and classified into gelatin powder with a particle size finer than 6 microns, and the gelatin powder is mixed with a solvent such as dimethylformamide or toluene. A resin film comprising: 5. Powdered or granular gelatin is pulverized with a jet mill and classified into gelatin powder with a particle size finer than 6 microns, and the gelatin powder is mixed with a solvent such as dimethylformamide or toluene. A paint characterized by being a part of the paint component.