JPH01280375A - Semiconductor substrate having superconductor layer - Google Patents
Semiconductor substrate having superconductor layerInfo
- Publication number
- JPH01280375A JPH01280375A JP63110018A JP11001888A JPH01280375A JP H01280375 A JPH01280375 A JP H01280375A JP 63110018 A JP63110018 A JP 63110018A JP 11001888 A JP11001888 A JP 11001888A JP H01280375 A JPH01280375 A JP H01280375A
- Authority
- JP
- Japan
- Prior art keywords
- buffer layer
- composite oxide
- semiconductor
- substrate
- oxide superconductor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【発明の詳細な説明】
産業上の利用分野
本発明は、半導体基板に関する。より詳細には、少なく
とも1層の超電導体層を有する半導体単結晶基板に関す
るものである。DETAILED DESCRIPTION OF THE INVENTION Field of the Invention The present invention relates to semiconductor substrates. More specifically, the present invention relates to a semiconductor single crystal substrate having at least one superconductor layer.
本発明の半導体基板は上記超電導体層を半導体集積回路
の線材料として用いるだけで無く、上記超電導体にジョ
セフソン結合を形成したジョセフソン素子あるいは超電
導体と半導体とを組み合わせた超電導トランジスタやホ
ットエレクトロントランジスタ等の素子の材料として用
いることができる。The semiconductor substrate of the present invention not only uses the superconductor layer as a line material for a semiconductor integrated circuit, but also a Josephson element in which a Josephson bond is formed in the superconductor, a superconducting transistor in which a superconductor and a semiconductor are combined, and a hot electron It can be used as a material for elements such as transistors.
従来の技術
従来の半導体集積回路はシリコン等の半導体単結晶基板
上に絶縁膜を形成してバターニングを施し、熱拡散、イ
オン注入等で不純物をドープすることにより必要な素子
を作製し、金属を蒸着させて配線している。Conventional technology Conventional semiconductor integrated circuits are fabricated by forming an insulating film on a semiconductor single crystal substrate such as silicon, subjecting it to buttering, doping with impurities by thermal diffusion, ion implantation, etc. to fabricate the necessary elements, is vapor-deposited for wiring.
上記金属配線パターンは、蒸着で形成されるため断面積
が非常に微小となり、信号電流のロスがあった。Since the metal wiring pattern is formed by vapor deposition, its cross-sectional area is extremely small, resulting in loss of signal current.
また、超電導体と半導体とを組み合わせた超電導トラン
ジスタやホットエレクトロントランジスタ等の集積回路
素子は概念的には提案されているが複合酸化物超電導材
料を具体的に用いたものは作製されていない。Furthermore, although integrated circuit elements such as superconducting transistors and hot electron transistors that combine superconductors and semiconductors have been conceptually proposed, none have been manufactured using composite oxide superconducting materials specifically.
発明が解決しようとする課題
半導体集積回路の金属配線パターンは、蒸着等で形成さ
れるため断面積が微小で信号電流のロスが避けられなか
った。また、半導体集積回路の動作速度を向上させるに
は、素子そのものの動作速度を向上させることも重要で
あるが、配線における信号伝播速度を向上させることも
必要である。Problems to be Solved by the Invention The metal wiring patterns of semiconductor integrated circuits are formed by vapor deposition or the like, so their cross-sectional area is minute, and loss of signal current is unavoidable. Furthermore, in order to improve the operating speed of a semiconductor integrated circuit, it is important to improve the operating speed of the element itself, but it is also necessary to improve the signal propagation speed in wiring.
ところが、従来の半導体集積回路では配線部分における
ロスのため信号伝播速度を向上させるのに限界があった
。また、配線部分におけるロスのため素子の集積度があ
がり高密度化が進むと、消費電力が上昇し、それに伴う
発熱のため集積度の限界も自ずから決まってしまってい
た。However, in conventional semiconductor integrated circuits, there is a limit to improving the signal propagation speed due to loss in the wiring portion. Furthermore, as the degree of integration of elements increases due to loss in wiring portions and density increases, power consumption increases, and the heat generated thereby naturally limits the degree of integration.
さらに、超電導体と半導体とを組み合わせた超電導トラ
ンジスタやホットエレクトロントランジスタ、FET等
の素子を形成する場合には半導体単結晶基板上に超電導
材料の層を均一に形成した基板が必須であるが、従来の
Nb系の超電導材料では半導体基板上に超電導材料の層
を均一に形成したものはなかった。また、金属系超電導
体は、臨界温度が低く実用的でなかった。Furthermore, when forming elements such as superconducting transistors, hot electron transistors, and FETs that combine superconductors and semiconductors, a substrate with a uniform layer of superconducting material formed on a semiconductor single crystal substrate is essential. Among the Nb-based superconducting materials, there has been no one in which a layer of superconducting material is uniformly formed on a semiconductor substrate. Furthermore, metal-based superconductors have low critical temperatures and are not practical.
本発明の目的は、上記の問題を解決して半導体単結晶基
板上に、臨界温度を始めとする超電導特性が優れた複合
酸化物超電導体薄膜層を有する半導体基板を提供するこ
とにある。An object of the present invention is to solve the above problems and provide a semiconductor substrate having a composite oxide superconductor thin film layer having excellent superconducting properties including critical temperature on a semiconductor single crystal substrate.
課題を解決するための手段
本発明に従うと、GaAs単結晶上に形成されている1
r02 またはMgOからなるバッファ層を具備する基
板上に、複合酸化物超電導体よりなる薄膜層が形成され
ていることを特徴とする超電導体層を有する半導体基板
が提供される。Means for Solving the Problems According to the present invention, 1 formed on a GaAs single crystal
There is provided a semiconductor substrate having a superconductor layer, characterized in that a thin film layer made of a composite oxide superconductor is formed on a substrate provided with a buffer layer made of r02 or MgO.
本発明においては、上記ZrO□または1.4 g○の
バッファ層の厚さは、50〜1000人であることが好
ましい。また、上記ZrO□またはMgOのバッファ層
の結晶構造は以下のいずれかであることが好ましい。In the present invention, the thickness of the ZrO□ or 1.4 g◯ buffer layer is preferably 50 to 1000 layers. Further, the crystal structure of the ZrO□ or MgO buffer layer is preferably one of the following.
1、ZrO2またはMgOバッファ層がアモルファス構
造であること。1. The ZrO2 or MgO buffer layer has an amorphous structure.
2.2rO□バッファ層が正方晶であって、(100)
面が表面となる配向性を有するか、または(100)面
が表面となる単結晶であること。2.2rO□ buffer layer is tetragonal, (100)
It has an orientation in which the plane is the surface, or it is a single crystal in which the (100) plane is the surface.
3、2rO,バッファ層が立方晶であって、(100)
面が表面となる配向性を有するか、または(100)面
が表面となる単結晶であること。3,2rO, the buffer layer is cubic crystal, (100)
It has an orientation in which the plane is the surface, or it is a single crystal in which the (100) plane is the surface.
4、MgO□バッファ層が(100)面が表面となる配
向性を有するか、または(100)面が表面となる単結
晶であること。4. The MgO□ buffer layer has an orientation with the (100) plane as the surface, or is a single crystal with the (100) plane as the surface.
5、Mg0zバツフア層が(111)面が表面となる配
向性を有するか、または(111)面が表面となる単結
晶であること。5. The Mg0z buffer layer has an orientation with the (111) plane as the surface, or is a single crystal with the (111) plane as the surface.
本発明に従うと、上記超電導体は複合酸化物超電導材料
によって形成されているのが好ましい。According to the invention, the superconductor is preferably formed of a composite oxide superconducting material.
この複合酸化物超電導材料としては公知の任意の材料を
用いることができる。例えば、
式:(αl−XβX)γyO8
(但し、αは周期律表■a族に含まれる元素であり、β
は周期律表IIIa族に含まれる元素であり、γは周期
律表I b、 II b、 llIb、 ■aおよび■
a族から選択される少なくとも一つの元素であり、xS
y、zはそれぞれ0.1 ≦X≦0.9.0.4≦y≦
3.0.1≦2≦5を満たす数である)
で示されるペロブスカイト型または擬似ペロブスカイト
型酸化物を主体としていると考えられる複合酸化物が好
ましい。Any known material can be used as this composite oxide superconducting material. For example, the formula: (αl-XβX)γyO8 (however, α is an element included in group ■a of the periodic table, and β
is an element included in group IIIa of the periodic table, and γ is an element included in group IIIa of the periodic table, and γ is an element included in group IIIa of the periodic table.
at least one element selected from group a, xS
y and z are each 0.1 ≦X≦0.9.0.4≦y≦
A composite oxide that is considered to be mainly composed of a perovskite-type or pseudo-perovskite-type oxide represented by the formula 3.0.1≦2≦5 is preferred.
上記周期律表IIa族元素αとしては、Ba5Sr1C
a、 Mg、 Be等が好ましく、例えば、Ba、 S
rを挙げることができ、この元素αの10〜80%をM
g、 Ca。As the Group IIa element α of the periodic table, Ba5Sr1C
a, Mg, Be, etc. are preferable, for example, Ba, S
r, and 10 to 80% of this element α is M
g, Ca.
Srから選択された1種または2種の元素で置換するこ
ともできる。また上記周期律表■a族元素βはとしては
、Yの他La5ScSCe、 Gd5IloSBr、
Tm。It can also be replaced with one or two elements selected from Sr. In addition to Y, the elements β of Group A of the periodic table include La5ScSCe, Gd5IloSBr,
Tm.
Yb、 Lu等ランタノイド元素が好ましく、例えばY
。Lanthanoid elements such as Yb and Lu are preferred, for example Y
.
la、 loとすることができ、この元素βのうち、1
0〜80%をScまたはランタノイド元素から選択され
た1種または2種の元素で置換することもできる。la, lo, and of this element β, 1
0 to 80% can also be replaced with one or two elements selected from Sc or lanthanide elements.
前記元素γは一般にCuであるが、その一部を周期律表
より; ]lb、l]Jb、I’Vaおよび■a族から
選択される他の元素、例えば、TI、V等で置換するこ
ともできる。具体的には、
Y1Ba2Cu30?−X% La+Ba2CIJ+
Ch−x、。The element γ is generally Cu, but a part of it is replaced with other elements selected from the periodic table; ]lb, l]Jb, I'Va, and ■a group, such as TI, V, etc. You can also do that. Specifically, Y1Ba2Cu30? -X% La+Ba2CIJ+
Ch-x,.
La+5rzCu30+−X% HO+Ba2Cu30
7−x、Nd + Ba2Cu307−X N Sm
I Ba2Cu30 ?−X、1EU1Ba2cu30
q−xSGd+Ba2Cu3Ch−xsDyiBa2C
u30t−xs Br+Ba2Cu30t−xsYb+
Ba2CUs 07−x
(ただしXはQ<x<1を満たす数である)で表される
複合酸化物超電導体が好ましい。La+5rzCu30+-X% HO+Ba2Cu30
7-x, Nd + Ba2Cu307-X N Sm
I Ba2Cu30? -X, 1EU1Ba2cu30
q-xSGd+Ba2Cu3Ch-xsDyiBa2C
u30t-xs Br+Ba2Cu30t-xsYb+
A composite oxide superconductor represented by Ba2CUs 07-x (where X is a number satisfying Q<x<1) is preferable.
また、本発明においては、
式: D L (E I−n、Can) Jurt O
p+*(ここで、DはBiまたはTIであり、EはDが
BiのときはSrであり、DがTIのときはBaであり
、1=4であり、mは6≦m≦10を満たし、nは4≦
n≦8を満たし、p = (31+2m+2n) /
2であり、#は0 <#< 1を満たし、*は一2≦*
≦2を満たす数を表す)
で表される組成の、
B14Sr4Ca4CU6020+* (ただし*は一
2≦*≦+2を満たす数を表す)
BI2Sr2Ca2Cui○lQ+* (ただし*は一
2≦*≦十2を満たす数を表す)
T14Ba4Ca4Cu602Q** (ただし*は一
2≦*≦+2を満たす数を表す)
または
Tl□Ba2Ca2Cu30 + O+* (ただし*
は一2≦*≦+2を満たす数を表す)
等で示される複合酸化物を主とした混合相と考えられる
超電導体を用いることも好ましいが、上記いずれかの複
合酸化物の単相であってもよい。Moreover, in the present invention, the formula: D L (E I-n, Can) Jurt O
p+*(Here, D is Bi or TI, E is Sr when D is Bi, Ba is when D is TI, 1=4, and m is 6≦m≦10. satisfies, n is 4≦
Satisfy n≦8, p = (31+2m+2n) /
2, # satisfies 0 <#< 1, and * satisfies 12≦*
B14Sr4Ca4CU6020+* (where * represents a number that satisfies 12≦*≦+2) BI2Sr2Ca2Cui○lQ+* (where * represents a number that satisfies 12≦*≦12) (Represents a number) T14Ba4Ca4Cu602Q** (However, * represents a number that satisfies -2≦*≦+2) Or Tl□Ba2Ca2Cu30 + O+* (However, *
is a number satisfying -2≦*≦+2) It is also preferable to use a superconductor that is considered to be a mixed phase mainly composed of complex oxides expressed by You can.
上記ZrO□またはMgOバッファ層は、上記GaAs
基板の(100)面上に形成されていることが有利であ
る。The ZrO□ or MgO buffer layer is made of the GaAs
Advantageously, it is formed on the (100) plane of the substrate.
作用
本発明の超電導体層を有する半導体基板は、半導体単結
晶基板上に、ZrO2またはMgOからなるバッファ層
を介して複合酸化物超電導体層が形成されているところ
にその主要な特徴がある。すなわち、本発明の超電導体
層を有する半導体基板は、従来のものと異なり、単に半
導体と複合酸化物超電導体を組み合わせただけでなく、
半導体と複合酸化物超電導体との界面状態を改善するバ
ッファ層を備えている。Function The main feature of the semiconductor substrate having a superconductor layer of the present invention is that a composite oxide superconductor layer is formed on a semiconductor single crystal substrate with a buffer layer made of ZrO2 or MgO interposed therebetween. That is, unlike conventional ones, the semiconductor substrate having a superconductor layer of the present invention is not only a combination of a semiconductor and a composite oxide superconductor;
It includes a buffer layer that improves the interface state between the semiconductor and the composite oxide superconductor.
従来の超電導体層を有する半導体基板は、半導体基板上
に単に複合酸化物超電導体薄膜を形成しただけであった
。そのため、半導体と複合酸化物超電導体との界面状態
は、不安定であり、半導体デバイスとして機能しなかっ
たり、特性が悪いものがほとんどであった。A conventional semiconductor substrate having a superconductor layer is simply a composite oxide superconductor thin film formed on a semiconductor substrate. Therefore, the interface state between the semiconductor and the composite oxide superconductor is unstable, and most devices do not function as a semiconductor device or have poor characteristics.
本発明においては、半導体単結晶上にZrO2またはM
gOからなるバッファ層を設け、さらにその上に複合酸
化物超電導体薄膜を形成しているため、従来のものと比
較して、界面の状態が大幅に改善され、半導体デバイス
としての特性も向上した。In the present invention, ZrO2 or M
By providing a buffer layer made of gO and further forming a composite oxide superconductor thin film on top of it, the interface condition has been significantly improved compared to conventional ones, and the characteristics as a semiconductor device have also been improved. .
本発明において、上記バッファ層を形成するZrO□ま
たはMgOの結晶構造は、以下のいずれかであることが
好ましい。In the present invention, the crystal structure of ZrO□ or MgO forming the buffer layer is preferably one of the following.
1、 ZrCh マタはMgOバッファ層がアモルファ
ス構造であること。1. The MgO buffer layer of ZrCh material has an amorphous structure.
2、ZrO2バッファ層が正方晶であって、(100)
面が表面となる配向性を有するか、または(100)面
が表面となる単結晶であること。2. The ZrO2 buffer layer is tetragonal and (100)
It has an orientation in which the plane is the surface, or it is a single crystal in which the (100) plane is the surface.
3、ZrO□バッファ層が立方晶であって、(100)
面が表面となる配向性を有するか、または(100)面
が表面となる単結晶であること。3. The ZrO□ buffer layer is cubic crystal, (100)
It has an orientation in which the plane is the surface, or it is a single crystal in which the (100) plane is the surface.
4、MgO□バッファ層が(100)面が表面となる配
向性を有するか、または(100)面が表面となる単結
晶であること。4. The MgO□ buffer layer has an orientation with the (100) plane as the surface, or is a single crystal with the (100) plane as the surface.
5、MgO2バッファ層が(111)面が表面となる配
向性を有するか、または(111)面が表面となる単結
晶であること。5. The MgO2 buffer layer has an orientation with the (111) plane as the surface, or is a single crystal with the (111) plane as the surface.
これは、複合酸化物超電導体の結晶性を向上させるため
で、上記の結晶構造のバッファ層上に形成された複合酸
化物超電導体薄膜は、結晶のC軸が基板成膜面に平行に
近い角度で揃う配向性を有するため特定の面方向および
深さ方向の臨界電流密度Jcが向上する。This is to improve the crystallinity of the composite oxide superconductor, and in the composite oxide superconductor thin film formed on the buffer layer with the above crystal structure, the C-axis of the crystal is close to parallel to the substrate deposition surface. Since it has an orientation that is aligned at an angle, the critical current density Jc in a specific surface direction and depth direction is improved.
本発明の超電導体層を有する半導体基板は、配線部を従
来の金属から複合酸化物超電導体に置き換えた半導体集
積回路基板としてのみ使用できるだけでなく、複合酸化
物超電導体の部分にジョセフソン接合を形成した半導体
デバイスあるいは半導体基板と超電導体とを組み合わせ
た超電導トランジスタや熱電子トランジスタのような新
規な半導体素子を形成するためのデバイス用材料として
も用いることができる。The semiconductor substrate having the superconductor layer of the present invention can not only be used as a semiconductor integrated circuit board in which the wiring part is replaced with a composite oxide superconductor from conventional metal, but also can be used as a semiconductor integrated circuit board in which the wiring part is replaced with a composite oxide superconductor. It can also be used as a device material for forming semiconductor devices or new semiconductor elements such as superconducting transistors and thermionic transistors in which a semiconductor substrate and a superconductor are combined.
本発明の超電導体層を有する半導体基板に使用する複合
酸化物超電導体としては、YBCOと称されるY、Ba
2Cu30.−8で代表されるような多層ペロブスカイ
ト結晶構造を有する複合酸化物超電導体、
B14Sr4Ca4Cu60zo+* (ただし*は一
2≦*≦。The composite oxide superconductor used in the semiconductor substrate having a superconductor layer of the present invention includes Y, Ba
2Cu30. A composite oxide superconductor having a multilayer perovskite crystal structure as represented by -8, B14Sr4Ca4Cu60zo+* (where * is 12≦*≦).
+2を満たす数を表す)
で示される複合酸化物超電導体、またはT14Ba4C
a4Cu602o+* (ただし*は一2≦*≦+2を
満たす数を表す)
で示される複合酸化物超電導体等が好ましい。しかしな
がら、本発明で使用される超電導体はこれらに限定され
るものではなく、公知の超電導体の任意のものを使用す
ることが可能である。(represents a number that satisfies +2) or T14Ba4C
A composite oxide superconductor represented by a4Cu602o+* (where * represents a number satisfying -2≦*≦+2) is preferable. However, the superconductor used in the present invention is not limited to these, and any known superconductor can be used.
また、半導体単結晶基板と複合酸化物超電導体の界面の
状態を改善するために設けるZrO2またはMgOバッ
ファ層を形成するには、スパッタリング、イオンブレー
ティング、分子線エピタキシー、CVD (化学的気相
反応法〉等の方法を用いることが好ましく、その膜厚は
、界面の状態を改善するために50Å以上必要であり、
また、半導体と絶縁体との超電導近接効果が起こり得る
ためには、1000Å以下であることが好ましい。In addition, sputtering, ion blasting, molecular beam epitaxy, CVD (chemical vapor phase reaction), etc. can be used to form a ZrO2 or MgO buffer layer to improve the interface between the semiconductor single crystal substrate and the composite oxide superconductor. It is preferable to use a method such as the above method, and the film thickness needs to be 50 Å or more in order to improve the interface condition.
Further, in order to cause a superconducting proximity effect between the semiconductor and the insulator, the thickness is preferably 1000 Å or less.
さらに、本発明の超電導体層を有する半導体基板を作製
するには、ZrO□バッファ層またはMgOバッファ層
を形成した半導体単結晶基板上にスパッタリング、イオ
ンブレーティング、分子線エピタキシー、CVD (化
学的気相反応法)等の蒸着法あるいは蒸着法に類似の方
法で複合酸化物超電導体層を形成するのが好ましい。そ
の際、半導体単結晶の物性を損なわないよう基板温度を
700℃以下で複合酸化物超電導体層を形成させること
が好ましい。Furthermore, in order to fabricate a semiconductor substrate having a superconductor layer of the present invention, sputtering, ion blasting, molecular beam epitaxy, CVD (chemical vapor deposition), etc. It is preferable to form the composite oxide superconductor layer by a vapor deposition method such as a phase reaction method or a method similar to a vapor deposition method. At that time, it is preferable to form the composite oxide superconductor layer at a substrate temperature of 700° C. or lower so as not to impair the physical properties of the semiconductor single crystal.
さらに、上記の2rOzバッファ層またはMgOバッフ
ァ層はGaAs単結晶基板の(100)面に形成するこ
とが好ましい。これは、バッファ層が前記した結晶構造
を採り易いためで、GaAs単結晶基板の上記の面に形
成された上記バッファ層は、前述の本発明において好ま
しい結晶構造を採り易く、また、界面の状態を改善する
のにも有利である。Further, the 2rOz buffer layer or the MgO buffer layer described above is preferably formed on the (100) plane of the GaAs single crystal substrate. This is because the buffer layer can easily adopt the crystal structure described above, and the buffer layer formed on the above-mentioned surface of the GaAs single crystal substrate can easily adopt the crystal structure preferred in the present invention, and the interface condition It is also advantageous for improving
実施例
以下、本発明を実施例により具体的に説明するが、以下
に記載するものは本発明の単なる実施例に過ぎず、以下
の開示により、本発明の範囲が何等制限されないことは
勿論である。EXAMPLES Hereinafter, the present invention will be specifically explained by examples, but the following are merely examples of the present invention, and it goes without saying that the scope of the present invention is not limited in any way by the following disclosure. be.
GaAs単結晶基板上にバッファ層として2rOzを5
00人コートし、バッファ層上に複合酸化物超電導体層
を形成し、本発明の超電導体層を有する半導体基板を作
製した。ZrO□バッファ層は、スパッタリング法によ
り、GaAs単結晶基板の温度300℃で形成した。2rOz was deposited as a buffer layer on a GaAs single crystal substrate.
A composite oxide superconductor layer was formed on the buffer layer to produce a semiconductor substrate having a superconductor layer of the present invention. The ZrO□ buffer layer was formed using a sputtering method at a temperature of 300° C. on a GaAs single crystal substrate.
市販の8izO*粉末、5rCCh粉末、CaCO3粉
末、CuO粉末を 81と、Srと、Caと、Cuの原
子比Bi :Sr :Ca :Cuを1.4: l :
1 :1.5 とした原料粉末を常法に従って焼結し
て作ったBi −3r−Ca−Cu−0複合酸化物、Y
Ba2Cu4. s Ox焼結体粉末およびHOBa2
.2Cu4.70x焼結体粉末をターゲットとして、公
知のマグネトロンスパッタリング法により、上記バッフ
ァ層を形成したGaAs半導体単結晶基板の(100)
面上に複合酸化物超電導体層を形成する。基板とターゲ
ットの位置関係および高周波電力の大きさに特に注意し
、基板温度700℃でスパッタリングを行い、複合酸化
物超電導体層を1000人まで成長させ、試料とする。Commercially available 8izO* powder, 5rCCh powder, CaCO3 powder, and CuO powder were used as 81, and the atomic ratio of Sr, Ca, and Cu was Bi:Sr:Ca:Cu as 1.4:l:
Bi-3r-Ca-Cu-0 composite oxide, Y
Ba2Cu4. s Ox sintered powder and HOBa2
.. (100) of a GaAs semiconductor single crystal substrate on which the buffer layer was formed by a known magnetron sputtering method using 2Cu4.70x sintered body powder as a target.
A composite oxide superconductor layer is formed on the surface. Paying special attention to the positional relationship between the substrate and target and the magnitude of high-frequency power, sputtering is performed at a substrate temperature of 700° C. to grow a composite oxide superconductor layer of up to 1000 layers and use it as a sample.
なお、比較のためバッファ層を形成しないGaAs半導
体単結晶基板の(100)面上に全く等しい条件で複合
酸化物超電導体層を形成した。For comparison, a composite oxide superconductor layer was formed under exactly the same conditions on the (100) plane of a GaAs semiconductor single crystal substrate on which no buffer layer was formed.
上記の本発明の超電導体層を有する半導体基板は、いず
れのものも半導体とバッファ層およびバッファ層と超電
導体層の界面の状態がよく、半導体デバイス材料として
優れた特性を有している。All of the above semiconductor substrates having a superconductor layer of the present invention have good interface conditions between the semiconductor and the buffer layer, and between the buffer layer and the superconductor layer, and have excellent properties as semiconductor device materials.
また、それぞれの試料の超電導体層の超電導臨界温度お
よび77Kにおける臨界電流を以下に示す。Further, the superconducting critical temperature and critical current at 77K of the superconducting layer of each sample are shown below.
以上説明したように、本発明の超電導体層を有する半導
体基板は、半導体デバイス用基板としてたいへん有効で
ある。As explained above, the semiconductor substrate having the superconductor layer of the present invention is very effective as a substrate for semiconductor devices.
発明の効果
本発明により、新規な半導体デバイス材料としてたいへ
ん有効な超電導体層を有する半導体基板が提供される。Effects of the Invention The present invention provides a semiconductor substrate having a superconductor layer that is very effective as a novel semiconductor device material.
本発明により、半導体デバイスの高速化、高密度化がさ
らに推進される。さらに、本発明はジョセフソン累子と
異なり、3端子以上の端子を有する超電導体を利用した
半導体デバイス等に応用が可能である。The present invention further promotes higher speed and higher density of semiconductor devices. Further, unlike the Josephson separator, the present invention can be applied to semiconductor devices using superconductors having three or more terminals.
特許出願人 住友電気工業株式会社Patent applicant: Sumitomo Electric Industries, Ltd.
Claims (1)
MgOからなるバッファ層を具備する基板上に、複合酸
化物超電導体よりなる薄膜層が形成されていることを特
徴とする超電導体層を有する半導体基板。A semiconductor substrate having a superconductor layer, characterized in that a thin film layer made of a composite oxide superconductor is formed on a substrate provided with a buffer layer made of ZrO_2 or MgO formed on a GaAs single crystal.