JPH01268613A - 歯科用印象材 - Google Patents
歯科用印象材Info
- Publication number
- JPH01268613A JPH01268613A JP63096536A JP9653688A JPH01268613A JP H01268613 A JPH01268613 A JP H01268613A JP 63096536 A JP63096536 A JP 63096536A JP 9653688 A JP9653688 A JP 9653688A JP H01268613 A JPH01268613 A JP H01268613A
- Authority
- JP
- Japan
- Prior art keywords
- oil
- impression material
- vinyl acetate
- oral cavity
- impression
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
[産業上の利用分野コ
本発明は歯科用に用いられる印象材に関する。
[従来の技術]
従来、歯科用印象材として、非弾性印象材たる石膏印象
材、亜鉛華ニーシノール印象材、モデリングコンパウン
ド及び弾性印象材たる寒天印象材、アルジネート印象材
、ポリサルファイドラバー印象材、シリコーンラバー印
象材、ポリエーテルラバー印象材が知られている。この
中で主に親水性系の寒天印象材とアルギン酸ナトリウム
、疎水性系のシリコーンラバー印象材が使用されでいる
。そして、この寒天印象材及びシリコーンラバー印象材
はアンダーカットのある印象採得に適当であるとともに
、寒天印象材は、安価でかつ口腔粘膜面に対し親和性を
有する利点を有し、−方、シリコーンラバー印象材は口
腔内組繊細部の再現性の精度が高くかつシャープさを有
すると共に口腔内浸出液による影響がないという利点を
有している。
材、亜鉛華ニーシノール印象材、モデリングコンパウン
ド及び弾性印象材たる寒天印象材、アルジネート印象材
、ポリサルファイドラバー印象材、シリコーンラバー印
象材、ポリエーテルラバー印象材が知られている。この
中で主に親水性系の寒天印象材とアルギン酸ナトリウム
、疎水性系のシリコーンラバー印象材が使用されでいる
。そして、この寒天印象材及びシリコーンラバー印象材
はアンダーカットのある印象採得に適当であるとともに
、寒天印象材は、安価でかつ口腔粘膜面に対し親和性を
有する利点を有し、−方、シリコーンラバー印象材は口
腔内組繊細部の再現性の精度が高くかつシャープさを有
すると共に口腔内浸出液による影響がないという利点を
有している。
し発明が解決しようとする課題]
上記親水性系印象材は、上記利点を有するものの離液現
象を起し、精度が低くシャープさに欠け、口腔内浸出液
により印象寸法に誤差を生じるという問題があり、また
シリコーンラバー印象材は、高価でかつ口腔粘膜面に対
し親和性に欠けるという問題があった。
象を起し、精度が低くシャープさに欠け、口腔内浸出液
により印象寸法に誤差を生じるという問題があり、また
シリコーンラバー印象材は、高価でかつ口腔粘膜面に対
し親和性に欠けるという問題があった。
そこで本発明は、アンダーカットのある印象採得に適し
、口腔粘膜面に対して親和性がアリ、かつシリコーンラ
バー印象材の利点を兼備した印象材を提供することをト
1的とする。
、口腔粘膜面に対して親和性がアリ、かつシリコーンラ
バー印象材の利点を兼備した印象材を提供することをト
1的とする。
[課題を解決するための手段」
本発明は、無毒で弾性強度を有し、かつ軟化温度を自由
に選択できるエチレン−1酢酸ビニル共重合体(以下E
VA樹脂という)の性質に着目してなされたものである
。
に選択できるエチレン−1酢酸ビニル共重合体(以下E
VA樹脂という)の性質に着目してなされたものである
。
E V A fθ1脂単独では未だ軟化温度が高く、少
し高温であっても粘りのある鳥もち状でI。
し高温であっても粘りのある鳥もち状でI。
かないため印象材としては好ましくない9本発明者は鋭
意研究の結果、EVA樹脂に適当量の油を均一に混和混
合することにより、印象採得時の約60℃では容易に流
動し、且つ体温近傍以下では、形状が十分保持でき、さ
らに弾性体として固化する特性を有する印象材として有
効な組成物を見出し□完成させたものである。
意研究の結果、EVA樹脂に適当量の油を均一に混和混
合することにより、印象採得時の約60℃では容易に流
動し、且つ体温近傍以下では、形状が十分保持でき、さ
らに弾性体として固化する特性を有する印象材として有
効な組成物を見出し□完成させたものである。
本発明で得られた組成物は口腔内組織に粘着せず、再現
性に優れ、且つアンターカット部を含む印象ができ常温
における経時変化によって寸法変化がないという特徴を
有する印象材である。
性に優れ、且つアンターカット部を含む印象ができ常温
における経時変化によって寸法変化がないという特徴を
有する印象材である。
すなわち本発明は、エチレン−酢酸ビニル共重合体20
〜80垂量%と油80〜20重量%とからなる印象材で
ある。
〜80垂量%と油80〜20重量%とからなる印象材で
ある。
必要に応じて、これらに更に添加剤を加えても良い。
前記EVAvA脂は、下記の反復構造式[A]と[B]
とを有する共重合体であって、酢酸ビニル含有量が特定
の一種のEVA樹脂を用いてもよく、あるいは酢酸ビニ
ル含有量が異なる複数種のものを組み合せて用いてもよ
い。
とを有する共重合体であって、酢酸ビニル含有量が特定
の一種のEVA樹脂を用いてもよく、あるいは酢酸ビニ
ル含有量が異なる複数種のものを組み合せて用いてもよ
い。
そして酢酸ビニル含有量は20へ・50wtが好ましい
。
。
一+CI、 −CH,−+−(A )
→C1l、 −C1l→−(t3〕
IL
前記油は、綿実油、落花生油、オリーブ油、オレンジ油
、とうもろこし肝油、ひまし油、ごま油、ヤシ油などの
植物性油脂および鯨油、牛脂油、豚脂などの動物性油脂
、および更に。
、とうもろこし肝油、ひまし油、ごま油、ヤシ油などの
植物性油脂および鯨油、牛脂油、豚脂などの動物性油脂
、および更に。
鉱物質油、合成油などが好ましい。
前記添加物は、パラフィン等のワ/クス類、炭酸カルシ
ウム、タルク、ライラストナイト、二酸化ゲイ素、酸化
チタン、珪藻上、珪酸カルシウム、カラス、ガラスピー
ズ、カラスバルーンなどの無機充填材、並びに、プラス
ナック粉末、例えばポリエチレン粉末、スチレンビーズ
、アクリルビーズ、8酸ビニル樹脂などの有機充填材な
どが好ましい。
ウム、タルク、ライラストナイト、二酸化ゲイ素、酸化
チタン、珪藻上、珪酸カルシウム、カラス、ガラスピー
ズ、カラスバルーンなどの無機充填材、並びに、プラス
ナック粉末、例えばポリエチレン粉末、スチレンビーズ
、アクリルビーズ、8酸ビニル樹脂などの有機充填材な
どが好ましい。
もちろんこれらの他に、顔料染料等による着色および賦
香甘味の添加等は適宜行うことができる。
香甘味の添加等は適宜行うことができる。
[実施例]
以下に本発明をより具体的に説明するために実施例を示
すが、本発明の要旨をこえない限りこれらの例に限定さ
れるものではない。
すが、本発明の要旨をこえない限りこれらの例に限定さ
れるものではない。
実施例1〜6を第1表に示す、第1表において、E V
A樹脂(A>は#酸ビニル含有量が28wt%、メル
トフローレートが2Of/10nin、EVA樹脂<8
>は酢酸ビニル含有量が28wt、%、メルトフローレ
ートが7g/10n+in 、 EVAI!A脂(C)
は#酸ビニル含有Iが32wt%、メルトフローレート
が601r/10nin 、 EVA樹脂(D)は酢酸
ビニル含有量が25w t%、メルトフローレートが3
g/10Ilin 、 EVA樹脂(’E)は酢酸ビニ
ル含有量が41wt%、メルトフローレ−1・が60+
r/10m1nである。
A樹脂(A>は#酸ビニル含有量が28wt%、メル
トフローレートが2Of/10nin、EVA樹脂<8
>は酢酸ビニル含有量が28wt、%、メルトフローレ
ートが7g/10n+in 、 EVAI!A脂(C)
は#酸ビニル含有Iが32wt%、メルトフローレート
が601r/10nin 、 EVA樹脂(D)は酢酸
ビニル含有量が25w t%、メルトフローレートが3
g/10Ilin 、 EVA樹脂(’E)は酢酸ビニ
ル含有量が41wt%、メルトフローレ−1・が60+
r/10m1nである。
実施例1〜5の成分をそれぞれ150°Cにて均一に混
合して印象材とし、これを例えばチューブ状容器に充填
して60°Cにて保存する。
合して印象材とし、これを例えばチューブ状容器に充填
して60°Cにて保存する。
使用時にチューブから押し出してトレーに盛り、口腔内
にセットすると2〜3分間で固化する。これに石膏を注
入して型を成型する。
にセットすると2〜3分間で固化する。これに石膏を注
入して型を成型する。
実施例1は、超高粘度の印象材、実施例2は高粘度の印
象材、実施例3は中粘度の印象材、実施例4は低粘度の
印象材、実施例5は無機充填材を添加した低粘度の印象
材の配合例である。
象材、実施例3は中粘度の印象材、実施例4は低粘度の
印象材、実施例5は無機充填材を添加した低粘度の印象
材の配合例である。
これら実施例によって得られた印象・1才は、熱可塑性
、可逆性、弾性及び疎水性であり、寸法精度が良く口腔
粘膜の再現性に対して優れたものであった。
、可逆性、弾性及び疎水性であり、寸法精度が良く口腔
粘膜の再現性に対して優れたものであった。
実施例6は、複印象用絹成物であり、実施例1〜5と同
様に150’Cにて均一に混合して、複模型を成型する
際の印象材として使用する。
様に150’Cにて均一に混合して、複模型を成型する
際の印象材として使用する。
例えば、これを容器内で60〜80°Cに加温し、リン
ク内にセットされた模39!上に流し込み、冷却固化さ
せこれに石膏を注入し、複模型を作製する。実施例1〜
・5の利点を有するとともに、くり返し使用できる特徴
を有するものであった。
ク内にセットされた模39!上に流し込み、冷却固化さ
せこれに石膏を注入し、複模型を作製する。実施例1〜
・5の利点を有するとともに、くり返し使用できる特徴
を有するものであった。
第1表
[発明の効果]
本発明は、次の効果を有する。すなわち従来では使用時
に2液温合や粉と液の混合を必要とする印象材は混合割
′合が不正確であったり練和か不十分であると硬化時間
や寸法精度にばらつきを生じ、取扱いが難しかったが、
本発明の印象材では、例えばチューブから押し出すだけ
で簡単に使用でき熟練した技術を必要としない。また比
較的安価でかつ口腔粘膜面及び石膏に対し親和性を有す
る。また口腔内組1N細部の再現性の精度が高くかつシ
ャープさを有し、口腔内浸出液による影響がない、また
水を含んでいないため経時変化を生じないと共に再使用
可能である。また臭さ、熱さ等によって患者に苦痛を与
えることがなく、オレンジ油、ハツカ油、香料を使用す
ることによって患者に良悪を与えることができる。さら
に印象材と印象材の接着が可能であるため、1回目の印
象が失敗してもその上に印象材を追加して再度印象する
ことができる。
に2液温合や粉と液の混合を必要とする印象材は混合割
′合が不正確であったり練和か不十分であると硬化時間
や寸法精度にばらつきを生じ、取扱いが難しかったが、
本発明の印象材では、例えばチューブから押し出すだけ
で簡単に使用でき熟練した技術を必要としない。また比
較的安価でかつ口腔粘膜面及び石膏に対し親和性を有す
る。また口腔内組1N細部の再現性の精度が高くかつシ
ャープさを有し、口腔内浸出液による影響がない、また
水を含んでいないため経時変化を生じないと共に再使用
可能である。また臭さ、熱さ等によって患者に苦痛を与
えることがなく、オレンジ油、ハツカ油、香料を使用す
ることによって患者に良悪を与えることができる。さら
に印象材と印象材の接着が可能であるため、1回目の印
象が失敗してもその上に印象材を追加して再度印象する
ことができる。
また辺縁等の印像の場合、盛り足し可能であり、辺縁の
みを温水等で温めR能印象を採得できる。またティッシ
ュコンディショナー、弾性裏装剤としても適用可能であ
る。
みを温水等で温めR能印象を採得できる。またティッシ
ュコンディショナー、弾性裏装剤としても適用可能であ
る。
本発明はエチレン−酢酸ビニル共重合体に油を加えてな
り、寒天印象材とシリコーンラバー印象材の利点を兼備
した印象材を提供できる。
り、寒天印象材とシリコーンラバー印象材の利点を兼備
した印象材を提供できる。
特 許 出 願 人 有限会社シンセイ、デンタル
、ラボラトリ−
、ラボラトリ−
Claims (1)
- エチレン−酢酸ビニル共重合体20〜80重量%と油8
0〜20重量%とからなる歯科用印象材。