JP7507627B2 - Laminate for packaging bag and packaging bag - Google Patents

Laminate for packaging bag and packaging bag Download PDF

Info

Publication number
JP7507627B2
JP7507627B2 JP2020126412A JP2020126412A JP7507627B2 JP 7507627 B2 JP7507627 B2 JP 7507627B2 JP 2020126412 A JP2020126412 A JP 2020126412A JP 2020126412 A JP2020126412 A JP 2020126412A JP 7507627 B2 JP7507627 B2 JP 7507627B2
Authority
JP
Japan
Prior art keywords
polyethylene
layer
film
stretched
laminate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2020126412A
Other languages
Japanese (ja)
Other versions
JP2022023461A (en
Inventor
弘嗣 桑原
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fujimori Kogyo Co Ltd
Original Assignee
Fujimori Kogyo Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fujimori Kogyo Co Ltd filed Critical Fujimori Kogyo Co Ltd
Priority to JP2020126412A priority Critical patent/JP7507627B2/en
Publication of JP2022023461A publication Critical patent/JP2022023461A/en
Application granted granted Critical
Publication of JP7507627B2 publication Critical patent/JP7507627B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Description

本発明は、可撓性の包装袋として用いられる積層体に関し、特にバリア性を有する包装袋に適した積層体に関する。 The present invention relates to a laminate for use as a flexible packaging bag, and in particular to a laminate suitable for a packaging bag having barrier properties.

一般に、この種の包装袋は、ポリエチレン（ＰＥ）、ポリプロピレン（ＰＰ）、ポリエチレンテレフタレート（ＰＥＴ）などの複数種の樹脂層を積層した積層体によって構成されている。さらに、アルミ箔などの金属層が設けられることで空気バリア性が付与された積層体も知られている。 Generally, this type of packaging bag is made of a laminate of multiple resin layers, such as polyethylene (PE), polypropylene (PP), and polyethylene terephthalate (PET). Furthermore, laminates that have air barrier properties due to the inclusion of a metal layer, such as aluminum foil, are also known.

特開２００５－２７０３９６号公報JP 2005-270396 A

異種材質フィルムの積層体からなる袋は、ゴミとして回収された後に材質ごとに分別するのが容易でなく、リサイクル性が低い。積層体をポリエチレンだけで構成すれば、リサイクルが容易になるが、金属層を無くすとバリア性が失われる。
本発明は、かかる事情に鑑み、可撓性の包装袋用の積層体のリサイクル性とバリア性を両立させることを目的とする。 Bags made of laminates of films of different materials have low recyclability because it is difficult to separate the materials after they are collected as garbage. If the laminate is made of polyethylene only, recycling becomes easier, but removing the metal layer will result in a loss of barrier properties.
In view of the above circumstances, an object of the present invention is to provide a laminate for flexible packaging bags that achieves both recyclability and barrier properties.

前記課題を解決するため、本発明は、可撓性の包装袋として用いられる積層体であって、
１又は複数の延伸ポリエチレン系フィルムを含む基材層と、
前記基材層に積層されたシーラント層と、
を備え、前記シーラント層が、直鎖状低密度ポリエチレンを含む無延伸ポリエチレン系フィルムと、前記無延伸ポリエチレン系フィルムにおけるシール面以外の面に被膜された金属蒸着層とを含むことを特徴とする。 In order to solve the above problems, the present invention provides a laminate for use as a flexible packaging bag, comprising:
A substrate layer comprising one or more stretched polyethylene-based films;
A sealant layer laminated on the base layer;
The sealant layer comprises a non-oriented polyethylene-based film containing a linear low-density polyethylene, and a metal vapor-deposited layer coated on a surface of the non-oriented polyethylene-based film other than the sealing surface.

好ましくは、前記基材層が、積層された複数の延伸ポリエチレン系フィルムを含み、各延伸ポリエチレン系フィルムが、高密度ポリエチレン、中密度ポリエチレン、直鎖状低密度ポリエチレンの少なくとも１つを含む。 Preferably, the substrate layer includes a plurality of laminated stretched polyethylene-based films, each of which includes at least one of high-density polyethylene, medium-density polyethylene, and linear low-density polyethylene.

好ましくは、前記シーラント層が、前記シール面を有する第１無延伸ポリエチレン系フィルムと、前記第１無延伸ポリエチレン系フィルムにおける前記シール面とは反対側の前記基材層を向く面に層内接着層を介して積層された第２無延伸ポリエチレン系フィルムとを備え、
前記第１、第２無延伸ポリエチレン系フィルムが、それぞれ直鎖状低密度ポリエチレンを含み、
前記第１、第２無延伸ポリエチレン系フィルムの何れかにおけるシール面以外の面に前記金属蒸着層が被膜されている。 Preferably, the sealant layer comprises a first unstretched polyethylene-based film having the sealing surface, and a second unstretched polyethylene-based film laminated via an intralayer adhesive layer on a surface of the first unstretched polyethylene-based film facing the base layer on the opposite side to the sealing surface,
The first and second unstretched polyethylene films each contain a linear low-density polyethylene,
The metal vapor deposition layer is formed on the surface of either the first or second unstretched polyethylene film other than the sealing surface.

好ましくは、前記基材層と前記シーラント層との間に層間接着層が介在されている。 Preferably, an interlayer adhesive layer is interposed between the base layer and the sealant layer.

好ましくは、前記基材層が、第１の延伸ポリエチレン系フィルムと、前記第１の延伸ポリエチレン系フィルムと前記シーラント層との間に介在された第２の延伸ポリエチレン系フィルムとを含み、これら第１、第２の延伸ポリエチレン系フィルムがそれぞれ２以上のポリエチレン層を含み、
前記第１の延伸ポリエチレン系フィルムにおける、第２の延伸ポリエチレン系フィルム側とは反対側の外面層を構成するポリエチレン層が、高密度ポリエチレンを含み、かつ前記外面層の第２の延伸ポリエチレン系フィルム側に積層されたポリエチレン層が、中密度ポリエチレン層又は直鎖状低密度ポリエチレンを含む。
融点が高く耐熱性に優れた高密度ポリエチレンによって外面層を構成しておくことで、製袋工程におけるシールバーの高熱によって、基材層が劣化したり損傷したりするのを防止できる。 Preferably, the base layer includes a first stretched polyethylene-based film and a second stretched polyethylene-based film interposed between the first stretched polyethylene-based film and the sealant layer, and each of the first and second stretched polyethylene-based films includes two or more polyethylene layers;
In the first stretched polyethylene-based film, the polyethylene layer constituting the outer surface layer on the side opposite to the second stretched polyethylene-based film side contains high-density polyethylene, and the polyethylene layer laminated on the second stretched polyethylene-based film side of the outer surface layer contains a medium-density polyethylene layer or a linear low-density polyethylene.
By constructing the outer surface layer from high-density polyethylene, which has a high melting point and excellent heat resistance, it is possible to prevent the base material layer from being deteriorated or damaged by the high heat of the sealing bar during the bag making process.

好ましくは、前記第２の延伸ポリエチレン系フィルムにおける、前記シーラント層と対面する内面層を構成するポリエチレン層が、高密度ポリエチレンを含み、かつ前記内面層の第１の延伸ポリエチレン側に積層されたポリエチレン層が、中密度ポリエチレン層又は直鎖状低密度ポリエチレンを含み、
前記内面層と前記シーラント層との間に、低密度ポリエチレン又は直鎖状低密度ポリエチレンの薄膜からなる層間接着層が介在されている。
融点が高く耐熱性に優れた高密度ポリエチレンによって内面層を構成しておくことで、基材層とシーラント層とのラミネート成形時に、溶融された層間接着層の熱によって、第２ポリエチレンフィルムが劣化したり損傷したりするのを防止できる。 Preferably, in the second stretched polyethylene film, the polyethylene layer constituting the inner surface layer facing the sealant layer contains high density polyethylene, and the polyethylene layer laminated on the first stretched polyethylene side of the inner surface layer contains a medium density polyethylene layer or a linear low density polyethylene,
Between the inner surface layer and the sealant layer is interposed an interlayer adhesive layer made of a thin film of low density polyethylene or linear low density polyethylene.
By constructing the inner surface layer from high-density polyethylene, which has a high melting point and excellent heat resistance, it is possible to prevent the second polyethylene film from being deteriorated or damaged by the heat of the molten interlayer adhesive layer during lamination molding of the base material layer and the sealant layer.

好ましくは、前記第１、第２の延伸ポリエチレン系フィルムにおける互いに対向するポリエチレン層が、高密度ポリエチレンを含み、
前記第１、第２の延伸ポリエチレン系フィルムどうしの間に、低密度ポリエチレン又は直鎖状低密度ポリエチレンの薄膜からなる層内接着層が介在されている。
これによって、第１、第２の延伸ポリエチレン系フィルムどうしのラミネート成形時に、溶融された層内接着層の熱によって、第１及び第２の延伸ポリエチレン系フィルムフィルムが劣化したり損傷したりするのを防止できる。 Preferably, the opposing polyethylene layers in the first and second stretched polyethylene-based films contain high density polyethylene,
Between the first and second stretched polyethylene films, an intralayer adhesive layer made of a thin film of low density polyethylene or linear low density polyethylene is interposed.
This makes it possible to prevent the first and second stretched polyethylene films from being deteriorated or damaged by the heat of the molten intralayer adhesive layer when laminating the first and second stretched polyethylene films together.

好ましくは、前記積層体を構成するポリエチレンの少なくとも一部が、植物由来ポリエチレン又はリサイクルポリエチレンである。これによって、環境負荷を軽減できる。 Preferably, at least a portion of the polyethylene constituting the laminate is plant-derived polyethylene or recycled polyethylene. This reduces the environmental impact.

好ましくは、前記基材層に印刷層が設けられている。
また、本発明は、前記の積層体からなる包装袋を特徴とする。 Preferably, a print layer is provided on the base layer.
The present invention also features a packaging bag made of the above laminate.

本発明によれば、可撓性の包装袋用の積層体のリサイクル性とバリア性を両立させることができる。 According to the present invention, it is possible to achieve both recyclability and barrier properties in a laminate for flexible packaging bags.

図１は、本発明の第１実施形態に係る積層体からなる包装袋の斜視図である。FIG. 1 is a perspective view of a packaging bag made of a laminate according to a first embodiment of the present invention. 図２（ａ）は、前記積層体の拡大断面図である。図２（ｂ）は、図１の円部１１ｂにおける拡大断面図である。2(a) is an enlarged cross-sectional view of the laminate, and FIG. 2(b) is an enlarged cross-sectional view of the circular portion 11b in FIG. 図３は、前記包装袋の製造方法の一例を示すフロー図である。FIG. 3 is a flow diagram showing an example of a method for producing the packaging bag. 図４は、本発明の第２実施形態に係る積層体の断面図である。FIG. 4 is a cross-sectional view of a laminate according to a second embodiment of the present invention. 図５は、本発明の第３実施形態に係る積層体の断面図である。FIG. 5 is a cross-sectional view of a laminate according to a third embodiment of the present invention. 図６は、本発明の第４実施形態に係る積層体の断面図である。FIG. 6 is a cross-sectional view of a laminate according to a fourth embodiment of the present invention. 図７は、本発明の第５実施形態に係る積層体の断面図である。FIG. 7 is a cross-sectional view of a laminate according to a fifth embodiment of the present invention. 図８は、本発明の第６実施形態に係る積層体の断面図である。FIG. 8 is a cross-sectional view of a laminate according to a sixth embodiment of the present invention.

以下、本発明の実施形態を図面にしたがって説明する。
＜第１実施形態（図１～図３）＞
図１は、自立袋からなる包装袋１を示したものである。包装袋１は、一対の胴部フィルム２と、底フィルム３を含み、可撓性及び自立性を有している。胴部フィルム２及び底フィルム３は、積層体１０によって構成されている。 Hereinafter, an embodiment of the present invention will be described with reference to the drawings.
First embodiment (FIGS. 1 to 3)
1 shows a packaging bag 1 which is a self-supporting bag. The packaging bag 1 includes a pair of body films 2 and a bottom film 3, and has flexibility and self-supporting properties. The body film 2 and the bottom film 3 are formed of a laminate 10.

図２（ａ）に示すように、積層体１０は、基材層１１と、層間接着層１６と、シーラント層２０を含む。基材層１１は、延伸ポリエチレン系フィルム１２と、印刷層１３を含む。延伸ポリエチレン系フィルム１２は、好ましくは二軸延伸されているが、一軸延伸でもよい。一軸延伸の場合、その延伸方向は、包装袋１（自立袋）の高さ方向（図１において上下方向）であることが好ましい。
延伸倍率は好ましくは２～１５倍である。 As shown in Fig. 2(a), the laminate 10 includes a base layer 11, an interlayer adhesive layer 16, and a sealant layer 20. The base layer 11 includes a stretched polyethylene film 12 and a printed layer 13. The stretched polyethylene film 12 is preferably biaxially stretched, but may be uniaxially stretched. In the case of uniaxial stretching, the stretching direction is preferably the height direction of the packaging bag 1 (self-supporting bag) (the vertical direction in Fig. 1).
The stretching ratio is preferably 2 to 15 times.

延伸ポリエチレン系フィルム１２ひいては基材層１１は、高密度ポリエチレン（ＨＤＰＥ）、中密度ポリエチレン（ＭＤＰＥ）、直鎖状低密度ポリエチレン（ＬＬＤＰＥ）のうち少なくとも１つを主成分として含み、これらポリエチレンのうち２種以上の混合物であってもよい。
「主成分として含む」とは、その成分がフィルムの少なくとも５０ｗｔ％以上を占めることを言い、好ましくは９０ｗｔ％以上、より好ましくは９９ｗｔ％以上を占めることを言う。
高密度ポリエチレン（ＨＤＰＥ）は、密度０．９４１ｇ／ｍ３～０．９７０ｇ／ｍ３程度のポリエチレンを言う。
中密度ポリエチレン（ＭＤＰＥ）は、密度が高密度ポリエチレンの密度範囲より小さく直鎖状低密度ポリエチレン（ＬＬＤＰＥ）の密度範囲より大きいポリエチレンを言い、具体的には密度０．９２６ｇ／ｍ３～０．９４０ｇ／ｍ３程度のポリエチレンを言う。
直鎖状低密度ポリエチレン（ＬＬＤＰＥ）の密度範囲は、０．９１１ｇ／ｍ３～０．９２５ｇ／ｍ３程度である。 The stretched polyethylene film 12, and therefore the base layer 11, contain at least one of high density polyethylene (HDPE), medium density polyethylene (MDPE), and linear low density polyethylene (LLDPE) as a main component, and may be a mixture of two or more of these polyethylenes.
The phrase "contains as a main component" means that the component occupies at least 50 wt % or more of the film, preferably 90 wt % or more, and more preferably 99 wt % or more.
High density polyethylene (HDPE) refers to polyethylene with a density of approximately 0.941 g/m 3 to 0.970 g/m 3 .
Medium density polyethylene (MDPE) refers to polyethylene whose density is lower than the density range of high density polyethylene and higher than the density range of linear low density polyethylene (LLDPE), and specifically refers to polyethylene with a density of about 0.926 g/m 3 to 0.940 g/m 3 .
The density range of linear low density polyethylene (LLDPE) is approximately 0.911 g/m 3 to 0.925 g/m 3 .

延伸ポリエチレン系フィルム１２には、主成分のポリエチレンの他、必要に応じて酸化防止剤、スリップ剤等の少量の添加剤が添加されていてもよく、微量の不可避的不純物が含まれていてもよい。
延伸ポリエチレン系フィルム１２を構成するポリエチレンの少なくとも一部は、植物から生成したエチレンを重合させてなる植物由来ポリエチレンであることが好ましい。
基材層１１の厚みは、２０μｍ～１００μｍ程度であるが、これに限定されるものではない。 In addition to the main component polyethylene, the stretched polyethylene film 12 may contain small amounts of additives such as antioxidants and slip agents as necessary, and may also contain trace amounts of unavoidable impurities.
At least a portion of the polyethylene constituting the stretched polyethylene film 12 is preferably plant-derived polyethylene obtained by polymerizing ethylene produced from plants.
The thickness of the base layer 11 is about 20 μm to 100 μm, but is not limited to this.

延伸ポリエチレン系フィルム１２の片面の所定領域には、印刷層１３が設けられている。印刷層１３には、画像、絵柄、商品名、ロゴマーク、商品説明などが表されている。印刷層１３は、延伸ポリエチレン系フィルム１２における外側面（シーラント層とは反対側の面）に設けられているが、延伸ポリエチレン系フィルム１２における内側面（シーラント層と対面する面）に設けられていてもよい。 A printed layer 13 is provided in a predetermined area on one side of the stretched polyethylene film 12. The printed layer 13 displays an image, a design, a product name, a logo mark, a product description, etc. The printed layer 13 is provided on the outer surface of the stretched polyethylene film 12 (the surface opposite the sealant layer), but may also be provided on the inner surface of the stretched polyethylene film 12 (the surface facing the sealant layer).

図２（ａ）に示すように、基材層１１の内側面（同図において下面）に層間接着層１６を介してシーラント層２０が積層されている。層間接着層１６は、好ましくは低密度ポリエチレン（ＬＤＰＥ）、直鎖状低密度ポリエチレン（ＬＬＤＰＥ）等のポリエチレンの薄膜で構成されているが、これに限らず、溶剤型や無溶剤型などの一般的な樹脂接着剤を用いてもよい。層間接着層１６の厚みは、例えば１０μｍ～３０μｍ程度であるが、これに限定されるものではない。 As shown in FIG. 2(a), a sealant layer 20 is laminated on the inner surface (the lower surface in the figure) of the base layer 11 via an interlayer adhesive layer 16. The interlayer adhesive layer 16 is preferably composed of a thin film of polyethylene such as low-density polyethylene (LDPE) or linear low-density polyethylene (LLDPE), but is not limited thereto and may be a general resin adhesive such as a solvent-based or solventless type. The thickness of the interlayer adhesive layer 16 is, for example, about 10 μm to 30 μm, but is not limited thereto.

シーラント層２０は、無延伸ポリエチレン系フィルム２１と、金属蒸着層２２を含む。無延伸ポリエチレン系フィルム２１は、好ましくは直鎖状低密度ポリエチレン（ＬＬＤＰＥ）を主成分として含む。
無延伸ポリエチレン系フィルム２１には、必要に応じて酸化防止剤、スリップ剤等の少量の添加剤が添加されていてもよく、微量の不可避的不純物が含まれていてもよい。
無延伸ポリエチレン系フィルム２１の厚み（実質的にシーラント層２０の厚み）は、５０μｍ～２００μｍ程度であるが、これに限定されるものではない。 The sealant layer 20 includes a non-oriented polyethylene film 21 and a metal vapor deposition layer 22. The non-oriented polyethylene film 21 preferably contains linear low density polyethylene (LLDPE) as a main component.
The unstretched polyethylene film 21 may contain small amounts of additives such as antioxidants and slip agents as necessary, and may also contain trace amounts of unavoidable impurities.
The thickness of the unstretched polyethylene film 21 (substantially the thickness of the sealant layer 20) is about 50 μm to 200 μm, but is not limited to this.

無延伸ポリエチレン系フィルム２１を構成するポリエチレンの少なくとも一部は、植物から生成したエチレンを重合させてなる植物由来ポリエチレンであることが好ましい。ひいては、積層体１０を構成するポリエチレンの少なくとも一部は、植物由来ポリエチレンであることが好ましい。 At least a portion of the polyethylene constituting the unstretched polyethylene film 21 is preferably plant-derived polyethylene obtained by polymerizing ethylene produced from plants. In addition, at least a portion of the polyethylene constituting the laminate 10 is preferably plant-derived polyethylene.

あるいは、積層体１０を構成するポリエチレンの少なくとも一部が、ポリエチレン製品をリサイクルしたリサイクルポリエチレンであってもよい。リサイクルポリエチレンは、メカニカルリサイクルされたポリエチレンでもよく、ケミカルリサイクルされたポリエチレンでもよい。 Alternatively, at least a portion of the polyethylene constituting the laminate 10 may be recycled polyethylene obtained by recycling polyethylene products. The recycled polyethylene may be mechanically recycled polyethylene or chemically recycled polyethylene.

無延伸ポリエチレン系フィルム２１における基材層１１とは反対側（図２（ａ）において下側）の面は、他の積層体１０と接合されるシール面２１ａとなっている（図２（ｂ）参照）。
無延伸ポリエチレン系フィルム２１における基材層１１を向く面（シール面２１ａ以外の面）には、金属蒸着層２２が被膜されている。金属蒸着層２２は、アルミニウムなどの金属によって構成されている。金属蒸着層２２の厚みは、１０ｎｍ～１００ｎｍ程度であり、無延伸ポリエチレン系フィルム２１の厚みに対して無視できるほど小さい。
図２（ａ）においては、金属蒸着層２２の厚みが誇張されている。 The surface of the unstretched polyethylene film 21 opposite the base layer 11 (the lower side in FIG. 2(a)) serves as a seal surface 21a to be joined to another laminate 10 (see FIG. 2(b)).
The surface of the unstretched polyethylene film 21 facing the base layer 11 (the surface other than the sealing surface 21a) is coated with a metal vapor deposition layer 22. The metal vapor deposition layer 22 is made of a metal such as aluminum. The thickness of the metal vapor deposition layer 22 is about 10 nm to 100 nm, which is negligibly small compared to the thickness of the unstretched polyethylene film 21.
In FIG. 2(a), the thickness of the metal deposition layer 22 is exaggerated.

図２（ｂ）に示すように、包装袋１においては、一対の胴部フィルム２どうしが重ねられている。各胴部フィルム２の基材層１１は外面側へ向けられ、シーラント層２０は内面側へ向けられている。これら胴部フィルム２の左右の縁部におけるシーラント層２０どうしが融着されている。また、胴部フィルム２の底側の縁部及び底部フィルム３の周縁部どうしが融着されている（図１参照）。
なお、図２（ｂ）において、各層１１，２０の厚みは幅に対して誇張されている。 As shown in Fig. 2(b), in the packaging bag 1, a pair of body films 2 are overlapped. The base material layer 11 of each body film 2 faces the outer surface side, and the sealant layer 20 faces the inner surface side. The sealant layers 20 at the left and right edges of these body films 2 are fused to each other. In addition, the bottom edge of the body film 2 and the peripheral edge of the bottom film 3 are fused to each other (see Fig. 1).
In FIG. 2(b), the thickness of each layer 11, 20 is exaggerated relative to its width.

図３に例示するように、積層体１０は、次のようにして製造される。
延伸ポリエチレン系フィルム１２が押出及び延伸成形される。延伸ポリエチレン系フィルム１２の所定領域には印刷層１３が形成される。なお、印刷層１３が延伸ポリエチレン系フィルム１２の外側面に設けられている場合は、無延伸ポリエチレン系フィルム２１とのラミネート後に印刷を行ってもよい。 As shown in FIG. 3, the laminate 10 is manufactured as follows.
The stretched polyethylene film 12 is extruded and stretched. A printed layer 13 is formed in a predetermined region of the stretched polyethylene film 12. When the printed layer 13 is provided on the outer surface of the stretched polyethylene film 12, printing may be performed after lamination with the unstretched polyethylene film 21.

別途、無延伸ポリエチレン系フィルム２１が押出成形される。該無延伸ポリエチレン系フィルム２１に金属蒸着層２２が蒸着される。蒸着工程は、押出成形後、ロール状態に巻かれる前の成形ライン上で行ってもよく、押出成形されて一旦ロール状態にされた後、蒸着専用ラインに移して行ってもよい。延伸ポリエチレン系フィルム１２ではなく、無延伸ポリエチレン系フィルム２１に金属蒸着層２２に形成することで、延伸ポリエチレン系フィルム１２への印刷工程においては、金属蒸着層２２を気にすることなく、フィルム１２の送り等を厳密に制御して印刷ピッチを管理することができ、印刷ずれを確実に防止できる。 Separately, a non-stretched polyethylene film 21 is extruded. A metal vapor deposition layer 22 is vapor-deposited on the non-stretched polyethylene film 21. The vapor deposition process may be performed on the molding line before the film is wound into a roll after extrusion, or may be performed on a line dedicated to vapor deposition after the film is extruded and rolled. By forming the metal vapor deposition layer 22 on the non-stretched polyethylene film 21 instead of the stretched polyethylene film 12, the printing pitch can be managed by strictly controlling the feeding of the film 12 without worrying about the metal vapor deposition layer 22 in the printing process on the stretched polyethylene film 12, and printing deviations can be reliably prevented.

作製された連続フィルム状の基材層１１及びシーラント層２０の原反が、ラミネート装置にセットされて繰り出されるとともに、両層１１，２０の間に層間接着層１６となるポリエチレンが溶融状態で押し出されてサンドイッチされる。これによって、基材層１１及びシーラント層２０が貼り合わされる。このようにして、長尺連続シート状の積層体１０の原反がラミネート成形される。
前記積層体１０が製袋機にセットされ、製袋機によって積層体１０から包装袋１が作製される。 The raw rolls of the continuous film-like base material layer 11 and sealant layer 20 thus produced are set in a laminating device and fed out, and polyethylene that will become the interlayer adhesive layer 16 is extruded in a molten state between the two layers 11, 20 to sandwich them together, thereby bonding the base material layer 11 and the sealant layer 20 together. In this manner, the raw rolls of the long continuous sheet-like laminate 10 are laminated and formed.
The laminate 10 is set in a bag making machine, and a packaging bag 1 is made from the laminate 10 by the bag making machine.

積層体１０からなる包装袋１によれば、積層体１０に金属蒸着層２２が設けられているために、ガスの透過、漏洩、侵入を阻止でき、ガス気バリア性を確保できる。
加えて、積層体１０の略全体がポリエチレンの単一素材によって構成されているために、リサイクルが容易である。積層体１０は、ポリエチレンのほか、金属蒸着層２２をも含んでいるが、金属蒸着層２２は厚みがナノメートルオーダーで極めて薄く、ポリエチレンと比べて極めて少量であるから、リサイクル性が損なわれることはほとんどない。
ちなみに、アルミ箔をバリア層として用いた場合、アルミ箔の厚みはミクロンメートルオーダー（例えば５～１５μｍ程度）であるため単一素材性が劣る。
好ましくは、積層体１０を構成するポリエチレンを植物由来としたり、リサイクルポリエチレンを用いたりすることによって環境負荷を軽減できる。 According to the packaging bag 1 made of the laminate 10, since the laminate 10 is provided with the metal vapor deposition layer 22, gas permeation, leakage, and intrusion can be prevented, and gas barrier properties can be ensured.
In addition, since the laminate 10 is almost entirely made of a single material, polyethylene, it is easy to recycle. The laminate 10 includes the metal vapor deposition layer 22 in addition to polyethylene, but the metal vapor deposition layer 22 is extremely thin, on the order of nanometers, and the amount of the metal vapor deposition layer 22 is extremely small compared to polyethylene, so recyclability is hardly impaired.
Incidentally, when aluminum foil is used as a barrier layer, the thickness of the aluminum foil is on the order of micrometers (for example, about 5 to 15 μm), and therefore the properties of a single material are inferior.
Preferably, the polyethylene constituting the laminate 10 is derived from plants or recycled polyethylene is used, thereby reducing the environmental impact.

次に、本発明の他の実施形態を説明する。以下の実施形態において、既述の形態と重複する構成に関しては、図面に同一符号を付して説明を省略する。
＜第２実施形態（図４）＞
図４に示すように、第２実施形態の積層体１０Ｂにおいては、基材層１１が２つ（複数）の延伸ポリエチレン系フィルム１２Ａ，１２Ｂの積層構造になっている。好ましくは、延伸ポリエチレン系フィルム１２Ａ，１２Ｂは、共押出によって成形されている。
延伸ポリエチレン系フィルム１２Ａ，１２Ｂを互いに別々に押出成形した後、接着層を介して貼り合わせてもよい。 Next, another embodiment of the present invention will be described. In the following embodiment, the same reference numerals are given to the same components as those in the above-described embodiment, and the description thereof will be omitted.
Second embodiment (FIG. 4)
As shown in Fig. 4, in the laminate 10B of the second embodiment, the base layer 11 has a laminate structure of two (a plurality of) stretched polyethylene-based films 12A and 12B. Preferably, the stretched polyethylene-based films 12A and 12B are formed by coextrusion.
The stretched polyethylene films 12A and 12B may be extruded separately from each other and then bonded together via an adhesive layer.

各延伸ポリエチレン系フィルム１２Ａ，１２Ｂは、高密度ポリエチレン（ＨＤＰＥ）、中密度ポリエチレン（ＭＤＰＥ）、直鎖状低密度ポリエチレン（ＬＬＤＰＥ）のうち少なくとも１つを主成分として含み、これらポリエチレンのうち２種以上の混合物であってもよい。２つの延伸ポリエチレン系フィルム１２Ａ，１２Ｂが同じ種類又は組成のポリエチレンで構成されていてもよく、異なる種類又は組成のポリエチレンで構成されていてもよい。これらポリエチレンの少なくとも一部は、植物から生成したエチレンを重合させてなる植物由来ポリエチレン又はリサイクルポリエチレンであることが好ましい。 Each of the stretched polyethylene films 12A, 12B contains at least one of high density polyethylene (HDPE), medium density polyethylene (MDPE), and linear low density polyethylene (LLDPE) as a main component, and may be a mixture of two or more of these polyethylenes. The two stretched polyethylene films 12A, 12B may be composed of polyethylene of the same type or composition, or may be composed of polyethylene of different types or compositions. It is preferable that at least a portion of these polyethylenes is plant-derived polyethylene or recycled polyethylene obtained by polymerizing ethylene produced from plants.

外側の延伸ポリエチレン系フィルム１２Ａの外側面（図４において上面）には、印刷層１３が設けられている。
なお、印刷層１３が、内側の延伸ポリエチレン系フィルム１２Ｂのシーラント層２０を向く内側面（図４において下面）に設けられていてもよい。複数の延伸ポリエチレン系フィルム１２を互いに別々に押出成形した後、貼り合わせる場合には、印刷層１３が外側の延伸ポリエチレン系フィルム１２Ａの内側面（図４において下面）に設けられていてもよく、印刷層１３が内側の延伸ポリエチレン系フィルム１２Ｂの外側面（図４において上面）に設けられていてもよい。
延伸ポリエチレン系フィルムの積層数は、２つに限らず３つ以上でもよい。
第２実施形態によれば、積層体１０Ｂの強度を高めることができ、ひいては包装袋１の強度を高めて破袋を防止できる。 A print layer 13 is provided on the outer surface (upper surface in FIG. 4) of the outer stretched polyethylene film 12A.
The printed layer 13 may be provided on the inner surface (lower surface in FIG. 4 ) of the inner stretched polyethylene film 12B facing the sealant layer 20. When a plurality of stretched polyethylene films 12 are extrusion molded separately from one another and then bonded together, the printed layer 13 may be provided on the inner surface (lower surface in FIG. 4 ) of the outer stretched polyethylene film 12A, or the printed layer 13 may be provided on the outer surface (upper surface in FIG. 4 ) of the inner stretched polyethylene film 12B.
The number of layers of the stretched polyethylene film is not limited to two, but may be three or more.
According to the second embodiment, the strength of the laminate 10B can be increased, and the strength of the packaging bag 1 can be increased to prevent the bag from breaking.

＜第３実施形態（図５）＞
図５に示すように、第５実施形態の積層体１０Ｃにおいては、シーラント層２０が、
第１無延伸ポリエチレン系フィルム２３と、第２無延伸ポリエチレン系フィルム２４とを備えている。基材層１１側（図５において上側）の第１無延伸ポリエチレン系フィルム２３は、無延伸の直鎖状低密度ポリエチレンを主成分として含む。第１無延伸ポリエチレン系フィルム２３の内側面（図５において下面）は、他の積層体と融着されるシール面２３ａとなっている。 Third embodiment (FIG. 5)
As shown in FIG. 5, in the laminate 10C of the fifth embodiment, the sealant layer 20 is
The laminate includes a first unstretched polyethylene film 23 and a second unstretched polyethylene film 24. The first unstretched polyethylene film 23 on the base layer 11 side (upper side in FIG. 5 ) contains unstretched linear low-density polyethylene as a main component. The inner surface (lower surface in FIG. 5 ) of the first unstretched polyethylene film 23 serves as a seal surface 23a to be fused to other laminates.

第１無延伸ポリエチレン系フィルム２３におけるシール面２３ａとは反対側の面（基材層１１を向く面）には、層内接着層２６を介して、第２無延伸ポリエチレン系フィルム２４が積層されている。層内接着層２６は、好ましくは低密度ポリエチレン（ＬＬＤＰＥ）、直鎖状低密度ポリエチレン（ＬＬＤＰＥ）等のポリエチレンの薄膜で構成されているが、これに限らず、溶剤型や無溶剤型などの一般的な樹脂接着剤を用いてもよい。層内接着層２６の厚みは、例えば１０μｍ～３０μｍ程度であるが、これに限定されるものではない。 A second unstretched polyethylene film 24 is laminated to the surface of the first unstretched polyethylene film 23 opposite the sealing surface 23a (the surface facing the base layer 11) via an intralayer adhesive layer 26. The intralayer adhesive layer 26 is preferably made of a thin film of polyethylene such as low density polyethylene (LLDPE) or linear low density polyethylene (LLDPE), but is not limited thereto and may be a general resin adhesive such as a solvent-based or solventless type. The thickness of the intralayer adhesive layer 26 is, for example, about 10 μm to 30 μm, but is not limited thereto.

第２無延伸ポリエチレン系フィルム２４は、無延伸の直鎖状低密度ポリエチレンを主成分として含む。第２無延伸ポリエチレン系フィルム２４における外側面（シール面２３ａ以外の面）に金属蒸着層２２が被膜されている。
積層体１０Ｃにおけるシーラント２０の全体厚さは、例えば５０μｍ～２００μｍ程度であるが、これに限定されるものではない。
積層体１０Ｃを構成するポリエチレンの少なくとも一部は、植物から生成したエチレンを重合させてなる植物由来ポリエチレン又はリサイクルポリエチレンであることが好ましい。 The second unstretched polyethylene film 24 contains unstretched linear low-density polyethylene as a main component. The second unstretched polyethylene film 24 has an outer surface (a surface other than the sealing surface 23a) coated with a metal vapor deposition layer 22.
The total thickness of the sealant 20 in the laminate 10C is, for example, about 50 μm to 200 μm, but is not limited to this.
At least a portion of the polyethylene constituting the laminate 10C is preferably plant-derived polyethylene obtained by polymerizing ethylene produced from plants, or recycled polyethylene.

シーラント２０の作製時には、第１、第２無延伸ポリエチレン系フィルム２３，２４を別々に押出成形し、第２無延伸ポリエチレン系フィルム２４には金属蒸着層２２を蒸着させた後、２つのフィルム２３，２４を層内接着層２６を介してラミネートする。
第３実施形態によれば、金属蒸着層２２を被膜するフィルム２４の厚みをシーラント２０の全体厚さの数分の１にすることで、フィルム２４をロール状にしたときの１本のロールあたりのフィルム長さを増大できる。したがって、蒸着加工時のロール取り替えなどの段取り回数やロスを減らすことができ、加工コストを低く抑えることができる。
一方、複数のフィルム２３，２４を積層してシーラント層２０全体の厚みを大きくすることで、シール強度を高めたり、シーラント層２０ひいては積層体１０Ｃにコシを付与したりして、包装袋１としての強度を確保することができる。 When producing the sealant 20, the first and second unstretched polyethylene films 23, 24 are extruded separately, a metal vapor deposition layer 22 is vapor-deposited onto the second unstretched polyethylene film 24, and then the two films 23, 24 are laminated together via an intralayer adhesive layer 26.
According to the third embodiment, the thickness of the film 24 that coats the metal deposition layer 22 is set to a fraction of the total thickness of the sealant 20, so that the length of the film 24 per roll can be increased. This makes it possible to reduce the number of setups and losses, such as roll replacement, during deposition processing, and to keep processing costs low.
On the other hand, by stacking multiple films 23, 24 to increase the overall thickness of the sealant layer 20, the sealing strength can be increased and stiffness can be imparted to the sealant layer 20 and ultimately to the laminate 10C, thereby ensuring the strength of the packaging bag 1.

複数の延伸ポリエチレン系フィルムが、それぞれ２～３以上のポリエチレン層を含んでいてもよい。
＜第４実施形態（図６）＞
図６に示すように、第４実施形態の積層体１０Ｄにおいては、外側（第１）の延伸ポリエチレン系フィルム１７が２つのポリエチレン層１７ａ，１７ｂを含む。内側（第２）の延伸ポリエチレン系フィルム１８が２つのポリエチレン層１８ａ，１８ｂを含む。 Each of the multiple stretched polyethylene films may include two or more polyethylene layers.
<Fourth embodiment (FIG. 6)>
6, in the laminate 10D of the fourth embodiment, the outer (first) stretched polyethylene-based film 17 includes two polyethylene layers 17a, 17b. The inner (second) stretched polyethylene-based film 18 includes two polyethylene layers 18a, 18b.

外側の延伸ポリエチレン系フィルム１７において、シーラント層とは反対側（図６の上側）の外面層を構成するポリエチレン層１７ａは、高密度ポリエチレン（ＨＤＰＥ）を含有する。
前記外面層１７ａのシーラント層側に積層されたポリエチレン層１７ｂは、中密度ポリエチレン層（ＭＤＰＥ）又は直鎖状低密度ポリエチレン（ＬＬＤＰＥ）を含有する。 In the outer stretched polyethylene film 17, a polyethylene layer 17a constituting the outer surface layer on the side opposite to the sealant layer (upper side in FIG. 6) contains high density polyethylene (HDPE).
The polyethylene layer 17b laminated on the sealant layer side of the outer layer 17a contains a medium density polyethylene layer (MDPE) or a linear low density polyethylene (LLDPE).

内側の延伸ポリエチレン系フィルム１８において、内面層（シーラント層２０と対面する層）を構成するポリエチレン層１８ｂは、高密度ポリエチレン（ＨＤＰＥ）を含有する。
前記内面層１８ｂのフィルム１７側（シーラント層とは反対側）に積層されたポリエチレン層１８ａは、中密度ポリエチレン層（ＭＤＰＥ）又は直鎖状低密度ポリエチレン（ＬＬＤＰＥ）を含有する。 In the inner stretched polyethylene film 18, the polyethylene layer 18b constituting the inner surface layer (the layer facing the sealant layer 20) contains high density polyethylene (HDPE).
The polyethylene layer 18a laminated on the film 17 side (the side opposite to the sealant layer) of the inner surface layer 18b contains a medium density polyethylene layer (MDPE) or a linear low density polyethylene (LLDPE).

ポリエチレン層１７ｂ，１８ａどうしが、これら間に介在された層内接着層１５Ｄによって接着されている。層内接着層１５Ｄは、例えば溶剤型又は無溶剤型の樹脂接着剤によって構成されている。 The polyethylene layers 17b and 18a are bonded to each other by an intralayer adhesive layer 15D interposed between them. The intralayer adhesive layer 15D is made of, for example, a solvent-based or solventless resin adhesive.

内面層１８ｂひいては基材層１１と、シーラント層２０とは、これらの間に介在された層間接着層１６Ｄによって接着されている。層間接着層１６Ｄは、低密度ポリエチレン（ＬＬＤＰＥ）又は直鎖状低密度ポリエチレン（ＬＬＤＰＥ）等のポリエチレンの薄膜によって構成されている。 The inner surface layer 18b, and thus the base material layer 11, and the sealant layer 20 are bonded together by an interlayer adhesive layer 16D interposed therebetween. The interlayer adhesive layer 16D is made of a thin film of polyethylene such as low-density polyethylene (LLDPE) or linear low-density polyethylene (LLDPE).

第４実施形態において、延伸ポリエチレン系フィルム１７，１８は、それぞれ共押出成形等によって形成され、かつ互いに直交する方向に一軸延伸される。
これらフィルム１７，１８が層内接着層１５Ｄによって接着され、基材層１１が形成される。
該基材層１１とシーラント層２０とが重ねられるとともに、両者間に層内接着層１５Ｅとなるポリエチレンが加熱溶融状態で押し出されてサンドイッチされる。これによって、積層体１０Ｄがラミネート成形される。層間接着層１６Ｄと接する内面層１８ｂを、融点が高く耐熱性に優れたＨＤＰＥによって構成しておくことで、前記ラミネート成形時の熱によって、基材層１１が劣化したり損傷したりするのを防止できる。
続いて、製袋工程においては、シートシール部３３（図３（ｂ））の高熱のシールバーが外面層１７ａに押し当てられる。該外面層１７ａをＨＤＰＥによって構成することで、基材層１１が熱による劣化や損傷を受けるのを防止できる。 In the fourth embodiment, the stretched polyethylene films 17 and 18 are formed by coextrusion or the like, and are uniaxially stretched in directions perpendicular to each other.
These films 17 and 18 are bonded together by the intralayer adhesive layer 15D to form the base material layer 11.
The base material layer 11 and the sealant layer 20 are overlapped, and polyethylene that will become the interlayer adhesive layer 15E is extruded in a heated and molten state and sandwiched between them, thereby forming the laminate 10D. By forming the inner surface layer 18b that contacts the interlayer adhesive layer 16D from HDPE, which has a high melting point and excellent heat resistance, it is possible to prevent the base material layer 11 from being deteriorated or damaged by the heat during the laminate formation.
Next, in the bag making process, a high-temperature seal bar of a sheet seal unit 33 (FIG. 3B) is pressed against the outer layer 17a. By forming the outer layer 17a from HDPE, it is possible to prevent the base layer 11 from being deteriorated or damaged by heat.

＜第５実施形態（図７）＞
図７に示すように、第５実施形態の積層体１０Ｅにおいては、外側（第１）の延伸ポリエチレン系フィルム１７が３つのポリエチレン層１７ｃ，１７ｄ，１７ｅを含む。内側（第２）の延伸ポリエチレン系フィルム１８が２つのポリエチレン層１８ｃ，１８ｄを含む。 Fifth embodiment (FIG. 7)
7, in the laminate 10E of the fifth embodiment, the outer (first) stretched polyethylene film 17 includes three polyethylene layers 17c, 17d, and 17e, and the inner (second) stretched polyethylene film 18 includes two polyethylene layers 18c and 18d.

外側の延伸ポリエチレン系フィルム１７において、シーラント層とは反対側（図７の上側）の外面層を構成するポリエチレン層１７ｃは、高密度ポリエチレン（ＨＤＰＥ）を含有する。
外面層１７ｃのシーラント層側に積層されたポリエチレン層１７ｄは、中密度ポリエチレン層（ＭＤＰＥ）又は直鎖状低密度ポリエチレン（ＬＬＤＰＥ）を含有する。
延伸ポリエチレン系フィルム１８と対面するポリエチレン層１７ｅは、高密度ポリエチレン（ＨＤＰＥ）を含有する。 In the outer stretched polyethylene film 17, the polyethylene layer 17c constituting the outer surface layer on the side opposite to the sealant layer (upper side in FIG. 7) contains high density polyethylene (HDPE).
The polyethylene layer 17d laminated on the sealant layer side of the outer layer 17c contains a medium density polyethylene layer (MDPE) or a linear low density polyethylene (LLDPE).
The polyethylene layer 17e facing the stretched polyethylene film 18 contains high density polyethylene (HDPE).

内側の延伸ポリエチレン系フィルム１８において、延伸ポリエチレン系フィルム１７と対面するポリエチレン層１８ｃは、高密度ポリエチレン（ＨＤＰＥ）を含有する。
シーラント層２０と対面するポリエチレン層１８ｄは、中密度ポリエチレン層（ＭＤＰＥ）又は直鎖状低密度ポリエチレン（ＬＬＤＰＥ）を含有する。 In the inner stretched polyethylene film 18, the polyethylene layer 18c facing the stretched polyethylene film 17 contains high density polyethylene (HDPE).
The polyethylene layer 18d facing the sealant layer 20 comprises a medium density polyethylene layer (MDPE) or a linear low density polyethylene (LLDPE).

したがって、延伸ポリエチレン系フィルム１７，１８における互いに対向するポリエチレン層１７ｅ，１８ｃは、共に高密度ポリエチレン（ＨＤＰＥ）を含有する。
これらポリエチレン層１７ｅ，１８ｃどうし、ひいては延伸ポリエチレン系フィルム１７，１８どうしが、これらの間に介在された層内接着層１５Ｅによって接着されている。層内接着層１５Ｅは、低密度ポリエチレン又は直鎖状低密度ポリエチレンの薄膜によって構成されている。 Therefore, the opposing polyethylene layers 17e, 18c in the stretched polyethylene-based films 17, 18 both contain high density polyethylene (HDPE).
The polyethylene layers 17e, 18c, and in turn the stretched polyethylene films 17, 18 are bonded together by an intralayer adhesive layer 15E interposed therebetween. The intralayer adhesive layer 15E is made of a thin film of low-density polyethylene or linear low-density polyethylene.

第５実施形態において、延伸ポリエチレン系フィルム１７，１８は、それぞれ共押出成形等によって形成され、かつ互いに直交する方向に一軸延伸される。
その後、これらフィルム１７，１８が重ねられるとともに、両フィルム１７，１８の間に層内接着層１５Ｅとなるポリエチレンが溶融状態で押し出されてサンドイッチされる。これによって、基材層１１がラミネート成形される。延伸ポリエチレン系フィルム１７，１８における互いに対向するポリエチレン層１７ｅ，１８ｃを、融点が高く耐熱性に優れたＨＤＰＥによって構成しておくことで、ラミネート成形時の熱によって、フィルム１７，１８が劣化したり損傷したりするのを防止できる。 In the fifth embodiment, the stretched polyethylene films 17 and 18 are formed by coextrusion or the like, and are uniaxially stretched in directions perpendicular to each other.
Thereafter, these films 17, 18 are overlapped, and polyethylene that will become the intralayer adhesive layer 15E is extruded in a molten state between the two films 17, 18 to sandwich them together, thereby forming the laminated base material layer 11. By forming the opposing polyethylene layers 17e, 18c of the stretched polyethylene films 17, 18 from HDPE, which has a high melting point and excellent heat resistance, it is possible to prevent the films 17, 18 from being deteriorated or damaged by the heat during the laminated formation.

積層体１０Ｅの基材層１１とシーラント層２０とは、これらの間に介在された層間接着層１６Ｅを介して接着されている。層間接着層１６Ｅは、たとえば溶剤型又は無溶剤型の樹脂接着剤によって構成されている。
外面層１７ｃを融点が高く耐熱性に優れたＨＤＰＥによって構成しておくことで、製袋工程において基材層１１がシールバーの高熱による劣化や損傷を受けるのを防止できる点は第４実施形態と同様である。 The base material layer 11 and the sealant layer 20 of the laminate 10E are bonded to each other via an interlayer adhesive layer 16E interposed therebetween. The interlayer adhesive layer 16E is made of, for example, a solvent-based or solventless resin adhesive.
As in the fourth embodiment, by making the outer layer 17c from HDPE, which has a high melting point and excellent heat resistance, the base material layer 11 can be prevented from being deteriorated or damaged by the high heat of the sealing bar during the bag making process.

＜第６実施形態（図８）＞
図８に示すように、第６実施形態の積層体１０Ｆは、内側（第２）の延伸ポリエチレン系フィルム１８が３つのポリエチレン層１８ｆ，１８ｇ，１８ｈを含むこと、及び層間接着層１６Ｆの材質において、第５実施形態（図７）の積層体１０Ｅと異なっている。
積層体１０Ｆの延伸ポリエチレン系フィルム１８においては、延伸ポリエチレン系フィルム１７と対面するポリエチレン層１８ｆは、高密度ポリエチレン（ＨＤＰＥ）を含有する。したがって、延伸ポリエチレン系フィルム１７，１８における互いに対向するポリエチレン層１７ｅ，１８ｆは、共に融点が高く耐熱性に優れたＨＤＰＥによって構成されている。これによって、ポリエチレン系フィルム１７，１８どうしのラミネート成形時に、溶融された層内接着層１５Ｆの熱によって、フィルム１７，１８が劣化したり損傷したりするのを防止できる。 Sixth embodiment (FIG. 8)
As shown in Figure 8, the laminate 10F of the sixth embodiment differs from the laminate 10E of the fifth embodiment (Figure 7) in that the inner (second) stretched polyethylene film 18 includes three polyethylene layers 18f, 18g, and 18h, and in the material of the interlayer adhesive layer 16F.
In the stretched polyethylene film 18 of the laminate 10F, the polyethylene layer 18f facing the stretched polyethylene film 17 contains high density polyethylene (HDPE). Therefore, the polyethylene layers 17e, 18f facing each other in the stretched polyethylene films 17, 18 are both made of HDPE, which has a high melting point and excellent heat resistance. This makes it possible to prevent the films 17, 18 from being deteriorated or damaged by the heat of the molten intralayer adhesive layer 15F when the polyethylene films 17, 18 are laminated together.

延伸ポリエチレン系フィルム１８における中間の（後記内面層のシーラント層側とは反対側に積層された）ポリエチレン層１８ｇは、中密度ポリエチレン層（ＭＤＰＥ）又は直鎖状低密度ポリエチレン（ＬＬＤＰＥ）を含有する。
シーラント層２０と対面する内面層を構成するポリエチレン層１８ｈは、高密度ポリエチレン（ＨＤＰＥ）を含有する。これによって、基材層１１とシーラント層２０とのラミネート成形時に、溶融された層間接着層１６Ｆの熱によって、ポリエチレン系フィルム１８が劣化したり損傷したりするのを防止できる。
外面層１７ｃを融点が高く耐熱性に優れたＨＤＰＥによって構成しておくことで、製袋工程において基材層１１がシールバーの高熱による劣化や損傷を受けるのを防止できる点は第４実施形態と同様である。 The intermediate polyethylene layer 18g (laminated on the side opposite to the sealant layer side of the inner layer described below) in the stretched polyethylene film 18 contains a medium density polyethylene layer (MDPE) or a linear low density polyethylene (LLDPE).
The polyethylene layer 18h constituting the inner surface layer facing the sealant layer 20 contains high density polyethylene (HDPE). This makes it possible to prevent the polyethylene-based film 18 from being deteriorated or damaged by the heat of the molten interlayer adhesive layer 16F during lamination molding of the base material layer 11 and the sealant layer 20.
As in the fourth embodiment, by making the outer layer 17c from HDPE, which has a high melting point and excellent heat resistance, the base material layer 11 can be prevented from being deteriorated or damaged by the high heat of the sealing bar during the bag making process.

本発明は、前記実施形態に限定されるものではなく、種々の改変をなすことができる。
例えば、金属蒸着層２２は、シーラント層２０の無延伸ポリエチレン系フィルムにおけるシール面以外の面に被膜されていえばよい。第３実施形態において、金属蒸着層２２が、第１無延伸ポリエチレン系フィルム２３におけるフィルム２４を向く外側面に蒸着されていてもよく、第２無延伸ポリエチレン系フィルム２４におけるフィルム２３を向く内側面に蒸着されていてもよい。
各フィルムの製造工程及び製袋工程は図３に例示したものに限らず、適宜改変できるい。
第４～第６実施形態において、印刷層１３が、何れかのフィルム１７，１８の何れかのポリエチレン層の何れかの面に設けられていてもよい。
印刷層２２を省略してもよい。 The present invention is not limited to the above-described embodiment, and various modifications can be made.
For example, the metal vapor-deposited layer 22 may be coated on a surface other than the sealing surface of the unstretched polyethylene-based film of the sealant layer 20. In the third embodiment, the metal vapor-deposited layer 22 may be deposited on the outer surface of the first unstretched polyethylene-based film 23 facing the film 24, or on the inner surface of the second unstretched polyethylene-based film 24 facing the film 23.
The manufacturing process of each film and the bag making process are not limited to those illustrated in FIG. 3, and may be modified as appropriate.
In the fourth to sixth embodiments, the printed layer 13 may be provided on either surface of either polyethylene layer of either film 17, 18.
The printing layer 22 may be omitted.

本発明は、例えば食品、洗剤などを収容する可撓性の包装袋に適用できる。 The present invention can be applied to flexible packaging bags for storing, for example, food, detergent, etc.

１ 包装袋
２ 胴部フィルム
３ 底フィルム
１０ 積層体
１０Ｂ，１０Ｃ，１０Ｄ，１０Ｅ，１０Ｆ 積層体
１１ 基材層
１２ 延伸ポリエチレン系フィルム
１２Ａ，１２Ｂ 延伸ポリエチレン系フィルム
１３ 印刷層
１５Ｄ，１５Ｅ，１５Ｆ 層内接着層
１６ 層間接着層
１６Ｄ，１６Ｅ，１６Ｆ 層間接着層
１７ 第１の延伸ポリエチレン系フィルム
１７ａ ポリエチレン層（外面層）
１７ｂ 外面層のシーラント層側に積層されたポリエチレン層
１７ｃ ポリエチレン層（外面層）
１７ｄ 外面層のシーラント層側に積層されたポリエチレン層
１７ｅ 第２の延伸ポリエチレン系フィルムと対面するポリエチレン層
１８ 第２の延伸ポリエチレン系フィルム
１８ａ 内面層のシーラント層側とは反対側に積層されたポリエチレン層
１８ｂ ポリエチレン層（内面層）
１８ｃ 第１の延伸ポリエチレン系フィルムと対面するポリエチレン層
１８ｄ シーラント層と対面するポリエチレン層
１８ｆ 第１ポリエチレン系フィルムと対面するポリエチレン層
１８ｇ 内面層のシーラント層側とは反対側に積層されたポリエチレン層
１８ｈ ポリエチレン層（内面層）
２０ シーラント層
２１ 無延伸ポリエチレン系フィルム
２２ 金属蒸着層
２１ａ シール面
２３ 第１無延伸ポリエチレン系フィルム
２３ａ シール面
２４ 第２無延伸ポリエチレン系フィルム
２６ 層内接着層 1 Packaging bag 2 Body film 3 Bottom film 10 Laminate 10B, 10C, 10D, 10E, 10F Laminate 11 Base material layer 12 Stretched polyethylene-based film 12A, 12B Stretched polyethylene-based film 13 Printed layer 15D, 15E, 15F Intralayer adhesive layer 16 Interlayer adhesive layer 16D, 16E, 16F Interlayer adhesive layer 17 First stretched polyethylene-based film 17a Polyethylene layer (outer surface layer)
17b: Polyethylene layer laminated on the sealant layer side of the outer layer 17c: Polyethylene layer (outer layer)
17d: Polyethylene layer 17e laminated on the sealant layer side of the outer layer; Polyethylene layer 18 facing the second stretched polyethylene film; Second stretched polyethylene film 18a: Polyethylene layer 18b laminated on the opposite side of the sealant layer side of the inner layer (inner layer)
18c: Polyethylene layer facing the first stretched polyethylene film; 18d: Polyethylene layer facing the sealant layer; 18f: Polyethylene layer facing the first polyethylene film; 18g: Polyethylene layer laminated on the opposite side of the inner layer from the sealant layer side; 18h: Polyethylene layer (inner layer)
20 sealant layer 21 unstretched polyethylene film 22 metal deposition layer 21a sealing surface 23 first unstretched polyethylene film 23a sealing surface 24 second unstretched polyethylene film 26 intralayer adhesive layer

Claims (8)

可撓性の包装袋として用いられる積層体であって、
１又は複数の延伸ポリエチレン系フィルムを含む基材層と、
前記基材層に積層されたシーラント層と、
を備え、前記シーラント層が、直鎖状低密度ポリエチレンを含む無延伸ポリエチレン系フィルムと、前記無延伸ポリエチレン系フィルムにおけるシール面以外の面に被膜された金属蒸着層とを含み、
前記基材層が、第１の延伸ポリエチレン系フィルムと、前記第１の延伸ポリエチレン系フィルムと前記シーラント層との間に介在された第２の延伸ポリエチレン系フィルムとを含み、これら第１、第２の延伸ポリエチレン系フィルムがそれぞれ２以上のポリエチレン層を含み、
前記第１の延伸ポリエチレン系フィルムにおける、第２の延伸ポリエチレン系フィルム側とは反対側の外面層を構成するポリエチレン層が、高密度ポリエチレンを含み、かつ前記外面層の第２の延伸ポリエチレン系フィルム側に積層されたポリエチレン層が、中密度ポリエチレン層又は直鎖状低密度ポリエチレンを含み、
前記第１、第２の延伸ポリエチレン系フィルムにおける互いに対向するポリエチレン層が、高密度ポリエチレンを含み、
前記第１、第２の延伸ポリエチレン系フィルムどうしの間に、低密度ポリエチレン又は直鎖状低密度ポリエチレンの薄膜からなる層内接着層が介在されていることを特徴とする包装袋用積層体。 A laminate used as a flexible packaging bag,
A substrate layer comprising one or more stretched polyethylene-based films;
A sealant layer laminated on the base layer;
The sealant layer includes a non-oriented polyethylene film containing a linear low-density polyethylene, and a metal vapor-deposited layer coated on a surface of the non-oriented polyethylene film other than the sealing surface,
the base layer includes a first stretched polyethylene-based film and a second stretched polyethylene-based film interposed between the first stretched polyethylene-based film and the sealant layer, and each of the first and second stretched polyethylene-based films includes two or more polyethylene layers;
In the first stretched polyethylene-based film, a polyethylene layer constituting an outer surface layer on the side opposite to the second stretched polyethylene-based film side contains high density polyethylene, and a polyethylene layer laminated on the second stretched polyethylene-based film side of the outer surface layer contains a medium density polyethylene layer or a linear low density polyethylene,
The opposing polyethylene layers of the first and second stretched polyethylene-based films contain high density polyethylene,
A laminate for packaging bags, characterized in that an intralayer adhesive layer consisting of a thin film of low density polyethylene or linear low density polyethylene is interposed between the first and second stretched polyethylene films . 前記シーラント層が、前記シール面を有する第１無延伸ポリエチレン系フィルムと、前記第１無延伸ポリエチレン系フィルムにおける前記シール面とは反対側の前記基材層を向く面に層内接着層を介して積層された第２無延伸ポリエチレン系フィルムとを備え、
前記第１、第２無延伸ポリエチレン系フィルムが、それぞれ直鎖状低密度ポリエチレンを含み、
前記第１、第２無延伸ポリエチレン系フィルムの何れかにおけるシール面以外の面に前記金属蒸着層が被膜されている請求項１に記載の積層体。 the sealant layer comprises a first unstretched polyethylene-based film having the sealing surface, and a second unstretched polyethylene-based film laminated via an intralayer adhesive layer on a surface of the first unstretched polyethylene-based film facing the base layer on the opposite side to the sealing surface,
The first and second unstretched polyethylene films each contain a linear low-density polyethylene,
2. The laminate according to claim 1, wherein the metal vapor deposition layer is formed on a surface of either the first or second unstretched polyethylene film other than the sealing surface. 前記基材層と前記シーラント層との間に層間接着層が介在されている請求項１又は２に記載の積層体。 3. The laminate according to claim 1, further comprising an interlayer adhesive layer interposed between the base layer and the sealant layer. 前記第２の延伸ポリエチレン系フィルムにおける、前記シーラント層と対面する内面層を構成するポリエチレン層が、高密度ポリエチレンを含み、かつ前記内面層の第１の延伸ポリエチレン側に積層されたポリエチレン層が、中密度ポリエチレン層又は直鎖状低密度ポリエチレンを含み、
前記内面層と前記シーラント層との間に、低密度ポリエチレン又は直鎖状低密度ポリエチレンの薄膜からなる層間接着層が介在されている請求項１又は２に記載の積層体。 In the second stretched polyethylene film, a polyethylene layer constituting an inner surface layer facing the sealant layer contains high density polyethylene, and a polyethylene layer laminated on the first stretched polyethylene side of the inner surface layer contains a medium density polyethylene layer or a linear low density polyethylene,
3. The laminate according to claim 1, wherein an interlayer adhesive layer made of a thin film of low-density polyethylene or linear low-density polyethylene is interposed between the inner surface layer and the sealant layer. 前記積層体を構成するポリエチレンの少なくとも一部が、植物由来ポリエチレンである請求項１～４のいずれか一項に記載の積層体。 5. The laminate according to claim 1 , wherein at least a part of the polyethylene constituting the laminate is a plant-derived polyethylene. 前記積層体を構成するポリエチレンの少なくとも一部が、リサイクルポリエチレンである請求項１～４のいずれか一項に記載の積層体。 5. The laminate according to claim 1 , wherein at least a part of the polyethylene constituting the laminate is recycled polyethylene. 前記基材層に印刷層が設けられている請求項１～６のいずれか一項に記載の積層体。 The laminate according to any one of claims 1 to 6 , wherein a printed layer is provided on the base layer. 請求項１～７のいずれか一項に記載の積層体からなる包装袋。 A packaging bag comprising the laminate according to any one of claims 1 to 7 .
JP2020126412A 2020-07-27 2020-07-27 Laminate for packaging bag and packaging bag Active JP7507627B2 (en)