JP7453303B1 - 液状急結剤、吹付けコンクリート - Google Patents
液状急結剤、吹付けコンクリート Download PDFInfo
- Publication number
- JP7453303B1 JP7453303B1 JP2022153726A JP2022153726A JP7453303B1 JP 7453303 B1 JP7453303 B1 JP 7453303B1 JP 2022153726 A JP2022153726 A JP 2022153726A JP 2022153726 A JP2022153726 A JP 2022153726A JP 7453303 B1 JP7453303 B1 JP 7453303B1
- Authority
- JP
- Japan
- Prior art keywords
- mass
- setting agent
- liquid quick
- quick
- setting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
[2] 30℃における粘度が200~3,000mPa・sである[1]に記載の液状急結剤。
[3] [1]又は[2]に記載の液状急結剤を含む吹付けコンクリート。
本実施形態に係る液状急結剤は、液状急結剤の質量を100%とすると、アルミニウムがAl2O3換算で9.0~15.0%、硫黄がSO3換算で22.0~35.0%、粘土鉱物が0.5~2.0質量%、アミン系化合物が0.5~5.0質量%含有されている。
液状急結剤中のAl2O3換算のアルミニウム濃度は、JISK1423硫酸アルミニウム(硫酸バンド)に記載の方法に準拠して測定することができる。
SO3換算の硫黄濃度は、イオンクロマトグラフィーなどにより測定することができる。
なお、粘土鉱物の平均粒子径は0.5~20μmが好ましく、1~10μmがより好ましい。粘土鉱物の平均粒子径はレーザ回折法により測定することができる。
アミン系化合物の含有量は、高速液体クロマトグラフ分析法などにより測定することができる。
本発明者らは、既述の各成分の濃度とともに、当該分散粒子のHeywood平均径の範囲が、急結性及び強度発現性を良好にしながら、分散粒子の分散安定性(貯蔵安定性)に重要であるとの知見を得た。すなわち、分散粒子のHeywood平均径が3μm未満であると、液状急結剤の粘度が高くなり吹付ノズルへの送液が不安定となって急結性や強度発現性が低下する場合がある。また、本実施形態の液状急結剤を安定して製造すること(生産性)を考慮すると、分散粒子のHeywood平均径は3μm以上が好ましい。分散粒子のHeywood平均径が30μmを超えると、貯蔵安定性、急結性、及び強度発現性のいずれかが低下してしまう。
Heywood平均径は3~25μmであることが好ましく、5~20μmであることがより好ましい。
また、析出している分散粒子の量(濃度)や粘度も当該平均径に影響する場合がある。例えば、Al2O3換算濃度やSO3換算濃度が高いものほど分散粒子の量が多くなり、粘度も高くなるため、反応槽内での液状急結材の攪拌や粒子の粉砕に支障が生じ、結果としてHeywood平均径が大きくなりやすい。
当該粘度は、既述の粘土鉱物を添加する等して調整したり、Heywood平均径を制御して調製したりすることができる。
なお、液状急結剤中の全アルカリ量R2Oは、原子吸光法により測定することができる。また、全アルカリ量R2Oは、原料中の全アルカリ量R2Oが低いものを適宜使用することで調整することができる。
なお、ここでいう「有効成分濃度」とは、Al2O3換算のアルミニウム濃度、SO3換算での硫黄濃度、粘度鉱物の濃度、及び、アミン系化合物の濃度の合計濃度(%)をいう。また、「有効成分量」といった場合は、Al2O3換算のアルミニウム、SO3換算での硫黄、粘度鉱物、及びアミン系化合物の合計量をいう。
ハイシェアミキサーとしては、例えば、Silverson社製ハイシェアバッチミキサーAX5シリーズ等を使用することができる。
またワークヘッドの形状や拡販ブレードも粒子サイズの制御に非常に重要である。ワークヘッドには、標準丸形、角孔型、乳化用、軸流ヘッド、スロット型などがあるが、本実施形態では、標準型、角孔型、乳化型を用いることが好ましい。
本実施形態に係る吹付けコンクリートは、既述の本発明の液状急結剤を含む。
本発明の液状急結剤は単独で用いてもよいし、カルシウムアルミネートを主成分とした粉体急結剤と併用してもよい。
これらの方法により吹付けコンクリートとした後は、吹付け対象物に吹付け処理が施される。
<液状急結剤の調製>
粉末硫酸アルミニウム、硫酸、水酸化アルミニウム、粘土鉱物、アミン系化合物を、Al2O3換算のアルミニウム濃度、SO3換算での硫黄濃度、粘土鉱物、アミン系化合物が表1に示す量となるように各種原料を調整し、50℃で所定量の水と混合し、1Lの液状急結剤を作製した。
なお、混合には、高速ミキサー(ハイスピード)又はハイシェアミキサー(ハイシェア)を用いた。具体的な混合条件は下記のとおりである。
・水:純水
・粉末硫酸アルミニウム:13~16水塩、工業用品市販品
・硫酸:工業用市販品
・水酸化アルミニウム:工業用市販品
・粘土鉱物a:セピオライト、含水珪酸マグネシウム、平均粒子径3μm、市販品
・アミン系化合物a:ジエタノールアミン、市販品
高速ミキサー:スリーワンモーター撹拌機、回転速度及び撹拌時間は表1に示す条件とした。
ハイシェアミキサー:Silverson社製ハイシェアバッチミキサーL5M-A、撹拌ヘッドEmulsor Screen、回転速度及び撹拌時間は表1に示す条件とした。
調製した液状急結剤における析出粒子の粒度分布測定は以下に示す方法で定量した。なお、測定時の液状急結剤の温度は、20℃とした。
・観察装置:金属顕微鏡 BX-51 オリンパス製
・観察手法:スライドガラスに液状急結剤を10μL滴下、その上にカバーガラスを載置して検鏡試料を調製した。その後、透過光による観察(撮影)を実施した。
・粒度分布解析:撮影した写真を用いて、画像解析式粒度分布測定ソフト「Mac-View Ver.4」で解析した。粒子径は選択粒子と同一の面積をもつ円の直径に換算したHeywood径で換算した。測定粒子数は、300個とし、その平均を求めた。
メスシリンダー100mlに試料を充填して質量を計測し、質量を体積で除した値を密度とした。
<pH>
市販のpHメータにより、液状急結剤のpHを測定した。
Brookfield社製回転粘度計を用い、スピンドルS63、回転速度20rpmの条件下で、30℃における粘度を測定した。
普通ポルトランドセメント700質量部と、表乾砂2100質量部を基本配合とし、調製した液状急結剤は有効成分量で28質量部(セメント100質量部に対して4.0質量部)を水350質量部と一緒に添加した。なお水の量は液状急結剤に含まれる水分を考慮して調整した。低速で10秒、高速で10秒練り混ぜた後に型詰および成形し、凝結試験・圧縮強度試験を行った。
試験は、JIS R5201「セメントの物理試験方法」に準拠し、始発時間及び終結時間ならびに各材齢(12時間、1日、7日、28日)における圧縮強度を計測した。試験は20℃で実施した。結果を下記表1に示す。
調整した液状急結剤を透明1,000ml容器に充填して20℃環境下で静置し、容器上部に相分離の高さを評価した。上面に形成される分離相の割合が全体の10%未満を〇、10~20%を△、20%超を×とした。結果を下記表1に示す。評価は充填して1か月後に実施した。
<液状急結剤の調製>
粉末硫酸アルミニウム、硫酸、水酸化アルミニウム、粘土鉱物、アミン系化合物を、Al2O3換算のアルミニウム濃度、SO3換算での硫黄濃度、粘土鉱物、アミン系化合物が表2に示す量となるように各種原料を調整し、50℃で所定量の水と混合し、1Lの液状急結剤を作製した。
なお、混合には、高速ミキサー(ハイスピード)又はハイシェアミキサー(ハイシェア)を用いた。具体的な混合条件は下記のとおりである。
・粘土鉱物b:アタパルジャイト(含水珪酸アルミニウム・マグネシウム)、平均粒子径5μm、市販品
・アミン系化合物b:ジイソプロピルアミン、市販品
高速ミキサー:スリーワンモーター撹拌機、回転速度及び撹拌時間は表2に示す条件とした。
ハイシェアミキサー:Silverson社製ハイシェアバッチミキサーL5M-A、撹拌ヘッドEmulsor Screen、回転速度及び撹拌時間は表2に示す条件とした。
<吹付けコンクリートの調製>
セメント400kg、水200kg、細骨材1100kg、粗骨材(新潟県姫川水系6号砕石、密度2.67g/cm3)716kgのコンクリートを調製した。このコンクリート中のセメント100質量部に対して、液状急結剤の有効成分量を4.0質量部で混合し、吹付けコンクリートを調製した。なお、試験は30℃環境で実施した。
液状急結剤としては、実験No.3-1では実験No.1-3で調製した液状急結剤を使用し、実験No.3-2では実験No.1-7で調製した液状急結剤を使用した。
得られた吹付けコンクリートを用いて、圧縮強度試験を行った。また、付着性の試験も行った。これらの試験結果を表3に示す。
・長期強度:JSCE-F561に準じて型枠に吹付け、JIS A1107に準じて材齢28日時点でコアを採取して、圧縮強度を測定した。
・付着性:吹付けた量(A)と吹き付け面から跳ね返ったり落下したりしたコンクリートの重量(B)を定量して、リバウンド率(B/A)から付着性を評価した。リバウンド率が15%未満である場合を◎とし、15~30%を〇とし、30%を超える場合を×とした。
Claims (4)
- アルミニウムがAl2O3換算で9.0~15.0質量%、硫黄がSO3換算で22.0~35.0質量%、粘土鉱物が0.5~2.0質量%、アミン系化合物が0.5~5.0質量%含有され、
透過光を用いた光学顕微鏡観察による分散粒子のHeywood平均径が3~30μmであり、
前記分散粒子が不溶解分の硫酸アルミニウムを含む液状急結剤。 - アルミニウムがAl 2 O 3 換算で9.0~14.0質量%、硫黄がSO 3 換算で22.0~33.0質量%、粘土鉱物が0.5~2.0質量%、アミン系化合物が0.5~5.0質量%含有され、
透過光を用いた光学顕微鏡観察による分散粒子のHeywood平均径が3~30μmである液状急結剤。 - 30℃における粘度が200~3,000mPa・sである請求項1又は2に記載の液状急結剤。
- 請求項1又は2に記載の液状急結剤を含む吹付けコンクリート。