JP7411229B2 - ポリエステル樹脂シート用改質剤、ポリエステル樹脂組成物、ポリエステル樹脂シート、積層シート及び成形体の製造方法 - Google Patents
ポリエステル樹脂シート用改質剤、ポリエステル樹脂組成物、ポリエステル樹脂シート、積層シート及び成形体の製造方法 Download PDFInfo
- Publication number
- JP7411229B2 JP7411229B2 JP2020214251A JP2020214251A JP7411229B2 JP 7411229 B2 JP7411229 B2 JP 7411229B2 JP 2020214251 A JP2020214251 A JP 2020214251A JP 2020214251 A JP2020214251 A JP 2020214251A JP 7411229 B2 JP7411229 B2 JP 7411229B2
- Authority
- JP
- Japan
- Prior art keywords
- polyester resin
- modifier
- parts
- resin sheet
- sheets
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
また、加工により形状付与された、例えば、容器は、通常、多数個が積み重ねられて運搬され、その後、容器が1個ずつ取り出されてから、容器内に物品が収容される。しかしながら、樹脂素材の滑り性が十分でなかったり、ブロッキングしていたりすると、複数の容器が重なったまま取り出されることがある。
特許文献1には、平均粒径8~50ミクロンの易滑剤粒子(シリカ等)を0.04~1重量%と、ポリエステル99.0~99.96重量%を配合した組成物からなる無延伸又は低倍率延伸ポリエステルシートが開示されている。特許文献2には、カルシウム元素およびリン元素を含有する内部粒子と50~750ppmのシリカ粒子を含有し、カルシウム元素の含有量が0.01~0.1重量%で、リン元素の含有量がカルシウム元素に対する元素量比で0.5~2倍当量であるポリエステルからなり、最大径が5μm以下の突起がフィルム表面に20~60個/μm2の密度で存在することを特徴とする二軸延伸ポリエステルフィルムが開示されている。また、特許文献3には、少なくとも3層以上の積層構造を有し、一方のフィルム表面の表面粗さ(Ra)が0.001~0.005μmの範囲内であり、当該表面を構成する層中に酸化アルミニウム粒子を1000ppm以上含有し、当該表面に離型層、グリーンシートが順次設けられており、もう一方のフィルム表面の表面粗さ(Ra)が0.010~0.030μmの範囲内であるグリーンシート用離型積層ポリエステルフィルムであり、当該グリーンシート表面における、深さ0.2μm以上の凹みが1個以下/100cm2であり、当該表面を構成する層中に炭素-炭素二重結合を一分子中に2個以上含有する化合物により架橋構造を達成したポリスチレン粒子を含有する積層ポリエステルフィルムであることを特徴とするグリーンシート用離型積層ポリエステルフィルムが開示されている。
本発明のポリエステル樹脂シート用改質剤は、ポリエステル樹脂シートの製造に用いられる改質剤であって、成分(A)として、3~6価の多価アルコールと、炭素原子数が8~22の炭化水素基を有する脂肪酸とのエステル化合物、及び、成分(B)として、カルシウム元素を含む化合物であって、タルク及びゼオライトから選ばれる少なくとも一つを含有し、カルシウム元素の含有割合は、改質剤に対して0.1~3.0質量%であることを特徴とする。
本発明のポリエステル樹脂組成物は、ポリエステル樹脂シートの製造に用いられる樹脂組成物であって、ポリエステル樹脂と、上記本発明のポリエステル樹脂シート用改質剤とを含有することを特徴とする。
本発明のポリエステル樹脂シートは、ポリエステル樹脂と、上記本発明のポリエステル樹脂シート用改質剤とを含有することを特徴とする。
本発明の積層シートは、上記本発明のポリエステル樹脂シートからなる樹脂層と、他の樹脂層とを備えることを特徴とする。
本発明の成形体の製造方法は、上記本発明のポリエステル樹脂シート又は積層シートを、成形加工に供することを特徴とする。
本発明のポリエステル樹脂シート又は積層シートを、従来、公知の成形加工に供することにより、所定形状の成形体を容易に得ることができる。得られる成形体の複数を重ねた場合には、ブロッキングの発生を抑制することができる。
ポリエステル樹脂シート用改質剤に含まれるカルシウム元素は、上記成分(B)のカルシウム元素を有する化合物に由来するカルシウム元素でもよく、それ以外のカルシウム元素でもよい。
本発明において、ポリエステル樹脂シート用改質剤におけるカルシウム元素の含有割合が上記範囲内であれば、ポリエステル樹脂と併用してポリエステル樹脂組成物とすることにより、透明性を損なわずに表面の滑り性に優れたポリエステル樹脂シート等の成形体を容易に製造することができる。
(1)成分(A)及び成分(B)からなる改質剤
(2)成分(A)、成分(B)及び他の充填剤とからなる改質剤
ジカルボン酸成分は、好ましくは、テレフタル酸、ナフタレンジカルボン酸等であり、ジヒドロキシ成分は、好ましくは、エチレングリコール、ジエチレングリコール、ブタンジオール、シクロヘキサンジメタノール等である。代表的なホモポリエステルは、ポリエチレンテレフタレート(PET)、ポリプロピレンテレフタレート(PPT)、ポリブチレンテレフタレート(PBT)、ポリヘキサメチレンテレフタレート、ポリシクロヘキサン-1,4-ジメチルテレフタレート、ポリネオペンチルテレフタレート等のポリアルキレンテレフタレート、ポリエチレンイソフタレート、ポリエチレンナフタレート、ポリブチレンナフタレート、ポリヘキサメチレンナフタレート等のポリアルキレンナフタレート等である。これらのうち、PETが特に好ましい。
ジカルボン酸成分は、好ましくは、イソフタル酸、フタル酸、テレフタル酸、ナフタレンジカルボン酸、アジピン酸、セバシン酸等から選ばれた1種又は2種以上であり、ジヒドロキシ成分は、好ましくは、エチレングリコール、ジエチレングリコール、プロピレングリコール、ブタンジオール、4-シクロヘキサンジメタノール、ネオペンチルグリコール等の1種又は2種以上であり、オキシカルボン酸は、例えば、p-オキシ安息香酸等である。代表的なコポリエステル樹脂は、テレフタル酸と、エチレングリコールと、4-シクロヘキサンジメタノールとからなる縮合物(「PETG樹脂」といわれることがある)、ポリエチレンテレフタレート/イソフタレート樹脂等である。
(1)上記本発明のポリエステル樹脂シート用改質剤と、ポリエステル樹脂とを、タンブラーブレンダー、ヘンシェルミキサー、スーパーミキサー等の混合機に投入して混合した後、単軸押出機、多軸押出機等の押出機により溶融混練しつつ造粒してマスターバッチを得る方法
(2)ポリエステル樹脂を単軸押出機や多軸押出機等の押出機により溶融状態としたところへ、上記本発明のポリエステル樹脂シート用改質剤、添加剤等をサイドフィード又は液状注入により混合し、溶融混練しつつ造粒してマスターバッチを得る方法
ポリエステル樹脂シート用改質剤の製造に用いた原料を以下に示す。充填剤の平均粒径は、レーザー回折・散乱法による測定値である。
A-1:ペンタエリスリトールテトラステアレート
A-2:グリセリントリステアレート
A-3:ソルビタントリステアレート
A-4:グリセリンモノステアレート
A-5:ジグリセリンモノラウレート
A-6:ペンタエリスリトールジステアレート
a-1:エチレングリコールモノステアレート
a-2:デカグリセリンモノラウレート
B-1:ゼオライト粒子(平均粒径:7μm、Ca量:5.73%)
B-2:ゼオライト粒子(平均粒径:5μm、Ca量:5.20%)
B-3:ゼオライト粒子(平均粒径:3μm、Ca量:5.26%)
B-4:ゼオライト粒子(平均粒径:10μm、Ca量:5.40%)
B-5:タルク粒子(平均粒径:4μm、Ca量:0.19%)
B-6:タルク粒子(平均粒径:6μm、Ca量:0.29%)
B-7:タルク粒子(平均粒径:10μm、Ca量:0.10%)
B-8:タルク粒子(平均粒径:15μm、Ca量:0.27%)
B-9:ゼオライト粒子(平均粒径:12μm、Ca量:5.54%)
B-10:ゼオライト粒子(平均粒径:0.5μm、Ca量:5.20%)
C-1:シリカ粒子(平均粒径:3μm)
C-2:タルク粒子(平均粒径:8μm、Ca非含有)
C-3:シリカ粒子(平均粒径:8μm)
C-4:シリカ粒子(平均粒径:3μm)
C-5:シリカ粒子(平均粒径:0.5μm)
実施例及び比較例におけるポリエステル樹脂シート用改質剤のカルシウム元素の含有割合(含有量)は、株式会社リガク製蛍光X線分析装置「ZSX101e」により定量した。
実施例1-1
38.5部の脂肪酸エステルA-1と、7.7部のゼオライト粒子B-1と、30.8部のタルク粒子B-5と、7.7部のシリカ粒子C-1と、15.3部のタルク粒子C-2とをミキサーにより撹拌して、均一混合物からなるポリエステル樹脂シート用改質剤(以下、「樹脂シート用改質剤E-1」という)を得た(表1参照)。この表1には、本発明に係る成分(A)及び(B)の合計を100%としたときの割合と、ポリエステル樹脂シート用改質剤に含まれるカルシウム元素の割合(Ca量)とを併記した。
50部の脂肪酸エステルA-1と、15部のゼオライト粒子B-1と、35部のタルク粒子C-2とを用いて、実施例1-1と同様の操作を行いポリエステル樹脂シート用改質剤(以下、「樹脂シート用改質剤E-2」という)を得た(表1参照)。
60部の脂肪酸エステルA-1と、2.5部の脂肪酸エステルA-4と、9.4部のゼオライト粒子B-1と、28.1部のゼオライト粒子B-2とを用いて、実施例1-1と同様の操作を行いポリエステル樹脂シート用改質剤(以下、「樹脂シート用改質剤E-3」という)を得た(表1参照)。
60部の脂肪酸エステルA-2と、25部のゼオライト粒子B-2と、15部のシリカ粒子C-3とを用いて、実施例1-1と同様の操作を行いポリエステル樹脂シート用改質剤(以下、「樹脂シート用改質剤E-4」という)を得た(表1参照)。
40部の脂肪酸エステルA-2と、30部のゼオライト粒子B-4と、30部のタルク粒子B-7とを用いて、実施例1-1と同様の操作を行いポリエステル樹脂シート用改質剤(以下、「樹脂シート用改質剤E-5」という)を得た(表1参照)。
59部の脂肪酸エステルA-1と、6.3部のゼオライト粒子B-3と、34.7部のタルク粒子B-6とを用いて、実施例1-1と同様の操作を行いポリエステル樹脂シート用改質剤(以下、「樹脂シート用改質剤E-6」という)を得た(表1参照)。
40.5部の脂肪酸エステルA-1と、46.5部のゼオライト粒子B-3と、13部のタルク粒子B-8とを用いて、実施例1-1と同様の操作を行いポリエステル樹脂シート用改質剤(以下、「樹脂シート用改質剤E-7」という)を得た(表1参照)。
27.3部の脂肪酸エステルA-2と、31.8部のゼオライト粒子B-3と、40.9部のタルク粒子B-5とを用いて、実施例1-1と同様の操作を行いポリエステル樹脂シート用改質剤(以下、「樹脂シート用改質剤E-8」という)を得た(表1参照)。
70部の脂肪酸エステルA-2と、3.7部の脂肪酸エステルA-5と、26.3部のゼオライト粒子B-9とを用いて、実施例1-1と同様の操作を行いポリエステル樹脂シート用改質剤(以下、「樹脂シート用改質剤E-9」という)を得た(表1参照)。
78.6部の脂肪酸エステルA-2と、1.4部のゼオライト粒子B-1と、20部のタルク粒子B-5とを用いて、実施例1-1と同様の操作を行いポリエステル樹脂シート用改質剤(以下、「樹脂シート用改質剤E-10」という)を得た(表1参照)。
61.1部の脂肪酸エステルA-3と、38.9部のゼオライト粒子B-10とを用いて、実施例1-1と同様の操作を行いポリエステル樹脂シート用改質剤(以下、「樹脂シート用改質剤E-11」という)を得た(表1参照)。
47.4部の脂肪酸エステルA-1と、1.4部のゼオライト粒子B-1と、51.2部のシリカ粒子C-4とを用いて、実施例1-1と同様の操作を行いポリエステル樹脂シート用改質剤(以下、「樹脂シート用改質剤e-1」という)を得た(表1参照)。
25部の脂肪酸エステルA-6と、75部のゼオライト粒子B-10とを用いて、実施例1-1と同様の操作を行いポリエステル樹脂シート用改質剤(以下、「樹脂シート用改質剤e-2」という)を得た(表1参照)。
62.5部の脂肪酸エステルa-1と、18.75部のゼオライト粒子B-1と、18.75部のシリカ粒子C-3とを用いて、実施例1-1と同様の操作を行いポリエステル樹脂シート用改質剤(以下、「樹脂シート用改質剤e-3」という)を得た(表1参照)。
30.3部の脂肪酸エステルa-2と、15.15部のゼオライト粒子B-2と、14.55部のタルク粒子C-2と、40部のシリカ粒子C-5とを用いて、実施例1-1と同様の操作を行いポリエステル樹脂シート用改質剤(以下、「樹脂シート用改質剤e-4」という)を得た(表1参照)。
上記で得られたポリエステル樹脂シート用改質剤と、中国石化儀征化繊社製ポリエチレンテレフタレート「BG-80」(商品名)とを用いて、マスターバッチ(樹脂組成物)を製造した。
100部の上記ポリエチレンテレフタレート(PET)と、35.1部の樹脂シート用改質剤E-1とを、タンブラーにより撹拌した後、日本製鋼所社製二軸混練押出機「TEX30α」(型式名)を用いて、250℃~270℃で溶融混練して、マスターバッチM-1を得た(表2参照)。
100部の上記ポリエチレンテレフタレート(PET)と、25.0部の樹脂シート用改質剤E-2とを用いて、実施例2-1と同様の操作を行い、マスターバッチM-2を得た(表2参照)。
100部の上記ポリエチレンテレフタレート(PET)と、25.0部の樹脂シート用改質剤E-4とを用いて、実施例2-1と同様の操作を行い、マスターバッチM-3を得た(表2参照)。
100部の上記ポリエチレンテレフタレート(PET)と、25.0部の樹脂シート用改質剤E-5とを用いて、実施例2-1と同様の操作を行い、マスターバッチM-4を得た(表2参照)。
100部の上記ポリエチレンテレフタレート(PET)と、22.7部の樹脂シート用改質剤E-7とを用いて、実施例2-1と同様の操作を行い、マスターバッチM-5を得た(表2参照)。
100部の上記ポリエチレンテレフタレート(PET)と、22.0部の樹脂シート用改質剤E-11とを用いて、実施例2-1と同様の操作を行い、マスターバッチM-6を得た(表2参照)。
上記ポリエチレンテレフタレート(PET)と、上記で得られたポリエステル樹脂シート用改質剤又はマスターバッチとを用いて、ポリエステル樹脂シート形成用の樹脂組成物を製造した。
100部の上記ポリエチレンテレフタレート(PET)と、0.50部の樹脂シート用改質剤E-1とを、タンブラーにより撹拌した後、日本製鋼所社製二軸混練押出機「TEX30α」(型式名)を用いて、250℃~270℃で溶融混練して、ポリエステル樹脂シート製造用の組成物(以下、「樹脂組成物T-1」という)を得た。次いで、この樹脂組成物T-1の溶融混練物をTダイより40℃に調温した冷却ロール上に押出し、厚さが300μmのポリエステル樹脂シート(以下、「樹脂シートS-1」という)を得た(表3参照)。
ポリエステル樹脂シートを、20℃及び65%R.H.で24時間調湿した後、同雰囲気にて東洋精機社製摩擦測定機「TR-2」(型式名)を用い、JIS K7125に準拠して静摩擦係数を測定した。測定は3枚の樹脂シートの任意の表面に対して行い、合計3点の平均値を採用して、以下の基準で滑り性を評価した。
◎◎:0.35以下
◎:0.35超~0.40以下
〇:0.40超~0.60以下
×:0.60超
ポリエステル樹脂シートのHAZEを、日本電色工業社製ヘーズメーター「NDH5000」(型式名)を用い、JIS K7136に準拠して測定した。測定は5枚の樹脂シートの任意の位置に対して行い、合計5点の平均値を採用して、以下の基準で透明性を評価した。
◎:5%以下
〇:5%超~10%以下
×:10%超
99.60部の上記ポリエチレンテレフタレート(PET)と、0.54部のマスターバッチM-1とを用いた以外は、実施例3-1と同様にして樹脂組成物T-2を製造し、次いで、表3に示す樹脂シートS-2を製造した。その後、滑り性及び透明性の評価を行った(表3参照)。
96.58部の上記ポリエチレンテレフタレート(PET)と、4.62部のマスターバッチM-1とを用いた以外は、実施例3-1と同様にして樹脂組成物T-3を製造し、次いで、表3に示す樹脂シートS-3を製造した。その後、滑り性及び透明性の評価を行った(表3参照)。
100部の上記ポリエチレンテレフタレート(PET)と、1.01部の樹脂シート用改質剤E-1とを用いた以外は、実施例3-1と同様にして樹脂組成物T-4を製造し、次いで、表3に示す樹脂シートS-4を製造した。その後、滑り性及び透明性の評価を行った(表3参照)。
100部の上記ポリエチレンテレフタレート(PET)と、0.60部の樹脂シート用改質剤E-2とを用いた以外は、実施例3-1と同様にして樹脂組成物T-5を製造し、次いで、表3に示す樹脂シートS-5を製造した。その後、滑り性及び透明性の評価を行った(表3参照)。
98.48部の上記ポリエチレンテレフタレート(PET)と、1.90部のマスターバッチM-2とを用いた以外は、実施例3-1と同様にして樹脂組成物T-6を製造し、次いで、表3に示す樹脂シートS-6を製造した。その後、滑り性及び透明性の評価を行った(表3参照)。
100部の上記ポリエチレンテレフタレート(PET)と、0.91部の樹脂シート用改質剤E-3とを用いた以外は、実施例3-1と同様にして樹脂組成物T-7を製造し、次いで、表3に示す樹脂シートS-7を製造した。その後、滑り性及び透明性の評価を行った(表3参照)。
100部の上記ポリエチレンテレフタレート(PET)と、0.55部の樹脂シート用改質剤E-4とを用いた以外は、実施例3-1と同様にして樹脂組成物T-8を製造し、次いで、表3に示す樹脂シートS-8を製造した。その後、滑り性及び透明性の評価を行った(表3参照)。
95.60部の上記ポリエチレンテレフタレート(PET)と、5.50部のマスターバッチM-3とを用いた以外は、実施例3-1と同様にして樹脂組成物T-9を製造し、次いで、表3に示す樹脂シートS-9を製造した。その後、滑り性及び透明性の評価を行った(表3参照)。
100部の上記ポリエチレンテレフタレート(PET)と、0.70部の樹脂シート用改質剤E-5とを用いた以外は、実施例3-1と同様にして樹脂組成物T-10を製造し、次いで、表3に示す樹脂シートS-10を製造した。その後、滑り性及び透明性の評価を行った(表3参照)。
97.20部の上記ポリエチレンテレフタレート(PET)と、3.50部のマスターバッチM-4とを用いた以外は、実施例3-1と同様にして樹脂組成物T-11を製造し、次いで、表3に示す樹脂シートS-11を製造した。その後、滑り性及び透明性の評価を行った(表3参照)。
100部の上記ポリエチレンテレフタレート(PET)と、0.81部の樹脂シート用改質剤E-6とを用いた以外は、実施例3-1と同様にして樹脂組成物T-12を製造し、次いで、表3に示す樹脂シートS-12を製造した。その後、滑り性及び透明性の評価を行った(表3参照)。
100部の上記ポリエチレンテレフタレート(PET)と、0.50部の樹脂シート用改質剤E-7とを用いた以外は、実施例3-1と同様にして樹脂組成物T-13を製造し、次いで、表3に示す樹脂シートS-13を製造した。その後、滑り性及び透明性の評価を行った(表3参照)。
93.83部の上記ポリエチレンテレフタレート(PET)と、7.57部のマスターバッチM-5とを用いた以外は、実施例3-1と同様にして樹脂組成物T-14を製造し、次いで、表3に示す樹脂シートS-14を製造した。その後、滑り性及び透明性の評価を行った(表3参照)。
100部の上記ポリエチレンテレフタレート(PET)と、0.20部の樹脂シート用改質剤E-8とを用いた以外は、実施例3-1と同様にして樹脂組成物T-15を製造し、次いで、表3に示す樹脂シートS-15を製造した。その後、滑り性及び透明性の評価を行った(表3参照)。
100部の上記ポリエチレンテレフタレート(PET)と、1.32部の樹脂シート用改質剤E-9とを用いた以外は、実施例3-1と同様にして樹脂組成物T-16を製造し、次いで、表3に示す樹脂シートS-16を製造した。その後、滑り性及び透明性の評価を行った(表3参照)。
100部の上記ポリエチレンテレフタレート(PET)と、1.21部の樹脂シート用改質剤E-10とを用いた以外は、実施例3-1と同様にして樹脂組成物T-17を製造し、次いで、表3に示す樹脂シートS-17を製造した。その後、滑り性及び透明性の評価を行った(表3参照)。
100部の上記ポリエチレンテレフタレート(PET)と、1.01部の樹脂シート用改質剤E-11とを用いた以外は、実施例3-1と同様にして樹脂組成物T-18を製造し、次いで、表3に示す樹脂シートS-18を製造した。その後、滑り性及び透明性の評価を行った(表3参照)。
98.18部の上記ポリエチレンテレフタレート(PET)と、2.22部のマスターバッチM-6とを用いた以外は、実施例3-1と同様にして樹脂組成物T-19を製造し、次いで、表3に示す樹脂シートS-19を製造した。その後、滑り性及び透明性の評価を行った(表3参照)。
100部の上記ポリエチレンテレフタレート(PET)と、0.50部の樹脂シート用改質剤e-1とを用いた以外は、実施例3-1と同様にして樹脂組成物t-1を製造し、次いで、表3に示す樹脂シートs-1を製造した。その後、滑り性及び透明性の評価を行った(表3参照)。
100部の上記ポリエチレンテレフタレート(PET)と、0.30部の樹脂シート用改質剤e-2とを用いた以外は、実施例3-1と同様にして樹脂組成物t-2を製造し、次いで、表3に示す樹脂シートs-2を製造した。その後、滑り性及び透明性の評価を行った(表3参照)。
100部の上記ポリエチレンテレフタレート(PET)と、0.81部の樹脂シート用改質剤e-3とを用いた以外は、実施例3-1と同様にして樹脂組成物t-3を製造し、次いで、表3に示す樹脂シートs-3を製造した。その後、滑り性及び透明性の評価を行った(表3参照)。
100部の上記ポリエチレンテレフタレート(PET)と、0.50部の樹脂シート用改質剤e-4とを用いた以外は、実施例3-1と同様にして樹脂組成物t-4を製造し、次いで、表3に示す樹脂シートs-4を製造した。その後、滑り性及び透明性の評価を行った(表3参照)。
上記で得られたポリエステル樹脂組成物と中国石化儀征化繊社製ポリエチレンテレフタレート「BG-80」(商品名)を用いて、積層シートを製造した。
実施例3-1と同様にして作成した樹脂シートS-1製造用の樹脂組成物T-1を両表層に、上記ポリエチレンテレフタレート樹脂を中間層に、それぞれの溶融混練物をTダイより40℃に調温した冷却ロール上に共押出し、厚さが300μm、層比=1/8/1の3層積層シート(以下、「積層シートU-1」という)を得た(表4参照)。
実施例4-1と同様にして、表3に示すポリエステル樹脂シート(S-2~S-19)製造用の樹脂組成物(T-2~T-19)を用いて表4に示す積層シートU-2~U-19を得た(表4参照)。
実施例4-1と同様にして、表3に示すポリエステル樹脂シート(s-1~s-4)製造用の樹脂組成物(t-1~t-4)を用いて表4に示す積層シートu-1~u-4を得た(表4参照)。
上記のポリエステル樹脂シート又は積層シートを用いて、成形体を製造した。
表3に示すポリエステル樹脂シート(S-1)を用いて、布施真空(株)製NGF-0912型真空成形機により樹脂温度90℃にて真空成型を行い、縦10cm×横15cm×深さ3cmのトレイ型の成形体(以下、「成形体V-1」という)を得た(表5参照)。
実施例5-1と同様にして、表3に示すポリエステル樹脂シート(S-2~S-19)を用いて表5に示す成形体V-2~V-19を得た(表5参照)。
実施例5-1と同様にして、表4に示す積層シート(U-1~U-19)を用いて表6に示す成形体V-20~V-38を得た(表6参照)。
実施例5-1と同様にして、表3に示すポリエステル樹脂シート(s-1~s-4)を用いて表7に示す成形体v-1~v-4を得た(表7参照)。
実施例5-1と同様にして、表4に示す積層シート(u-1~u-4)を用いて表7に示す成形体v-5~v-8を得た(表7参照)。
Claims (12)
- ポリエステル樹脂シートの製造に用いられる改質剤であって、
下記の成分(A)及び下記の成分(B)を含有し、前記成分(B)がタルク及びゼオライトから選ばれる少なくとも1つを含み、前記改質剤中にカルシウム元素を0.1~3.0質量%の割合で含有することを特徴とするポリエステル樹脂シート用改質剤。
成分(A):3~6価の多価アルコールと、炭素原子数が8~22の炭化水素基を有する脂肪酸とのエステル化合物。
成分(B):カルシウム元素を含む化合物。 - 前記成分(A)の形成に用いる前記多価アルコールが、ペンタエリスリトール及びグリセリンから選ばれる少なくとも一つを含む請求項1に記載のポリエステル樹脂シート用改質剤。
- 前記成分(A)の形成に用いる前記脂肪酸が、前記炭素原子数が12~18の炭化水素基を有するものである請求項1又は2に記載のポリエステル樹脂シート用改質剤。
- 前記成分(A)及び前記成分(B)の含有割合の合計を100質量%とした場合に、前記成分(A)を40~80質量%及び前記成分(B)を20~60質量%の割合で含有する請求項1から3のいずれか一項に記載のポリエステル樹脂シート用改質剤。
- ポリエステル樹脂シートの製造に用いられる樹脂組成物であって、
ポリエステル樹脂と、請求項1から4のいずれか一項に記載のポリエステル樹脂シート用改質剤とを含有することを特徴とするポリエステル樹脂組成物。 - 前記ポリエステル樹脂の含有割合を100質量部とした場合に、前記ポリエステル樹脂シート用改質剤を0.1~45質量部の割合で含有する請求項5に記載のポリエステル樹脂組成物。
- 前記ポリエステル樹脂の含有量を100質量部とした場合に、前記ポリエステル樹脂シート用改質剤を10~45質量部の割合で含有する請求項6に記載のポリエステル樹脂組成物。
- ポリエステル樹脂と、請求項1から4のいずれか一項に記載のポリエステル樹脂シート用改質剤とを含有することを特徴とするポリエステル樹脂シート。
- 前記ポリエステル樹脂の含有割合を100質量部とした場合に、前記ポリエステル樹脂シート用改質剤を0.1~1.5質量部の割合で含有する請求項8に記載のポリエステル樹脂シート。
- 請求項8又は9に記載のポリエステル樹脂シートから成る樹脂層と、他の樹脂層とを備えることを特徴とする積層シート。
- 請求項8又は9に記載のポリエステル樹脂シートを、成形加工に供することを特徴とする成形体の製造方法。
- 請求項10に記載の積層シートを、成形加工に供することを特徴とする成形体の製造方法。