JP7405553B2 - ワイヤロープ - Google Patents
ワイヤロープ Download PDFInfo
- Publication number
- JP7405553B2 JP7405553B2 JP2019181415A JP2019181415A JP7405553B2 JP 7405553 B2 JP7405553 B2 JP 7405553B2 JP 2019181415 A JP2019181415 A JP 2019181415A JP 2019181415 A JP2019181415 A JP 2019181415A JP 7405553 B2 JP7405553 B2 JP 7405553B2
- Authority
- JP
- Japan
- Prior art keywords
- wire rope
- lubricant
- strand
- sulfur
- molybdenum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
A-1.ワイヤロープ10の構成:
図1は、第1実施形態におけるワイヤロープ10の構成を概略的に示す断面斜視図であり、図2は、第1実施形態におけるワイヤロープ10の横断面構成を示す説明図である。第1実施形態のワイヤロープ10は、種々の用途(例えば、自動車用のウィンドレギュレータ用ワイヤロープやスライドドア用ワイヤロープ、産業分野における動力伝達用ワイヤロープ、建築関係の窓開閉装置用ワイヤロープ)に用いられ得る。
次に、本実施形態におけるワイヤロープ10の製造方法の一例を説明する。はじめに、潤滑剤40が素線21,23の間に介在した芯ストランド20と、側ストランド30とを作製する。
以上説明したように、第1実施形態のワイヤロープ10は、ロープ本体15と、潤滑剤40と、樹脂層50とを備える。ロープ本体15は、芯ストランド20と側ストランド30とを有している。芯ストランド20は、互いに撚り合わされた複数の素線21,23から形成されている。側ストランド30は、互いに撚り合わされた複数の素線31,33から形成されている。潤滑剤40は、芯ストランド20を構成する複数の素線21,23の間と、側ストランド30を構成する複数の素線31,33の間の少なくとも一部とに介在している。樹脂層50は、ロープ本体15の外周を、潤滑剤40とともに被覆している。潤滑剤40は、硫黄含有有機モリブデン化合物を有している。
ワイヤロープの耐久性について、性能評価を行った。図3は、性能評価の結果を示す説明図であり、図4は、性能評価の評価方法を示す説明図である。
<芯ストランド20>
・芯素線21:1本(直径0.17mm)
・側素線23a:6本(直径0.16mm)
・側素線23b:6本(直径0.17mm)
・側素線23c:6本(直径0.13mm)
・芯ストランド20の外径:0.75mm
・芯ストランド20の材料:SWRH62A
<側ストランド30>
・側ストランド30の本数:8本
・芯素線31:1本(直径0.15mm)
・側素線33:6本(直径0.14mm)
・側ストランド30の外径:0.43mm
・側ストランド30の材料:SWRH62A
<ロープ本体15>
・外径:1.61mm
<潤滑剤40>
・オイルS1:硫黄含有有機モリブデン化合物含有オイル(40℃における粘度100mm2/s)
・1m長のワイヤロープ10に対する潤滑剤40の含有量:1.5重量%
<樹脂層50>
・樹脂の種類:ポリアミド12
・被覆厚さ:0.15mm
<ワイヤロープ10>
・外径:1.91mm
・ロープ本体15、樹脂層50については、ワイヤロープAと同様である。
<潤滑剤>
・オイルS2:硫黄化合物含有オイル(40℃における粘度120mm2/s)
・1m長のワイヤロープ10に対する潤滑剤の含有量:1.5重量%
・ロープ本体15、潤滑剤40については、ワイヤロープAと同様である。
<樹脂層>
・なし
・ロープ本体15については、ワイヤロープAと同様であり、潤滑剤については、ワイヤロープX1と同様である。
<樹脂層>
・なし
<プーリ103a.103b>
・溝直径L:25mm
・溝角度θ:30°
・溝底部の曲率半径R:0.9mm
・材質:ポリアセタール樹脂
次に、第2実施形態におけるワイヤロープについて説明する。本実施形態におけるワイヤロープは、潤滑剤が、硫黄非含有有機モリブデン化合物と、硫黄含有有機化合物とを含有する点で、第1実施形態のワイヤロープ10と異なる。以下では、第2実施形態のワイヤロープの構成の内、上述した第1実施形態のワイヤロープ10と同一の構成については、その説明を適宜省略する。
図5は、第3実施形態におけるワイヤロープ10Aの横断面構成を示す説明図である。以下では、第3実施形態のワイヤロープ10Aの構成のうち、上述した第1実施形態のワイヤロープ10の構成と同一の構成については、同一の符号を付すことによってその説明を適宜省略する。
図6は、第4実施形態におけるワイヤロープ10Bの横断面構成を示す説明図である。以下では、第4実施形態のワイヤロープ10Bの構成のうち、上述した実施形態のワイヤロープ10,10Aの構成と同一の構成については、同一の符号を付すことによってその説明を適宜省略する。
図7は、第5実施形態におけるワイヤロープ10Cの横断面構成を示す説明図である。以下では、第5実施形態のワイヤロープ10Cの構成のうち、上述した実施形態のワイヤロープ10,10A,10Bの構成と同一の構成については、同一の符号を付すことによってその説明を適宜省略する。
図8は、第6実施形態におけるワイヤロープ10Dの横断面構成を示す説明図である。以下では、第6実施形態のワイヤロープ10Dの構成のうち、上述した実施形態のワイヤロープ10,10A,10B,10Cの構成と同一の構成については、同一の符号を付すことによってその説明を適宜省略する。
本明細書で開示される技術は、上述の実施形態に限られるものではなく、その要旨を逸脱しない範囲において種々の形態に変形することができ、例えば次のような変形も可能である。
Claims (12)
- ワイヤロープであって、
互いに撚り合わされた複数の素線から形成されるストランドを有するロープ本体と、
前記ストランドを構成する複数の素線の間に介在する潤滑剤と、
前記ロープ本体の外周を、前記潤滑剤とともに被覆する樹脂層と、を備え、
前記潤滑剤は、常温で液体であり、かつ、硫黄含有有機モリブデン化合物を含有し、前記ストランドを構成する素線表面と前記樹脂層の内周面とにより形成される空間に存在しており、
前記硫黄含有有機モリブデン化合物は、摩擦熱により二硫化モリブデンを生成することが可能な化合物である、
ワイヤロープ。 - 請求項1に記載のワイヤロープであって、
前記潤滑剤の常温での粘度は、100mm2/s以上、14100mm2/s以下である、
ワイヤロープ。 - 請求項1または請求項2に記載のワイヤロープであって、
前記ロープ本体は、前記ストランドとして芯ストランドを有する、
ワイヤロープ。 - 請求項3に記載のワイヤロープであって、
前記芯ストランドは、ウォーリントン撚りである、
ワイヤロープ。 - 請求項3または請求項4に記載のワイヤロープであって、
前記ロープ本体は、前記ストランドとして、さらに、前記芯ストランドの周りに撚り合わされた複数の側ストランドを有する、
ワイヤロープ。 - 請求項1から請求項5までのいずれか一項に記載のワイヤロープであって、
前記硫黄含有有機モリブデン化合物は、ジアルキルジチオカルバミン酸モリブデンとジアルキルジチオリン酸モリブデンとのうちの少なくとも1つである、
ワイヤロープ。 - ワイヤロープであって、
互いに撚り合わされた複数の素線から形成されるストランドを有するロープ本体と、
前記ストランドを構成する複数の素線の間に介在する潤滑剤と、
前記ロープ本体の外周を、前記潤滑剤とともに被覆する樹脂層と、を備え、
前記潤滑剤は、常温で液体であり、かつ、硫黄非含有有機モリブデン化合物と、硫黄含有有機化合物と、を含有し、前記ストランドを構成する素線表面と前記樹脂層の内周面とにより形成される空間に存在しており、
前記硫黄非含有有機モリブデン化合物および硫黄含有有機化合物は、摩擦熱により二硫化モリブデンを生成することが可能な化合物である、
ワイヤロープ。 - 請求項7に記載のワイヤロープであって、
前記潤滑剤の常温での粘度は、100mm2/s以上、14100mm2/s以下である、
ワイヤロープ。 - 請求項7または請求項8に記載のワイヤロープであって、
前記ロープ本体は、前記ストランドとして芯ストランドを有する、
ワイヤロープ。 - 請求項9に記載のワイヤロープであって、
前記芯ストランドは、ウォーリントン撚りである、
ワイヤロープ。 - 請求項9または請求項10に記載のワイヤロープであって、
前記ロープ本体は、前記ストランドとして、さらに、前記芯ストランドの周りに撚り合わされた複数の側ストランドを有する、
ワイヤロープ。 - 請求項7から請求項11までのいずれか一項に記載のワイヤロープであって、
前記硫黄非含有有機モリブデン化合物は、モリブデン-アミン錯体、モリブデン-コハク酸イミド錯体、有機酸のモリブデン塩、アルコールのモリブデン塩の少なくとも1つであり、
前記硫黄含有有機化合物は、チアジアゾール、硫化オレフィン、硫化油脂、硫化エステル、ポリサルファイドの少なくとも1つである、
ワイヤロープ。