JP7395657B2 - 発泡イソシアネート系ポリマー - Google Patents
発泡イソシアネート系ポリマー Download PDFInfo
- Publication number
- JP7395657B2 JP7395657B2 JP2022096585A JP2022096585A JP7395657B2 JP 7395657 B2 JP7395657 B2 JP 7395657B2 JP 2022096585 A JP2022096585 A JP 2022096585A JP 2022096585 A JP2022096585 A JP 2022096585A JP 7395657 B2 JP7395657 B2 JP 7395657B2
- Authority
- JP
- Japan
- Prior art keywords
- biomass
- isocyanate
- particulate material
- carbonaceous particulate
- foamed isocyanate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本出願は、2016年6月29日に出願された米国仮特許出願第62/493,304号の35U.S.C.§119(e)に基づく利益を主張するものであり、その内容は参照により本明細書に組み込まれる。
発明の分野
その1つの側面において、本発明は改良された特性を有する発泡イソシアネート系ポリマーに関する。その別の側面において、本発明はそのような発泡イソシアネート系ポリマーの製造方法に関する。そのさらに別の側面において、本発明はイソシアネート系発泡体の特性を改良する方法に関する。そのさらに別の側面において、本発明は、とりわけ発泡イソシアネート系ポリマーの製造に有用なポリオール系分散体に関する。
イソシアネート系ポリマーは当技術分野で公知である。一般に、当業者はイソシアネート系ポリマーをポリウレタン、ポリ尿素、ポリイソシアヌレートおよびこれらの混合物であると理解している。
本発明の目的は、先行技術の上記不都合の少なくとも1つを取り除くかまたは和らげることである。
イソシアネート;
ベースのポリオール中に分散されている第1の所定量のポリマー粒子を含むポリオール組成物;
第2の所定量のバイオマス系の炭素質微粒子状材料;および
発泡剤
を含む反応混合物から誘導される発泡イソシアネート系ポリマーであって、
発泡イソシアネート系ポリマーが、ASTM D3574-11に従って測定したとき、反応混合物からバイオマス系の炭素質微粒子状材料を省略し、ポリマーポリオール組成物中のポリマー粒子の量を増大して第1の所定量および第2の所定量の総和と等しくすることにより生成した参照発泡体の約15%以内の押込み力撓みを有する、発泡イソシアネート系ポリマーを提供する。
イソシアネート;および
ベースのポリオール中に分散されているポリマー粒子を任意に含んでいてもよいポリオール組成物;
バイオマス系の炭素質微粒子状材料
から誘導される発泡イソシアネート系ポリマーであって、
発泡ポリマーが複数の相互に接続した支柱を含む多孔性マトリックスを有しており、バイオマス系の炭素質微粒子状材料がバイオマス系の炭素質微粒子状材料の重量%当たり少なくとも約5ニュートンの投入効率を多孔性マトリックスに付与する、発泡イソシアネート系ポリマーを提供する。
(a)イソシアネート;ベースのポリオール中に分散されている第1の所定量のポリマー粒子を任意に含んでいてもよいポリオール組成物、第2の所定量のバイオマス系の炭素質微粒子状材料および発泡剤を接触させて反応混合物を生成させる工程と;
(b)反応混合物を膨張させて発泡イソシアネート系ポリマーを生成させる工程と
を含む、発泡イソシアネート系ポリマーを製造する方法を提供する。
(a)第1の所定量のバイオマス系の炭素質微粒子状材料ポリマー粒子;および
(b)ポリオール
を含むポリオール系分散体であって、
分散体が第2の所定量のポリマー粒子を任意に含んでいてもよい、ポリオール系分散体を提供する。
その1つの側面において、本発明は、イソシアネート;ベースのポリオール中に分散されている第1の所定量のポリマー粒子を含むポリオール組成物;第2の所定量のバイオマス系の炭素質微粒子状材料;および発泡剤を含む反応混合物から誘導された発泡イソシアネート系ポリマーであって、ASTM D3574-11に従って測定したとき、反応混合物からバイオマス系の炭素質微粒子状材料を省略し、ポリマーポリオール組成物中のポリマー粒子の量を増大させて第1の所定量および第2の所定量の総和と等しくすることにより製造された参照発泡体の約15%以内の押込み力撓み(indentation force deflection)を有する、発泡イソシアネート系ポリマーに関する。
・第1の所定量がゼロであって、ベースのポリオール組成物がベースのポリオールである;
・バイオマス系の炭素質微粒子状材料が、反応混合物の形成前にベースのポリオール組成物に分散されている;
・バイオマス系の炭素質微粒子状材料が、約50μm未満のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.01μm~約50μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.1μm~約50μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.1μm~約45μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.1μm~約40μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.1μm~約35μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.2μm~約30μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.2μm~約25μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.2μm~約20μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.2μm~約15μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.2μm~約10μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.2μm~約8μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.2μm~約6μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.3μm~約6μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.4μm~約6μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.5μm~約6μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約6μmのD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約1.3μmのD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.9μmのD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.5μmのD50粒径を有する;
・発泡イソシアネート系ポリマーが、ASTM D3574-11に従って測定したとき、参照発泡体の約13%以内の押込み力撓みを有する;
・発泡イソシアネート系ポリマーが、ASTM D3574-11に従って測定したとき、参照発泡体の約11%以内の押込み力撓みを有する;
・発泡イソシアネート系ポリマーが、ASTM D3574-11に従って測定したとき、参照発泡体の約10%以内の押込み力撓みを有する;
・発泡イソシアネート系ポリマーが、ASTM D3574-11に従って測定したとき、参照発泡体の約8%以内の押込み力撓みを有する;
・発泡イソシアネート系ポリマーが、ASTM D3574-11に従って測定したとき、参照発泡体の約6%以内の押込み力撓みを有する;
・発泡イソシアネート系ポリマーが、ASTM D3574-11に従って測定したとき、参照発泡体の約5%以内の押込み力撓みを有する;
・バイオマス系の炭素質微粒子状材料が、ASTM D4373を用いて乾式燃焼により測定したとき、約50%~約98%の範囲の有機炭素含有率を含む;
・バイオマス系の炭素質微粒子状材料が、ASTM D4373を用いて乾式燃焼により測定したとき、約75%~約98%の範囲の有機炭素含有率を含む;
・バイオマス系の炭素質微粒子状材料が、ASTM D4373を用いて乾式燃焼により測定したとき、約85%~約98%の範囲の有機炭素含有率を含む;
・バイオマス系の炭素質微粒子状材料が、ASTM D4373を用いて乾式燃焼により測定したとき、約0.10~約0.85の範囲の水素対炭素のモル比を含む;
・バイオマス系の炭素質微粒子状材料が、ASTM D4373を用いて乾式燃焼により測定したとき、約0.35~約0.85の範囲の水素対炭素のモル比を含む;
・バイオマス系の炭素質微粒子状材料が、ASTM D4373を用いて乾式燃焼により測定したとき、約0.70~約0.85の範囲の水素対炭素のモル比を含む;
・バイオマス系の炭素質微粒子状材料が、BET法により測定したとき約10~約4,000m2/gの表面積を有する;
・バイオマス系の炭素質微粒子状材料が、BET法により測定したとき約50~約3,000m2/gの表面積を有する;
・バイオマス系の炭素質微粒子状材料が、BET法により測定したとき約150~約2,000m2/gの表面積を有する;
・反応混合物が、ベースのポリオール中に分散されているポリマー粒子を実質的に完全に含まない;
・ベースのポリオールが、ポリエーテル、ポリエステル、ポリカーボネート、ポリジエンおよびポリカプロラクトンからなる群から選択されるメンバーのヒドロキシルを末端基とする主鎖を含む;
・ベースのポリオールが、ヒドロキシルを末端基とするポリ炭化水素、ヒドロキシルを末端基とするポリホルマール、脂肪酸トリグリセリド、ヒドロキシルを末端基とするポリエステル、ヒドロキシメチルを末端基とするポリエステル、ヒドロキシメチルを末端基とするペルフルオロメチレン、ポリアルキレンエーテルグリコール、ポリアルキレンアリーレンエーテルグリコール、ポリアルキレンエーテルトリオールおよびこれらの混合物からなる群から選択される;
・ベースのポリオールが、アジピン酸-エチレングリコールポリエステル、ポリ(ブチレングリコール)、ポリ(プロピレングリコール)、ヒドロキシルを末端基とするポリブタジエンおよびこれらの混合物からなる群から選択される;
・ベースのポリオールがポリエーテルポリオールである;
・ポリエーテルポリオールが、約200~約10,000の範囲の分子量を有する;
・ポリエーテルポリオールが、約2,000~約7,000の範囲の分子量を有する;
・ポリエーテルポリオールが、約2,000~約6,000の範囲の分子量を有する;
・反応混合物が、ポリアミン、ポリアルカノールアミンおよびこれらの任意の混合物からなる群から選択される活性水素含有化合物をさらに含む;
・ポリアミンが、一級アミンを末端基とするポリエーテル、二級アミンを末端基とするポリエーテルおよびこれらの任意の混合物からなる群から選択される;
・イソシアネートがプレポリマーを含む;
・イソシアネートが、1,6-ヘキサメチレンジイソシアネート、1,4-ブチレンジイソシアネート、フルフリリデンジイソシアネート、2,4-トルエンジイソシアネート、2,6-トルエンジイソシアネート、2,4’-ジフェニルメタンジイソシアネート、4,4’-ジフェニルメタンジイソシアネート、4,4’-ジフェニルプロパンジイソシアネート、4,4’-ジフェニル-3,3’-ジメチルメタンジイソシアネート、1,5-ナフタレンジイソシアネート、1-メチル-2,4-ジイソシアネート-5-クロロベンゼン、2,4-ジイソシアナト-s-トリアジン、1-メチル-2,4-ジイソシアナトシクロヘキサン、p-フェニレンジイソシアネート、m-フェニレンジイソシアネート、1,4-ナフタレンジイソシアネート、ジアニシジンジイソシアネート、ビトリレンジイソシアネート、1,4-キシリレンジイソシアネート、1,3-キシリレンジイソシアネート、ビス-(4-イソシアナトフェニル)メタン、ビス-(3-メチル-4-イソシアナトフェニル)メタン、ポリメチレンポリフェニルポリイソシアネートおよびこれらの混合物からなる群から選択される;
・イソシアネートが、2,4-トルエンジイソシアネート、2,6-トルエンジイソシアネートおよびこれらの混合物からなる群から選択される;
・イソシアネートが、(i)2,4’-ジフェニルメタンジイソシアネート、4,4’-ジフェニルメタンジイソシアネートおよびこれらの混合物;ならびに(ii)(i)と2,4-トルエンジイソシアネート、2,6-トルエンジイソシアネートおよびこれらの混合物からなる群から選択されるイソシアネートとの混合物から本質的になる群から選択される、請求項1~48のいずれか一項に記載の発泡イソシアネート系ポリマー;
・発泡剤が水を含む;
・発泡剤が水からなる;
・水が、反応混合物中に使用されるベースのポリオール100重量部当たり約0.5~約40重量部の範囲の量で使用される;
・水が、反応混合物中に使用されるベースのポリオール100重量部当たり約1.0~約10重量部の範囲の量で使用される;および/または
・発泡イソシアネート系ポリマーが成形される。
・第1の所定量がゼロであって、ベースのポリオール組成物がベースのポリオールである;
・バイオマス系の炭素質微粒子状材料が、反応混合物の形成前にベースのポリオール組成物に分散されている;
・バイオマス系の炭素質微粒子状材料が、約50μm未満のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.01μm~約50μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.1μm~約50μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.1μm~約45μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.1μm~約40μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.1μm~約35μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.2μm~約30μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.2μm~約25μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.2μm~約20μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.2μm~約15μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.2μm~約10μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.2μm~約8μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.2μm~約6μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.3μm~約6μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.4μm~約6μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.5μm~約6μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約6μmのD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約1.3μmのD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.9μmのD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.5μmのD50粒径を有する;
・発泡イソシアネート系ポリマーが、ASTM D3574-11に従って測定したとき、反応混合物中のバイオマス系の炭素質微粒子状材料の量と等しい量の、ベースのポリオール中のポリマー粒子で置換することによって生成した参照発泡体の約15%以内の押込み力撓みを有する;
・発泡イソシアネート系ポリマーが、ASTM D3574-11に従って測定したとき、参照発泡体の約13%以内の押込み力撓みを有する;
・発泡イソシアネート系ポリマーが、ASTM D3574-11に従って測定したとき、参照発泡体の約11%以内の押込み力撓みを有する;
・発泡イソシアネート系ポリマーが、ASTM D3574-11に従って測定したとき、参照発泡体の約10%以内の押込み力撓みを有する;
・発泡イソシアネート系ポリマーが、ASTM D3574-11に従って測定したとき、参照発泡体の約8%以内の押込み力撓みを有する;
・発泡イソシアネート系ポリマーが、ASTM D3574-11に従って測定したとき、参照発泡体の約6%以内の押込み力撓みを有する;
・発泡イソシアネート系ポリマーが、ASTM D3574-11に従って測定したとき、参照発泡体の約5%以内の押込み力撓みを有する;
・バイオマス系の炭素質微粒子状材料が、ASTM D4373を用いて乾式燃焼により測定したとき、約50%~約98%の範囲の有機炭素含有率を含む;
・バイオマス系の炭素質微粒子状材料が、ASTM D4373を用いて乾式燃焼により測定したとき、約75%~約98%の範囲の有機炭素含有率を含む;
・バイオマス系の炭素質微粒子状材料が、ASTM D4373を用いて乾式燃焼により測定したとき、約85%~約98%の範囲の有機炭素含有率を含む;
・バイオマス系の炭素質微粒子状材料が、ASTM D4373を用いて乾式燃焼により測定したとき、約0.10~約0.85の範囲の水素対炭素のモル比を含む;
・バイオマス系の炭素質微粒子状材料が、ASTM D4373を用いて乾式燃焼により測定したとき、約0.35~約0.85の範囲の水素対炭素のモル比を含む;
・バイオマス系の炭素質微粒子状材料が、ASTM D4373を用いて乾式燃焼により測定したとき、約0.70~約0.85の範囲の水素対炭素のモル比を含む;
・バイオマス系の炭素質微粒子状材料が、BET法により測定したとき約10~約4,000m2/gの表面積を有する;
・バイオマス系の炭素質微粒子状材料が、BET法により測定したとき約50~約3,000m2/gの表面積を有する;
・バイオマス系の炭素質微粒子状材料が、BET法により測定したとき約150~約2,000m2/gの表面積を有する;
・反応混合物が、ベースのポリオール中に分散されているポリマー粒子を実質的に完全に含まない;
・ベースのポリオールが、ポリエーテル、ポリエステル、ポリカーボネート、ポリジエンおよびポリカプロラクトンからなる群から選択されるメンバーのヒドロキシルを末端基とする主鎖を含む;
・ベースのポリオールが、ヒドロキシルを末端基とするポリ炭化水素、ヒドロキシルを末端基とするポリホルマール、脂肪酸トリグリセリド、ヒドロキシルを末端基とするポリエステル、ヒドロキシメチルを末端基とするポリエステル、ヒドロキシメチルを末端基とするペルフルオロメチレン、ポリアルキレンエーテルグリコール、ポリアルキレンアリーレンエーテルグリコール、ポリアルキレンエーテルトリオールおよびこれらの混合物からなる群から選択される;
・ベースのポリオールが、アジピン酸-エチレングリコールポリエステル、ポリ(ブチレングリコール)、ポリ(プロピレングリコール)、ヒドロキシルを末端基とするポリブタジエンおよびこれらの混合物からなる群から選択される;
・ベースのポリオールがポリエーテルポリオールである;
・ポリエーテルポリオールが、約200~約10,000の範囲の分子量を有する;
・ポリエーテルポリオールが、約2,000~約7,000の範囲の分子量を有する;
・ポリエーテルポリオールが、約2,000~約6,000の範囲の分子量を有する;
・反応混合物が、ポリアミン、ポリアルカノールアミンおよびこれらの任意の混合物からなる群から選択される活性水素含有化合物をさらに含む;
・ポリアミンが、一級アミンを末端基とするポリエーテル、二級アミンを末端基とするポリエーテルおよびこれらの任意の混合物からなる群から選択される;
・イソシアネートがプレポリマーを含む;
・イソシアネートが、1,6-ヘキサメチレンジイソシアネート、1,4-ブチレンジイソシアネート、フルフリリデンジイソシアネート、2,4-トルエンジイソシアネート、2,6-トルエンジイソシアネート、2,4’-ジフェニルメタンジイソシアネート、4,4’-ジフェニルメタンジイソシアネート、4,4’-ジフェニルプロパンジイソシアネート、4,4’-ジフェニル-3,3’-ジメチルメタンジイソシアネート、1,5-ナフタレンジイソシアネート、1-メチル-2,4-ジイソシアネート-5-クロロベンゼン、2,4-ジイソシアナト-s-トリアジン、1-メチル-2,4-ジイソシアナトシクロヘキサン、p-フェニレンジイソシアネート、m-フェニレンジイソシアネート、1,4-ナフタレンジイソシアネート、ジアニシジンジイソシアネート、ビトリレンジイソシアネート、1,4-キシリレンジイソシアネート、1,3-キシリレンジイソシアネート、ビス-(4-イソシアナトフェニル)メタン、ビス-(3-メチル-4-イソシアナトフェニル)メタン、ポリメチレンポリフェニルポリイソシアネートおよびこれらの混合物からなる群から選択される;
・イソシアネートが、2,4-トルエンジイソシアネート、2,6-トルエンジイソシアネートおよびこれらの混合物からなる群から選択される;
・イソシアネートが、(i)2,4’-ジフェニルメタンジイソシアネート、4,4’-ジフェニルメタンジイソシアネートおよびこれらの混合物;ならびに(ii)(i)と2,4-トルエンジイソシアネート、2,6-トルエンジイソシアネートおよびこれらの混合物からなる群から選択されるイソシアネートとの混合物から本質的になる群から選択される;
・発泡剤が水を含む;
・発泡剤が水からなる;
・水が、反応混合物中に使用されるベースのポリオール100重量部当たり約0.5~約40重量部の範囲の量で使用される;
・水が、反応混合物中に使用されるベースのポリオール100重量部当たり約1.0~約10重量部の範囲の量で使用される;および/または
・発泡イソシアネート系ポリマーが成形される。
・第1の所定量がゼロであって、ベースのポリオール組成物がベースのポリオールである;
・バイオマス系の炭素質微粒子状材料が、反応混合物の形成前にベースのポリオール組成物に分散されている;
・バイオマス系の炭素質微粒子状材料が、約50μm未満のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.01μm~約50μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.1μm~約50μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.1μm~約45μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.1μm~約40μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.1μm~約35μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.2μm~約30μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.2μm~約25μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.2μm~約20μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.2μm~約15μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.2μm~約10μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.2μm~約8μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.2μm~約6μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.3μm~約6μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.4μm~約6μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.5μm~約6μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約6μmのD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約1.3μmのD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.9μmのD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.5μmのD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、ASTM D4373を用いて乾式燃焼により測定したとき、約50%~約98%の範囲の有機炭素含有率を含む;
・バイオマス系の炭素質微粒子状材料が、ASTM D4373を用いて乾式燃焼により測定したとき、約75%~約98%の範囲の有機炭素含有率を含む;
・バイオマス系の炭素質微粒子状材料が、ASTM D4373を用いて乾式燃焼により測定したとき、約85%~約98%の範囲の有機炭素含有率を含む;
・バイオマス系の炭素質微粒子状材料が、ASTM D4373を用いて乾式燃焼により測定したとき、約0.10~約0.85の範囲の水素対炭素のモル比を含む;
・バイオマス系の炭素質微粒子状材料が、ASTM D4373を用いて乾式燃焼により測定したとき、約0.35~約0.85の範囲の水素対炭素のモル比を含む;
・バイオマス系の炭素質微粒子状材料が、ASTM D4373を用いて乾式燃焼により測定したとき、約0.70~約0.85の範囲の水素対炭素のモル比を含む;
・バイオマス系の炭素質微粒子状材料が、BET法により測定したとき約10~約4,000m2/gの表面積を有する;
・バイオマス系の炭素質微粒子状材料が、BET法により測定したとき約50~約3,000m2/gの表面積を有する;
・バイオマス系の炭素質微粒子状材料が、BET法により測定したとき約150~約2,000m2/gの表面積を有する;
・反応混合物が、ベースのポリオール中に分散されているポリマー粒子を実質的に完全に含まない;
・ベースのポリオールが、ポリエーテル、ポリエステル、ポリカーボネート、ポリジエンおよびポリカプロラクトンからなる群から選択されるメンバーのヒドロキシルを末端基とする主鎖を含む;
・ベースのポリオールが、ヒドロキシルを末端基とするポリ炭化水素、ヒドロキシルを末端基とするポリホルマール、脂肪酸トリグリセリド、ヒドロキシルを末端基とするポリエステル、ヒドロキシメチルを末端基とするポリエステル、ヒドロキシメチルを末端基とするペルフルオロメチレン、ポリアルキレンエーテルグリコール、ポリアルキレンアリーレンエーテルグリコール、ポリアルキレンエーテルトリオールおよびこれらの混合物からなる群から選択される;
・ベースのポリオールが、アジピン酸-エチレングリコールポリエステル、ポリ(ブチレングリコール)、ポリ(プロピレングリコール)、ヒドロキシルを末端基とするポリブタジエンおよびこれらの混合物からなる群から選択される;
・ベースのポリオールがポリエーテルポリオールである;
・ポリエーテルポリオールが、約200~約10,000の範囲の分子量を有する;
・ポリエーテルポリオールが、約2,000~約7,000の範囲の分子量を有する;
・ポリエーテルポリオールが、約2,000~約6,000の範囲の分子量を有する;
・反応混合物が、ポリアミン、ポリアルカノールアミンおよびこれらの任意の混合物からなる群から選択される活性水素含有化合物をさらに含む;
・ポリアミンが、一級アミンを末端基とするポリエーテル、二級アミンを末端基とするポリエーテルおよびこれらの任意の混合物からなる群から選択される;
・イソシアネートがプレポリマーを含む;
・イソシアネートが、1,6-ヘキサメチレンジイソシアネート、1,4-ブチレンジイソシアネート、フルフリリデンジイソシアネート、2,4-トルエンジイソシアネート、2,6-トルエンジイソシアネート、2,4’-ジフェニルメタンジイソシアネート、4,4’-ジフェニルメタンジイソシアネート、4,4’-ジフェニルプロパンジイソシアネート、4,4’-ジフェニル-3,3’-ジメチルメタンジイソシアネート、1,5-ナフタレンジイソシアネート、1-メチル-2,4-ジイソシアネート-5-クロロベンゼン、2,4-ジイソシアナト-s-トリアジン、1-メチル-2,4-ジイソシアナトシクロヘキサン、p-フェニレンジイソシアネート、m-フェニレンジイソシアネート、1,4-ナフタレンジイソシアネート、ジアニシジンジイソシアネート、ビトリレンジイソシアネート、1,4-キシリレンジイソシアネート、1,3-キシリレンジイソシアネート、ビス-(4-イソシアナトフェニル)メタン、ビス-(3-メチル-4-イソシアナトフェニル)メタン、ポリメチレンポリフェニルポリイソシアネートおよびこれらの混合物からなる群から選択される;
・イソシアネートが、2,4-トルエンジイソシアネート、2,6-トルエンジイソシアネートおよびこれらの混合物からなる群から選択される;
・イソシアネートが、(i)2,4’-ジフェニルメタンジイソシアネート、4,4’-ジフェニルメタンジイソシアネートおよびこれらの混合物;ならびに(ii)(i)と2,4-トルエンジイソシアネート、2,6-トルエンジイソシアネートおよびこれらの混合物からなる群から選択されるイソシアネートとの混合物から本質的になる群から選択される;
・発泡剤が水を含む;
・発泡剤が水からなる;
・水が、反応混合物中に使用されるベースのポリオール100重量部当たり約0.5~約40重量部の範囲の量で使用される;
・水が、反応混合物中に使用されるベースのポリオール100重量部当たり約1.0~約10重量部の範囲の量で使用される;
・工程(b)を、発泡イソシアネート系ポリマーを成形発泡体として製造するように構成された密閉モールドで行う;および/または
・工程(b)を、オープントップを有するチャネルで行って、発泡イソシアネート系ポリマーをスラブ発泡体として製造する。
・バイオマス系の炭素質微粒子状材料が、約50μm未満のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.01μm~約50μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.1μm~約50μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.1μm~約45μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.1μm~約40μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.1μm~約35μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.2μm~約30μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.2μm~約25μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.2μm~約20μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.2μm~約15μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.2μm~約10μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.2μm~約8μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.2μm~約6μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.3μm~約6μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.4μm~約6μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.5μm~約6μmの範囲のD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約6μmのD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約1.3μmのD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.9μmのD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、約0.5μmのD50粒径を有する;
・バイオマス系の炭素質微粒子状材料が、ASTM D4373を用いて乾式燃焼により測定したとき、約50%~約98%の範囲の有機炭素含有率を含む;
・バイオマス系の炭素質微粒子状材料が、ASTM D4373を用いて乾式燃焼により測定したとき、約75%~約98%の範囲の有機炭素含有率を含む;
・バイオマス系の炭素質微粒子状材料が、ASTM D4373を用いて乾式燃焼により測定したとき、約85%~約98%の範囲の有機炭素含有率を含む;
・バイオマス系の炭素質微粒子状材料が、ASTM D4373を用いて乾式燃焼により測定したとき、約0.10~約0.85の範囲の水素対炭素のモル比を含む;
・バイオマス系の炭素質微粒子状材料が、ASTM D4373を用いて乾式燃焼により測定したとき、約0.35~約0.85の範囲の水素対炭素のモル比を含む;
・バイオマス系の炭素質微粒子状材料が、ASTM D4373を用いて乾式燃焼により測定したとき、約0.70~約0.85の範囲の水素対炭素のモル比を含む;
・バイオマス系の炭素質微粒子状材料が、BET法により測定したとき約10~約4,000m2/gの表面積を有する;
・バイオマス系の炭素質微粒子状材料が、BET法により測定したとき約50~約3,000m2/gの表面積を有する;
・バイオマス系の炭素質微粒子状材料が、BET法により測定したとき約150~約2,000m2/gの表面積を有する;
・分散体がポリマー粒子を実質的に完全に含まない;
・ベースのポリオールが、ポリエーテル、ポリエステル、ポリカーボネート、ポリジエンおよびポリカプロラクトンからなる群から選択されるメンバーのヒドロキシルを末端基とする主鎖を含む;
・ベースのポリオールが、ヒドロキシルを末端基とするポリ炭化水素、ヒドロキシルを末端基とするポリホルマール、脂肪酸トリグリセリド、ヒドロキシルを末端基とするポリエステル、ヒドロキシメチルを末端基とするポリエステル、ヒドロキシメチルを末端基とするペルフルオロメチレン、ポリアルキレンエーテルグリコール、ポリアルキレンアリーレンエーテルグリコール、ポリアルキレンエーテルトリオールおよびこれらの混合物からなる群から選択される;
・ベースのポリオールが、アジピン酸-エチレングリコールポリエステル、ポリ(ブチレングリコール)、ポリ(プロピレングリコール)、ヒドロキシルを末端基とするポリブタジエンおよびこれらの混合物からなる群から選択される;
・ベースのポリオールがポリエーテルポリオールである;
・ポリエーテルポリオールが、約200~約10,000の範囲の分子量を有する;
・ポリエーテルポリオールが、約2,000~約7,000の範囲の分子量を有する;
・ポリエーテルポリオールが、約2,000~約6,000の範囲の分子量を有する;
・反応混合物が、ポリアミン、ポリアルカノールアミンおよびこれらの任意の混合物からなる群から選択される活性水素含有化合物をさらに含む;および/または
・ポリアミンが、一級アミンを末端基とするポリエーテル、二級アミンを末端基とするポリエーテルおよびこれらの任意の混合物からなる群から選択される。
Q(NCO)i
(式中、iは2以上の整数であり、Qはiの原子価を有する有機のラジカルである)
で表されてもよい。Qは置換または無置換の炭化水素基(たとえば、アルキレンまたはアリーレン基)であってよい。また、Qは一般式:
Q1-Z-Q1
(式中、Q1はアルキレンまたはアリーレン基であり、Zは-O-、-O-Q1-、-CO-、-S-、-S-Q1-S-および-SO2-を含む群から選択される)
で表されてもよい。この定義の範囲内に入るイソシアネート化合物の例には、ヘキサメチレンジイソシアネート、1,8-ジイソシアナト-p-メタン、キシリルジイソシアネート、(OCNCH2CH2CH2OCH2O)2、1-メチル-2,4-ジイソシアナトシクロヘキサン、フェニレンジイソシアネート、トリレンジイソシアネート、クロロフェニレンジイソシアネート、ジフェニルメタン-4,4’-ジイソシアネート、ナフタレン-1,5-ジイソシアネート、トリフェニルメタン-4,4’,4”-トリイソシアネートおよびイソプロピルベンゼン-アルファ-4-ジイソシアネートがある。
[Q”(NCO)i]j
(式中、iとjの両方は2以上の値を有する整数であり、Q”は多官能性の有機のラジカルである)
を有するポリマーのジイソシアネート、および/または、反応混合物中の追加の成分としての、一般式:
L(NCO)i
(式中、iは1以上の値を有する整数であり、Lは単官能または多官能の原子またはラジカルである)
を有する化合物から選択されてもよい。この定義の範囲内に入るイソシアネート化合物の例には、エチルホスホン酸ジイソシアネート、フェニルホスホン酸ジイソシアネート、=Si-NCO基を含有する化合物、スルホンアミド(QSO2NCO)、シアン酸およびチオシアン酸から誘導されたイソシアネート化合物がある。
Hyperlite(商標)E866、ベースのポリオール、Covestroから市販;
Hyperlite(商標)E850、a 43%固形分のコポリマー(SAN)ポリオール、Covestroから市販;
Voranol(商標)CP1421、ベースのポリオール、DOWから市販;
ベースのポリオール中に分散されている無定形炭素;
DEOA LF、ジエタノールアミン、架橋剤、Air Productsから市販;
グリセリン、架橋剤、Cargillから市販;
水、間接発泡剤;
Dabco 33LV、ゲル化触媒、Air Productsから市販;
Niax A-1、発泡触媒、Momentiveから市販;
Polycat 77、三級アミン触媒、Air Productsから市販;
Fyrol FR-2、難燃剤、Suprestaから市販;
DC5043、界面活性剤、Dow Corningから市販;および
Mondur(商標)E445、TDI(80%)とMDI(20%)とのブレンド、Covestroから市販。
工程1-炭素を微粉化する:実験室規模の粉砕機を使用し、0.5mmの篩を用いて200gの炭素を微粉化する。炭素は、D100が500μm、D50が250μmの粒径に微粉化する。
実施例1で使用した実際の配合物は表1-5に見いだすことができる。表1の配合物は全てSANコポリマーポリマーを様々なレベルで含有し、無定形炭素分散体を含有しない。したがって、表1の配合物から生成した発泡体は比較の目的のみであり、本発明には包含されない。表2-5の配合物は全て無定形炭素を様々なレベルで含有し、SANコポリマー(またはその他のポリマー)ポリオールを含有しない。表2-5の配合物間の差は無定形炭素分散体中の無定形炭素のD50粒径に関する。
IFD@25%撓み;
IFD@50%撓み;
%ヒステリシス損失;
密度(kg/m3);
引裂強度(N/m);
引張強さ(kPa);
破断点伸び(%);
ボール反発(%);
50%圧縮永久歪み(%);
50%湿潤圧縮永久歪み(%);
50%熱エージング圧縮永久歪み(HACS)、5時間@120℃(%);および
50%HACS、3時間@105℃(%)。
実施例2-6で使用した実際の配合物は表7に見いだすことができる。表7の配合物、たとえば2-6は全てSANコポリマーポリマーおよび無定形炭素を一定のレベルで含有していた。「対照」とされた配合物は無定形炭素分散体を含有せず、したがって、表7のこの配合物から生成した発泡体は比較の目的のみであり、本発明に包含されない。表7の配合物は全て無定形炭素を含有しており、無定形炭素分散体中の無定形炭素のD50粒径は同じで0.8μmである。
IFD@25%撓み;
IFD@50%撓み;
IFD@65%撓み;
%ヒステリシス損失;
密度(kg/m3);
引裂強度(N/m);
引張強さ(kPa);
破断点伸び(%);
50%圧縮永久歪み(%);
50%湿潤圧縮永久歪み(%);
50%熱エージング圧縮永久歪み(HACS)、5時間@120℃(%);および
50%HACS、3時間@105℃(%)。
Claims (42)
- イソシアネート;
ベースのポリオール中に分散されている第1の所定量のスチレン-アクリロニトリルポリマー粒子を含むポリオール組成物;
第2の所定量のバイオマス系の炭素質微粒子状材料;および
発泡剤
を含む反応混合物から誘導される発泡イソシアネート系ポリマーであって、
前記発泡イソシアネート系ポリマーを25%撓ませる押込み力(IFD@25%撓み)が、ASTM D3574-11に従って測定したとき、前記反応混合物から前記バイオマス系の炭素質微粒子状材料を省略し、前記ポリオール組成物中のポリマー粒子の量を増大して前記第1の所定量および前記第2の所定量の総和と等しくすることにより生成した参照発泡体の15%以内であり、
前記バイオマス系の炭素質微粒子状材料を、ASTM D6866試験に従って測定したとき、85%より大きい現代炭素率「pMC」を有し、前記バイオマス系の炭素質微粒子状材料は微孔性活性炭ではなく、
前記バイオマス系の炭素質微粒子状材料と前記スチレン-アクリロニトリルポリマー粒子の固形分の総和の上限は20重量%である、
発泡イソシアネート系ポリマー。 - 前記バイオマス系の炭素質微粒子状材料が、前記反応混合物の形成前にベースのポリオール組成物に分散されている、請求項1に記載の発泡イソシアネート系ポリマー。
- 前記バイオマス系の炭素質微粒子状材料が、0.2μm~6μmの範囲のD50粒径を有する、請求項1または2に記載の発泡イソシアネート系ポリマー。
- 前記バイオマス系の炭素質微粒子状材料が、0.3μm~6μmの範囲のD50粒径を有する、請求項1または2に記載の発泡イソシアネート系ポリマー。
- 前記バイオマス系の炭素質微粒子状材料が、0.4μm~6μmの範囲のD50粒径を有する、請求項1または2に記載の発泡イソシアネート系ポリマー。
- 前記バイオマス系の炭素質微粒子状材料が、0.5μm~6μmの範囲のD50粒径を有する、請求項1または2に記載の発泡イソシアネート系ポリマー。
- 前記バイオマス系の炭素質微粒子状材料が、1.3μmのD50粒径を有する、請求項1または2に記載の発泡イソシアネート系ポリマー。
- 前記バイオマス系の炭素質微粒子状材料が、0.9μmのD50粒径を有する、請求項1または2に記載の発泡イソシアネート系ポリマー。
- 前記バイオマス系の炭素質微粒子状材料が、0.5μmのD50粒径を有する、請求項1または2に記載の発泡イソシアネート系ポリマー。
- 前記発泡イソシアネート系ポリマーを25%撓ませる押込み力(IFD@25%撓み)が、ASTM D3574-11に従って測定したとき、前記参照発泡体の13%以内である、請求項1~9のいずれか一項に記載の発泡イソシアネート系ポリマー。
- 前記発泡イソシアネート系ポリマーを25%撓ませる押込み力(IFD@25%撓み)が、ASTM D3574-11に従って測定したとき、前記参照発泡体の11%以内である、請求項1~9のいずれか一項に記載の発泡イソシアネート系ポリマー。
- 前記発泡イソシアネート系ポリマーを25%撓ませる押込み力(IFD@25%撓み)が、ASTM D3574-11に従って測定したとき、前記参照発泡体の10%以内である、請求項1~9のいずれか一項に記載の発泡イソシアネート系ポリマー。
- 前記発泡イソシアネート系ポリマーを25%撓ませる押込み力(IFD@25%撓み)が、ASTM D3574-11に従って測定したとき、前記参照発泡体の8%以内である、請求項1~9のいずれか一項に記載の発泡イソシアネート系ポリマー。
- 前記発泡イソシアネート系ポリマーを25%撓ませる押込み力(IFD@25%撓み)が、ASTM D3574-11に従って測定したとき、前記参照発泡体の6%以内である、請求項1~9のいずれか一項に記載の発泡イソシアネート系ポリマー。
- 前記発泡イソシアネート系ポリマーを25%撓ませる押込み力(IFD@25%撓み)が、ASTM D3574-11に従って測定したとき、前記参照発泡体の5%以内である、請求項1~9のいずれか一項に記載の発泡イソシアネート系ポリマー。
- 前記バイオマス系の炭素質微粒子状材料が、ASTM D4373を用いて乾式燃焼により測定したとき50%~98%の範囲の有機炭素含有率を含む、請求項1~15のいずれか一項に記載の発泡イソシアネート系ポリマー。
- 前記バイオマス系の炭素質微粒子状材料が、ASTM D4373を用いて乾式燃焼により測定したとき75%~98%の範囲の有機炭素含有率を含む、請求項1~15のいずれか一項に記載の発泡イソシアネート系ポリマー。
- 前記バイオマス系の炭素質微粒子状材料が、ASTM D4373を用いて乾式燃焼により測定したとき85%~98%の範囲の有機炭素含有率を含む、請求項1~15のいずれか一項に記載の発泡イソシアネート系ポリマー。
- 前記バイオマス系の炭素質微粒子状材料が、ASTM D4373を用いて乾式燃焼により測定したとき0.10~0.85の範囲の水素対炭素のモル比を含む、請求項1~18のいずれか一項に記載の発泡イソシアネート系ポリマー。
- 前記バイオマス系の炭素質微粒子状材料が、ASTM D4373を用いて乾式燃焼により測定したとき0.35~0.85の範囲の水素対炭素のモル比を含む、請求項1~18のいずれか一項に記載の発泡イソシアネート系ポリマー。
- 前記バイオマス系の炭素質微粒子状材料が、ASTM D4373を用いて乾式燃焼により測定したとき0.70~0.85の範囲の水素対炭素のモル比を含む、請求項1~18のいずれか一項に記載の発泡イソシアネート系ポリマー。
- 前記バイオマス系の炭素質微粒子状材料が、BET法により測定したとき10~4,000m2/gの表面積を有する、請求項1~21のいずれか一項に記載の発泡イソシアネート系ポリマー。
- 前記バイオマス系の炭素質微粒子状材料が、BET法により測定したとき50~3,000m2/gの表面積を有する、請求項1~21のいずれか一項に記載の発泡イソシアネート系ポリマー。
- 前記バイオマス系の炭素質微粒子状材料が、BET法により測定したとき150~2,000m2/gの表面積を有する、請求項1~21のいずれか一項に記載の発泡イソシアネート系ポリマー。
- 前記ベースのポリオールが、ポリエーテル、ポリエステル、ポリカーボネート、ポリジエンおよびポリカプロラクトンからなる群から選択されるメンバーのヒドロキシルを末端基とする主鎖を含む、請求項1~24のいずれか一項に記載の発泡イソシアネート系ポリマー。
- 前記ベースのポリオールが、ヒドロキシルを末端基とするポリ炭化水素、ヒドロキシルを末端基とするポリホルマール、脂肪酸トリグリセリド、ヒドロキシルを末端基とするポリエステル、ヒドロキシメチルを末端基とするポリエステル、ヒドロキシメチルを末端基とするペルフルオロメチレン、ポリアルキレンエーテルグリコール、ポリアルキレンアリーレンエーテルグリコール、ポリアルキレンエーテルトリオールおよびこれらの混合物からなる群から選択される、請求項1~24のいずれか一項に記載の発泡イソシアネート系ポリマー。
- 前記ベースのポリオールが、アジピン酸-エチレングリコールポリエステル、ポリ(ブチレングリコール)、ポリ(プロピレングリコール)、ヒドロキシルを末端基とするポリブタジエンおよびこれらの混合物からなる群から選択される、請求項1~24のいずれか一項に記載の発泡イソシアネート系ポリマー。
- 前記ベースのポリオールがポリエーテルポリオールである、請求項1~24のいずれか一項に記載の発泡イソシアネート系ポリマー。
- 前記ポリエーテルポリオールが、200~10,000の範囲の分子量を有する、請求項28に記載の発泡イソシアネート系ポリマー。
- 前記ポリエーテルポリオールが、2,000~7,000の範囲の分子量を有する、請求項28に記載の発泡イソシアネート系ポリマー。
- 前記ポリエーテルポリオールが、2,000~6,000の範囲の分子量を有する、請求項28に記載の発泡イソシアネート系ポリマー。
- 前記反応混合物が、ポリアミン、ポリアルカノールアミンおよびこれらの任意の混合物からなる群から選択される活性水素含有化合物をさらに含む請求項28~31のいずれか一項に記載の発泡イソシアネート系ポリマー。
- 前記ポリアミンが、一級アミンを末端基とするポリエーテル、二級アミンを末端基とするポリエーテルおよびこれらの任意の混合物からなる群から選択される、請求項32に記載の発泡イソシアネート系ポリマー。
- 前記イソシアネートがプレポリマーを含む、請求項1~33のいずれか一項に記載の発泡イソシアネート系ポリマー。
- 前記イソシアネートが、1,6-ヘキサメチレンジイソシアネート、1,4-ブチレンジイソシアネート、フルフリリデンジイソシアネート、2,4-トルエンジイソシアネート、2,6-トルエンジイソシアネート、2,4’-ジフェニルメタンジイソシアネート、4,4’-ジフェニルメタンジイソシアネート、4,4’-ジフェニルプロパンジイソシアネート、4,4’-ジフェニル-3,3’-ジメチルメタンジイソシアネート、1,5-ナフタレンジイソシアネート、1-メチル-2,4-ジイソシアネート-5-クロロベンゼン、2,4-ジイソシアナト-s-トリアジン、1-メチル-2,4-ジイソシアナトシクロヘキサン、p-フェニレンジイソシアネート、m-フェニレンジイソシアネート、1,4-ナフタレンジイソシアネート、ジアニシジンジイソシアネート、ビトリレンジイソシアネート、1,4-キシリレンジイソシアネート、1,3-キシリレンジイソシアネート、ビス-(4-イソシアナトフェニル)メタン、ビス-(3-メチル-4-イソシアナトフェニル)メタン、ポリメチレンポリフェニルポリイソシアネートおよびこれらの混合物からなる群から選択される、請求項1~33のいずれか一項に記載の発泡イソシアネート系ポリマー。
- 前記イソシアネートが、2,4-トルエンジイソシアネート、2,6-トルエンジイソシアネートおよびこれらの混合物からなる群から選択される、請求項1~33のいずれか一項に記載の発泡イソシアネート系ポリマー。
- 前記イソシアネートが、(i)2,4’-ジフェニルメタンジイソシアネート、4,4’-ジフェニルメタンジイソシアネートおよびこれらの混合物;ならびに(ii)(i)と2,4-トルエンジイソシアネート、2,6-トルエンジイソシアネートおよびこれらの混合物からなる群から選択されるイソシアネートとの混合物から本質的になる群から選択される、請求項1~33のいずれか一項に記載の発泡イソシアネート系ポリマー。
- 前記発泡剤が水を含む、請求項1~37のいずれか一項に記載の発泡イソシアネート系ポリマー。
- 前記発泡剤が水からなる、請求項1~37のいずれか一項に記載の発泡イソシアネート系ポリマー。
- 前記水が、前記反応混合物中に使用されるベースのポリオール100重量部当たり0.5~40重量部の範囲の量で使用される、請求項38または39に記載の発泡イソシアネート系ポリマー。
- 前記水が、前記反応混合物中に使用されるベースのポリオール100重量部当たり1.0~10重量部の範囲の量で使用される、請求項38または39に記載の発泡イソシアネート系ポリマー。
- 前記発泡イソシアネート系ポリマーが成形される、請求項1~41のいずれか一項に記載の発泡イソシアネート系ポリマー。