JP7389631B2 - 摺動部材 - Google Patents
摺動部材 Download PDFInfo
- Publication number
- JP7389631B2 JP7389631B2 JP2019218761A JP2019218761A JP7389631B2 JP 7389631 B2 JP7389631 B2 JP 7389631B2 JP 2019218761 A JP2019218761 A JP 2019218761A JP 2019218761 A JP2019218761 A JP 2019218761A JP 7389631 B2 JP7389631 B2 JP 7389631B2
- Authority
- JP
- Japan
- Prior art keywords
- resin
- particles
- overlay layer
- solid lubricant
- resin binder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
前記樹脂オーバレイ層は、樹脂バインダと、前記樹脂バインダに分散する20体積%以上の異方性の形状の固体潤滑剤の粒子と、を有する。
前記摺動面と平行な仮想的な直線を0°、前記摺動面に垂直な仮想的な軸を90°、前記樹脂バインダの任意の観察領域に含まれる前記粒子の総数をN、分布のパラメータをaと定義し、
前記摺動面から前記軸までの0°~90°の範囲を、10°刻みであるA-10°<x≦A(A=10、20、30、・・・、90)の角度範囲に区分し、前記粒子の長軸の角度が前記角度範囲のいずれに含まれるか分類するとともに、前記角度範囲に含まれる前記粒子の数nをそれぞれカウントしたとき、
前記樹脂バインダに含まれる前記粒子の分布割合n/N(%)は、下記の式(1)で示される摺動部材。
この式(1)では、分布のパラメータaは、10≦a≦160であることが望ましく、25≦a≦80であることがより望ましい。
なお、式(1)において、左辺のn/N[%]は、百分率として換算した値を意味する。また、摺動面に平行な仮想的な直線から軸までの0°~90°の範囲は、10°刻みでA-10°<x≦A°(A=10、20、30、・・・、90)の角度範囲に区分される。すなわち、直線から軸までの範囲は、0°≦x≦10°、10°<x≦20°、20°<x≦30°、30°<x≦40°、40°<x≦50°、50°<x≦60°、60°<x≦70°、70°<x≦80°、80°<x≦90にそれぞれ分割される。この場合、A=10のときに限り、下限となるθ=0°は0°~10°の角度範囲に含むものとする。
図2に示すように摺動部材10は、裏金層11、軸受合金層12及び樹脂オーバレイ層13を備えている。なお、摺動部材10は、裏金層11と軸受合金層12との間に図示しない中間層を備えていてもよい。また、摺動部材10は、図2に示す例に限らず、裏金層11と樹脂オーバレイ層13との間に、複数の軸受合金層12や中間層、その他の機能を有する層を備えていてもよい。摺動部材10は、樹脂オーバレイ層13側の端部に相手部材と摺動する摺動面14を形成する。図2に示す本実施形態の場合、摺動部材10は、裏金層11の摺動面14側に軸受合金層12及び樹脂オーバレイ層13が順に積層されている。裏金層11は、例えば鉄や鋼などの金属又は合金で形成されている。軸受合金層12は、例えばAl若しくはCu又はそれらの合金などで形成されている。
図4に示すように裏金層11の一方の面側に軸受合金層12が形成されたバイメタル40は、円筒形状に成形される。この場合、バイメタル40は、裏金層11を円筒形状とした後、内周側に軸受合金層12を形成してもよい。また、バイメタル40は、円筒形状に限らず、半円筒形状又は円筒を周方向へ複数に分割した形状であってもよい。バイメタル40は、内周側である軸受合金層12と対向する位置にスプレー部41及び熱源42が配置される。スプレー部41は、ノズル43を有している。ノズル43は、樹脂オーバレイ層13を形成するための固体潤滑剤の粒子21を含む樹脂バインダ20を噴射する。また、熱源42は、噴射された樹脂バインダ20を乾燥するためにバイメタル40の内周側を加熱する。
上記の手順によって製造した摺動部材10の実施例及び比較例の試料は、図5に示す条件を用いて摩耗量から耐摩耗性を評価するとともに、摩擦係数を測定した。図5に示す試験条件において、回転数は、500rpmで一定ではなく、5秒ごとに0rpmと500rpmとを繰り返す「起動-停止」試験である。
Claims (2)
- 軸受合金層の摺動面側に樹脂オーバレイ層を備える摺動部材であって、
前記樹脂オーバレイ層は、
樹脂バインダと、
前記樹脂バインダに分散する20体積%以上の異方性の形状の固体潤滑剤の粒子と、を有し、
前記摺動面と平行な仮想的な直線を0°、前記摺動面に垂直な仮想的な軸を90°、前記樹脂バインダの任意の観察領域に含まれる前記粒子の総数をN、分布のパラメータをaと定義し、
前記摺動面から前記軸までの0°~90°の範囲を、10°刻みであるA-10°<x≦A(A=10、20、30、・・・、90)の角度範囲に区分し、前記粒子の長軸の角度が前記角度範囲のいずれに含まれるか分類するとともに、前記角度範囲に含まれる前記粒子の数nをそれぞれカウントしたとき、
前記樹脂バインダに含まれる前記粒子の分布割合n/N(%)は、下記の式(1)で示されるとともに、
前記分布のパラメータaは、10≦a≦160である、
摺動部材。
- 前記分布のパラメータaは、25≦a≦80である請求項1記載の摺動部材。