JP7380900B2 - 鋼の連続鋳造方法 - Google Patents
鋼の連続鋳造方法 Download PDFInfo
- Publication number
- JP7380900B2 JP7380900B2 JP2022551342A JP2022551342A JP7380900B2 JP 7380900 B2 JP7380900 B2 JP 7380900B2 JP 2022551342 A JP2022551342 A JP 2022551342A JP 2022551342 A JP2022551342 A JP 2022551342A JP 7380900 B2 JP7380900 B2 JP 7380900B2
- Authority
- JP
- Japan
- Prior art keywords
- mass
- molten steel
- sliding nozzle
- nozzle plate
- steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
炭素は、磁気時効を起こして鉄損を増加させる元素であり、特に、0.0050質量%を超えると、鉄損の増加が顕著となることから、0.0050質量%以下に制限する。好ましくは0.0030質量%以下である。尚、下限については、少ないほど好ましいので、特に規定しない。
珪素は、鋼の電気抵抗を高めて鉄損を低減するのに有効な元素である。特に、本発明では、珪素と同じ効果を有するアルミニウムを低減しているために、珪素を1.5質量%以上含有させる。しかし、珪素が5.0質量%を超えると、磁束密度が低下するだけでなく、鋼が脆化し、冷間圧延中に亀裂を生じるなど、製造性を大きく低下させる。よって、上限は5.0質量%とする。
マンガンは、珪素と同様、鋼の電気抵抗を高めて鉄損を低減するのに有効な元素である。一方、マンガンが3.0質量%を超えると、磁束密度が低下するので、上限は3.0質量%とする。より好ましくはマンガンを0.05質量%以上含有させる。
アルミニウムは、珪素と同様、鋼の電気抵抗を高めて鉄損を低減するのに有効な元素であるが、本発明においては、集合組織を改善し、磁束密度を高める目的から、アルミニウムを低減し、酸可溶アルミニウムで0.003質量%以下に制限する。下限については、少ないほど好ましいので、特に規定しない。
燐は、微量の含有量で鋼の硬さを高める効果が大きい有用な元素であり、要求される硬さに応じて適宜含有させる。しかし、燐の過剰な含有は、冷間圧延性の低下をもたらすので、燐の上限は0.2質量%とする。
硫黄は、硫化物となって介在物を形成し、製造性(熱間圧延性)や製品鋼板の磁気特性を低下させるので、少ないほど好ましい。そこで、本発明においては、上限は0.0050質量%まで許容されるが、磁気特性を重視する場合には、0.0025質量%以下とすることが好ましい。尚、硫黄は少ないほど好ましいので、下限は特に規定しない。
カルシウムは、CaSとなって粗大な硫化物を形成し、MnSなどの微細な硫化物の析出を抑制するので、結晶粒の成長を改善して鉄損を低減する効果がある。このため、全カルシウムは0.001質量%以上とする。一方で、全カルシウムが0.008質量%を超えると、カルシウムの硫化物や酸化物の量が増加して結晶粒の成長を阻害し、却って鉄損特性が低下する。したがって、全カルシウムの上限を0.0080質量%とする。
Claims (3)
- アルミニウムが無添加で、珪素で脱酸され、カルシウムが添加されてカルシウムを含有する溶鋼を連続鋳造して鋳片を製造する鋼の連続鋳造方法であって、
アルミナ-ジルコニア-カーボン質耐火物からなる第1のスライディングノズルプレートで構成されるスライディングノズルが設置された取鍋に前記溶鋼を収容し、
マグネシア-スピネル質耐火物からなる第2のスライディングノズルプレートで構成されるスライディングノズルが設置されたタンディッシュに、前記取鍋から前記溶鋼を注入し、
前記第2のスライディングノズルプレートの流出孔を流下する前記溶鋼中に不活性ガスを吹き込みながら前記タンディッシュから鋳型に前記溶鋼を注入して、前記溶鋼を連続鋳造し、
前記第1のスライディングノズルプレートは、成分組成で、Al 2 O 3 が70~81質量%、SiO 2 が10質量%以下、ZrO 2 が5~18質量%、固定炭素が3~10質量%であり、
前記第2のスライディングノズルプレートは、成分組成で、MgOが89~97質量%、Al 2 O 3 が4~7質量%であることを特徴とする、鋼の連続鋳造方法。 - 前記溶鋼は、成分組成で、珪素が1.5質量%以上、酸可溶アルミニウムが0.003質量%以下(ゼロを含む)、全カルシウムが0.001質量%以上であることを特徴とする、請求項1に記載の鋼の連続鋳造方法。
- 前記溶鋼は、成分組成で、炭素が0.0050質量%以下、珪素が1.5~5.0質量%、マンガンが3.0質量%以下、燐が0.2質量%以下、硫黄が0.0050質量%以下、酸可溶アルミニウムが0.003質量%以下(ゼロを含む)、全カルシウムが0.001~0.008質量%であることを特徴とする、請求項2に記載の鋼の連続鋳造方法。