JP7305379B2 - 金属3dプリンタによる溶着積層造形用の金属ワイヤ - Google Patents
金属3dプリンタによる溶着積層造形用の金属ワイヤ Download PDFInfo
- Publication number
- JP7305379B2 JP7305379B2 JP2019045695A JP2019045695A JP7305379B2 JP 7305379 B2 JP7305379 B2 JP 7305379B2 JP 2019045695 A JP2019045695 A JP 2019045695A JP 2019045695 A JP2019045695 A JP 2019045695A JP 7305379 B2 JP7305379 B2 JP 7305379B2
- Authority
- JP
- Japan
- Prior art keywords
- less
- metal
- welding
- metal wire
- additive manufacturing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
C:0.32%以下、
Si:2.5%以下、
Mn:5.0%以下、
S:0.0002~0.4%、
P:0.1%以下、
Ni:0.05~6.0%、
Cr:5.0~18.0%、
Mo、Wの1種又は2種を合計で0.05~5.0%、
N:0.1%以下、
O:0.03%以下、
Al:2.0%以下であり、残部Feおよび不可避的不純物からなる化学成分を有し、(a)式で表されるMs点が50℃以上で、且つ、(b)式で表されるAc1点が800℃以下であることを特徴とする金属3Dプリンタによる溶着積層造形用の金属ワイヤ。
Ms(℃)=600-600C-600N-13Mn-30Ni-12Cr-54Cu-46Mo・・(a)
Ac1(℃)=700-70Ni-25Mn+10Cr+25Si+30Al ・・・(b)
上記式中の元素記号は、当該元素の含有量(質量%)を意味する。
(2)更に質量%で、
Cu:5.0%以下、
Co:5.0%以下、
B:1.0%以下の内、1種類以上を含有することを特徴とする前記(1)に記載の金属3Dプリンタによる溶着積層造形用の金属ワイヤ。
(3)更に質量%で、
Sn:0.5%以下、
Sb:0.5%以下、
Au:0.5%以下、
In:0.5%以下の内、1種類以上を含有することを特徴とする前記(1)または(2)に記載の金属3Dプリンタによる溶着積層造形用の金属ワイヤ。
(4)更に質量%で、
Mg:0.003%以下、
Ca:0.002%以下、
Hf:0.008%以下、
REM:0.004%以下の内、1種類以上を含有することを特徴とする(1)~(3)のいずれか1つに記載の金属3Dプリンタによる溶着積層造形用の金属ワイヤ。
(5)更に質量%で、
Ti:2.0%以下、
Nb:2.0%以下、
V:2.0%以下、
Ta:2.0%以下、
Zr:2.0%以下の内、1種類以上を含有することを特徴とする(1)~(4)のいずれか1つに記載の金属3Dプリンタによる溶着積層造形用の金属ワイヤ。
(6)更に質量%で、
Bi:0.4%以下、
Pb:0.4%以下、
Ag:0.4%以下、
Se:0.4%以下、
Te:0.4%以下、
Zn:0.1%以下の内、1種類以上を含有することを特徴とする(1)~(5)のいずれか1つに記載の金属3Dプリンタによる溶着積層造形用の金属ワイヤ。
C、Nは、内部割れを抑制し、材質均一性を確保するためにCは0.35%以下、Nは0.1%以下に限定する。Cが0.35%を超え、あるいはNが0.1%を超えると、繰り返しの溶着、加熱、冷却工程で内部割れが発生し易く、また、炭窒化物系析出物を析出促進させ硬さや金属組織がばらつき、鋭敏化により耐食性も劣化する。好ましくは、Cは0.20%以下、Nは0.05%以下である。更に、好ましくは、Cは0.08%以下、Nは0.03%以下である。C、Nは低いほど好ましく、下限を設けない。
Cu、Co、Bは、マトリックスの靭性を向上させるため、必要に応じて添加してもよい。しかしながら、CuやCoがそれぞれ5.0%を超えて含有すると、繰り返しの溶着、加熱、冷却工程でマルテンサイト組織が安定的に得られず、材質均一性が劣化する。そのため、CuやCoの上限を5.0%にする。また、Bが1.0%を超えて含有すると内部割れが発生し易くなる。そのため、Bの上限を1.0%に限定する。好ましくは、Cu:4.0%以下、Co:4.0%以下、B:0.3%以下である。
代表的な不可避的不純物としては、Ge,Na、Be、F、Ga等が挙げられ、通常、鉄鋼の製造プロセスで不可避的不純物として、0.01%以下の範囲で混入する場合がある。
また、任意添加元素について、代表的なものを上記(2)~(6)で規定しているが、本明細書中に記載されていない元素であっても、本発明の効果を損なわない範囲で含有させることができる。
金属組織の均一性について、耐食性(耐久性)に悪影響を及ぼす炭窒化物および鋭敏化の存在を確認するため、前記埋め込み・研磨した試料について、JIS G 0571のエッチテストを行った。溝状組織が認められない場合を〇、溝状組織が認められる場合を×として評価した。
本発明の金属ワイヤを使用した場合、材料均一性、金属組織の均一性はともに評価結果は〇であり、材質・金属組織の均一性に優れていた。
2 積層方向
10 金属部品
Claims (6)
- 質量%で、
C:0.32%以下、
Si:2.5%以下、
Mn:5.0%以下、
S:0.0002~0.4%、
P:0.1%以下、
Ni:0.05~6.0%、
Cr:5.0~18.0%、
Mo、Wの1種又は2種を合計で0.05~5.0%、
N:0.1%以下、
O:0.03%以下、
Al:2.0%以下
であり、残部Feおよび不可避的不純物からなる化学成分を有し、(a)式で表されるMs点が50℃以上で、且つ、(b)式で表されるAc1点が800℃以下であることを特徴とする金属3Dプリンタによる溶着積層造形用の金属ワイヤ。
Ms(℃)=600-600C-600N-13Mn-30Ni-12Cr-54Cu-46Mo ・・・(a)
Ac1(℃)=700-70Ni-25Mn+10Cr+25Si+30Al ・・・(b)
上記式中の元素記号は、当該元素の含有量(質量%)を意味する。 - 更に質量%で、
Cu:5.0%以下、
Co:5.0%以下、
B:1.0%以下の内、1種類以上を含有することを特徴とする請求項1に記載の金属3Dプリンタによる溶着積層造形用の金属ワイヤ。 - 更に質量%で、
Sn:0.5%以下、
Sb:0.5%以下、
Au:0.5%以下、
In:0.5%以下の内、1種類以上を含有することを特徴とする請求項1または請求項2に記載の金属3Dプリンタによる溶着積層造形用の金属ワイヤ。 - 更に質量%で、
Mg:0.003%以下、
Ca:0.002%以下、
Hf:0.008%以下、
REM:0.004%以下の内、1種類以上を含有することを特徴とする請求項1~請求項3のいずれか1項に記載の金属3Dプリンタによる溶着積層造形用の金属ワイヤ。 - 更に質量%で、
Ti:2.0%以下、
Nb:2.0%以下、
V:2.0%以下、
Ta:2.0%以下、
Zr:2.0%以下の内、1種類以上を含有することを特徴とする請求項1~請求項4のいずれか1項に記載の金属3Dプリンタによる溶着積層造形用の金属ワイヤ。 - 更に質量%で、
Bi:0.4%以下、
Pb:0.4%以下、
Ag:0.4%以下、
Se:0.4%以下、
Te:0.4%以下、
Zn:0.1%以下の内、1種類以上を含有することを特徴とする請求項1~請求項5のいずれか1項に記載の金属3Dプリンタによる溶着積層造形用の金属ワイヤ。