JP7144953B2 - disposable diaper - Google Patents
disposable diaper Download PDFInfo
- Publication number
- JP7144953B2 JP7144953B2 JP2018053989A JP2018053989A JP7144953B2 JP 7144953 B2 JP7144953 B2 JP 7144953B2 JP 2018053989 A JP2018053989 A JP 2018053989A JP 2018053989 A JP2018053989 A JP 2018053989A JP 7144953 B2 JP7144953 B2 JP 7144953B2
- Authority
- JP
- Japan
- Prior art keywords
- sheet
- hot
- melt adhesive
- disposable diaper
- reactive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、使い捨ておむつに関し、特に使い捨ておむつを構成する部材の接合技術に関する。 TECHNICAL FIELD The present invention relates to a disposable diaper, and more particularly to a technology for joining members constituting a disposable diaper.
使い捨ておむつの組立には、ホットメルト接着剤が使用されている。例えば、ホットメルト接着剤は、バックシートと吸収コアとを接合する、あるいは、トップシートとバックシートとを接合する箇所に使用されている（例えば、特許文献１）。 Hot melt adhesives are used in the assembly of disposable diapers. For example, hot-melt adhesives are used where the backsheet and absorbent core are joined, or where the topsheet and backsheet are joined (for example, Patent Document 1).
使い捨ておむつを着用する着用者からの***液を吸収した吸収コアは膨潤して厚みが厚くなる。吸収コアの膨潤は、吸収コア周囲の接合部を剥離するように作用する。また、使い捨ておむつに着用者の荷重がかかると、一旦吸収されていた***液が、吸収コアから絞り出される場合がある。吸収コアの周囲の接合部が、この***液に曝されると、剥離しやすくなるという問題がある。さらに、この絞り出された***液には、着用者の体重による圧力が負荷される場合もある。加圧された***液は、吸収コア周囲の接合部の剥離を促進する。特に、使い捨ておむつの着用者が暖房器具（電気毛布、こたつ等）を使用すると、吸収コア周囲の接合部が温められる。そのため、吸収コア周囲の接合に使用されているホットメルト接着剤が軟化して、***液が漏れやすくなるという問題がある。 The absorbent core that has absorbed excrement from the wearer of the disposable diaper swells and becomes thicker. The swelling of the absorbent core acts to delaminate the joints around the absorbent core. In addition, when the wearer's load is applied to the disposable diaper, excretions once absorbed may be squeezed out from the absorbent core. There is a problem that when the joint part around the absorbent core is exposed to this excreted fluid, it tends to peel off. Furthermore, the squeezed excrement may be pressured by the weight of the wearer. The pressurized exudate promotes detachment of the joints around the absorbent core. In particular, when a wearer of disposable diapers uses a heater (electric blanket, kotatsu, etc.), the joints around the absorbent core are warmed. As a result, there is a problem that the hot-melt adhesive used for bonding around the absorbent core softens, making it easier for excrement to leak.
本発明者らは、吸収コアの膨潤が吸収コア周囲の接合部を剥離するように作用する原因を検討した結果、吸収コア周囲の接合部に使用されるホットメルト接着剤が、吸収コアの膨潤に伴って変形せず、吸収コアの厚みの増大が、接合部を剥離するように作用していることを見出した。また、従来使用されているゴム系ホットメルト接着剤あるいはオレフィン系ホットメルト接着剤は、使い捨ておむつを構成する材料に対する反応性がなく、使い捨ておむつを構成する材料との界面接着強度が低い。そのため、吸収コア周囲の接合部が、排出液に曝された場合に、接合部に使用されているホットメルト接着剤が、おむつを構成する材料から剥離しやすくなることを見出した。 The inventors of the present invention have investigated the reason why the swelling of the absorbent core acts to separate the joints around the absorbent core. It was found that the increase in the thickness of the absorbent core acted to separate the joints without deforming along with the deformation. In addition, conventionally used rubber-based hot-melt adhesives or olefin-based hot-melt adhesives have no reactivity with materials constituting disposable diapers, and have low interfacial adhesive strength with materials constituting disposable diapers. Therefore, the inventors have found that when the joints around the absorbent core are exposed to the discharged liquid, the hot-melt adhesive used in the joints is easily peeled off from the materials constituting the diaper.
本発明は、前記課題に鑑みてなされたものであり、吸収コアと、吸収コアの肌面側に設けられた表面シートと、吸収コアの外面側に設けられた外装シートとを有する使い捨ておむつであって、吸収コアの周囲に設けられた接合部の接着強度を高めることを課題とする。また、使い捨ておむつの使用者が暖房器具を使用した場合でも、吸収コアの周囲に設けられた接合部の接着強度が高い使い捨ておむつを提供することをさらなる課題とする。 The present invention has been made in view of the above problems, and is a disposable diaper having an absorbent core, a surface sheet provided on the skin surface side of the absorbent core, and an outer sheet provided on the outer surface side of the absorbent core. Therefore, an object of the present invention is to increase the adhesive strength of the joint provided around the absorbent core. Another object of the present invention is to provide a disposable diaper in which the bonding strength of the joints provided around the absorbent core is high even when the user of the disposable diaper uses a heater.
本発明の使い捨ておむつは、吸収コアと、吸収コアの肌面側に設けられた表面シートと、吸収コアの外面側に設けられた外装シートとを有する使い捨ておむつであって、前記使い捨ておむつの縦方向両端部および幅方向両側部の少なくとも一箇所において、前記表面シートと外装シートとが、反応性ウレタンホットメルト接着剤の硬化物により接合されている接合部が設けられていることを特徴とする。 A disposable diaper of the present invention is a disposable diaper having an absorbent core, a surface sheet provided on the skin surface side of the absorbent core, and an outer sheet provided on the outer surface side of the absorbent core. In at least one of both ends in the direction and both sides in the width direction, joints are provided in which the surface sheet and the exterior sheet are joined by a cured product of a reactive urethane hot-melt adhesive. .
本発明で使用する反応性ウレタンホットメルト接着剤は、荷重に対する変形量が大きい。そのため、吸収コアの膨潤による変形に伴い、反応性ウレタンホットメルト接着剤の硬化物も変形しやすく、吸収コアの膨潤による変形が、接合部を剥離するように作用するのを抑制できる。また、反応性ウレタンホットメルト接着剤を使用することにより、接着強度が向上する理由は、明確ではないが、反応性ウレタンホットメルト接着剤が、使い捨ておむつを構成する材料が有する官能基（例えば、ヒドロキシル基、カルボキシル基など）と反応して、反応性ウレタンホットメルト接着剤の硬化物と、使い捨ておむつを構成する材料との間に化学結合が生成する。その結果、界面での接着力が向上するもの考えられる。また、本発明で使用する反応性ウレタンホットメルト接着剤の硬化物は、三次元架橋構造を有しているので、耐熱接着強度が高い。 The reactive urethane hot-melt adhesive used in the present invention has a large amount of deformation against load. Therefore, the cured product of the reactive urethane hot-melt adhesive is easily deformed with the deformation due to the swelling of the absorbent core, so that the deformation due to the swelling of the absorbent core can be suppressed from peeling off the joints. Also, the reason why the adhesive strength is improved by using a reactive urethane hot-melt adhesive is not clear, but the reactive urethane hot-melt adhesive has a functional group (for example, hydroxyl group, carboxyl group, etc.) to form a chemical bond between the cured reactive urethane hot-melt adhesive and the materials that make up the disposable diaper. As a result, it is conceivable that the adhesive force at the interface is improved. Moreover, since the cured product of the reactive urethane hot-melt adhesive used in the present invention has a three-dimensional crosslinked structure, it has high heat-resistant adhesive strength.
前記使い捨ておむつは、縦方向両端部において、少なくとも吸収コアが設置されている幅に渡って、表面シートと外装シートとが、反応性ウレタンホットメルト接着剤の硬化物により接合されている接合部が設けられていることが好ましい。 The disposable diaper has joints at both ends in the longitudinal direction where the surface sheet and the exterior sheet are joined by a cured reactive urethane hot-melt adhesive over at least the width where the absorbent core is installed. is preferably provided.
前記使い捨ておむつは、使い捨ておむつの幅方向両側部において、少なくとも吸収コアが設置されている長さに渡って、表面シートと外装シートとが、反応性ウレタンホットメルト接着剤の硬化物により接合されている接合部が設けられていることが好ましい。 In the disposable diaper, the surface sheet and the exterior sheet are joined by a cured reactive urethane hot-melt adhesive over at least the length where the absorbent core is installed on both sides in the width direction of the disposable diaper. Preferably, a joint is provided.
前記表面シートは、トップシートであり、前記外装シートは、バックシートであることが好ましい。 It is preferable that the surface sheet is a top sheet and the exterior sheet is a back sheet.
前記表面シートは、トップシートと前記トップシートの幅方向両側部に設けられたサイドシートからなる積層シートであり、前記外装シートは、バックシートであり、前記使い捨ておむつの幅方向両側部において、サイドシートとバックシートとが、反応性ウレタンホットメルト接着剤の硬化物により接合されている接合部が設けられていることが好ましい。 The surface sheet is a laminated sheet made up of a top sheet and side sheets provided on both sides in the width direction of the top sheet. It is preferable that a joint portion is provided in which the sheet and the back sheet are joined by a cured product of a reactive urethane hot-melt adhesive.
接合部における反応性ウレタンホットメルト接着剤の硬化物の塗布量は、５ｇ／ｍ２～３０ｇ／ｍ２であることが好ましい。 The amount of the cured reactive urethane hot-melt adhesive applied to the joint is preferably 5 g/m 2 to 30 g/m 2 .
本発明によれば、吸収コアと、吸収コアの肌面側に設けられた表面シートと、吸収コアの外面側に設けられた外装シートとを有する使い捨ておむつであって、吸収コアの周囲に設けられた接合部の接着強度が高められた使い捨ておむつが得られる。また、吸収コアから絞り出された***液に対して優れた接着強度を有する使い捨ておむつが得られる。 According to the present invention, there is provided a disposable diaper having an absorbent core, a surface sheet provided on the skin surface side of the absorbent core, and an outer sheet provided on the outer surface side of the absorbent core. A disposable diaper is obtained in which the bonding strength of the joined portion is enhanced. In addition, a disposable diaper can be obtained which has excellent adhesion strength to excrement squeezed out from the absorbent core.
本発明の使い捨ておむつは、吸収コアと、吸収コアの肌面側に設けられた表面シートと、吸収コアの外面側に設けられた外装シートとを有する使い捨ておむつであって、前記使い捨ておむつの縦方向両端部および幅方向両側部の少なくとも一箇所において、前記表面シートと外装シートとが、反応性ウレタンホットメルト接着剤の硬化物により接合されている接合部（以下、「反応性ウレタンホットメルト接合部」という場合がある）が設けられていることを特徴とする。 A disposable diaper of the present invention is a disposable diaper having an absorbent core, a surface sheet provided on the skin surface side of the absorbent core, and an outer sheet provided on the outer surface side of the absorbent core. Joints in which the surface sheet and the exterior sheet are joined by a cured product of a reactive urethane hot-melt adhesive (hereinafter referred to as "reactive urethane hot-melt joint (sometimes referred to as "part") is provided.
（反応性ウレタンホットメルト接着剤）
まず、本発明で使用する反応性ウレタンホットメルト接着剤について説明する。反応性ウレタンホットメルト接着剤は、湿気硬化型接着剤であり、空気中の水分と反応することで、三次元架橋を形成して硬化する。反応性ウレタンホットメルト接着剤の硬化物は、三次元架橋構造を有し、耐熱性に非常に優れている。また、反応性ウレタンホットメルト接着剤は、従来のホットメルト接着剤と同様に溶融状態で塗布することができ、かつ、冷却固化させることで被接着物を仮接合できる。よって、反応性ウレタンホットメルト接着剤を使用すれば、従来の製造設備を使用することができ、かつ、生産性の低下も抑制できる。前記反応性ウレタンホットメルト接着剤は、分子鎖の末端にイソシアネート基を有するウレタンプレポリマーを含有することが好ましい。
(reactive urethane hot melt adhesive)
First, the reactive urethane hot-melt adhesive used in the present invention will be explained. A reactive urethane hot-melt adhesive is a moisture-curing adhesive that reacts with moisture in the air to form three-dimensional crosslinks and cure. A cured product of a reactive urethane hot-melt adhesive has a three-dimensional crosslinked structure and is extremely excellent in heat resistance. In addition, the reactive urethane hot melt adhesive can be applied in a molten state in the same manner as conventional hot melt adhesives, and can be temporarily bonded to adherends by cooling and solidifying. Therefore, by using a reactive urethane hot-melt adhesive, it is possible to use conventional manufacturing equipment and to suppress a decrease in productivity. The reactive urethane hot-melt adhesive preferably contains a urethane prepolymer having an isocyanate group at the terminal of the molecular chain.
前記ウレタンプレポリマーは、ポリオールとポリイソシアネートとを、イソシアネート基が過剰になるような条件で反応させて得られたものであることが好ましい。 The urethane prepolymer is preferably obtained by reacting a polyol and a polyisocyanate under conditions in which isocyanate groups are excessive.
前記ポリオールとしては、特に限定されないが、例えば、ポリエーテルポリオール、ポリエステルポリオール、ポリカーボネートポリオール、ポリカプロラクトンなどが挙げられる。また、トリメチロールプロパンなどのトリオールを挙げることができる。 Examples of the polyol include, but are not particularly limited to, polyether polyol, polyester polyol, polycarbonate polyol, polycaprolactone, and the like. Mention may also be made of triols such as trimethylolpropane.
前記ポリイソシアネートは、分子中に少なくとも２つのイソシアネート基を有する化合物である。前記ポリイソシアネートとしては、ジフェニルメタンジイソシアネート、ジメチルジフェニルメタンジイソシアネート、トリレンジイソシアネート、フェニレンジイソシアネートなどの黄変タイプジイソシアネート；および、ヘキサメチレンジイソシアネート、ジシクロヘキシルメタンジイソシアネート、キシリレンジイソシアネート、イソホロンジイソシアネートなどの無黄変ジイソシアネート或いは難黄変ジイソシアネートを挙げることができる。本発明で使用する反応性ウレタンホットメルト接着剤は、ポリイソシアネート成分として、無黄変ジイソシアネート或いは難黄変ジイソシアネートを含有することが好ましい。 Said polyisocyanate is a compound having at least two isocyanate groups in the molecule. Examples of the polyisocyanate include yellowing type diisocyanates such as diphenylmethane diisocyanate, dimethyldiphenylmethane diisocyanate, tolylene diisocyanate and phenylene diisocyanate; Mention may be made of yellowing diisocyanates. The reactive urethane hot-melt adhesive used in the present invention preferably contains a non-yellowing diisocyanate or a non-yellowing diisocyanate as a polyisocyanate component.
本発明で使用する反応性ウレタンホットメルト接着剤のイソシアネート基の含有率は、１質量％以上が好ましく、より好ましくは３質量％以上、さらに好ましくは５質量％以上であり、２５質量％以下が好ましく、より好ましくは２３質量％以下、さらに好ましくは２１質量％以下である。前記イソシアネート基の含有率が１質量％以上であれば、湿気硬化性が発現しやすくなり、２５質量％以下であれば、硬化後の接着強度が良好となる。 The isocyanate group content of the reactive urethane hot-melt adhesive used in the present invention is preferably 1% by mass or more, more preferably 3% by mass or more, still more preferably 5% by mass or more, and 25% by mass or less. It is preferably 23% by mass or less, more preferably 21% by mass or less. When the isocyanate group content is 1% by mass or more, moisture curability is easily exhibited, and when the content is 25% by mass or less, adhesive strength after curing is improved.
前記反応性ウレタンホットメルト接着剤の溶融粘度は、１２０℃で、２，０００ｍＰａ・ｓ以上が好ましく、４，０００ｍＰａ・ｓ以上がより好ましく、６，０００ｍＰａ・ｓ以上がさらに好ましく、２０，０００ｍＰａ・ｓ以下が好ましく、１５，０００ｍＰａ・ｓ以下がより好ましく、１０，０００ｍＰａ・ｓ以下がさらに好ましい。前記反応性ウレタンホットメルト接着剤の溶融粘度が、前記範囲内であれば、反応性ウレタンホットメルトの塗工性が良好である。 The melt viscosity of the reactive urethane hot-melt adhesive at 120° C. is preferably 2,000 mPa·s or more, more preferably 4,000 mPa·s or more, further preferably 6,000 mPa·s or more, further preferably 20,000 mPa·s. s or less, preferably 15,000 mPa·s or less, and even more preferably 10,000 mPa·s or less. When the melt viscosity of the reactive urethane hot-melt adhesive is within the above range, the reactive urethane hot-melt has good coatability.
本発明で使用する反応性ウレタンホットメルト接着剤のオープンタイムは、１０秒以上であることが好ましく、１５秒以上であることがより好ましく、２０秒以上であることがさらに好ましく、６０秒以下であることが好ましく、５０秒以下であることがより好ましく、４０秒以下であることがさらに好ましい。反応性ウレタンホットメルト接着剤のオープンタイムが前記範囲内であれば、接合部の接着強度が向上しやすくなるからである。 The open time of the reactive urethane hot melt adhesive used in the present invention is preferably 10 seconds or longer, more preferably 15 seconds or longer, still more preferably 20 seconds or longer, and 60 seconds or shorter. It is preferably 50 seconds or less, more preferably 40 seconds or less. This is because if the open time of the reactive urethane hot-melt adhesive is within the above range, the adhesive strength of the joint is likely to be improved.
本発明の反応性ウレタンホットメルト接合部において、表面シートと外装シートは、反応性ウレタンホットメルト接着剤の硬化物のみによって接合されることが好ましいが、反応性ウレタンホットメルト接着剤の硬化物と非反応性ホットメルト接着剤とによって接合されていてもよい。 In the reactive urethane hot-melt joint of the present invention, the surface sheet and the exterior sheet are preferably joined only by the cured product of the reactive urethane hot-melt adhesive. It may be joined with a non-reactive hot-melt adhesive.
前記非反応性ホットメルト接着剤は、加熱により軟化あるいは溶融した状態で、被着対象物に塗布され、常温に冷却・固化することにより接着力を発現する。非反応性ホットメルト接着剤としては、例えば、ゴム系ホットメルト接着剤、オレフィン系ホットメルト接着剤、ポリアミド系ホットメルト接着剤、ポリエステル系ホットメルト接着剤などを挙げることができる。 The non-reactive hot-melt adhesive is applied to an object to be adhered in a state of being softened or melted by heating, and develops adhesive strength by cooling to room temperature and solidifying. Examples of non-reactive hot-melt adhesives include rubber-based hot-melt adhesives, olefin-based hot-melt adhesives, polyamide-based hot-melt adhesives, and polyester-based hot-melt adhesives.
ゴム系ホットメルト接着剤は、ベースポリマーとして、合成ゴムを含有することが好ましく、スチレンブロックコポリマーを含有することがより好ましい。前記合成ゴムとしては、例えば、スチレン－アクリロニトリル、アクリロニトリル－ブタジエン－スチレン、スチレン－ブタジエンゴム、ブタジエン－スチレンエラストマー、スチレン－イソプレン（SI）、スチレン－イソプレン－スチレン（SIS）、スチレン－ブタジエン－スチレン（SBS）、スチレン－エチレン／ブチレン－スチレン（SEBS）、および、スチレン－エチレン／プロピレン－スチレン（SEPS）よりなる群から選択される少なくとも１種を挙げることができる。これらの中でも、合成ゴムとしては、スチレン－イソプレン（SI）、スチレン－イソプレン－スチレン（SIS）、スチレン－ブタジエン－スチレン（SBS）、スチレン－エチレン／ブチレン－スチレン（SEBS）、および、スチレン－エチレン／プロピレン－スチレン（SEPS）よりなる群から選択される少なくとも１種が好ましい。前記スチレンブロックコポリマーは、直鎖状分子構造、あるいは、放射状の分子構造を有することができる。 The rubber-based hot-melt adhesive preferably contains a synthetic rubber, more preferably a styrene block copolymer, as a base polymer. Examples of the synthetic rubber include styrene-acrylonitrile, acrylonitrile-butadiene-styrene, styrene-butadiene rubber, butadiene-styrene elastomer, styrene-isoprene (SI), styrene-isoprene-styrene (SIS), styrene-butadiene-styrene ( SBS), styrene-ethylene/butylene-styrene (SEBS), and at least one selected from the group consisting of styrene-ethylene/propylene-styrene (SEPS). Among these, synthetic rubbers include styrene-isoprene (SI), styrene-isoprene-styrene (SIS), styrene-butadiene-styrene (SBS), styrene-ethylene/butylene-styrene (SEBS), and styrene-ethylene /propylene-styrene (SEPS). The styrene block copolymer can have a linear molecular structure or a radial molecular structure.
オレフィン系ホットメルト接着剤は、オレフィン系ポリマーを含有することが好ましい。前記オレフィン系ポリマーとしては、例えば、ポリオレフィン、ポリオレフィンコポリマー、オレフィン／α－オレフィンインターポリマーを挙げることができる。前記オレフィン系ポリマーとしては、非晶質、半結晶性、または、結晶性のものを挙げることができ、例えば、非晶質（アモルファス）ポリオレフィンを好適に使用できる。 The olefinic hot melt adhesive preferably contains an olefinic polymer. Examples of the olefin-based polymer include polyolefins, polyolefin copolymers, and olefin/α-olefin interpolymers. Examples of the olefin-based polymer include amorphous, semi-crystalline, and crystalline polymers. For example, amorphous polyolefin can be preferably used.
オレフィン系ポリマーとしては、例えば、エチレン／酢酸ビニル（ＥＶＡ）、エチレン／アクリレート、エチレン／メタクリレート、エチレン／ｎ－ブチルアクリレート、エチレン／ｎ－ヘキシルアクリレート、エチレン／プロピレン、エチレン／ブテン、エチレン／オクテン、ポリプロピレンなどが挙げられる。前記オレフィン系ポリマーは、単独で、あるいは、２種以上を組み合わせて使用してもよい。 Examples of olefinic polymers include ethylene/vinyl acetate (EVA), ethylene/acrylate, ethylene/methacrylate, ethylene/n-butyl acrylate, ethylene/n-hexyl acrylate, ethylene/propylene, ethylene/butene, ethylene/octene, Polypropylene etc. are mentioned. The olefinic polymer may be used alone or in combination of two or more.
前記反応性ウレタンホットメルト接着剤および非反応性ホットメルト接着剤は、粘着付与剤、可塑剤、ワックスなどを含有することができる。 The reactive urethane hot melt adhesives and non-reactive hot melt adhesives can contain tackifiers, plasticizers, waxes, and the like.
前記粘着付与剤としては、例えば、ガムロジン、ウッドロジン、トール油ロジン、蒸留ロジン、水素化ロジン、二量化ロジン、および重合化ロジンなどを挙げることができる。 Examples of the tackifier include gum rosin, wood rosin, tall oil rosin, distilled rosin, hydrogenated rosin, dimerized rosin, and polymerized rosin.
前記可塑剤としては、例えば、ナフテン系油、パラフィン系油（例えば、シクロパラフィン油）、鉱物系油、フタル酸エステル、アジピン酸エステル、オレフィンオリゴマー（例えば、ポリプロピレン、ポリブテン及び水素化ポリイソプレンのオリゴマー）、ポリブテン、ポリイソプレン、水素化ポリイソプレン、ポリブタジエン、安息香酸エステル、動物油、植物油（例えば、ヒマシ油、大豆油）、油の誘導体、脂肪酸のグリセロールエステル、ポリエステル、ポリエーテル、などを挙げることができる。 Examples of the plasticizer include naphthenic oils, paraffinic oils (e.g., cycloparaffinic oils), mineral oils, phthalate esters, adipate esters, olefin oligomers (e.g., oligomers of polypropylene, polybutene and hydrogenated polyisoprene). ), polybutene, polyisoprene, hydrogenated polyisoprene, polybutadiene, benzoic acid esters, animal oils, vegetable oils (e.g., castor oil, soybean oil), oil derivatives, glycerol esters of fatty acids, polyesters, polyethers, etc. can.
前記ワックスとしては、例えば、パラフィンワックス、微結晶性ワックス、ポリエチレンワックス、ポリプロピレンワックス、副生成物ポリエチレンワックス、フィッシャー－トロプシュワックス、酸化フィッシャー－トロプシュワックス、ならびにヒドロキシステアラミドワックスおよび脂肪アミドワックスなどの官能基化ワックスなどを挙げることができる。 Said waxes include, for example, paraffin waxes, microcrystalline waxes, polyethylene waxes, polypropylene waxes, by-product polyethylene waxes, Fischer-Tropsch waxes, oxidized Fischer-Tropsch waxes, and functionalized waxes such as hydroxystearamide waxes and fatty amide waxes. Base wax etc. can be mentioned.
前記反応性ウレタンホットメルト接着剤および非反応性ホットメルト接着剤は、さらに、安定剤、抗酸化剤、顔料、染料、紫外線吸収剤などの添加剤を含むことができる。 The reactive urethane hot-melt adhesives and non-reactive hot-melt adhesives may further contain additives such as stabilizers, antioxidants, pigments, dyes, and UV absorbers.
（使い捨ておむつ）
本発明の使い捨ておむつは、吸収コアと、吸収コアの肌面側に設けられた表面シートと、吸収コアの外面側に設けられた外装シートとを有する。
(disposable diaper)
The disposable diaper of the present invention has an absorbent core, a surface sheet provided on the skin surface side of the absorbent core, and an exterior sheet provided on the outer surface side of the absorbent core.
前記使い捨ておむつは、液体を吸収する吸収コアを有し、着用者にあてがわれる。前記使い捨ておむつは、前方部、股部、後方部を有する。前記前方部が着用者の腹側、前記後方部が着用者の背側、前記股部が着用者の股下にそれぞれあてがわれる。なお、本発明の使い捨ておむつにおいて、着用時に着用者の肌に対向する側が肌面側であり、この肌側の裏面が外面側である。 The disposable diaper has an absorbent core that absorbs liquid and is applied to the wearer. The disposable diaper has a front portion, a crotch portion and a rear portion. The front portion is applied to the abdomen of the wearer, the rear portion is applied to the back of the wearer, and the crotch portion is applied to the crotch of the wearer. In addition, in the disposable diaper of the present invention, the side facing the wearer's skin when worn is the skin surface side, and the back surface of the skin side is the outer surface side.
本発明の使い捨ておむつは、液体を吸収する吸収コアを有する。吸収コアは、着用者が***した***液（例えば、尿、便に含まれる水分）を吸収し、保持する。具体的には、吸収コアは、吸水性樹脂粉末および／または吸水性繊維を含有する。前記吸水性樹脂粉末としては、従来吸収性物品に使用されているものを使用できる。前記吸水性樹脂粉末としては、例えば、ポリアクリル酸塩系、ポリスルホン酸塩系、無水マレイン酸塩系、ポリアクリルアミド系、ポリビニルアルコール系、ポリエチレンオキシド系などの合成ポリマー系の吸水性樹脂粉末；および、ポリグルタミン酸系、ポリアルギン酸系、デンプン系、セルロース系などの天然物由来の吸水性樹脂粉末が挙げられる。前記吸水性繊維としては、パルプ繊維、セルロース繊維、レーヨン、アセテート繊維などが挙げられる。前記吸収コアの平面視形状は特に限定されず、例えば、長方形型、砂時計型、ひょうたん型、羽子板型などが挙げられる。 Disposable diapers of the present invention have an absorbent core that absorbs liquids. The absorbent core absorbs and retains excretory fluids excreted by the wearer (for example, water contained in urine and feces). Specifically, the absorbent core contains water-absorbing resin powder and/or water-absorbing fibers. As the water absorbent resin powder, those conventionally used in absorbent articles can be used. Examples of the water-absorbent resin powder include synthetic polymer-based water-absorbent resin powders such as polyacrylate, polysulfonate, maleic anhydride, polyacrylamide, polyvinyl alcohol, and polyethylene oxide; and , polyglutamic acid-based, polyalginic acid-based, starch-based, and cellulose-based water absorbent resin powders derived from natural products. Examples of the water-absorbing fibers include pulp fibers, cellulose fibers, rayon, and acetate fibers. The planar view shape of the absorbent core is not particularly limited, and examples thereof include a rectangular shape, an hourglass shape, a gourd shape, and a battledore shape.
本発明の使い捨ておむつは、前記吸収コアの肌面側に配置された表面シート、および、前記吸収コアの外面側に配置された外装シートを有する。 The disposable diaper of the present invention has a surface sheet arranged on the skin surface side of the absorbent core and an exterior sheet arranged on the outer surface side of the absorbent core.
表面シートは、吸収コアの肌面側に設置され、使い捨ておむつの表面を構成するシートである。表面シートは、例えば、トップシートのみからなってもよいし、あるいは、トップシートとトップシートの幅方向両側部に設けられる一対のサイドシートとからなる積層シートであってもよい。トップシートおよびサイドシートはいずれも、使い捨ておむつの表面を構成する。表面シートの形状は、特に限定されず、例えば、長方形、砂時計型、ひょうたん型、羽子板型などが挙げられる。 The surface sheet is a sheet that is placed on the skin side of the absorbent core and constitutes the surface of the disposable diaper. The surface sheet may be composed of, for example, only the top sheet, or may be a laminated sheet composed of the top sheet and a pair of side sheets provided on both sides in the width direction of the top sheet. Both the topsheet and the sidesheet constitute the surface of the disposable diaper. The shape of the surface sheet is not particularly limited, and examples thereof include a rectangle, an hourglass shape, a gourd shape, and a battledore shape.
表面シートを構成するトップシートは、透液性を有し、着用者からの***液を速やかに透過する。前記トップシートとしては、親水性繊維により形成された不織布が挙げられる。前記親水性繊維としては、セルロース、レーヨン、コットンなどが挙げられる。前記不織布としては、例えば、ポイントボンド不織布、エアスルー不織布、スパンレース不織布、スパンボンド不織布、エアレイド不織布が挙げられる。トップシートの形状は、特に限定されず、例えば、長方形、砂時計型、ひょうたん型、羽子板型などが挙げられ、長方形であることが好ましい。 The top sheet that constitutes the surface sheet is liquid-permeable and allows the wearer's excreted liquids to quickly permeate. Examples of the top sheet include a nonwoven fabric formed of hydrophilic fibers. Examples of the hydrophilic fibers include cellulose, rayon, and cotton. Examples of the nonwoven fabric include point-bond nonwoven fabric, air-through nonwoven fabric, spunlace nonwoven fabric, spunbond nonwoven fabric, and air-laid nonwoven fabric. The shape of the top sheet is not particularly limited, and examples thereof include a rectangle, an hourglass shape, a gourd shape, a battledore shape, etc., preferably a rectangle.
本発明の使い捨ておむつは、肌面側に左右のサイドシートを有してもよい。左右のサイドシートは、トップシートの肌面側において、幅方向に間隔をあけて縦方向（前後方向）に沿って、トップシートの肌面側の両側部に接合されていることが好ましい。サイドシートとトップシートとの接合点から幅方向内側のサイドシートは、トップシートに接合せずに、自由端とされている。左右のサイドシートの幅方向内側先端（起立した際の上端）には、前後方向に伸長された弾性部材が配置されている。左右のサイドシートの内側先端は、この弾性部材の収縮力によって、トップシートから離反する方向（肌面側）に起立可能と構成されている。このサイドシートおよび弾性部材によって、立体ギャザーが構成され、この立体ギャザーによって***された尿、便の横漏れが防止される。前記サイドシートとしては、疎水性繊維（例えば、ポリプロピレン、ポリエチレン、ポリエステル、ポリアミド）にて形成された撥水性または不透液性の不織布（例えば、スパンボンド不織布、メルトブロー不織布、ＳＭＳ（スパンボンド・メルトブロー・スパンボンド）不織布）を使用することが好ましい。 The disposable diaper of the present invention may have left and right side sheets on the skin side. The left and right side sheets are preferably joined to both sides of the skin surface of the top sheet along the longitudinal direction (front-rear direction) with a gap in the width direction on the skin surface side of the top sheet. The side sheets on the inner side in the width direction from the joining point between the side sheets and the top sheet are not joined to the top sheet and are free ends. Elastic members that are elongated in the front-rear direction are arranged at the widthwise inner ends (upper ends when the vehicle is standing) of the left and right side seats. The inner ends of the left and right side sheets are configured to be able to stand up in the direction away from the top sheet (skin surface side) due to the contractile force of the elastic member. The side sheet and the elastic member constitute a three-dimensional gather, and the three-dimensional gather prevents excreted urine and feces from leaking sideways. As the side sheet, a water-repellent or liquid-impermeable nonwoven fabric (e.g., spunbond nonwoven fabric, meltblown nonwoven fabric, SMS (spunbond meltblown nonwoven fabric) made of hydrophobic fibers (e.g., polypropylene, polyethylene, polyester, polyamide)・It is preferable to use a spunbond (non-woven fabric).
サイドシートの形状は、特に限定されないが、外装シートの両側部を被覆するような形状を有していることを好ましく、例えば、砂時計型のシートを幅方向中央線で縦方向に二等分した形状を有することが好ましい。 Although the shape of the side sheet is not particularly limited, it is preferable that the side sheet has a shape that covers both sides of the exterior sheet. It preferably has a shape.
サイドシートに使用する不織布の目付は、１０ｇ／ｍ2以上が好ましく、１２ｇ／ｍ2以上がより好ましく、１３ｇ／ｍ2以上がさらに好ましく、２５ｇ／ｍ2以下が好ましく、２１ｇ／ｍ2以下がより好ましく、１８ｇ／ｍ2以下がさらに好ましい。 The basis weight of the nonwoven fabric used for the side sheets is preferably 10 g/m 2 or more, more preferably 12 g/m 2 or more, still more preferably 13 g/m 2 or more, preferably 25 g/m 2 or less, and 21 g/m 2 or less. More preferably, it is 18 g/m 2 or less.
サイドシートに使用する不織布としては、ポリプロピレン（樹脂）製のＳＭＭＳ（スパンボンド・メルトブロー・メルトブロー・スパンボンド）法で得られた不織布を用いることが好ましい。 As the nonwoven fabric used for the side sheets, it is preferable to use a nonwoven fabric made of polypropylene (resin) obtained by the SMMS (spunbond-meltblown-meltblown-spunbond) method.
本発明で使用する外装シートは、透液性シートおよび不透液性シートのいずれでもよいが、不透液性シートが好ましい。不透液性シートであれば、外装シートに到達した***液が、おむつ本体の外面側にしみ出すのを防止できる。不透液性シートとしては、疎水性繊維（例えば、ポリプロピレン、ポリエチレン、ポリエステル、ポリアミド）にて形成された撥水性または不透液性の不織布（例えば、スパンボンド不織布、メルトブロー不織布、ＳＭＭＳ（スパンボンド・メルトブロー・メルトブロー・スパンボンド）不織布）や、撥水性または不透液性のプラスチックフィルムが利用できる。外装シートの形状は、特に限定されず、例えば、長方形、砂時計型、ひょうたん型、羽子板型などが挙げられ、砂時計型あるいはひょうたん型であることが好ましい。 The exterior sheet used in the present invention may be either a liquid-permeable sheet or a liquid-impermeable sheet, but the liquid-impermeable sheet is preferred. A liquid-impermeable sheet can prevent excreted liquid that has reached the outer sheet from seeping out to the outer surface of the diaper body. As the liquid-impermeable sheet, a water-repellent or liquid-impermeable nonwoven fabric (e.g., spunbond nonwoven fabric, meltblown nonwoven fabric, SMMS (spunbond・Meltblown, meltblown, spunbond) non-woven fabrics) and water-repellent or liquid-impermeable plastic films can be used. The shape of the exterior sheet is not particularly limited, and examples thereof include a rectangular shape, an hourglass shape, a gourd shape, and a battledore shape, with the hourglass shape and the gourd shape being preferred.
また、前記外装シートは、不透液性シートと、この不透液性シートの外面側に貼り合わされた不織布から構成された積層シートであることが好ましい。外装シートが、不透液性シートと、この不透液性シートの外側に貼り合わされた合わされた不織布からなる積層シートの場合、外装シートの後方部の両側縁部は、不透液性のシートが配置されておらず、不織布のみから構成されていてもよい。 Further, the exterior sheet is preferably a laminated sheet composed of a liquid-impermeable sheet and a non-woven fabric bonded to the outer surface of the liquid-impermeable sheet. When the exterior sheet is a laminated sheet consisting of a liquid-impermeable sheet and a non-woven fabric laminated on the outside of the liquid-impermeable sheet, both side edges of the rear portion of the exterior sheet are covered with the liquid-impermeable sheet. may not be arranged, and may be composed only of nonwoven fabric.
外装シートに使用する不織布の目付は、１２ｇ／ｍ2以上が好ましく、１４ｇ／ｍ2以上がより好ましく、１５ｇ／ｍ2以上がさらに好ましく、２５ｇ／ｍ2以下が好ましく、２１ｇ／ｍ2以下がより好ましく、１８ｇ／ｍ2以下がさらに好ましい。 The basis weight of the nonwoven fabric used for the exterior sheet is preferably 12 g/m 2 or more, more preferably 14 g/m 2 or more, still more preferably 15 g/m 2 or more, preferably 25 g/m 2 or less, and 21 g/m 2 or less. More preferably, it is 18 g/m 2 or less.
外装シートに使用する不織布としては、ポリプロピレン（樹脂）製のＳＭＭＳ（スパンボンド・メルトブロー・メルトブロー・スパンボンド）法で得られた不織布を用いることが好ましい。 As the nonwoven fabric used for the exterior sheet, it is preferable to use a nonwoven fabric made of polypropylene (resin) obtained by the SMMS (spunbond-meltblown-meltblown-spunbond) method.
本発明の使い捨ておむつは、ファスニング部材を有することが好ましい。ファスニング部材を有することにより、本発明の使い捨ておむつを着用者に着用させるのが容易になるからである。ファスニング部材は、使い捨ておむつの後方部の両側縁部に接合されており、おむつ本体から幅方向の外側に延びるように形成されている。また、前記ファスニング部材は、ファスニング基材と、ファスニング基材の肌面側に設けられた第１止着部材とを有する。ファスニング基材は、おむつ本体に接合される固定端部と、第１止着部材が設けられる先端部とを有する。これらの左右の一対のファスニング部材と、これらのファスニング部材に設けられた第１止着部材と、前記おむつ本体に設けられた第２止着部材とによって、ファスニング手段が構成される。前記ファスニング手段は、使い捨ておむつを着用する際に、おむつ本体の前方部と後方部とを止着し、腰回りを形成するのに用いられる。 The disposable diaper of the present invention preferably has fastening members. This is because the provision of the fastening member makes it easier for the wearer to wear the disposable diaper of the present invention. The fastening members are joined to both side edges of the rear portion of the disposable diaper and formed to extend outward in the width direction from the main body of the disposable diaper. Further, the fastening member has a fastening base material and a first fastening member provided on the skin surface side of the fastening base material. The fastening base material has a fixed end to be joined to the diaper body and a tip to which the first fastening member is provided. The pair of left and right fastening members, the first fastening members provided on these fastening members, and the second fastening members provided on the diaper main body constitute fastening means. The fastening means is used to fasten the front part and the rear part of the diaper main body to form the waist when the disposable diaper is put on.
ファスニング基材は、例えば、不織布、織布、編布、樹脂フィルム材から適宜選択できる。ファスニング基材としては、スパンボンド法、エアスルー法、ポイントボンド法、メルトブロー法及びエアレイド法のうちの１つ又は複数の製法の組み合わせによって製造される不織布が好ましい。さらに、目付３０ｇ／ｍ2～１００ｇ／ｍ2で、スパンボンド法、又は、スパンボンド法とメルトブロー法とを組み合わせたＳＭＳ法により製造された不織布が強度の点から好ましい。ファスニング基材として、最も好ましいのは、目付５０ｇ／ｍ2～８５ｇ／ｍ2でスパンボンド法により製造された不織布である。材質としては、ポリプロピレン、ポリエチレン、ポリエステル、ポリアミド等の合成繊維、パルプ、絹等の天然繊維から適宜選択できるが、好ましくはポリプロピレン、ポリエチレン、ポリエステルといった合成繊維が利用できる。ファスニング基材としては、ポリプロピレン、ポリエステル繊維を主成分とするものは強度があり、好適である。ファスニング基材の材質として、最も好ましいのはポリエステル繊維である。 The fastening base material can be appropriately selected from, for example, nonwoven fabrics, woven fabrics, knitted fabrics, and resin film materials. The fastening base material is preferably a nonwoven fabric manufactured by one or a combination of manufacturing methods selected from the spunbonding method, the air-through method, the point bonding method, the melt blowing method, and the airlaid method. Further, a nonwoven fabric having a basis weight of 30 g/m 2 to 100 g/m 2 and manufactured by a spunbond method or an SMS method combining a spunbond method and a melt blow method is preferable from the viewpoint of strength. The most preferable fastening base material is a nonwoven fabric with a basis weight of 50 g/m 2 to 85 g/m 2 produced by a spunbond method. The material can be appropriately selected from synthetic fibers such as polypropylene, polyethylene, polyester, and polyamide, and natural fibers such as pulp and silk, but preferably synthetic fibers such as polypropylene, polyethylene, and polyester can be used. As the fastening base material, those containing polypropylene or polyester fiber as a main component are strong and suitable. The most preferred material for the fastening base material is polyester fiber.
前記第１止着部材と第２止着部材は、これらを着脱自在に止着し得るものであれば特に限定されない。第１止着部材と第２止着部材との組合せとしては、例えば、第１止着部材と第２止着部材とが面ファスナーを構成する態様；第１止着部材が粘着テープであり、第２止着部材が粘着テープを着脱自在に付着できる付着シートである態様；が挙げられる。なお、面ファスナーを採用する場合、第１止着部材にフック材を配置し、第２止着部材にループ材を配置することが好ましい。 The first fastening member and the second fastening member are not particularly limited as long as they can be detachably fastened. As a combination of the first fastening member and the second fastening member, for example, a mode in which the first fastening member and the second fastening member constitute a hook-and-loop fastener; the first fastening member is an adhesive tape, A mode in which the second fastening member is an adhesive sheet to which the adhesive tape can be attached in a detachable manner. In addition, when adopting a hook-and-loop fastener, it is preferable to arrange a hook material on the first fixing member and arrange a loop material on the second fixing member.
第１止着部材としては、例えば複数のフックが面状に密に設けられたフック材が好ましく用いられる。そのフック材のフックの形状としては、錨形や、駒形や、キノコ形等が好ましい。前記フック材としては、例えば「マジックテープ（登録商標）」（クラレ社製）、「クイックロン（登録商標）」（ＹＫＫ社製）、「マジクロス（登録商標）」（カネボウベルタッチ社製）等の市販品を用いることができる。第２止着部材としては、例えば微細なループ構造が面状に密に設けられたループ材（不織布、織布、編み物等や、不織布、織布等を表面に有する樹脂フィルム複合材等）が用いられる。 As the first fastening member, for example, a hook material in which a plurality of hooks are densely provided in a planar shape is preferably used. The shape of the hook of the hook material is preferably an anchor shape, a piece shape, a mushroom shape, or the like. Examples of the hook material include "Velcro (registered trademark)" (manufactured by Kuraray Co., Ltd.), "Quicklon (registered trademark)" (manufactured by YKK), and "Majicross (registered trademark)" (manufactured by Kanebo Belltouch). can be used. As the second fastening member, for example, a loop material (non-woven fabric, woven fabric, knitted fabric, etc., resin film composite material having a non-woven fabric, woven fabric, etc. on the surface) in which a fine loop structure is densely provided in a planar shape is used. Used.
本発明の使い捨ておむつは、使い捨ておむつの縦方向両端部および幅方向両側部の少なくとも一箇所において、表面シートと外装シートとが、反応性ウレタンホットメルト接着剤の硬化物により接合されている接合部（単に「反応性ウレタンホットメルト接合部」という場合がある）が設けられている。吸収コアの近辺に、反応性ウレタンホットメルト接合部を設けることにより、***液が使い捨ておむつから漏れるのを防止することができる。 In the disposable diaper of the present invention, the surface sheet and the exterior sheet are joined at at least one of the lengthwise end portions and the width direction end portions of the disposable diaper by a cured reactive urethane hot-melt adhesive. (sometimes simply referred to as a "reactive urethane hot-melt joint") is provided. By providing a reactive urethane hot-melt joint in the vicinity of the absorbent core, it is possible to prevent excrement from leaking out of the disposable diaper.
使い捨ておむつの縦方向端部とは、縦方向の端縁から幅５ｃｍの部分をいう。また、使い捨ておむつの幅方向側部とは、幅方向の側縁から幅３ｃｍの部分をいう。 The lengthwise end of the disposable diaper refers to a portion of width 5 cm from the lengthwise edge. Further, the width direction side portion of the disposable diaper refers to a portion having a width of 3 cm from the width direction side edge.
また、外装シートが、透液性領域と不透液性領域とを有する場合には、反応性ウレタンホットメルト接合部は、外装シートの不透液性領域に設けられることが好ましい。外装シートに到達した***液が、外装シートの外側にしみ出すのを防止できるからである。 Moreover, when the exterior sheet has a liquid-permeable region and a liquid-impermeable region, the reactive urethane hot-melt joint is preferably provided in the liquid-impermeable region of the exterior sheet. This is because it is possible to prevent the excreted liquid that has reached the exterior sheet from seeping out to the outside of the exterior sheet.
本発明の好ましい態様では、使い捨ておむつの縦方向両端部において、少なくとも吸収コアが設置されている幅に渡って、反応性ウレタンホットメルト接合部が設けられる。吸収コアの縦方向端部の少なくとも吸収コアが設置されている幅に渡って、反応性ウレタホットメルト接合部を設けることにより、吸収コア近辺の使い捨ておむつの縦方向両端部から***液が漏れだすのを低減することができる。 In a preferred embodiment of the present invention, reactive urethane hot-melt joints are provided at both longitudinal ends of the disposable diaper over at least the width of the absorbent core. By providing a reactive urethane hot-melt joint part over at least the width where the absorbent core is installed at the longitudinal ends of the absorbent core, excreted liquid leaks from the longitudinal both ends of the disposable diaper in the vicinity of the absorbent core. can be reduced.
本発明のより好ましい態様では、使い捨ておむつの縦方向両端部において、使い捨ておむつの幅方向全域に渡って、反応性ウレタンホットメルト接合部を設ける。使い捨ておむつの縦方向両端部において、使い捨ておむつの幅方向全域に渡って、反応性ウレタンホットメルト接合部を設けることにより、使い捨ておむつの縦方向両端部からの***液が漏れだすのをより確実に低減することができる。 In a more preferred embodiment of the present invention, reactive urethane hot-melt joints are provided across the width of the disposable diaper at both longitudinal ends of the disposable diaper. By providing reactive urethane hot-melt joints over the entire width of the disposable diaper at both ends of the disposable diaper in the longitudinal direction, leakage of excreted liquid from both ends of the disposable diaper in the longitudinal direction is more reliably prevented. can be reduced.
本発明の使い捨ておむつは、幅方向両側部において、表面シートと外装シートとが、反応性ウレタンホットメルト接着剤の硬化物により接合されている接合部を設けることが好ましく、少なくとも股部の両側縁部において、反応性ウレタンホットメルト接合部を設けることがより好ましく、幅方向両側部の少なくとも吸収コアが設置されている長さに渡って、反応性ウレタンホットメルト接合部を設けることがさらに好ましい。吸収コア近辺の幅方向両側部に、反応性ウレタンホットメルト接合部を設けることにより、使い捨ておむつから***液が漏れだすのを低減することができる。 In the disposable diaper of the present invention, on both sides in the width direction, it is preferable to provide joints in which the surface sheet and the outer sheet are joined by a cured product of a reactive urethane hot-melt adhesive. It is more preferable to provide a reactive urethane hot-melt joint in the portion, and more preferably, to provide a reactive urethane hot-melt joint over at least the length where the absorbent core is installed on both sides in the width direction. By providing reactive urethane hot-melt joints on both sides in the width direction near the absorbent core, it is possible to reduce leakage of excreted liquid from the disposable diaper.
本発明の使い捨ておむつは、幅方向両側部において、縦方向の長さに全域に渡って、反応性ウレタンホットメルト接合部を設けることも好ましい。斯かる構成により、使い捨ておむつの幅方向両側部から、***液が漏れ出すのをより確実に防止することができる。 In the disposable diaper of the present invention, it is also preferable to provide reactive urethane hot-melt joints over the entire longitudinal length on both sides in the width direction. With such a configuration, it is possible to more reliably prevent leakage of the excreted liquid from both sides in the width direction of the disposable diaper.
本発明の使い捨ておむつは、反応性ウレタンホットメルト接合部において、前記反応性ウレタンホットメルト接着剤の硬化物の塗布量は、５ｇ／ｍ２以上が好ましく、１０ｇ／ｍ2以上がより好ましく、１５ｇ／ｍ2以上がさらに好ましく、３０ｇ／ｍ２以下が好ましく、２６ｇ／ｍ2以下がより好ましく、２２ｇ／ｍ2以下がさらに好ましい。反応性ウレタンホットメルト接着剤の硬化物の塗布量が、前記範囲内であれば、接着強度および耐水接着強度が良好になるからである。 In the disposable diaper of the present invention, the coating amount of the cured product of the reactive urethane hot-melt adhesive is preferably 5 g/m 2 or more, more preferably 10 g/m 2 or more, and more preferably 15 g at the reactive urethane hot-melt joints. /m 2 or more, preferably 30 g/m 2 or less, more preferably 26 g/m 2 or less, and even more preferably 22 g/m 2 or less. This is because, if the coating amount of the cured product of the reactive urethane hot-melt adhesive is within the above range, the adhesive strength and water-resistant adhesive strength will be good.
反応性ウレタンホットメルト接合部は、使い捨ておむつの縦方向両端部あるいは幅方向両側部において、使い捨ておむつの外縁（縦方向端縁または幅方向側縁）から、２ｃｍ以上の幅で設けられることが好ましく、２．５ｃｍ以上の幅で設けられることがより好ましく、３ｃｍ以上の幅で設けられることがさらに好ましく、１０ｃｍ以下の幅で設けられることが好ましく、８ｃｍ以下の幅で設けられることが好ましく、６ｃｍ以下の幅で設けられることがさらに好ましい。また、反応性ウレタンホットメルト接合部は、その長さ方向に渡って、均一の幅であってもよいし、使い捨ておむつの外縁の形状に応じて、その幅が変化してもよい。 It is preferable that the reactive urethane hot-melt joints are provided with a width of 2 cm or more from the outer edge (longitudinal edge or widthwise side edge) of the disposable diaper at both longitudinal ends or lateral sides of the disposable diaper. , more preferably with a width of 2.5 cm or more, more preferably with a width of 3 cm or more, preferably with a width of 10 cm or less, preferably with a width of 8 cm or less, and 6 cm It is more preferable to provide the following widths. Also, the reactive urethane hot-melt joint may have a uniform width along its length, or its width may vary according to the shape of the outer edge of the disposable diaper.
使い捨ておむつの縦方向両端部において、反応性ウレタンホットメルト接合部を設ける態様としては、縦方向両端部の一部に反応性ウレタンホットメルト接合部を設ける態様、あるいは、縦方向両端部の全域に反応性ウレタンホットメルト接合部を設ける態様が挙げられる。 As a form of providing the reactive urethane hot-melt joints at both ends in the longitudinal direction of the disposable diaper, a form in which the reactive urethane hot-melt joints are provided at part of both ends in the longitudinal direction, or a form in which the reactive urethane hot-melt joints are provided at both ends in the longitudinal direction An embodiment in which a reactive urethane hot-melt joint is provided is exemplified.
使い捨ておむつの幅方向両側部において、反応性ウレタンホットメルト接合部を設ける態様としては、幅方向両側部の一部に反応性ウレタンホットメルト接合部を設ける態様、あるいは、幅方向両側部の全域に反応性ウレタンホットメルト接合部を設ける態様が挙げられる。 As a mode in which the reactive urethane hot-melt joints are provided on both sides in the width direction of the disposable diaper, there is a mode in which the reactive urethane hot-melt joints are provided on part of both sides in the width direction, or in the entirety of both sides in the width direction. An embodiment in which a reactive urethane hot-melt joint is provided is exemplified.
本発明において、反応性ウレタンホットメルト接合部は、反応性ウレタンホットメルト接着剤の硬化物のみにより接合されていることが好ましいが、反応性ウレタンホットメルトと非反応性ホットメルト接着剤とにより接合されていてもよい。接着強度を一層高める観点から、重畳的に塗布する場合があるからである。 In the present invention, the reactive urethane hot-melt joint is preferably joined only by the cured product of the reactive urethane hot-melt adhesive. may have been This is because, from the viewpoint of further increasing the adhesive strength, the coating may be applied in a superimposed manner.
反応性ウレタンホットメルト接合部において、非反応性ホットメルト接着剤を使用する場合、非反応性ホットメルト接着剤の塗布量は、１０ｇ／ｍ２以上が好ましく、１２ｇ／ｍ2以上がより好ましく、１４ｇ／ｍ2以上がさらに好ましく、３０ｇ／ｍ２以下が好ましく、２５ｇ／ｍ2以下がより好ましく、２０ｇ／ｍ2以下がさらに好ましい。 When using a non-reactive hot-melt adhesive in a reactive urethane hot-melt joint, the coating amount of the non-reactive hot-melt adhesive is preferably 10 g/m 2 or more, more preferably 12 g/m 2 or more. It is more preferably 14 g/m 2 or more, preferably 30 g/m 2 or less, more preferably 25 g/m 2 or less, and even more preferably 20 g/m 2 or less.
反応性ウレタンホットメルト接合部において、反応性ウレタンホットメルト接着剤の硬化物と非反応性ホットメルト接着剤との塗布量の質量比率（Ｒｅａｃｔｉｖｅ ＰＵＨＭ／Ｎｏｎ－Ｒｅａｃｔｉｖｅ ＨＭ）が、５／３０～３０／１０であることが好ましく、１０／２５～２６／１２であることがより好ましく、１５／２０～２２／１４であることがさらに好ましい。 In the reactive urethane hot-melt joint, the mass ratio of the coating amount of the cured product of the reactive urethane hot-melt adhesive and the non-reactive hot-melt adhesive (Reactive PUHM/Non-Reactive HM) is 5/30 to 30. /10, more preferably 10/25 to 26/12, even more preferably 15/20 to 22/14.
反応性ウレタンホットメルト接合部の接着強度は、１Ｎ／５０ｍｍ以上であることが好ましく、１．５Ｎ／５０ｍｍ以上であることがより好ましく、２Ｎ／５０ｍｍ以上であることがさらに好ましく、３０Ｎ／５０ｍｍ以下であることが好ましく、２５Ｎ／５０ｍｍ以下であることがより好ましく、２０Ｎ／５０ｍｍ以下であることがさらに好ましい。 The adhesive strength of the reactive urethane hot melt joint is preferably 1 N/50 mm or more, more preferably 1.5 N/50 mm or more, further preferably 2 N/50 mm or more, and 30 N/50 mm or less. , more preferably 25 N/50 mm or less, and even more preferably 20 N/50 mm or less.
以下、本発明の使い捨ておむつについて、図面を参照しながら説明するが、本発明は図面に示された態様に限定されるものではない。 The disposable diaper of the present invention will be described below with reference to the drawings, but the present invention is not limited to the embodiments shown in the drawings.
図１は、本発明の一実施形態に係る使い捨ておむつ１を、展開した状態でトップシート１０側から見た平面図である。図２は、使い捨ておむつ１を、展開した状態で外装シート２０側から見た平面図である。図３は、使い捨ておむつ１を図１中のＩＩＩ－ＩＩＩ線で切断した断面図である。なお、図１および図２は、後述するサイドシート用弾性部材４１、腰周り用弾性部材５１、脚周り用弾性部材５２を、いずれも伸長させた状態を示している。図では、矢印Ａを縦方向（前後方向）とし、矢印Ｂを幅方向と定義付ける。また、矢印Ａ，Ｂにより形成される面上の方向を、平面方向と定義付ける。また、矢印Ａ，Ｂにより形成される面に対して垂直方向が上下方向Ｃを表す。
FIG. 1 is a plan view of a
図１～図３に示すように、使い捨ておむつ１は、透液性のトップシート１０と、不透液性の外装シート２０と、両シート１０，２０の間に介在する吸収コア３０とを有する積層体であるおむつ本体２を備えている。
As shown in FIGS. 1 to 3, the
おむつ本体２は、着用者の腹面にあてがわれる前方部２ａと、着用者の背面にあてがわれる後方部２ｂと、前方部２ａと後方部２ｂを繋ぐ股部２ｃとを有している。以下では、前方部２ａ、股部２ｃ、後方部２ｂが連なる方向を「縦方向（前後方向）」と称し、縦方向に直交しかつおむつ本体２の表面に沿う方向を「幅方向」と称する。おむつ本体２は、前方部２ａから後方部２ｂにかけて縦方向にのび、その中間に位置する股部２ｃにおいて幅方向にくびれた形状となっている。
The diaper
トップシート１０は、おむつ本体２の肌面側に配置された透液性のシートである。トップシート１０は、前方部２ａから後方部２ｂにかけて帯状にのび、その幅方向の寸法は、おむつ本体２の外縁の幅方向の寸法よりも小さい。
The
外装シート２０は、おむつ本体２の外面側に配置されている。外装シート２０は、平面視において、おむつ本体２とほぼ同等の形状を有する。すなわち、外装シート２０は、おむつ本体２の下面全体を覆っている。外装シート２０は、不透液性シート２０ａと、この不透液性シート２０ａの外側に貼り合わされた不織布２０ｂからなる積層シートである。本態様では、不透液性シート２０ａと不織布２０ｂの平面視形状および大きさが同じであり、外装シートの全域が不透液性領域である。
The
吸収コア３０は、トップシート１０と外装シート２０との間に固定され、吸液性および保液性を有する。図３に示すように、吸収コア３０は、トップシート１０と外装シート２０との間に、非反応性ホットメルト接着剤５５により固定されていることが好ましい。また、図１に示すように、吸収コア３０は、平面視において、おむつ本体２の外縁より一回り小さく形成されている。
The
前記外装シート２０の前方部２ａの外面側には、第２止着部材７０が設けられている。図２では、第２止着部材７０の形状を矩形状としているが、この形状に限定されない。
A
トップシート１０の上面側には、側方への尿漏れを防止するための一対のサイドシート４０が設けられている。一対のサイドシート４０は、おむつ本体２の左右の側縁部を覆うように、縦方向（前後方向）にのびている。本態様では、トップシート１０と一対のサイドシート４０が表面シートを構成する。
A pair of
図３に示したように、一対のサイドシート４０は、トップシート１０の肌面側において、幅方向に間隔をあけて縦方向（前後方向）に沿って、トップシート１０の肌面側の両側部に接合されていることが好ましい。サイドシート４０とトップシート１０との接合点から幅方向内側のサイドシート４０は、トップシート１０に接合せずに、自由端とされている。サイドシート４０の幅方向内側の先端部には、前後方向にのびる複数本のサイドシート用弾性部材４１が配置されている。サイドシート用弾性部材４１は、自然長よりも伸長された状態で、サイドシート４０に接着剤（図示省略）により取り付けられている。このため、サイドシート用弾性部材４１は、サイドシート４０を縦方向（前後方向）に収縮させる弾性力を発生させる。使い捨ておむつを開いたときには、サイドシート用弾性部材４１の弾性力により、サイドシート４０の幅方向内側の先端部が立ち上がる。これにより、おむつ本体２の上面に一対の起立した堰が形成され、着用者が***した尿の側方への漏れが防止される。
As shown in FIG. 3, the pair of
図３に示す態様では、使い捨ておむつの股部２ｃの両側縁部において、トップシート１０の幅が、外装シート２０の幅よりも短いために、外装シート２０幅方向の両側縁部の上方には、トップシート１０が存在せず、サイドシート４０が設けられている。本態様の使い捨ておむつは、吸収コア３０の幅方向外側領域、すなわち、使い捨ておむつの幅方向両側縁部において、表面シートを構成するサイドシート４０と外装シート２０とが、反応性ウレタンホットメルト接着剤の硬化物により接合されている接合部８０が設けられている。
In the embodiment shown in FIG. 3, the width of the
前方部２ａおよび後方部２ｂには、幅方向にのびる複数本の腰周り用弾性部材５１が設けられている。腰周り用弾性部材５１は、自然長よりも伸長された状態で、トップシート１０と外装シート２０との間に、接着剤（図示省略）により取り付けられている。このため、腰周り用弾性部材５１は、前方部２ａおよび後方部２ｂを、幅方向に収縮させる弾性力を発生させる。着用者が使い捨ておむつ１を着用したときには、腰周り用弾性部材５１の収縮力により、前方部２ａおよび後方部２ｂを、着用者の腰周りにフィットさせることができる。
A plurality of waist
また、股部２ｃの幅方向の両側縁部には、前後方向にのびる複数本の脚周り用弾性部材５２が設けられている。脚周り用弾性部材５２は、自然長よりも伸長された状態で、サイドシート４０とバックシート２０との間に、接着剤（図示省略）により取り付けられている。このため、脚周り用弾性部材５２は、股部２ｃの両側縁部を、縦方向（前後方向）に収縮させる弾性力を発生させる。着用者が使い捨ておむつ１を着用したときには、脚周り用弾性部材５２の収縮力により、股部２ｃの両側縁部を、着用者の大腿部にフィットさせることができる。
In addition, a plurality of leg-surrounding
なお、サイドシート用弾性部材４１、腰周り用弾性部材５１、及び脚周り用弾性部材５２には、例えば、ポリウレタン糸等の糸状の弾性部材を使用すればよい。また、糸状の弾性部材に代えて、ポリウレタンや天然ゴム等を素材とする平板状の弾性部材を使用してもよい。
For the side seat
図１の態様の使い捨ておむつ１は、一対のファスニング部材６０を備えている。各ファスニング部材６０は、ファスニング基材６１と、ファスニング基材６１の自由端側の端辺から幅方向外側に張り出した２つの舌片状のつまみ部６２とを有している。各つまみ部６２の肌面側には、第１止着部材６３が設けられている。ファスニング基材６１は、幅方向内側の固定端部において、サイドシート４０と外装シート２０に挟まれて、おむつ本体に接合されている。本実施形態の第１止着部材６３には、面ファスナーのフック材（雄部材）が用いられている。一方、図２に示したように、おむつ本体２の前方部２ａの外側面には、第１止着部材６３を着脱自在に止着させる第２止着部材７０が設けられている。本実施形態の第２止着部材７０には、面ファスナーのループ材（雌部材）が用いられている。
The
次に、本発明における反応性ウレタンホットメルト接合部を設ける態様について説明する。なお、図４～図８は、本発明の好ましい態様の使い捨ておむつについて、トップシート側から見た平面図であるが、理解を容易にするために、弾性部材は示されていない。 Next, a mode of providing a reactive urethane hot-melt joint in the present invention will be described. 4 to 8 are plan views of the preferred embodiment of the disposable diaper of the present invention, viewed from the top sheet side, but elastic members are not shown for ease of understanding.
図４には、例えば、使い捨ておむつの縦方向両端部において、反応性ウレタンホットメルト接合部８０が設けられている態様が示されている。反応性ウレタンホットメルト接合部８０は、少なくとも吸収コアが設置されている幅に渡って設けられている。使い捨ておむつ縦方向両端部と吸収コアとは、近接して配置されている。吸収コアに近接している領域に、反応性ウレタンホットメルト接合部を設けることにより、使い捨ておむつから、***液が漏れるのを効果的に防止することができる。
FIG. 4 shows, for example, a mode in which reactive urethane hot-
反応性ウレタンホットメルト接合部８０は、使い捨ておむつの幅方向に長辺を、縦方向に短辺を有する長方形に設けられている。図４に示した反応性ウレタンホットメルト接合部の長辺方向の中央領域では、トップシート１０が存在し、表面シートとしてトップシート１０と外装シート２０とが、反応性ウレタンホットメルト接着剤の硬化物により接合されている。反応性ウレタンホットメルト接合部の長辺方向両側縁は、トップシートの両側縁１０１よりも、使い捨ておむつの幅方向外側に位置する。すなわち、反応性ウレタンホットメルト接合部の長辺方向両端部には、トップシート１０が存在しないので、表面シートとしてサイドシート４０と外装シート２０とが反応性ウレタンホットメルト接着剤の硬化物により接合されている。
The reactive urethane hot-melt
図５に示した態様では、使い捨ておむつの縦方向両端部において、使い捨ておむつの幅全域に渡って、反応性ウレタンホットメルト接合部８０が設けられている。反応性ウレタンホットメルト接合部８０を、使い捨ておむつの幅方向全域に設けることにより、***液が使い捨ておむつの縦方向両端部から、***液が漏れるのを効果的に防止できる。
In the embodiment shown in FIG. 5, reactive urethane hot-
図５に示した反応性ウレタンホットメルト接合部の長辺方向中央領域では、トップシート１０が存在し、表面シートとしてトップシート１０と外装シート２０とが、反応性ウレタンホットメルト接着剤の硬化物により接合されている。一方、反応性ウレタンホットメルト接合部８０の長辺方向両端部には、トップシート１０が存在しないので、表面シートとしてサイドシート４０と外装シート２０とが反応性ウレタンホットメルト接着剤の硬化物により接合されている。
In the central region in the longitudinal direction of the reactive urethane hot-melt joint shown in FIG. are joined by On the other hand, since the
図４および図５の態様において、反応性ウレタンホットメルト接合部は、おむつ本体の縦方向の端縁から、２ｃｍ以上の幅で設けられることが好ましく、２．５ｃｍ以上の幅で設けられることがより好ましく、３．０ｃｍ以上の幅で設けられることがさらに好ましく、１０ｃｍ以下の幅で設けられることが好ましく、８ｃｍ以下の幅で設けられることがより好ましく、６ｃｍ以下の幅で設けられることがさらに好ましい。 In the embodiments of FIGS. 4 and 5, the reactive urethane hot-melt joints are preferably provided with a width of 2 cm or more, and may be provided with a width of 2.5 cm or more, from the longitudinal edge of the diaper body. More preferably, it is provided with a width of 3.0 cm or more, preferably with a width of 10 cm or less, more preferably with a width of 8 cm or less, and further preferably with a width of 6 cm or less. preferable.
図６には、使い捨ておむつの幅方向両端部において、使い捨ておむつの股部２ｃの両側部のみに反応性ウレタンホットメルト接合部８０が設けられている。使い捨ておむつの股部２ｃの両側部と吸収コアとは、近接している。吸収コアに近接している領域に、反応性ウレタンホットメルト接合部を設けることにより、使い捨ておむつから、***液が漏れるのを効果的に防止することができる。
In FIG. 6, reactive urethane hot-
図７には、使い捨ておむつの幅方向両側部において、縦方向（前後方向）の長さに全域に渡って、反応性ウレタンホットメルト接合部８０が設けられている。反応性ウレタンホットメルト接合部８０を、使い捨ておむつの縦方向（前後方向）全域に設けることにより、***液が使い捨ておむつの幅方向両側部から、***液が漏れるのを効果的に防止できる。
In FIG. 7, reactive urethane hot-
図６および図７の態様において、反応性ウレタンホットメルト接合部８０は、おむつ本体の幅方向の側縁から、１０ｃｍ以上の幅で設けられることが好ましく、１３ｃｍ以上の幅で設けられることがより好ましく、１５ｃｍ以上の幅で設けられることがさらに好ましく、２８ｃｍ以下の幅で設けられることが好ましく、２４ｃｍ以下の幅で設けられることがより好ましく、２０ｃｍ以下の幅で設けられることがさらに好ましい。 6 and 7, the reactive urethane hot-melt joint 80 is preferably provided with a width of 10 cm or more, more preferably 13 cm or more, from the side edge in the width direction of the diaper body. Preferably, it is provided with a width of 15 cm or more, more preferably with a width of 28 cm or less, more preferably with a width of 24 cm or less, and even more preferably with a width of 20 cm or less.
図８は、使い捨ておむつの幅方向両側部において、縦方向（前後方向）の長さに全域に渡って、反応性ウレタンホットメルト接合部８０が設けられる変形例である。反応性ウレタンホットメルト接合部８０の幅方向内側縁は、使い捨ておむつの縦方向に直線状とされている。使い捨ておむつの前方部２ａおよび後方部２ｂでは、反応性ウレタンホットメルト接合部８０は、ほぼ一定の幅を有するが、股部２ｃでは、股部２ｃの外縁のくびれに応じて、反応性ウレタンホットメルト接合部８０の幅が狭くなっている。
FIG. 8 shows a modification in which reactive urethane hot-
図９には、使い捨ておむつの幅方向両側部において縦方向（前後方向）の長さ全域、および、縦方向両端部において幅方向の長さ全域において、反応性ウレタンホットメルト接合部が設けられている。吸収コアの周囲に位置する全域に、反応性ウレタンホットメルト接合部を設けることにより、使い捨ておむつから***液が漏れ出すのが、より確実に防止される。 In FIG. 9, reactive urethane hot-melt joints are provided on both sides in the width direction of the disposable diaper over the entire length in the longitudinal direction (front-rear direction), and over the entire length in the width direction on both ends in the longitudinal direction. there is By providing the reactive urethane hot-melt joints in the entire area around the absorbent core, leakage of excrement from the disposable diaper is more reliably prevented.
図１０（ａ）には、図４に示した反応性ウレタン接合部８０において、反応性ウレタンホットメルト接着剤７２を塗布する態様を示した。反応性ウレタンホットメルト接着剤７２が、使い捨ておむつの縦方向と略平行にストライプ状に塗布されている。反応性ウレタンホットメルト接着剤は、例えば、表面シートおよび外装シートの少なくとも一方の縦方向両端部に塗布されればよく、表面シートおよび外装シートの両方の縦方向両端部に塗布されることも好ましい。反応性ウレタンホットメルト接着剤は、例えば、幅０．７ｍｍ～１．５ｍｍのストライプ状に、ストライプのピッチ間距離が、１ｍｍ～３ｍｍで塗布されることが好ましい。
FIG. 10(a) shows a mode in which the reactive urethane hot-
図１０（ｂ）には、図４に示した反応性ウレタン接合部８０において、反応性ウレタンホットメルト接着剤７２と、非反応性ホットメルト接着剤５５とを塗布する態様を示した。この態様は、例えば、非反応性ホットメルト接着剤５５を外装シートの縦方向端部の肌面側に塗布し、反応性ウレタンホットメルト接着剤７２を表面シートの縦方向端部の外面側に塗布することで得られる。また、逆に、例えば、反応性ウレタンホットメルト接着剤７２を外装シートの縦方向端部の肌面側に塗布し、非反応性ホットメルト接着剤５５を表面シートの縦方向端部の外面側に塗布するようにしてもいい。
FIG. 10(b) shows a mode in which the reactive urethane hot-
図１０（ｂ）の態様において、反応性ウレタンホットメルト接着剤は、例えば、幅０．７ｍｍ～１．５ｍｍのストライプ状に、ストライプのピッチ間距離が、１ｍｍ～３ｍｍで塗布されることが好ましい。また、非反応性ホットメルト接着剤５５は、例えば、幅０．７ｍｍ～３．５ｍｍのストライプ状に、ストライプのピッチ間距離が、１ｍｍ～９ｍｍで塗布されることが好ましい。反応性ウレタンホットメルト接着剤のストライプと、非反応性ホットメルト接着剤のストライプとは、重なり合ってもよいが、重なり合わないことが好ましい。すなわち、非反応性ホットメルトのストライプは、反応性ウレタンホットメルトのストライプ間の間隙に存在することが好ましい。
In the embodiment of FIG. 10(b), the reactive urethane hot-melt adhesive is preferably applied, for example, in stripes with a width of 0.7 mm to 1.5 mm with a pitch distance between the stripes of 1 mm to 3 mm. . The non-reactive hot-
図１１には、図８に示した反応性ウレタン接合部８０において、反応性ウレタンホットメルト接着剤７２を塗布する態様を示した。反応性ウレタンホットメルト接着剤７２は、使い捨ておむつの縦方向と略平行にストライプ状に塗布されている。反応性ウレタンホットメルト接着剤は、例えば、表面シートおよび外装シートの少なくとも一方の縦方向両端部に塗布されればよく、表面シートおよび外装シートの両方の縦方向両端部に塗布されることも好ましい。
FIG. 11 shows a mode of applying the reactive urethane hot-
本発明の使い捨ておむつの製造方法は、吸収コアと、吸収コアの肌面側に設けられた表面シートと、吸収コアの外面側に設けられた外装シートとを有する使い捨ておむつであって、前記使い捨ておむつの縦方向両端部および幅方向両側部の少なくとも一箇所において、前記表面シートと外装シートとを、反応性ウレタンホットメルト接着剤により接合する接合部を設けることを特徴とする。 A method for manufacturing a disposable diaper of the present invention is a disposable diaper having an absorbent core, a surface sheet provided on the skin surface side of the absorbent core, and an exterior sheet provided on the outer surface side of the absorbent core, the disposable diaper comprising: The diaper is characterized in that joints for joining the surface sheet and the outer sheet with a reactive urethane hot-melt adhesive are provided in at least one of both longitudinal and lateral sides of the diaper.
反応性ウレタンホットメルト接着剤は、使い捨ておむつの縦方向両端部あるいは幅方向両側部において、表面シートと外装シートとを接合することができる限り、表面シートおよび外装シートのいずれに塗布してもよく、おむつ本体の構成、表面シートと外装シートの接合態様などに基づいて、適宜決定すればよい。表面シートおよび外装シートの両方に反応性ウレタンホットメルト接着剤を塗布するようにしてもよい。 The reactive urethane hot-melt adhesive may be applied to either the top sheet or the exterior sheet as long as the top sheet and the exterior sheet can be joined at both ends in the longitudinal direction or both sides in the width direction of the disposable diaper. , the structure of the main body of the diaper, the manner of bonding between the surface sheet and the exterior sheet, and the like. A reactive urethane hot-melt adhesive may be applied to both the surface sheet and the exterior sheet.
例えば、図８および図１１に示した使い捨ておむつの態様のように、縦方向（前後方向）全域の幅方向両側部において、表面シートと外装シートとを反応性ウレタンホットメルト接着剤の硬化物で接合する製造方法について、以下、説明する。 For example, as in the embodiment of the disposable diaper shown in FIGS. 8 and 11, the surface sheet and the exterior sheet are coated with a cured product of a reactive urethane hot-melt adhesive on both sides in the width direction in the entire longitudinal direction (front-rear direction). A manufacturing method for bonding will be described below.
ア）外装シート（バックシート）２０の肌面側に、非反応性ホットメルト接着剤５５と反応性ウレタンホットメルト接着剤７２とを塗布する工程。非反応性ホットメルト接着剤５５は、外装シート（バックシート）の吸収コアが配置される箇所に塗布される。吸収コア３０は、この非反応性ホットメルト接着剤５５によって、外装シート（バックシート）２０と接合される。吸収コア３０が配置されない外装シート（バックシート）２０の幅方向両側部には、反応性ウレタンホットメルト接着剤７２を塗布する。反応性ウレタンホットメルト接着剤７２は、使い捨ておむつの両側部において、外装シート（バックシート）２０とサイドシート４０とを接合する。非反応性ホットメルト接着剤５５および反応性ウレタンホットメルト接着剤７２は、接触式あるいは非接触式の塗布装置によって塗布されることが好ましい。また、ストライプ状あるいはスパイラル状に塗布することができる。
a) A step of applying a non-reactive hot-
イ）吸収コア３０を、非反応性ホットメルト接着剤５５が塗布された外装シート（バックシート）２０上に積層する工程。積層時には、外装シート（バックシート）２０の幅方向中心線と吸収コア３０の幅方向中心線とが、略一致するように位置取りすることが好ましい。
b) A step of laminating the
ウ）トップシート１０とサイドシート４０とを積層する工程。
トップシート１０の肌面側の幅方向両端部もしくはサイドシート４０に塗布された接着剤により、または、熱溶着により、トップシート１０の肌面側の幅方向両端部にサイドシート４０を接合して、トップシート１０の肌面側の幅方向両端部にサイドシート４０を接合した積層体（表面シート）を作製する。なお、トップシート１０とサイドシート４０とを予め積層することなく、吸収コアが配置された外装シート２０にトップシート１０およびサイドシート４０を順次積層するようにしてもよい。
c) A step of laminating the
The
また、サイドシート４０の外面側の幅方向内側領域の縦方向両端部において、非反応性ホットメルト接着剤５５を塗布しておくことが好ましい。サイドシート４０の幅方向内側部は、縦方向両端部において、非反応性ホットメルト接着剤５５によりトップシート１０に接合される。サイドシート４０の幅方向内側領域の起立部に相当する箇所には、非反応性ホットメルト接着剤５５は、塗布しないことが好ましい。非反応性ホットメルト接着剤５５は、接触式あるいは非接触式の塗布装置によって塗布されることが好ましい。また、非反応性ホットメルト接着剤５５は、ストライプ状あるいはスパイラル状に塗布することが好ましい。
In addition, it is preferable to apply a non-reactive hot-
エ）ファスニング部材６０（ファスニング基材６１の固定端部６１ａ）の肌面側に、非反応性ホットメルト接着剤５５を塗布する工程。非反応性ホットメルト接着剤５５は、接触式あるいは非接触式の塗布装置によって塗布されることが好ましく、接触式がより好ましい。また、非反応性ホットメルト接着剤は、カーテン状、オメガ状、ストライプ状あるいはスパイラル状に塗布することが好ましく、ストライプ状がより好ましい。
d) A step of applying a non-reactive hot-
オ）トップシート１０とサイドシート４０との積層体（表面シート）に、ファスニング部材６０を積層する工程。ファスニング部材６０の肌面側に塗布された非反応性ホットメルト接着剤５５により、サイドシート４０の外面側の幅方向両端部にファスニング部材６０の肌面側を接合して、サイドシート４０の外面側の幅方向両端部にファスニング部材６０を接合した積層体（トップシート１０とサイドシート４０とファスニング部材６０との積層体）を作製する。
e) A step of laminating the
カ）トップシート１０とサイドシート４０とファスニング部材６０との積層体の外面側に、非反応性ホットメルト接着剤５５と、反応性ウレタンホットメルト接着剤７２とを塗布する工程。非反応性ホットメルト接着剤５５は、トップシート１０の外面側に塗布されることが好ましい。また、サイドシート４０の外面側には、反応性ウレタンホットメルト接着剤７２が塗布されることが好ましい。この非反応性ホットメルト接着剤５５は、トップシート２０と吸収コア３０とを接合するために使用される。反応性ホットメルト接着剤７２は、サイドシート４０と外装シート２０とを接合するために使用される。ホットメルト接着剤は、接触式あるいは非接触式の塗布装置によって塗布されることが好ましい。また、ホットメルト接着剤は、ストライプ状あるいはスパイラル状に塗布することが好ましい。
f) A step of applying a non-reactive hot-
キ）トップシート１０とサイドシート４０とファスニング部材６０との積層体と、吸収コア３０が配置された外装シート（バックシート）２０とを積層し、おむつ本体を作製する工程。すなわち、表面シート（サイドシート４０）と外装シート（バックシート）２０の幅方向両端部は、反応性ウレタンホットメルト接着剤７２によって接合される。接合部は、ローラなどで加圧処理されることが好ましい。
g) A step of laminating the laminate of the
カ）反応性ウレタンホットメルト接着剤を用いて、製造した使い捨ておむつは、湿度４０％～９０％、１５～３０℃で、１２０時間程度養生することが好ましい。養生は、特別な処理を必要とせず、最終製品として、倉庫に保管していることによる行うことが好ましい。前記条件で養生することにより、反応性ウレタンホットメルト接着剤の湿気硬化反応が進んで硬化する。その結果、３次元架橋構造が形成され、耐熱接着強度が発現される。 f) Disposable diapers manufactured using a reactive urethane hot-melt adhesive are preferably cured at a humidity of 40% to 90% and 15 to 30°C for about 120 hours. Curing does not require any special treatment and is preferably carried out by being stored in a warehouse as a final product. Curing under the above conditions promotes the moisture curing reaction of the reactive urethane hot-melt adhesive to cure it. As a result, a three-dimensional crosslinked structure is formed, and heat-resistant adhesive strength is exhibited.
次に、図１２ないし図１５を参照して、表面シート１０または外装シート２０（以下、「表面シートなど１０（２０）」という場合がある）にホットメルト接着剤を塗布する工程について、具体的に説明する。
Next, referring to FIGS. 12 to 15, the step of applying the hot-melt adhesive to the
表面シートなど１０（２０）へのホットメルト接着剤の塗布は、図１２に示すようなコーターヘッド１５１を用いて行われることが好ましい。このコーターヘッド１５１は、ホットメルト接着剤を排出する後述する接着剤排出部１５２，１５３が塗工面（ここでは、表面シート１０または外装シート２０の表面）に接触した状態で配置される、あるいは僅かな隙間を介して近接して配置される接触式の接着剤塗布装置である。また変形例として、ホットメルト接着剤を排出する接着剤排出部１５２，１５３が塗工面と間隔をあけて配置されるスパイラル塗布装置等の非接触式の接着剤塗布装置を採用してもよい。
Application of the hot-melt adhesive to the surface sheet 10 (20) is preferably carried out using a
このコーターヘッド１５１は、図１３ないし図１５に示すように、種類が異なるホットメルト接着剤が排出される複数（例えば２つ）の接着剤排出部１５２，１５３を有する。接着剤排出部１５２、１５３は、接着剤塗布領域に対応する位置に配置されている。反応性ウレタンホットメルト接着剤と非反応性ホットメルト接着剤は、いずれの接着剤排出部１５２，１５３から排出するようにしてもよい。そして、この接着剤排出部１５２，１５３が表面シートなど１０（２０）の反応性ウレタンホットメルト接合部８０を形成すべき位置に対向するようにコーターヘッド１５１を配置し、接着剤排出部１５２，１５３からホットメルト接着剤を排出させながら、表面シートなど１０（２０）を縦方向Ｙと平行な搬送方向に搬送することにより、表面シートなど１０（２０）の所定位置に縦方向Ｙにそってホットメルト接着剤が帯状に塗布される。
As shown in FIGS. 13 to 15, the
次に、コーターヘッド１５１の具体的な構成例について説明する。なお、コーターヘッド１５１の構成としては種々の構成が採用可能であり、ここで説明する構成に限定されるものではない。コーターヘッド１５１は、図１３ないし図１５に示すように、第１及び第２ヘッド部１５６，１５７と、シム１５８とを備えている。第１及び第２ヘッド部１５６，１５７は、それらの間にシム１５８を挟み込んで互いに対向した状態で固定される。
Next, a specific configuration example of the
シム１５８は、略板状の形状を有し、複数（ここでは２つ）の接着剤排出部１５２，１５３が形成されている。各接着剤排出部１５２，１５３には、シム１５８の下縁の一部が略くし歯状に下降されて１又は複数のスリット１５９が形成されている。
The
第１ヘッド部１５６のシム１５８との対向面におけるシム１５８の接着剤排出部１５２と対向する部分には、接着剤排出部１５２に、例えば、反応性ウレタンホットメルト接着剤を供給するための接着剤供給凹部１５６ａが設けられている。接着剤供給凹部１５６ａへの接着剤の供給は、供給路１５６ｂを介して行われる。また、第２ヘッド部１５７のシム１５８との対向面におけるシム１５８の接着剤排出部１５３と対向する部分には、接着剤排出部１５３に、例えば、非反応性ホットメルト接着剤を供給するための接着剤供給凹部１５７ａがそれぞれ設けられている。接着剤供給凹部１５７ａへの接着剤の供給は、供給路１５７ｂを介して行われる。
A portion of the
なお、この図１５等に示す構成では、接着剤排出部１５２，１５３に接着剤を供給するための２つ接着剤供給凹部１５６ａ，１５７ａを２つのヘッド部１５６，１５７に分けて形成するようにしたが、いずれか一方のヘッド部１５６，１５７に２つの接着剤供給凹部１５６ａ，１５７ａをすべて形成して他方のヘッド部１５６，１５７を省略してもよい。
In the configuration shown in FIG. 15 and the like, two
前記のような接着剤の塗布工程によれば、表面シートなど１０（２０）への反応性ウレタンホットメルト接着剤７２と、非反応性ホットメルト接着剤５５が１つのコーターヘッド１５１によって同時に塗布されるため、製造工程の簡略化が図れる。
According to the adhesive application process as described above, the reactive urethane hot-
また、コーターヘッド１５１を接着剤の種類毎に複数配置するようにしてもよい。例えば、１つのコーターヘッドで、反応性ウレタンホットメルト接着剤７２あるいは非反応性ホットメルト接着剤５５のいずれか一方を塗布し、２つ目のコーターヘッドで、他方のホットメルト接着剤を塗布するようにすればよい。 Also, a plurality of coater heads 151 may be arranged for each type of adhesive. For example, one coater head applies either the reactive urethane hot melt adhesive 72 or the non-reactive hot melt adhesive 55, and the second coater head applies the other hot melt adhesive. You should do it like this.
前記では、表面シートなど１０（２０）に反応性ウレタンホットメルト接着剤と非反応性ホットメルト接着剤とを塗布する方法について説明したが、反応性ウレタンホットメルト接着剤のみを塗布する場合には、ホットメルト接着剤として、反応性ウレタンホットメルト接着剤のみを使用すればよい。また、コーターヘッドとして、１種類のホットメルト接着剤を塗布するものを用いることもできる。 In the above description, the method of applying the reactive urethane hot-melt adhesive and the non-reactive hot-melt adhesive to the surface sheet 10 (20) was explained. , only reactive urethane hot-melt adhesives may be used as hot-melt adhesives. A coater head that applies one kind of hot melt adhesive can also be used.
以下、本発明を実施例によって詳細に説明するが、本発明は、下記実施例によって限定されるものではなく、本発明の趣旨を逸脱しない範囲の変更、実施の態様は、いずれも本発明の範囲内に含まれる。 Hereinafter, the present invention will be described in detail with reference to examples, but the present invention is not limited to the following examples, and any modifications and embodiments that do not depart from the scope of the present invention can be made within the scope of the present invention. Included in scope.
［評価方法］
（溶融粘度）
ＪＩＳ－Ｋ６６６２に準拠して、Ｂ型粘度計を用いて１２０℃で粘度を測定した。
[Evaluation method]
(melt viscosity)
The viscosity was measured at 120° C. using a Brookfield viscometer in accordance with JIS-K6662.
（オープンタイム）
１５ｍｍ幅のスパンボンド不織布（２０ｇ／ｍ２）に反応性ウレタンホットメルト接着剤を１８０℃で５０ｇ／ｍ２塗工する。次に、塗工から２秒以内に他のスパンボンド不織布（２０ｇ／ｍ２）を載置し、２ｋｇ荷重で圧着する。一定時間放置後、剥離速度３００ｍｍ／minで、１８０°剥離試験を行い、接着剤塗工時から、塗工領域における８０％以上の不織布が材質破壊したときの剥離試験時までに経過した時間をオープンタイムとした。
(open time)
A 15 mm wide spunbond nonwoven fabric (20 g/m 2 ) is coated with 50 g/m 2 of reactive urethane hot melt adhesive at 180°C. Next, another spunbond nonwoven fabric (20 g/m 2 ) is placed within 2 seconds after coating and pressed under a load of 2 kg. After standing for a certain period of time, a 180° peeling test was performed at a peeling speed of 300 mm/min, and the time elapsed from the time when the adhesive was applied to the time when 80% or more of the nonwoven fabric in the coated area was destroyed. Open time.
（接着力試験）
おむつ本体の後方部における幅方向の両側縁部とファスニング部材とを、反応性ウレタンホットメルト接着剤で接合して、使い捨ておむつを製造した。サイドシートの外面側接合面とファスニング基材の肌面側接合面が、反応性ウレタンホットメルト接着剤の硬化物で接合されている。製造後、所定時間経過後の使い捨ておむつを用い、サイドシートとファスニング部材の接合部からサイドシートから外方に延出するファスニング部材に至る長さ１００ｍｍの試験片を、５０ｍｍ幅で作製した（図１６参照、試験片９０）。試験片の長手方向が引っ張り方向となるように、引っ張り試験機（エー・アンド・デイ製、テンシロン万能試験機ＲＴＧ－１２１０）の上側チャックにファスニング部材、下側チャックにサイドシートをそれぞれ取り付けた。次いで、試験片を３００ｍｍ／分の速度で１８０度の方向に引っ張り、ファスニング部材がおむつ本体から剥離されるまで応力を測定し、応力の最大値を接着力とした。結果を表１に示した。なお、接着力は、５つの使い捨ておむつの左右のファスニング部材のそれぞれについて試験を行い、平均値で示した。
(Adhesion test)
A disposable diaper was manufactured by bonding both side edges in the width direction of the rear portion of the diaper body to the fastening member with a reactive urethane hot-melt adhesive. The joint surface on the outer surface side of the side sheet and the joint surface on the skin surface side of the fastening base material are joined with a cured product of a reactive urethane hot-melt adhesive. Using the disposable diaper after the lapse of a predetermined period of time after production, a 100 mm long test piece extending from the joint between the side sheet and the fastening member to the fastening member extending outward from the side sheet was prepared with a width of 50 mm (Fig. 16, specimen 90). A fastening member was attached to the upper chuck of a tensile tester (Tensilon universal tester RTG-1210, manufactured by A&D), and a side sheet was attached to the lower chuck so that the longitudinal direction of the test piece was the tensile direction. Next, the test piece was pulled in a direction of 180 degrees at a speed of 300 mm/min, and the stress was measured until the fastening member was separated from the main body of the diaper. Table 1 shows the results. In addition, the adhesive force was tested for each of the left and right fastening members of five disposable diapers, and the average value was shown.
表１の結果から、明らかなように、反応性ウレタンホットメルト接着剤を用いた接合部は、経時により接着力が高くなっていることが分かる。この結果は、反応性ウレタンホットメルト接着剤が、湿気硬化反応により、接着力を発現していることを示している。 As can be seen from the results in Table 1, the adhesive strength of the joints using the reactive urethane hot-melt adhesive increased over time. This result indicates that the reactive urethane hot-melt adhesive exhibits adhesive strength due to moisture curing reaction.
（耐熱接着力試験）
製造後、常温で５日以上経過した使い捨ておむつを用い、ファスニング部材より幅方向内方に位置するおむつ本体から、ファスニング部材とおむつ本体が重なる部分を介し、おむつ本体より幅方向外方に位置するファスニング部材に到る領域を含む、長さ１００ｍｍの試験片を幅２５ｍｍで作製した。次に、ファスニング部材に５００ｇの錘を取り付けた後、おむつ本体側を上にして４０℃雰囲気下で吊り上げ、ファスニング部材がおむつ本体から離れて落下するまでの時間を測定した。結果を表２に示した。なお、サイドシートの外面側接合面とファスニング基材の肌面側接合面が、反応性ウレタンホットメルト接着剤の硬化物で接合されている。また、剥離時間は、４つの使い捨ておむつの左右のファスニング部材のそれぞれについて試験を行い、平均値で示した。
(Heat-resistant adhesion test)
Using a disposable diaper that has passed at room temperature for 5 days or more after production, the diaper body is positioned widthwise outward from the diaper body via a portion where the fastening member and the diaper body overlap from the diaper body positioned widthwise inward from the fastening member. A 100 mm long test piece with a width of 25 mm was produced, including the region extending to the fastening member. Next, after attaching a weight of 500 g to the fastening member, the diaper was lifted with the main body side up in an atmosphere of 40° C., and the time until the fastening member separated from the main body of the diaper and dropped was measured. Table 2 shows the results. In addition, the outer joint surface of the side sheet and the skin surface joint surface of the fastening base material are joined with a cured reactive urethane hot-melt adhesive. In addition, the peeling time was shown as an average value after testing each of the left and right fastening members of the four disposable diapers.
反応性ホットメルト接着剤を使用した接合部の剥離時間は、１０００分以上であり、非反応性ホットメルト接着剤を使用した接合部の剥離時間は７３分である。この結果より、反応性ホットメルト接着剤を使用した接合部は、耐熱接着性に優れていることが分かる。 The peel time for joints using reactive hot melt adhesives is greater than 1000 minutes and the peel time for joints using non-reactive hot melt adhesives is 73 minutes. From this result, it can be seen that the joints using the reactive hot-melt adhesive are excellent in heat-resistant adhesiveness.
接着力試験、および、耐熱接着力試験において、ホットメルト接着剤としては、以下の特性を有するものを使用した。
[反応性ウレタンホットメルト接着剤Ａ]
Ａ）溶融粘度１３０００～２００００ｍＰａ・ｓ／１２０℃
Ｂ）軟化点１００～１３０℃
Ｃ）ウレタンプレポリマーの数平均分子量は、１０００～１００００
Ｄ）ウレタンプレポリマー中のイソシアネート基含有率（ＮＣＯ％）は、１．７～５．０
Ｅ）ポリイソシアネートのイソシアネート基の合計と、ポリオール（Ｂ）水酸基の合計との比率（以下、ＮＣＯ／ＯＨ比と記す）は、１．１～５．０
[非反応性ホットメルト接着剤Ｂ]
モレスコ社製の非反応性ホットメルト接着剤（ＳＢＳ系ブロック共重合体、溶融粘度5200mPa・s／160℃、軟化点102℃）
In the adhesive force test and the heat resistant adhesive force test, hot melt adhesives having the following properties were used.
[Reactive Urethane Hot Melt Adhesive A]
A) Melt viscosity 13,000 to 20,000 mPa s/120°C
B) Softening point 100-130°C
C) The number average molecular weight of the urethane prepolymer is 1000 to 10000
D) The isocyanate group content (NCO%) in the urethane prepolymer is 1.7 to 5.0
E) The ratio of the total isocyanate groups of the polyisocyanate to the total hydroxyl groups of the polyol (B) (hereinafter referred to as the NCO/OH ratio) is 1.1 to 5.0.
[Non-reactive hot melt adhesive B]
Non-reactive hot melt adhesive manufactured by MORESCO (SBS block copolymer, melt viscosity 5200 mPa s/160°C, softening point 102°C)
１：使い捨ておむつ、２：おむつ本体、２ａ：前方部、２ｂ：後方背部、２ｃ：股部、１０：トップシート、２０：バックシート、３０：吸収コア、４０：サイドシート、４１：サイドシート用弾性部材、５１：腰周り用弾性部材、５２：足周り用弾性部材、５５：ホットメルト接着剤、６０：ファスニング部材、６１：ファスニング基材、６２：つまみ部、６３：第１止着部材、７０：第２止着部材、７２：反応性ウレタンホットメルト接着剤、９０：試験片 1: disposable diaper, 2: diaper main body, 2a: front part, 2b: rear back part, 2c: crotch part, 10: top sheet, 20: back sheet, 30: absorbent core, 40: side sheet, 41: for side sheet Elastic member 51: Waist elastic member 52: Leg elastic member 55: Hot melt adhesive 60: Fastening member 61: Fastening base material 62: Knob portion 63: First fastening member 70: Second fastening member, 72: Reactive urethane hot melt adhesive, 90: Test piece
Claims (9)
吸収コアの肌面側に設けられた表面シートと、
吸収コアの外面側に設けられた外装シートとを有する使い捨ておむつであって、
前記使い捨ておむつの縦方向両端部および幅方向両側部の少なくとも一箇所において、
前記表面シートと外装シートとが、反応性ウレタンホットメルト接着剤の硬化物と、非反応性ホットメルト接着剤とにより接合されている接合部が設けられていることを特徴とする使い捨ておむつ。 an absorbent core;
a surface sheet provided on the skin side of the absorbent core;
A disposable diaper having an outer sheet provided on the outer surface side of the absorbent core,
At least one of both longitudinal ends and both lateral sides of the disposable diaper,
A disposable diaper, wherein the surface sheet and the exterior sheet are provided with joints where they are joined by a cured reactive urethane hot-melt adhesive and a non-reactive hot-melt adhesive .