JP7068737B1 - 無機繊維用サイジング剤、無機繊維、その製造方法、及び複合材料 - Google Patents
無機繊維用サイジング剤、無機繊維、その製造方法、及び複合材料 Download PDFInfo
- Publication number
- JP7068737B1 JP7068737B1 JP2021198785A JP2021198785A JP7068737B1 JP 7068737 B1 JP7068737 B1 JP 7068737B1 JP 2021198785 A JP2021198785 A JP 2021198785A JP 2021198785 A JP2021198785 A JP 2021198785A JP 7068737 B1 JP7068737 B1 JP 7068737B1
- Authority
- JP
- Japan
- Prior art keywords
- resin
- sizing agent
- inorganic fiber
- surfactant
- inorganic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
上記課題を解決するために、本発明の一態様の無機繊維用サイジング剤では、樹脂(A)、及び下記の含フッ素界面活性剤(B)を含有することを要旨とする。
前記無機繊維用サイジング剤において、前記無機繊維用サイジング剤の不揮発分中における前記含フッ素界面活性剤(B)の含有割合が、10ppm以上60000ppm以下であってもよい。
前記無機繊維用サイジング剤において、前記樹脂(A)が、エポキシ樹脂、ビニルエステル樹脂、ポリアミド樹脂、ポリオレフィン樹脂、ポリウレタン樹脂、ポリカーボネート樹脂、ポリエステル樹脂、PEEK樹脂、フッ素樹脂、フェノキシ樹脂、フェノール樹脂、BMI樹脂、ポリイミド樹脂、ポリイミド樹脂前駆体、ポリエーテルスルホン樹脂、及びポリエーテルエステル樹脂から選ばれる少なくとも1つを含有するものであってもよい。
前記無機繊維用サイジング剤において、前記樹脂(A)の不揮発分及び前記界面活性剤(C)の含有割合の合計を100質量部とすると、前記樹脂(A)の不揮発分を20質量部以上99質量部以下及び前記界面活性剤(C)を1質量部以上80質量部以下の割合で含有してもよい。
上記課題を解決するために、本発明の別の態様の無機繊維の製造方法では、前記無機繊維用サイジング剤を無機繊維に付着させる工程を含むことを要旨とする。
先ず、本発明に係る無機繊維用サイジング剤(以下、サイジング剤ともいう)を具体化した第1実施形態について説明する。サイジング剤は、樹脂(A)と所定の含フッ素界面活性剤(B)とを含有する。
本実施形態のサイジング剤に供される樹脂(A)は、サイジング剤が付与される無機繊維の用途等に応じて適宜公知のものから選択される。樹脂の具体例としては、例えばエポキシ樹脂、ビニルエステル樹脂、ポリアミド樹脂、ポリオレフィン樹脂、ポリウレタン樹脂、ポリカーボネート樹脂、ポリエステル樹脂、PEEK樹脂、フッ素樹脂、フェノキシ樹脂、フェノール樹脂、BMI樹脂、ポリイミド樹脂、ポリイミド樹脂前駆体、ポリエーテルスルホン樹脂、ポリエーテルエステル樹脂等が挙げられる。これらの樹脂は、1種の樹脂を単独で使用してもよく、2種以上の樹脂を組み合わせて使用してもよい。
本実施形態のサイジング剤に供される含フッ素界面活性剤(B)は、分子中にパーフルオロアルケニル基を有する界面活性剤が適用される。また、本実施形態のサイジング剤に供される含フッ素界面活性剤(B)は、ポリオキシアルキレンパーフルオロアルケニルエーテルを含むものが好ましい。かかる構成により、マトリックス樹脂と無機繊維との接着性を向上できる。
サイジング剤は、必要によりさらに界面活性剤(C)(ただし、前記含フッ素界面活性剤(B)に該当するものを除く)を配合してもよい。界面活性剤(C)を配合することにより、サイジング剤の乳化安定性を向上できる。界面活性剤(C)としては、例えばアニオン界面活性剤、カチオン界面活性剤、非イオン界面活性剤、両性界面活性剤が挙げられる。これらの界面活性剤(C)は、1種の界面活性剤を単独で使用してもよく、2種以上の界面活性剤を組み合わせて使用してもよい。
サイジング剤中において、樹脂(A)の不揮発分及び界面活性剤(C)の含有割合の合計を100質量部とすると、樹脂(A)の不揮発分を20質量部以上99質量部以下及び界面活性剤(C)を1質量部以上80質量部以下の割合で含有することが好ましい。かかる範囲に規定されることにより、サイジング剤の乳化安定性を向上できる。
(1-1)本実施形態のサイジング剤では、樹脂(A)及び所定の含フッ素界面活性剤(B)を含有するように構成した。したがって、無機繊維に対する付着斑の低減効果を向上できる。また、サイジング剤で処理された無機繊維の集束性を向上できる。また、母材に対する無機繊維の接着性を向上できる。
次に本発明に係る無機繊維の製造方法を具体化した第2実施形態について説明する。第2実施形態について、下記の記載以外は、第1実施形態と同様の構成が適用される。
本実施形態において適用される無機繊維の種類としては、特に限定されず、例えばガラス繊維、炭素繊維、セラミック繊維、金属繊維、鉱物繊維、岩石繊維、スラッグ繊維等が挙げられる。これらの中でも本発明の効果をより有効に発現できる観点からガラス繊維、炭素繊維が好ましい。炭素繊維の種類としては、例えばアクリル繊維を原料として得られたPAN系炭素繊維、ピッチを原料として得られたピッチ系炭素繊維、リサイクル炭素繊維、ポリエステル繊維、ポリエチレン樹脂、フェノール樹脂、セルロース樹脂、リグニン樹脂等を原料として得られる炭素繊維が挙げられる。本発明において、濾材を構成するガラス繊維にバインダーとフッ素系界面活性剤とを付着させたエアフィルタ用濾材は除かれる。
(2-1)本実施形態の無機繊維の製造方法では、樹脂(A)及び所定の含フッ素界面活性剤(B)を含有するサイジング剤を炭素繊維に付着させる工程を含んでいる。したがって、無機繊維に対するサイジング剤の付着斑の低減効果が期待され、効率的にサイジング剤を無機繊維に対して付着処理できる。
次に、本発明に係る複合材料を具体化した第3実施形態について説明する。第3実施形態について、下記の記載以外は、第1,2実施形態と同様の構成が適用される。
マトリックス樹脂は、複合材料の目的、用途等に応じて公知のものから適宜選択される。マトリックス樹脂の具体例としては、例えばエポキシ樹脂、ビニルエステル樹脂、ポリアミド樹脂、ポリオレフィン樹脂、ポリウレタン樹脂、ポリカーボネート樹脂、ポリエステル樹脂、PEEK樹脂、フッ素樹脂、フェノキシ樹脂、フェノール樹脂、BMI樹脂、ポリイミド樹脂、ポリイミド樹脂前駆体、ポリエーテルスルホン樹脂等が挙げられる。ポリオレフィン樹脂の具体例としては、例えばポリプロピレン樹脂、ポリエチレン等が挙げられる。
(3-1)本実施形態の複合材料では、樹脂(A)及び所定の含フッ素界面活性剤(B)を含有するサイジング剤を適用している。したがって、無機繊維とマトリックス樹脂との優れた接着性により、特に機械特性等の各種特性に優れる繊維強化樹脂複合材料が得られる。
・上記実施形態のサイジング剤は、本発明の効果を阻害しない範囲内において、サイジング剤の性能を維持する観点、無機繊維に対する付与性向上等の観点から、その他の成分として、水又は有機溶媒、平滑剤、酸化防止剤、防腐剤等を配合することを妨げるものではない。
実施例1のサイジング剤は、原料として表1に示される含フッ素界面活性剤(B-1)、樹脂(A)として表2に示されるエポキシ樹脂(A-1)、界面活性剤(C)として表3に示されるトリスチレン化フェノールのエチレンオキサイド34モルとプロピレンオキサイド4モルのランダム付加物(C-1)を使用した。
C:予め製造された樹脂(A)を含む乳化物と含フッ素界面活性剤(B)を混合することでサイジング剤の水性液を得た。
E:樹脂(A)と界面活性剤(C)を混合したものに徐々に水を加えてサイジング剤の水性液を得た。
含フッ素界面活性剤(B)の種類と含有量、樹脂(A)の種類と不揮発分としての含有量、界面活性剤(C)の種類と含有量、サイジング剤の調製方法を、表4の「含フッ素界面活性剤(B)」欄、「樹脂(A)」欄、「界面活性剤(C)」欄、「製造時の混合方法」欄にそれぞれ示す。
エポキシ樹脂(三菱ケミカル社製 商品名:jER828+トリエチレンテトラミン)
ビニルエステル樹脂(昭和電工社製 商品名:リポキシR-804B(同社製メチルエチルケトンパーオキシド硬化剤使用))
ポリアミド樹脂(宇部興産社製 UBEナイロン 1011FB)
ポリプロピレン樹脂:2%無水マレイン酸変性ポリプロピレン
*1)樹脂(A)の不揮発分100部に対する含有割合(部)
*2)サイジング剤の不揮発分中における含フッ素界面活性剤(B)の含有割合(ppm)
*3)不揮発分基準
なお、不揮発分は、対象物を105℃で2時間熱処理して揮発性物質を十分に除去した絶乾物の質量として求めた。
接着性は、市販の複合材界面特性評価装置を用いてマイクロドロップレット法によって測定される応力により評価した。図1に複合材界面特性評価装置10の概略図を示す。
エポキシ樹脂:60MPa
ビニルエステル樹脂:40MPa
ポリアミド樹脂:50MPa
ポリプロピレン樹脂:22MPa
・接着性の評価基準
◎◎(優れる):増加率が12%以上
◎(良好):増加率が9%以上12%未満
○(可):増加率が1%以上9%未満
×(不可):増加率が1%未満
試験区分3(付着斑抑制の評価)
試験区分2で得られたサイジング剤が付与されたストランド状炭素繊維について、十分に乾燥させた炭素繊維束から1m毎に10か所で5mgの炭素繊維をサンプリングした。熱重量・示差熱同時測定(TG-DTA)で40℃→500℃まで10℃/分で昇温後、10分500℃を保持させた際の初期質量から最終質量の差分をサイジング剤付着量とした。10か所の測定値の標準偏差の値を以下の基準で評価した。結果を表4の「付着斑抑制」欄に示す。
◎(良好):0.2未満
○(可):0.2以上0.3未満
×(不可):0.3以上
試験区分4(集束性の評価)
試験区分2で得られたサイジング剤が付与されたストランド状炭素繊維について、乾燥工程を経たのちの金属ローラー部分での糸の集束性を目視にて以下の基準で評価した。結果を表4の「集束性」欄に示す。
○(可):糸が纏まって金属ローラーを通過しており、工程性に問題が無い場合
×(不可):糸が纏まっておらず金属ローラーへの巻きつきが生じている場合
以上表4の結果からも明らかなように、各実施例のサイジング剤が付与された無機繊維は、付着斑抑制及び集束性の評価はいずれも可以上であった。また、サイジング剤が付与された無機繊維のマトリックス樹脂に対する接着性の評価はいずれも可以上であった。本発明によれば、付着斑抑制、集束性、接着性を向上できるという効果が生じる。
11…ホルダー
12…繊維
13…樹脂滴
14…接着剤
15…ロードセル
16…基板
17,18…ブレード
Claims (13)
- 樹脂(A)、及び下記の含フッ素界面活性剤(B)を含有することを特徴とする無機繊維用サイジング剤。
含フッ素界面活性剤(B):分子中にパーフルオロアルケニル基を有する界面活性剤。 - 前記無機繊維用サイジング剤の不揮発分中における前記含フッ素界面活性剤(B)の含有割合が、10ppm以上60000ppm以下である請求項1に記載の無機繊維用サイジング剤。
- 前記含フッ素界面活性剤(B)が、ポリオキシアルキレンパーフルオロアルケニルエーテルを含むものである請求項1又は2に記載の無機繊維用サイジング剤。
- 前記樹脂(A)が、エポキシ樹脂、ビニルエステル樹脂、ポリアミド樹脂、ポリオレフィン樹脂、ポリウレタン樹脂、ポリカーボネート樹脂、ポリエステル樹脂、PEEK樹脂、フッ素樹脂、フェノキシ樹脂、フェノール樹脂、BMI樹脂、ポリイミド樹脂、ポリイミド樹脂前駆体、ポリエーテルスルホン樹脂、及びポリエーテルエステル樹脂から選ばれる少なくとも1つを含有するものである請求項1~3のいずれか一項に記載の無機繊維用サイジング剤。
- 前記樹脂(A)の不揮発分の全質量を100質量部としたとき、前記含フッ素界面活性剤(B)を0.001質量部以上6質量部以下の割合で含有する請求項1~4のいずれか一項に記載の無機繊維用サイジング剤。
- 更に、界面活性剤(C)(ただし、前記含フッ素界面活性剤(B)に該当するものを除く)を含有する請求項1~4のいずれか一項に記載の無機繊維用サイジング剤。
- 前記樹脂(A)の不揮発分及び前記界面活性剤(C)の含有割合の合計を100質量部とすると、前記樹脂(A)の不揮発分を20質量部以上99質量部以下及び前記界面活性剤(C)を1質量部以上80質量部以下の割合で含有する請求項6に記載の無機繊維用サイジング剤。
- 請求項1~7のいずれか一項に記載の無機繊維用サイジング剤が付着していることを特徴とする無機繊維(濾材を構成するガラス繊維にバインダーとフッ素系界面活性剤とを付着させたエアフィルタ用濾材を除く)。
- 請求項1~7のいずれか一項に記載の無機繊維用サイジング剤を無機繊維に付着させる工程を含むことを特徴とする無機繊維の製造方法。
- 請求項8に記載の無機繊維とマトリックス樹脂とを含む複合材料であって、前記無機繊維用サイジング剤中の樹脂が、エポキシ樹脂、ポリウレタン樹脂、ポリエステル樹脂、フェノキシ樹脂、及びポリエーテルエステル樹脂から選ばれる少なくとも1つを含み、前記マトリックス樹脂がエポキシ樹脂であることを特徴とする複合材料。
- 請求項8に記載の無機繊維とマトリックス樹脂とを含む複合材料であって、前記無機繊維用サイジング剤中の樹脂がポリウレタン樹脂、ポリイミド樹脂前駆体、及びポリアミド樹脂から選ばれる少なくとも1つを含み、前記マトリックス樹脂がポリアミド樹脂であることを特徴とする複合材料。
- 請求項8に記載の無機繊維とマトリックス樹脂とを含む複合材料であって、前記無機繊維用サイジング剤中の樹脂がビニルエステル樹脂を含み、前記マトリックス樹脂がビニルエステル樹脂であることを特徴とする複合材料。
- 請求項8に記載の無機繊維とマトリックス樹脂とを含む複合材料であって、前記無機繊維用サイジング剤中の樹脂がポリオレフィン樹脂を含み、前記マトリックス樹脂がポリプロピレン樹脂であることを特徴とする複合材料。