JP7022721B2 - Anti-termite electric wire / cable - Google Patents
Anti-termite electric wire / cable Download PDFInfo
- Publication number
- JP7022721B2 JP7022721B2 JP2019115597A JP2019115597A JP7022721B2 JP 7022721 B2 JP7022721 B2 JP 7022721B2 JP 2019115597 A JP2019115597 A JP 2019115597A JP 2019115597 A JP2019115597 A JP 2019115597A JP 7022721 B2 JP7022721 B2 JP 7022721B2
- Authority
- JP
- Japan
- Prior art keywords
- termite
- sheath
- mass
- cable
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、防蟻電線・ケーブルに関する。 The present invention relates to an anti-termite electric wire / cable.
電線などのケーブルにおいては、シロアリなどの蟻による食害を防止するために、たとえば、防蟻剤が添加された防蟻コンパウンドで形成された防蟻シースで周囲を被覆することが提案されている。防蟻剤としては、たとえば、クロチアニジンなどのネオニコチノイド系化合物が用いられている。 In cables such as electric wires, it has been proposed to cover the periphery with an anti-termite sheath formed of an anti-termite compound, for example, in order to prevent feeding damage by ants such as termites. As the termiticide, for example, a neonicotinoid compound such as clothianidin is used.
クロチアニジンは、クロチアニジンの添加量を多くしすぎた場合、防蟻効果が飽和し、高価な材料であるので不経済になる。また、クロチアニジンの添加割合が増加するに伴って、耐寒性が低下する。これに対して、ケーブルの寿命を考慮して防蟻効果を長期的に持続させるように、クロチアニジンの初期添加量を設定する必要がある。このため、耐寒性と防蟻効果とを両立させることは容易でない。 If the amount of clothianidin added is too large, the clothianidin has a saturated anti-termite effect and is an expensive material, which is uneconomical. Further, as the addition ratio of clothianidin increases, the cold resistance decreases. On the other hand, it is necessary to set the initial addition amount of clothianidin so that the anti-termite effect can be maintained for a long period of time in consideration of the life of the cable. Therefore, it is not easy to achieve both cold resistance and ant-proofing effect.
防蟻剤が添加された防蟻シースを使用せずに、ナイロン樹脂などのように硬く強靭な樹脂の被覆をケーブルの最外層に設けることが提案されている。しかし、この場合には、ケーブルの可撓性が低下し、許容曲げ半径が大きくなる問題がある。 It has been proposed to provide a coating of a hard and tough resin such as nylon resin on the outermost layer of the cable without using an anti-termite sheath to which an anti-termite agent is added. However, in this case, there is a problem that the flexibility of the cable is lowered and the allowable bending radius is increased.
上記したように、従来の防蟻コンパウンドを用いた防蟻シースにおいては、耐寒性と防蟻効果とを両立させることが容易でない。 As described above, in the anti-termite sheath using the conventional anti-termite compound, it is not easy to achieve both cold resistance and anti-termite effect.
したがって、本発明が解決しようとする課題は、耐寒性と防蟻効果とを容易に両立可能な防蟻電線・ケーブルを提供することである。 Therefore, an object to be solved by the present invention is to provide an anti-termite electric wire / cable that can easily achieve both cold resistance and anti-termite effect.
本発明の防蟻電線・ケーブルは、100質量部の塩化ビニル樹脂に対して、0.01質量部以上0.17質量部以下のクロチアニジンと、20質量部以上40質量部以下の可塑剤と、を含有する防蟻コンパウンドを用いて形成され、前記可塑剤は、少なくとも10質量部以上の脂肪族二塩基酸エステルを含み、前記脂肪族二塩基酸エステルは、アジピン酸エステルとアゼライン酸エステルとセバシン酸エステルの少なくとも1つが用いられる。 The anti-termite electric wire / cable of the present invention comprises 100 parts by mass of vinyl chloride resin, 0.01 parts by mass or more and 0.17 parts by mass or less of clothianidin, and 20 parts by mass or more and 40 parts by mass or less of a plasticizer. The plasticizer contains at least 10 parts by mass or more of an aliphatic dibasic acid ester, and the aliphatic dibasic acid ester is an adipate ester, an azelaic acid ester and a sebacic acid. At least one of the acid esters is used.
本発明によれば、耐寒性と防蟻効果とを容易に両立可能な防蟻電線・ケーブルを提供することができる。 According to the present invention, it is possible to provide an anti-termite electric wire / cable that can easily achieve both cold resistance and anti-termite effect.
以下より、発明の実施形態について図面を用いて例示する。なお、発明は、図面の内容に限定されない。また、図面は、概略を示すものであって、各部の寸法比などは、現実のものとは必ずしも一致しない。 Hereinafter, embodiments of the invention will be illustrated with reference to the drawings. The invention is not limited to the contents of the drawings. Further, the drawings show an outline, and the dimensional ratios of each part do not always match the actual ones.
[A]防蟻電線・ケーブル
図1は、実施形態に係る防蟻電線・ケーブル1の構成を模式的に示す断面図である。図1では、防蟻電線・ケーブル1の延在方向zが直交する断面(xy面)を示している。
[A] Anti-termite electric wire / cable FIG. 1 is a cross-sectional view schematically showing the configuration of the anti-termite electric wire /
実施形態の防蟻電線・ケーブル1は、図1に示すように、ケーブルコア10とシース20と防蟻シース30とを有する。防蟻電線・ケーブル1を構成する各部について順次説明する。
As shown in FIG. 1, the anti-termite electric wire /
[A-1]ケーブルコア10
ケーブルコア10は、複数の絶縁線心11を含む。ここでは、3本の絶縁線心11を含むようにケーブルコア10が構成されている。
[A-1]
The
ケーブルコア10において、絶縁線心11は、導体111の外周面が絶縁層112で被覆されている。絶縁線心11のうち、導体111は、銅、アルミニウムなどの導電材料で形成されており、絶縁層112は、ポリエチレン、架橋ポリエチレンなどの絶縁材料で形成されている。そして、ケーブルコア10では、複数の絶縁線心11が介在12と共に撚り合わされて構成されている。介在12は、紙、ジュートなどの絶縁材料で形成されている。
In the
[A-2]シース20
シース20は、ケーブルコア10の外周面を被覆するように設けられている。シース20は、ポリエチレン、架橋ポリエチレン、塩化ビニル樹脂などの絶縁樹脂について押出成形を実行することによって形成されている。
[A-2] Sheath 20
The
[A-3]防蟻シース30
防蟻シース30は、シース20を介してケーブルコア10の外周面を被覆するように設けられている。防蟻シース30は、厚みが、たとえば、0.2mm以上である。防蟻シース30は、防蟻剤を含む防蟻コンパウンドについて押出成形を実行することによって形成されている。
[A-3]
The
[B]防蟻コンパウンド
防蟻シース30の形成で用いられる防蟻コンパウンドについて説明する。
[B] Anti-termite compound An anti-termite compound used in forming the
本実施形態において、防蟻コンパウンドは、塩化ビニル樹脂(ポリ塩化ビニル)と防蟻剤と可塑剤とを含有している混合物(防蟻樹脂組成物)である。具体的には、本実施形態の防蟻コンパウンドは、100質量部の塩化ビニル樹脂に対して、0.01質量部以上0.50質量部以下のクロチアニジンを防蟻剤として含有すると共に、脂肪族二塩基酸エステルを含む可塑剤を含有する。 In the present embodiment, the anti-termite compound is a mixture (anti-termite resin composition) containing a vinyl chloride resin (polyvinyl chloride), an anti-termite agent and a plasticizer. Specifically, the anti-termite compound of the present embodiment contains 0.01 parts by mass or more and 0.50 parts by mass or less of clothianidin as an anti-termite agent with respect to 100 parts by mass of vinyl chloride resin, and is aliphatic. Contains a plasticizer containing a dibasic acid ester.
[B-1]防蟻剤
防蟻コンパウンドにおいて防蟻剤として添加されるクロチアニジンは、下記の化学式で示される。
[B-1] Termiticide The clothianidin added as an termiticide in the termiticide compound is represented by the following chemical formula.
クロチアニジンは、シロアリに対する防蟻効果(殺蟻効果)に優れる防蟻剤であって、蒸気圧が非常に低く環境へ容易に揮散しないので、環境汚染性が低い。また、クロチアニジンは、毒劇物取締法の適用も受けない。このため、クロチアニジンは、安全性が非常に高い。さらに、クロチアニジンは、防蟻コンパウンドの押出加工性を損なわず、ケーブルにおいて一般に要求される電気特性などの特性を低下させることもない。 Crossianidin is an anti-termite agent having an excellent anti-termite effect (anti-termite effect) on termites, and has a very low vapor pressure and does not easily volatilize into the environment, so that it has low environmental pollution. In addition, clothianidin is not subject to the Poisonous and Deleterious Substances Control Law. For this reason, clothianidin is extremely safe. In addition, clothianidin does not impair the extrudability of the anti-termite compound and does not reduce properties such as electrical properties commonly required for cables.
上述したように、防蟻コンパウンドでは、100質量部の塩化ビニル樹脂に対して、0.01質量部以上0.50質量部以下のクロチアニジンが添加される。クロチアニジンの添加割合が上記範囲の下限値未満である場合には、防蟻シース30の防蟻効果に関する耐久性が不十分になる場合がある。クロチアニジンの添加割合が上記範囲の上限値を超える場合には、防蟻効果が上記範囲とほぼ同等であるにも関わらずに、クロチアニジンによる材料コストが上昇すると共に、耐寒性の低下が生ずる場合がある。
As described above, in the anti-termite compound, clothianidin of 0.01 part by mass or more and 0.50 part by mass or less is added to 100 parts by mass of vinyl chloride resin. If the addition ratio of clothianidin is less than the lower limit of the above range, the durability of the
防蟻コンパウンドにおいて、クロチアニジンは、たとえば、塩化ビニル樹脂に直接練り込まれている。この他に、クロチアニジンが徐々に外部へ放出する徐放性を有するように、クロチアニジンをマイクロカプセルの内部に包含した状態で塩化ビニル樹脂に混入されていてもよい。 In the anti-termite compound, clothianidin is kneaded directly into, for example, a vinyl chloride resin. In addition, the clothianidin may be mixed with the vinyl chloride resin in a state of being encapsulated in the microcapsules so that the clothianidin has a sustained release property that is gradually released to the outside.
[B-2]可塑剤
防蟻コンパウンドにおいて、可塑剤は、少なくとも脂肪族二塩基酸エステルが用いられる。
[B-2] Plasticizer In the anti-termite compound, at least an aliphatic dibasic acid ester is used as the plasticizer.
脂肪族二塩基酸エステルとしては、下記に示すように、アジピン酸エステルとアゼライン酸エステルとセバシン酸エステルの少なくとも1つを用いることが好適である。 As the aliphatic dibasic acid ester, as shown below, it is preferable to use at least one of adipate ester, azelaic acid ester and sebacic acid ester.
(アジピン酸エステル)
・アジピン酸ジ(2-エチルヘキシル)(略号:DOA)
・アジピン酸ジイソノニル(略号:DINA)
・アジピン酸ジイソデシル(略号:DIDA)
(Adipate ester)
・ Di (2-ethylhexyl) adipate (abbreviation: DOA)
・ Diisononyl adipate (abbreviation: DINA)
・ Diisodecyl adipate (abbreviation: DIDA)
(アゼライン酸エステル)
・アゼライン酸ジ(2-エチルヘキシル)(略号:DOZ)
(Azelaic acid ester)
-Di (2-ethylhexyl) azelaic acid (abbreviation: DOZ)
(セバシン酸エステル)
・セバシン酸ジ(2-エチルヘキシル)(略号:DOS)
( Sebacic acid ester)
-Di (2-ethylhexyl) sebacate (abbreviation: DOS)
また、上記の脂肪族二塩基酸エステル以外の可塑剤を用いてもよい。たとえば、下記に示すように、一般的に用いられている可塑剤を、脂肪族二塩基酸エステルと併用してもよい。
・フタル酸ジイソノニル(略号:DINP)
・トリオクチルトリメリテート(略号:TOTM)
Further, a plasticizer other than the above-mentioned aliphatic dibasic acid ester may be used. For example, as shown below, commonly used plasticizers may be used in combination with aliphatic dibasic acid esters.
・ Diisononyl phthalate (abbreviation: DINP)
・ Trioctilt Limeritate (abbreviation: TOTM)
防蟻コンパウンドにおいて、可塑剤を添加する添加割合は、防蟻シース30において必要な特性に応じて任意に設定可能であるが、たとえば、100質量部の塩化ビニル樹脂に対して、20質量部以上60質量部以下の可塑剤を添加することが好ましい。これにより、防蟻シース30について強度と柔軟性とを両立可能である。
In the anti-termite compound, the addition ratio of the plasticizer can be arbitrarily set according to the characteristics required for the
また、脂肪族二塩基酸エステルについては、100質量部の塩化ビニル樹脂に対して、2質量部以上を可塑剤として添加することが好ましい。詳細については後述するが、これにより、防蟻シース30の耐寒性について十分に向上可能である。
As for the aliphatic dibasic acid ester, it is preferable to add 2 parts by mass or more as a plasticizer to 100 parts by mass of the vinyl chloride resin. The details will be described later, but this can sufficiently improve the cold resistance of the ant-
[B-3]その他の添加剤
防蟻コンパウンドにおいては、必要な特性に応じて、防蟻剤および可塑剤以外の添加剤を塩化ビニル樹脂に添加してもよい。たとえば、防蟻シース30に難燃性を付与する場合には、難燃剤を防蟻コンパウンドに添加してよい。当然ながら、シース20が難燃剤を含有していてもよい。また、シース20が難燃剤を含有し、防蟻シース30が難燃剤を含有せずに、防蟻剤および可塑剤を含有するように構成してもよい。
[B-3] Other Additives In the termiticide compound, additives other than termiticide and plasticizer may be added to the vinyl chloride resin, depending on the required properties. For example, when imparting flame retardancy to the
その他、添加剤として、充填剤や熱安定剤を、適宜、添加してもよい。 In addition, as an additive, a filler or a heat stabilizer may be appropriately added.
[C]製造方法
本実施形態の防蟻電線・ケーブル1の製造方法について説明する。
[C] Manufacturing Method A manufacturing method of the anti-termite electric wire /
上記の防蟻電線・ケーブル1を製造する際には、たとえば、押出機を用いて、ケーブルコア10の外周面にシース20と防蟻シース30とを同時に形成する。この他に、ケーブルコア10の外周面にシース20を形成した後に、シース20の外周面に防蟻シース30を形成してもよい。
When manufacturing the above-mentioned anti-termite electric wire /
[D]まとめ
以上のように、実施形態に係る防蟻コンパウンドで作製された防蟻シース30は、防蟻剤であるクロチアニジンの添加割合が上記した特定範囲であるので、環境汚染性が低く、押出加工性が高く、好適な電気特性を備える。また、詳細については後述の実施例等で説明するが、実施形態に係る防蟻コンパウンドで作製された防蟻シース30は、耐寒性と防蟻効果とを両立可能である。
[D] Summary As described above, the
[E]変形例
上記の実施形態では、ケーブルコア10とシース20と防蟻シース30とを有する防蟻電線・ケーブル1について説明したが、これに限らない。
[E] Modification Example In the above embodiment, the ant-proof electric wire /
図2および図3は、実施形態の変形例に係る防蟻電線・ケーブル1の構成を模式的に示す断面図である。図2および図3では、図1と同様に、防蟻電線・ケーブル1の延在方向zが直交する断面(xy面)を示している。
2 and 3 are cross-sectional views schematically showing the configuration of the ant-proof electric wire /
図2に示すように、防蟻電線・ケーブル1は、シース20(図1参照)を備えておらず、ケーブルコア10の外周面を防蟻シース30が直接被覆するように構成してもよい。この場合、防蟻シース30の厚みを、上記実施形態の場合(図1参照)よりも厚くしてもよい。
As shown in FIG. 2, the anti-termite electric wire /
この他に、図3に示すように、防蟻電線・ケーブル1は、絶縁線心11が複数でなく、単数であってもよい。この場合には、たとえば、絶縁線心11の外周面をシース20と防蟻シース30とが順次積層するように構成する。図示を省略しているが、防蟻電線・ケーブル1は、絶縁線心11の外周面を防蟻シース30が直接被覆する構成(図3においてシース20を備えない構成)としてもよい。また、防蟻電線・ケーブル1は、導体111の外周面に防蟻コンパウンドを用いて形成される絶縁層からなる構成(図3においてシース20、防蟻シース30を備えず、かつ、絶縁層112の材料が防蟻シース30の材料で形成される構成)としてもよい。
In addition to this, as shown in FIG. 3, the ant-proof electric wire /
以下より、実施例および比較例に関して、表1および表2を用いて説明する。なお、理解を容易にするため、実施例および比較例の説明では、上記の実施形態と同様に、各部の符号を適宜用いている。 Hereinafter, Examples and Comparative Examples will be described with reference to Tables 1 and 2. In addition, in order to facilitate understanding, in the description of Examples and Comparative Examples, the reference numerals of the respective parts are appropriately used as in the above-described embodiment.
[1]試料の作製
[1-1]実施例A-1から実施例A-4
実施例A-1においては、表1に示すように、塩化ビニル樹脂に、可塑剤としてアゼライン酸ジ(2-エチルヘキシル)(略号:DOZ)とフタル酸ジイソノニル(略号:DINP)とを添加し、防蟻剤としてクロチアニジンを添加し、充填剤として炭酸カルシウムを添加し、熱安定剤として非鉛安定剤を添加することによって、防蟻コンパウンドを作製した。
[1] Preparation of sample [1-1] Examples A-1 to A-4
In Example A-1, as shown in Table 1, di (2-ethylhexyl) azelaic acid (abbreviation: DOZ) and diisononyl phthalate (abbreviation: DINP) were added to the vinyl chloride resin as plasticizers. An anti-termite compound was prepared by adding clothianidin as an anti-termite agent, calcium carbonate as a filler, and a lead-free stabilizer as a heat stabilizer.
具体的には、100質量部の塩化ビニル樹脂(重合度:1700)と、10質量部のアゼライン酸ジ(2-エチルヘキシル)(略号:DOZ)と、30質量部のフタル酸ジイソノニル(略号:DINP)と、0.01質量部のクロチアニジンと、30質量部の炭酸カルシウム(平均粒径:1.8μm,比表面積:12000cm2/g)と、5質量部の非鉛安定剤(ステアリン酸亜鉛とハイドロタルサイトとの混合物)とを混合し、160℃のオープンロールを用いて均一に混練した後、180℃でプレス成形し、防蟻コンパウンドのシート試料を作製した。 Specifically, 100 parts by mass of vinyl chloride resin (polymerization degree: 1700), 10 parts by mass of di (2-ethylhexyl) azereate (abbreviation: DOZ), and 30 parts by mass of diisononyl phthalate (abbreviation: DINP). ), 0.01 parts by mass of clothianidin, 30 parts by mass of calcium carbonate (average particle size: 1.8 μm, specific surface area: 12000 cm 2 / g), and 5 parts by mass of lead-free stabilizer (with zinc stearate). (Mixed with hydrotalcite) was mixed and uniformly kneaded using an open roll at 160 ° C., and then press-molded at 180 ° C. to prepare a sheet sample of an anti-termite compound.
実施例A-2、参考例A-3、参考例A-4のそれぞれにおいては、表1に示すように、クロチアニジンの添加割合が実施例A-1の場合と異なる点を除き、実施例A-1の場合と同様に、防蟻コンパウンドを作製した後に、試料を形成した。 In each of Example A-2 , Reference Example A-3, and Reference Example A-4 , as shown in Table 1, Example A except that the addition ratio of clothianidin is different from that of Example A-1. As in the case of -1, a sample was formed after preparing the anti-termite compound.
[1-2]参考例B-1,実施例B-2
参考例B-1、実施例B-2のそれぞれにおいては、表1に示すように、アゼライン酸ジ(2-エチルヘキシル)(略号:DOZ)およびフタル酸ジイソノニル(略号:DINP)との添加割合が実施例A-2の場合と異なる点を除き、実施例A-2の場合と同様に、防蟻コンパウンドを作製した後に、試料を形成した。
[1-2] Reference Example B-1 , Example B-2
In Reference Example B-1 and Example B-2, as shown in Table 1, the addition ratios of di (2-ethylhexyl) azelaate (abbreviation: DOZ) and diisononyl phthalate (abbreviation: DINP) are As in the case of Example A-2, a sample was formed after preparing the anti-termite compound, except that the case was different from that of Example A-2.
[1-3]実施例C-1から実施例C-4
実施例C-1から実施例C-4のそれぞれにおいては、表2に示すように、アゼライン酸ジ(2-エチルヘキシル)(略号:DOZ)以外の脂肪族二塩基酸エステルを用いた点を除き、実施例A-1の場合と同様に、防蟻コンパウンドを作製した後に、シート状の試料を形成した。
[1-3] Examples C-1 to C-4
In each of Examples C-1 to C-4, as shown in Table 2, except that an aliphatic dibasic acid ester other than di (2-ethylhexyl) azelaic acid (abbreviation: DOZ) was used. In the same manner as in Example A-1, a sheet-shaped sample was formed after preparing the anti-termite compound.
具体的には、実施例C-1では、アジピン酸ジ(2-エチルヘキシル)(略号:DOA)を用いた。実施例C-2では、アジピン酸ジイソノニル(略号:DINA)を用いた。実施例C-3では、アジピン酸ジイソデシル(略号:DIDA)を用いた。実施例C-4では、セバシン酸ジ(2-エチルヘキシル)(略号:DOS)を用いた。 Specifically, in Example C-1, di (2-ethylhexyl) adipate (abbreviation: DOA) was used. In Example C-2, diisononyl adipate (abbreviation: DINA) was used. In Example C-3, diisodecyl adipate (abbreviation: DIDA) was used. In Example C-4, di (2-ethylhexyl) sebacate (abbreviation: DOS) was used.
[1-4]参考例D
参考例Dにおいては、表2に示すように、アゼライン酸ジ(2-エチルヘキシル)(略号:DOZ)およびフタル酸ジイソノニル(略号:DINP)との添加割合が参考例A-4の場合と異なる点を除き、参考例A-4の場合と同様に、防蟻コンパウンドを作製した後に、試料を形成した。
[1-4] Reference Example D
In Reference Example D, as shown in Table 2, the addition ratios of di (2-ethylhexyl) azelaate (abbreviation: DOZ) and diisononyl phthalate (abbreviation: DINP) are different from those in Reference Example A-4. A sample was formed after preparing the anti-termite compound in the same manner as in Reference Example A-4.
[1-5]比較例X-1,比較例X-2
比較例X-1においては、表2に示すように、クロチアニジンの添加割合が実施例A-1の場合と異なる点を除き、実施例A-1の場合と同様に、防蟻コンパウンドを作製した後に、試料を形成した。
[1-5] Comparative Example X-1, Comparative Example X-2
In Comparative Example X-1, as shown in Table 2, an ant-proof compound was prepared in the same manner as in Example A-1 except that the addition ratio of clothianidin was different from that in Example A-1. Later, a sample was formed.
比較例X-2においては、アゼライン酸ジ(2-エチルヘキシル)(略号:DOZ)およびフタル酸ジイソノニル(略号:DINP)との添加割合が実施例A-4の場合と異なる点を除き、実施例A-4の場合と同様に、防蟻コンパウンドを作製した後に、シート状の試料を形成した。比較例X-2では、アゼライン酸ジ(2-エチルヘキシル)(略号:DOZ)が添加されていない。 In Comparative Example X-2, Examples were obtained except that the addition ratios of di (2-ethylhexyl) azelaic acid (abbreviation: DOZ) and diisononyl phthalate (abbreviation: DINP) were different from those of Example A-4. As in the case of A-4, a sheet-shaped sample was formed after preparing the anti-termite compound. In Comparative Example X-2, di (2-ethylhexyl) azelaic acid (abbreviation: DOZ) was not added.
[2]試験方法
上記のように作製した各例の試料に関して、表1および表2に示すように、各種の試験を行った。
[2] Test method As shown in Tables 1 and 2, various tests were performed on the samples of each example prepared as described above.
[2-1]防蟻効果
防蟻効果を確認する試験を行う際には、まず、各例において作成した防蟻シート(50×50mm、厚さ1mm)の上面に塩化ビニル製のパイプ(直径25mm、高さ10mm)を設置した。ここでは、パイプの管軸がシートの上面に対して直交するように、パイプの設置を行った。その後、シートの上面に設置されたパイプの内部に、50頭のシロアリを入れた。そして、シロアリの挙動を経時的に観察し、シロアリのノックダウン率を求めた。なお、シロアリのノックダウン率とは、試験に使用したシロアリのうち死亡したシロアリの割合である。
[2-1] Anti-termite effect When conducting a test to confirm the anti-termite effect, first, a vinyl chloride pipe (diameter) is placed on the upper surface of the anti-termite sheet (50 × 50 mm,
表1および表2においては、下記の判定基準に基づいて、防蟻効果の確認試験を行った結果を示した。
・○;シロアリのノックダウン率が24時間以内に80%を超えた場合
・×;シロアリのノックダウン率が24時間以内に80%以下の場合
Tables 1 and 2 show the results of a confirmation test of the ant-proofing effect based on the following criteria.
・ ○; When the termite knockdown rate exceeds 80% within 24 hours ・ ×; When the termite knockdown rate is 80% or less within 24 hours
[2-2]耐寒性
耐寒性を確認する試験については、「JIS C 3005(2014) 4.22項 耐寒」に記載された内容に基づいて実行した。試験は、温度を1℃刻みで変えた条件で実行した。
[2-2] Cold resistance The test for confirming cold resistance was carried out based on the contents described in "JIS C 3005 (2014) Section 4.22 Cold resistance". The test was performed under conditions where the temperature was changed in 1 ° C increments.
表1および表2においては、各例の試料において破壊が発生しない最低温度を示した。 In Tables 1 and 2, the minimum temperature at which fracture does not occur in the samples of each example is shown.
[3]試験結果
[3-1]実施例A-1、実施例A-2、参考例A-3、参考例A-4の試験結果について
実施例A-1、実施例A-2、参考例A-3、参考例A-4のそれぞれの防蟻コンパウンドは、100質量部の塩化ビニル樹脂に対して、0.01質量部以上0.50質量部以下のクロチアニジンを防蟻剤として含有すると共に、脂肪族二塩基酸エステルを含む可塑剤を含有している。このため、実施例A-1、実施例A-2、参考例A-3、参考例A-4では、耐寒性と防蟻効果とを両立可能である。
[3] Test results [3-1] Test results of Example A-1 , Example A-2, Reference Example A-3, Reference Example A-4 Example A-1 , Example A-2, Reference Each of the anti-termite compounds of Examples A-3 and Reference Example A-4 contains 0.01 parts by mass or more and 0.50 parts by mass or less of clothianidin as an anti-termite agent with respect to 100 parts by mass of vinyl chloride resin. At the same time, it contains a plasticizer containing an aliphatic dibasic acid ester. Therefore, in Example A-1 , Example A-2, Reference Example A-3, and Reference Example A-4 , both cold resistance and anti-termite effect can be achieved at the same time.
具体的には、実施例A-1、実施例A-2、参考例A-3、参考例A-4は、比較例X-1の場合よりも、優れた防蟻効果を備えている。そして、実施例A-1から実施例A-4では、-15℃以上の温度では破壊が発生しないので、比較例X-2の場合よりも優れた耐寒性を備えている。 Specifically, Example A-1 , Example A-2, Reference Example A-3, and Reference Example A-4 have an excellent anti-termite effect as compared with the case of Comparative Example X-1. Further, in Examples A-1 to A-4, fracture does not occur at a temperature of −15 ° C. or higher, so that the examples have better cold resistance than the case of Comparative Example X-2.
[3-2]参考例B-1、実施例B-2の試験結果について
参考例B-1と実施例B-2とのそれぞれの防蟻コンパウンドにおいては、アゼライン酸ジ(2-エチルヘキシル)(略号:DOZ)およびフタル酸ジイソノニル(略号:DINP)との添加割合が、実施例A-2の場合と異なっている。
[3-2] About the test results of Reference Example B-1 and Example B-2
In each of the anti-termite compounds of Reference Example B-1 and Example B-2, the addition ratio of di (2-ethylhexyl) azelaic acid (abbreviation: DOZ) and diisononyl phthalate (abbreviation: DINP) was carried out. This is different from the case of Example A-2.
参考例B-1では、アゼライン酸ジ(2-エチルヘキシル)(略号:DOZ)の含有割合は、2質量部であり、実施例A-2の場合よりも少ない。しかし、表1に示すように、参考例B-1では、参考例B-1においても、実施例A-2の場合と同様に、優れた防蟻効果が得られている。これと共に、参考例B-1では、-15℃以上の温度で破壊が発生しないので、優れた耐寒性を備えている。
In Reference Example B-1 , the content ratio of di (2-ethylhexyl) azelaic acid (abbreviation: DOZ) is 2 parts by mass, which is smaller than that in Example A-2. However, as shown in Table 1, in Reference Example B-1 , even in Reference Example B-1, an excellent ant-proofing effect is obtained as in the case of Example A-2. At the same time, Reference Example B-1 has excellent cold resistance because no fracture occurs at a temperature of −15 ° C. or higher.
実施例B-2では、アゼライン酸ジ(2-エチルヘキシル)(略号:DOZ)の含有割合は、20質量部であり、実施例A-2の場合よりも多い。しかし、表1に示すように、実施例B-2では、実施例A-2の場合と同様に、優れた防蟻効果が得られている。これと共に、実施例B-2では、-15℃以上の温度で破壊が発生しないので、優れた耐寒性を備えている。 In Example B-2, the content ratio of di (2-ethylhexyl) azelaic acid (abbreviation: DOZ) is 20 parts by mass, which is higher than that in Example A-2. However, as shown in Table 1, in Example B-2, as in the case of Example A-2, an excellent ant-proofing effect is obtained. At the same time, Example B-2 has excellent cold resistance because no fracture occurs at a temperature of −15 ° C. or higher.
[3-3]実施例C-1から実施例C-4の試験結果について
実施例C-1から実施例C-4の防蟻コンパウンドのそれぞれにおいては、表2に示すように、アゼライン酸ジ(2-エチルヘキシル)(略号:DOZ)以外の脂肪族二塩基酸エステルを含む。実施例C-1から実施例C-4の結果から判るように、アゼライン酸ジ(2-エチルヘキシル)(略号:DOZ)以外の脂肪族二塩基酸エステルを用いた場合においても、実施例A-2の場合と同様に、耐寒性と防蟻効果とを両立可能である。
[3-3] About the test results of Examples C-1 to C-4 In each of the anti-termite compounds of Examples C-1 to C-4, as shown in Table 2, the azelaic acid didi. Contains aliphatic dibasic acid esters other than (2-ethylhexyl) (abbreviation: DOZ). As can be seen from the results of Examples C-1 to C-4, even when an aliphatic dibasic acid ester other than di (2-ethylhexyl) azelaic acid (abbreviation: DOZ) is used, Example A- As in the case of 2, both cold resistance and anti-termite effect can be achieved.
[3-4]参考例Dの試験結果について
参考例Dの防蟻コンパウンドにおいては、表2に示すように、アゼライン酸ジ(2-エチルヘキシル)(略号:DOZ)の含有割合が、1質量部であって、参考例A-4の場合よりも少ない。しかし、表2に示すように、参考例Dでは、参考例A-4の場合と同様に、優れた防蟻効果が得られている。参考例Dでは、耐寒性の試験において、参考例A-4の場合よりも高い温度で破壊が生ずるが、-5℃以上の温度では破壊が発生しないので、優れた耐寒性を備えている。
[3-4] Test Results of Reference Example D In the anti-termite compound of Reference Example D, as shown in Table 2, the content ratio of di (2-ethylhexyl) azelaic acid (abbreviation: DOZ) is 1 part by mass. However, it is less than the case of Reference Example A-4. However, as shown in Table 2, in Reference Example D, an excellent ant-proofing effect is obtained as in the case of Reference Example A-4. In Reference Example D, in the cold resistance test, fracture occurs at a higher temperature than in Reference Example A-4, but fracture does not occur at a temperature of −5 ° C. or higher, so that the reference example D has excellent cold resistance.
1…防蟻電線・ケーブル、10…ケーブルコア、11…絶縁線心、12…介在、20…シース、30…防蟻シース、111…導体、112…絶縁層 1 ... Anti-termite wire / cable, 10 ... Cable core, 11 ... Insulated wire core, 12 ... Interposition, 20 ... Sheath, 30 ... Anti-termite sheath, 111 ... Conductor, 112 ... Insulation layer
Claims (2)
0.01質量部以上0.17質量部以下のクロチアニジンと、
20質量部以上40質量部以下の可塑剤と、
を含有する防蟻コンパウンドを用いて形成され、
前記可塑剤は、少なくとも10質量部以上の脂肪族二塩基酸エステルを含み、
前記脂肪族二塩基酸エステルは、アジピン酸エステルとアゼライン酸エステルとセバシン酸エステルの少なくとも1つが用いられる、
防蟻電線・ケーブル。 For 100 parts by mass of vinyl chloride resin
With clothianidin of 0.01 parts by mass or more and 0.17 parts by mass or less,
With a plasticizer of 20 parts by mass or more and 40 parts by mass or less,
Formed using an ant-proof compound containing
The plasticizer contains at least 10 parts by mass or more of an aliphatic dibasic acid ester.
As the aliphatic dibasic acid ester, at least one of adipate ester, azelaic acid ester and sebacic acid ester is used.
Anti-termite electric wire / cable.
請求項1記載の防蟻電線・ケーブル。 The plasticizer comprises the aliphatic dibasic acid ester and a plasticizer other than the aliphatic dibasic acid ester.
The anti-termite electric wire / cable according to claim 1.