JP7000312B2 - Adhesive sheet for non-slip construction - Google Patents
Adhesive sheet for non-slip construction Download PDFInfo
- Publication number
- JP7000312B2 JP7000312B2 JP2018510612A JP2018510612A JP7000312B2 JP 7000312 B2 JP7000312 B2 JP 7000312B2 JP 2018510612 A JP2018510612 A JP 2018510612A JP 2018510612 A JP2018510612 A JP 2018510612A JP 7000312 B2 JP7000312 B2 JP 7000312B2
- Authority
- JP
- Japan
- Prior art keywords
- slip
- adhesive sheet
- layer
- adhesive
- construction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、滑り止め施工用粘着シートに関する。 The present invention relates to an adhesive sheet for non-slip construction.
従来、建物の床材には、大理石等の天然石や各種樹脂から構成されるタイル材などが用いられている。しかし、このような床材は、強度や耐候性に優れているが、表面に水分を纏うと滑りやすくなるという欠点を有している。このため、床材の表面に防滑性を付与する試みがなされている。床材の表面に防滑性を付与する方法としては、床材の表面に粒子等を配合した塗料樹脂を塗布し、滑り止め層を形成する方法や、床面の表面に凹凸形状を形成する方法等が知られている。 Conventionally, natural stones such as marble and tile materials made of various resins have been used as flooring materials for buildings. However, although such a flooring material is excellent in strength and weather resistance, it has a drawback that it becomes slippery when the surface is covered with water. For this reason, attempts have been made to impart anti-slip properties to the surface of the flooring material. As a method of imparting anti-slip property to the surface of the floor material, a method of applying a paint resin containing particles or the like to the surface of the floor material to form a non-slip layer, or a method of forming an uneven shape on the surface of the floor material. Etc. are known.
例えば、特許文献１には、滑り止め要素として粒子を含む床カバーが開示されている。ここでは、滑り止め要素の粒子が表面に突出することで、滑り止め機能を発揮している。また、特許文献２には、フィルム上に部分的に接着剤を付与し、その上に所定粒径の粒子を接着させて圧着することで形成されるノンスリップ床材が開示されている。さらに特許文献３の従来技術には、床材の表面に部分的な滑り止め加工を施す方法が開示されている。特許文献３の図３では、床材の表面にマスキングシートを載置し、マスキングシートの開口部に樹脂材料等を塗布して防滑層を形成する方法が開示されている。ここでは、マスキングシートは１層構成の樹脂シートが用いられている。
For example,
特許文献１及び２のような床全面を覆う床カバーを用いた場合、床材が本来有する風合いや模様等の意匠性が損なわれるという問題があった。また、このような床カバーを用いた場合、歩行性や台車の通行性が悪化する場合があり問題となっていた。
When a floor cover that covers the entire floor as in
一方で、床材の表面に部分的に防滑層を形成する方法を採用した場合、床材の意匠性が損なわれることは少ないが、その施工に技術を要する場合が多く、このような施工方法の採用が進んでいないのが現状であった。また、従来のマスキングシートを用いて防滑層を形成した場合は、防滑層の形状等が安定せず、十分な防滑性能を発揮できないという問題もあった。 On the other hand, when a method of partially forming an anti-slip layer on the surface of the floor material is adopted, the design of the floor material is not impaired, but the construction often requires technology, and such a construction method. The current situation is that the adoption of is not progressing. Further, when the anti-slip layer is formed by using the conventional masking sheet, there is a problem that the shape of the anti-slip layer is not stable and sufficient anti-slip performance cannot be exhibited.
そこで本発明者らは、このような従来技術の課題を解決するために、床材の意匠性を損なわずに優れた防滑性を付与し得る防滑層を形成するための粘着シートを提供することを目的として検討を進めた。 Therefore, in order to solve the problems of the prior art, the present inventors provide an adhesive sheet for forming an anti-slip layer capable of imparting excellent anti-slip properties without impairing the design of the floor material. We proceeded with the study for the purpose.
上記の課題を解決するために鋭意検討を行った結果、本発明者らは、滑り止め施工用粘着シートを所定の層構成で形成し、かつ滑り止め施工用粘着シートに複数の貫通孔を形成することで優れた防滑性を発揮する防滑層を形成し得ることを見出した。
具体的に、本発明は、以下の構成を有する。As a result of diligent studies to solve the above problems, the present inventors have formed an adhesive sheet for non-slip construction with a predetermined layer structure, and formed a plurality of through holes in the adhesive sheet for non-slip construction. It has been found that the anti-slip layer can be formed to exhibit excellent anti-slip properties.
Specifically, the present invention has the following configurations.
［１］ 表面層と、粘着剤層とを有し、表面層及び粘着剤層を貫通する複数の貫通孔を有することを特徴とする滑り止め施工用粘着シート。
［２］ 貫通孔の数は、滑り止め施工用粘着シート１００ｃｍ2あたり３～１０００個である［１］に記載の滑り止め施工用粘着シート。
［３］ 貫通孔１つあたりの面積は０．０１～２０．０ｃｍ2である［１］又は［２］に記載の滑り止め施工用粘着シート。
［４］ 貫通孔の総面積が、滑り止め施工用粘着シートの全面積の２～６０％である［１］～［３］のいずれかに記載の滑り止め施工用粘着シート。
［５］ 厚みが０．０５～１ｍｍである［１］～［４］のいずれかに記載の滑り止め施工用粘着シート。
［６］ 表面層の厚みが１００～５００μｍである［１］～［５］のいずれかに記載の滑り止め施工用粘着シート。
［７］ 粘着剤層は再剥離性を有する［１］～［６］のいずれかに記載の滑り止め施工用粘着シート。
［８］ 粘着剤層の粘着力が０．５～１０．０Ｎ／５０ｍｍである［１］～［７］のいずれかに記載の滑り止め施工用粘着シート。
［９］ 表面層がプラスチックフィルムである［１］～［８］のいずれかに記載の滑り止め施工用粘着シート。
［１０］ 表面層の少なくとも表面露出面にはエンボス加工が施されている［１］～［９］のいずれかに記載の滑り止め施工用粘着シート。
［１１］ ［１］～［１０］のいずれかに記載の滑り止め施工用粘着シートの粘着剤層の一方の面側であって、表面層が積層された面とは反対の面側にさらに剥離剤層を有する剥離剤層付き滑り止め施工用粘着シート。
［１２］ 表面層と、粘着剤層を有する貫通孔形成用粘着シート。
［１３］ 粘着剤層の粘着力が０.３～８.０Ｎ／２５ｍｍである［１２］に記載の貫通孔形成用粘着シート。[1] A non-slip adhesive sheet having a surface layer and an adhesive layer, and having a plurality of through holes penetrating the surface layer and the adhesive layer.
[2] The non-slip adhesive sheet according to [1], wherein the number of through holes is 3 to 1000 per 100 cm 2 of the non-slip adhesive sheet.
[3] The non-slip adhesive sheet according to [1] or [2], wherein the area per through hole is 0.01 to 20.0 cm 2 .
[4] The non-slip adhesive sheet according to any one of [1] to [3], wherein the total area of the through holes is 2 to 60% of the total area of the non-slip adhesive sheet.
[5] The non-slip adhesive sheet according to any one of [1] to [4], which has a thickness of 0.05 to 1 mm.
[6] The non-slip adhesive sheet according to any one of [1] to [5], wherein the surface layer has a thickness of 100 to 500 μm.
[7] The non-slip adhesive sheet according to any one of [1] to [6], wherein the adhesive layer has removability.
[8] The non-slip adhesive sheet according to any one of [1] to [7], wherein the adhesive strength of the adhesive layer is 0.5 to 10.0 N / 50 mm.
[9] The non-slip adhesive sheet according to any one of [1] to [8], wherein the surface layer is a plastic film.
[10] The non-slip adhesive sheet according to any one of [1] to [9], wherein at least the exposed surface of the surface layer is embossed.
[11] Further on one surface side of the pressure-sensitive adhesive layer of the non-slip construction adhesive sheet according to any one of [1] to [10], and on the surface side opposite to the surface on which the surface layers are laminated. Adhesive sheet for non-slip construction with a release agent layer having a release agent layer.
[12] A pressure-sensitive adhesive sheet for forming through holes having a surface layer and a pressure-sensitive adhesive layer.
[13] The pressure-sensitive adhesive sheet for forming a through hole according to [12], wherein the pressure-sensitive adhesive force of the pressure-sensitive adhesive layer is 0.3 to 8.0 N / 25 mm.
本発明によれば、所定の層構成及び構造を有する滑り止め施工用粘着シートを用いて滑り止め施工を行うことにより、簡便な方法で防滑層を形成することができる。
また、本発明の滑り止め施工用粘着シートを用いれば、所望の形状の防滑層を形成することができるため、床材等の被着物に優れた防滑性を付与することができる。According to the present invention, the anti-slip layer can be formed by a simple method by performing the non-slip construction using the non-slip construction adhesive sheet having a predetermined layer structure and structure.
Further, by using the non-slip adhesive sheet of the present invention, it is possible to form an anti-slip layer having a desired shape, so that it is possible to impart excellent anti-slip properties to an adherend such as a flooring material.
以下において、本発明について詳細に説明する。以下に記載する構成要件の説明は、代表的な実施形態や具体例に基づいてなされることがあるが、本発明はそのような実施形態に限定されるものではない。なお、本明細書において「～」を用いて表される数値範囲は「～」前後に記載される数値を下限値および上限値として含む範囲を意味する。 Hereinafter, the present invention will be described in detail. The description of the constituent elements described below may be based on typical embodiments and specific examples, but the present invention is not limited to such embodiments. In addition, the numerical range represented by using "-" in this specification means the range including the numerical values before and after "-" as the lower limit value and the upper limit value.
（滑り止め施工用粘着シート）
本発明は、表面層と、粘着剤層とを有する滑り止め施工用粘着シートに関する。本発明の滑り止め施工用粘着シートは、表面層及び粘着剤層を貫通する複数の貫通孔を有する。ここで、本発明の滑り止め施工用粘着シートにおける粘着剤層は感圧粘着剤層である。
本発明の滑り止め施工用粘着シートは、上記構成を有するため、所望の形状の防滑層を容易に形成することができ、床材等の被着物に優れた防滑性を付与することができる。(Adhesive sheet for non-slip construction)
The present invention relates to a non-slip adhesive sheet having a surface layer and an adhesive layer. The non-slip adhesive sheet of the present invention has a plurality of through holes penetrating the surface layer and the adhesive layer. Here, the pressure-sensitive adhesive layer in the non-slip construction pressure-sensitive adhesive sheet of the present invention is a pressure-sensitive pressure-sensitive adhesive layer.
Since the non-slip adhesive sheet of the present invention has the above-mentioned structure, it is possible to easily form an anti-slip layer having a desired shape, and it is possible to impart excellent anti-slip properties to an adherend such as a flooring material.
さらに、本発明の滑り止め施工用粘着シートを用いた場合、滑り止め施工時のハンドリング性が良化する。なお、本明細書において、滑り止め施工時のハンドリング性が良好であることは、（１）滑り止め施工用粘着シートを対象物表面に貼り付け易く、（２）充填剤を硬化させた後の滑り止め施工用粘着シートを対象物から剥離し易く、（３）滑り止め施工用粘着シートを対象物から剥離する際には、糊残りなく剥離可能であり、（４）充填剤を貫通孔に確実に充填し易いことをいう。 Further, when the adhesive sheet for non-slip construction of the present invention is used, the handling property at the time of non-slip construction is improved. In the present specification, the good handling property at the time of non-slip construction is that (1) the adhesive sheet for non-slip construction can be easily attached to the surface of the object, and (2) after the filler is cured. The non-slip adhesive sheet for non-slip construction can be easily peeled off from the object, (3) when the non-slip adhesive sheet for non-slip construction is peeled off from the object, it can be peeled off without adhesive residue, and (4) the filler is placed in the through hole. It means that it is easy to fill reliably.
図１は、本発明の滑り止め施工用粘着シートの構成を説明する図である。図１（ａ）は、本発明の滑り止め施工用粘着シート１００の平面図であり、滑り止め施工用粘着シート１００には複数の貫通孔３０が設けられている。なお、図１（ａ）の平面図は、表面層側から見た平面図であるが、粘着剤層側から見た平面図であっても同様の構成となる。図１（ｂ）は、本発明の滑り止め施工用粘着シート１００の断面図である。図１（ｂ）の断面図は、図１（ａ）において、滑り止め施工用粘着シート１００をＡ－Ａ'線で切断した際の断面図である。滑り止め施工用粘着シート１００は、表面層１０と粘着剤層２０を有し、貫通孔３０は表面層と粘着剤層を貫通している。
FIG. 1 is a diagram illustrating a configuration of an adhesive sheet for non-slip construction of the present invention. FIG. 1A is a plan view of the non-slip construction
滑り止め施工をする際には、まず、本発明の滑り止め施工用粘着シートが床材等の被着物に貼着される。その後、滑り止め施工用粘着シートの貫通孔内に、防滑層を形成する充填剤を充填する。そして、充填剤を硬化させた後に、本発明の滑り止め施工用粘着シートを被着物から剥離することで、部分的に防滑層が形成されることとなる。 When performing anti-slip construction, first, the adhesive sheet for non-slip construction of the present invention is attached to an adherend such as a flooring material. After that, the through hole of the non-slip adhesive sheet is filled with a filler that forms an anti-slip layer. Then, after the filler is cured, the anti-slip adhesive sheet of the present invention is peeled off from the adherend to partially form an anti-slip layer.
充填剤を硬化させた後に、本発明の滑り止め施工用粘着シートを被着物から剥離する様子は、図２に示されている。図２では、施工方法をわかりやすく説明するために、貫通孔を大きく、かつ可視化して示している。また、図２では、滑り止め施工を施す対象を床面Ｐとしているが、滑り止め施工は床面以外にも施すことができる。また、本明細書においては、防滑層とは、図２に示されているような防滑突起部（防滑層５０）または、防滑突起部の集合体をいう。 FIG. 2 shows how the non-slip adhesive sheet of the present invention is peeled off from the adherend after the filler is cured. In FIG. 2, in order to explain the construction method in an easy-to-understand manner, the through holes are shown in a large size and visualized. Further, in FIG. 2, the target to which the anti-slip construction is applied is the floor surface P, but the anti-slip construction can be applied to other than the floor surface. Further, in the present specification, the anti-slip layer means an anti-slip protrusion (anti-slip layer 50) as shown in FIG. 2 or an aggregate of anti-slip protrusions.
本発明の滑り止め施工用粘着シートの厚みは、０．０５～１ｍｍであることが好ましく、０．１～０．８ｍｍであることがより好ましく、０．１５～０．６ｍｍであることがさらに好ましく、０．２～０．５ｍｍであることが特に好ましい。滑り止め施工用粘着シートの厚みを上記範囲内とすることにより、形成される防滑層の厚み（高さ）を好ましい範囲とすることができる。これにより、防滑層は水はけを促すことができ、優れた防滑性を発揮することができる。また、滑り止め施工用粘着シートの厚みを上記範囲内とすることにより、歩行時の躓き等を抑制でき、防滑層に起因した歩行性の悪化を抑制することができる。さらに、滑り止め施工用粘着シートの厚みを上記範囲内とすることにより、歩行時に加わる衝撃等により防滑層が被着物から離脱することも抑制することができる。 The thickness of the non-slip adhesive sheet of the present invention is preferably 0.05 to 1 mm, more preferably 0.1 to 0.8 mm, and further preferably 0.15 to 0.6 mm. It is preferably 0.2 to 0.5 mm, and particularly preferably 0.2 to 0.5 mm. By setting the thickness of the non-slip adhesive sheet within the above range, the thickness (height) of the anti-slip layer to be formed can be set within a preferable range. As a result, the anti-slip layer can promote drainage and can exhibit excellent anti-slip properties. Further, by setting the thickness of the non-slip adhesive sheet within the above range, it is possible to suppress stumbling during walking and to suppress deterioration of walking performance due to the anti-slip layer. Further, by setting the thickness of the non-slip adhesive sheet within the above range, it is possible to prevent the anti-slip layer from coming off from the adherend due to an impact applied during walking or the like.
本発明の滑り止め施工用粘着シートは、後述するように床材以外にも適用可能であるが、床材（床面）に滑り止め施工を施すために用いられることが好ましい。このため、本発明の滑り止め施工用粘着シートは、床用滑り止め施工用粘着シートであることが好ましい。 The adhesive sheet for non-slip construction of the present invention can be applied to other than the floor material as described later, but it is preferably used for applying the non-slip construction to the floor material (floor surface). Therefore, the non-slip construction adhesive sheet of the present invention is preferably a floor non-slip construction adhesive sheet.
（貫通孔）
本発明の滑り止め施工用粘着シートは複数の貫通孔を有する。滑り止め施工用粘着シート１００ｃｍ2あたりに設けられる貫通孔の数は、３～１０００個であることが好ましく、１０～８００個であることがより好ましく、３０～５００個であることがさらに好ましい。
また、貫通孔１つあたりの面積は０．０１～２０．０ｃｍ2であることが好ましく、０．０２～１０．０ｃｍ2であることがより好ましく、０．０３～８．０ｃｍ2であることがさらに好ましい。貫通孔１つあたりの面積を上記下限値以上とすることにより、防滑性能に優れた防滑層を施工することができる。加えて、滑り止め施工用粘着シート上に充填剤を充填する際に、貫通孔に充填剤が充填されたことを容易に視認することができ、効率よく施工できるとともに、充填不良による施工ミスを防ぐことができる。(Through hole)
The non-slip adhesive sheet of the present invention has a plurality of through holes. The number of through holes provided per 100 cm 2 of the non-slip adhesive sheet is preferably 3 to 1000, more preferably 10 to 800, and even more preferably 30 to 500.
The area per through hole is preferably 0.01 to 20.0 cm 2 , more preferably 0.02 to 10.0 cm 2 , and 0.03 to 8.0 cm 2 . Is even more preferable. By setting the area per through hole to the above lower limit value or more, an anti-slip layer having excellent anti-slip performance can be constructed. In addition, when filling the adhesive sheet for non-slip construction with the filler, it is possible to easily visually recognize that the filler has been filled in the through holes, and the construction can be performed efficiently, and construction mistakes due to poor filling can be detected. Can be prevented.
貫通孔の総面積は、滑り止め施工用粘着シートの全面積の２～６０％であることが好ましく、３～６０％であることがより好ましく、５～５０％であることがさらに好ましい。上記の条件となるように貫通孔を形成することにより、所望の大きさ及び形状を有する防滑層を形成することができる。また、滑り止め施工用粘着シートの柔軟性や強度も適切な範囲とすることができ、滑り止め施工時のハンドリング性を良好なものとすることができる。 The total area of the through holes is preferably 2 to 60%, more preferably 3 to 60%, and even more preferably 5 to 50% of the total area of the non-slip adhesive sheet. By forming the through holes so as to meet the above conditions, it is possible to form an anti-slip layer having a desired size and shape. Further, the flexibility and strength of the non-slip adhesive sheet can be set in an appropriate range, and the handleability at the time of non-slip construction can be improved.
貫通孔１つあたりの面積は上記範囲内であることが好ましく、このような面積を有する貫通孔であれば貫通孔の形状は特に制限されない。貫通孔の形状としては、例えば、円形、楕円形、四角形、三角形、星形、ハート型、動植物型等とすることができる。貫通孔の形状が四角形である場合、一定間隔の長方形として、ストライプ状に貫通孔を形成してもよい。中でも貫通孔の形状は円形であることが好ましく、円形の貫通孔を均一パターン（ドット状）となるように形成することで、水はけ性に優れた防滑層を容易に形成することができる。 The area per through hole is preferably within the above range, and the shape of the through hole is not particularly limited as long as the through hole has such an area. The shape of the through hole may be, for example, a circle, an ellipse, a quadrangle, a triangle, a star, a heart, an animal or plant type, or the like. When the shape of the through hole is a quadrangle, the through hole may be formed in a striped shape as a rectangle at regular intervals. Above all, the shape of the through hole is preferably circular, and by forming the circular through hole so as to have a uniform pattern (dot shape), an anti-slip layer having excellent drainage property can be easily formed.
なお、貫通孔の形状は全て同一でなくてもよく、貫通孔は均一パターンとなるように形成されなくてもよい。例えば、貫通孔の形状を文字形状として、各種文字を並べることで、会社名を表記したり、広告として表示させることもできる。このような貫通孔に充填剤を充填して防滑層を形成することで、床材等の被着物に会社名や広告のロゴを防滑層を用いて表示することができる。この場合、充填剤には色素等を含有させて、着色した防滑層を形成することもできる。このように、貫通孔は様々な形状や性状とすることができ、防滑層は防滑性を発揮するのみならず、広告表示機能や意匠性を発揮することもできる。 The shapes of the through holes do not have to be the same, and the through holes do not have to be formed so as to have a uniform pattern. For example, by using the shape of the through hole as a character shape and arranging various characters, the company name can be displayed or displayed as an advertisement. By filling such through holes with a filler to form an anti-slip layer, a company name or an advertisement logo can be displayed on an adherend such as a flooring material by using the anti-slip layer. In this case, the filler may contain a dye or the like to form a colored anti-slip layer. As described above, the through hole can have various shapes and properties, and the anti-slip layer can not only exhibit anti-slip properties but also exhibit an advertisement display function and design.
貫通孔は、表面層と粘着剤層を有する貫通孔形成用粘着シートにパンチング加工やレーザー加工等を施すことで形成されることが好ましい。加工法は、貫通孔の形状等に併せて適宜選択することができる。 The through hole is preferably formed by subjecting a through hole forming pressure-sensitive adhesive sheet having a surface layer and an adhesive layer to a punching process, a laser process, or the like. The processing method can be appropriately selected according to the shape of the through hole and the like.
（表面層）
本発明の滑り止め施工用粘着シートは、表面層を有する。表面層の材質は特に制限されない。例えば、表面層には、プラスチックフィルムや、合成紙等に代表される紙基材等を用いることができる。プラスチックフィルム（樹脂基材）としては、ＰＶＣ（ポリ塩化ビニル）フィルム、ＰＥＴ（ポリエチレン・テレフタラート）フィルム、ＰＥ（ポリエチレン）フィルム、ＰＰ（ポリプロピレン）フィルム、ＰＯ（ポリオレフィン）フィルム、ＰＳ（ポリスチレン）フィルム、ＥＶＡ（エチレン・酢酸ビニル共重合）フィルム、シリコーンフィルム等を挙げることができる。また、合成紙としては、例えば、ユポ・コーポレーション社製のユポコート（登録商標）を挙げることができる。表面層は、単層構造であってもよく、上述した基材を２種以上積層した構成であってもよい。(Surface layer)
The non-slip adhesive sheet of the present invention has a surface layer. The material of the surface layer is not particularly limited. For example, a plastic film, a paper base material typified by synthetic paper, or the like can be used for the surface layer. Examples of the plastic film (resin base material) include PVC (polyvinyl chloride) film, PET (polyethylene / terephthalate) film, PE (polyethylene) film, PP (polypropylene) film, PO (polyethylene) film, PS (polystyrene) film, and the like. EVA (polyethylene / vinyl acetate copolymer) film, silicone film and the like can be mentioned. Further, as the synthetic paper, for example, Yupo Coat (registered trademark) manufactured by Yupo Corporation can be mentioned. The surface layer may have a single-layer structure, or may have a structure in which two or more of the above-mentioned base materials are laminated.
中でも、表面層は透明基材であることが好ましく、透明樹脂基材を用いることがより好ましい。透明樹脂基材としては、ＰＶＣ（ポリ塩化ビニル）フィルム、ＰＥＴ（ポリエチレン・テレフタラート）フィルム、ＰＥ（ポリエチレン）フィルム又はＰＯ（ポリオレフィン）フィルムを用いることがより好ましく、ポリ塩化ビニルフィルム、ポリオレフィンフィルム又はポリエチレンフィルムを用いることがより好ましく、ポリ塩化ビニルフィルム又はポリオレフィンフィルムを用いることがさらに好ましい。ポリ塩化ビニルフィルムや、ポリオレフィンフィルム、ポリエチレンフィルムは基材としての柔軟性に優れており、これらのフィルムを表面層に用いた場合、金属ヘラで充填剤を均した際のヘラの滑り性が良好であるため、好ましく用いられる。 Above all, the surface layer is preferably a transparent base material, and it is more preferable to use a transparent resin base material. As the transparent resin base material, it is more preferable to use a PVC (polyvinyl chloride) film, PET (polyethylene / terephthalate) film, PE (polyethylene) film or PO (polyethylene) film, and a polyvinyl chloride film, a polyolefin film or polyethylene. It is more preferable to use a film, and it is further preferable to use a polyvinyl chloride film or a polyolefin film. Polyvinyl chloride film, polyolefin film, and polyethylene film have excellent flexibility as a base material, and when these films are used for the surface layer, the slipperiness of the spatula when the filler is leveled with a metal spatula is good. Therefore, it is preferably used.
表面層としてポリ塩化ビニルフィルムを用いる場合、フィルムには可塑剤が含まれることが好ましい。このような可塑剤としては、モノメリック系可塑剤やポリメリック系可塑剤が挙げられるが、本発明では、表面層にはポリメリック系可塑剤が含まれることが好ましい。ポリメリック系可塑剤を用いることにより、表面層に積層される粘着剤層へのブリードアウトを抑制することができ、粘着剤層の粘着力の低下を抑制することができ、経時後であっても粘着剤層の粘着力を所望の範囲内にすることができる。 When a polyvinyl chloride film is used as the surface layer, it is preferable that the film contains a plasticizer. Examples of such a plasticizer include a monomeric plasticizer and a polypeptide-based plasticizer, but in the present invention, it is preferable that the surface layer contains the polypeptide-based plasticizer. By using a polypeptide-based plasticizer, it is possible to suppress bleeding out to the pressure-sensitive adhesive layer laminated on the surface layer, and it is possible to suppress a decrease in the adhesive strength of the pressure-sensitive adhesive layer, even after a lapse of time. The adhesive strength of the pressure-sensitive adhesive layer can be within a desired range.
ポリメリック系可塑剤は、モノメリック系に比べ、柔軟性、耐候性および安定性に長けた複雑な構造を有するため好ましく用いられる。ポリメリック系可塑剤は、分子鎖が長く複雑であるため、分子同士が絡み合い、安定性が高い。このため、フィルム表面へのブリードアウトが起き難く、耐候年数が長い等の特徴を有する。 Polymeric plasticizers are preferably used because they have a complex structure that is superior in flexibility, weather resistance and stability to monomeric plasticizers. Polymeric plasticizers have long molecular chains and are complicated, so that the molecules are entangled with each other and have high stability. Therefore, bleed-out to the film surface is unlikely to occur, and the weather resistance is long.
なお、一般的な可塑剤としては、例えば、フタル酸エステル系（ＤＥＨＰ、ＤＢＰ、ＢＢＰ、ＤＩＮＰ、ＤＩＤＰ、ＤＮＯＰ、ＤＯＴＰ）、アジピン酸エステル系、リン酸エステル系、トリメリット酸、クエン酸エステル系、エポキシ系、ポリエステル系などの可塑剤を挙げることができる。 As general plasticizers, for example, phthalate ester type (DEHP, DBP, BBP, DINP, DIDP, DNOP, DOTP), adipate type, phosphoric acid ester type, trimellitic acid, citric acid ester type. , Ester-based, polyester-based and other plasticizers can be mentioned.
表面層の少なくとも一方の表面にはエンボス加工を施すことが好ましい。特に表面層の表面露出面（粘着剤層が積層されている面とは反対側の面）に、エンボス加工を施すことが好ましい。このようなエンボス加工を施すことにより、表面層には微細な凹凸形状が形成され、表面層は半透明状態になる。表面層は透明基材であることが好ましいが、このようなエンボス加工を施した半透明基材も好ましく用いられる。 It is preferable to emboss at least one surface of the surface layer. In particular, it is preferable to emboss the exposed surface of the surface layer (the surface opposite to the surface on which the adhesive layer is laminated). By performing such embossing, a fine uneven shape is formed on the surface layer, and the surface layer becomes translucent. The surface layer is preferably a transparent base material, but such an embossed translucent base material is also preferably used.
表面層にエンボス加工が施される場合は、エンボス加工が施された表面の表面粗さ（算術平均粗さ（Ｒａ））は１～１０であることが好ましく、２～７であることがより好ましく、２～５であることがさらに好ましい。なお、算術平均粗さ（Ｒａ）は、粗さ曲線からその平均線の方向に基準長さだけを抜き取り、この抜取り部分の平均線の方向にＸ軸を、縦倍率の方向にＹ軸を取り、粗さ曲線を ｙ＝ｆ（ｘ）で表したときに、次の式によって求められる値をマイクロメートル（μｍ）で表したものをいう。なお、下記式においてｌは基準長さを表す。
表面層が半透明基材である場合、充填剤には透明なものを用いることが好ましい。透明な充填剤としては、例えば、シリコーン樹脂、アクリル系樹脂、ウレタン系樹脂、エポキシ系樹脂等が挙げられる。表面層が半透明である場合、透明な充填剤との色度や透明度が異なるため、充填剤と表面層の見分けがつきやすい。このため、滑り止め施工用粘着シートの貫通孔に充填剤の充填がなされたことを確認しやすくなり、充填剤の充填漏れ（充填抜け）を防止することができる。このように、表面層の色度や透明度は、充填剤の色度や透明度と異なるものであることが好ましい。
なお、表面層と充填剤の色度を異なるものとするために、表面層に色素を含有させてもよい。表面層を着色することで、充填剤の充填を確認しやすくすることも可能である。When the surface layer is a translucent base material, it is preferable to use a transparent filler. Examples of the transparent filler include silicone resin, acrylic resin, urethane resin, epoxy resin and the like. When the surface layer is translucent, the chromaticity and transparency are different from those of the transparent filler, so that it is easy to distinguish between the filler and the surface layer. Therefore, it becomes easy to confirm that the through hole of the non-slip adhesive sheet is filled with the filler, and it is possible to prevent the filler from leaking (filling omission). As described above, the chromaticity and transparency of the surface layer are preferably different from the chromaticity and transparency of the filler.
In addition, in order to make the chromaticity of the surface layer different from that of the filler, the surface layer may contain a dye. By coloring the surface layer, it is possible to make it easier to confirm the filling of the filler.
表面層の少なくとも一方の表面にはエンボス加工が施されていることが好ましい。この場合、表面層の全光線透過率は７０～９８％であることが好ましく、７５～９５％であることがさらに好ましい。また、表面層のヘーズは、１０～９８％であることが好ましく、１５～９５％であることが好ましい。なお、本願明細書においては、全光線透過率及びヘーズは、ＪＩＳ Ｋ ７１３６に準拠した方法で測定される値のことをいう。 It is preferable that at least one surface of the surface layer is embossed. In this case, the total light transmittance of the surface layer is preferably 70 to 98%, more preferably 75 to 95%. The haze of the surface layer is preferably 10 to 98%, preferably 15 to 95%. In the specification of the present application, the total light transmittance and the haze are values measured by a method based on JIS K 7136.
また、上述したようなエンボス加工を施すことで、滑り止め施工時に充填剤を充填する際のヘラの滑り性を高めることもできる。これは表面層の表面露出面に形成されたエンボスにより、ヘラを動かす際の摩擦抵抗が低減されることによるものであると考えられる。このようにエンボス加工を施すことにより、滑り止め施工時の作業性をより高めることができる。 Further, by embossing as described above, it is possible to improve the slipperiness of the spatula when filling the filler at the time of anti-slip construction. It is considered that this is because the frictional resistance when moving the spatula is reduced by the embossing formed on the surface exposed surface of the surface layer. By embossing in this way, workability during non-slip construction can be further improved.
表面層の厚みは３０～９００μｍであることが好ましく、５０μｍより大きく９００μｍ以下であることがより好ましく、１００～５００μｍであることがさらに好ましく、１５０～４００μｍであることが一層好ましい。表面層の厚みを上記範囲内とすることにより、形成される防滑層の厚み（高さ）を好ましい範囲とすることができる。これにより、防滑層は優れた防滑性を発揮できることに加え、防滑層に起因した歩行性の悪化を抑制することができる。また、表面層の厚みを上記範囲内とすることにより、歩行時に加わる衝撃等により防滑層が被着物から離脱することも抑制することができる。さらに表面層の厚みを上記範囲内とすることにより、滑り止め施工用粘着シートの柔軟性を維持することができ、施工時に滑り止め施工用粘着シートを被着物に貼り合わせる際のハンドリング性を高めることができる。 The thickness of the surface layer is preferably 30 to 900 μm, more preferably larger than 50 μm and 900 μm or less, further preferably 100 to 500 μm, and even more preferably 150 to 400 μm. By setting the thickness of the surface layer within the above range, the thickness (height) of the anti-slip layer to be formed can be set within a preferable range. As a result, the anti-slip layer can exhibit excellent anti-slip properties and can suppress deterioration of walking performance caused by the anti-slip layer. Further, by setting the thickness of the surface layer within the above range, it is possible to prevent the anti-slip layer from being separated from the adherend due to an impact applied during walking or the like. Furthermore, by setting the thickness of the surface layer within the above range, the flexibility of the non-slip construction adhesive sheet can be maintained, and the handleability when the non-slip construction adhesive sheet is attached to the adherend during construction is improved. be able to.
表面層の引張強度は、１０Ｎ／１０ｍｍ以上であることが好ましく、２０Ｎ／１０ｍｍ以上であることがより好ましい。また、表面層の引張強度の上限値は１５０Ｎ／１０ｍｍ以下であることが好ましい。なお、上記引張強度は表面層の長さ方向及び幅方向の引張強度の相乗平均値である。 The tensile strength of the surface layer is preferably 10 N / 10 mm or more, and more preferably 20 N / 10 mm or more. Further, the upper limit of the tensile strength of the surface layer is preferably 150 N / 10 mm or less. The tensile strength is a geometric mean value of the tensile strength in the length direction and the width direction of the surface layer.
（粘着剤層）
本発明の滑り止め施工用粘着シートは、粘着剤層を有する。本発明では、粘着剤層は再剥離性を有することが好ましい。ここで、再剥離性とは、粘着剤層を被着物から糊残りなく剥がせる性質のことをいう。また、再剥離性は、滑り止め施工用粘着シートの粘着力を所定の範囲内とすること等によって調整することができる。(Adhesive layer)
The non-slip adhesive sheet of the present invention has an adhesive layer. In the present invention, the pressure-sensitive adhesive layer preferably has removability. Here, the removability means a property that the adhesive layer can be peeled off from the adherend without adhesive residue. Further, the removability can be adjusted by setting the adhesive strength of the non-slip adhesive sheet within a predetermined range or the like.
粘着剤層を構成する粘着剤としては、溶剤型粘着剤、エマルション型粘着剤、ホットメルト型粘着剤が挙げられる。中でも、貫通孔の加工のしやすさ等の観点から、溶剤型粘着剤が好ましく用いられる。 Examples of the pressure-sensitive adhesive constituting the pressure-sensitive adhesive layer include a solvent-type pressure-sensitive adhesive, an emulsion-type pressure-sensitive adhesive, and a hot-melt type pressure-sensitive adhesive. Of these, a solvent-based pressure-sensitive adhesive is preferably used from the viewpoint of ease of processing through holes.
溶剤型粘着剤は、有機溶媒中に粘着剤（粘着成分）を含むものである。溶剤型粘着剤を構成する粘着剤としては、アクリル系粘着剤、ポリエステル系粘着剤、ウレタン系粘着剤、ポリエーテル系粘着剤、ゴム系粘着剤、シリコーン系粘着剤、ポリアミド系粘着剤、フッ素系粘着剤等の、公知の各種粘着剤を挙げることができる。中でも、本発明では、アクリル系粘着剤又はウレタン系粘着剤を用いることが好ましく、アクリル系粘着剤を用いることがより好ましい。 The solvent type pressure-sensitive adhesive contains a pressure-sensitive adhesive (adhesive component) in an organic solvent. The adhesives that make up the solvent-based adhesives include acrylic adhesives, polyester adhesives, urethane adhesives, polyether adhesives, rubber adhesives, silicone adhesives, polyamide adhesives, and fluorine adhesives. Various known pressure-sensitive adhesives such as pressure-sensitive adhesives can be mentioned. Above all, in the present invention, it is preferable to use an acrylic pressure-sensitive adhesive or a urethane-based pressure-sensitive adhesive, and it is more preferable to use an acrylic-based pressure-sensitive adhesive.
アクリル系粘着剤のベースポリマーであるアクリルポリマーは、（メタ）アクリルモノマーを重合してなるものである。アクリルポリマーとしては、公知のポリマーを使用することができる。例えば、（メタ）アクリル酸、イタコン酸、（無水）マレイン酸、（無水）フマル酸、クロトン酸等のカルボキシル基もしくはその無水物基を有する重合性モノマー、アルキル（メタ）アクリレート〔メチル（メタ）アクリレート、エチル（メタ）アクリレート、ブチル（メタ）アクリレート、２－エチルヘキシル（メタ）アクリレート、イソオクチル（メタ）アクリレート、ラウリル（メタ）アクリレート等〕、２－ヒドロキシエチル（メタ）アクリレート等のモノ（メタ）アクリレート、ジエチレングリコールジ（メタ）アクリレート、ヘキサンジオールジ（メタ）アクリレート等のジ（メタ）アクリレート、ペンタエリスリトールトリ（メタ）アクリレート等のトリ（メタ）アクリレート、（メタ）アクリルアミド、Ｎ，Ｎ－ジメチル（メタ）アクリルアミド等の（メタ）アクリルアミド等の（メタ）アクリル系モノマーから選択されたモノマーのホモポリマー、並びに上記の２種以上から選択されたモノマーのコポリマー、ターポリマー等の多元ポリマーが挙げられる。また、アクリルポリマーには、本発明の効果を顕著に損なわない範囲で、上記以外のモノマー（その他モノマー）が共重合されていてもよい。 The acrylic polymer, which is the base polymer of the acrylic pressure-sensitive adhesive, is obtained by polymerizing a (meth) acrylic monomer. As the acrylic polymer, a known polymer can be used. For example, a polymerizable monomer having a carboxyl group such as (meth) acrylic acid, itaconic acid, (anhydrous) maleic acid, (anhydrous) fumaric acid, and crotonic acid or an anhydride group thereof, an alkyl (meth) acrylate [methyl (meth)). Acrylate, ethyl (meth) acrylate, butyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, isooctyl (meth) acrylate, lauryl (meth) acrylate, etc.], 2-hydroxyethyl (meth) acrylate, etc. Di (meth) acrylates such as acrylates, diethylene glycol di (meth) acrylates and hexanediol di (meth) acrylates, tri (meth) acrylates such as pentaerythritol tri (meth) acrylates, (meth) acrylamides, N, N-dimethyl ( Examples thereof include a homopolymer of a monomer selected from a (meth) acrylic monomer such as (meth) acrylamide such as meta) acrylamide, a copolymer of a monomer selected from the above two or more kinds, and a polymorphic polymer such as a tarpolymer. Further, the acrylic polymer may be copolymerized with a monomer (other monomer) other than the above as long as the effect of the present invention is not significantly impaired.
中でも本発明では、アクリル系溶剤型粘着剤を用いることが好ましい。アクリル系溶剤型粘着剤は貫通孔を形成しやすく、加工適性に優れている。また、貫通孔を形成した後の安定性にも優れており、所望の形状を有する防滑層が形成されやすいという利点がある。 Above all, in the present invention, it is preferable to use an acrylic solvent type pressure-sensitive adhesive. Acrylic solvent-based adhesives easily form through holes and are excellent in processing suitability. In addition, it is also excellent in stability after forming a through hole, and has an advantage that an anti-slip layer having a desired shape is easily formed.
アクリル系溶剤型粘着剤のベースポリマーであるアクリルポリマーとしては、アルキル（メタ）アクリレート〔メチル（メタ）アクリレート、エチル（メタ）アクリレート、ブチル（メタ）アクリレート、２－エチルヘキシル（メタ）アクリレート、イソオクチル（メタ）アクリレート、ラウリル（メタ）アクリレート等〕、２－ヒドロキシエチル（メタ）アクリレート、４－ヒドロキシブチル（メタ）アクリレート、２－ヒドロキシプロピル（メタ）アクリレート、２－エチルヘキシル（メタ）アクリレート等のホモポリマーやコポリマーが挙げられる。 As the acrylic polymer which is the base polymer of the acrylic solvent type pressure-sensitive adhesive, alkyl (meth) acrylate [methyl (meth) acrylate, ethyl (meth) acrylate, butyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, isooctyl ( Meta) acrylate, lauryl (meth) acrylate, etc.], 2-hydroxyethyl (meth) acrylate, 4-hydroxybutyl (meth) acrylate, 2-hydroxypropyl (meth) acrylate, 2-ethylhexyl (meth) acrylate and other homopolymers. And polymers.
粘着剤層を形成する粘着剤には、粘着性を向上させる目的で、粘着付与剤が配合されてもよく、装置適合性を考慮して軟化剤が配合されてもよい。
粘着付与剤としては、例えば、ロジン、エステルガム、エステルガムＨ、ポリテルペン樹脂、Ｃ５系石油樹脂、Ｃ９系石油樹脂、ＤＣＰＤ系石油樹脂、スチレン系樹脂、アルキルフェノール樹脂、テルペンフェノール樹脂、およびこれらの水添物等が挙げられる。中でも、ポリテルペン樹脂、Ｃ５系石油樹脂の水添物およびＣ９系石油樹脂の水添物が好ましく用いられる。
軟化剤としては、例えば、各種可塑剤、ポリブテン、液状粘着付与剤樹脂、ポリイソブチレン低重合体、ポリビニルイソブチルエーテル低重合体、ラノリン、解重合ゴム、プロセスオイル、ナフテン系オイル、パラフィン系オイル、加硫オイル等が挙げられる。
その他、必要に応じて、増粘剤、ｐＨ調整剤、消泡剤、防腐防黴剤、顔料、無機充填剤、安定剤、濡れ剤、湿潤剤等を配合することができる。The pressure-sensitive adhesive forming the pressure-sensitive adhesive layer may be blended with a tackifier for the purpose of improving the tackiness, or may be blended with a softening agent in consideration of device compatibility.
Examples of the tackifier include rosin, ester gum, ester gum H, polyterpene resin, C5 petroleum resin, C9 petroleum resin, DCPD petroleum resin, styrene resin, alkylphenol resin, terpenephenol resin, and water thereof. Esters and the like can be mentioned. Of these, a polyterpene resin, a hydrogenated product of C5 petroleum resin, and a hydrogenated product of C9 petroleum resin are preferably used.
Examples of the softening agent include various plasticizers, polybutenes, liquid tackifier resins, polyisobutylene low polymers, polyvinylisobutyl ether low polymers, lanolin, depolymerized rubbers, process oils, naphthenic oils, paraffin oils, and additions. Examples include vulcanized oil.
In addition, if necessary, a thickener, a pH adjuster, an antifoaming agent, an antiseptic / antifungal agent, a pigment, an inorganic filler, a stabilizer, a wetting agent, a wetting agent and the like can be blended.
粘着剤層の２３℃環境下における粘着力は、０．５～１０．０Ｎ／５０ｍｍであることが好ましく、０．７～９．０Ｎ／５０ｍｍであることがより好ましく、０．９～８．０Ｎ／５０ｍｍであることがさらに好ましく、１．０～７．０Ｎ／５０ｍｍであることが特に好ましい。ここで、上記粘着力は、貫通孔を有する状態における粘着力であり、ＪＩＳ Ｚ ０２３７に準じて測定した値である。粘着剤層の粘着力を上記範囲内とすることにより、滑り止め施工用粘着シートと被着物の密着性を高めることができ、滑り止め施工時に充填剤が意図しない場所に染み出すことを抑制することができる。また、粘着剤層の粘着力を上記範囲内とすることにより、滑り止め施工後に粘着シートを被着物から剥離する際の再剥離性を高めることができ、被着物上から糊残りなく粘着シートを剥離することができる。 The adhesive strength of the pressure-sensitive adhesive layer in an environment of 23 ° C. is preferably 0.5 to 10.0 N / 50 mm, more preferably 0.7 to 9.0 N / 50 mm, and 0.9 to 8. It is more preferably 0N / 50mm, and particularly preferably 1.0 to 7.0N / 50mm. Here, the adhesive force is an adhesive force in a state of having a through hole, and is a value measured according to JIS Z 0237. By keeping the adhesive strength of the adhesive layer within the above range, the adhesion between the adhesive sheet for non-slip construction and the adherend can be improved, and the filler can be prevented from seeping out to an unintended place during non-slip construction. be able to. Further, by setting the adhesive strength of the adhesive layer within the above range, it is possible to improve the re-peelability when the adhesive sheet is peeled off from the adherend after the non-slip construction, and the adhesive sheet can be made without adhesive residue from the adherend. Can be peeled off.
粘着剤層を構成する粘着剤の温度０～６０℃の範囲、周波数１Ｈｚで測定される貯蔵弾性率は、５×１０3～５×１０6Ｐａであることが好ましく、１×１０4～５×１０5Ｐａであることがより好ましい。貯蔵弾性率は、周波数１Ｈｚ、０～６０℃の範囲内であれば、どの温度条件で測定した場合でも粘着剤の貯蔵弾性率が上記範囲内であることが好ましい。貯蔵弾性率が上記下限値以上であれば、被着物との密着性を高めつつ再剥離性も高めることができる。The storage elastic modulus of the pressure-sensitive adhesive constituting the pressure-sensitive adhesive layer in the range of 0 to 60 ° C. and a frequency of 1 Hz is preferably 5 × 10 3 to 5 × 10 6 Pa, and is preferably 1 × 10 4 to 5. It is more preferably × 10 5 Pa. The storage elastic modulus is preferably within the above range as long as the frequency is within the range of 1 Hz and 0 to 60 ° C., regardless of the temperature conditions. When the storage elastic modulus is at least the above lower limit value, the removability can be improved while improving the adhesion to the adherend.
粘着剤層の厚みは、５～１００μｍであることが好ましく、８～８０μｍであることがより好ましく、１０～５０μｍであることがさらに好ましい。粘着剤層の厚みを上記範囲内とすることにより、形成される防滑層の厚み（高さ）を好ましい範囲とすることができる。また、粘着剤層の厚みを上記範囲内とすることにより、貫通孔を形成した後の粘着剤層の安定性を高めることができ、所望の形状を有する防滑層を形成することができる。なお、粘着剤層の厚みは、被着物の表面性状によって適宜調節することができる。例えば、被着物の表面が凹凸形状を有する場合、凹凸追従性を高めるために、粘着剤層の厚みを厚くすることも好ましい。 The thickness of the pressure-sensitive adhesive layer is preferably 5 to 100 μm, more preferably 8 to 80 μm, and even more preferably 10 to 50 μm. By setting the thickness of the pressure-sensitive adhesive layer within the above range, the thickness (height) of the anti-slip layer to be formed can be set within a preferable range. Further, by setting the thickness of the pressure-sensitive adhesive layer within the above range, the stability of the pressure-sensitive adhesive layer after forming the through holes can be enhanced, and the anti-slip layer having a desired shape can be formed. The thickness of the pressure-sensitive adhesive layer can be appropriately adjusted depending on the surface texture of the adherend. For example, when the surface of the adherend has an uneven shape, it is also preferable to increase the thickness of the pressure-sensitive adhesive layer in order to improve the unevenness-following property.
（剥離剤層）
本発明は、滑り止め施工用粘着シートの粘着剤層の一方の面側であって、表面層が積層された面とは反対の面側にさらに剥離剤層を有する剥離剤層付き滑り止め施工用粘着シートに関するものであってもよい。このような剥離剤層を設けることにより、粘着剤層の表面にゴミや埃等の付着物が付着することを抑制することができる。これにより、粘着剤層と被着物の密着性の低下を防止することができる。
剥離剤層としては、例えば、周知の剥離シートが使用される。周知の剥離シートとしては、例えば、キャストコート紙、アート紙、コート紙、上質紙、クラフト紙、グラシン紙、ポリエチレンテレフタレート（ＰＥＴ）フィルム、ポリプロピレン（ＰＰ）フィルム等の支持体の表面に、必要に応じて目止め層を形成した上で、シリコーン系等の剥離剤を塗布した剥離シートなどが挙げられる。(Release layer)
The present invention is a non-slip construction with a release agent layer which is one surface side of the pressure-sensitive adhesive layer of the adhesive sheet for non-slip construction and further has a release agent layer on the surface side opposite to the surface on which the surface layers are laminated. It may be related to an adhesive sheet for use. By providing such a release agent layer, it is possible to prevent deposits such as dust and dirt from adhering to the surface of the pressure-sensitive adhesive layer. This makes it possible to prevent a decrease in the adhesion between the pressure-sensitive adhesive layer and the adherend.
As the release agent layer, for example, a well-known release sheet is used. As a well-known release sheet, for example, cast coated paper, art paper, coated paper, high-quality paper, kraft paper, glassin paper, polyethylene terephthalate (PET) film, polypropylene (PP) film and the like are required on the surface of a support. A release sheet or the like, which is formed by forming a sealing layer and then coated with a release agent such as a silicone type, may be mentioned.
本発明の滑り止め施工用粘着シートは、剥離剤層を有さず、表面層と粘着剤層の２層構成からなる粘着シートであってもよく、この場合は、ロール状に巻き取られたテープであってもよい。また、剥離剤層を有する剥離剤層付き滑り止め施工用粘着シートの場合もロール状に巻き取られた状態で保管されてもよい。 The non-slip adhesive sheet of the present invention may be an adhesive sheet having a two-layer structure of a surface layer and an adhesive layer without having a release agent layer, and in this case, it is wound into a roll. It may be a tape. Further, a non-slip adhesive sheet with a release agent layer having a release agent layer may also be stored in a rolled state.
（滑り止め施工用粘着シートの製造方法）
本発明の滑り止め施工用粘着シートの製造工程は、剥離剤層上に粘着剤層を構成する粘着剤塗工液を塗工する工程と、粘着剤層の一方の面側であって、剥離剤層が積層された面とは反対の面側に表面層を積層する工程と、貫通孔を形成する工程を含むことが好ましい。
粘着剤塗工液を塗工する工程の後には、粘着剤層を硬化する工程を含むことが好ましく、粘着剤層を溶剤型粘着剤から形成する場合は、乾燥工程を含むことが好ましい。(Manufacturing method of adhesive sheet for non-slip construction)
The manufacturing process of the non-slip adhesive sheet of the present invention is a step of applying an adhesive coating liquid constituting the adhesive layer on the release agent layer and a step of applying the adhesive coating liquid constituting the adhesive layer on one surface side of the adhesive layer. It is preferable to include a step of laminating the surface layer on the surface side opposite to the surface on which the agent layer is laminated and a step of forming a through hole.
After the step of applying the pressure-sensitive adhesive coating liquid, it is preferable to include a step of curing the pressure-sensitive adhesive layer, and when the pressure-sensitive adhesive layer is formed from a solvent-type pressure-sensitive adhesive, it is preferable to include a drying step.
また、表面層を積層する工程の前工程として、表面層の少なくとも一方の面にエンボス加工を施す工程を設けることが好ましい。 Further, as a pre-step of the step of laminating the surface layer, it is preferable to provide a step of embossing at least one surface of the surface layer.
貫通孔を形成する工程は、剥離剤層と、粘着剤層と、表面層がこの順で積層された剥離剤層付き貫通孔形成用粘着シートにパンチング加工やレーザー加工等を施す工程である。加工法は、貫通孔の形状等に併せて適宜選択することができる。 The step of forming the through hole is a step of punching, laser processing, or the like on the adhesive sheet for forming the through hole with the release agent layer in which the release agent layer, the pressure-sensitive adhesive layer, and the surface layer are laminated in this order. The processing method can be appropriately selected according to the shape of the through hole and the like.
（貫通孔形成用粘着シート）
本発明は、貫通孔を形成する前の貫通孔形成用粘着シートに関するものでもある。貫通孔形成用粘着シートは、表面層と、粘着剤層を有し、上述したような貫通孔を形成するための粘着シートである。(Adhesive sheet for forming through holes)
The present invention also relates to an adhesive sheet for forming a through hole before forming the through hole. The pressure-sensitive adhesive sheet for forming through-holes has a surface layer and an adhesive layer, and is a pressure-sensitive adhesive sheet for forming through-holes as described above.
貫通孔形成用粘着シートの２３℃環境下における粘着力は、０．３～８．０Ｎ／２５ｍｍであることが好ましく、０．５～７．７Ｎ／２５ｍｍであることがより好ましく、０．８～７.５Ｎ／２５ｍｍであることがさらに好ましく、１．０～７．０Ｎ／２５ｍｍであることが特に好ましい。ここで、上記粘着力は、貫通孔を形成する前の状態における粘着力であり、ＪＩＳ Ｚ ０２３７に準じて測定した値である。粘着剤層の粘着力を上記範囲内とすることにより、貫通孔の形成が容易となり、さらに貫通孔を形成した後の滑り止め施工用粘着シートと被着物の密着性を高めることができる。 The adhesive strength of the adhesive sheet for forming a through hole in an environment of 23 ° C. is preferably 0.3 to 8.0 N / 25 mm, more preferably 0.5 to 7.7 N / 25 mm, and 0.8. It is more preferably to 7.5 N / 25 mm, and particularly preferably 1.0 to 7.0 N / 25 mm. Here, the adhesive force is the adhesive force in the state before forming the through hole, and is a value measured according to JIS Z 0237. By setting the adhesive strength of the pressure-sensitive adhesive layer within the above range, the formation of through holes can be facilitated, and the adhesiveness between the non-slip adhesive sheet for anti-slip construction and the adherend after forming the through holes can be improved.
（滑り止め施工方法）
本発明の滑り止め施工用粘着シートは滑り止め施工方法に使用される。具体的には、滑り止め施工用粘着シートが床面等の被着物に貼着され、その後、滑り止め施工用粘着シートの貫通孔内に、防滑層を形成する充填剤を充填し、硬化することで防滑層が形成される。本発明の滑り止め施工用粘着シートは防滑層が形成された後に、被着物から剥離される。(Non-slip construction method)
The non-slip adhesive sheet of the present invention is used in the non-slip construction method. Specifically, the non-slip construction adhesive sheet is attached to an adherend such as a floor surface, and then the through hole of the non-slip construction adhesive sheet is filled with a filler forming an anti-slip layer and cured. As a result, an anti-slip layer is formed. The non-slip adhesive sheet of the present invention is peeled off from the adherend after the anti-slip layer is formed.
図２は、本発明の滑り止め施工用粘着シートを用いて滑り止め施工を施す様子を説明する図である。図２では、施工方法をわかりやすく説明するために、貫通孔を大きく、かつ可視化して示している。また、図２では、滑り止め施工を施す対象を床面Ｐとしているが、滑り止め施工は床面以外にも施すことができる。
以下で、滑り止め施工方法について詳述する。FIG. 2 is a diagram illustrating a state in which anti-slip construction is performed using the non-slip construction adhesive sheet of the present invention. In FIG. 2, in order to explain the construction method in an easy-to-understand manner, the through holes are shown in a large size and visualized. Further, in FIG. 2, the target to which the anti-slip construction is applied is the floor surface P, but the anti-slip construction can be applied to other than the floor surface.
The non-slip construction method will be described in detail below.
滑り止め施工方法は、（Ａ）本発明の滑り止め施工用粘着シート１００を床面に貼り付ける工程と、（Ｂ）滑り止め施工用粘着シート１００の貫通孔３０と床面Ｐとで形成された空間の中に充填剤を充填し、充填剤３５の少なくとも一部を床面Ｐに付着させる工程と、（Ｃ）滑り止め施工用粘着シート１００を床から取り除く工程と、を含む。滑り止め施工方法は、さらに（Ｄ）床面Ｐ上に付着した充填剤３５を硬化させる工程を含むことが好ましい。
The non-slip construction method is formed by (A) a step of attaching the non-slip
（Ａ）工程の前には、床面Ｐの清浄化工程を含むことが好ましい。清浄化工程においては、床面のゴミや埃等を除去した後、薬剤等を用いて床面Ｐの油汚れやその他の汚れを除去することが好ましい。薬剤としては、例えば、イソプロパノールやアセトンの有機溶剤を用いることができる。 (A) It is preferable to include a cleaning step of the floor surface P before the step. In the cleaning step, it is preferable to remove dust and dirt on the floor surface, and then use a chemical or the like to remove oil stains and other stains on the floor surface P. As the drug, for example, an organic solvent such as isopropanol or acetone can be used.
（Ａ）工程においては、本発明の滑り止め施工用粘着シート１００が床面Ｐに貼着される。滑り止め施工用粘着シート１００を貼着する際には、滑り止め施工用粘着シート１００と床面Ｐとの密着性を高めるために、圧締ローラーで圧締することが好ましい。
In the step (A), the non-slip
（Ｂ）工程においては、滑り止め施工用粘着シート１００の貫通孔３０に、充填剤３５が充填される。この時、充填剤３５は、貫通孔３０の総容積よりも多い量が用いられ、貫通孔３０内に充填されずに余った充填剤は、ヘラなどを用いることで除去される。このような工程をスキージ工程と呼ぶこともある。スキージ工程では、ヘラで表面層の表面を均すことにより、貫通孔３０内に充填剤を密に充填することができ、さらに、充填剤の上面を平らにすることができる。
In the step (B), the
本発明の滑り止め施工用粘着シート１００の表面層１０は、上述した通り、透明基材であることが好ましい。また、表面層１０の表面露出面にはエンボス加工が施されていることが好ましい。このようなエンボス加工が施されていることにより、表面層には微細な凹凸形状が形成され、表面で光が乱反射することにより、表面層は半透明状態になる。このような表面層は充填剤が透明な場合に、充填剤の充填がなされたことを確認しやすく好ましい。すなわち、表面層の色度や透明度は、充填剤の色度や透明度と異なっていることが好ましい。
As described above, the
（Ｂ）工程は、充填剤を硬化させる工程を含むことが好ましい。充填剤としては室温で硬化するものを用いることが好ましい。また、必要に応じてドライヤー等を用いて加熱硬化をしてもよい。なお、室温で充填剤を硬化させる場合には、充填後１～２４時間経過した後に（Ｃ）工程に移ることが好ましいが、充填剤の性状によっては、直ちに（Ｃ）工程に移行することも可能である。充填後に十分に硬化させることによって、（Ｃ）工程において滑り止め施工用粘着シート１００を床から取り除いた後にも充填剤がその周辺に拡がって立体形状を失うことを防ぐことができる。
The step (B) preferably includes a step of curing the filler. As the filler, it is preferable to use one that cures at room temperature. Further, if necessary, it may be heat-cured using a dryer or the like. When the filler is cured at room temperature, it is preferable to move to the step (C) 1 to 24 hours after filling, but depending on the properties of the filler, the step (C) may be performed immediately. It is possible. By sufficiently curing after filling, it is possible to prevent the filler from spreading around the floor and losing its three-dimensional shape even after the non-slip
（Ｃ）工程では、滑り止め施工用粘着シート１００は床面Ｐから剥離され、処分される。滑り止め施工用粘着シート１００を床面Ｐから剥離した後には、貫通孔３０内で硬化した充填剤が床面Ｐ上に突設され、このような硬化充填剤を防滑層５０と呼ぶことができる。防滑層５０は、滑り止め施工用粘着シート１００に設けられた貫通孔３０の数の分だけ形成されることになる。このようにして形成された多数の防滑層５０が床面の水はけを促し、滑り止め効果が発揮される。
In the step (C), the non-slip
滑り止め施工方法において（Ｄ）工程を設ける場合は、この（Ｄ）工程は（Ｂ）工程で硬化させた充填剤をさらに完全硬化させる工程となる。（Ｄ）工程においては、例えば、薬剤等を噴霧することにより完全硬化を促進してもよく、加熱乾燥等をさらに行ってもよい。また、紫外線照射をすることによって硬化を促進してもよい。
なお、用いる充填剤の種類によっては、このような完全硬化工程を設けなくても、（Ｂ）工程で充填剤を完全硬化させることも可能である。When the step (D) is provided in the non-slip construction method, the step (D) is a step of further completely curing the filler cured in the step (B). In the step (D), for example, complete curing may be promoted by spraying a chemical or the like, or heat drying or the like may be further performed. Further, curing may be promoted by irradiating with ultraviolet rays.
Depending on the type of filler used, it is possible to completely cure the filler in the step (B) without providing such a complete curing step.
＜充填剤＞
充填剤としては、例えば、シリコーン樹脂、アクリル樹脂、ウレタン樹脂、エポキシ樹脂等を挙げることができる。上記充填剤には添加剤として、各種着色染料、顔料、蛍光剤および／または畜光剤を添加することもできる。このような添加剤は、充填剤の色度や透明度を、表面層の色度や透明度と異なるものとすることができる。これにより、滑り止め施工用粘着シートの貫通孔に充填剤の充填がなされたことを確認しやすくなり、充填剤の充填漏れ（充填抜け）を防止することができる。さらに、上記充填剤には、形成される防滑層の強度を上げるために、ガラスビーズを添加してもよい。<Filler>
Examples of the filler include silicone resin, acrylic resin, urethane resin, epoxy resin and the like. Various coloring dyes, pigments, fluorescent agents and / or photochromic agents can be added to the filler as additives. Such additives can make the chromaticity and transparency of the filler different from the chromaticity and transparency of the surface layer. This makes it easier to confirm that the through hole of the non-slip adhesive sheet has been filled with the filler, and it is possible to prevent the filler from leaking (filling omission). Further, glass beads may be added to the filler in order to increase the strength of the anti-slip layer to be formed.
＜施工対象＞
滑り止め施工を施す対象としては、例えば、床、携帯電話の筐体、おぼんの表裏面、食器棚等が挙げられる。特に、滑り止め施工を床に施す場合は、公共施設の床、ペットサロン等の床、浴室の床、調理場の床、工場の床、駅構内の床や階段など、床面に水が付着する可能性のある床に好ましく用いることができる。中でも、セラミックタイル製の床材、御影石、大理石等の天然石床材、および塩化ビニル樹脂など硬質な素材を使ったプラスチック系床材などに好ましく用いることができ、特にセラミックタイル製の床材に好ましく用いられることが出来る。<Construction target>
Examples of objects to be subjected to anti-slip construction include floors, mobile phone housings, front and back surfaces of trays, cupboards, and the like. In particular, when anti-slip construction is applied to the floor, water adheres to the floor surface such as the floor of public facilities, the floor of pet salons, the floor of bathrooms, the floor of kitchens, the floor of factories, the floor of station premises and stairs. It can be preferably used for possible floors. Among them, it can be preferably used for ceramic tile flooring materials, natural stone flooring materials such as mikage stone and marble, and plastic flooring materials using hard materials such as vinyl chloride resin, and is particularly preferable for ceramic tile flooring materials. Can be used.
また、本発明は、滑り止め施工用粘着シートと、滑り止め施工用粘着シートの貫通孔に充填する充填剤を含む滑り止め施工用キットに関するものとしてもよい。 Further, the present invention may relate to a non-slip construction kit including a non-slip construction adhesive sheet and a filler for filling the through holes of the non-slip construction adhesive sheet.
以下に実施例と比較例を挙げて本発明の特徴をさらに具体的に説明する。以下の実施例に示す材料、使用量、割合、処理内容、処理手順等は、本発明の趣旨を逸脱しない限り適宜変更することができる。したがって、本発明の範囲は以下に示す具体例により限定的に解釈されるべきものではない。なお、以下において、実施例１は、参考例１と読み替えるものとする。 Hereinafter, the features of the present invention will be described in more detail with reference to Examples and Comparative Examples. The materials, amounts used, ratios, treatment contents, treatment procedures, etc. shown in the following examples can be appropriately changed as long as they do not deviate from the gist of the present invention. Therefore, the scope of the present invention should not be construed as limiting by the specific examples shown below. In the following, Example 1 shall be read as Reference Example 1.
（実施例１）
アクリル系粘着剤（トーヨーケム株式会社製ＢＰＳ５３０３－２ＯＪＩ）１００質量部に、東ソー株式会社製コロネートＬ 質量５部を配合して粘着剤を得た。上記粘着剤を、剥離紙（王子タック株式会社製青グラシン８２）に、コンマコータにより塗工し、１００℃、２分間加熱して、粘着剤層（厚さ：２０μｍ）を形成した。
上記粘着剤層の露出面に、透明塩化ビニルシート（アキレス株式会社製、ＦＣＺＡ３５０２、厚さ：２００μｍ）を貼り合わせた。その後、タレットパンチング加工機を用いて、表１に記載の形状を有する貫通孔を形成した。このようにして実施例１の滑り止め施工用粘着シートを得た。(Example 1)
An acrylic pressure-sensitive adhesive (BPS5303-2OJI manufactured by Toyo Chem Co., Ltd.) was mixed with 5 parts by mass of Coronate L manufactured by Tosoh Corporation to obtain a pressure-sensitive adhesive. The above pressure-sensitive adhesive was applied to a release paper (blue glassine 82 manufactured by Oji Tac Co., Ltd.) with a comma coater and heated at 100 ° C. for 2 minutes to form a pressure-sensitive adhesive layer (thickness: 20 μm).
A transparent vinyl chloride sheet (manufactured by Achilles Corporation, FCZA3502, thickness: 200 μm) was attached to the exposed surface of the pressure-sensitive adhesive layer. Then, using a turret punching machine, through holes having the shapes shown in Table 1 were formed. In this way, the non-slip construction adhesive sheet of Example 1 was obtained.
（実施例２）
透明塩化ビニルシートとしてエンボス加工が施されたシート（アキレス株式会社製、ＦＣＮＡ３５０２、厚さ：２００μｍ）を用い、貫通孔の形状を表１に記載の通りとなるように変更した以外は実施例１と同様にして滑り止め施工用粘着シートを得た。(Example 2)
Example 1 except that an embossed sheet (manufactured by Achilles Corporation, FCNA3502, thickness: 200 μm) was used as a transparent vinyl chloride sheet, and the shape of the through hole was changed to be as shown in Table 1. In the same manner as above, an adhesive sheet for non-slip construction was obtained.
（実施例３～５）
透明塩化ビニルシートの厚みを表１の通りとし、粘着剤層の厚みを表１の通りとし、かつ貫通孔の形状を表１に記載の通りとなるように変更した以外は実施例２と同様にして滑り止め施工用粘着シートを得た。(Examples 3 to 5)
Same as Example 2 except that the thickness of the transparent vinyl chloride sheet is as shown in Table 1, the thickness of the adhesive layer is as shown in Table 1, and the shape of the through holes is changed as shown in Table 1. And obtained an adhesive sheet for non-slip construction.
（実施例６）
透明塩化ビニルシートを透明ポリオレフィンシート（オカモト株式会社製、ＰＯ系コンビニフィルム、厚さ：３００μｍ）とし、かつアクリル系粘着剤をウレタン系粘着剤（トーヨーケム株式会社製、ＳＰ－２０５）に変更した以外は実施例５と同様にして滑り止め施工用粘着シートを得た。(Example 6)
Other than changing the transparent vinyl chloride sheet to a transparent polyolefin sheet (Okamoto Co., Ltd., PO-based convenience film, thickness: 300 μm) and changing the acrylic-based adhesive to a urethane-based adhesive (Toyo Chem Co., Ltd., SP-205). Obtained an adhesive sheet for non-slip construction in the same manner as in Example 5.
（実施例７）
ウレタン系粘着剤をアクリル系粘着剤に変更し、粘着剤層の厚みを表１の通りとし、かつ貫通孔の形状を表１に記載の通りとなるように変更した以外は実施例６と同様にして滑り止め施工用粘着シートを得た。(Example 7)
Same as Example 6 except that the urethane adhesive was changed to an acrylic adhesive, the thickness of the adhesive layer was changed as shown in Table 1, and the shape of the through holes was changed as shown in Table 1. And obtained an adhesive sheet for non-slip construction.
（比較例１）
透明塩化ビニルシートを自己吸着白色発泡ウレタンフォーム（イノアックコーポレーション社製ＰｕｒｅＣｅｌｌ、厚み１０００μｍ）に変更し、粘着剤層を設けなかった以外は実施例２と同様にして滑り止め施工用粘着シートを得た。(Comparative Example 1)
The transparent vinyl chloride sheet was changed to a self-adsorbing white urethane foam (PureCell manufactured by Inoac Corporation, thickness 1000 μm), and an adhesive sheet for non-slip construction was obtained in the same manner as in Example 2 except that an adhesive layer was not provided. ..
（比較例２）
透明塩化ビニルシートをエンボス加工がされていないものに変更し、粘着剤層を形成しなかった以外は実施例３と同様にして滑り止め施工用粘着シートを得た。(Comparative Example 2)
The transparent vinyl chloride sheet was changed to one that was not embossed, and a non-slip adhesive sheet was obtained in the same manner as in Example 3 except that the adhesive layer was not formed.
（比較例３）
比較例２で用いた透明塩化ビニルシートに、表１の形状を有する貫通孔を形成し、エポキシ系接着剤（スリーボンド社製、ＴＢ２０８１Ｄ）を１０μｍの厚みになるよう塗布し、滑り止め施工用粘着シートを得た。(Comparative Example 3)
A through hole having the shape shown in Table 1 is formed in the transparent vinyl chloride sheet used in Comparative Example 2, and an epoxy adhesive (TB2081D manufactured by ThreeBond Co., Ltd.) is applied to a thickness of 10 μm to obtain a non-slip adhesive. I got a sheet.
（実施例８）
トーヨーケム株式会社ＢＰＳ５３０３－２ＯＪＩ １００質量部に、東ソー株式会社製コロネートＬ ５質量部を配合して粘着剤を得た。上記粘着剤を、剥離紙（王子タック株式会社製青グラシン８２）に、リップコータにより塗工し、１００℃、７分間加熱して、粘着剤層（厚さ：１２０μｍ）を形成した。上記粘着剤層の露出面に、エンボス加工が施された透明塩化ビニルシートであって、厚みが３００μｍの透明塩化ビニルシートを貼り合わせ、実施例１と同様の貫通孔を形成した。このようにして実施例８の滑り止め施工用粘着シートを得た。(Example 8)
Toyo Chem Co., Ltd. BPS5303-
（実施例９）
表面層として、白色ユポ（ユポコーポレーション社製、ニューユポＦＧＳ、厚み：２００μｍ）を用い、粘着剤層の厚みを表１の通りとし、かつ貫通孔の形状を表１に記載の通りとなるように変更した以外は実施例１と同様にして滑り止め施工用粘着シートを得た。(Example 9)
As the surface layer, white Yupo (manufactured by Yupo Corporation, New Yupo FGS, thickness: 200 μm) is used, the thickness of the adhesive layer is as shown in Table 1, and the shape of the through hole is as shown in Table 1. An adhesive sheet for non-slip construction was obtained in the same manner as in Example 1 except that the change was made.
（実施例１０）
表面層として、透明ＰＥＴフィルム（東レ株式会社製、ルミラーＳ－１０、厚み：１８８μｍ）を用い、貫通孔の形状を表１に記載の通りとなるように変更した以外は実施例１と同様にして滑り止め施工用粘着シートを得た。(Example 10)
A transparent PET film (manufactured by Toray Industries, Inc., Lumirror S-10, thickness: 188 μm) was used as the surface layer, and the same as in Example 1 except that the shape of the through hole was changed to be as shown in Table 1. Obtained an adhesive sheet for non-slip construction.
（評価）
＜滑り止め施工方法＞
セラミックタイル製の床材を清浄した後に、実施例及び比較例で得られた滑り止め施工用粘着シートを床面に貼着した。その後、シリコーン樹脂とガラスビーズ（粒径：８０μｍ）を含む充填剤を貫通孔に充填し、室温下℃で２４時間硬化させた。その後、滑り止め施工用粘着シートを床面から剥離し、防滑層を形成した。
滑り止め施工時のハンドリング性について、下記の評価基準にて評価した。(evaluation)
<Non-slip construction method>
After cleaning the floor material made of ceramic tile, the non-slip adhesive sheet obtained in Examples and Comparative Examples was attached to the floor surface. Then, a filler containing a silicone resin and glass beads (particle size: 80 μm) was filled in the through holes and cured at room temperature for 24 hours. Then, the non-slip adhesive sheet was peeled off from the floor surface to form an anti-slip layer.
The handleability during non-slip construction was evaluated according to the following evaluation criteria.
＜貼り易さ及び充填剤漏れ＞
床面表面に滑り止め施工用粘着シートを貼付する際、任意の場所へ貼合できるか否かを評価した。また、充填剤を貫通孔に充填し、貫通孔周辺の樹脂漏れの有無を確認した。
○：粘着剤層と床面表面間に気泡の噛み込みがなく、床面の任意の位置に貼付できる。また充填剤を貫通孔に漏れなく充填できる。
△：粘着剤層と床面表面間での一部気泡の噛み込みにより貼付作業に時間を要するが、床面の任意の位置に貼付できる。また充填剤を貫通孔に漏れなく充填できる。
×：粘着剤層と床面表面間での気泡の噛み込みにより、何度も貼り替え作業を要する。また充填剤が貫通孔から漏れ出る。<Easy to apply and leakage of filler>
When attaching the non-slip adhesive sheet to the floor surface, it was evaluated whether or not it could be attached to any place. In addition, the filler was filled in the through hole, and the presence or absence of resin leakage around the through hole was confirmed.
◯: There is no air bubbles getting caught between the adhesive layer and the floor surface, and it can be attached to any position on the floor surface. In addition, the filler can be filled in the through holes without leakage.
Δ: It takes time to apply due to the biting of some air bubbles between the adhesive layer and the floor surface surface, but it can be applied to any position on the floor surface. In addition, the filler can be filled in the through holes without leakage.
X: Due to air bubbles getting caught between the adhesive layer and the floor surface surface, reattachment work is required many times. Also, the filler leaks out of the through hole.
＜剥がし易さ＞
床面に貼付した滑り止め施工用粘着シート上に充填剤を充填後、滑り止め施工用粘着シートを剥がす工程にて、作業者が滑り止め施工用粘着シートを床面から全面剥がす際の剥がしやすさを評価した。
○：床面から滑り止め施工用粘着シートをスムーズに剥がせる。
△：かなり力を使うが床面から滑り止め施工用粘着シートを剥がせる。
×：床面から滑り止め施工用粘着シートを剥がせない、剥がし途中で止まる。<Easy to peel off>
After filling the non-slip adhesive sheet attached to the floor with a filler, it is easy for the operator to peel off the non-slip adhesive sheet from the floor in the process of peeling off the non-slip adhesive sheet. I evaluated it.
◯: The non-slip adhesive sheet can be smoothly peeled off from the floor.
△: Although it uses a lot of force, the non-slip adhesive sheet can be peeled off from the floor.
×: The non-slip adhesive sheet cannot be peeled off from the floor, and it stops in the middle of peeling.
＜糊残り＞
作業者が床面全面から滑り止め施工用粘着シートを剥がした後、粘着剤層の糊残りを目視で確認した。
○：床面の表面に糊残りがない。
△：床面の一部に糊残りを起こす。
×：床面全面に糊残りを起こす。<Remaining glue>
After the operator peeled off the non-slip adhesive sheet from the entire floor surface, the adhesive residue on the adhesive layer was visually confirmed.
◯: There is no adhesive residue on the floor surface.
Δ: Glue residue is generated on a part of the floor surface.
X: Causes adhesive residue on the entire floor surface.
＜（ヘラの）表面滑り性＞
滑り止め施工用粘着シートの貫通孔に充填剤を充填する際、ヘラでスキージ作業を行い、すべり性を評価した。
○：ヘラが滑り止め施工用粘着シート表面をスムーズに滑り、気泡を噛み込まず充填剤を貫通孔に充填できる。
△：ヘラが滑り止め施工用粘着シート表面をスムーズに滑るが、気泡を噛み込みながら充填剤を貫通孔に充填できる。
×：ヘラが滑り止め施工用粘着シート表面を滑らず、充填剤を貫通孔に充填できない。<Spatula (spatula) surface slipperiness>
When filling the through holes of the non-slip adhesive sheet with the filler, squeegee work was performed with a spatula and the slipperiness was evaluated.
◯: The spatula slides smoothly on the surface of the non-slip adhesive sheet, and the filler can be filled in the through hole without biting air bubbles.
Δ: The spatula slides smoothly on the surface of the non-slip adhesive sheet, but the filler can be filled in the through hole while biting air bubbles.
X: The spatula does not slip on the surface of the non-slip adhesive sheet, and the filler cannot be filled in the through hole.
＜充填確認容易性＞
滑り止め施工用粘着シート上に充填剤を充填した際に、充填部分の認識容易性を評価した。
○：滑り止め施工用粘着シート上の充填剤塗工部と未塗工部がはっきりと認識できる。
△：滑り止め施工用粘着シート上の充填剤塗工部と未塗工部がなんとか認識できる。局所的な塗工抜けがある。
×：滑り止め施工用粘着シート上の充填剤塗工部と未塗工部との差異が認識できない。塗抜けが発生する。<Easy to check filling>
When the filler was filled on the non-slip adhesive sheet, the ease of recognition of the filled portion was evaluated.
◯: The filled part and the uncoated part on the non-slip adhesive sheet can be clearly recognized.
Δ: The filler-coated part and the uncoated part on the non-slip adhesive sheet can be recognized somehow. There is a local coating omission.
X: The difference between the filled part and the uncoated part on the non-slip adhesive sheet cannot be recognized. Paint through occurs.
＜防滑層性状（防滑性）＞
ＪＩＳ Ａ １４５４に定める床材の滑り性試験によって測定される滑り抵抗係数（ＣＳＲ値）による防滑層のすべり難さを評価した。
◎：ＣＳＲ値が０．５０以上
○：ＣＳＲ値が０．４５以上０．５０未満
△：ＣＳＲ値が０．４０以上０．４５未満
×：ＣＳＲ値が０．４０未満<Anti-slip layer properties (anti-slip properties)>
The slip resistance of the anti-slip layer was evaluated by the slip resistance coefficient (CSR value) measured by the slip resistance test of the floor material specified in JIS A 1454.
⊚: CSR value is 0.50 or more ○: CSR value is 0.45 or more and less than 0.50 Δ: CSR value is 0.40 or more and less than 0.45 ×: CSR value is less than 0.40
＜粘着力評価（貫通孔形成前）＞
貫通孔形成前の滑り止め施工用粘着シートを２５ｍｍ×１００ｍｍに裁断後、剥離紙（セパレータ）を剥がしてＳＵＳ板に２ｋｇ荷重ロールで圧着し、常温で３０分間放置した。その後、引張試験機（型式：オートグラフＡＧＳ－Ｊ、島津製作所社製）を用い、ＪＩＳ Ｚ ０２３７に準じて引張速度３００ｍｍ／分で１８０度剥離した際の剥離強度を測定し、その剥離強度を貫通孔形成前の粘着力とした。<Adhesive strength evaluation (before formation of through hole)>
After cutting the non-slip adhesive sheet before forming the through hole to 25 mm × 100 mm, the release paper (separator) was peeled off, crimped onto a SUS plate with a 2 kg load roll, and left at room temperature for 30 minutes. After that, using a tensile tester (model: Autograph AGS-J, manufactured by Shimadzu Corporation), the peel strength when peeling 180 degrees at a tensile speed of 300 mm / min was measured according to JIS Z 0237, and the peel strength was measured. The adhesive strength before forming the through hole was used.
＜粘着力評価（貫通孔形成後）＞
貫通孔形成後の滑り止め施工用粘着シートを５０ｍｍ×１００ｍｍに裁断後、剥離紙（セパレータ）を剥がしてＳＵＳ板に２ｋｇ荷重ロールで圧着し、常温で３０分間放置した。その後、引張試験機（型式：オートグラフＡＧＳ－Ｊ、島津製作所社製）を用い、ＪＩＳ Ｚ ０２３７に準じて引張速度３００ｍｍ／分で１８０度剥離した際の剥離強度を測定し、その剥離強度を貫通孔形成後の粘着力とした。<Adhesive strength evaluation (after forming through holes)>
After cutting the non-slip adhesive sheet after forming the through hole into 50 mm × 100 mm, the release paper (separator) was peeled off, crimped onto a SUS plate with a 2 kg load roll, and left at room temperature for 30 minutes. After that, using a tensile tester (model: Autograph AGS-J, manufactured by Shimadzu Corporation), the peel strength when peeling 180 degrees at a tensile speed of 300 mm / min was measured according to JIS Z 0237, and the peel strength was measured. The adhesive strength after the formation of the through hole was used.
実施例で得られた滑り止め施工用粘着シートを用いた場合、防滑層が所望の形状で形成されており、十分な防滑性能を発揮することができる。特に実施例１～７で得られた滑り止め施工用粘着シートを用いた場合、滑り止め施工用粘着シートの貼り易さ及び剥がし易さが優れており、施工時に充填剤等をヘラで均す際のヘラの滑り性等が良好であり、ハンドリング性に優れていた。 When the non-slip adhesive sheet obtained in the examples is used, the anti-slip layer is formed in a desired shape, and sufficient anti-slip performance can be exhibited. In particular, when the non-slip adhesive sheet obtained in Examples 1 to 7 is used, the non-slip adhesive sheet is excellent in ease of sticking and peeling, and the filler or the like is leveled with a spatula at the time of construction. The slipperiness of the spatula was good, and the handling property was excellent.
１０ 表面層
２０ 粘着剤層
３０ 貫通孔
３５ 充填剤
５０ 防滑層
１００ 滑り止め施工用粘着シート
Ｐ 床面10
Claims (10)
前記表面層の少なくとも表面露出面にはエンボス加工が施されている、滑り止め施工用粘着シート。 It has a surface layer and a pressure-sensitive adhesive layer, and has a plurality of through holes penetrating the surface layer and the pressure-sensitive adhesive layer.
An adhesive sheet for non-slip construction in which at least the exposed surface of the surface layer is embossed.