JP6912539B2 - 光輝性顔料とその製造方法、顔料含有組成物、及び顔料含有塗装体 - Google Patents
光輝性顔料とその製造方法、顔料含有組成物、及び顔料含有塗装体 Download PDFInfo
- Publication number
- JP6912539B2 JP6912539B2 JP2019185529A JP2019185529A JP6912539B2 JP 6912539 B2 JP6912539 B2 JP 6912539B2 JP 2019185529 A JP2019185529 A JP 2019185529A JP 2019185529 A JP2019185529 A JP 2019185529A JP 6912539 B2 JP6912539 B2 JP 6912539B2
- Authority
- JP
- Japan
- Prior art keywords
- pigment
- titanium oxide
- fine particles
- oxide film
- flake
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
フレーク状ガラスと、前記フレーク状ガラス上に形成された酸化チタン膜と、前記酸化チタン膜上に付着した、又は前記フレーク状ガラスと前記酸化チタン膜との間に配置された金微粒子とを備え、前記酸化チタン膜の膜厚が150nm以上であり、D65光源を用いて測定した反射色が、L*C*h表色系に基づいて15以上のC*と150〜300の範囲のhとにより示される、光輝性顔料、を提供する。
フレーク状ガラスと、前記フレーク状ガラス上に形成された酸化チタン膜と、前記酸化チタン膜上に付着した、又は前記フレーク状ガラスと前記酸化チタン膜との間に配置された金微粒子とを備えた光輝性顔料の製造方法であって、
前記フレーク状ガラスと前記酸化チタン膜とを備えた基体顔料、又は前記フレーク状ガラスと、平均粒径が1〜40nmの範囲にある金微粒子を含む金コロイド溶液とを接触させて、前記基体顔料の前記酸化チタン膜上、又は前記フレーク状ガラス上に前記金微粒子を付着させる付着工程と、
前記金微粒子が付着した前記基体顔料、又は前記金微粒子が付着した前記フレーク状ガラスの表面に前記酸化チタン膜が形成された微粒子挟持顔料を加熱することにより、D65光源を用いて測定した、前記金微粒子が付着した前記基体顔料又は前記微粒子挟持顔料の反射色のL*C*h表色系のC*を増加させる加熱工程と、を備え、
前記基体顔料又は前記微粒子挟持顔料の前記酸化チタン膜の膜厚が150nm以上であり、
前記光輝性顔料のD65光源を用いて測定した反射色がL*C*h表色系に基づいて15以上のC*と150〜300の範囲のhにより示される、光輝性顔料の製造方法、を提供する。
・金コロイド溶液の調製
塩化金酸四水和物(粉末、大浦貴金属工業製、純度99.0%以上)25gを240gの水で希釈し、10.4質量(wt)%の塩化金酸溶液を作製した。また、クエン酸ナトリウム(ナカライテスク製)を純水で10wt%に希釈したクエン酸ナトリウム溶液を作製した。1Lの丸底フラスコに10.4wt%の塩化金酸溶液2.0gと純水993.5gとを投入し、100℃に保持しながら30分加熱還流した。引き続き、丸底フラスコに10wt%クエン酸ナトリウム溶液4.5gを投入し、100℃に保持しながらさらに30分加熱還流した後、丸底フラスコを水中で室温まで冷却して、金コロイド溶液を得た。透過型電子顕微鏡(TEM)を用いて得られた金微粒子(金コロイド粒子)の1次粒径を測定し、平均粒径を算出した。金コロイド粒子の平均粒径は5〜10nmの範囲にあった。
上記合成方法で作製した金コロイド溶液800gと青色の基体顔料50gとを1Lビーカーに投入した。用いた基体顔料は、フレーク状ガラス上に厚み160nmのルチル型酸化チタン膜を形成した日本板硝子製「メタシャインMT1030RB」である。なお、この基体顔料及び以下で使用した基体顔料を構成するフレーク状ガラスは、粒径が約33μm、厚みが約1.3μmである。ビーカー内で攪拌羽根を用いて金コロイド溶液及び基体顔料を攪拌しながら塩酸を投入してpHを2〜4に調整し、10分攪拌を行った。その後、ろ過により上澄み液から光輝性顔料を分離し、光輝性顔料を600℃で2時間熱処理した。こうして、鮮やかな青色に発色する光輝性顔料を得た。
・フレーク状ガラスへの金微粒子の付着
上記合成方法で作製した金コロイド溶液2gとフレーク状ガラス50gとを1Lビーカーに投入した。用いたフレーク状ガラスは、平均粒径33μm、厚み1.3μmのフレーク状ガラス(日本板硝子製)である。ビーカー内で攪拌羽根を用いて金コロイド溶液及びフレーク状ガラスを攪拌しながら塩酸を投入してpHを2〜4に調整し、10分攪拌を行った。その後、ろ過により上澄み液からフレーク状ガラスを分離し、180℃で乾燥し、その後600℃で2時間焼成し、金微粒子を付着させた金微粒子付きフレーク状ガラスを得た。
金微粒子付きフレーク状ガラス50gにイオン交換水を加えて全容量を500mlにした後、これらを攪拌機で攪拌しながら希塩酸を加えてpHを1.5に調整してスラリー液を得た。得られたスラリー液に常温の塩化スズ(IV)0.7wt%水溶液を67ml加えた後、そのpHを希塩酸で1.5に調整して混合スラリー液を得た。得られた混合スラリー液を5分間攪拌した後、混合スラリー液からフレーク状ガラスを減圧ろ過により回収した。回収したフレーク状ガラスをイオン交換水で水洗してスズによる前処理を行ったフレーク状ガラスを得た。
実施例1と同様にして作製した金コロイド溶液800gと緑色の基体顔料50gとを1Lビーカーに投入した。用いた基体顔料は、フレーク状ガラス上に厚み175nmのルチル型酸化チタン膜を形成した日本板硝子製「メタシャインMT1030RG」である。ビーカー内で攪拌羽根を用いて金コロイド溶液及び基体顔料を攪拌しながら塩酸を投入してpHを2〜4に調整し、10分攪拌を行った。その後、ろ過により上澄み液から光輝性顔料を分離し、光輝性顔料を700℃で2時間熱処理した。こうして、緑色に発色する光輝性顔料を得た。
ルチル型酸化チタン膜の形成のための四塩化チタン水溶液と水酸化ナトリウム水溶液との添加をさらに継続して実施し、パール調の緑色を有するルチル型酸化チタン膜を形成したことを除いては、実施例2と同様にして、緑色に発色する光輝性顔料を得た。酸化チタン膜の形成は、予めその膜厚が175nmとなる時間を測定しておいてその時間だけ継続した。
・金コロイド溶液の調製
カゼイン(関東化学製)3.8mgを、5.52mol/Lに希釈した3−アミノ−1−プロパノール(和光純薬工業製)5.2mlに加え、15分間撹拌し、カゼインを溶解させた。さらに、0.2mol/Lの塩化金酸溶液(三津和化学製)0.8mlを添加し、撹拌した。この溶液に、ジメチルアミンボラン(和光純薬製)4.7mgとアスコルビン酸ナトリウム(和光純薬製)158mgとを純水2mlに溶解させて調製した還元剤溶液を添加し、80℃で加熱処理し、金コロイド溶液を調製した。投入量から求めた金に対するカゼインのモル比は0.010である。得られた金微粒子(金コロイド粒子)の平均粒径を実施例と同様にして測定したところ、5〜10nmの範囲にあった。
上記合成方法で作製した金コロイド溶液2gと黄色の基体顔料50gとを1Lビーカーに投入した。用いた基体顔料は、フレーク状ガラス上に厚み100nmのルチル型酸化チタン膜を形成した日本板硝子製「メタシャインMT1030RY」である。ビーカー内で攪拌羽根を用いて金コロイド溶液及び基体顔料を攪拌しながら塩酸を投入してpHを2〜4に調整し、10分攪拌を行った。その後、ろ過により上澄み液から分離して、やや黄色味が強い橙色に発色する光輝性顔料を得た。
・金コロイド溶液の調製
比較例と同様にして金コロイド溶液を調製した。
基体顔料としてフレーク状ガラス上に厚み130nmのルチル型酸化チタン膜を形成した日本板硝子製「メタシャインMT1030RR」(赤色)を用いた以外は、比較例と同様にして、赤色に発色する光輝性顔料を得た。
・金コロイド溶液の調製
比較例と同様にして金コロイド溶液を調製した。
基体顔料として酸化チタン膜が形成されていない平均粒径33μm、厚み1.3μmのフレーク状ガラス(日本板硝子製)を用いた以外は、比較例と同様にして、赤色に発色する光輝性顔料を得た。
上記実施例、比較例及び参照例から得た光輝性顔料の粉体と用いた基体顔料の粉体に関し、分光測色計CM−5(コニカミノルタ製)を使用して測色を実施した。測色する粉体は微小シャーレ(φ3mm)に充填して測定に供した。光源はD65を用い、SCE(正反射光除去)法、視野角2°の条件で測色した。結果を表1に示す。
上記実施例、比較例及び参照例から得た光輝性顔料の粉体及び基体顔料の粉体に関し、塗布体を作製した。塗布体は、アクリル樹脂に粉体10wt%を混合した塗布用組成物を基材とした白地の紙の上に塗布して作製した。塗膜の厚みは70〜80μmとした。
担持率は王水を用いて金を溶解し、ICP−MSで測定した。サンプル10mgを秤量し、オートクレーブのPTFE容器の底に静かに入れた。メスピペットで王水5mlを、サンプルの入ったPTFE容器に入れた。オートクレーブの金属容器を密閉し、150℃で7時間の熱処理を行った。温度が常温まで下がった後、容器を空け、溶液を取り出した。所定濃度に希釈したのち、ICP−MSで液濃度を測定した。希釈率から金の担持率を算出した。結果を表1に示す。
ろ過により上澄み液から光輝性顔料を分離するところまでを実施例1と同様に実施し、サンプルAを得た。また、サンプルAを100℃、2時間の条件で乾燥させ、サンプルBを得た。さらに、サンプルBを700℃、2時間熱処理して、サンプルCを得た。
実施例3から得た光輝性顔料をサンプルDとした。
サンプルA〜Dについて金微粒子の結晶子径を測定した。結晶子径は、粉末のX線回折測定(X線回折装置として株式会社リガク製「SmartLab」を使用)により得られた回折スペクトルを解析することにより求めた。サンプル粉末をガラス製の試料ホルダーに充填してCuのKα線(波長1.54Å)を用いてθ−2θ測定を行った。
Claims (10)
- フレーク状ガラスと、前記フレーク状ガラス上に形成された酸化チタン膜と、前記酸化チタン膜上に付着した、又は前記フレーク状ガラスと前記酸化チタン膜との間に配置された金微粒子とを備え、前記酸化チタン膜の膜厚が150nm以上であり、D65光源を用いて測定した反射色が、L*C*h表色系に基づいて、15以上のC*と150〜300の範囲のhとにより示され、前記金微粒子の結晶子径が12nm以上である、光輝性顔料。
- 前記hが225〜300である、請求項1に記載の光揮性顔料。
- 前記C*が25以上である、請求項2に記載の光揮性顔料。
- 前記hが150〜225である、請求項1に記載の光揮性顔料。
- 前記酸化チタン膜の膜厚が150nm〜185nmである、請求項1に記載の光輝性顔料。
- 前記フレーク状ガラス、前記酸化チタン膜及び前記金微粒子の合計質量に対する、前記金微粒子の質量の比率により定義される担持率が、0.01〜3%である、請求項1に記載の光輝性顔料。
- 請求項1に記載の光輝性顔料を含む顔料含有組成物。
- 基材と、請求項1に記載の光輝性顔料を含む、前記基材上に形成された塗膜とを備えた顔料含有塗装体。
- フレーク状ガラスと、前記フレーク状ガラス上に形成された酸化チタン膜と、前記酸化チタン膜上に付着した、又は前記フレーク状ガラスと前記酸化チタン膜との間に配置された金微粒子とを備えた光輝性顔料の製造方法であって、
前記フレーク状ガラスと前記酸化チタン膜とを備えた基体顔料、又は前記フレーク状ガラスと、平均粒径が1〜40nmの範囲にある金微粒子を含む金コロイド溶液とを接触させて、前記基体顔料の前記酸化チタン膜上、又は前記フレーク状ガラス上に前記金微粒子を付着させる付着工程と、
前記酸化チタン膜上に前記金微粒子が付着した前記基体顔料、又は前記金微粒子が付着した前記フレーク状ガラスの表面に前記酸化チタン膜が形成された微粒子挟持顔料を加熱することにより、D65光源を用いて測定した、前記金微粒子が付着した前記基体顔料又は前記微粒子挟持顔料の反射色のL*C*h表色系のC*を増加させる加熱工程と、を備え、
前記基体顔料又は前記微粒子挟持顔料の前記酸化チタン膜の膜厚が150nm以上であり、
前記光輝性顔料のD65光源を用いて測定した反射色がL*C*h表色系に基づいて、15以上のC*と150〜300の範囲のhとにより示され、前記金微粒子の結晶子径が12nm以上である、光輝性顔料の製造方法。 - 前記付着工程において前記基体顔料の前記酸化チタン膜上に前記金微粒子を付着させ、
前記加熱工程において前記金微粒子を覆う被膜が存在しない状態で前記基体顔料を加熱する、請求項9に記載の製造方法。