JP6896582B2 - Label for display - Google Patents
Label for display Download PDFInfo
- Publication number
- JP6896582B2 JP6896582B2 JP2017195043A JP2017195043A JP6896582B2 JP 6896582 B2 JP6896582 B2 JP 6896582B2 JP 2017195043 A JP2017195043 A JP 2017195043A JP 2017195043 A JP2017195043 A JP 2017195043A JP 6896582 B2 JP6896582 B2 JP 6896582B2
- Authority
- JP
- Japan
- Prior art keywords
- pressure
- sensitive adhesive
- resin
- adhesive layer
- display label
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、表示用ラベルに関するものであり、特に医療用器具や医薬品容器への貼付に好適な表示用ラベルに関するものである。 The present invention relates to a display label, and particularly relates to a display label suitable for attachment to a medical device or a pharmaceutical container.
シリンジ等の医療用器具や、医薬品が収容される医薬品容器といった医療用製品では、当該器具や容器の材料として、従来はガラス製のものが用いられてきた。しかしながら、使用時の煩雑さや流通コスト等の観点から、近年、樹脂製の材料に変更されることが多くなっている。 In medical products such as medical instruments such as syringes and pharmaceutical containers in which pharmaceutical products are stored, glass materials have been conventionally used as the material for the instruments and containers. However, in recent years, the material is often changed to a resin material from the viewpoint of complexity at the time of use, distribution cost, and the like.
このような樹脂製の医療用製品に対して従来の表示用ラベルを使用した場合、当該表示用ラベルが備える粘着剤層から溶出する粘着成分によって、医療用製品が汚染される懸念が存在する。特に、医療用製品が樹脂製であることにより、当該粘着成分が内部にまで浸透する可能性もある。このような粘着成分による汚染を抑制するため、粘着剤層から粘着成分が溶出し難い表示用ラベルの開発が進められている。 When a conventional display label is used for such a resin-made medical product, there is a concern that the medical product may be contaminated by the adhesive component eluted from the pressure-sensitive adhesive layer included in the display label. In particular, since the medical product is made of resin, the adhesive component may penetrate into the inside. In order to suppress such contamination by the adhesive component, the development of a display label in which the adhesive component is difficult to elute from the adhesive layer is underway.
例えば、特許文献１には、上述のような表示用ラベルに用いられる粘着テープとして、粘着テープからの総揮発性有機化合物（ＴＶＯＣ）の放散量が、粘着剤層の面１ｃｍ２当たり、ｎ−デカン換算量として１．０μｇ以下である粘着テープが開示されている。 For example, in Patent Document 1, as the adhesive tape used for the above-mentioned display label, the amount of total volatile organic compounds (TVOC) emitted from the adhesive tape is n- per 1 cm 2 of the surface of the adhesive layer. An adhesive tape having a decan equivalent amount of 1.0 μg or less is disclosed.
ところで、医療用製品に係る器具や容器の材料として、コスト低減の観点から、ポリプロピレン樹脂等のオレフィン系樹脂を使用することが検討されている。しかしながら、オレフィン系樹脂からなる表面に対して、アクリル系の粘着剤組成物から形成された粘着剤層を備える従来の表示用ラベルを貼付した場合、十分な粘着力が発揮されない場合がある。この場合、医療用製品の保管や使用において、表示用ラベルが医療用製品から剥がれたり脱落し易くなるという問題がある。 By the way, from the viewpoint of cost reduction, the use of an olefin resin such as a polypropylene resin is being studied as a material for instruments and containers related to medical products. However, when a conventional display label having a pressure-sensitive adhesive layer formed of an acrylic pressure-sensitive adhesive composition is attached to a surface made of an olefin-based resin, sufficient adhesive strength may not be exhibited. In this case, in the storage and use of the medical product, there is a problem that the display label is easily peeled off or dropped from the medical product.
本発明は、上記のような実状に鑑みてなされたものであり、粘着成分の溶出が生じ難いとともに、所定の樹脂製部材の表面に対しても十分な粘着力を発揮できる表示用ラベルを提供することを目的とする。 The present invention has been made in view of the above-mentioned actual conditions, and provides a display label capable of exerting sufficient adhesive force on the surface of a predetermined resin member as well as being less likely to cause elution of adhesive components. The purpose is to do.
上記目的を達成するために、本発明は、基材と、前記基材の一方の面側に積層された粘着剤層とを備えた表示用ラベルであって、前記粘着剤層が、アクリル系共重合体と、粘着付与剤とを含有する粘着剤組成物から形成されたものであり、前記アクリル系共重合体の分子量分布（Ｍｗ／Ｍｎ）が、３．０以下であることを特徴とする表示用ラベルを提供する（発明１）。 In order to achieve the above object, the present invention is a display label including a base material and a pressure-sensitive adhesive layer laminated on one surface side of the base material, wherein the pressure-sensitive adhesive layer is an acrylic type. It is formed from a pressure-sensitive adhesive composition containing a copolymer and a pressure-sensitive adhesive, and is characterized in that the molecular weight distribution (Mw / Mn) of the acrylic copolymer is 3.0 or less. A label for display is provided (Invention 1).
上記発明（発明１）に係る表示用ラベルでは、粘着剤層が、アクリル系共重合体と粘着付与剤とを含有する粘着剤組成物から形成されたものであるとともに、アクリル系共重合体の分子量分布（Ｍｗ／Ｍｎ）が、３．０以下であることにより、粘着成分の溶出が生じ難いとともに、通常の粘着剤層では粘着力を発揮し難い樹脂製部材の表面に対しても十分な粘着力を発揮できる。 In the display label according to the above invention (Invention 1), the pressure-sensitive adhesive layer is formed of a pressure-sensitive adhesive composition containing an acrylic copolymer and a pressure-sensitive adhesive, and is made of an acrylic copolymer. When the molecular weight distribution (Mw / Mn) is 3.0 or less, it is difficult for the adhesive component to elute, and it is sufficient for the surface of the resin member, which is difficult to exert adhesive force with a normal adhesive layer. Can exert adhesive strength.
上記発明（発明１）において、前記アクリル系共重合体の重量平均分子量（Ｍｗ）は、３０，０００以上、３００，０００以下であることが好ましい（発明２）。 In the above invention (Invention 1), the weight average molecular weight (Mw) of the acrylic copolymer is preferably 30,000 or more and 300,000 or less (Invention 2).
上記発明（発明１，２）において、前記粘着剤組成物中における前記粘着付与剤の含有量は、前記アクリル系共重合体および前記粘着付与剤の含有量の合計に対して、５質量％以上、５０質量％以下であることが好ましい（発明３）。 In the above inventions (Inventions 1 and 2), the content of the tackifier in the pressure-sensitive adhesive composition is 5% by mass or more with respect to the total content of the acrylic copolymer and the tackifier. , 50% by mass or less is preferable (Invention 3).
上記発明（発明１〜３）において、前記粘着付与剤は、ロジン系樹脂およびスチレン系樹脂の少なくとも一種を含むことが好ましい（発明４）。 In the above inventions (Inventions 1 to 3), the tackifier preferably contains at least one of a rosin-based resin and a styrene-based resin (Invention 4).
上記発明（発明１〜４）において、前記粘着付与剤は、軟化点が５０℃以上、１２０℃以下であることが好ましい（発明５）。 In the above inventions (Inventions 1 to 4), the tackifier preferably has a softening point of 50 ° C. or higher and 120 ° C. or lower (Invention 5).
上記発明（発明１〜５）において、前記アクリル系共重合体は、アクリル系ポリマーのトリブロック共重合体を含むことが好ましい（発明６）。 In the above inventions (Inventions 1 to 5), it is preferable that the acrylic copolymer contains a triblock copolymer of an acrylic polymer (Invention 6).
上記発明（発明１〜６）において、ＪＩＳ Ｚ０２３７：２００９に準拠して測定された、ポリプロピレン板に対する１８０°引きはがし粘着力は、１．０Ｎ／２５ｍｍ以上であることが好ましい（発明７）。 In the above inventions (Inventions 1 to 6), the 180 ° peeling adhesive force with respect to the polypropylene plate measured in accordance with JIS Z0237: 2009 is preferably 1.0 N / 25 mm or more (Invention 7).
上記発明（発明１〜７）においては、医療用製品に使用されることが好ましい（発明８）。 In the above inventions (Inventions 1 to 7), it is preferably used for medical products (Invention 8).
上記発明（発明８）において、前記医療用製品の表面の少なくとも一部は、オレフィン系樹脂からなり、前記表示用ラベルは、オレフィン系樹脂からなる前記表面に貼付されることが好ましい（発明９）。 In the above invention (Invention 8), it is preferable that at least a part of the surface of the medical product is made of an olefin resin, and the display label is affixed to the surface made of an olefin resin (Invention 9). ..
本発明に係る表示用ラベルは、粘着成分の溶出が生じ難いとともに、所定の樹脂製部材の表面に対しても十分な粘着力を発揮できる。 The display label according to the present invention is less likely to cause elution of adhesive components and can exhibit sufficient adhesive force on the surface of a predetermined resin member.
以下、本発明の実施形態について説明する。
本発明の一実施形態に係る表示用ラベルは、基材と、当該基材の一方の面側に積層された粘着剤層とを備える。
Hereinafter, embodiments of the present invention will be described.
The display label according to the embodiment of the present invention includes a base material and an adhesive layer laminated on one surface side of the base material.
本実施形態に係る表示用ラベルでは、粘着剤層が、アクリル系共重合体と、粘着付与剤とを含有する粘着剤組成物から形成されたものである。ここで、当該粘着剤組成物が粘着付与剤を含有することにより、形成された粘着剤層は、被着体に対して十分な粘着力を発揮することができる。その結果、本実施形態に係る表示用ラベルは、従来の表示用ラベルでは粘着力を発揮し難い、ポリプロピレン樹脂といったオレフィン系樹脂からなる表面に対しても十分な粘着力を発揮できる。そのため、本実施形態に係る表示用ラベルは、被着体からの剥がれや脱落が生じ難い。 In the display label according to the present embodiment, the pressure-sensitive adhesive layer is formed of a pressure-sensitive adhesive composition containing an acrylic copolymer and a pressure-sensitive adhesive. Here, when the pressure-sensitive adhesive composition contains a pressure-sensitive adhesive, the formed pressure-sensitive adhesive layer can exhibit sufficient adhesive strength with respect to the adherend. As a result, the display label according to the present embodiment can exhibit sufficient adhesive force even on a surface made of an olefin resin such as polypropylene resin, which is difficult to exhibit adhesive force with the conventional display label. Therefore, the display label according to the present embodiment is unlikely to be peeled off or dropped from the adherend.
また、本実施形態に係る表示用ラベルでは、上述したアクリル系共重合体の分子量分布（Ｍｗ／Ｍｎ）が、３．０以下である。これにより、粘着剤層中における低分子量の粘着成分の含有量は比較的少ないものとなり、粘着剤層からの粘着成分の溶出が抑制される。そのため、本実施形態に係る表示用ラベルを医療用製品に貼付した場合であっても、表示用ラベルから当該医療用製品に対する粘着成分の溶出が抑制され、それに伴い、当該医療用製品の内部への粘着成分の透過も抑制される。その結果、当該医療用製品の信頼性が高いものとなる。 Further, in the display label according to the present embodiment, the molecular weight distribution (Mw / Mn) of the above-mentioned acrylic copolymer is 3.0 or less. As a result, the content of the low molecular weight pressure-sensitive adhesive component in the pressure-sensitive adhesive layer becomes relatively small, and the elution of the pressure-sensitive adhesive component from the pressure-sensitive adhesive layer is suppressed. Therefore, even when the display label according to the present embodiment is attached to the medical product, the elution of the adhesive component from the display label to the medical product is suppressed, and accordingly, the inside of the medical product is suppressed. Permeation of the adhesive component of is also suppressed. As a result, the reliability of the medical product is high.
１．基材
本実施形態に係る表示用ラベルにおいて、基材の材料は限定されない。樹脂系の材料を主成分とする樹脂系シートから構成されていてもよいし、紙系の材料から構成されていてもよい。
1. 1. Base material In the display label according to the present embodiment, the material of the base material is not limited. It may be composed of a resin-based sheet containing a resin-based material as a main component, or may be composed of a paper-based material.
樹脂系シートに係る樹脂の成分としては、ポリエチレン、ポリプロピレン等のオレフィン系重合体；ポリエチレンテレフタレート、ポリブチレンテレフタレート等のエステル系重合体；ナイロン６，６、ナイロン６といったナイロン等のアミド系重合体などが例示される。上記の樹脂系シートに係る樹脂として、上記の成分を含有する樹脂のほかに、例えば、アセテート樹脂、アクリロニトリル−ブタジエン−スチレン共重合（ＡＢＳ）樹脂、ポリスチレン樹脂、塩化ビニル樹脂、ポリエステルアミド樹脂、ポリエーテル樹脂、ポリイミド樹脂、ポリアミドイミド樹脂、ポリ−ｐ−フェニレンスルフィド樹脂、ポリエーテルエステル樹脂などが挙げられる。これらの中でも、ポリエチレンテレフタレートを使用することが好ましい。基材はこれらの材料の一種を含有してもよいし、二種以上を含有してもよい。 Examples of the resin component of the resin sheet include olefin polymers such as polyethylene and polypropylene; ester polymers such as polyethylene terephthalate and polybutylene terephthalate; and amide polymers such as nylon such as nylon 6, 6 and nylon 6. Is exemplified. As the resin related to the above resin-based sheet, in addition to the resin containing the above components, for example, acetate resin, acrylonitrile-butadiene-styrene copolymer (ABS) resin, polystyrene resin, vinyl chloride resin, polyesteramide resin, poly Examples thereof include ether resin, polyimide resin, polyamideimide resin, poly-p-phenylene sulfide resin, and polyether ester resin. Among these, it is preferable to use polyethylene terephthalate. The base material may contain one of these materials, or may contain two or more of these materials.
基材は、上述した樹脂成分を材料とする合成紙であってもよく、特に、当該合成紙は、上述したオレフィン系重合体および上述したエステル系重合体の少なくとも一種を材料とするものであることが好ましい。 The base material may be a synthetic paper made of the above-mentioned resin component as a material, and in particular, the synthetic paper is made of at least one of the above-mentioned olefin-based polymer and the above-mentioned ester-based polymer. Is preferable.
基材を構成する樹脂系シートは、加熱により収縮する性質を有するものであってもよい。このような樹脂系シートの好ましい例としては、そのような収縮性を有するポリエチレンテレフタレートフィルム、ポリスチレンフィルム、ポリエチレンフィルム、ポリプロピレンフィルム等が挙げられる。このような熱収縮性を有する樹脂系シートは、一般的に収縮ラベルとして使用されており、本実施形態に係る表示用ラベルにおける基材としてこのような樹脂系シートを使用することで、表示用ラベルを、貼付する対象となる医療用製品に合った形状に熱収縮させて密着させることが可能となる。 The resin-based sheet constituting the base material may have a property of shrinking by heating. Preferred examples of such a resin-based sheet include polyethylene terephthalate film, polystyrene film, polyethylene film, polypropylene film and the like having such shrinkage. A resin-based sheet having such heat shrinkage property is generally used as a shrinkage label, and by using such a resin-based sheet as a base material in the display label according to the present embodiment, it is used for display. The label can be heat-shrinked into a shape suitable for the medical product to be affixed and brought into close contact with the label.
また、基材を構成する樹脂系シートは、未延伸のものであってもよいし、縦、横などの一軸方向または二軸方向に延伸されたものであってもよい。延伸されたものを使用する場合、特に二軸延伸ポリプロピレンフィルムを使用することが好ましい。 Further, the resin-based sheet constituting the base material may be unstretched, or may be stretched in the uniaxial direction or the biaxial direction such as vertical and horizontal. When a stretched film is used, it is particularly preferable to use a biaxially stretched polypropylene film.
基材は、上記の樹脂系シートの一層から構成されていてもよいし、上記の樹脂系シートが複数積層されて基材を構成していてもよい。複数層からなる基材の例としては、ポリエチレンテレフタレートフィルムと、エチレン−ビニルアルコール共重合体フィルムとの積層体、ポリエチレンテレフタレートフィルムと、エチレン−ビニルアルコール共重合体フィルムと、ポリエチレンテレフタレートフィルムとを順に積層してなる積層体、ポリエチレンテレフタレートフィルムと、エチレン−ビニルアルコール共重合体フィルムと、二軸延伸ポリプロピレンフィルムとを順に積層してなる積層体、ポリエチレンテレフタレートフィルムと、エチレン−ビニルアルコール共重合体フィルムと、ナイロンフィルムとを順に積層してなる積層体等が挙げられる。 The base material may be composed of one layer of the above-mentioned resin-based sheet, or may be formed by laminating a plurality of the above-mentioned resin-based sheets to form a base material. Examples of the base material composed of a plurality of layers include a laminate of a polyethylene terephthalate film and an ethylene-vinyl alcohol copolymer film, a polyethylene terephthalate film, an ethylene-vinyl alcohol copolymer film, and a polyethylene terephthalate film in this order. Laminated laminate, polyethylene terephthalate film, ethylene-vinyl alcohol copolymer film, and biaxially stretched polypropylene film laminated in order, polyethylene terephthalate film, ethylene-vinyl alcohol copolymer film And a laminated body formed by laminating nylon films in order.
基材が樹脂系の材料から構成される場合には、基材は、粘着剤層と共押出成形により製造されたものであってもよい。 When the base material is composed of a resin-based material, the base material may be manufactured by coextrusion molding with the pressure-sensitive adhesive layer.
基材が紙系の材料から構成される場合の具体例としては、上質紙、アート紙、コート紙等が挙げられる。 Specific examples of the case where the base material is composed of a paper-based material include high-quality paper, art paper, coated paper, and the like.
基材における少なくとも一方の面には、表示用ラベルとしての表示を構成するための所望の印刷を施してもよい。当該印刷は、従来公知の方法により行うことができる。 At least one side of the substrate may be printed as desired to form a label as a label. The printing can be performed by a conventionally known method.
基材を構成する材料が着色材料（カーボンブラック、二酸化チタンなどの顔料、および染料が例示される。）を含有することにより、基材が着色されていてもよい。さらに、機械特性を高めたり耐ブロッキング性を付与したりする観点から、基材を構成する材料がシリカなどの微粒子を含有していてもよい。基材は、用途に応じて、充填剤、酸化防止剤、紫外線吸収剤などの成分をさらに含有していてもよい。 The base material may be colored by containing a coloring material (for example, pigments such as carbon black and titanium dioxide, and dyes) in the material constituting the base material. Further, from the viewpoint of enhancing mechanical properties and imparting blocking resistance, the material constituting the base material may contain fine particles such as silica. The base material may further contain components such as a filler, an antioxidant, and an ultraviolet absorber, depending on the intended use.
基材には、プライマーコート層、印刷層、コーティング層、金属蒸着層、紫外線防止層等の機能性層が形成されていてもよく、また、少なくとも片面に金属箔が積層されていてもよい。これらの層および金属箔は、その用途に応じて、基材のどちらの面に設けてもよい。 A functional layer such as a primer coat layer, a printing layer, a coating layer, a metal vapor deposition layer, and an ultraviolet protection layer may be formed on the base material, or a metal foil may be laminated on at least one side thereof. These layers and metal foils may be provided on either side of the substrate, depending on the application.
基材の厚さは、用途に応じて適宜設定でき、特に限定されない。例えば基材の厚さは、１０μｍ以上であることが好ましく、特に２０μｍ以上であることが好ましく、さらには２５μｍ以上であることが好ましい。また、当該厚さは、１０００μｍ以下であることが好ましく、特に５００μｍ以下であることが好ましく、さらには２００μｍ以下であることが好ましい。なお、本明細書において、基材の厚さとは、前述した機能性層や金属箔等を含む厚さを意味する。 The thickness of the base material can be appropriately set according to the application and is not particularly limited. For example, the thickness of the base material is preferably 10 μm or more, particularly preferably 20 μm or more, and further preferably 25 μm or more. The thickness is preferably 1000 μm or less, particularly preferably 500 μm or less, and further preferably 200 μm or less. In the present specification, the thickness of the base material means the thickness including the above-mentioned functional layer, metal foil, and the like.
２．粘着剤層
本実施形態に係る表示用ラベルでは、粘着剤層が、アクリル系共重合体と、粘着付与剤とを含有する粘着剤組成物から形成されたものである。これにより、本実施形態に係る表示用ラベルは、被着体に対して十分な粘着力を発揮するものとなり、特に、ポリプロピレン樹脂といったオレフィン系樹脂からなる表面に対しても十分な粘着力を発揮できる。
2. Adhesive layer In the label for display according to the present embodiment, the adhesive layer is formed of an adhesive composition containing an acrylic copolymer and a pressure-sensitive adhesive. As a result, the display label according to the present embodiment exhibits sufficient adhesive strength to the adherend, and in particular, exhibits sufficient adhesive strength to the surface made of an olefin resin such as polypropylene resin. it can.
（１）アクリル系共重合体
上記アクリル系共重合体は、分子量分布（Ｍｗ／Ｍｎ）が、３．０以下であり、１．５以下であることが好ましい。当該分子量分布（Ｍｗ／Ｍｎ）が３．０を超える場合、アクリル系共重合体は、低分子量の共重合体を比較的多く含むものとなり、得られる粘着剤層中の低分子量の粘着成分の含有量が多くなる結果、粘着剤層からの粘着成分の溶出が生じ易くなる。なお、上記分子量分布（Ｍｗ／Ｍｎ）の下限値は、特に制限されないものの、１．０以上であることが好ましい。
(1) Acrylic copolymer The above acrylic copolymer has a molecular weight distribution (Mw / Mn) of 3.0 or less, preferably 1.5 or less. When the molecular weight distribution (Mw / Mn) exceeds 3.0, the acrylic copolymer contains a relatively large amount of the low molecular weight copolymer, and the low molecular weight pressure-sensitive adhesive component in the obtained pressure-sensitive adhesive layer As a result of increasing the content, elution of the adhesive component from the adhesive layer is likely to occur. The lower limit of the molecular weight distribution (Mw / Mn) is not particularly limited, but is preferably 1.0 or more.
また、上記アクリル系共重合体の重量平均分子量（Ｍｗ）は、３０，０００以上であることが好ましく、特に４０，０００以上であることが好ましく、さらには５０，０００以上であることが好ましい。また、当該重量平均分子量（Ｍｗ）は、３００，０００以下であることが好ましく、特に２５０，０００以下であることが好ましく、さらには２００，０００以下であることが好ましい。上記アクリル系共重合体の重量平均分子量（Ｍｗ）が３０，０００以上であることで、得られる粘着剤層中の低分子量（例えば、１０，０００以下）の粘着成分の量がより少なくなり、粘着剤層からの粘着成分の溶出が効果的に抑制される。また、当該重量平均分子量（Ｍｗ）が３００，０００以下であることで、アクリル系共重合体の粘性が過度に高くなることが抑制され、粘着剤層をシート状に形成し易いものとなる。 The weight average molecular weight (Mw) of the acrylic copolymer is preferably 30,000 or more, particularly preferably 40,000 or more, and further preferably 50,000 or more. The weight average molecular weight (Mw) is preferably 300,000 or less, particularly preferably 250,000 or less, and further preferably 200,000 or less. When the weight average molecular weight (Mw) of the acrylic copolymer is 30,000 or more, the amount of low molecular weight (for example, 10,000 or less) adhesive component in the obtained pressure-sensitive adhesive layer becomes smaller. Elution of the adhesive component from the adhesive layer is effectively suppressed. Further, when the weight average molecular weight (Mw) is 300,000 or less, the viscosity of the acrylic copolymer is suppressed from becoming excessively high, and the pressure-sensitive adhesive layer can be easily formed into a sheet shape.
なお、本明細書において、重量平均分子量（Ｍｗ）および数平均分子量（Ｍｎ）の値は、テトラヒドロフラン（ＴＨＦ）を溶媒とするゲル・パーミエーションクロマトグラフィー（ＧＰＣ）による標準ポリスチレン換算値として測定された値を意味する。具体的には、ＧＰＣ測定装置（東ソー社製「ＨＬＣ−８２２０ＧＰＣ」）を使用して、以下に示す条件にて行うものとする。
カラム：ＴＳＫｇｅｌＧＭＨＸＬ→ＴＳＫｇｅｌＧＭＨＸＬ→ＴＳＫｇｅｌ２０００ＨＸＬ
注入量：８０μｌ
測定温度：４０℃
流速：１ｍｌ／分
検出器：示差屈折計
試料濃度：１％（ｗ／ｖ）
In the present specification, the values of the weight average molecular weight (Mw) and the number average molecular weight (Mn) were measured as standard polystyrene-equivalent values by gel permeation chromatography (GPC) using tetrahydrofuran (THF) as a solvent. Means a value. Specifically, a GPC measuring device (“HLC-8220 GPC” manufactured by Tosoh Corporation) shall be used, and the measurement shall be performed under the conditions shown below.
Column: TSKgelGMHXL → TSKgelGMHXL → TSKgel2000HXL
Injection volume: 80 μl
Measurement temperature: 40 ° C
Flow velocity: 1 ml / min Detector: Differential refractometer Sample concentration: 1% (w / v)
アクリル系共重合体の具体的な例としては、分子量分布（Ｍｗ／Ｍｎ）が３．０以下であるとともに、形成される粘着剤層によって所望の粘着力が発揮される限り、特に限定されないが、これらの事項を満たし易いという観点から、アクリル系共重合体は、アクリル系ポリマーのトリブロック共重合体を含むことが好ましい。アクリル系ポリマーのトリブロック共重合体は、通常、アクリル系モノマーのリビングアニオン重合により得られる。このようなリビングアニオン重合は、アクリル系モノマーの共重合を行う際に一般的なフリーラジカル重合と比較して、未反応のモノマー原料が生じ難い。そのため、リビングアニオン重合により得られた共重合体の分子量分布は、フリーラジカル重合により得られた重合体の分子量分布に比べて、シャープなピークを有する傾向がある。したがって、アクリル系ポリマーのトリブロック共重合体は、所望の粘着力を有する粘着剤を形成しながらも、分子量分布（Ｍｗ／Ｍｎ）が３．０以下という物性を満たし易い。 Specific examples of the acrylic copolymer are not particularly limited as long as the molecular weight distribution (Mw / Mn) is 3.0 or less and the desired adhesive force is exhibited by the formed adhesive layer. From the viewpoint of easily satisfying these matters, the acrylic copolymer preferably contains a triblock copolymer of an acrylic polymer. A triblock copolymer of an acrylic polymer is usually obtained by living anionic polymerization of an acrylic monomer. In such living anionic polymerization, an unreacted monomer raw material is less likely to be generated as compared with general free radical polymerization when copolymerizing an acrylic monomer. Therefore, the molecular weight distribution of the copolymer obtained by living anionic polymerization tends to have a sharper peak than the molecular weight distribution of the polymer obtained by free radical polymerization. Therefore, the triblock copolymer of an acrylic polymer can easily satisfy the physical characteristics of a molecular weight distribution (Mw / Mn) of 3.0 or less while forming a pressure-sensitive adhesive having a desired adhesive strength.
アクリル系モノマーのトリブロック共重合体は、ブロックセグメントＡと、当該ブロックセグメントＡとは異なるブロックセグメントＢとを想定した場合、Ａ−Ｂ−Ａ型のブロック構造を有する。 The triblock copolymer of the acrylic monomer has an ABA type block structure when the block segment A and the block segment B different from the block segment A are assumed.
上記ブロックセグメントＡはハードセグメントであり、上記ブロックセグメントＢはソフトセグメントであることが好ましい。このように、ハードセグメントがトリブロック共重合体の両端に位置することにより、粘着剤層が良好な粘着力を発揮し易くなる。また、粘着剤組成物の押出成型により粘着剤層を形成する場合において、加工適性が良好なものとなる。 It is preferable that the block segment A is a hard segment and the block segment B is a soft segment. By locating the hard segments at both ends of the triblock copolymer in this way, the pressure-sensitive adhesive layer tends to exhibit good adhesive strength. Further, when the pressure-sensitive adhesive layer is formed by extrusion molding of the pressure-sensitive adhesive composition, the processability becomes good.
上記ブロックセグメントＡを構成するモノマーとしては、メタクリル酸メチル、メタクリル酸エチル、メタクリル酸イソプロピル、メタクリル酸ｎ−プロピル、メタクリル酸ｎ−ブチル、メタクリル酸イソブチル、メタクリル酸ｓｅｃ−ブチル、メタクリル酸ｔｅｒｔ−ブチル、メタクリル酸ｎ−ヘキシル、メタクリル酸シクロヘキシル、メタクリル酸２−エチルヘキシル、メタクリル酸ｎ−オクチル、メタクリル酸ラウリル、メタクリル酸トリデシル、メタクリル酸ステアリル、メタクリル酸イソボルニル、メタクリル酸フェニル、メタクリル酸ベンジル、メタクリル酸メトキシエチル、メタクリル酸エトキシエチル、メタクリル酸ジエチルアミノエチル、メタクリル酸２−ヒドロキシエチル、メタクリル酸２−アミノエチル、メタクリル酸グリシジル、メタクリル酸テトラヒドロフルフリル等が挙げられる。これらは単独で用いてもよく、２種以上を併用してもよい。これらの中でも、上記ブロックセグメントＡを構成するモノマーは、得られる粘着剤層の、透明性、耐熱性、耐久性を向上させる観点から、メタクリル酸メチル、メタクリル酸エチル、メタクリル酸ｔｅｒｔ−ブチル、メタクリル酸シクロヘキシル、メタクリル酸イソボルニル、メタクリル酸フェニルがより好ましく、メタクリル酸メチルがさらに好ましい。 Examples of the monomer constituting the block segment A include methyl methacrylate, ethyl methacrylate, isopropyl methacrylate, n-propyl methacrylate, n-butyl methacrylate, isobutyl methacrylate, sec-butyl methacrylate and tert-butyl methacrylate. , N-hexyl methacrylate, cyclohexyl methacrylate, 2-ethylhexyl methacrylate, n-octyl methacrylate, lauryl methacrylate, tridecyl methacrylate, stearyl methacrylate, isobornyl methacrylate, phenyl methacrylate, benzyl methacrylate, methoxy methacrylate Examples thereof include ethyl, ethoxyethyl methacrylate, diethylaminoethyl methacrylate, 2-hydroxyethyl methacrylate, 2-aminoethyl methacrylate, glycidyl methacrylate, tetrahydrofurfuryl methacrylate and the like. These may be used alone or in combination of two or more. Among these, the monomers constituting the block segment A are methyl methacrylate, ethyl methacrylate, tert-butyl methacrylate and methacrylic acid from the viewpoint of improving the transparency, heat resistance and durability of the obtained pressure-sensitive adhesive layer. Cyclohexyl acetate, isobornyl methacrylate, phenyl methacrylate are more preferred, and methyl methacrylate is even more preferred.
上記ブロックセグメントＡは、当該ブロックセグメントＡを構成するモノマー単位として、ホモポリマーとしてのガラス転移温度（Ｔｇ）が１００℃以上であるモノマーを含むことが好ましい。また、当該ガラス転移温度（Ｔｇ）は１５０℃以下であることが好ましい。ブロックセグメントＡが上記のようなモノマーを含むことで、粘着剤層が良好な粘着力を発揮し易くなる。さらに、粘着剤層の耐熱性、耐久性、押出成型の加工適性を最適な範囲に制御することも可能となる。 The block segment A preferably contains a monomer having a glass transition temperature (Tg) of 100 ° C. or higher as a homopolymer as a monomer unit constituting the block segment A. The glass transition temperature (Tg) is preferably 150 ° C. or lower. When the block segment A contains the above-mentioned monomers, the pressure-sensitive adhesive layer tends to exhibit good adhesive strength. Further, it is possible to control the heat resistance, durability, and processability of extrusion molding of the pressure-sensitive adhesive layer within the optimum range.
上記ブロックセグメントＢを構成するモノマーとしては、アクリル酸ｎ−ブチル、アクリル酸イソブチル、アクリル酸ｓｅｃ−ブチル、アクリル酸ｔｅｒｔ−ブチル、アクリル酸アミル、アクリル酸イソアミル、アクリル酸ｎ−ヘキシル、アクリル酸シクロヘキシル、アクリル酸フェニル、アクリル酸メトキシエチル、アクリル酸エトキシエチル、アクリル酸ジエチルアミノエチル、アクリル酸２−ヒドロキシエチル、アクリル酸２−アミノエチル、アクリル酸グリシジル、アクリル酸テトラヒドロフルフリル、アクリル酸２−エチルヘキシル、アクリル酸ｎ−オクチル、アクリル酸イソオクチル、アクリル酸デシル、アクリル酸イソボルニル、アクリル酸ラウリル、アクリル酸ベンジル、アクリル酸フェノキシエチル等が挙げられる。これらは単独で用いてもよく、２種以上を併用してもよい。これらの中でも、上記ブロックセグメントＢを構成するモノマーは、得られる粘着剤組成物の、柔軟性、粘着特性を向上させる観点から、アクリル酸ｎ−ブチル、アクリル酸ｎ−ヘキシルなどのアクリル酸エステルがより好ましく、アクリル酸ｎ−ブチルがさらに好ましい。これらは単独で用いてもよく、２種以上を併用してもよい。 Examples of the monomer constituting the block segment B include n-butyl acrylate, isobutyl acrylate, sec-butyl acrylate, tert-butyl acrylate, amyl acrylate, isoamyl acrylate, n-hexyl acrylate, and cyclohexyl acrylate. , Phenyl acrylate, methoxyethyl acrylate, ethoxyethyl acrylate, diethylaminoethyl acrylate, 2-hydroxyethyl acrylate, 2-aminoethyl acrylate, glycidyl acrylate, tetrahydrofurfuryl acrylate, 2-ethylhexyl acrylate, Examples thereof include n-octyl acrylate, isooctyl acrylate, decyl acrylate, isobornyl acrylate, lauryl acrylate, benzyl acrylate, and phenoxyethyl acrylate. These may be used alone or in combination of two or more. Among these, the monomer constituting the block segment B is an acrylic acid ester such as n-butyl acrylate or n-hexyl acrylate from the viewpoint of improving the flexibility and adhesive properties of the obtained pressure-sensitive adhesive composition. More preferably, n-butyl acrylate is further preferable. These may be used alone or in combination of two or more.
上記ブロックセグメントＢは、当該ブロックセグメントＢを構成するモノマー単位として、ホモポリマーとしてのガラス転移温度（Ｔｇ）が−７０℃以上であるモノマーを含むことが好ましい。また、当該ガラス転移温度（Ｔｇ）は−３０℃以下であることが好ましい。ブロックセグメントＢが上記のようなモノマーを含むことで、粘着剤層の弾性率を良好に低下させることができ、より良好な粘着力が発揮される。 The block segment B preferably contains a monomer having a glass transition temperature (Tg) of −70 ° C. or higher as a homopolymer as a monomer unit constituting the block segment B. The glass transition temperature (Tg) is preferably −30 ° C. or lower. When the block segment B contains the above-mentioned monomers, the elastic modulus of the pressure-sensitive adhesive layer can be satisfactorily lowered, and better adhesive strength is exhibited.
本実施形態に係る表示用ラベルでは、アクリル系モノマーのトリブロック共重合体における各セグメントの質量比（ブロックセグメントＡ／ブロックセグメントＢ）は、粘着力を効果的に向上させる観点から、５／９５（すなわち０．０５）以上であることが好ましく、特に１０／９０（すなわち０．１１）以上であることが好ましく、さらには１５／８５（すなわち０．１８）以上であることが好ましい。７０／３０（すなわち２．３３）以下であることが好ましく、特に５０／５０（すなわち１．００）以下であることが好ましく、さらには３０／７０（すなわち０．４３）以下であることが好ましい。 In the display label according to the present embodiment, the mass ratio of each segment (block segment A / block segment B) in the triblock copolymer of the acrylic monomer is 5/95 from the viewpoint of effectively improving the adhesive strength. It is preferably (that is, 0.05) or more, particularly preferably 10/90 (that is, 0.11) or more, and further preferably 15/85 (that is, 0.18) or more. It is preferably 70/30 (ie, 2.33) or less, particularly preferably 50/50 (ie, 1.00) or less, and further preferably 30/70 (ie, 0.43) or less. ..
アクリル系モノマーのトリブロック共重合体の具体例としては、ポリメタクリル酸メチル（ＰＭＭＡ）−ポリアクリル酸ブチル（ＰＢＡ）−ポリメタクリル酸メチル（ＰＭＭＡ）、ポリメタクリル酸メチル（ＰＭＭＡ）−ポリアクリル酸−２−エチルヘキシル（２ＥＨＡ）−ポリメタクリル酸メチル（ＰＭＭＡ）等が挙げられ、特に、ポリメタクリル酸メチル（ＰＭＭＡ）−ポリアクリル酸ブチル（ＰＢＡ）−ポリメタクリル酸メチル（ＰＭＭＡ）を使用することが好ましい。 Specific examples of the triblock copolymer of the acrylic monomer include polymethylmethacrylate (PMMA) -butylpolyacrylate (PBA) -methylmethylmethacrylate (PMMA) and polymethylmethacrylate (PMMA) -polyacrylic acid. -2-Ethylhexyl (2EHA) -polymethylmethacrylate (PMMA) and the like can be mentioned, and in particular, polymethylmethacrylate (PMMA) -butylpolyacrylate (PBA) -methylmethylmethacrylate (PMMA) can be used. preferable.
（２）粘着付与剤
本実施形態における粘着剤組成物は、粘着付与剤を含有する。これにより、形成される粘着剤層の粘着力が良好に向上し、ポリエチレン樹脂やポリプロピレン樹脂といったオレフィン系樹脂からなる表面に対しても十分な粘着力を発揮できるものとなる。
(2) Adhesive-imparting agent The pressure-sensitive adhesive composition in the present embodiment contains a pressure-sensitive adhesive. As a result, the adhesive strength of the formed pressure-sensitive adhesive layer is satisfactorily improved, and sufficient adhesive strength can be exhibited even on a surface made of an olefin resin such as a polyethylene resin or a polypropylene resin.
上記粘着付与剤は、形成される粘着剤層によって所望の粘着力が発揮されるとともに、粘着剤層からの粘着成分の溶出を極力抑制できるものである限り、特に限定されない。粘着付与剤としては、例えば、ロジン系樹脂、スチレン系樹脂等が挙げられる。ロジン系樹脂の例としては、ロジン樹脂、ロジンエステル樹脂、ロジン変性フェノール樹脂、これらを水素化した樹脂等が挙げられる。スチレン系樹脂の例としては、α−メチルスチレンまたはβ−メチルスチレン等のスチレン系モノマーと脂肪族系モノマーとを共重合して得られる樹脂、これらを水素化した樹脂等が挙げられる。これらは単独で用いてもよく、２種以上を併用してもよい。本実施形態に係る表示用ラベルでは、粘着付与剤として、上記の中でも、得られた粘着剤層が優れた粘着力を発揮し易いという観点から、ロジン系樹脂およびスチレン系樹脂の少なくとも一種を使用することが好ましい。 The pressure-sensitive adhesive is not particularly limited as long as the desired pressure-sensitive adhesive strength is exhibited by the pressure-sensitive adhesive layer formed and the elution of the pressure-sensitive adhesive component from the pressure-sensitive adhesive layer can be suppressed as much as possible. Examples of the tackifier include rosin-based resins and styrene-based resins. Examples of the rosin-based resin include a rosin resin, a rosin ester resin, a rosin-modified phenol resin, and a resin obtained by hydrogenating these. Examples of the styrene-based resin include a resin obtained by copolymerizing a styrene-based monomer such as α-methylstyrene or β-methylstyrene with an aliphatic monomer, and a resin obtained by hydrogenating these. These may be used alone or in combination of two or more. In the display label according to the present embodiment, at least one of a rosin-based resin and a styrene-based resin is used as the pressure-sensitive adhesive from the viewpoint that the obtained pressure-sensitive adhesive layer easily exhibits excellent adhesive strength. It is preferable to do so.
粘着付与剤は、軟化点が、５０℃以上であることが好ましく、特に６０℃以上であることが好ましく、さらには８０℃以上であることが好ましい。また、当該軟化点は、１２０℃以下であることが好ましい。粘着付与剤の軟化点が上記範囲であることで、得られる粘着剤層が良好な粘着力を発揮し易いものとなる。なお、２種以上の粘着付与剤を併用する場合、それらの粘着付与剤の軟化点の加重平均が上記範囲であることが好ましい。また、本明細書において、粘着付与剤の軟化点は、ＪＩＳ Ｋ２２０７に準拠して測定した値を意味する。 The tackifier has a softening point of preferably 50 ° C. or higher, particularly preferably 60 ° C. or higher, and further preferably 80 ° C. or higher. Further, the softening point is preferably 120 ° C. or lower. When the softening point of the tackifier is in the above range, the obtained pressure-sensitive adhesive layer can easily exhibit good adhesive strength. When two or more kinds of tackifiers are used in combination, it is preferable that the weighted average of the softening points of those tackifiers is in the above range. Further, in the present specification, the softening point of the tackifier means a value measured according to JIS K2207.
粘着剤組成物中における粘着付与剤の含有量は、アクリル系共重合体および粘着付与剤の含有量の合計に対して、５質量％以上であることが好ましく、特に１０質量％以上であることが好ましい。また、粘着剤組成物中における粘着付与剤の含有量は、アクリル系共重合体および粘着付与剤の含有量の合計に対して、５０質量％以下であることが好ましく、特に３０質量％以下であることが好ましい。粘着付与剤の含有量が、アクリル系共重合体および粘着付与剤の含有量の合計に対して５質量％以上であることで、得られる粘着剤層がより良好な粘着力を発揮し易いものとなる。また、粘着付与剤の含有量が、アクリル系共重合体および粘着付与剤の含有量の合計に対して５０質量％以下であることで、粘着剤層から粘着付与剤の溶出を効果的に抑制することができる。 The content of the tackifier in the pressure-sensitive adhesive composition is preferably 5% by mass or more, particularly 10% by mass or more, based on the total content of the acrylic copolymer and the pressure-sensitive adhesive. Is preferable. The content of the tackifier in the pressure-sensitive adhesive composition is preferably 50% by mass or less, particularly 30% by mass or less, based on the total content of the acrylic copolymer and the pressure-sensitive adhesive. It is preferable to have. When the content of the tackifier is 5% by mass or more with respect to the total content of the acrylic copolymer and the tackifier, the obtained pressure-sensitive adhesive layer tends to exhibit better adhesive strength. It becomes. Further, when the content of the tackifier is 50% by mass or less with respect to the total content of the acrylic copolymer and the tackifier, the elution of the tackifier from the pressure-sensitive adhesive layer is effectively suppressed. can do.
（３）その他の成分
本実施形態における粘着剤組成物における、アクリル系共重合体および粘着付与剤以外の成分については、形成される粘着剤層によって所望の粘着力が発揮される限り、特に限定されない。
(3) Other Components In the pressure-sensitive adhesive composition of the present embodiment, components other than the acrylic copolymer and the pressure-sensitive adhesive are particularly limited as long as the desired pressure-sensitive adhesive strength is exhibited by the formed pressure-sensitive adhesive layer. Not done.
粘着剤組成物は、着色材料（カーボンブラック、二酸化チタンなどの顔料、および染料が例示される。）を含有してもよい。この場合、得られる粘着剤層を所望の色に着色することができる。また、粘着剤組成物は、用途に応じて、充填剤、酸化防止剤、紫外線吸収剤などの成分をさらに含有していてもよい。 The pressure-sensitive adhesive composition may contain a coloring material (for example, pigments such as carbon black and titanium dioxide, and dyes). In this case, the resulting pressure-sensitive adhesive layer can be colored to a desired color. In addition, the pressure-sensitive adhesive composition may further contain components such as a filler, an antioxidant, and an ultraviolet absorber, depending on the intended use.
また、本発明の効果を損なわない範囲内で、粘着剤層を形成するための粘着剤組成物に、非架橋型樹脂、架橋型樹脂、カップリング剤、充填剤、軟化剤、可塑剤、界面活性剤、酸化防止剤、熱安定剤、光安定剤、紫外線吸収剤、着色剤、消泡剤、難燃剤又は帯電防止剤などの添加剤が添加されてもよい。但し、粘着剤層から被着体への低分子量成分の溶出を抑制する観点から、低分子量の添加剤の添加量を必要最小限とするか、低分子量の添加剤を使用しないことが好ましい。 Further, in the pressure-sensitive adhesive composition for forming the pressure-sensitive adhesive layer within the range not impairing the effect of the present invention, a non-crosslinked resin, a crosslinked resin, a coupling agent, a filler, a softener, a plasticizer, and a surfactant are used. Additives such as activators, antioxidants, heat stabilizers, light stabilizers, UV absorbers, colorants, antifoaming agents, flame retardants or antistatic agents may be added. However, from the viewpoint of suppressing the elution of the low molecular weight component from the pressure-sensitive adhesive layer to the adherend, it is preferable to minimize the amount of the low molecular weight additive added or not to use the low molecular weight additive.
非架橋型樹脂は、粘度調整や自着防止に有効である。非架橋型樹脂は、押出機のホッパー内の温度領域において粉体となりうるものであることが好ましい。また、粘着剤組成物中のその他の成分との間で相溶性を有する事が好ましい。添加樹脂がそのような相溶性を有することをより安定的に実現する観点から、添加樹脂は、粘着剤組成物中のその他の成分と同系列の樹脂であることがより好ましい。すなわち、添加樹脂は、アクリル系共重合体と同様に、アクリル酸系樹脂であることが好ましい。粘着剤層における添加樹脂の含有量は、粘着剤組成物の粘度を調整する機能を果たすことができる限り、限定されない。粘着剤層の添加樹脂の含有量については、０．０１質量％超、１０質量％未満であることが好ましく、０．１質量％以上、５質量％以下であることがより好ましく、０．５質量％以上、３質量％以下であることが特に好ましい。 The non-crosslinked resin is effective for adjusting the viscosity and preventing self-adhesion. The non-crosslinked resin is preferably one that can become a powder in the temperature range in the hopper of the extruder. Further, it is preferable that the pressure-sensitive adhesive composition has compatibility with other components. From the viewpoint of more stably realizing that the added resin has such compatibility, it is more preferable that the added resin is a resin in the same series as the other components in the pressure-sensitive adhesive composition. That is, the additive resin is preferably an acrylic acid-based resin, like the acrylic copolymer. The content of the additive resin in the pressure-sensitive adhesive layer is not limited as long as it can function to adjust the viscosity of the pressure-sensitive adhesive composition. The content of the added resin in the pressure-sensitive adhesive layer is preferably more than 0.01% by mass and less than 10% by mass, more preferably 0.1% by mass or more and 5% by mass or less, and more preferably 0.5. It is particularly preferable that it is mass% or more and 3 mass% or less.
（４）粘着剤層の厚さ
粘着剤層の厚さは、１μｍ以上であることが好ましく、２μｍ以上であることがより好ましく、特に５μｍ以上であることが好ましく、さらには１０μｍ以上であることが好ましい。また、当該厚さは、１０００μｍ以下であることが好ましく、５００μｍ以下であることがより好ましく、特に１００μｍ以下であることが好ましく、さらには５０μｍ以下であることが好ましい。当該厚さが１μｍ以上であることで、表示用ラベルの被着体に対する粘着力が効果的に向上する。また、当該厚さが１０００μｍ以下であることで、粘着剤層から被着体への粘着成分の溶出を効果的に抑制することが可能となる。
(4) Thickness of Adhesive Layer The thickness of the adhesive layer is preferably 1 μm or more, more preferably 2 μm or more, particularly preferably 5 μm or more, and further preferably 10 μm or more. Is preferable. The thickness is preferably 1000 μm or less, more preferably 500 μm or less, particularly preferably 100 μm or less, and further preferably 50 μm or less. When the thickness is 1 μm or more, the adhesive strength of the display label to the adherend is effectively improved. Further, when the thickness is 1000 μm or less, it is possible to effectively suppress the elution of the adhesive component from the adhesive layer to the adherend.
３．剥離ライナー
本実施形態に係る表示用ラベルでは、粘着剤層における基材とは反対側の面を保護する目的で、当該面に剥離ライナーが貼付されていてもよい。
3. 3. Release liner In the display label according to the present embodiment, a release liner may be attached to the surface of the pressure-sensitive adhesive layer opposite to the base material for the purpose of protecting the surface.
剥離ライナーとしては、例えば、ポリエチレンフィルム、ポリプロピレンフィルム、ポリエチレンテレフタレートフィルムなどのフィルムや、グラシン紙や上質紙などの紙を用いることができる。また、これらのフィルムの複数が積層された積層フィルムであってもよい。 As the release liner, for example, a film such as a polyethylene film, a polypropylene film, or a polyethylene terephthalate film, or a paper such as glassin paper or woodfree paper can be used. Further, it may be a laminated film in which a plurality of these films are laminated.
上記剥離ライナーにおける粘着剤層と接する面（以下、「剥離面」という場合がある。）には、剥離処理が施されていることが好ましい。剥離処理に使用される剥離剤としては、例えば、アルキッド系、シリコーン系、フッ素系、不飽和ポリエステル系、ポリオレフィン系、ワックス系の剥離剤が挙げられる。 It is preferable that the surface of the release liner in contact with the pressure-sensitive adhesive layer (hereinafter, may be referred to as "release surface") is subjected to a release treatment. Examples of the release agent used in the release treatment include alkyd-based, silicone-based, fluorine-based, unsaturated polyester-based, polyolefin-based, and wax-based release agents.
剥離ライナーの厚さについては特に限定されず、通常、２０μｍ以上、１５０μｍ以下である。 The thickness of the release liner is not particularly limited, and is usually 20 μm or more and 150 μm or less.
剥離ライナーは、押出成形など成形加工により製造されたものであってもよい。この場合において、剥離ライナーは粘着剤層と共押出成形により形成されてもよい。 The release liner may be manufactured by a molding process such as extrusion molding. In this case, the release liner may be formed by coextrusion molding with the pressure-sensitive adhesive layer.
４．物性等
本実施形態に係る表示用ラベルでは、表示用ラベルを約５ｃｍ×約０．５ｃｍの大きさに裁断して得られた試験片と超純水２００ｍＬとを含む密閉容器を、高圧蒸気滅菌器を用いて７０℃で２４時間加熱し、続いて室温になるまで放置した後、密閉容器中の超純水の紫外吸収スペクトルを測定した場合に、２２０〜２４０ｎｍの波長域の最大吸光度が、０．０８以下であることが好ましく、２４１〜３５０ｎｍの波長域の最大吸光度が、０．０５以下であることが好ましい。本実施形態に係る表示用ラベルでは、前述した通り粘着成分の溶出が生じ難いため、上述の紫外吸収スペクトルを測定した場合には、２２０〜２４０ｎｍの波長域および２４１〜３５０ｎｍの波長域の最大吸光度が、それぞれ上述した範囲を満たし易いものとなる。なお、上述した最大吸光度の詳細な測定方法は、後述する試験例に記載の通りである。
4. Physical properties, etc. In the display label according to the present embodiment, a closed container containing a test piece obtained by cutting the display label into a size of about 5 cm × about 0.5 cm and 200 mL of ultrapure water is sterilized by high pressure steam. When the ultraviolet absorption spectrum of ultrapure water in a closed container was measured after heating at 70 ° C. for 24 hours using a vessel and then allowing it to reach room temperature, the maximum absorbance in the wavelength range of 220 to 240 nm was determined. It is preferably 0.08 or less, and the maximum absorbance in the wavelength range of 241 to 350 nm is preferably 0.05 or less. In the display label according to the present embodiment, as described above, elution of the adhesive component is unlikely to occur. Therefore, when the above-mentioned ultraviolet absorption spectrum is measured, the maximum absorbance in the wavelength range of 220 to 240 nm and the wavelength range of 2413 to 550 nm. However, each of them easily satisfies the above-mentioned range. The detailed measurement method of the maximum absorbance described above is as described in the test example described later.
本実施形態に係る表示用ラベルでは、ＪＩＳ Ｚ０２３７：２００９（ＩＳＯ ２９８６２：２００７）に準拠して測定されたポリプロピレン板に対する１８０°引きはがし粘着力が、１．０Ｎ／２５ｍｍ以上であることが好ましく、特に５Ｎ／２５ｍｍ以上であることが好ましく、さらには８Ｎ／２５ｍｍ以上であることが好ましい。本実施形態に係る表示用ラベルでは、粘着剤層が、アクリル系共重合体と粘着付与剤とを含有する粘着剤組成物から形成されていることにより、従来の粘着剤層では粘着力を発揮し難いポリプロピレン板に対しても上記のように十分に高い粘着力を達成することができ、その結果、本実施形態に係る表示用ラベルは、被着体からの剥がれや脱落が生じ難い。なお、粘着力の上限については特に限定されず、例えば、３０Ｎ／２５ｍｍ以下であってよく、特に２０Ｎ／２５ｍｍ以下であってよい。また、上記粘着力の測定方法は、後述する試験例に示す通りである。 In the display label according to the present embodiment, the 180 ° peeling adhesive strength to the polypropylene plate measured in accordance with JIS Z0237: 2009 (ISO 29862: 2007) is preferably 1.0 N / 25 mm or more. In particular, it is preferably 5N / 25mm or more, and more preferably 8N / 25mm or more. In the display label according to the present embodiment, the pressure-sensitive adhesive layer is formed of a pressure-sensitive adhesive composition containing an acrylic copolymer and a pressure-sensitive adhesive, so that the conventional pressure-sensitive adhesive layer exhibits adhesive strength. As described above, it is possible to achieve a sufficiently high adhesive strength even with respect to a polypropylene plate which is difficult to carry out, and as a result, the display label according to the present embodiment is unlikely to be peeled off or fall off from the adherend. The upper limit of the adhesive force is not particularly limited, and may be, for example, 30 N / 25 mm or less, and particularly 20 N / 25 mm or less. The method for measuring the adhesive strength is as shown in a test example described later.
本実施形態に係る表示用ラベルでは、ＪＩＳ Ｚ０２３７：２００９に準拠して測定された、傾斜角３０°におけるボールタックが１０以上であることが好ましい。上記のボールタックが１０以上であることにより、表示用ラベルの粘着剤層の面のべたつきがより適切となって、かかる表示用ラベルの被着体への貼付性が向上する。表示用ラベルの被着体に対する貼付性を適切に確保することをより安定的に実現する観点から、上記のボールタックは、１２以上であることがより好ましく、１５以上であることがさらに好ましい。 In the display label according to the present embodiment, it is preferable that the ball tack at an inclination angle of 30 °, measured in accordance with JIS Z0237: 2009, is 10 or more. When the ball tack is 10 or more, the stickiness of the surface of the pressure-sensitive adhesive layer of the display label becomes more appropriate, and the stickability of the display label to the adherend is improved. From the viewpoint of more stably realizing the stickability of the display label to the adherend, the ball tack is more preferably 12 or more, and further preferably 15 or more.
本実施形態に係る表示用ラベルでは、ＪＩＳ Ｚ０２３７：２００９（ＩＳＯ２９８６３：２００７）に準拠して行われた、試験片の貼り付け面積２５ｍｍ×２５ｍｍ、おもりの質量１０００ｇ、温度４０℃の保持力試験において、表示用ラベルが剥がれ落ちるまでの時間が１時間以上であることが好ましい。かかる保持時間が１時間以上であることにより、表示用ラベルを被着体に貼付したときに、粘着剤層の構成成分が染み出す問題が生じにくく、表示用ラベルの被着体に対して適切な貼付性を有しやすい。 In the display label according to this embodiment, in a holding force test of a test piece having an area of 25 mm × 25 mm, a weight of 1000 g, and a temperature of 40 ° C., which was carried out in accordance with JIS Z0237: 2009 (ISO29863: 2007). It is preferable that the time until the display label is peeled off is 1 hour or more. When the holding time is 1 hour or more, when the display label is attached to the adherend, the problem that the constituent components of the adhesive layer exude is less likely to occur, which is appropriate for the adherend of the display label. Easy to have good stickability.
５．表示用ラベルの製造方法
本実施形態に係る表示用ラベルの製造方法は特に限定されない。例えば、次のような、粘着剤組成物の塗布により粘着剤層を形成する工程を備える製造方法により製造することができる。すなわち、粘着剤層の材料を含む粘着剤組成物、および所望によりさらに溶媒または分散媒を含有する粘着剤組成物の塗布液を調製する。この塗布液を、剥離ライナーの剥離面上に、ダイコーター、カーテンコーター、スリットコーター、ナイフコーター等により塗布して塗膜を形成する。さらに、当該塗膜を乾燥させることにより、粘着剤層を形成する。その後、剥離ライナー上の粘着剤層と基材とを貼合することで粘着シートを作製し、さらに、必要に応じて、当該粘着シートの基材に対する印刷、当該粘着シートの裁断等を行うことで、表示用ラベルを得ることができる。粘着剤組成物の塗布液は、塗布を行うことが可能であればその性状は特に限定されない。粘着剤層を形成するための成分は、粘着剤組成物の塗布液中に溶質として含有されてもよく、または分散質として含有されてもよい。
5. Manufacturing method of display label The manufacturing method of the display label according to the present embodiment is not particularly limited. For example, it can be produced by the following manufacturing method including a step of forming a pressure-sensitive adhesive layer by applying the pressure-sensitive adhesive composition. That is, a pressure-sensitive adhesive composition containing the material of the pressure-sensitive adhesive layer and, if desired, a coating liquid of the pressure-sensitive adhesive composition further containing a solvent or a dispersion medium are prepared. This coating liquid is applied onto the peeling surface of the release liner with a die coater, a curtain coater, a slit coater, a knife coater, or the like to form a coating film. Further, the pressure-sensitive adhesive layer is formed by drying the coating film. After that, the pressure-sensitive adhesive layer on the release liner is bonded to the base material to prepare a pressure-sensitive adhesive sheet, and if necessary, printing on the base material of the pressure-sensitive adhesive sheet, cutting of the pressure-sensitive adhesive sheet, and the like are performed. You can get a label for display. The properties of the coating liquid of the pressure-sensitive adhesive composition are not particularly limited as long as it can be applied. The component for forming the pressure-sensitive adhesive layer may be contained as a solute or as a dispersoid in the coating liquid of the pressure-sensitive adhesive composition.
本実施形態における粘着剤層が、アクリル系モノマーのトリブロック共重合体を含有する粘着剤組成物から形成されている場合には、当該粘着剤組成物の押出成形により粘着剤層を形成してもよい。この場合、当該粘着剤組成物の押出成形により、基材の片面側と前述した剥離ライナーの剥離面との間に粘着剤層を設けることが好ましい。アクリル系モノマーのトリブロック共重合体を含有する粘着剤組成物は、一般的に、押出成形によって粘着剤層を形成するのに適している。また、押出成形は、粘着剤組成物を希釈するための溶剤を使用することなく行うことができるため、残溶剤に起因した、粘着剤層から被着体への低分子量成分の溶出を低減することが可能となる。 When the pressure-sensitive adhesive layer in the present embodiment is formed from a pressure-sensitive adhesive composition containing a triblock copolymer of an acrylic monomer, the pressure-sensitive adhesive layer is formed by extrusion molding of the pressure-sensitive adhesive composition. May be good. In this case, it is preferable to provide an adhesive layer between one side of the base material and the release surface of the release liner described above by extrusion molding of the pressure-sensitive adhesive composition. A pressure-sensitive adhesive composition containing a triblock copolymer of an acrylic monomer is generally suitable for forming a pressure-sensitive adhesive layer by extrusion molding. Further, since extrusion molding can be performed without using a solvent for diluting the pressure-sensitive adhesive composition, elution of low molecular weight components from the pressure-sensitive adhesive layer to the adherend due to the residual solvent is reduced. It becomes possible.
押出成形により粘着剤層を設ける具体的な方法は、基材と剥離ライナーとの間に粘着剤層を形成できる限り、特に限定されない。例えば、Ｔダイ製膜機等を使用して、前述した粘着剤組成物を溶融・混練し、剥離ライナーおよび基材を一定の速度にて移動させながら、基材の片面側と剥離ライナーの剥離面との間に、溶融した粘着剤組成物を押出しラミネートすることで、基材と粘着剤層と剥離ライナーとが順に積層された粘着シートを作製する。あるいは、Ｔダイ製膜機等を使用して、前述した粘着剤組成物および基材の材料をそれぞれ溶融・混練し、剥離ライナーを一定の速度にて移動させながら、剥離ライナーの剥離面に、溶融した粘着剤組成物および基材の材料を共押出しラミネートすることで、基材と粘着剤層と剥離ライナーとが順に積層された粘着シートを作製する。そして、作製された粘着シートにおいて、必要に応じて、当該粘着シートの基材に対する印刷、当該粘着シートのハーフカットや裁断等を行うことで、表示用ラベルを得ることができる。 The specific method for providing the pressure-sensitive adhesive layer by extrusion molding is not particularly limited as long as the pressure-sensitive adhesive layer can be formed between the base material and the release liner. For example, using a T-die film forming machine or the like, the above-mentioned pressure-sensitive adhesive composition is melted and kneaded, and the release liner and the base material are moved at a constant speed to separate one side of the base material from the release liner. By extruding and laminating the molten pressure-sensitive adhesive composition between the surfaces, a pressure-sensitive adhesive sheet in which the base material, the pressure-sensitive adhesive layer, and the release liner are laminated in this order is produced. Alternatively, using a T-die film forming machine or the like, the above-mentioned pressure-sensitive adhesive composition and the material of the base material are melted and kneaded, respectively, and the release liner is moved at a constant speed to the release surface of the release liner. By co-extruding and laminating the melted pressure-sensitive adhesive composition and the material of the base material, a pressure-sensitive adhesive sheet in which the base material, the pressure-sensitive adhesive layer, and the release liner are laminated in order is produced. Then, in the produced pressure-sensitive adhesive sheet, a label for display can be obtained by printing on the base material of the pressure-sensitive adhesive sheet, half-cutting or cutting the pressure-sensitive adhesive sheet, or the like, if necessary.
以上のように、粘着剤層を押出成形により設ける場合、粘着剤組成物に含有されるアクリル系ポリマーのトリブロック共重合体は、押出形成を行い易いという観点から、分子量分布（Ｍｗ／Ｍｎ）が３．０以下であることに加えて、重量平均分子量（Ｍｗ）が３０，０００以上、３００，０００以下であることも満たすことが好ましい。 As described above, when the pressure-sensitive adhesive layer is provided by extrusion molding, the triblock copolymer of the acrylic polymer contained in the pressure-sensitive adhesive composition has a molecular weight distribution (Mw / Mn) from the viewpoint of easy extrusion formation. Is 3.0 or less, and it is also preferable that the weight average molecular weight (Mw) is 30,000 or more and 300,000 or less.
６．表示用ラベルの使用方法
本実施形態に係る表示用ラベルは、種々の用途に使用することができるものの、特に、医療用製品に使用することが好ましい。本実施形態に係る表示用ラベルは、分子量分布（Ｍｗ／Ｍｎ）が３．０以下であるアクリル系共重合体を含有する粘着剤組成物により粘着剤層が形成されていることにより、粘着剤層から被着体への粘着成分の溶出が生じ難い。そのため、本実施形態に係る表示用ラベルは、そのような粘着成分による汚染を避けることが強く求められる医療用製品への使用に好適である。
6. How to use the display label Although the display label according to the present embodiment can be used for various purposes, it is particularly preferable to use it for medical products. The label for display according to the present embodiment is a pressure-sensitive adhesive because the pressure-sensitive adhesive layer is formed by a pressure-sensitive adhesive composition containing an acrylic copolymer having a molecular weight distribution (Mw / Mn) of 3.0 or less. Elution of adhesive components from the layer to the adherend is unlikely to occur. Therefore, the labeling label according to the present embodiment is suitable for use in medical products for which it is strongly required to avoid contamination by such adhesive components.
ここで、医療用製品とは、医療の目的のために使用されるものであれば特に限定されず、医療用器具や医薬品が収容される医薬品容器等を含むものとする。医療用器具の具体的な例としては、シリンジ、チューブ等が挙げられる。また、医薬品が収容される医薬品容器の具体的な例としては、目薬用容器、点鼻薬用容器、生理食塩水等の容器としてのバッグ等が挙げられる。医療用製品における表示用ラベルが貼付される部分の材料としては、樹脂、ガラス、金属、紙等であってよく、特に樹脂であることが好ましい。樹脂材料の例としては、ポリエチレン、ポリプロピレン等のオレフィン系樹脂、ポリエチレンテレフタラート、ポリブチレンテレフタラート等のエステル系樹脂等が挙げられ、これらの中でも、本実施形態に係る表示用ラベルの被着体の材料としては、オレフィン系樹脂が好適である。本実施形態に係る表示用ラベルは、優れた粘着力を発揮することができるため、オレフィン系樹脂といった、通常の粘着剤が十分な粘着力を発揮し難い樹脂を材料とする被着体であっても、優れた粘着力を発揮することができる。 Here, the medical product is not particularly limited as long as it is used for medical purposes, and includes a medical device, a drug container in which a drug is stored, and the like. Specific examples of medical instruments include syringes, tubes and the like. Further, specific examples of the drug container in which the drug is stored include an eye medicine container, a nasal spray container, a bag as a container for physiological saline and the like. The material of the portion to which the display label is attached in the medical product may be resin, glass, metal, paper or the like, and resin is particularly preferable. Examples of the resin material include olefin resins such as polyethylene and polypropylene, ester resins such as polyethylene terephthalate and polybutylene terephthalate, and among these, the adherend of the display label according to the present embodiment. As the material of, an olefin resin is suitable. Since the display label according to the present embodiment can exhibit excellent adhesive strength, it is an adherend made of a resin such as an olefin resin, which is difficult for ordinary adhesives to exert sufficient adhesive strength. However, it can exhibit excellent adhesive strength.
以上説明した実施形態は、本発明の理解を容易にするために記載されたものであって、本発明を限定するために記載されたものではない。したがって、上記実施形態に開示された各要素は、本発明の技術的範囲に属する全ての設計変更や均等物をも含む趣旨である。 The embodiments described above are described for facilitating the understanding of the present invention, and are not described for limiting the present invention. Therefore, each element disclosed in the above embodiment is intended to include all design changes and equivalents belonging to the technical scope of the present invention.
例えば、基材と粘着剤層との間には、他の層が介在していてもよい。 For example, another layer may be interposed between the base material and the pressure-sensitive adhesive layer.
以下、実施例等により本発明をさらに具体的に説明するが、本発明の範囲はこれらの実施例等に限定されるものではない。 Hereinafter, the present invention will be described in more detail with reference to Examples and the like, but the scope of the present invention is not limited to these Examples and the like.
〔実施例１〕
アクリル系モノマーのトリブロック共重合体として、ポリメタクリル酸メチル（ＰＭＭＡ）−ポリアクリル酸ブチル（ＰＢＡ）−ＰＭＭＡを作製した。ＰＭＭＡ比率は、２７ｍｏｌ％であり、重量平均分子量（Ｍｗ）を後述する方法にて測定したところ、１２７，０００であり、分子量分布（Ｍｗ／Ｍｎ）を、後述する方法にて測定した重量平均分子量（Ｍｗ）および数平均分子量（Ｍｎ）から算出したところ、１．３であった。
[Example 1]
Polymethylmethylmethacrylate (PMMA) -butyl polyacrylate (PBA) -PMMA was prepared as a triblock copolymer of an acrylic monomer. The PMMA ratio was 27 mol%, and when the weight average molecular weight (Mw) was measured by the method described later, it was 127,000, and the molecular weight distribution (Mw / Mn) was measured by the method described later. It was 1.3 when calculated from (Mw) and the number average molecular weight (Mn).
得られたアクリル系モノマーのトリブロック共重合体９０質量部（固形分換算値；以下同様に表記）と、粘着付与剤としての水素化ロジンエステル樹脂（荒川化学工業社製，「パインクリスタルＫＥ−３１１」，軟化点：９５℃）１０質量部とを酢酸エチル中にて混合し、固形分濃度が３０質量％である粘着剤組成物の塗布液を調製した。 90 parts by mass of the triblock copolymer of the obtained acrylic monomer (solid content conversion value; the same applies hereinafter) and rosin hydride ester resin as a tackifier (manufactured by Arakawa Chemical Industry Co., Ltd., "Pine Crystal KE-" 311 ”, softening point: 95 ° C.) and 10 parts by mass were mixed in ethyl acetate to prepare a coating solution of a pressure-sensitive adhesive composition having a solid content concentration of 30% by mass.
得られた粘着剤組成物の塗布液を、厚さ３８μｍのポリエチレンテレフタレートフィルムの片面にシリコーン系の剥離剤層が形成されてなる剥離ライナーの剥離面に、ロールナイフコーターを用いて塗布し、得られた塗膜を１２０℃で１分間乾燥させて、厚さ３０μｍの粘着剤層を形成した。 The coating liquid of the obtained pressure-sensitive adhesive composition is applied to the peeling surface of the peeling liner in which a silicone-based release agent layer is formed on one side of a polyethylene terephthalate film having a thickness of 38 μm using a roll knife coater. The coating film was dried at 120 ° C. for 1 minute to form a pressure-sensitive adhesive layer having a thickness of 30 μm.
上記のように得られた剥離ライナーと粘着剤層との積層体における粘着剤層側の面と、基材としてのポリエチレンテレフタレートフィルム（厚さ５０μｍ）の片面とを貼り合わせて、基材と粘着剤層と剥離ライナーとがこの順に積層されてなる粘着シートを得た。なお、当該粘着シートは、基材への印刷、ハーフカットや裁断等を適宜行うことで、表示用ラベルとすることができる。 The surface of the laminate of the release liner and the pressure-sensitive adhesive layer obtained as described above on the pressure-sensitive adhesive layer side and one side of a polyethylene terephthalate film (thickness 50 μm) as a base material are bonded to each other to adhere to the base material. An adhesive sheet obtained by laminating the agent layer and the release liner in this order was obtained. The adhesive sheet can be used as a display label by appropriately printing on a base material, half-cutting, cutting, or the like.
なお、上述した重量平均分子量（Ｍｗ）および数平均分子量（Ｍｎ）の値は、ＧＰＣ測定装置（東ソー社製「ＨＬＣ−８２２０ＧＰＣ」）を使用して、以下に示す条件により、テトラヒドロフラン（ＴＨＦ）を溶媒とするゲル・パーミエーションクロマトグラフィー（ＧＰＣ）によって、標準ポリスチレン換算値として測定したものである。
カラム：ＴＳＫｇｅｌＧＭＨＸＬ→ＴＳＫｇｅｌＧＭＨＸＬ→ＴＳＫｇｅｌ２０００ＨＸＬ
注入量：８０μｌ
測定温度：４０℃
流速：１ｍｌ／分
検出器：示差屈折計
試料濃度：１％（ｗ／ｖ）
The above-mentioned weight average molecular weight (Mw) and number average molecular weight (Mn) values are obtained by using a GPC measuring device (“HLC-8220 GPC” manufactured by Toso Co., Ltd.) and using tetrahydrofuran (THF) under the following conditions. It was measured as a standard polystyrene conversion value by gel permeation chromatography (GPC) using a solvent.
Column: TSKgelGMHXL → TSKgelGMHXL → TSKgel2000HXL
Injection volume: 80 μl
Measurement temperature: 40 ° C
Flow velocity: 1 ml / min Detector: Differential refractometer Sample concentration: 1% (w / v)
〔実施例２および３〕
アクリル系共重合体の配合量および粘着付与剤の配合量を表１に示すように変更した以外は、実施例１と同様にして粘着シートを得た。
[Examples 2 and 3]
A pressure-sensitive adhesive sheet was obtained in the same manner as in Example 1 except that the blending amount of the acrylic copolymer and the blending amount of the tackifier were changed as shown in Table 1.
〔比較例１〕
粘着付与剤を使用しないこと以外は、実施例１と同様にして粘着シートを得た。
[Comparative Example 1]
A pressure-sensitive adhesive sheet was obtained in the same manner as in Example 1 except that no pressure-sensitive adhesive was used.
〔比較例２〕
アクリル酸ブチル９７質量部、アクリル酸３質量部、トルエン７５質量部、酢酸エチル７５質量部を仕込み、アゾビスイソブチロニトリル０．３質量部を加え、窒素ガス雰囲気下で８０℃にて８時間重合を行うことで、アクリル系共重合体を得た。当該アクリル系共重合体の重量平均分子量を前述した方法にて測定したところ、７８０，０００であり、分子量分布（Ｍｗ／Ｍｎ）を、前述した方法にて測定した重量平均分子量（Ｍｗ）および数平均分子量（Ｍｎ）から算出したところ、３．５であった。
[Comparative Example 2]
97 parts by mass of butyl acrylate, 3 parts by mass of acrylic acid, 75 parts by mass of toluene and 75 parts by mass of ethyl acetate were charged, 0.3 parts by mass of azobisisobutyronitrile was added, and 8 at 80 ° C. under a nitrogen gas atmosphere. Acrylic copolymer was obtained by time polymerization. The weight average molecular weight of the acrylic copolymer was measured by the method described above and found to be 780,000. The molecular weight distribution (Mw / Mn) was measured by the method described above and the weight average molecular weight (Mw) and the number. When calculated from the average molecular weight (Mn), it was 3.5.
上記の通り得たアクリル系共重合体１００質量部に対して、イソシアネート系架橋剤（東ソー社製，製品名「コロネートＬ」）１．５質量部を使用するとともに、粘着付与剤を使用しないこと以外は、実施例１と同様にして粘着シートを得た。 For 100 parts by mass of the acrylic copolymer obtained as described above, 1.5 parts by mass of an isocyanate-based cross-linking agent (manufactured by Tosoh Corporation, product name "Coronate L") should be used, and no tackifier should be used. An adhesive sheet was obtained in the same manner as in Example 1 except for the above.
〔比較例３〕
比較例２と同様に作製したアクリル系共重合体８０質量部に対して、イソシアネート系架橋剤（東ソー社製，製品名「コロネートＬ」）１．２質量部を使用するとともに、粘着付与剤２０質量部を使用したこと以外は、実施例１と同様にして粘着シートを得た。
[Comparative Example 3]
To 80 parts by mass of the acrylic copolymer produced in the same manner as in Comparative Example 2, 1.2 parts by mass of an isocyanate-based cross-linking agent (manufactured by Tosoh Corporation, product name "Coronate L") was used, and the tackifier 20 was used. An adhesive sheet was obtained in the same manner as in Example 1 except that parts by mass were used.
〔試験例１〕（粘着力の測定）
実施例および比較例にて作製した粘着シートを２５ｍｍ×１５０ｍｍに裁断した後、剥離ライナーを剥離して粘着シート試験片を得た。ＪＩＳ Ｚ ０２３７：２００９（ＩＳＯ ２９８６２：２００７）に基づき、２３℃、相対湿度５０％環境下で、上記の粘着シート試験片をポリプロピレン板に貼付して試験サンプルとした。貼付２４時間後の粘着力（単位：Ｎ／２５ｍｍ）を、１８０°引きはがし法によって引張り速度３００ｍｍ／分にて測定した。結果を表１に示す。
[Test Example 1] (Measurement of adhesive strength)
The pressure-sensitive adhesive sheets produced in Examples and Comparative Examples were cut into 25 mm × 150 mm, and then the release liner was peeled off to obtain a pressure-sensitive adhesive sheet test piece. Based on JIS Z 0237: 2009 (ISO 29862: 2007), the above pressure-sensitive adhesive sheet test piece was attached to a polypropylene plate in an environment of 23 ° C. and a relative humidity of 50% to prepare a test sample. The adhesive strength (unit: N / 25 mm) 24 hours after application was measured by a 180 ° peeling method at a tensile speed of 300 mm / min. The results are shown in Table 1.
〔試験例２〕（粘着成分の溶出量の測定）
実施例および比較例にて作製した粘着シートを、約５ｃｍ×約０．５ｃｍの大きさに裁断して、試験片を得た。当該試験片を超純水で洗浄した後、室温で乾燥した。乾燥後の試験片を硬質ガラス製容器に入れ、超純水２００ｍＬを加え、密栓した。そして、試験片および超純水が入った硬質ガラス製容器を、高圧蒸気滅菌器を用いて７０℃で２４時間加熱した後、室温になるまで放置した。放置後の容器内の液を試験液とした。
[Test Example 2] (Measurement of elution amount of adhesive component)
The pressure-sensitive adhesive sheets prepared in Examples and Comparative Examples were cut into a size of about 5 cm × about 0.5 cm to obtain test pieces. The test piece was washed with ultrapure water and then dried at room temperature. The dried test piece was placed in a hard glass container, 200 mL of ultrapure water was added, and the mixture was sealed. Then, the hard glass container containing the test piece and ultrapure water was heated at 70 ° C. for 24 hours using a high-pressure steam sterilizer, and then left to stand until it reached room temperature. The liquid in the container after being left to stand was used as the test liquid.
一方、超純水のみを入れた硬質ガラス製容器についても、高圧蒸気滅菌器を用いて７０℃で２４時間加熱した後、室温になるまで放置した。放置後の容器内の液を対照液とした。 On the other hand, the hard glass container containing only ultrapure water was also heated at 70 ° C. for 24 hours using a high-pressure steam sterilizer and then left to stand until it reached room temperature. The liquid in the container after being left to stand was used as a control liquid.
上記の通り得た試験液および対照液について、第一六改正日本薬局方 ７．０２ プラスチック製医薬品容器試験法 １．２ 溶出物試験の「（ｉｖ）紫外吸収スペクトル」に記載の試験方法に基づいて、紫外吸収スペクトルを測定し、上記対照液による測定値に基づいてバックグラウンド補正を行うことで、２２０〜２４０ｎｍの波長域および２４１〜３５０ｎｍの波長域の最大吸光度をそれぞれ測定した。これらの結果を表１に示す。なお、ここにおいて、最大吸光度の値が高いほど、表示用ラベルから試験液中に溶出した成分の量が多いことを意味する。 The test solution and control solution obtained as described above are based on the test method described in "(iv) Ultraviolet absorption spectrum" of the Japanese Pharmacopoeia 7.02 Plastic Pharmaceutical Container Test Method 1.2 Eluent Test. Then, the ultraviolet absorption spectrum was measured, and background correction was performed based on the values measured by the control solution to measure the maximum absorbances in the wavelength range of 220 to 240 nm and the wavelength range of 2413 to 550 nm, respectively. These results are shown in Table 1. Here, the higher the value of the maximum absorbance, the larger the amount of the component eluted from the display label into the test solution.
なお、表１に記載の略号等の詳細は以下の通りである。
［アクリル系共重合体］
ＰＭＭＡ−ＰＢＡ−ＰＭＭＡ：ポリメタクリル酸メチル−ポリアクリル酸ブチル−ポリメタクリル酸メチルの構成を有する、アクリル系モノマーのトリブロック共重合体
ＢＡ：アクリル酸ブチル
ＡＡ：アクリル酸
［粘着付与剤］
ロジン系：水素化ロジンエステル樹脂（荒川化学工業社製，「パインクリスタルＫＥ−３１１」，軟化点：９５℃）
［イソシアネート系架橋剤］
イソシアネート系架橋剤：イソシアネート系架橋剤（東ソー社製，製品名「コロネートＬ」）
Details of the abbreviations and the like shown in Table 1 are as follows.
[Acrylic copolymer]
PMMA-PBA-PMMA: Triblock copolymer of acrylic monomer having the composition of polymethylmethacrylate-butylpolyacrylate-polymethylmethacrylate BA: butyl acrylate AA: acrylate [adhesive-imparting agent]
Rosin type: Hydrogenated rosin ester resin (manufactured by Arakawa Chemical Industry Co., Ltd., "Pine Crystal KE-311", softening point: 95 ° C.)
[Isocyanate cross-linking agent]
Isocyanate-based cross-linking agent: Isocyanate-based cross-linking agent (manufactured by Tosoh Corporation, product name "Coronate L")
表１から明らかなように、実施例で製造した表示用ラベルは、十分な粘着力を発揮することができる。さらに、実施例で製造した表示用ラベルは、粘着剤層からの粘着成分の溶出も生じ難い。 As is clear from Table 1, the display label produced in the examples can exhibit sufficient adhesive strength. Further, the display label produced in the examples is less likely to cause elution of the adhesive component from the adhesive layer.
本発明に係る表示用ラベルは、医療用器具や医薬品が収容される医薬品容器といった医療用製品に貼付される表示用ラベルとして好適に使用することができる。 The labeling label according to the present invention can be suitably used as a labeling label attached to a medical product such as a medical device or a pharmaceutical container containing a drug.
Claims (7)
前記粘着剤層が、アクリル系共重合体と、粘着付与剤とを含有する粘着剤組成物から形成されたものであり、
前記アクリル系共重合体の分子量分布（Ｍｗ／Ｍｎ）が、３．０以下であり、
前記医療用製品の表面の少なくとも一部が、オレフィン系樹脂からなり、
前記表示用ラベルが、オレフィン系樹脂からなる前記表面に貼付される
ことを特徴とする表示用ラベル。 A display label used in a medical product , comprising a base material and an adhesive layer laminated on one surface side of the base material.
The pressure-sensitive adhesive layer is formed of a pressure-sensitive adhesive composition containing an acrylic copolymer and a pressure-sensitive adhesive.
The molecular weight distribution of the acrylic copolymer molecular weight distribution (Mw / Mn) state, and are 3.0 or less,
At least a part of the surface of the medical product is made of an olefin resin.
A display label characterized in that the display label is affixed to the surface made of an olefin resin.