JP6889984B2 - 伸縮性積層体およびそれを含む物品 - Google Patents
伸縮性積層体およびそれを含む物品 Download PDFInfo
- Publication number
- JP6889984B2 JP6889984B2 JP2016051242A JP2016051242A JP6889984B2 JP 6889984 B2 JP6889984 B2 JP 6889984B2 JP 2016051242 A JP2016051242 A JP 2016051242A JP 2016051242 A JP2016051242 A JP 2016051242A JP 6889984 B2 JP6889984 B2 JP 6889984B2
- Authority
- JP
- Japan
- Prior art keywords
- olefin
- present
- stretchable laminate
- stretched
- laminate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
エラストマー層の少なくとも一方の側にオレフィン系樹脂層を有する、長尺状の伸縮性積層体であって、
長尺方向をMD方向、長尺方向と直交する方向をCD方向とするとき、
該伸縮性積層体の〔MD方向10%伸長強度(N/30mm)〕/〔坪量(gsm)〕が0.14(N/30mm・gsm)以上である。
本発明の伸縮性積層体は、エラストマー層の少なくとも一方の側にオレフィン系樹脂層を有する。すなわち、本発明の伸縮性積層体は、エラストマー層の片方の側のみにオレフィン系樹脂層を有していても良いし、エラストマー層の両方の側にオレフィン系樹脂層を有していても良い。本発明の伸縮性積層体がこのような構成を有すれば、本発明の伸縮性積層体は、耐オイル性に優れ得る。また、エラストマー性を有する樹脂(例えば、オレフィン系エラストマーやスチレン系エラストマーなど)からなる層は、それ同士が積層された場合にブロッキングが起こりやすい。このため、例えば、エラストマー性を有する樹脂からなる層同士が積層されるような状態で伸縮性積層体をロール体とした場合には、エラストマー性を有する樹脂からなる層同士が容易にブロッキングしてしまい、巻戻しが困難になりやすい。本発明の伸縮性積層体は、エラストマー層の少なくとも一方の側にオレフィン系樹脂層を有するので、耐ブロッキング性に優れ得る。
エラストマー層の層数は、任意の適切な数を採用し得る。このようなエラストマー層の層数は、好ましくは1層〜5層であり、より好ましくは1層〜3層であり、さらに好ましくは1層〜2層であり、特に好ましくは1層である。
オレフィン系樹脂層の層数は、任意の適切な数を採用し得る。このようなオレフィン系樹脂層の層数は、好ましくは1層〜5層であり、より好ましくは1層〜3層であり、さらに好ましくは1層〜2層であり、特に好ましくは2層(例えば、エラストマー層の両側に1層ずつ)である。
本発明の伸縮性積層体を製造する方法としては、エラストマー層の少なくとも一方の側にオレフィン系樹脂層を有するような構成を構築できる方法であれば、本発明の効果を損なわない範囲で、任意の適切な方法を採用し得る。
本発明の伸縮性積層体は、本発明の効果を有効に利用できる任意の適切な物品に用いることができる。すなわち、本発明の物品は、本発明の伸縮性積層体を含む。このような物品としては、代表的には、例えば、衛生用品などが挙げられる。このような衛生用品としては、例えば、おむつ(特に、イヤー(耳)部分や、腰周りや脚周りの開口部分の伸縮性部材(ウエストバント゛やギャザー)として本発明の伸縮性積層体が使用されたおむつ)、サポーター、マスクなどが挙げられる。
実施例および比較例にて得られた伸縮性積層体または積層体を幅方向で30mmに切断し、長手方向にチャック間40mmにて引張試験機(島津製作所製:AG−20kNG)にセットし、引張速度300mm/minにて10%まで伸長した際の引張強度を測定した。
実施例および比較例にて得られた伸縮性積層体または積層体を幅方向で100mm、長手方向で200mmに切断し、試験片の重量を電子天秤にて測定した。本測定を3回繰り返し、重量の平均値から坪量(平米面積当たりの重量)を算出した。
実施例および比較例にて得られた伸縮性積層体または積層体のロール体を幅方向で30mmに切断し、23℃×50RH%の状態で24時間保存した後、巻戻速度300mm/minにて巻き戻した。その巻き戻しの際に、伸縮性積層体または積層体が破断したものを×、破断しなかったものを○とし、破断せず、かつ、保存前後で巻戻し感に全く変化が見られなかったものを◎とした。
実施例および比較例にて得られた伸縮性積層体または積層体を長手方向に50mm、幅方向に10mmで切断し、長手方向に100%伸長した状態で、ガラス板の上に貼付け固定した。伸長された伸縮性積層体または積層体の表面にベビーオイル(ピジョン製、ベビーオイルQ、主成分:トリ(カプリル酸/カプリン酸)グリセリル)を0.5mL滴下し、下記の基準で評価した。
×:60分後に伸縮性積層体または積層体に、ベビーオイルによって溶解することによる穴や亀裂が発生して破断している。
△:60分後に伸縮性積層体または積層体に、ベビーオイルによって溶解することによる穴や亀裂ができているが破断まで至っていない。
○:60分後に伸縮性積層体または積層体に、ベビーオイルによって溶解することによる穴や亀裂が形成していない。
なお、本発明において、滴下耐オイル性の試験に使用される「ベビーオイル」としては、上記「ベビーオイルQ」以外にも、ピジョン株式会社から販売されている「ベビーオイルP」等のトリ(カプリル酸/カプリン酸)グリセリルを主成分とする「ベビーオイル」を使用することができる。
実施例および比較例にて得られた伸縮性積層体または積層体を幅方向で30mmに切断し、長手方向にチャック間40mmにて引張試験機(島津製作所製:AG−20kNG)にセットし、引張速度300mm/minにて100%伸長した。100%伸長後、伸長状態にて固定し、10分間室温にて保持した。10分後、伸長状態を解放し、初期チャック間距離40mm(A)、試験後フィルム長さ(40+α)mm(B)を計測後、[{(B)−(A)}/(A)]×100にて変動率を計測した。変動率が20%を超えたものを×、20%以下のものを○とした。
実施例および比較例において、3種3層(A層/B層/C層)押し出しTダイ成形機を用いて伸縮性積層体または積層体を成形した。その押出温度は以下の条件にて実施した。
A層:200℃
B層:200℃
C層:200℃
ダイス温度:200℃
Tダイから共押出成形して一体化させ、得られた伸縮性積層体または積層体が十分に固化した後に、ロール形状に巻き取ることによってロール体とした。
部分延伸する場合は、凸部のピッチ幅が1mm、凹部のピッチ幅(凸部と凸部の間隔)が2mmの2本の凹凸ロールを、上下から3.5mm重ね合わせた間に、ロール体から繰り出した伸縮性積層体または積層体を20m/minの速度で通過させ、700%延伸を実施した。
全面延伸する場合は、ロール体から繰り出した伸縮性積層体または積層体のエッジをテンタークリップで掴み、幅方向に400%伸張させた。
非エラストマー性オレフィン系樹脂としてHDPE(東ソー社製、商品名:ニポロンハード1000)を押出機のA層に、オレフィン系エラストマーとしてEPR(エクソンモービル社製、商品名:ビスタマックス6202)を押出機のB層に、非エラストマー性オレフィン系樹脂としてHDPE(東ソー社製、商品名:ニポロンハード1000)を押出機のC層に投入し、A層/B層/C層=4μm/32μm/4μm、計40μmの厚みの積層体を押し出した。得られた積層体を部分延伸することで、伸縮性積層(1)を得た。
結果を表1に示した。
非エラストマー性オレフィン系樹脂としてHDPE(Basell社製、商品名:52518)を使用した以外は実施例1と同様にして、伸縮性積層体(2)を得た。
結果を表1に示した。
A層/B層/C層=5.5μm/44μm/5.5μm、計55μmの厚みとした以外は実施例1と同様にして、伸縮性積層体(3)を得た。
結果を表1に示した。
オレフィン系エラストマーとしてEPR(エクソンモービル社製、商品名:ビスタマックス7010)を使用した以外は実施例1と同様にして、伸縮性積層体(4)を得た。
結果を表1に示した。
オレフィン系エラストマーの代わりにスチレン系エラストマーとしてSIS(日本ゼオン株式会社製、商品名:クインタック3390)を使用した以外は実施例1と同様にして、伸縮性積層体(5)を得た。
結果を表1に示した。
オレフィン系エラストマーの代わりにスチレン系エラストマーとしてSBS(クレイトンポリマー製、商品名:クレイトンD1191)を使用した以外は実施例1と同様にして、伸縮性積層体(C1)を得た。
結果を表1に示した。
部分延伸する代わりに全面延伸を実施した以外は実施例1と同様にして、伸縮性積層体(C1)を得た。
結果を表1に示した。
部分延伸する代わりに全面延伸を実施した以外は実施例3と同様にして、伸縮性積層体(C2)を得た。
結果を表1に示した。
20a オレフィン系樹脂層
20b オレフィン系樹脂層
30 延伸部分
40 非延伸部分
100 伸縮性積層体
200 積層体
300 伸縮性積層体
1000 ロール
1100 小径ロール部
1200 大径ロール部
2000 ロール
2100 小径ロール部
2200 大径ロール部
Claims (9)
- エラストマー層の少なくとも一方の側にオレフィン系樹脂層を有する、長尺状の伸縮性積層体であって、
該エラストマー層がオレフィン系エラストマーを含み、該エラストマー層中のオレフィン系エラストマーの含有割合が80重量%〜100重量%であり、
長尺方向をMD方向、長尺方向と直交する方向をCD方向とするとき、
該伸縮性積層体の〔MD方向10%伸長強度(N/30mm)〕/〔坪量(gsm)〕が0.14(N/30mm・gsm)以上であり、
前記CD方向に沿って延伸部分と非延伸部分とが存在し、
前記延伸部分と前記非延伸部分の面積比率(延伸部分:非延伸部分)が、1:0.5〜1:3である、
伸縮性積層体。 - 前記〔MD方向10%伸長強度(N/30mm)〕/〔坪量(gsm)〕が0.15(N/30mm・gsm)以上である、請求項1に記載の伸縮性積層体。
- 前記オレフィン系樹脂層が非エラストマー性オレフィン系樹脂を含む、請求項1または2に記載の伸縮性積層体。
- 前記CD方向に沿って延伸部分と非延伸部分とが交互に存在する、請求項1から3のいずれかに記載の伸縮性積層体。
- 事前延伸されている、請求項1から4までのいずれかに記載の伸縮性積層体。
- 前記事前延伸が部分延伸である、請求項5に記載の伸縮性積層体。
- 前記延伸部分と前記非延伸部分が、径の異なる凹部分と凸部分とを有する2本の凹凸ロールを互いの凹部と凸部によって噛み合わせたロール延伸によって形成される、請求項1から6までのいずれかに記載の伸縮性積層体。
- 衛生用品に用いられる、請求項1から7までのいずれかに記載の伸縮性積層体。
- 請求項1から7までのいずれかに記載の伸縮性積層体を含む物品。