JP6880268B1 - Molding method for molding twisted resin molded products - Google Patents

Molding method for molding twisted resin molded products Download PDF

Info

Publication number
JP6880268B1
JP6880268B1 JP2020050374A JP2020050374A JP6880268B1 JP 6880268 B1 JP6880268 B1 JP 6880268B1 JP 2020050374 A JP2020050374 A JP 2020050374A JP 2020050374 A JP2020050374 A JP 2020050374A JP 6880268 B1 JP6880268 B1 JP 6880268B1
Authority
JP
Japan
Prior art keywords
molded product
resin
tape
molding
mold
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2020050374A
Other languages
Japanese (ja)
Other versions
JP2021146654A (en
Inventor
清貴 中山
清貴 中山
粋和 河本
粋和 河本
孝治 松崎
孝治 松崎
西田　正三
正三 西田
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Japan Steel Works Ltd
Original Assignee
Japan Steel Works Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Japan Steel Works Ltd filed Critical Japan Steel Works Ltd
Priority to JP2020050374A priority Critical patent/JP6880268B1/en
Application granted granted Critical
Publication of JP6880268B1 publication Critical patent/JP6880268B1/en
Publication of JP2021146654A publication Critical patent/JP2021146654A/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

【課題】小コストで捻れのある複雑な形状の成形品を成形する成形方法を提供する。【解決手段】長手方向に配向した強化繊維が樹脂によってバインドされロール状に巻かれて提供されている強化繊維テープ（Ｔ）を使用する。まず強化繊維テープ（Ｔ）から所定幅、所定長さに切断した複数本のテープ片（９）を金型（１）にインサートする。このときキャビティ内で複数本のテープ片（９）が互いに所定の間隔を空けるように配置する。次いで樹脂を射出する。そうすると複数本のテープ片（９）が貼合された成形品（１１）が得られる。樹脂が完全に冷却固化する前に成形品（１２）を金型から取り出して冷却する。強化繊維テープ（Ｔ）と樹脂は熱膨張率に違いがあるので、冷却時に成形品（１１）は変形する。これによって捻れのある成形品（１２）を得る。【選択図】 図２PROBLEM TO BE SOLVED: To provide a molding method for molding a molded product having a complicated shape with a twist at a low cost. SOLUTION: A reinforcing fiber tape (T) provided by binding reinforcing fibers in a longitudinal direction with a resin and winding them in a roll shape is used. First, a plurality of tape pieces (9) cut from the reinforcing fiber tape (T) to a predetermined width and a predetermined length are inserted into the mold (1). At this time, a plurality of tape pieces (9) are arranged in the cavity so as to be spaced apart from each other at a predetermined distance. Then the resin is injected. Then, a molded product (11) in which a plurality of tape pieces (9) are bonded is obtained. Before the resin is completely cooled and solidified, the molded product (12) is taken out from the mold and cooled. Since the reinforcing fiber tape (T) and the resin have different coefficients of thermal expansion, the molded product (11) is deformed during cooling. As a result, a twisted molded product (12) is obtained. [Selection diagram] Fig. 2

Description

本発明は、射出成形によって捻れのある複雑な形状を備えた樹脂成形品を成形する成形方法に関するものである。 The present invention relates to a molding method for molding a resin molded product having a complicated shape with a twist by injection molding.

捻れのある複雑な形状を備えた成形品は、色々な分野で利用されており、例えばプロペラ、インペラのブレード等が周知である。一般的にはプロペラ、インペラ等のブレードは金属板からなり所定の捻れが形成されている。捻れを形成するには、成形品の形状に近い曲げ型を使用して板材をプレス加工する方法が周知であるが、例えば特許文献１に記載されているように２組のロール対で板材を挟み、両ロール対の間に相対的な捻れ方向の変位を与えた状態で、ロール回転によって板材を送り出し、それによって捻れを形成する方法もある。つまり金属板から緩やかに曲げるようにして成形されている。ところで近年、捻れのある複雑な形状の成形品を、軽量で安価な樹脂から成形したいというニーズが多くなってきている。例えばプロペラ、インペラのブレードについても樹脂による成形が試みられている。熱可塑性の樹脂から捻れのある成形品を成形する場合、例えば特許文献２に記載されているように、押出機によって成形することもできる。しかしながら押出方法によって成形する場合、連続的に一定の捻れが形成された軸状の成形品を成形することはできるが、プロペラ、インペラのブレード等のように捻れが一定でない、あるいは板幅が変化するような複雑な形状の成形品を成形することはできない。このような複雑な形状の成形品は、所定の金型を使用して射出成形機により射出成形するようにしている。 Molded articles having a complicated shape with a twist are used in various fields, and for example, propellers, impeller blades, and the like are well known. Generally, blades such as propellers and impellers are made of metal plates and have a predetermined twist. In order to form a twist, a method of pressing a plate material using a bending die close to the shape of a molded product is well known. For example, as described in Patent Document 1, the plate material is formed by two pairs of rolls. There is also a method in which the plate material is sent out by the rotation of the rolls while being sandwiched and the displacement in the relative twisting direction is given between the two roll pairs, thereby forming the twist. That is, it is formed so as to be gently bent from the metal plate. By the way, in recent years, there has been an increasing need to mold a molded product having a complicated shape with a twist from a lightweight and inexpensive resin. For example, molding of propeller and impeller blades with resin has been attempted. When molding a twisted molded product from a thermoplastic resin, it can also be molded by an extruder, for example, as described in Patent Document 2. However, when molding by the extrusion method, it is possible to mold a shaft-shaped molded product in which a constant twist is continuously formed, but the twist is not constant or the plate width changes like a propeller, an impeller blade, etc. It is not possible to mold a molded product having such a complicated shape. A molded product having such a complicated shape is injection-molded by an injection molding machine using a predetermined mold.

特開昭６１−２５５７２４号公報Japanese Unexamined Patent Publication No. 61-255724 特開平６−２９７０３２号公報Japanese Unexamined Patent Publication No. 6-297032 特開２０１８−２０２６７７号公報Japanese Unexamined Patent Publication No. 2018-202677

捻れのある樹脂成形品の成形方法と直接関係はないが、炭素繊維、ガラス繊維等を含んだ強化繊維テープを貼合した成形品を成形する方法が周知であり、例えば特許文献３に記載されている。強化繊維テープは、長手方向に配向された炭素繊維、ガラス繊維等の強化繊維が樹脂によりバインドされたものであり、ロール状に巻かれた状態で提供されている。可撓性を備えているが、比較的強い弾性も備えている。特許文献３に記載の成形方法は、このような強化繊維テープをインサートして樹脂を射出する。そうすると強化繊維テープが所定の長さ貼合された樹脂成形品が成形できる。 Although it is not directly related to the molding method of the twisted resin molded product, the method of molding the molded product to which the reinforcing fiber tape containing carbon fiber, glass fiber, etc. is bonded is well known, and is described in, for example, Patent Document 3. ing. The reinforcing fiber tape is obtained by binding reinforcing fibers such as carbon fibers and glass fibers oriented in the longitudinal direction with a resin, and is provided in a rolled state. It is flexible, but also has relatively strong elasticity. In the molding method described in Patent Document 3, such a reinforcing fiber tape is inserted and the resin is injected. Then, a resin molded product in which the reinforcing fiber tape is bonded to a predetermined length can be molded.

捻れのある樹脂成形品を射出成形により成形する場合、必然的にアンダーカット部が多くできるので、金型は複雑な構造から構成しなければならない。例えば金型を３個、４個から構成したり中子を設けたりする必要がある。そうすると金型のコストが高くなって、成形に要するコストが大きくなるという問題がある。特に近年は、消費者のニーズに応えるために多品種少量生産が要求される場合が多い。捻れの大きさが少しずつ異なる成形品を少量ずつ成形したい場合、それぞれの形状毎に金型を用意しなければならず、コスト高になってしまう。 When a twisted resin molded product is molded by injection molding, there are inevitably many undercut portions, so the mold must be composed of a complicated structure. For example, it is necessary to configure the mold from three or four or to provide a core. Then, there is a problem that the cost of the mold becomes high and the cost required for molding increases. Especially in recent years, high-mix low-volume production is often required to meet consumer needs. If it is desired to mold a molded product having a slightly different twist size little by little, a mold must be prepared for each shape, resulting in high cost.

本発明は以上のような問題を解決することを目的としており、具体的には、射出成形によって捻れのある複雑な形状の成形品を成形する成形方法であって、シンプルな金型でも実施でき、コストが小さく、捻れの大きさが異なる成形品であっても新たに金型を用意することなく必要な捻れを形成することができる、捻れのある成形品を成形する成形方法を提供することを目的としている。 An object of the present invention is to solve the above problems. Specifically, it is a molding method for molding a molded product having a complicated shape with a twist by injection molding, and can be carried out even with a simple mold. To provide a molding method for molding a twisted molded product, which can form the required twist without preparing a new mold even if the molded product has a low cost and a different twist size. It is an object.

本発明は上記目的を達成するために、長方形状の板状を呈する凹部からなるキャビティを備えた金型と、長手方向に配向した強化繊維が樹脂によってバインドされロール状に巻かれて提供されている強化繊維テープを使用する。まず強化繊維テープから所定幅、所定長さに切断して複数本のテープ片を得、これをインサート品とする。これら複数本のテープ片を金型にインサートするときキャビティ内で複数本のテープ片が互いに所定の間隔を空けるようにかつ長方形の長手方向に対して所定の角度傾けた状態で配置する。次いで樹脂を射出する。そうすると複数本のテープ片が貼合された成形品が得られる。樹脂が完全に冷却固化する前に成形品を金型から取り出して冷却する。強化繊維テープと樹脂は熱膨張率に違いがあるので、冷却時に成形品は変形する。これによって捻れのある成形品を得る。 In order to achieve the above object, the present invention is provided in which a mold having a cavity composed of a concave portion having a rectangular plate shape and a reinforcing fiber oriented in the longitudinal direction are bound by a resin and wound in a roll shape. Use the reinforcing fiber tape that is available. First, a plurality of tape pieces are obtained by cutting the reinforcing fiber tape into a predetermined width and a predetermined length , and these are used as insert products. The tape piece of a plurality of arranged in a state tape piece a plurality of inside cavity inclined a predetermined angle and with respect to the longitudinal direction of the rectangle as spaced a predetermined distance from each other when inserted into the mold. Then the resin is injected. Then, a molded product in which a plurality of tape pieces are bonded can be obtained. The molded product is removed from the mold and cooled before the resin is completely cooled and solidified. Since the reinforcing fiber tape and the resin have different coefficients of thermal expansion, the molded product is deformed during cooling. As a result, a twisted molded product is obtained.

すなわち本発明の請求項１に係る発明は、長方形状の板状を呈する凹部からなるキャビティを備えた金型を使用して、インサート成形により成形品を得る成形方法であって、長手方向に配向した強化繊維が樹脂によってバインドされている強化繊維テープを所定幅、所定長さで切断して得た複数本のテープ片をインサート品とし、前記キャビティに前記複数本のテープ片を互いに間隔を空けるように、かつ前記長方形の長手方向に対して所定の角度傾けた状態でインサートし、該金型に樹脂を射出して複数本のテープ片が貼合された成形品を得、樹脂が完全に冷却固化する前に前記成形品を前記金型から取り出して冷却させ、強化繊維テープと樹脂の熱膨張率の違いにより前記成形品に変形が生じるようにすることを特徴とする、捻れのある成形品の成形方法として構成される。

That is, the invention according to claim 1 of the present invention is a molding method for obtaining a molded product by insert molding using a mold provided with a cavity having a concave portion having a rectangular plate shape, and is oriented in the longitudinal direction. A plurality of tape pieces obtained by cutting a reinforcing fiber tape to which the reinforcing fibers are bound by a resin with a predetermined width and a predetermined length are used as an insert product, and the plurality of tape pieces are spaced apart from each other in the cavity. As described above, the insert is inserted at a predetermined angle with respect to the longitudinal direction of the rectangle, and the resin is injected into the mold to obtain a molded product in which a plurality of tape pieces are bonded, and the resin is completely formed. Twisted molding, characterized in that the molded product is taken out of the mold and cooled before being cooled and solidified so that the molded product is deformed due to the difference in thermal expansion rate between the reinforcing fiber tape and the resin. It is configured as a molding method for products.

以上のように本発明は、長手方向に配向した強化繊維が樹脂によってバインドされている強化繊維テープを使用する。この強化繊維テープから所定幅、所定長さで切断された複数本のテープ片をキャビティ内で互いに間隔を空けて金型にインサートし、該金型に樹脂を射出して複数本のテープ片が貼合された成形品を得る。そして樹脂が完全に冷却固化する前に前記成形品を前記金型から取り出して冷却させ、強化繊維テープと樹脂の熱膨張率の違いにより前記成形品に変形が生じるようにする。後で詳しく説明するように、所定のパターンでテープ片を貼合すると捻れのある成形品を得ることができる。つまり複雑な捻れのある成形品であっても、キャビティの形状が複雑で、構造も複雑な金型を用意する必要がなく製造コストは小さい。そして冷却時の変形は、テープ片の配置等によってその方向や大きさを調整することができるので、テープ片の貼合位置、枚数等を変えるだけで任意の形状に変形させることができる。つまり、捻れの大きさが少しずつことなる成形品を得る場合であっても、必要な金型の個数は少なくて済むという効果が得られる。 As described above, the present invention uses a reinforcing fiber tape in which reinforcing fibers oriented in the longitudinal direction are bound by a resin. A plurality of tape pieces cut from this reinforcing fiber tape with a predetermined width and a predetermined length are inserted into a mold at intervals in the cavity, and resin is injected into the mold to form the plurality of tape pieces. Obtain a bonded molded product. Then, before the resin is completely cooled and solidified, the molded product is taken out from the mold and cooled so that the molded product is deformed due to the difference in the coefficient of thermal expansion between the reinforcing fiber tape and the resin. As will be described in detail later, a twisted molded product can be obtained by laminating the tape pieces in a predetermined pattern. That is, even if the molded product has a complicated twist, the shape of the cavity is complicated, it is not necessary to prepare a mold having a complicated structure, and the manufacturing cost is low. Since the direction and size of the deformation at the time of cooling can be adjusted by arranging the tape pieces or the like, it can be deformed into an arbitrary shape only by changing the bonding position, the number of tape pieces, or the like. That is, even when a molded product having a slightly different twist size is obtained, the effect that the number of required molds can be reduced can be obtained.

その（Ａ）は、本実施の形態に係る捻れのある成形品を成形する成形用金型を示す斜視図、その（Ｂ）は本実施の形態に係る捻れのある成形品の成形方法において材料として使用するロール状に巻かれた強化繊維テープを示す斜視図である。(A) is a perspective view showing a molding die for molding a twisted molded product according to the present embodiment, and (B) is a material in the method for molding a twisted molded product according to the present embodiment. It is a perspective view which shows the reinforcing fiber tape wound in the form of a roll used as a roll. 本実施の形態に係る捻れのある成形品の成形方法を説明する図で、その（Ａ）は本実施の形態に係る成形用金型に強化繊維テープからなるテープ片をインサートした様子を示す成形用金型の斜視図、その（Ｂ）は冷却前におけるテープ片が貼合された成形品を示す斜視図、その（Ｃ）は冷却後におけるテープ片が貼合された成形品を示す斜視図である。It is a figure explaining the molding method of the molded article with a twist which concerns on this Embodiment, (A) | molding which shows the state which the tape piece made of the reinforcing fiber tape was inserted into the molding die which concerns on this Embodiment. A perspective view of the mold, (B) is a perspective view showing a molded product to which a tape piece is bonded before cooling, and (C) is a perspective view showing a molded product to which a tape piece is bonded after cooling. Is. 冷却によって成形品の表面が収縮する様子を模式的に示す図で、その（Ａ）はテープ片が貼合されていない樹脂の表面が収縮する様子を、そしてその（Ｂ）はテープ片が貼合されている樹脂においてテープ片近傍の樹脂の表面の収縮する様子を、それぞれ示す平面図である。It is a diagram schematically showing how the surface of a molded product shrinks due to cooling, in which (A) shows how the surface of a resin to which a tape piece is not attached shrinks, and in (B), a tape piece is attached. It is a top view which shows the state of shrinkage of the surface of the resin in the vicinity of a tape piece in the combined resin. 冷却によってテープ片が貼合された成形品が変形し、捻れがある成形品に変化する様子を示す図で、その（Ａ）は冷却前における、その（Ｂ）は冷却中における成形品を示す正面図であり、その（Ｃ）は冷却後における成形品を示す斜視図である。It is a figure which shows how the molded product to which a tape piece is attached is deformed by cooling and changes into a molded product with a twist, in which (A) shows a molded product before cooling and (B) shows a molded product during cooling. It is a front view, and (C) is a perspective view which shows the molded article after cooling.

本発明の実施の形態について説明する。本実施の形態に係る成形方法は、比較的シンプルな構造の金型を使用して捻れのある複雑な形状の成形品を得る方法である。図１の（Ａ）には、本実施の形態に係る成形用金型１が示されている。本実施の形態に係る成形用金型１は、竪型射出成形機に取り付けられる金型であり、竪型射出成形機の上可動盤に取り付けられる上金型３と、固定盤に取り付けられる下金型４とから構成されている。下金型４には、パーティングラインから長方形状に所定深さだけ窪んだ凹部６が形成されている。この凹部６に後で説明するように強化繊維テープから切断された複数本のテープ片がインサートされるようになっている。本実施の形態において凹部６の底面は滑らかに形成されているが、凹部６の底面に多数の微小な吸引孔を設けて負圧源に接続し、インサートされたテープ片を吸引してその位置がずれないようにしてもよい。上金型３はそのパーティングラインは示されていないが、凹部６と同じ形状の長方形状の凹部が形成されている。上金型３には樹脂を射出するためのスプル７が設けられている。 Embodiments of the present invention will be described. The molding method according to the present embodiment is a method of obtaining a molded product having a complicated shape with a twist by using a mold having a relatively simple structure. FIG. 1A shows a molding die 1 according to the present embodiment. The molding die 1 according to the present embodiment is a mold attached to a vertical injection molding machine, and is an upper mold 3 attached to an upper movable plate of a vertical injection molding machine and a lower mold 3 attached to a fixed plate. It is composed of a mold 4. The lower mold 4 is formed with a recess 6 that is rectangularly recessed from the parting line by a predetermined depth. As will be described later, a plurality of tape pieces cut from the reinforcing fiber tape are inserted into the recess 6. In the present embodiment, the bottom surface of the recess 6 is smoothly formed, but a large number of minute suction holes are provided on the bottom surface of the recess 6 to connect to a negative pressure source, and the inserted tape piece is sucked to the position. You may prevent it from slipping. Although the parting line of the upper mold 3 is not shown, a rectangular recess having the same shape as the recess 6 is formed. The upper mold 3 is provided with a sprue 7 for injecting resin.

本実施の形態に係る捻れのある成形品を成形する成形方法においては、図１の（Ｂ）に示されているような、ロールＲに巻かれた強化繊維テープＴを使用する。本実施の形態においては強化繊維テープＴは強化繊維として炭素繊維が採用されている。強化繊維テープＴは多数の炭素繊維が長手方向に配向され、所定の樹脂によってこれが固められて所定幅、所定厚さのテープ状に形成されたものである。このような強化繊維テープＴは、可撓性を備えておりロール状に巻かれて提供されている。 In the molding method for molding the twisted molded product according to the present embodiment, the reinforcing fiber tape T wound on the roll R as shown in FIG. 1 (B) is used. In the present embodiment, carbon fiber is adopted as the reinforcing fiber in the reinforcing fiber tape T. The reinforcing fiber tape T is formed by orienting a large number of carbon fibers in the longitudinal direction and solidifying them with a predetermined resin to form a tape having a predetermined width and a predetermined thickness. Such a reinforcing fiber tape T has flexibility and is provided by being rolled into a roll.

本実施の形態に係る捻れのある成形品を成形する成形方法を説明する。まず、強化繊維テープＴを所定幅、所定長さで切断し、複数本のテープ片９、９、…を得る。これらのテープ片９、９、…を、図２の（Ａ）に示されているように、下金型４の凹部６にインサートする。複数本のテープ片９、９、…は、長方形状の凹部６に対してその長手方向に対して所定の角度に傾けた状態に配置し、互いに所定の間隔だけ離間させるようにしてインサートする。次いでこの下金型４と図に示されていない上金型３とを型閉じ、型締めし、成形用金型１内にキャビティを構成する。キャビティに樹脂を射出する。そうするとテープ片９、９、…が一方の面に貼合された成形品１１が成形される。完全に冷却固化しない状態で成形用金型１を開いて成形品１１を取り出す。取り出した直後の成形品１１が図２の（Ｂ）に示されている。成形品１１を成形用金型１の外で冷却させる。そうすると強化繊維テープと樹脂の熱膨張率の違いにより成形品１１に捻れが生じて、図２の（Ｃ）に示されているように変形する。冷却後の成形品、つまり捻れのある成形品１２が得られる。 A molding method for molding a twisted molded product according to the present embodiment will be described. First, the reinforcing fiber tape T is cut to a predetermined width and a predetermined length to obtain a plurality of tape pieces 9, 9, .... These tape pieces 9, 9, ... Are inserted into the recess 6 of the lower mold 4 as shown in FIG. 2 (A). The plurality of tape pieces 9, 9, ... Are arranged in a state of being tilted at a predetermined angle with respect to the longitudinal direction of the rectangular concave portion 6, and are inserted so as to be separated from each other by a predetermined distance. Next, the lower mold 4 and the upper mold 3 not shown in the figure are closed and molded to form a cavity in the molding mold 1. Inject resin into the cavity. Then, the molded product 11 in which the tape pieces 9, 9, ... Are bonded to one surface is molded. The molding die 1 is opened and the molded product 11 is taken out in a state where it is not completely cooled and solidified. The molded product 11 immediately after being taken out is shown in FIG. 2 (B). The molded product 11 is cooled outside the molding die 1. Then, the molded product 11 is twisted due to the difference in the coefficient of thermal expansion between the reinforcing fiber tape and the resin, and is deformed as shown in FIG. 2 (C). A molded product after cooling, that is, a molded product 12 having a twist is obtained.

冷却時に成形品１１が変形して捻れのある成形品１２に形成される理由を説明する。樹脂は比較的熱膨張率が大きく、射出成形した直後の高熱の状態から冷却されると熱収縮により収縮する。図３の（Ａ）には、成形品１１においてテープ片９から離間した所定の部分の樹脂表面が示されている。このようにテープ片９の影響を受けない部分の樹脂表面において樹脂が熱収縮するとき、仮想的な微小円２５の樹脂は冷却により仮想的な微小円２５’に変化する。つまり矢印２６で示されているように、冷却によって樹脂は均一に収縮する。このような熱収縮は任意の箇所において均等なので、冷却されても全体が均一に収縮してその形状は実質的に変化しない。これに対して、図３の（Ｂ）に示されているように、テープ片９が貼合されている部分における樹脂の熱収縮では状況が異なる。テープ片９は強化繊維からなるので熱膨張率は樹脂に比して小さい。つまり実質的に熱収縮はほとんどない。従ってテープ片９が貼合されてテープ片９にその表面が覆われている樹脂はほとんど収縮せず、テープ片９から露出している樹脂が収縮することになる。その結果、テープ片９に覆われている部分と露出している部分との境界線２７近傍における仮想的な微小円２８の樹脂は冷却により収縮すると微小楕円２８’のように変化する。つまり境界線２７近傍の樹脂は、矢印３０で示されているように、境界線２７に対して直交する方向に収縮することになる。 The reason why the molded product 11 is deformed and formed into the twisted molded product 12 during cooling will be described. The resin has a relatively large coefficient of thermal expansion, and when cooled from a high heat state immediately after injection molding, it shrinks due to heat shrinkage. FIG. 3A shows the resin surface of a predetermined portion of the molded product 11 separated from the tape piece 9. When the resin heat-shrinks on the resin surface of the portion that is not affected by the tape piece 9 in this way, the resin of the virtual microcircle 25 changes into a virtual microcircle 25'by cooling. That is, as shown by the arrow 26, the resin shrinks uniformly by cooling. Since such heat shrinkage is uniform at any place, the whole shrinks uniformly even when cooled, and its shape does not substantially change. On the other hand, as shown in FIG. 3B, the situation is different in the heat shrinkage of the resin at the portion where the tape piece 9 is attached. Since the tape piece 9 is made of reinforcing fibers, the coefficient of thermal expansion is smaller than that of the resin. That is, there is virtually no heat shrinkage. Therefore, the resin to which the tape piece 9 is attached and its surface is covered with the tape piece 9 hardly shrinks, and the resin exposed from the tape piece 9 shrinks. As a result, the resin of the virtual minute circle 28 in the vicinity of the boundary line 27 between the portion covered with the tape piece 9 and the exposed portion changes like a minute ellipse 28'when contracted by cooling. That is, as shown by the arrow 30, the resin in the vicinity of the boundary line 27 shrinks in the direction orthogonal to the boundary line 27.

さて、樹脂が熱い状態の成形品１１には、図４の（Ａ）に示されているように、その表面に複数本のテープ片９、９、…が貼合されている。冷却すると複数本のテープ片９、９で囲まれた領域の樹脂は、矢印３２、３２、…で示されているように、テープ片９、９の方向と直交する方向に収縮する。そうすると、成形品１１の表面側では、図４の（Ｂ）に示されているように変形することになる。つまり図において左側が矢印３３で示されているように下側にずれ、右側が矢印３４で示されているように上側にずれるように変形する。しかしながら、成形品１１の裏面側ではテープ片９、９、…は貼合されていないので均一に収縮する。そうすると、符号３５で示されているように変形せずに長方形状に維持される。表面側だけが変形して裏面側が変形しないので、図４の（Ｃ）に示されているように全体に捻れが生じる。すなわち捻れのある成形品１２が得られる。 As shown in FIG. 4A, a plurality of tape pieces 9, 9, ... Are attached to the surface of the molded product 11 in a hot resin state. When cooled, the resin in the region surrounded by the plurality of tape pieces 9, 9 shrinks in a direction orthogonal to the direction of the tape pieces 9, 9, as indicated by arrows 32, 32, .... Then, the surface side of the molded product 11 is deformed as shown in FIG. 4 (B). That is, in the figure, the left side is deformed so as to be shifted downward as shown by the arrow 33, and the right side is deformed so as to be shifted upward as shown by the arrow 34. However, since the tape pieces 9, 9, ... Are not bonded to each other on the back surface side of the molded product 11, they shrink uniformly. Then, as shown by reference numeral 35, it is maintained in a rectangular shape without being deformed. Since only the front surface side is deformed and the back surface side is not deformed, twisting occurs as a whole as shown in FIG. 4 (C). That is, a twisted molded product 12 is obtained.

本実施の形態に係る捻れのある成形品の成形方法は色々な変形が可能である。例えば強化繊維テープとしてグラスファイバーからなる強化繊維テープを使用することもできる。テープ片９、９、…の配置についても変形が可能である。例えばテープ片９、９、…は成形品１１の一方の面にだけ貼合するように説明したが、他方の面つまり裏面側にも貼合してもよい。そうすると捻れの大きさを大きくすることができる。テープ片９、９、…の向き、相互の間隔、貼合する本数等を調整すれば単調な捻れだけでなく、複雑な形状を有する成形品を成形することもできる。なお、冷却により成形品１１は変形して捻れのある成形品１２に変化するが、熱収縮による変形が発生しているとき、所望の変形が得られた時点でそれ以上変形が進行しないように成形品１２の両端を拘束するようにして冷却するようにしてもよい。そうすると、以後は冷却による変形が進行しにくくなり、捻れの大きさは所望の大きさにすることができる。 The method for molding a twisted molded product according to the present embodiment can be variously modified. For example, a reinforcing fiber tape made of glass fiber can be used as the reinforcing fiber tape. The arrangement of the tape pieces 9, 9, ... Can also be modified. For example, the tape pieces 9, 9, ... Have been described so as to be bonded only to one surface of the molded product 11, but may also be bonded to the other surface, that is, the back surface side. Then, the magnitude of the twist can be increased. By adjusting the orientation of the tape pieces 9, 9, ..., the distance between them, the number of tape pieces to be bonded, and the like, it is possible to mold not only a monotonous twist but also a molded product having a complicated shape. The molded product 11 is deformed and changed to a twisted molded product 12 by cooling, but when the deformation due to heat shrinkage occurs, the deformation does not proceed any further when the desired deformation is obtained. Both ends of the molded product 12 may be constrained to be cooled. Then, after that, the deformation due to cooling is less likely to proceed, and the size of the twist can be set to a desired size.

１ 成形用金型 ３ 上金型
４ 下金型 ６ 凹部
９ テープ片 １１ 成形品
１２ 捻れのある成形品
Ｒ ロール Ｔ 強化繊維テープ 1 Mold for molding 3 Upper mold 4 Lower mold 6 Recess 9 Tape piece 11 Molded product 12 Twisted molded product R roll T Reinforced fiber tape

Claims (1)

長方形状の板状を呈する凹部からなるキャビティを備えた金型を使用して、インサート成形により成形品を得る成形方法であって、
長手方向に配向した強化繊維が樹脂によってバインドされている強化繊維テープを所定幅、所定長さで切断して得た複数本のテープ片をインサート品とし、
前記キャビティに前記複数本のテープ片を互いに間隔を空けるように、かつ前記長方形の長手方向に対して所定の角度傾けた状態でインサートし、
該金型に樹脂を射出して複数本のテープ片が貼合された成形品を得、
樹脂が完全に冷却固化する前に前記成形品を前記金型から取り出して冷却させ、強化繊維テープと樹脂の熱膨張率の違いにより前記成形品に変形が生じるようにすることを特徴とする、捻れのある成形品の成形方法。 A molding method for obtaining a molded product by insert molding using a mold having a cavity composed of concave portions having a rectangular plate shape.
A plurality of tape pieces obtained by cutting a reinforcing fiber tape in which reinforcing fibers oriented in the longitudinal direction are bound by a resin with a predetermined width and a predetermined length are used as insert products.
The plurality of tape pieces are inserted into the cavity so as to be spaced apart from each other and at a predetermined angle with respect to the longitudinal direction of the rectangle.
A resin is injected into the mold to obtain a molded product in which a plurality of tape pieces are bonded together.
The molded product is taken out from the mold and cooled before the resin is completely cooled and solidified so that the molded product is deformed due to the difference in the coefficient of thermal expansion between the reinforcing fiber tape and the resin. A method for molding a twisted molded product.
JP2020050374A 2020-03-20 2020-03-20 Molding method for molding twisted resin molded products Active JP6880268B1 (en)