JP6870919B2 - Male hook-and-loop fastener and ceiling structure using it - Google Patents
Male hook-and-loop fastener and ceiling structure using it Download PDFInfo
- Publication number
- JP6870919B2 JP6870919B2 JP2016070535A JP2016070535A JP6870919B2 JP 6870919 B2 JP6870919 B2 JP 6870919B2 JP 2016070535 A JP2016070535 A JP 2016070535A JP 2016070535 A JP2016070535 A JP 2016070535A JP 6870919 B2 JP6870919 B2 JP 6870919B2
- Authority
- JP
- Japan
- Prior art keywords
- male
- engaging
- loop fastener
- hook
- engaging element
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、雄型面ファスナー、より具体的には、係合相手を傷付けにくい雄型面ファスナー及びそれを用いた天井構造体に関する。 The present invention relates to a male hook-and-loop fastener, more specifically, a male hook-and-loop fastener that does not easily damage an engaging partner, and a ceiling structure using the male hook-and-loop fastener.
従来から、物体の表面に対象物を取り付ける手段の一つとして、物体と対象物のいずれか一方の表面にフック状係合素子を有する雄型面ファスナーを固定するとともに、もう一方の表面にループ状係合素子を有するループ面ファスナーを固定し、そして両方の面ファスナーを重ね合わせて両方の係合素子を係合させることにより、物体の表面に対象物を取り付ける方法が用いられている。 Conventionally, as one of the means for attaching an object to the surface of an object, a male hook-and-loop fastener having a hook-shaped engaging element is fixed to the surface of either the object or the object, and a loop is formed on the other surface. A method is used in which an object is attached to the surface of an object by fixing a loop hook-and-loop fastener having a shape engaging element and then overlapping both hook-and-loop fasteners to engage both engaging elements.
このような面ファスナーを表面に取り付ける際の作業として、まず物体の表面に一方の面ファスナーを固定するとともに対象物の表面にもう一方の面ファスナーを固定し、そして両面ファスナーの表面を重ね合わせて押さえつけて係合させて取り付ける方法が行われる。この際に対象物が所定の位置に正確に取り付けられることとなるか否かを確認するために、位置合わせと称して、面ファスナーを固定した対象物を該物体の面ファスナーに接する程度の距離まで近づけ、位置合わせが行われる。 As a work to attach such a hook-and-loop fastener to the surface, first fix one hook-and-loop fastener to the surface of the object, fix the other hook-and-loop fastener to the surface of the object, and then superimpose the surfaces of the double-sided fasteners. A method of pressing and engaging with each other is performed. At this time, in order to confirm whether or not the object is accurately attached to the predetermined position, it is called alignment, and the distance is such that the object to which the surface fastener is fixed is in contact with the surface fastener of the object. The alignment is performed.
しかしながら、従来の面ファスナーの場合には、位置合わせをするために両方の面ファスナーを軽く接触させただけで不要な係合が生じて、正確な位置合わせができない。このような不要な係合が生じた場合、面ファスナーの不要な係合を外して、位置合わせ作業を繰り返す必要がある。また、不要な係合が生じることを避けるために、両方の面ファスナーを近づけて面ファスナーの位置合わせを行う作業を省略して、面ファスナーを物体や対象物の表面の適当な場所に直接強固に取り付けた場合（すなわち位置合わせを省略して直接本止めを実施する場合）には、対象物の取り付け位置が正確な位置からずれていることがあり、これにより不具合な状況となる。そして、不要な係合を外す際に、新たな不要な係合が生じたり、対象物が損なわれたりすることも場合によっては生じることとなる。 However, in the case of the conventional hook-and-loop fastener, it is not possible to perform accurate alignment because unnecessary engagement occurs only by lightly contacting both hook-and-loop fasteners for alignment. When such unnecessary engagement occurs, it is necessary to disengage the unnecessary engagement of the hook-and-loop fastener and repeat the alignment work. Also, in order to avoid unnecessary engagement, the work of bringing both hook-and-loop fasteners close to each other to align the hook-and-loop fasteners is omitted, and the hook-and-loop fasteners are directly strengthened to an appropriate place on the surface of an object or object. When it is attached to (that is, when the main stop is performed directly without alignment), the attachment position of the object may deviate from the correct position, which causes a malfunction. Then, when the unnecessary engagement is disengaged, a new unnecessary engagement may occur or the object may be damaged in some cases.
さらに、特に対象物が大きな形状である場合、例えば家屋の天井材や壁材、あるいは自動車における天井材やトランクルームの壁面材や床材等の場合には、不要な係合を外し、再度位置合わせを行う作業を繰り返すことは多大な労力と手間を必要とし、さらに一定速度で流れる自動車の生産ラインにおいて、一定時間内に天井材や床材等を取り付ける作業を行わなければならない場合には、位置合わせに失敗した場合には生産ラインを止めたりする必要が生じ、位置合わせを正確にかつ速やかに行うことが極めて重要となる。 Furthermore, especially when the object has a large shape, for example, in the case of a ceiling material or wall material of a house, or a wall material or floor material of a ceiling material or a trunk room in an automobile, unnecessary engagement is removed and realignment is performed. It takes a lot of labor and effort to repeat the work of performing the above, and when it is necessary to install the ceiling material, floor material, etc. within a certain period of time in the production line of an automobile that flows at a constant speed, the position If the alignment fails, it will be necessary to stop the production line, and it is extremely important to perform the alignment accurately and promptly.
このような問題点を解消するためには、位置合わせ時に単に両方の面ファスナーを重ね合わせただけでは不要な係合が生じないことが必要であり、このような要求を満足する仮止め機能に優れた雄型面ファスナーが報告されている（特許文献１）。 In order to solve such a problem, it is necessary that unnecessary engagement does not occur simply by superimposing both hook-and-loop fasteners at the time of alignment, and a temporary fixing function that satisfies such a requirement is provided. An excellent male hook-and-loop fastener has been reported (Patent Document 1).
上記特許文献１には、仮止め機能に優れた面ファスナーとして、Ｄ／Ｈが０．３５〜０．７５で、かつ係合素子の基板被覆率が２５〜４５％を満足している雄型成形面ファスナーが記載されている。この雄型成形面ファスナーは、仮止め機能の点では優れているが、一方で係合用突起が厚く強固であることから、係合を剥離する際に、係合相手のループ面ファスナーのループ状係合素子を切断し易い。そのため、係合・剥離を繰り返すと、係合相手のループ面ファスナーの係合力を損なうおそれがあった。 According to Patent Document 1, as a surface fastener having an excellent temporary fixing function, a male type having a D / H of 0.35 to 0.75 and a substrate coverage of an engaging element of 25 to 45% is satisfied. Molded hook-and-loop fasteners are described. This male molded surface fastener is excellent in terms of temporary fixing function, but on the other hand, since the engaging protrusion is thick and strong, when the engagement is disengaged, the loop surface fastener of the engaging partner is looped. Easy to cut the engaging element. Therefore, if the engagement and disengagement are repeated, the engagement force of the loop surface fastener of the engagement partner may be impaired.
本発明は、上記事情に鑑みてなされたものであって、係合相手のループ面ファスナーを傷つけにくい面ファスナーを提供することを目的とする。そして、本発明者らは、雄型成形面ファスナーの係合用突起を途中で複数の小突起に分割することにより、係合用突起が撓み易くなることを見出した。 The present invention has been made in view of the above circumstances, and an object of the present invention is to provide a hook-and-loop fastener that does not easily damage the loop surface fastener of the engaging partner. Then, the present inventors have found that the engaging protrusions are easily bent by dividing the engaging protrusions of the male molded surface fastener into a plurality of small protrusions on the way.
一方、係合用突起を途中で複数の小突起に分割するという技術については、例えば、上記特許文献２記載のファスナー部材が知られている。しかし、特許文献２記載のファスナー部材においては、複数の太い係合用突起が異なる方向に突出していることから、ループ状係合素子は２本以上の係合用突起に同時に係合することは殆どない。したがって係合後の面ファスナー間でずれを生じることを防ぐことができず、正確な位置にしっかりと固定できないという難点があった。本発明は、そのような問題をも解決するものである。 On the other hand, as a technique for dividing the engaging protrusion into a plurality of small protrusions on the way, for example, the fastener member described in Patent Document 2 is known. However, in the fastener member described in Patent Document 2, since a plurality of thick engaging protrusions project in different directions, the loop-shaped engaging element rarely engages with two or more engaging protrusions at the same time. .. Therefore, it is not possible to prevent the surface fasteners from being displaced from each other after engagement, and there is a problem that the surface fasteners cannot be firmly fixed at an accurate position. The present invention also solves such a problem.
すなわち、本発明の一態様に係る雄型面ファスナーは、樹脂からなる基板の表面に立設する多数の雄型係合素子を有し、該雄型係合素子が、該樹脂基板から立ち上がるステムと該ステムからサイドに突出する係合用突起を有する雄型面ファスナーであって、前記係合用突起が、ステムから離れる方向に伸び、かつ、ステムの高さ方向に直交する方向に並ぶ複数の小突起に分岐しており、さらに、前記分岐した複数の小突起同士が平行であることを特徴とする。 That is, the male hook-and-loop fastener according to one aspect of the present invention has a large number of male engaging elements erected on the surface of a substrate made of resin, and the male engaging elements stand up from the resin substrate. A male hook-and-loop fastener having an engaging protrusion protruding from the stem to the side, wherein the engaging protrusion extends in a direction away from the stem and is arranged in a direction orthogonal to the height direction of the stem. It is characterized in that it is branched into protrusions, and that the plurality of branched small protrusions are parallel to each other.
また、前記雄型面ファスナーにおいて、前記基板から前記雄型係合素子の先端までの高さ（Ｈ）に対する、前記雄型係合素子先端から前記係合用突起の下端部までの長さ（Ｄ）の比（Ｄ／Ｈ）が０．３０〜０．６０であることが好ましい。 Further, in the male hook-and-loop fastener, the length (D) from the tip of the male engaging element to the lower end of the engaging protrusion with respect to the height (H) from the substrate to the tip of the male engaging element. ) Is preferably 0.30 to 0.60.
さらに、前記雄型面ファスナーにおいて、前記係合用突起が、係合用突起の付根から係合用突起の突出長の１／５〜１／２の部分で複数の小突起に分岐していることが好ましい。 Further, in the male hook-and-loop fastener, it is preferable that the engaging protrusion is branched into a plurality of small protrusions from the base of the engaging protrusion at a portion of 1/5 to 1/2 of the protruding length of the engaging protrusion. ..
また、前記雄型面ファスナーにおいて、前記分岐した複数の小突起の間に楔形切目が存在していることが好ましい。 Further, in the male hook-and-loop fastener, it is preferable that a wedge-shaped cut exists between the plurality of branched small protrusions.
さらに、前記分岐した複数の小突起が２本または３本の小突起であることが好ましい。 Further, it is preferable that the plurality of branched small protrusions are two or three small protrusions.
また、前記雄型面ファスナーにおいて、前記雄型係合素子が、基板から遠ざかる方向に突出するくっつき防止用突起を係合用突起より上に有していることが好ましい。 Further, in the male hook-and-loop fastener, it is preferable that the male engaging element has a protrusion for preventing sticking protruding in a direction away from the substrate above the engaging projection.
さらに、前記雄型面ファスナーにおいて、前記雄型係合素子の高さが１．３〜３．０ｍｍの範囲であることが好ましい。 Further, in the male hook-and-loop fastener, the height of the male engaging element is preferably in the range of 1.3 to 3.0 mm.
また、前記雄型面ファスナーにおいて、前記雄型係合素子の基板被覆率が３０〜４５％であることが好ましい。 Further, in the male hook-and-loop fastener, the substrate coverage of the male engaging element is preferably 30 to 45%.
また、前記雄型面ファスナーにおいて、前記小突起が先端に行くほど細くなっていることが好ましい。 Further, in the male hook-and-loop fastener, it is preferable that the small protrusions become thinner toward the tip.
さらに、前記雄型面ファスナーにおいて、前記小突起の断面形状が矩形であり、かつ、先端部に行くほど厚さおよび幅が薄くなっていることが好ましい。 Further, in the male hook-and-loop fastener, it is preferable that the cross-sectional shape of the small protrusion is rectangular, and the thickness and width become thinner toward the tip portion.
また、前記雄型面ファスナーにおいて、前記雄型係合素子が基板上に列をなして並んでおり、各雄型係合素子の係合用突起は列方向と交わる方向に突出しているが列方向と平行な方向には突出していないことが好ましい。 Further, in the male hook-and-loop fastener, the male engaging elements are arranged in a row on the substrate, and the engaging protrusions of the male engaging elements project in the direction intersecting the row direction, but in the row direction. It is preferable that it does not protrude in the direction parallel to.
さらに、前記雄型面ファスナーにおいて、雄型面ファスナーの基板および雄型係合素子を形成する樹脂がポリアミド系の樹脂であることが好ましい。 Further, in the male hook-and-loop fastener, it is preferable that the resin forming the substrate of the male hook-and-loop fastener and the male engaging element is a polyamide-based resin.
また、本発明の他の態様に係る天井構造体は、天井基材に天井材が固定された構造体であって、天井基材と天井材のいずれか一方に前記雄型面ファスナーが固定され、他方にループ状係合素子を有する雌型面ファスナーが固定されており、両者が係合することにより天井材が天井基材に取り付けられていることを特徴とする。 Further, the ceiling structure according to another aspect of the present invention is a structure in which a ceiling material is fixed to a ceiling base material, and the male hook-and-loop fastener is fixed to either the ceiling base material or the ceiling material. On the other hand, a female hook-and-loop fastener having a loop-shaped engaging element is fixed, and the ceiling material is attached to the ceiling base material by engaging the two.
本発明の雄型面ファスナーによれば、係合を剥離する際にループ状係合素子を切断することなく、係合用突起が容易に反り返って係合が外れることとなり、その結果、ループ状係合素子を切断することなく係合を剥離できる。 According to the male hook-and-loop fastener of the present invention, the engaging protrusion easily warps and disengages without breaking the loop-shaped engaging element when the engagement is disengaged, and as a result, the loop-shaped engaging element is engaged. The engagement can be disengaged without cutting the coupling element.
以下、図面等を用いて本発明の好適な実施形態を具体的に説明する。 Hereinafter, preferred embodiments of the present invention will be specifically described with reference to the drawings and the like.
本実施形態の雄型面ファスナーは、樹脂からなる基板の表面に立設する多数の雄型係合素子を有し、該雄型係合素子が、該樹脂基板から立ち上がるステムと該ステムからサイドに突出する係合用突起を有する雄型面ファスナーであって、前記係合用突起が、ステムから離れる方向に伸び、かつ、ステムの高さ方向に直交する方向に並ぶ複数の小突起に分岐しており、さらに、前記分岐した複数の小突起同士が平行であることを特徴とする。 The male hook-and-loop fastener of the present embodiment has a large number of male engaging elements erected on the surface of a substrate made of resin, and the male engaging elements stand up from the resin substrate and side from the stem. A male hook-and-loop fastener having an engaging protrusion protruding from the stem, and the engaging protrusion extends in a direction away from the stem and branches into a plurality of small protrusions arranged in a direction orthogonal to the height direction of the stem. Further, it is characterized in that the plurality of branched small protrusions are parallel to each other.
このような構成によれば、係合を剥離する際にループ状係合素子を切断することなく、係合用突起が容易に反り返って係合が外れることとなり、その結果、ループ状係合素子を切断することなく係合を剥離できると考えられる。すなわち、本実施形態の雄型面ファスナーは係合相手を傷付けにくい雄型面ファスナーである。 According to such a configuration, the engaging protrusion easily warps and disengages without cutting the loop-shaped engaging element when the engagement is disengaged, and as a result, the loop-shaped engaging element is disengaged. It is believed that the engagement can be disengaged without disconnection. That is, the male surface fastener of the present embodiment is a male surface fastener that does not easily damage the engaging partner.
さらに、上記構成によれば、係合用突起が複数の小突起に平行に並んで分かれていることから、係合したループ状係合素子は、１本の小突起に係合しているものと、２本以上の小突起に係合しているものが混在していることとなる。その結果、ループ状係合素子の一部は２本以上の小突起に係合することになるため、雄型面ファスナーとループ面ファスナーとの間で動き得る余裕が少なくなり、係合後の面ファスナー間でずれを生じることが少なく、正確な位置にしっかりと固定できるという利点もある。 Further, according to the above configuration, since the engaging protrusions are arranged and separated in parallel with the plurality of small protrusions, the engaged loop-shaped engaging element is assumed to be engaged with one small protrusion. Two or more small protrusions that are engaged with each other are mixed. As a result, a part of the loop-shaped engaging element engages with two or more small protrusions, so that there is less room for movement between the male hook-and-loop fastener and the loop hook-and-loop fastener, and after engagement, there is less room for movement. There is also the advantage that there is little deviation between the hook-and-loop fasteners and it can be firmly fixed in the correct position.
本実施形態の雄型面ファスナーを構成する雄型係合素子としては、例えば、図１に示すような係合素子が挙げられる。 Examples of the male engaging element constituting the male hook-and-loop fastener of the present embodiment include an engaging element as shown in FIG.
図中、Ｂが面ファスナーの樹脂からなる基板、Ｅが雄型係合素子であり、基板（Ｂ）の上に雄型係合素子（Ｅ）がほぼ垂直に立設されている。そして、雄型係合素子（Ｅ）は、基板から立ち上がるステム（Ｓ）とその上部でステムからサイドに突出する係合用突起（Ｔ）を有している。該係合用突起（Ｔ）が、ステムから離れる方向に伸び、かつ、ステムの高さ方向に直交する方向に並ぶ複数の小突起に分岐しており（図１では２本の突起に分かれている）、さらに、分岐した複数の小突起同士は平行になっている。そして、図２の雄型係合素子（Ｅ）の場合にはステムの先端部にくっつき防止用突起（Ｍ）を有している。 In the figure, B is a substrate made of resin for a hook-and-loop fastener, E is a male engaging element, and the male engaging element (E) is erected substantially vertically on the substrate (B). The male engaging element (E) has a stem (S) rising from the substrate and an engaging projection (T) protruding sideways from the stem at the upper portion thereof. The engaging protrusion (T) extends in a direction away from the stem and is branched into a plurality of small protrusions arranged in a direction orthogonal to the height direction of the stem (in FIG. 1, it is divided into two protrusions). ), Furthermore, the plurality of branched small protrusions are parallel to each other. The male engaging element (E) shown in FIG. 2 has a protrusion (M) for preventing sticking at the tip of the stem.
なお、雄型係合素子（Ｅ）において、係合用突起（Ｔ）および同突起の根元より上のステム部分と上記くっつき防止用突起（Ｍ）を合わせて係合素子のヘッド部と称することがある。したがって雄型係合素子は、サイドに係合用突起を有していないステム部と同ステム部より上に存在しているヘッド部からなると言い換えることもできる。 In the male engaging element (E), the engaging protrusion (T), the stem portion above the root of the protrusion, and the sticking prevention protrusion (M) may be collectively referred to as the head portion of the engaging element. is there. Therefore, it can be said that the male engaging element is composed of a stem portion having no engaging protrusion on the side and a head portion existing above the stem portion.
好ましい実施態様において、前記係合用突起が、係合用突起の付根から係合用突起の突出長（図１および図２に示すＶ）の１／５〜１／２の部分で複数の小突起に分岐していることが望ましい。そのような構成にすることにより、係合用突起を作成しやすくなり、さらに、係合用突起が折れることを防ぐことができると考えられる。より好ましくは、１／４〜１／３の部分で複数の小突起に分岐していることがより望ましい。 In a preferred embodiment, the engaging protrusion is branched into a plurality of small protrusions from the base of the engaging protrusion at a portion of 1/5 to 1/2 of the protrusion length (V shown in FIGS. 1 and 2) of the engaging protrusion. It is desirable to do. It is considered that such a configuration makes it easier to create the engaging protrusions and further prevents the engaging protrusions from breaking. More preferably, it is more desirable that the portion is branched into a plurality of small protrusions at a portion of 1/4 to 1/3.
また、分岐した前記小突起の間には、楔形切目が存在していることが好ましい。それにより、係合用突起が撓みやすくなり、係合を剥離する際にループ状係合素子を傷めにくいといった利点がある。 Further, it is preferable that a wedge-shaped cut is present between the branched small protrusions. As a result, the engaging protrusions are easily bent, and there is an advantage that the loop-shaped engaging element is not easily damaged when the engagement is disengaged.
さらに、前記分岐した複数の小突起が２本または３本の小突起であることが好ましい。それにより、より位置ズレしにくく、所定の位置に固定できるという利点が得られる。より好ましくは、小突起の折れ対策という観点から小突起が２本に分岐していることが望ましい。 Further, it is preferable that the plurality of branched small protrusions are two or three small protrusions. As a result, there is an advantage that the position is less likely to be displaced and the position can be fixed at a predetermined position. More preferably, it is desirable that the small protrusions are branched into two from the viewpoint of preventing the small protrusions from breaking.
前記分岐した小突起の形状は、先端にいくほど細くなっていることが好ましい。それにより、可撓性が良くなりループ係合素子を傷めにくくなるといった利点がある。 It is preferable that the shape of the branched small protrusions becomes thinner toward the tip. As a result, there is an advantage that the flexibility is improved and the loop engaging element is less likely to be damaged.
また、同様の理由により、前記小突起の断面形状が矩形であり、先端にいくほど厚みおよび幅が小さくなっていることが好ましい。 Further, for the same reason, it is preferable that the cross-sectional shape of the small protrusion is rectangular, and the thickness and width become smaller toward the tip.
本実施形態に好適に用いられる雄型成形面ファスナーでは、通常、このような係合素子が複数個、縦方向（図１および２に示すＹ方向）に一定間隔をおいて列をなして並んでおり（すなわち係合用突起を突出していない面方向に列をなして並んでおり）、そのような列が横方向（図１および２で示すＸ方向）にも平行に存在している。 In the male molded surface fastener preferably used in the present embodiment, a plurality of such engaging elements are usually arranged in a row at regular intervals in the vertical direction (Y direction shown in FIGS. 1 and 2). (Ie, they are lined up in rows in the plane direction where the engaging protrusions do not protrude), and such rows also exist in parallel in the lateral direction (X direction shown in FIGS. 1 and 2).
雄型係合素子（Ｅ）は、ステム（Ｓ）と同ステムからサイドに突出する係合用突起（Ｔ）を有しており、通常はステムから両サイドに対象に係合用突起（Ｔ）が突出しているのが好ましい。ステム（Ｓ）は、通常、基板（Ｂ）から直立している。そして、係合用突起（Ｔ）は係合力を高めるために、基板に平行に、あるいは図１または２に示すように、平行より先端部が基板側に下がるような方向に突出している。 The male engaging element (E) has a stem (S) and an engaging projection (T) protruding from the stem to the side, and usually, the engaging projection (T) is symmetrically provided on both sides from the stem. It is preferable that it protrudes. The stem (S) is usually upright from the substrate (B). Then, in order to increase the engaging force, the engaging protrusion (T) protrudes parallel to the substrate or in a direction in which the tip portion is lowered toward the substrate from the parallel as shown in FIG. 1 or 2.
好ましい実施形態においては、前記係合素子が、図３に示すように、各雄型係合素子の係合用突起は列方向と交わる方向に突出しているが列方向と平行な方向には突出していないことが望ましい。これは、すなわち、隣り合う係合素子が横方向に同列に存在していない、つまり、互い違いにずれて並んでいることを意味する。横方向にも同列に存在する場合、隣り合う係合素子の係合用突起（Ｔ）が近接しすぎてその間にスペースが生まれず、ループ面ファスナーのループがその間をうまく通らないおそれがある。 In a preferred embodiment, as shown in FIG. 3, the engaging elements of each male engaging element project in a direction intersecting the row direction, but project in a direction parallel to the row direction. It is desirable not to. This means that adjacent engaging elements do not exist in the same row in the lateral direction, that is, they are staggered and aligned. If they are also present in the same row in the lateral direction, the engaging projections (T) of adjacent engaging elements may be too close to each other to create a space between them, and the loop of the loop hook-and-loop fastener may not pass between them well.
基板（Ｂ）および雄型係合素子（Ｅ）はともにプラスチックからなり、基板（Ｂ）と雄型係合素子（Ｅ）は別々の樹脂から形成されていても良いが、生産性の点から通常は同一の樹脂から構成されている。 The substrate (B) and the male engaging element (E) are both made of plastic, and the substrate (B) and the male engaging element (E) may be formed of different resins, but from the viewpoint of productivity. It is usually composed of the same resin.
用いられる樹脂に関しては、特に限定されず、通常の射出成形に用いられる樹脂、例えば、ＡＢＳ（アクリロニトリル・ブタジエン・スチレン）、ＰＣ（ポリカーボネート）、ＰＡ（ポリアミド）、ＰＯＭ（ポリオキシメチレン）、ＰＰ（ポリプロピレン）、ＰＢＴ（ポリブチレンテレフタレート）等の合成樹脂、ナイロン６、ナイロン６６等のポリアミド系樹脂が挙げられる。中でも、強度と耐熱性及び耐衝撃性という観点からポリアミド系樹脂が好ましく用いられる。 The resin used is not particularly limited, and resins used for ordinary injection molding, for example, ABS (acrylonitrile butadiene styrene), PC (polyamide), PA (polyamide), POM (polyoxymethylene), PP ( Examples thereof include synthetic resins such as polypropylene) and PBT (polybutylene terephthalate), and polyamide resins such as nylon 6 and nylon 66. Among them, a polyamide resin is preferably used from the viewpoint of strength, heat resistance and impact resistance.
さらに好ましい実施形態では、前記係合素子は、係合素子の高さ（Ｈ）に対する係合素子（Ｅ）の最頂部から係合用突起（Ｔ）の下端部までの長さ（Ｄ）の割合（Ｄ／Ｈ）が０．３０〜０．６０となっていることが望ましい。このような構成とすることにより、単に重ね合わせただけで係合が生じて、位置合わせすることが極めて困難である従来の雄型成形面ファスナーを改良し、位置合わせ時には強固な係合が殆ど生じることがなく、本止めした後には高い係合力が得られる雄型成形面ファスナーを提供することができる。従来一般に知られている成形面ファスナーの係合素子の場合、その最頂部から係合用突起の下端部までの長さの割合（Ｄ／Ｈ）は、概ね０．１５〜０．２５の範囲である。 In a more preferred embodiment, the engaging element is the ratio of the length (D) from the top of the engaging element (E) to the lower end of the engaging projection (T) with respect to the height (H) of the engaging element. It is desirable that (D / H) is 0.30 to 0.60. With such a configuration, the conventional male molded hook-and-loop fastener, which is extremely difficult to align due to engagement caused by simply overlapping, has been improved, and most of the strong engagement occurs at the time of alignment. It is possible to provide a male molded hook-and-loop fastener that does not occur and a high engaging force can be obtained after the final fastening. In the case of a conventionally known engaging element of a molded surface fastener, the ratio (D / H) of the length from the uppermost portion to the lower end portion of the engaging protrusion is generally in the range of 0.15 to 0.25. is there.
なお、係合素子の高さが極めて低い成形面ファスナーの場合には、（Ｄ／Ｈ）の値を小さくすると係合用突起が必然的に薄くなり、それにより係合用突起が簡単に曲がることとなり、必要な係合力が得られないことから、（Ｄ／Ｈ）の値を高くしたものも存在するが、係合素子の高さ（Ｈ）が１．２ｍｍを超えるような係合素子の場合には、０．２０〜０．３０の範囲が採用されており、（Ｄ／Ｈ）が０．４０を超えるようなものは知られていない。 In the case of a molded hook-and-loop fastener in which the height of the engaging element is extremely low, if the value of (D / H) is reduced, the engaging protrusion is inevitably thinned, whereby the engaging protrusion is easily bent. Since the required engaging force cannot be obtained, there are some that have a higher value of (D / H), but in the case of an engaging element in which the height (H) of the engaging element exceeds 1.2 mm. The range of 0.20 to 0.30 is adopted, and there is no known one in which (D / H) exceeds 0.40.
図２は、本実施形態に用いられる雄型成形面ファスナーの好適な一例であるが、同図の係合素子では、この（Ｄ／Ｈ）の値を高くするために、係合素子の頂部にくっつき防止用突起（Ｍ）を設けている。もちろん、くっつき防止用突起は、係合素子の頂部に設けられている必要はなく、係合用突起部分（Ｔ）から、基板から遠ざかる方向に突出していてもよい。さらに、くっつき防止用突起は１本の係合素子に１個である必要はなく、複数個存在していてもよい。 FIG. 2 is a preferable example of the male molded surface fastener used in the present embodiment, but in the engaging element of the figure, in order to increase the value of this (D / H), the top of the engaging element is used. A protrusion (M) for preventing sticking is provided. Of course, the sticking prevention protrusion does not need to be provided on the top of the engaging element, and may protrude from the engaging protrusion portion (T) in a direction away from the substrate. Further, the number of protrusions for preventing sticking does not have to be one for one engaging element, and a plurality of protrusions may be present.
また、くっつき防止用突起は基板面に対して垂直である必要はなく、基板から遠ざかる方向に突出していればよい。さらにくっつき防止用突起は、各係合素子に１個以上存在しているのが好ましいが、係合素子の係合突起方向に隣り合う係合素子２〜３個に１個の割合であってもよい。また、このように係合素子の頂部にくっつき防止用突起を設けたものの他に、Ｄ／Ｈの値を高くするために、係合素子のヘッド部を極めて厚くしたものでも良い。 Further, the sticking prevention protrusion does not have to be perpendicular to the substrate surface, and may protrude in the direction away from the substrate. Further, it is preferable that one or more protrusions for preventing sticking are present in each engaging element, but the ratio is one in every two or three engaging elements adjacent to each other in the engaging protrusion direction of the engaging element. May be good. Further, in addition to the one provided with the protrusion for preventing sticking on the top of the engaging element in this way, the head portion of the engaging element may be made extremely thick in order to increase the D / H value.
くっつき防止用突起の高さあるいは係合素子のヘッド部の厚さとしては、上記（Ｄ／Ｈ）が０．３０〜０．６０の範囲となるような値である。すなわち、（Ｄ／Ｈ）が０．３０〜０．６０の値となるように、ヘッド部の上にくっつき防止用突起を設けるか、あるいはヘッド部の厚さを厚くすればよい。（Ｄ／Ｈ）の値が０．３０未満の場合には、位置合わせ時に係合しやすい場合があり、逆に０．６０を超える場合には、本止め後においても強固な係合が妨げられ、所期の係合力が得られない場合がある。好ましくは、０．３５〜０．５５の範囲である。 The height of the protrusion for preventing sticking or the thickness of the head portion of the engaging element is such that the above (D / H) is in the range of 0.30 to 0.60. That is, a protrusion for preventing sticking may be provided on the head portion or the thickness of the head portion may be increased so that (D / H) becomes a value of 0.30 to 0.60. If the value of (D / H) is less than 0.30, it may be easy to engage at the time of alignment, and conversely if it exceeds 0.60, strong engagement is hindered even after the final stop. In some cases, the desired engaging force may not be obtained. It is preferably in the range of 0.35 to 0.55.
くっつき防止用突起を設ける場合には、くっつき防止用突起の先端部が尖っていると、面ファスナーの手触り感が悪くなるため、くっつき防止用突起は、図２に示すようにヘッド部上に丸みを帯びた形状で存在しているのが好ましい。なお、くっつき防止用突起は、ステムやヘッド部と同一の樹脂で構成されているのが好ましい。 When the sticking prevention protrusion is provided, if the tip of the sticking prevention protrusion is sharp, the feel of the hook-and-loop fastener becomes poor. Therefore, the sticking prevention protrusion is rounded on the head portion as shown in FIG. It is preferable that the shape is tinged with. The sticking prevention protrusion is preferably made of the same resin as the stem and the head portion.
また、係合用突起がステムの両サイドに複数本上下方向に存在している場合には、本実施形態で言う、係合素子（Ｅ）の最頂部から係合用突起（Ｔ）の下端部までの長さ（Ｄ）は、もっとも上部に存在する係合用突起が対象となる。 When a plurality of engaging protrusions are present on both sides of the stem in the vertical direction, from the uppermost portion of the engaging element (E) to the lower end portion of the engaging protrusion (T) referred to in the present embodiment. The length (D) of is targeted at the engaging protrusion existing at the uppermost part.
上記したように、ステムの高さ（Ｈ）に対する係合素子（Ｅ）の最頂部から係合用突起（Ｔ）の下端部までの長さ（Ｄ）の割合（Ｄ／Ｈ）が上記範囲であることが、位置合わせ時の無用な係合発生を阻止する上で好ましい。 As described above, the ratio (D / H) of the length (D) from the top of the engaging element (E) to the lower end of the engaging protrusion (T) with respect to the height (H) of the stem is within the above range. It is preferable in order to prevent unnecessary engagement from occurring during alignment.
さらに、好ましい実施形態として、係合素子の基板被覆率が３０〜４５％の範囲内であることが望ましい。従来、一般に知られている雄型成形面ファスナーの場合には、係合素子の基板被覆率が１５〜２２％であることを考慮すると、３０〜４５％という値は、極めて高いと言える。係合素子の基板被覆率が３０％未満の場合には、位置合わせ時に係合が生じ易い。一方、４５％を越えると本止め後においても強固な係合が生じ難い。より好ましくは、２７〜４２％の範囲であり、さらに好ましくは２８〜４０％の範囲である。 Further, as a preferred embodiment, it is desirable that the substrate coverage of the engaging element is in the range of 30 to 45%. In the case of a conventionally known male molded surface fastener, a value of 30 to 45% can be said to be extremely high, considering that the substrate coverage of the engaging element is 15 to 22%. When the substrate coverage of the engaging element is less than 30%, engagement is likely to occur during alignment. On the other hand, if it exceeds 45%, strong engagement is unlikely to occur even after the final stop. More preferably, it is in the range of 27 to 42%, and even more preferably, it is in the range of 28 to 40%.
なお、本実施形態でいう係合素子の基板被覆率とは、雄型係合素子が立設されている基板部分の面積に対する雄型係合素子のヘッド部を上部から見た面積の割合で、具体的には、雄型係合素子が連続して存在する部分を上面から光学顕微鏡で写真を撮り、同写真から５０個の雄型係合素子が存在している任意の基板部を囲み、その囲った部分の面積（ｓ１）と、同部分に存在する５０個の雄型係合素子ヘッド部の上面の面積の合計（ｓ２）を求め、［（ｓ２）／（ｓ１）］×１００を算出することにより係合素子の基板被覆率が得られる。 The substrate coverage of the engaging element in the present embodiment is the ratio of the area of the head portion of the male engaging element viewed from above to the area of the substrate portion on which the male engaging element is erected. Specifically, a photograph is taken from the upper surface of a portion where the male engaging elements are continuously present with an optical microscope, and an arbitrary substrate portion in which 50 male engaging elements are present is surrounded from the photograph. , The total area (s2) of the area (s1) of the enclosed portion and the area of the upper surface of the 50 male engaging element head portions existing in the same portion was obtained, and [(s2) / (s1)] × 100 The substrate coverage of the engaging element can be obtained by calculating.
また、雄型係合素子の高さ（Ｈ）としては、１．３〜３．０ｍｍの高さが好ましく、高さが１．３ｍｍ未満の場合には、充分な係合力が得られず、また３．０ｍｍを超える場合には、雄型係合素子が倒れやすくなり、軽い力でループ状係合素子に引っ掛かり易くなり好ましくない。より好ましくは１．５〜２．７ｍｍの範囲、さらに好ましくは１．６〜２．６ｍｍの範囲である。 Further, the height (H) of the male engaging element is preferably 1.3 to 3.0 mm, and if the height is less than 1.3 mm, a sufficient engaging force cannot be obtained. On the other hand, if it exceeds 3.0 mm, the male engaging element tends to fall down and is easily caught by the loop-shaped engaging element with a light force, which is not preferable. It is more preferably in the range of 1.5 to 2.7 mm, still more preferably in the range of 1.6 to 2.6 mm.
また、雄型係合素子の係合用突起と、同突起方向（すなわち図に示すＸ方向）に隣り合う雄型係合素子の係合用突起との間隔は０．６〜２．５ｍｍの範囲が適当であり、０．６ｍｍより狭い場合には、充分な係合力が得られず、また２．５ｍｍより広い場合には、上記した雄型係合素子の基板被覆率を達成することが困難となる。 Further, the distance between the engaging projection of the male engaging element and the engaging projection of the male engaging element adjacent to each other in the same projection direction (that is, the X direction shown in the figure) is in the range of 0.6 to 2.5 mm. It is appropriate, and if it is narrower than 0.6 mm, sufficient engaging force cannot be obtained, and if it is wider than 2.5 mm, it is difficult to achieve the substrate coverage of the male engaging element described above. Become.
さらに本実施形態において係合用突起は、ステムから０．２〜１．０ｍｍ突出しているのが好ましい。すなわち、図１および２に示す係合素子において、Ｖが０．２〜１．０ｍｍであるのが好ましい。０．２ｍｍより突起が低い場合には、充分な係合力が得られず、また０．８ｍｍを超える場合には、係合が強固となり、剥離時に素子やループが破損してしまう。より好ましくは０．３〜０．６ｍｍである。そして、係合用突起は、通常、ステムと同一の樹脂から構成される。 Further, in the present embodiment, the engaging protrusion preferably protrudes from the stem by 0.2 to 1.0 mm. That is, in the engaging elements shown in FIGS. 1 and 2, V is preferably 0.2 to 1.0 mm. If the protrusion is lower than 0.2 mm, a sufficient engaging force cannot be obtained, and if it exceeds 0.8 mm, the engagement becomes strong and the element or loop is damaged at the time of peeling. More preferably, it is 0.3 to 0.6 mm. The engaging protrusions are usually made of the same resin as the stem.
さらに、雄型係合素子の係合素子列方向の厚さ（図２で示すＷ）は、雄型係合素子の高さ（Ｈ）の０．１５〜０．６倍の範囲が好ましい。０．１５倍未満の場合には、雄型係合素子の強度が低くなり充分な係合力が得られず、また０．６倍を超える場合も、ループ状係合素子との係合が困難となり、充分な係合力が得られない。より好ましくは０．１８〜０．５倍の範囲である。 Further, the thickness of the male engaging element in the engaging element row direction (W shown in FIG. 2) is preferably in the range of 0.15 to 0.6 times the height (H) of the male engaging element. If it is less than 0.15 times, the strength of the male engaging element becomes low and sufficient engaging force cannot be obtained, and if it exceeds 0.6 times, it is difficult to engage with the loop-shaped engaging element. Therefore, sufficient engaging force cannot be obtained. More preferably, it is in the range of 0.18 to 0.5 times.
さらに、雄型係合素子のステム部の太さとしては、上記係合素子の係合素子列方向の厚さ（Ｗ）と同一の理由により、基板に平行な面での断面積が０．３〜０．９ｍｍ２の範囲が好ましい。 Further, as the thickness of the stem portion of the male engaging element, the cross-sectional area on the plane parallel to the substrate is 0. For the same reason as the thickness (W) of the engaging element in the engaging element row direction. The range of 3 to 0.9 mm 2 is preferable.
なお、基板（Ｂ）の厚さとしては、特に限定されないが、０．５〜２．５ｍｍの範囲が適切である。また、係合素子密度としては、５〜３０個／ｃｍ２の範囲が好ましく、特に１０〜２０個／ｃｍ２がより好ましい。 The thickness of the substrate (B) is not particularly limited, but a range of 0.5 to 2.5 mm is appropriate. Further, as the engaging element density is preferably in the range of 5 to 30 pieces / cm 2, especially 10 to 20 / cm 2 is more preferable.
次に、このような雄型成形面ファスナーの製造方法について説明する。 Next, a method for manufacturing such a male molded surface fastener will be described.
本実施形態の面ファスナーの製造方法は、特に限定されないが、例えば、射出成形法によって製造することができる。具体的には、本実施形態の雄型成形面ファスナーと同一形状の空間を有する金型へ溶融樹脂液を流して、適度な圧力を加えることによって成形することができる。さらに、係合素子がくっつき防止用突起を有する場合は、基板樹脂シートの表面に多数の直立するステムを有する樹脂板を製造し、ステム先端のみをさらにくっつき防止用突起部用凹みを有する加熱金属板に圧着して溶融させ、ステムをキノコ形状とすると共に、キノコ先端部がくっつき防止用突起部となるように成形する、あるいはキノコの傘部分を厚くする方法等でも製造できる。 The method for manufacturing the surface fastener of the present embodiment is not particularly limited, but can be manufactured by, for example, an injection molding method. Specifically, it can be molded by flowing a molten resin liquid into a mold having a space having the same shape as the male molding surface fastener of the present embodiment and applying an appropriate pressure. Further, when the engaging element has a protrusion for preventing sticking, a resin plate having a large number of upright stems is manufactured on the surface of the substrate resin sheet, and only the tip of the stem is a heated metal having a recess for the protrusion for preventing sticking. It can also be manufactured by crimping it onto a plate and melting it to form a mushroom-shaped stem, and molding it so that the tip of the mushroom becomes a protrusion for preventing sticking, or a method of thickening the umbrella portion of the mushroom.
このように、本発明では、係合を剥離する際にループ状係合素子を切断することなく、係合用突起が容易に反り返って係合が外れることとなり、その結果、ループ状係合素子を切断することなく係合を剥離できる雄型成形面ファスナーを提供する。さらに、本発明では、係合後の面ファスナー間でずれを生じることが少なく、正確な位置にしっかりと固定できるという利点もある。 As described above, in the present invention, the engaging projection is easily warped and disengaged without breaking the loop-shaped engaging element when the engagement is disengaged, and as a result, the loop-shaped engaging element is provided. Provided is a male molded hook-and-loop fastener that can be disengaged without cutting. Further, the present invention has an advantage that the surface fasteners after engagement are less likely to be displaced from each other and can be firmly fixed at an accurate position.
このような雄型成形面ファスナーと対になって用いられる雌型面ファスナーとしては、従来の一般的な雌型面ファスナーを使用することができる。本発明の雄型成形面ファスナーと組み合わせて使用する限り、従来一般的に用いられている雄型面ファスナーと雌型面ファスナーの組み合わせと比べて、上述した効果がはるかに優れている。 As the female type surface fastener used in combination with such a male type surface fastener, a conventional general female type surface fastener can be used. As long as it is used in combination with the male molded surface fastener of the present invention, the above-mentioned effect is far superior to the combination of the male surface fastener and the female surface fastener which are generally used in the past.
以上のような優れた利点を有する本発明の雄型面ファスナーは、特に、自動車の生産の際に、一定速度で流れている生産ラインにおいて、自動車の天井基材に天井材を固定する作業や自動車のトランクルームにトランクルーム用表面材を固定する作業において、固定する位置を間違えると、係合を一旦剥がして再度固定する作業が必要となり、その際にループ係合素子を傷めるおそれがあるために、生産ラインに混乱が生じたり、ライン速度を落としたりするなどの対応が必要となるが、本発明の成形用面ファスナーを用いると、位置合わせが容易となるため、位置ずれが生じることを減らすことが可能となる。 The male hook-and-loop fastener of the present invention having the above-mentioned excellent advantages can be used for fixing the ceiling material to the ceiling base material of an automobile, especially in a production line flowing at a constant speed during the production of an automobile. In the work of fixing the surface material for the trunk room to the trunk room of an automobile, if the fixing position is wrong, it is necessary to temporarily remove the engagement and fix it again, which may damage the loop engaging element. It is necessary to take measures such as causing confusion in the production line or reducing the line speed. However, when the surface fastener for molding of the present invention is used, the alignment is facilitated, so that the occurrence of misalignment can be reduced. Is possible.
また、家屋等の内装工事において、天井材や壁材に本発明の雄型成形面ファスナーを用いると、位置ズレや位置ズレが生じた際の面ファスナーのダメージを防ぐことができ、作業手間の軽減や位置ズレを生じた天井材や壁材を取り外す際の天井材や壁材の損傷を防ぐことができ、特に取り付ける対象物が大きな形状である場合には、本発明の雄型成形面ファスナーを用いる効果は非常に大きい。 Further, in the interior work of a house or the like, if the male molded surface fastener of the present invention is used for the ceiling material or the wall material, it is possible to prevent the surface fastener from being damaged when the position is displaced or the position is displaced, which is laborious. It is possible to prevent damage to the ceiling material and wall material when removing the ceiling material and wall material that have been reduced or misaligned, and especially when the object to be attached has a large shape, the male molded surface fastener of the present invention. The effect of using is very large.
本発明の雄型成形面ファスナーは、面積の大きい対象物を所定の位置に固定する際の固定手段として極めて優れており、たとえば面積が０．１ｍ２以上、特に０．２ｍ２のシート、あるいは板状物が取り付け対象物である場合に特に優れた効果を発揮する。 The male molded surface fastener of the present invention is extremely excellent as a fixing means when fixing an object having a large area in a predetermined position. For example, a sheet having an area of 0.1 m 2 or more, particularly 0.2 m 2 or a sheet, or It exerts a particularly excellent effect when a plate-shaped object is an object to be attached.
また、本発明の雄型成形面ファスナーは、通常、接着剤や粘着剤によりあるいは融着や縫製、ホッチキス等により対象物や裏面、あるいは基材表面に取り付けられ、一方、雌型織面ファスナーは、同様に、接着剤や粘着剤により、あるいは融着や縫製、ホッチキスにより対象物の裏面や基材表面に取り付けられる。 Further, the male molded surface fastener of the present invention is usually attached to an object or the back surface or the surface of a base material by adhesive or adhesive, fusion, sewing, hotchkiss or the like, while the female woven surface fastener is Similarly, it is attached to the back surface of the object or the surface of the base material by an adhesive or an adhesive, or by fusing, sewing, or velcro.
さらに、本発明には、天井基材に天井材が固定された構造体であって、天井基材と天井材のいずれか一方に前記雄型面ファスナーが固定され、他方にループ状係合素子を有する雌型面ファスナーが固定されており、両者が係合することにより天井材が天井基材に取り付けられていることを特徴とする天井構造体も包含される。 Further, in the present invention, the structure is a structure in which the ceiling material is fixed to the ceiling base material, the male hook-and-loop fastener is fixed to either the ceiling base material or the ceiling material, and the loop-shaped engaging element is fixed to the other. A ceiling structure is also included, wherein the female hook-and-loop fastener having the above-mentioned is fixed, and the ceiling material is attached to the ceiling base material by engaging the two.
本明細書は、上述したように様々な態様の技術を開示しているが、そのうち主な技術を以下にまとめる。 As described above, the present specification discloses various aspects of technology, of which the main technologies are summarized below.
本発明の一態様に係る雄型面ファスナーは、樹脂からなる基板の表面に立設する多数の雄型係合素子を有し、該雄型係合素子が、該樹脂基板から立ち上がるステムと該ステムからサイドに突出する係合用突起を有する雄型面ファスナーであって、前記係合用突起が、ステムから離れる方向に伸び、かつ、ステムの高さ方向に直交する方向に並ぶ複数の小突起に分岐しており、さらに、前記分岐した複数の小突起同士が平行であることを特徴とする。 The male hook-and-loop fastener according to one aspect of the present invention has a large number of male engaging elements erected on the surface of a substrate made of resin, and the male engaging elements stand up from the resin substrate and the stem. A male hook-and-loop fastener having engaging protrusions protruding sideways from the stem, and the engaging protrusions extend in a direction away from the stem and form a plurality of small protrusions arranged in a direction orthogonal to the height direction of the stem. It is branched, and further, the plurality of branched small protrusions are parallel to each other.
そのような構成により、係合を剥離する際にループ状係合素子を切断することなく、係合用突起が容易に反り返って係合が外れることとなり、その結果、ループ状係合素子を切断することなく係合を剥離できることとなる。 With such a configuration, the engaging projection easily bends back and disengages without cutting the loop-shaped engaging element when the engagement is disengaged, and as a result, the loop-shaped engaging element is cut. The engagement can be disengaged without any need.
また、前記雄型面ファスナーにおいて、前記基板から前記雄型係合素子の先端までの高さ（Ｈ）に対する、前記雄型係合素子先端から前記係合用突起の下端部までの長さ（Ｄ）の比（Ｄ／Ｈ）が０．３０〜０．６０であることが好ましい。そのような構成により、仮止め時（すなわち位置合わせ時）に強固な係合が生じず、本止め後には強固な係合が得られるという利点がある。 Further, in the male hook-and-loop fastener, the length (D) from the tip of the male engaging element to the lower end of the engaging protrusion with respect to the height (H) from the substrate to the tip of the male engaging element. ) Is preferably 0.30 to 0.60. With such a configuration, there is an advantage that strong engagement does not occur at the time of temporary fixing (that is, at the time of alignment), and strong engagement can be obtained after final fixing.
さらに、前記雄型面ファスナーにおいて、前記係合用突起が、係合用突起の付根から係合用突起の突出長の１／５〜１／２の部分で複数の小突起に分岐していることが好ましい。そのような構成にすることにより、係合用突起を作成しやすくなり、さらに、係合用突起が折れることを防ぐことができると考えられる。 Further, in the male hook-and-loop fastener, it is preferable that the engaging protrusion is branched into a plurality of small protrusions from the base of the engaging protrusion at a portion of 1/5 to 1/2 of the protruding length of the engaging protrusion. .. It is considered that such a configuration makes it easier to create the engaging protrusions and further prevents the engaging protrusions from breaking.
また、分岐した前記小突起の間には、楔形切目が存在していることが好ましい。それにより、係合用突起が撓みやすくなり、係合を剥離する際にループ状係合素子を傷めにくいといった利点がある。 Further, it is preferable that a wedge-shaped cut is present between the branched small protrusions. As a result, there is an advantage that the engaging protrusions are easily bent and the loop-shaped engaging element is not easily damaged when the engagement is disengaged.
また、前記雄型面ファスナーにおいて、前記分岐した複数の小突起の間に楔形切目が存在していることが好ましい。それにより、さらに係合用突起が撓みやすくなり、係合を剥離する際にループ状係合素子を傷めにくいといった利点がある。 Further, in the male hook-and-loop fastener, it is preferable that a wedge-shaped cut exists between the plurality of branched small protrusions. As a result, the engaging protrusions are more likely to bend, and there is an advantage that the loop-shaped engaging element is less likely to be damaged when the engagement is disengaged.
さらに、前記分岐した複数の小突起が２本または３本の小突起であることが好ましい。れにより、より位置ズレしにくく、正確な位置にしっかりと固定できるという利点がある。 Further, it is preferable that the plurality of branched small protrusions are two or three small protrusions. This has the advantage that it is less likely to be misaligned and can be firmly fixed in the correct position.
また、前記雄型面ファスナーにおいて、前記雄型係合素子が、基板から遠ざかる方向に突出するくっつき防止用突起を係合用突起より上に有していることが好ましい。それにより、位置合わせが容易になり、位置ずれが生じることをより減少できるという利点がある。 Further, in the male hook-and-loop fastener, it is preferable that the male engaging element has a protrusion for preventing sticking protruding in a direction away from the substrate above the engaging projection. As a result, there is an advantage that the alignment can be facilitated and the occurrence of misalignment can be further reduced.
さらに、前記雄型面ファスナーにおいて、前記雄型係合素子の高さが１．３〜３．０ｍｍの範囲であることが好ましい。それにより、充分な係合力がより確実に得られ、軽い力ではループ状係合素子に引っ掛かりにくいという利点がある。 Further, in the male hook-and-loop fastener, the height of the male engaging element is preferably in the range of 1.3 to 3.0 mm. As a result, a sufficient engaging force can be obtained more reliably, and there is an advantage that the loop-shaped engaging element is less likely to be caught by a light force.
また、前記雄型面ファスナーにおいて、前記雄型係合素子の基板被覆率が３０〜４５％であることが好ましい。それにより、仮止め時（すなわち位置合わせ時）に強固な係合が生じず、本止め後には強固な係合が得られるという効果をより確実に奏することができる。 Further, in the male hook-and-loop fastener, the substrate coverage of the male engaging element is preferably 30 to 45%. As a result, a strong engagement does not occur at the time of temporary fixing (that is, at the time of alignment), and a strong engagement can be obtained after the final fixing, which is more reliable.
また、前記雄型面ファスナーにおいて、前記小突起が先端に行くほど細くなっていることが好ましい。それにより、可撓性が良くなりループ係合素子を傷めにくくなるといった利点がある。 Further, in the male hook-and-loop fastener, it is preferable that the small protrusions become thinner toward the tip. As a result, there is an advantage that the flexibility is improved and the loop engaging element is less likely to be damaged.
さらに、前記雄型面ファスナーにおいて、前記小突起の断面形状が矩形であり、かつ、先端部に行くほど厚さおよび幅が薄くなっていることが好ましい。それにより上記効果がより確実に得られると考えられる。 Further, in the male hook-and-loop fastener, it is preferable that the cross-sectional shape of the small protrusion is rectangular, and the thickness and width become thinner toward the tip portion. It is considered that the above effect can be obtained more reliably.
また、前記雄型面ファスナーにおいて、前記雄型係合素子が基板上に列をなして並んでおり、各雄型係合素子の係合用突起は列方向と交わる方向に突出しているが列方向と平行な方向には突出していないことが好ましい。それにより、ループ状係合素子との適切な係合がより容易になる。 Further, in the male hook-and-loop fastener, the male engaging elements are arranged in a row on the substrate, and the engaging protrusions of the male engaging elements project in the direction intersecting the row direction, but in the row direction. It is preferable that it does not protrude in the direction parallel to. This facilitates proper engagement with the loop engaging element.
さらに、前記雄型面ファスナーにおいて、雄型面ファスナーの基板および雄型係合素子を形成する樹脂がポリアミド系の樹脂であることが好ましい。それにより、強度と耐熱性及び耐衝撃性により優れるという利点がある。 Further, in the male hook-and-loop fastener, it is preferable that the resin forming the substrate of the male hook-and-loop fastener and the male engaging element is a polyamide-based resin. This has the advantage of being superior in strength, heat resistance and impact resistance.
また、本発明の他の態様に係る天井構造体は、天井基材に天井材が固定された構造体であって、天井基材と天井材のいずれか一方に前記雄型面ファスナーが固定され、他方にループ状係合素子を有する雌型面ファスナーが固定されており、両者が係合することにより天井材が天井基材に取り付けられていることを特徴とする。 Further, the ceiling structure according to another aspect of the present invention is a structure in which a ceiling material is fixed to a ceiling base material, and the male hook-and-loop fastener is fixed to either the ceiling base material or the ceiling material. On the other hand, a female hook-and-loop fastener having a loop-shaped engaging element is fixed, and the ceiling material is attached to the ceiling base material by engaging the two.
以下に、実施例により本発明を更に具体的に説明するが、本発明の範囲はこれらに限定されるものではない。 Hereinafter, the present invention will be described in more detail with reference to Examples, but the scope of the present invention is not limited thereto.
なお、以下の実施例および比較例において、雌型面ファスナーとしては、特に断りがない場合には、クラレファスニング（株）製、雌型面ファスナー（Ｂ９７５０Ｙ、クロス係合）を用いた。 In the following Examples and Comparative Examples, female hook-and-loop fasteners (B9750Y, cross-engaged) manufactured by Kuraray Fastening Co., Ltd. were used as the female hook-and-loop fasteners unless otherwise specified.
（実施例１）
雌型面ファスナーとして、図４に示す係合用突起の先端が２本の小突起に分岐している形状（Ｄ：１．３４ｍｍ、Ｈ：２．９７ｍｍ、係合用突起のＹ方向における幅：１．０７ｍｍ、雄型係合素子の高さ：２．９７ｍｍ）を有する雄型係合素子が、図５（面ファスナーの一部を示す上面図）に示すように並んでいる雌型面ファスナー（雄型係合素子の基板被覆率２８．５％）を、同一形状の空間を有する金型へ、溶融樹脂を流し込んで圧力をかけることによって成形した。樹脂としては、ＰＡ６（アミラン、東レ社製）を用いた。成形条件は、シリンダ温度は２３０〜２６０℃、射出圧力は５０Ｍｐａ、保圧圧力は３０Ｍｐａ、保圧時間は５ｓｅｃ、金型温度は１３０℃で製作した。
(Example 1)
As a female hook-and-loop fastener, the tip of the engaging protrusion shown in FIG. 4 is branched into two small protrusions (D: 1.34 mm, H: 2.97 mm, width of the engaging protrusion in the Y direction: 1). Female hook-and-loop fasteners (top view showing a part of the hook-and-loop fastener) in which male hook-and-loop fasteners having .07 mm and height of the male hook-and-loop element (2.97 mm) are arranged as shown in FIG. 5 (top view showing a part of the hook-and-loop fastener). The substrate coverage of the male engaging element (28.5%) was formed by pouring a molten resin into a mold having a space having the same shape and applying pressure. As the resin, PA6 (Amilan, manufactured by Toray Industries, Inc.) was used. The molding conditions were a cylinder temperature of 230 to 260 ° C., an injection pressure of 50 Mpa, a holding pressure of 30 Mpa, a holding pressure time of 5 sec, and a mold temperature of 130 ° C.
なお、得られた雄型成形面ファスナーにおいて、雄型係合素子の係合用突起と、同突起方向（すなわち図２に示すＸ方向）に隣り合う雄型係合素子の係合用突起との間隔は０．５ｍｍ、係合用突起の突出長さ（Ｖ）は０．９１ｍｍ、雄型係合素子の厚さ（図２で示すＷ）は１．０７ｍｍ、基板（Ｂ）の厚さは２．３８ｍｍ、係合素子密度は、１５．４個／ｃｍ2であった。 In the obtained male molded hook-and-loop fastener, the distance between the engaging projection of the male engaging element and the engaging projection of the male engaging element adjacent to each other in the same projection direction (that is, the X direction shown in FIG. 2). Is 0.5 mm, the protruding length (V) of the engaging protrusion is 0.91 mm, the thickness of the male engaging element (W shown in FIG. 2) is 1.07 mm, and the thickness of the substrate (B) is 2. It was 38 mm and the engagement element density was 15.4 elements / cm 2 .
（実施例２）
溶融樹脂を、ＡＢＳ（アクリロニトリル・ブタジエン・スチレン）に変更した以外は、実施例１と同様にして、雌型面ファスナーを製造した。
(Example 2)
A female hook-and-loop fastener was produced in the same manner as in Example 1 except that the molten resin was changed to ABS (acrylonitrile-butadiene-styrene).
（実施例３）
係合用突起の先端が２本に分岐しているが、Ｄの厚みが０．８０ｍｍと薄くなった金型を用いた以外は、実施例１と同様にして、雌型面ファスナーを製造した（雄型係合素子の形状は、図６（ａ）の通りである。なお、左が断面図で、右が上面図である）。
(Example 3)
A female hook-and-loop fastener was manufactured in the same manner as in Example 1 except that a mold having a thin D thickness of 0.80 mm was used, although the tip of the engaging protrusion was branched into two. The shape of the male engaging element is as shown in FIG. 6A. The left is a cross-sectional view and the right is a top view).
（比較例１）
係合用突起の先端が分岐していない金型を用いた以外は、実施例１と同様にして、雌型面ファスナーを製造した（雄型係合素子の形状は、図６（ｂ）の通りである）。
(Comparative Example 1)
A female hook-and-loop fastener was manufactured in the same manner as in Example 1 except that a mold in which the tip of the engaging protrusion was not branched was used (the shape of the male engaging element is as shown in FIG. 6B). Is).
（比較例２）
係合用突起の先端が分岐しておらず、係合用突起のＹ方向における幅が０．４６ｍｍである金型を用いた以外は、実施例１と同様にして、雌型面ファスナーを製造した（雄型係合素子の形状は、図６（ｃ）の通りである）。
(Comparative Example 2)
A female hook-and-loop fastener was manufactured in the same manner as in Example 1 except that a mold was used in which the tip of the engaging protrusion was not branched and the width of the engaging protrusion in the Y direction was 0.46 mm. The shape of the male engaging element is as shown in FIG. 6 (c)).
（比較例３）
係合用突起の先端が２本に分岐しているが、切れ目が楔形ではなく、それぞれの小突起が約９０°異なる方向に伸びた金型を用いた以外は、実施例１と同様にして、雌型面ファスナーを製造した（雄型係合素子の形状は、図６（ｄ）の通りである）。
(Comparative Example 3)
The tip of the engaging protrusion is branched into two, but the cut is not wedge-shaped, and the mold is used in which each small protrusion extends in different directions by about 90 °, in the same manner as in Example 1. A female hook-and-loop fastener was manufactured (the shape of the male engaging element is as shown in FIG. 6D).
（評価試験１）
［ブラッケト（ＢＲＫＴ）への把持］
雄型面ファスナーとループ面ファスナーを係合させ、面直方向へ２ｋｇ荷重を掛けた状態で９０℃雰囲気下で２４時間養生して評価した。雄型面ファスナーの変形なく２４時間保持したものを○、雄型面ファスナーの変形はあるが２４時間保持したものを△と評価した。
(Evaluation test 1)
[Gripping to BRKT]
The male hook-and-loop fastener and the loop hook-and-loop fastener were engaged with each other and cured for 24 hours in an atmosphere of 90 ° C. with a load of 2 kg applied in the direction perpendicular to the surface for evaluation. Those held for 24 hours without deformation of the male hook-and-loop fastener were evaluated as ◯, and those held for 24 hours with deformation of the male hook-and-loop fastener were evaluated as Δ.
［面直強力］
上記実施例１〜２および比較例１〜３で得られた雌型面ファスナーを、上述の雌型面ファスナーと５．６ｃｍ２係合させ、面直方向に３００ｍｍ／ｍｉｎの速度で引き剥がした時の最大強力を測定した。また、５回繰り返し後の面直強力は９８Ｎ／ｐｃ以上の強力が合格とする。
[Strong face-to-face]
The female hook-and-loop fasteners obtained in Examples 1 and 2 and Comparative Examples 1 to 3 were engaged with the above-mentioned female hook-and-loop fastener by 5.6 cm 2 and peeled off at a speed of 300 mm / min in the direction perpendicular to the plane. The maximum strength of time was measured. In addition, as for the surface strength after repeating 5 times, a strength of 98 N / pc or more is considered to pass.
［クリープ試験］
クリープ耐熱試験をクラレファスニング法にて実施した。
[Creep test]
The creep heat resistance test was carried out by the Kuraray fastening method.
クラレファスニング法：雄型面ファスナーとループ面ファスナーを５．６ｃｍ２係合し２４時間養生させ９０℃雰囲気下で面直方向に２ｋｇ荷重を掛けた状態で２４時間後落下しなければ合格とする。 Kuraray Fastening Method: Male hook-and-loop fastener and loop hook-and-loop fastener are engaged with each other by 5.6 cm 2 and cured for 24 hours. ..
以上の結果を、表１に示す。 The above results are shown in Table 1.
（考察）
係合用突起の形状が本発明の条件を満たしている実施例１および２ではいずれも、面直強力、クリープ試験ともに合格レベルの結果となった。
(Discussion)
In Examples 1 and 2 in which the shape of the engaging protrusion satisfies the conditions of the present invention, both the surface straight strength and the creep test gave a passing level result.
やわらかめの樹脂を用いて成形した実施例２では、把持力がやや劣る結果となった。 In Example 2 formed by using a soft resin, the gripping force was slightly inferior.
これに対し、比較例１では、係合用突起の先端が分岐していないため、突起の幅が大きくなり、ループが係りにくくなった。その結果、面直強力、クリープ試験の両方においてかなり劣る結果となった。 On the other hand, in Comparative Example 1, since the tip of the engaging protrusion was not branched, the width of the protrusion became large and the loop became difficult to engage. As a result, both the straight surface strength and the creep test were considerably inferior.
次に、係合用突起の先端が分岐しておらず、単に突起の幅を小さくした比較例２では、射出成形では成形が非常に困難であった上に、ステムが折れやすく、５回繰り返し後の面直強力が下がった。 Next, in Comparative Example 2 in which the tip of the engaging protrusion was not branched and the width of the protrusion was simply reduced, molding was very difficult by injection molding, and the stem was easily broken, and after repeating 5 times. The straightness of the face has decreased.
小突起同士の間が９０°ほど開いている比較例３では、斜め向かいに並ぶ雄型係合素子の係合用突起の先端同士が近接してしまい、ループが入りにくくなった。そのため、面直強力、クリープ試験の両方において劣る結果となった。 In Comparative Example 3 in which the small protrusions are open by about 90 °, the tips of the engaging protrusions of the male engaging elements lined up diagonally are close to each other, making it difficult for the loop to enter. Therefore, the results were inferior in both the straight surface strength and the creep test.
（評価試験２）
［作業性（誤着機能）評価］
実施例１〜３および比較例１〜３の雄型面ファスナーをループ面ファスナーの上に乗せ、１００ｇ荷重を掛けた状態で雄型面ファスナーをスライドすることにより、作業性を評価した。２００ｇ以下の強力でスライドしたものを○、３００ｇ以下の強力でスライドしたものを△と評価した。
(Evaluation test 2)
[Workability (wrong attachment function) evaluation]
Workability was evaluated by placing the male hook-and-loop fasteners of Examples 1 to 3 and Comparative Examples 1 to 3 on the loop hook-and-loop fastener and sliding the male hook-and-loop fastener with a load of 100 g applied. Those that slid with a force of 200 g or less were evaluated as ◯, and those that slid with a force of 300 g or less were evaluated as Δ.
その結果、Ｄ／Ｈが０．３０〜０．６０の範囲を満たす実施例１〜２および比較例１〜３では○となったが、Ｄ／Ｈが０．３未満となる実施例３では、雄型面ファスナーとループ面ファスナーが係合しスライドしないとなったため、作業性については×という結果となった。 As a result, in Examples 1 and 2 and Comparative Examples 1 to 3 in which the D / H satisfies the range of 0.30 to 0.60, the result was ◯, but in Example 3 in which the D / H was less than 0.3. Since the male hook-and-loop fastener and the loop hook-and-loop fastener were engaged and did not slide, the workability was x.
Ｂ 基板
Ｅ 雄型係合素子
Ｓ ステム
Ｔ 係合用突起
Ｍ くっつき防止用突起
Ｈ 基板からの係合素子の高さ
Ｄ 係合素子の最頂部から係合用突起下端部までの長さ
Ｗ 雄型係合素子の厚さ
Ｖ 係合用突起の突出長さ
Ｙ 係合素子列方向
Ｘ 係合素子の切れ目方向
B Board E Male engaging element S Stem T Engagement protrusion M Anti-sticking protrusion H Height of engaging element from the board D Length from the top of the engaging element to the lower end of the engaging protrusion W Male Thickness of mating element V Protruding length of engaging protrusion Y Engaging element row direction X Engaging element cut direction
Claims (11)
前記雄型係合素子が基板上に列をなして並んでおり、各雄型係合素子の係合用突起は列方向と交わる方向に突出しているが列方向と平行な方向には突出しておらず、
前記雄型係合素子の高さが１．３〜３．０ｍｍの範囲であり、
前記係合用突起が、ステムから離れる方向に伸び、かつステムの高さ方向に直交する方向に並ぶ複数の小突起に分岐しており、さらに前記分岐した複数の小突起同士が平行であることを特徴とする、雄型面ファスナー。 It has a large number of male engaging elements that stand on the surface of a substrate made of resin, and the male engaging elements are symmetrical to the stem rising from the resin substrate and both sides from the stem, and are parallel or parallel to the substrate. In a male molded hook-and-loop fastener having an engaging protrusion that protrudes in a direction in which the tip is lowered toward the substrate.
The male engaging elements are arranged in a row on the substrate, and the engaging protrusions of each male engaging element project in the direction intersecting the row direction but project in the direction parallel to the row direction. Zu,
The height of the male engaging element is in the range of 1.3 to 3.0 mm.
The engaging protrusions extend in the direction away from the stem and are branched into a plurality of small protrusions arranged in a direction orthogonal to the height direction of the stem, and the plurality of branched small protrusions are parallel to each other. A characteristic male hook-and-loop fastener.