JP6827760B2 - タイヤ部材およびその製造方法 - Google Patents
タイヤ部材およびその製造方法 Download PDFInfo
- Publication number
- JP6827760B2 JP6827760B2 JP2016202819A JP2016202819A JP6827760B2 JP 6827760 B2 JP6827760 B2 JP 6827760B2 JP 2016202819 A JP2016202819 A JP 2016202819A JP 2016202819 A JP2016202819 A JP 2016202819A JP 6827760 B2 JP6827760 B2 JP 6827760B2
- Authority
- JP
- Japan
- Prior art keywords
- rubber
- filler
- diene
- formula
- tire member
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、タイヤ部材およびその製造方法に関する。
従来から、廃タイヤなどのゴム製品廃材は再利用されており、例えばセメント工場などで燃料として再利用されているが、近年、環境問題を配慮し、廃タイヤなどを粉砕し、ゴム片またはゴム粉としてそのまま使用する、マテリアルリサイクルが推奨されている。しかしながら、廃タイヤなどを微粉砕化したゴム粉を新ゴムに混合した場合、そのゴム組成物の粘度上昇に伴う加工性悪化や、ゴム組成物を加硫して得られる加硫ゴムの物性の悪化、例えば引張強度などの悪化が問題となっていた。
下記特許文献１では、加硫ゴム粉末を配合したゴム組成物の加硫ゴムの引裂強度の低下を防止することを目的として、特定のブロックポリマーを添加する技術が報告されている。
ところで、下記特許文献２では、特定の化合物を配合したゴム組成物を原料とすることで、タイヤ物性の向上を図る技術が報告されている。
しかしながら、前記特許文献２では、廃タイヤなどを原料として得られるゴム粉を配合した加硫ゴムの物性、例えば引張強度などを向上する点について、何ら記載も示唆もしていない。
本発明は上記実情に鑑みてなされたものであり、その目的は、ゴム粉を含有し、引張強度および引裂強度の低下が抑制された加硫ゴムの原料となり得るタイヤ部材およびその製造方法を提供することにある。
上記目的は、下記の如き本発明により達成できる。即ち本発明は、ジエン系ゴム、充填材、ゴム粉および下記式（Ｉ）に記載の化合物：
（式（Ｉ）中、Ｒ１およびＲ２は、水素原子、ならびに炭素数１〜２０のアルキル基、アルケニル基またはアルキニル基を示し、Ｒ１およびＲ２は同一であっても異なっていてもよい。Ｍ＋はナトリウムイオン、カリウムイオンまたはリチウムイオンを示す。）を含有することを特徴とするタイヤ部材、に関する。
（式（Ｉ）中、Ｒ１およびＲ２は、水素原子、ならびに炭素数１〜２０のアルキル基、アルケニル基またはアルキニル基を示し、Ｒ１およびＲ２は同一であっても異なっていてもよい。Ｍ＋はナトリウムイオン、カリウムイオンまたはリチウムイオンを示す。）を含有することを特徴とするタイヤ部材、に関する。
本発明に係るタイヤ部材では、式（Ｉ）記載の化合物を介して、ジエン系ゴム成分と充填材、およびゴム粉と充填材とが、結合し易くなり、充填材の分散性が優れると共に、さらにジエン系ゴム成分とゴム粉とが、充填材を介して結合を形成し易くなる。つまり、ジエン系ゴム、充填材、ゴム粉および式（Ｉ）に記載の化合物の四者の分散性が向上するとともに、ジエン系ゴムとゴム粉との相互作用が強くなる。その結果、本発明に係るタイヤ部材は、加硫後の引張強度および引裂強度の低下が抑制される。
また、本発明は、ジエン系ゴム、充填材、ゴム粉および下記式（Ｉ）に記載の化合物：
（式（Ｉ）中、Ｒ１およびＲ２は、水素原子、ならびに炭素数１〜２０のアルキル基、アルケニル基またはアルキニル基を示し、Ｒ１およびＲ２は同一であっても異なっていてもよい。Ｍ＋はナトリウムイオン、カリウムイオンまたはリチウムイオンを示す。）を混合する工程を含むことを特徴とするタイヤ部材の製造方法、に関する。
（式（Ｉ）中、Ｒ１およびＲ２は、水素原子、ならびに炭素数１〜２０のアルキル基、アルケニル基またはアルキニル基を示し、Ｒ１およびＲ２は同一であっても異なっていてもよい。Ｍ＋はナトリウムイオン、カリウムイオンまたはリチウムイオンを示す。）を混合する工程を含むことを特徴とするタイヤ部材の製造方法、に関する。
上記タイヤ部材の製造方法において、ジエン系ゴム、充填材、ゴム粉および下記式（Ｉ）に記載の化合物：
（式（Ｉ）中、Ｒ１およびＲ２は、水素原子、ならびに炭素数１〜２０のアルキル基、アルケニル基またはアルキニル基を示し、Ｒ１およびＲ２は同一であっても異なっていてもよい。Ｍ＋はナトリウムイオン、カリウムイオンまたはリチウムイオンを示す。）を事前混合する工程を含むことが好ましく、特には老化防止剤やワックス、ステアリン酸、硫黄等を除いてジエン系ゴム、充填材、ゴム粉および下記式（Ｉ）に記載の化合物を事前混合する工程を含むことが好ましい。
（式（Ｉ）中、Ｒ１およびＲ２は、水素原子、ならびに炭素数１〜２０のアルキル基、アルケニル基またはアルキニル基を示し、Ｒ１およびＲ２は同一であっても異なっていてもよい。Ｍ＋はナトリウムイオン、カリウムイオンまたはリチウムイオンを示す。）を事前混合する工程を含むことが好ましく、特には老化防止剤やワックス、ステアリン酸、硫黄等を除いてジエン系ゴム、充填材、ゴム粉および下記式（Ｉ）に記載の化合物を事前混合する工程を含むことが好ましい。
前述のとおり、本発明に係るタイヤ部材は、ジエン系ゴム、充填材、ゴム粉および式（Ｉ）に記載の化合物の四者が結合するなどして、互いに相互作用することにより効果を発揮する。このため、ジエン系ゴム、充填材、ゴム粉および式（Ｉ）に記載の化合物の四者を予め混合し（事前混合）、四者の相互作用を高めてから、その後必要に応じて、老化防止剤やワックス、ステアリン酸、硫黄等の他の配合剤を配合することにより、タイヤ部材を製造することが好ましい。
本発明に係るタイヤ部材は、ジエン系ゴム、充填材、ゴム粉および式（Ｉ）に記載の化合物を含有する。
ジエン系ゴムとしては、例えば、天然ゴム（ＮＲ）；イソプレンゴム（ＩＲ）、ブタジエンゴム（ＢＲ）、スチレンブタジエンゴム（ＳＢＲ）、ブチルゴム（ＩＩＲ）、およびアクリルニトリルブタジエンゴム（ＮＢＲ）などのジエン系合成ゴム；臭素化ブチルゴム（ＢＲ−ＩＩＲ）などのハロゲン化ブチルゴム；その他ポリウレタンゴム、アクリルゴム、フッ素ゴム、シリコンゴム、およびクロロスルホン化ポリエチレンなどを含めた合成ゴム類などが挙げられる。これらの中でも、本発明においては、天然ゴムを使用することが好ましい。
本発明において、充填材とは、カーボンブラック、シリカ、クレー、タルク、炭酸カルシウム、炭酸マグネシウム、水酸化アルミニウムなど、ゴム工業において通常使用される無機充填材を意味する。上記無機充填材の中でも、本発明においてはカーボンブラックを特に好適に使用することができる。あるいは、カーボンブラックとシリカとを併用して使用することも可能である。
カーボンブラックとしては、例えばＳＡＦ、ＩＳＡＦ、ＨＡＦ、ＦＥＦ、ＧＰＦなど、通常のゴム工業で使用されるカーボンブラックの他、アセチレンブラックやケッチェンブラックなどの導電性カーボンブラックを使用することができる。カーボンブラックは、通常のゴム工業において、そのハンドリング性を考慮して造粒された、造粒カーボンブラックであってもよく、未造粒カーボンブラックであってもよい。
本発明において、タイヤ部材中の充填材の配合量は、ジエン系ゴム１００質量部に対し、２０〜１００質量部であることが好ましく、３０〜８０質量部であることがより好ましい。
ゴム粉は少なくとも一部が加硫されたものを好適に使用可能であり、特に環境問題を考慮した場合、使用済みタイヤを原料として得られた再生ゴムを粉末化したものが好ましい。得られる加硫ゴムの引張強度および引裂強度とタイヤ部材の加工性とを考慮した場合、ゴム粉の粒径はＡＳＴＭ Ｄ５６４４−０１に準拠したＭｅｓｈで８０〜２７０Ｍｅｓｈが好ましく、１４０〜２３０Ｍｅｓｈがより好ましい。
本発明においては、さらにタイヤ部材が下記式（Ｉ）に記載の化合物を含有する。
（式（Ｉ）中、Ｒ１およびＲ２は、水素原子、ならびに炭素数１〜２０のアルキル基、アルケニル基またはアルキニル基を示し、Ｒ１およびＲ２は同一であっても異なっていてもよい。Ｍ＋はナトリウムイオン、カリウムイオンまたはリチウムイオンを示す。）
（式（Ｉ）中、Ｒ１およびＲ２は、水素原子、ならびに炭素数１〜２０のアルキル基、アルケニル基またはアルキニル基を示し、Ｒ１およびＲ２は同一であっても異なっていてもよい。Ｍ＋はナトリウムイオン、カリウムイオンまたはリチウムイオンを示す。）
なお、充填材、特にはカーボンブラックへの親和性を高めるためには、式（Ｉ）中のＲ１およびＲ２が水素原子であり、Ｍ＋がナトリウムイオンである下記式（Ｉ’）に記載の化合物：
を使用することが特に好ましい。
を使用することが特に好ましい。
加硫ゴム特性を考慮した場合、ジエン系ゴム１００質量部に対し、式（Ｉ）に記載の化合物の配合量は０．１〜１０質量部であることが好ましく、０．２〜８質量部であることがより好ましい。
本発明のタイヤ部材は、ジエン系ゴム、充填材、ゴム粉および式（Ｉ）記載の化合物とともに、硫黄系加硫剤、加硫促進剤、シランカップリング剤、ステアリン酸、加硫促進助剤、加硫遅延剤、老化防止剤、ワックスやオイルなどの軟化剤、加工助剤などの通常ゴム工業で使用される配合剤を、本発明の効果を損なわない範囲において適宜配合し用いることができる。
加硫促進剤としては、ゴム加硫用として通常用いられる、スルフェンアミド系加硫促進剤、チウラム系加硫促進剤、チアゾール系加硫促進剤、チオウレア系加硫促進剤、グアニジン系加硫促進剤、ジチオカルバミン酸塩系加硫促進剤などの加硫促進剤を単独、または適宜混合して使用しても良い。
老化防止剤としては、ゴム用として通常用いられる、芳香族アミン系老化防止剤、アミン−ケトン系老化防止剤、モノフェノール系老化防止剤、ビスフェノール系老化防止剤、ポリフェノール系老化防止剤、ジチオカルバミン酸塩系老化防止剤、チオウレア系老化防止剤などの老化防止剤を単独、または適宜混合して使用しても良い。
本発明のタイヤ部材は、ジエン系ゴム、充填材、ゴム粉および式（Ｉ）記載の化合物、必要に応じて、硫黄系加硫剤、加硫促進剤、シランカップリング剤、ステアリン酸、加硫促進助剤、加硫遅延剤、老化防止剤、ワックスやオイルなどの軟化剤、加工助剤などを、バンバリーミキサー、ニーダー、ロールなどの通常のゴム工業において使用される混練機を用いて混練りすることにより得られる。
また、上記各成分の配合方法は特に限定されず、硫黄系加硫剤、および加硫促進剤などの加硫系成分以外の配合成分を予め混練してマスターバッチとし、残りの成分を添加してさらに混練する方法、各成分を任意の順序で添加し混練する方法、全成分を同時に添加して混練する方法などのいずれでもよい。
ただし、得られる加硫ゴムの引張強度および引裂強度の低下を十分に抑制するために、ジエン系ゴム、充填材、ゴム粉および式（Ｉ）に記載の化合物を事前混合し、これら四者を十分に混合・分散させた状態で、残りの配合剤を混合することにより、タイヤ部材を製造することが好ましい。
以下に、この発明の実施例を記載してより具体的に説明する。
（ゴム組成物の調製）
ジエン系ゴム１００質量部に対して、表１の配合処方に従い、実施例１〜６、比較例１〜２の各原料を配合し、通常のバンバリーミキサーを用いて混練し、タイヤ部材を調整した。なお、実施例３〜６については、予めジエン系ゴム、充填材、ゴム粉および式（Ｉ）に記載の化合物の四者を事前混合し、その後、残りの各原料を混合した。表１に記載の各使用原料を以下に示す。
ジエン系ゴム１００質量部に対して、表１の配合処方に従い、実施例１〜６、比較例１〜２の各原料を配合し、通常のバンバリーミキサーを用いて混練し、タイヤ部材を調整した。なお、実施例３〜６については、予めジエン系ゴム、充填材、ゴム粉および式（Ｉ）に記載の化合物の四者を事前混合し、その後、残りの各原料を混合した。表１に記載の各使用原料を以下に示す。
（使用原料）
天然ゴム（ＮＲ）；「ＲＳＳ＃３」
シリカ；「ニップシールＡＱ」（ＢＥＴ比表面積２０５ｍ２／ｇ、ＣＴＡＢ１７５ｍ２／ｇ、ＤＢＰ吸収量１５０ｃｍ３／１００ｇ 東ソー・シリカ社製
カーボンブラック；「シーストＫＨ」 東海カーボン社製
亜鉛華；亜鉛華１号 三井金属鉱業社製
老化防止剤；「ノクラック６Ｃ」 大内新興化学社製
ステアリン酸；「ルナックＳ２０」 花王社製
ワックス；「ＯＺＯＡＣＥ０３５５」 日本精蝋社製
シランカップリング剤；「ＳＩ７５」 デグサ社製
式（Ｉ）記載の化合物（（２Ｚ）−４−［（４−アミノフェニル）アミノ］−４−オキソ−２−ブテン酸ナトリウム）；「ＣＡ２０８」 住友化学社製
ゴム粉（Ａ）；「ＰｏｌｙＤｙｎｅ１４０」 Ｌｅｈｉｇｈ社製
ゴム粉（Ｂ）；「ＰｏｌｙＤｙｎｅ２００」 Ｌｅｈｉｇｈ社製
硫黄；「粉末硫黄」 鶴見化学工業社製
加硫促進剤；「ソクシールＣＺ」 住友化学社製
天然ゴム（ＮＲ）；「ＲＳＳ＃３」
シリカ；「ニップシールＡＱ」（ＢＥＴ比表面積２０５ｍ２／ｇ、ＣＴＡＢ１７５ｍ２／ｇ、ＤＢＰ吸収量１５０ｃｍ３／１００ｇ 東ソー・シリカ社製
カーボンブラック；「シーストＫＨ」 東海カーボン社製
亜鉛華；亜鉛華１号 三井金属鉱業社製
老化防止剤；「ノクラック６Ｃ」 大内新興化学社製
ステアリン酸；「ルナックＳ２０」 花王社製
ワックス；「ＯＺＯＡＣＥ０３５５」 日本精蝋社製
シランカップリング剤；「ＳＩ７５」 デグサ社製
式（Ｉ）記載の化合物（（２Ｚ）−４−［（４−アミノフェニル）アミノ］−４−オキソ−２−ブテン酸ナトリウム）；「ＣＡ２０８」 住友化学社製
ゴム粉（Ａ）；「ＰｏｌｙＤｙｎｅ１４０」 Ｌｅｈｉｇｈ社製
ゴム粉（Ｂ）；「ＰｏｌｙＤｙｎｅ２００」 Ｌｅｈｉｇｈ社製
硫黄；「粉末硫黄」 鶴見化学工業社製
加硫促進剤；「ソクシールＣＺ」 住友化学社製
（評価項目）
（１）引張特性（引張強度および引張伸び）
ＪＩＳＫ６２５１に準じて引張試験（ダンベル３号形、雰囲気温度２３℃）を実施した。比較例１を１００とした指数で示した。値が大きいほど引張強さ、引張伸びが優れることを示す。
（１）引張特性（引張強度および引張伸び）
ＪＩＳＫ６２５１に準じて引張試験（ダンベル３号形、雰囲気温度２３℃）を実施した。比較例１を１００とした指数で示した。値が大きいほど引張強さ、引張伸びが優れることを示す。
（２）引裂強度
ＪＩＳＫ６２５２に準拠して測定し、比較例１を１００とした指数で示した。値が大きいほど引裂強度が優れることを示す。
ＪＩＳＫ６２５２に準拠して測定し、比較例１を１００とした指数で示した。値が大きいほど引裂強度が優れることを示す。
Claims (1)
- ジエン系ゴム、充填材、ゴム粉および下記式（Ｉ）に記載の化合物：