JP6789693B2 - 耐食性に優れた高強度バネ鋼 - Google Patents
耐食性に優れた高強度バネ鋼 Download PDFInfo
- Publication number
- JP6789693B2 JP6789693B2 JP2016126995A JP2016126995A JP6789693B2 JP 6789693 B2 JP6789693 B2 JP 6789693B2 JP 2016126995 A JP2016126995 A JP 2016126995A JP 2016126995 A JP2016126995 A JP 2016126995A JP 6789693 B2 JP6789693 B2 JP 6789693B2
- Authority
- JP
- Japan
- Prior art keywords
- spring steel
- strength
- less
- corrosion
- content
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
近年には、排気ガスの低減や燃費改善を目的として自動車の軽量化や高出力化の要求条件が高くなっている実情であり、これによりエンジンやサスペンションなどに使われるコイルバネは高応力の設計を指向している。
このようなサスペンション用コイルバネとしては、C、Si、Mn、Crなどを主成分とし、1900Mpa程度の引張強度を持ち、幾分の耐食性を持つバネ鋼が使われており、ひいては合金元素の種類及び含量を調節して疲労寿命をさらに向上させることができる介在物制御技術に対する努力を注いでいる。
そして、疲労寿命は、KS B ISO 1143に従って線径4mmの試験片に対する回転曲げ疲労試験によって測定し、L10寿命は基本定格寿命(basic rating life)を90%の信頼度で回動数100万回単位で表示し、平均寿命(L50 mean life)または破損の間の平均時間の1/7であり、腐食性疲労評価は塩水噴霧試験方法(KS D 9502、ISO 3768/7263)で測定した。
Claims (1)
- 車両のサスペンションに使われるコイルバネ鋼であって、
重量%で、C:0.4〜0.9%、Si:1.3〜2.3%、Mn:0.5〜1.2%、Cr:0.6〜1.2%、Mo:0.1〜0.5%、Ni:0.05〜0.8%、V:0.05〜0.5%、Nb:0.05〜0.5%、Ti:0.05〜0.3%、Co:0.01〜3%、Zr:0.001〜0.2%、Y0.01〜1.5%、Cu:0.3%以下(0%除外)、Al:0.3%以下(0%除外)、N:0.03%以下(0%除外)、O:0.003%以下(0%除外)、残分Fe及びその他の不可避な不純物からなる、耐食性に優れた高強度バネ鋼。