JP6761250B2 - ジルコニア焼結体及び歯科用製品、並びにそれらの製造方法 - Google Patents
ジルコニア焼結体及び歯科用製品、並びにそれらの製造方法 Download PDFInfo
- Publication number
- JP6761250B2 JP6761250B2 JP2016008079A JP2016008079A JP6761250B2 JP 6761250 B2 JP6761250 B2 JP 6761250B2 JP 2016008079 A JP2016008079 A JP 2016008079A JP 2016008079 A JP2016008079 A JP 2016008079A JP 6761250 B2 JP6761250 B2 JP 6761250B2
- Authority
- JP
- Japan
- Prior art keywords
- sintered body
- zirconia sintered
- value
- zirconia
- rate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
前記第1視点の変形として、安定化剤として5mol%〜8mol%のイットリアを含有する部分安定化ジルコニアの焼結体であって、前記焼結体の外部の透光性ΔLをΔL1と表記し、前記焼結体の内部の透光性ΔLをΔL2と表記し、ΔL1からΔL2への変化率を以下の式:[ΔLの変化率]=(ΔL2−ΔL1)/ΔL1×100で表すとき、ΔLの変化率は−15%以上であり、かつ、正の値とならず、ただし、前記外部とは、焼結後の無加工の外表面から深さ4mmまでの部分であり、前記内部とは、前記外表面から深さ4mmよりも深い部分であり、前記内部及び前記外部のL*a*b*表色系(JISZ8781)における色度(色空間)のL*値について、F11を光源として用いて、試料の背景を白色にして測定したL*値を第1のL*値とし、第1のL*値を測定した同一の試料について、試料の背景を黒色にして測定したL*値を第2のL*値とするとき、ΔLは、前記第1のL*値から前記第2のL*値を控除した値であり、前記焼結体は、前記外表面のどの面からみても深さ4mmよりも深い前記内部が存在し、前記焼結体の体積は、27000mm3以下である、ジルコニア焼結体が提供される。
前記第3視点の変形として、安定化剤として5mol%〜8mol%のイットリアを含有するジルコニアの組成物を焼成して焼結体にする焼結工程を含み、前記焼結工程において、1000℃から最高温度までの昇温速度が5℃/分以下であり、前記焼結体の外部の透光性ΔLをΔL1と表記し、前記焼結体の内部の透光性ΔLをΔL2と表記し、ΔL1からΔL2への変化率を以下の式:[ΔLの変化率]=(ΔL2−ΔL1)/ΔL1×100で表すとき、ΔLの変化率は−15%以上であり、かつ、正の値とならず、ただし、前記外部とは、焼結後の無加工の外表面から深さ4mmまでの部分であり、前記内部とは、前記外表面から深さ4mmよりも深い部分であり、前記内部及び前記外部のL*a*b*表色系(JISZ8781)における色度(色空間)のL*値について、F11を光源として用いて、試料の背景を白色にして測定したL*値を第1のL*値とし、第1のL*値を測定した同一の試料について、試料の背景を黒色にして測定したL*値を第2のL*値とするとき、ΔLは、前記第1のL*値から前記第2のL*値を控除した値であり、前記焼結体は、前記外表面のどの面からみても深さ4mmよりも深い前記内部が存在し、前記焼結体の体積は、27000mm3以下である、ジルコニア焼結体の製造方法が提供される。
[ΔLの変化率(%)]=(ΔL2−ΔL1)/ΔL1×100
ジルコニア焼結体を作製し、焼結体内部と外部の透光性を比較した。また、ジルコニア焼結体の密度、結晶粒径及び切削性を測定した。比較例1〜3として、昇温速度を変えて作製したジルコニア焼結体についても同様の測定を行った。また、比較例4では、異なる寸法を有する焼結体について同様の測定を行った。
10 歯科用製品
11 取り付け具
20 試料
21 測定装置
22 下敷き
Claims (22)
- 安定化剤として5mol%〜8mol%のイットリアを含有する部分安定化ジルコニアの焼結体であって、
前記焼結体の外部の透光性ΔLをΔL1と表記し、
前記焼結体の内部の透光性ΔLをΔL2と表記し、
ΔL1からΔL2への変化率を以下の式:
[ΔLの変化率]=(ΔL2−ΔL1)/ΔL1×100
で表すとき、
ΔLの変化率は−15%以上であり、かつ、正の値とならず、
ただし、前記外部とは、焼結後の無加工の外表面から深さ4mmまでの部分であり、
前記内部とは、前記外表面から深さ4mmよりも深い部分であり、
前記内部及び前記外部のL*a*b*表色系(JISZ8781)における色度(色空間)のL*値について、F11を光源として用いて、試料の背景を白色にして測定したL*値を第1のL*値とし、
第1のL*値を測定した同一の試料について、試料の背景を黒色にして測定したL*値を第2のL*値とするとき、
ΔLは、前記第1のL*値から前記第2のL*値を控除した値であり、
前記焼結体は、前記外表面のどの面からみても深さ4mmよりも深い前記内部が存在し、
前記焼結体の体積は、27000mm3以下である、ジルコニア焼結体。 - 前記ΔLの変化率は、−10%以上である、請求項1に記載のジルコニア焼結体。
- 前記ΔLの変化率は、−5%以上である、請求項1又は2に記載のジルコニア焼結体。
- 断面積が900mm2以下の断面を有し、
前記断面における最短の差し渡し長が30mm以下である、請求項1〜3のいずれか一項に記載のジルコニア焼結体。 - 5μm以上の平均結晶粒径を有する、請求項1〜4のいずれか一項に記載のジルコニア焼結体。
- 六面体又は円柱体形状を有する、請求項1〜5のいずれか一項に記載のジルコニア焼結体。
- 前記焼結体の形状は、直方体であり、
前記直方体の寸法は、長さ13mm〜17mm、幅15mm〜19mm、高さ18mm〜32mmである、請求項1〜5のいずれか一項に記載のジルコニア焼結体。 - 請求項1〜5のいずれか一項に記載のジルコニア焼結体を備える、歯科用製品。
- 加工装置に取り付けるための取り付け具をさらに備え、
前記取り付け具は、前記ジルコニア焼結体に接合されている、請求項8に記載の歯科用製品。 - 前記ジルコニア焼結体は、六面体又は円柱体形状を有する、請求項8又は9に記載の歯科用製品。
- 前記ジルコニア焼結体の形状は、直方体であり、
前記直方体の寸法は、長さ13mm〜17mm、幅15mm〜19mm、高さ18mm〜32mmである、請求項8又は9に記載の歯科用製品。 - 前記ジルコニア焼結体は、歯冠形状を有する、請求項8又は9に記載の歯科用製品。
- 安定化剤として5mol%〜8mol%のイットリアを含有するジルコニアの組成物を焼成して焼結体にする焼結工程を含み、
前記焼結工程において、1000℃から最高温度までの昇温速度が5℃/分以下であり、
前記焼結体の外部の透光性ΔLをΔL1と表記し、
前記焼結体の内部の透光性ΔLをΔL2と表記し、
ΔL1からΔL2への変化率を以下の式:
[ΔLの変化率]=(ΔL2−ΔL1)/ΔL1×100
で表すとき、
ΔLの変化率は−15%以上であり、かつ、正の値とならず、
ただし、前記外部とは、焼結後の無加工の外表面から深さ4mmまでの部分であり、
前記内部とは、前記外表面から深さ4mmよりも深い部分であり、
前記内部及び前記外部のL*a*b*表色系(JISZ8781)における色度(色空間)のL*値について、F11を光源として用いて、試料の背景を白色にして測定したL*値を第1のL*値とし、
第1のL*値を測定した同一の試料について、試料の背景を黒色にして測定したL*値を第2のL*値とするとき、
ΔLは、前記第1のL*値から前記第2のL*値を控除した値であり、
前記焼結体は、前記外表面のどの面からみても深さ4mmよりも深い前記内部が存在し、
前記焼結体の体積は、27000mm3以下である、
ジルコニア焼結体の製造方法。 - 前記昇温速度が3℃/分以下である、請求項13に記載のジルコニア焼結体の製造方法。
- 前記最高温度が1550℃以上である、請求項13又は14に記載のジルコニア焼結体の製造方法。
- 前記組成物を六面体又は円柱体形状に成形する成形工程をさらに含む、請求項13〜15のいずれか一項に記載のジルコニア焼結体の製造方法。
- 前記組成物を直方体に成形する成形工程をさらに含み、
前記直方体の寸法は、長さ13mm〜17mm、幅15mm〜19mm、高さ18mm〜32mmである、
請求項13〜15のいずれか一項に記載のジルコニア焼結体の製造方法。 - 前記組成物を焼結に至らない温度で焼成して仮焼体を作製する仮焼工程をさらに含み、
前記焼結工程において、前記仮焼体を焼成する、請求項13〜17のいずれか一項に記載のジルコニア焼結体の製造方法。 - 前記焼結工程において、空気よりも酸素濃度が高い雰囲気下で焼成を行う、請求項13〜18のいずれか一項に記載のジルコニア焼結体の製造方法。
- 請求項13〜19のいずれか一項に記載のジルコニア焼結体の製造方法によって作製したジルコニア焼結体を成形する加工工程を含む、歯科用製品の製造方法。
- 前記ジルコニア焼結体に、加工装置に取り付けるための取り付け具を接合する工程をさらに含み、
前記加工工程において、前記加工装置で前記ジルコニア焼結体の成形を行う、請求項20に記載の歯科用製品の製造方法。 - 前記加工工程において、前記ジルコニア焼結体を歯冠形状に成形する、請求項20又は21に記載の歯科用製品の製造方法。