JP6752403B1 - 電子装置の製造方法 - Google Patents
電子装置の製造方法 Download PDFInfo
- Publication number
- JP6752403B1 JP6752403B1 JP2020536710A JP2020536710A JP6752403B1 JP 6752403 B1 JP6752403 B1 JP 6752403B1 JP 2020536710 A JP2020536710 A JP 2020536710A JP 2020536710 A JP2020536710 A JP 2020536710A JP 6752403 B1 JP6752403 B1 JP 6752403B1
- Authority
- JP
- Japan
- Prior art keywords
- adhesive resin
- adhesive
- mass
- electronic device
- manufacturing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
ファンアウト型WLPの作製方法のひとつであるeWLB(Embedded Wafer Level Ball Grid Array)では、支持基板に貼り付けた粘着性フィルム上に、半導体チップ等の複数の電子部品を離間させた状態で仮固定し、封止材により複数の電子部品を一括封止する手法が取られる。ここで、粘着性フィルムは、封止工程等においては電子部品および支持基板に固着させる必要があり、封止後は支持基板とともに封止された電子部品から除去する必要がある。
本発明は上記事情に鑑みてなされたものであり、封止工程における電子部品の位置ずれを抑制することが可能な電子装置の製造方法を提供するものである。
基材層と、上記基材層の第1面側に設けられ、かつ、電子部品を仮固定するための粘着性樹脂層(A)と、上記基材層の第2面側に設けられ、かつ、外部刺激により粘着力が低下する粘着性樹脂層(B)と、を備える粘着性フィルムと、
上記粘着性フィルムの上記粘着性樹脂層(A)に貼り付けられた電子部品と、
上記粘着性フィルムの上記粘着性樹脂層(B)に貼り付けられた支持基板と、を備える構造体を準備する準備工程と、
上記構造体を加熱するプリベーク工程と、
封止材により上記電子部品を封止する封止工程と、
を少なくとも備える電子装置の製造方法。
[2]
上記[1]に記載の電子装置の製造方法において、
上記プリベーク工程における加熱温度が160℃未満である電子装置の製造方法。
[3]
上記[1]または[2]に記載の電子装置の製造方法において、
上記プリベーク工程における加熱温度が70℃以上である電子装置の製造方法。
[4]
上記[1]乃至[3]のいずれか一つに記載の電子装置の製造方法において、
上記封止工程の後に、外部刺激を与えることにより上記粘着性樹脂層(B)の粘着力を低下させて上記構造体から上記支持基板を剥離する第1剥離工程をさらに備える電子装置の製造方法。
[5]
上記[4]に記載の電子装置の製造方法において、
上記第1剥離工程の後に、上記電子部品から上記粘着性フィルムを剥離する第2剥離工程をさらに備える電子装置の製造方法。
[6]
上記[1]乃至[5]のいずれか一つに記載の電子装置の製造方法において、
上記封止材がエポキシ樹脂系封止材である電子装置の製造方法。
[7]
上記[1]乃至[6]のいずれか一つに記載の電子装置の製造方法において、
上記粘着性樹脂層(A)を構成する粘着性樹脂が(メタ)アクリル系粘着性樹脂、シリコーン系粘着性樹脂、ウレタン系粘着性樹脂、オレフィン系粘着性樹脂およびスチレン系粘着性樹脂から選択される一種または二種以上を含む電子装置の製造方法。
はじめに、本実施形態に係る電子装置の製造方法について説明する。図1は、本発明に係る実施形態の粘着性フィルム50の構造の一例を模式的に示した断面図である。
図2および図3は、本発明に係る実施形態の電子装置の製造方法の一例を模式的に示した断面図である。
本実施形態に係る電子装置の製造方法は、以下の3つの工程を少なくとも備えている。
(1)基材層10と、基材層10の第1面10A側に設けられ、かつ、電子部品70を仮固定するための粘着性樹脂層(A)と、基材層10の第2面10B側に設けられ、かつ、外部刺激により粘着力が低下する粘着性樹脂層(B)と、を備える粘着性フィルム50と、粘着性フィルム50の粘着性樹脂層(A)に貼り付けられた電子部品70と、粘着性フィルム50の粘着性樹脂層(B)に貼り付けられた支持基板80と、を備える構造体100を準備する準備工程
(2)構造体100を加熱するプリベーク工程
(3)封止材60により電子部品70を封止する封止工程
本発明者らは、上記課題を達成するために鋭意検討を重ねた。その結果、電子部品を封止する工程において、封止材の流動による圧力に耐え切れずに、電子部品の位置ずれが生じてしまうことを知見した。さらに、粘着性フィルムに含まれる水分由来のアウトガス、特に支持基板に貼り付けられる側の粘着性樹脂層に含まれる水分由来のアウトガスによって、電子部品の位置ずれが生じてしまうことを知見した。
本発明者らは、上記知見をもとにさらに検討を重ねた。その結果、封止工程の前に構造体100を加熱するプリベーク工程をおこなうことによって、電子部品70に対する粘着性樹脂層(A)の粘着力が向上し、封止工程における電子部品の位置ずれを抑制できることを初めて見出した。
すなわち、本実施形態に係る電子装置の製造方法によれば、封止工程の前に構造体100を加熱するプリベーク工程をおこなうことで、電子部品70に対する粘着性樹脂層(A)の粘着力が向上するため、電子部品を封止する工程において、封止材60の流動による圧力や水分由来のアウトガスによって電子部品70の位置がずれてしまうことを抑制することができる。
以上のように、本実施形態に係る電子装置の製造方法によれば、封止工程における電子部品の位置ずれを抑制することが可能となる。
準備工程では、粘着性フィルム50と、粘着性フィルム50の粘着性樹脂層(A)に貼り付けられた電子部品70と、粘着性フィルム50の粘着性樹脂層(B)に貼り付けられた支持基板80と、を備える構造体100を準備する。
まず、支持基板80上に、粘着性フィルム50を、粘着性樹脂層(B)が支持基板80側となるように貼着する。粘着性樹脂層(B)上にはセパレータと称する保護フィルムが貼付けられていてもよく、当該保護フィルムを剥がし、粘着性樹脂層(B)の露出面を支持基板80表面に貼着することができる。
支持基板80としては、例えば、石英基板、ガラス基板、SUS基板等を使用することができる。
電子部品70としては、例えば、IC、LSI、ディスクリート、発光ダイオード、受光素子等の半導体チップや半導体パネル、半導体パッケージ等を挙げることができる。
プリベーク工程では、準備工程で得られた構造体100を加熱する。こうすることで、粘着性フィルム50において、電子部品70に対する粘着性樹脂層(A)の粘着力を向上させることができる。その結果、封止工程において、封止材60により電子部品70を封止する際に、封止材60の流動による圧力や水分由来のアウトガスによって電子部品70の位置がずれてしまうことを抑制することができる。
構造体100を加熱する方法は特に限定されるものではないが、例えば、オーブン、ドライヤー、加熱ロール、乾燥炉等の一般的に公知の加熱処理方法を用いることができる。
次いで、封止材60により電子部品70を封止する。
封止材60により電子部品70を覆い、例えば150℃以下の温度で封止材60を硬化させて、電子部品70を封止する。
また、封止材60の形態としては特に限定されないが、例えば、顆粒状、シート状または液状である。
特に、粘着性フィルム50への封止材60の親和性がより良好になり、電子部品70をより一層ムラなく封止することが可能となる点から、液状のエポキシ樹脂系封止材が好ましい。
このようなエポキシ樹脂系封止材としては、例えば、ナガセケムテックス社製のT693/R4000シリーズやT693/R1000シリーズ、T693/R5000シリーズ等を用いることができる。
本実施形態に係る電子装置の製造方法において、図3に示すように、(3)封止工程の後に、外部刺激を与えることにより粘着性樹脂層(B)の粘着力を低下させて構造体100から支持基板80を剥離する第1剥離工程をさらに備えてもよい。
支持基板80は、例えば、電子部品70を封止した後、150℃を超える温度に加熱して、粘着性樹脂層(B)の接着力を低下させることにより、粘着性フィルム50から容易に除去することができる。
本実施形態に係る電子装置の製造方法において、図3に示すように、第1剥離工程の後に、電子部品70から粘着性フィルム50を剥離し、電子装置200を得る第2剥離工程をさらに備えてもよい。
電子部品70から粘着性フィルム50を剥離する方法としては、例えば、機械的に剥離する方法や、粘着性フィルム50表面の粘着力を低下させてから剥離する方法等が挙げられる。
本実施形態に係る電子装置の製造方法において、図3に示すように、得られた電子装置200の露出面に、配線層310およびバンプ320を形成し、電子装置300を得る工程(6)をさらに備えてもよい。
電子装置300のダイシングは、公知の方法で行うことができる。
以下、本実施形態に係る粘着性フィルム50について説明する。
図1は、本発明に係る実施形態の粘着性フィルム50の構造の一例を模式的に示した断面図である。
基材層10は、粘着性フィルム50の取り扱い性や機械的特性、耐熱性等の特性をより良好にすることを目的として設けられる層である。
基材層10は特に限定されないが、例えば、樹脂フィルムが挙げられる。
上記樹脂フィルムを構成する樹脂としては、公知の熱可塑性樹脂を用いることができる。例えば、ポリエチレン、ポリプロピレン、ポリ(4−メチル−1−ペンテン)、ポリ(1−ブテン)等のポリオレフィン;ポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリエチレンナフタレート等のポリエステル;ナイロン−6、ナイロン−66、ポリメタキシレンアジパミド等のポリアミド;ポリアクリレート;ポリメタアクリレート;ポリ塩化ビニル;ポリ塩化ビニリデン;ポリイミド;ポリエーテルイミド;エチレン・酢酸ビニル共重合体;ポリアクリロニトリル;ポリカーボネート;ポリスチレン;アイオノマー;ポリスルホン;ポリエーテルスルホン;ポリフェニレンエーテル等から選択される一種または二種以上を挙げることができる。
これらの中でも、透明性や機械的強度、価格等のバランスに優れる観点から、ポリプロピレン、ポリエチレンテレフタレート、ポリエチレンナフタレート、ポリアミド、ポリイミドから選択される一種または二種以上が好ましく、ポリエチレンテレフタレート、ポリエチレンナフタレートから選択される少なくとも一種がより好ましい。
また、基材層10を形成するために使用する樹脂フィルムの形態としては、延伸フィルムであってもよいし、一軸方向または二軸方向に延伸したフィルムであってもよいが、基材層10の機械的強度を向上させる観点から、一軸方向または二軸方向に延伸したフィルムであることが好ましい。
基材層10は、他の層との接着性を改良するために、表面処理を行ってもよい。具体的には、コロナ処理、プラズマ処理、アンダーコート処理、プライマーコート処理等を行ってもよい。
粘着性樹脂層(A)は、基材層10の一方の面側に設けられる層であり、例えば、電子装置の製造工程において封止材により電子部品を封止する際に、電子部品の表面に接触して電子部品を仮固定するための層である。
粘着性樹脂(A1)としては、例えば、(メタ)アクリル系粘着性樹脂(a)、シリコーン系粘着性樹脂、ウレタン系粘着性樹脂、オレフィン系粘着性樹脂、スチレン系粘着性樹脂等が挙げられる。
これらの中でも粘着力の調整を容易にする観点等から、(メタ)アクリル系粘着性樹脂(a)が好ましい。
放射線架橋型粘着性樹脂層としては、紫外線架橋型粘着性樹脂層が好ましい。
本実施形態において、(メタ)アクリル酸アルキルエステルとは、アクリル酸アルキルエステル、メタクリル酸アルキルエステル、またはこれらの混合物を意味する。
本実施形態に係る(メタ)アクリル系粘着性樹脂(a)において、(メタ)アクリル酸アルキルエステルモノマー単位(a1)の含有量は、(メタ)アクリル系粘着性樹脂(a)中の全モノマー単位の合計を100質量%としたとき、10質量%以上98.9質量%以下であることが好ましく、50質量%以上97質量%以下であることがより好ましく、85質量%以上95質量%以下であることがさらに好ましい。
本実施形態に係る(メタ)アクリル系粘着性樹脂(a)において、モノマー単位(a2)の含有量は、(メタ)アクリル系粘着性樹脂(a)中の全モノマー単位の合計を100質量%としたとき、1質量%以上40質量%以下であることが好ましく、1質量%以上20質量%以下であることがより好ましく、1質量%以上10質量%以下であることがさらに好ましい。
重合性界面活性剤は、モノマー(a1)、モノマー(a2)およびモノマー(a3)と共重合する性質を有すると共に、乳化重合する場合には乳化剤としての作用を有する。
本実施形態に係る(メタ)アクリル系粘着性樹脂(a)において、重合性界面活性剤の含有量は、(メタ)アクリル系粘着性樹脂(a)中の全モノマー単位の合計を100質量%としたとき、0.1質量%以上30質量%以下であることが好ましく、0.1質量%以上15質量%以下であることがより好ましく、0.1質量%以上20質量%以下であることがさらに好ましく、0.1質量%以上5質量%以下であることが特に好ましい。
ラジカル重合反応によって重合する際、ラジカル重合開始剤として、ベンゾイルパーオキサイド、ジ−t−ブチルパーオキサイド、ジクミルパーオキサイド、3,3,5−トリメチルヘキサノイルパーオキサイド、ジ−2−エチルヘキシルパーオキシジカーボネート、メチルエチルケトンパーオキサイド、t−ブチルパーオキシフタレート、t−ブチルパーオキシベンゾエート、ジ−t−ブチルパーオキシアセテート、t−ブチルパーオキシイソブチレート、t−ブチルパーオキシ−2−ヘキサノエート、t−ブチルパーオキシ−2−エチルヘキサノエート、t−ブチルパーオキシ−3,5,5−トリメチルヘキサノエート、アセチルパーオキサイド、イソブチリルパーオキサイド、オクタノイルパーオキサイド、t−ブチルパーオキサイド、ジ−t−アミルパーオキサイド等の有機過酸化物;過硫酸アンモニウム、過硫酸カリウム、過硫酸ナトリウム等の無機過酸化物;2,2'−アゾビスイソブチロニトリル、2,2'−アゾビス−2−メチルブチロニトリル、4,4'−アゾビス−4−シアノバレリックアシッド等のアゾ化合物が挙げられる。
架橋性の官能基を1分子中に2個以上有する架橋剤(A2)は、粘着性樹脂(A1)が有する官能基と反応させ、粘着力および凝集力を調整するために用いる。
このような架橋剤(A2)としては、ソルビトールポリグリシジルエーテル、ポリグリセロールポリグリシジルエーテル、ペンタエリスリトールポリグリシジルエーテル、ジグリセロールポリグリシジルエーテル、グリセロールポリグリシジルエーテル、ネオペンチルグリコールジグリシジルエーテル、レソルシンジグリシジルエーテル等のエポキシ系化合物;テトラメチレンジイソシアネート、ヘキサメチレンジイソシアネート、トリメチロールプロパンのトルエンジイソシアネート3付加物、ポリイソシアネート、ジフェニルメタンジイソシアネート、トリレンジイソシアネート等のイソシアネート系化合物;トリメチロールプロパン−トリ−β−アジリジニルプロピオネート、テトラメチロールメタン−トリ−β−アジリジニルプロピオネート、N,N'−ジフェニルメタン−4,4'−ビス(1−アジリジンカルボキシアミド)、N,N'−ヘキサメチレン−1,6−ビス(1−アジリジンカルボキシアミド)、N,N'−トルエン−2,4−ビス(1−アジリジンカルボキシアミド)、トリメチロールプロパン−トリ−β−(2−メチルアジリジン)プロピオネート等のアジリジン系化合物;N,N,N',N'−テトラグリシジル−m−キシレンジアミン、1,3−ビス(N,N'−ジグリシジルアミノメチル)シクロヘキサン等の4官能性エポキシ系化合物;ヘキサメトキシメチロールメラミン等のメラミン系化合物等が挙げられる。これらは単独で使用してもよいし、2種以上を併用してもよい。
これらの中でも、エポキシ系化合物、イソシアネート系化合物およびアジリジン系化合物から選択される一種または二種以上を含むことが好ましい。
粘着性樹脂層(A)中の架橋剤(A2)の含有量は、粘着性樹脂層(A)の耐熱性や密着力とのバランスを向上させる観点から、粘着性樹脂(A1)100質量部に対し、0.1質量部以上15質量部以下であることが好ましい。
中でも有機溶剤に溶解した粘着剤塗布液が好ましい。有機溶剤は特に限定されず、溶解性や乾燥時間を鑑みて公知の中から適宜選択すればよい。有機溶剤としては、酢酸エチル、酢酸メチル等のエステル系;アセトン、MEK等のケトン系;ベンゼン、トルエン、エチルベンゼン等の芳香族系;ヘプタン、ヘキサン、シクロヘキサン等の直鎖ないし環状脂肪族系;イソプロパノール、ブタノール等のアルコール系を例示することができる。有機溶剤として酢酸エチル、トルエンが好ましい。これらの溶剤は、1種単独で用いてもよいし、2種以上を混合して用いてもよい。
粘着剤塗布液を塗布する方法としては、従来公知の塗布方法、例えば、ロールコーター法、リバースロールコーター法、グラビアロール法、バーコート法、コンマコーター法、ダイコーター法等が採用できる。塗布された粘着剤の乾燥条件には特に制限はないが、一般的には、80〜200℃の温度範囲において、10秒〜10分間乾燥することが好ましい。さらに好ましくは、80〜170℃において、15秒〜5分間乾燥する。架橋剤と粘着剤との架橋反応を十分に促進させるために、粘着剤塗布液の乾燥が終了した後、40〜80℃において5〜300時間程度加熱してもよい。
また、基材層10と粘着性樹脂層(A)とは共押出成形によって形成してもよいし、フィルム状の基材層10とフィルム状の粘着性樹脂層(A)とをラミネート(積層)して形成してもよい。
本実施形態に係る粘着性フィルム50は、基材層10の第1面10Aとは反対側の第2面10B側に外部刺激により粘着力が低下する粘着性樹脂層(B)を備える。
これにより、外部刺激を与えることで支持基板80から粘着性フィルム50を容易に剥離することができる。
ここで、外部刺激により粘着力が低下する粘着性樹脂層(B)としては、例えば、加熱により粘着力が低下する加熱剥離型の粘着性樹脂層や、放射線により粘着力が低下する放射線剥離型の粘着性樹脂層等が挙げられる。これらの中でも加熱により粘着力が低下する加熱剥離型の粘着性樹脂層が好ましい。
加熱剥離型の粘着性樹脂層としては、例えば、気体発生成分を含む加熱膨張型粘着剤、膨張して粘着力を低減できる熱膨張性の微小球を含む加熱膨張型粘着剤、熱により接着剤成分が架橋反応することで接着力が低下する加熱膨張型粘着剤等により構成された粘着性樹脂層が挙げられる。
ここで、150℃を超える温度で加熱することで接着力が低下または喪失することは、例えば、粘着性樹脂層(B)側をステンレス板に貼り付け、140℃で1時間の加熱処理をおこない、次いで、150℃を超える温度で2分間加熱した後に測定される、ステンレス板からの剥離強度により評価することができる。150℃を超える温度で加熱する際の具体的な加熱温度は、気体が発生する温度や熱膨張性の微小球が熱膨張する温度よりも高い温度に設定され、発生する気体や熱膨張性の微小球の種類によって適宜設定される。本実施形態において、接着力が喪失するとは、例えば、23℃、引張速度300mm/分の条件で測定される180°剥離強度が0.5N/25mm未満になる場合をいう。
熱膨張性の微小球は粘着性樹脂に添加することができる。
気体が発生する温度や熱膨張性の微小球が熱膨張する温度が、150℃を超える温度になるように設計することが好ましい。
本実施形態において、(メタ)アクリル酸アルキルエステルとは、アクリル酸アルキルエステル、メタクリル酸アルキルエステル、またはこれらの混合物を意味する。
本実施形態に係る(メタ)アクリル系粘着性樹脂(b)において、(メタ)アクリル酸アルキルエステルモノマー単位(b1)の含有量は、(メタ)アクリル系粘着性樹脂(b)中の全モノマー単位の合計を100質量%としたとき、10質量%以上98.9質量%以下であることが好ましく、50質量%以上97質量%以下であることがより好ましく、85質量%以上95質量%以下であることがさらに好ましい。
本実施形態に係る(メタ)アクリル系粘着性樹脂(b)において、モノマー単位(b2)の含有量は、(メタ)アクリル系粘着性樹脂(b)中の全モノマー単位の合計を100質量%としたとき、1質量%以上40質量%以下であることが好ましく、1質量%以上20質量%以下であることがより好ましく、1質量%以上10質量%以下であることがさらに好ましい。
重合性界面活性剤は、モノマー(b1)、モノマー(b2)およびモノマー(b3)と共重合する性質を有すると共に、乳化重合する場合には乳化剤としての作用を有する。
本実施形態に係る(メタ)アクリル系粘着性樹脂(b)において、重合性界面活性剤の含有量は、(メタ)アクリル系粘着性樹脂(b)中の全モノマー単位の合計を100質量%としたとき、0.1質量%以上30質量%以下であることが好ましく、0.1質量%以上15質量%以下であることがより好ましく、0.1質量%以上20質量%以下であることがさらに好ましく、0.1質量%以上5質量%以下であることが特に好ましい。
ラジカル重合反応によって重合する際、ラジカル重合開始剤として、ベンゾイルパーオキサイド、ジ−t−ブチルパーオキサイド、ジクミルパーオキサイド、3,3,5−トリメチルヘキサノイルパーオキサイド、ジ−2−エチルヘキシルパーオキシジカーボネート、メチルエチルケトンパーオキサイド、t−ブチルパーオキシフタレート、t−ブチルパーオキシベンゾエート、ジ−t−ブチルパーオキシアセテート、t−ブチルパーオキシイソブチレート、t−ブチルパーオキシ−2−ヘキサノエート、t−ブチルパーオキシ−2−エチルヘキサノエート、t−ブチルパーオキシ−3,5,5−トリメチルヘキサノエート、アセチルパーオキサイド、イソブチリルパーオキサイド、オクタノイルパーオキサイド、t−ブチルパーオキサイド、ジ−t−アミルパーオキサイド等の有機過酸化物;過硫酸アンモニウム、過硫酸カリウム、過硫酸ナトリウム等の無機過酸化物;2,2'−アゾビスイソブチロニトリル、2,2'−アゾビス−2−メチルブチロニトリル、4,4'−アゾビス−4−シアノバレリックアシッド等のアゾ化合物が挙げられる。
架橋性の官能基を1分子中に2個以上有する架橋剤(B2)は、粘着性樹脂(B1)が有する官能基と反応させ、粘着力および凝集力を調整するために用いる。
このような架橋剤(B2)としては、ソルビトールポリグリシジルエーテル、ポリグリセロールポリグリシジルエーテル、ペンタエリスリトールポリグリシジルエーテル、ジグリセロールポリグリシジルエーテル、グリセロールポリグリシジルエーテル、ネオペンチルグリコールジグリシジルエーテル、レソルシンジグリシジルエーテル等のエポキシ系化合物;テトラメチレンジイソシアネート、ヘキサメチレンジイソシアネート、トリメチロールプロパンのトルエンジイソシアネート3付加物、ポリイソシアネート、ジフェニルメタンジイソシアネート、トリレンジイソシアネート等のイソシアネート系化合物;トリメチロールプロパン−トリ−β−アジリジニルプロピオネート、テトラメチロールメタン−トリ−β−アジリジニルプロピオネート、N,N'−ジフェニルメタン−4,4'−ビス(1−アジリジンカルボキシアミド)、N,N'−ヘキサメチレン−1,6−ビス(1−アジリジンカルボキシアミド)、N,N'−トルエン−2,4−ビス(1−アジリジンカルボキシアミド)、トリメチロールプロパン−トリ−β−(2−メチルアジリジン)プロピオネート等のアジリジン系化合物;N,N,N',N'−テトラグリシジル−m−キシレンジアミン、1,3−ビス(N,N'−ジグリシジルアミノメチル)シクロヘキサン等の4官能性エポキシ系化合物;ヘキサメトキシメチロールメラミン等のメラミン系化合物等が挙げられる。これらは単独で使用してもよいし、2種以上を併用してもよい。
これらの中でも、エポキシ系化合物、イソシアネート系化合物およびアジリジン系化合物から選択される一種または二種以上を含むことが好ましい。
粘着性樹脂層(B)中の架橋剤(B2)の含有量は、粘着性樹脂(B1)100質量部に対し、0.1質量部以上10質量部以下であることが好ましく、0.5質量部以上5質量部以下であることがより好ましい。
粘着剤塗布液を塗布する方法としては、従来公知の塗布方法、例えば、ロールコーター法、リバースロールコーター法、グラビアロール法、バーコート法、コンマコーター法、ダイコーター法等が採用できる。塗布された粘着剤の乾燥条件には特に制限はないが、一般的には、80〜200℃の温度範囲において、10秒〜10分間乾燥することが好ましい。さらに好ましくは、80〜170℃において、15秒〜5分間乾燥する。架橋剤と粘着剤との架橋反応を十分に促進させるために、粘着剤塗布液の乾燥が終了した後、40〜80℃において5〜300時間程度加熱してもよい。
また、基材層10と粘着性樹脂層(B)とは共押出成形によって形成してもよいし、フィルム状の基材層10とフィルム状の粘着性樹脂層(B)とをラミネート(積層)して形成してもよい。
本実施形態に係る粘着性フィルム50は、本実施形態の効果を損なわない範囲で、基材層10と粘着性樹脂層(A)との間あるいは基材層10と粘着性樹脂層(B)との間に、例えば凹凸吸収層、衝撃吸収層、易接着層等がさらに設けられていてもよい。
脱イオンを行った純水中に、重合開始剤として4,4’−アゾビス−4−シアノバレリックアシッド(大塚化学(株)製、商品名:ACVA)を0.5質量部、モノマー(a1)としてアクリル酸−n−ブチルを74.3質量部、およびメタクリル酸メチルを13.7質量部、モノマー(a2)としてメタクリル酸−2−ヒドロキシエチルを9質量部、重合性界面活性剤としてポリオキシエチレンノニルフェニルエーテルの硫酸エステルのアンモニウム塩のベンゼン環に重合性の1−プロペニル基を導入したもの(第一工業製薬(株)製;商品名:アクアロンHS−1025)を3質量部それぞれ投入し、攪拌下で70〜72℃において8時間乳化重合を実施し、アクリル系樹脂エマルションを得た。これをアンモニア水で中和(pH=7.0)し、固形分濃度42.5%の粘着性樹脂溶液SA1を得た。
脱イオンを行った純水中に、重合開始剤として過硫酸アンモニウムを0.5質量部、モノマー(a1)としてアクリル酸−2−エチルヘキシルを63質量部、アクリル酸−n−ブチルを21質量部、およびメタクリル酸メチルを9質量部、モノマー(a2)としてメタクリル酸−2−ヒドロキシエチルを3質量部、モノマー(a3)としポリテトラメチレングリコールジアクリレート(日本油脂(株)製、商品名;ADT−250)を1質量部、重合性界面活性剤としてポリオキシエチレンノニルフェニルエーテルの硫酸エステルのアンモニウム塩のベンゼン環に重合性の1−プロペニル基を導入したもの(第一工業製薬(株)製;商品名:アクアロンHS−1025)を2質量部それぞれ投入し、攪拌下で70〜72℃において8時間乳化重合を実施し、アクリル系樹脂エマルションを得た。これをアンモニア水で中和(pH=7.0)し、固形分濃度56.5%の粘着性樹脂溶液SA2を得た。
粘着性樹脂溶液SA1を57.4質量部、粘着性樹脂溶液SA2を42.6質量部、ジメチルエタノールアミンを0.4質量部、架橋剤であるエポキシ系化合物(ナガセケムテックス社製、Ex−1610)を3.4質量部、それぞれ混合して、粘着剤塗布液A1を得た。
酢酸エチルおよびトルエンを含む混合溶剤中に、重合開始剤としてt−ブチルパーオキシ−2−エチルヘキサノエート(日本油脂社製、商品名:パーブチルO(登録商標))を0.536質量部、モノマー(b1)としてアクリル酸2−エチルヘキシルを34.9重量部、アクリル酸−n−ブチルを41質量部、およびアクリル酸エチルを14.7質量部、モノマー(b2)としてメタクリル酸−2−ヒドロキシエチルを9.4質量部それぞれ投入し、攪拌下で83〜87℃において11時間溶液重合を実施し、固形分濃度45質量%のアクリル系樹脂溶液を得た。これを粘着性樹脂溶液SB1とした。
粘着性樹脂溶液SB1を100質量部、イソシアネート系架橋剤(三井化学(株)製、商品名:オレスターP49−75S)0.9質量部(粘着性樹脂100質量部に対し、2質量部)それぞれ混合し、酢酸エチルで固形分濃度を40%に調整して粘着剤塗布液B1を得た。
粘着性樹脂溶液SB1を100質量部、重合ロジンエステル系粘着付与剤(荒川化学工業(株)製、商品名:ペンセルD−125)2.25重量部(粘着性樹脂100質量部に対し、5質量部)、イソシアネート系架橋剤(三井化学(株)製、商品名:オレスターP49−75S)1.2質量部(粘着性樹脂100質量部に対し、2質量部)、熱膨張性微小球(積水化学工業(株)製、商品名:アドバンセルEM−503)を6.75質量部(粘着性樹脂100質量部に対し、15質量部)それぞれ混合し、酢酸エチルで固形分濃度を30%に調整して粘着剤塗布液B2を調製した。
基材層であるポリエチレンテレフタレート(PET)フィルム(厚さ38μm)上に、粘着剤塗布液A1を乾燥させて形成した厚さ10μmの粘着性樹脂層(A)を設けた。次いで、PETフィルムの粘着性樹脂層(A)とは反対側の表面に、粘着剤塗布液B1を乾燥させて形成した厚さ20μmの凹凸吸収層を設け、その上に、粘着剤塗布液B2を乾燥させて形成した厚さが30μmの加熱剥離型の粘着性樹脂層(B)を設け粘着性フィルムを得た。
得られた粘着性フィルムの粘着性樹脂層(B)側を320mm角のSUS基板上に接着し、電子部品として、5mm角の半導体チップを2mm間隔の格子状となるように粘着性フィルムの粘着性樹脂層(A)上に載せて密着させ、構造体を得た。
次いで、得られた構造体に対して、100℃で30分間加熱処理することによって構造体をプリベークした。
○:すべての電子部品の位置ずれがない
×:少なくとも一つの電子部品が移動し、元の位置からずれている
さらに、プリベーク後の構造体について、目視により、粘着性樹脂層(B)の熱膨張の有無を観察し、以下の基準で評価した。得られた結果を表1に示す。
○:粘着性樹脂層(B)の外観に変化なし
×:粘着性樹脂層(B)が膨張している
次いで、目視により、半導体チップの位置ずれを観察し、以下の基準で評価した。得られた結果を表1に示す。
○:すべての電子部品の位置ずれがない
×:少なくとも一つの電子部品が移動し、元の位置からずれている
プリベーク工程における加熱処理の条件を表1に示す条件に変えた以外は実施例1と同様の方法で構造体および電子装置を作製し、実施例1と同様の評価をそれぞれおこなった。
得られた結果を表1に示す。
プリベーク工程をおこなわない以外は実施例1と同様の方法で構造体および電子装置を作製し、実施例1と同様の評価をそれぞれおこなった。
得られた結果を表1に示す。
B 粘着性樹脂層
10 基材層
10A 第1面
10B 第2面
50 粘着性フィルム
60 封止材
70 電子部品
80 支持基板
100 構造体
200 電子装置
300 電子装置
310 配線層
320 バンプ
400 電子装置
Claims (7)
- 基材層と、前記基材層の第1面側に設けられ、かつ、電子部品を仮固定するための粘着性樹脂層(A)と、前記基材層の第2面側に設けられ、かつ、外部刺激により粘着力が低下する粘着性樹脂層(B)と、を備える粘着性フィルムと、
前記粘着性フィルムの前記粘着性樹脂層(A)に貼り付けられた電子部品と、
前記粘着性フィルムの前記粘着性樹脂層(B)に貼り付けられた支持基板と、を備える構造体を準備する準備工程と、
前記構造体を加熱するプリベーク工程と、
封止材により前記電子部品を封止する封止工程と、
を少なくとも備える電子装置の製造方法。 - 請求項1に記載の電子装置の製造方法において、
前記プリベーク工程における加熱温度が160℃未満である電子装置の製造方法。 - 請求項1または2に記載の電子装置の製造方法において、
前記プリベーク工程における加熱温度が70℃以上である電子装置の製造方法。 - 請求項1乃至3のいずれか一項に記載の電子装置の製造方法において、
前記封止工程の後に、外部刺激を与えることにより前記粘着性樹脂層(B)の粘着力を低下させて前記構造体から前記支持基板を剥離する第1剥離工程をさらに備える電子装置の製造方法。 - 請求項4に記載の電子装置の製造方法において、
前記第1剥離工程の後に、前記電子部品から前記粘着性フィルムを剥離する第2剥離工程をさらに備える電子装置の製造方法。 - 請求項1乃至5のいずれか一項に記載の電子装置の製造方法において、
前記封止材がエポキシ樹脂系封止材である電子装置の製造方法。 - 請求項1乃至6のいずれか一項に記載の電子装置の製造方法において、
前記粘着性樹脂層(A)を構成する粘着性樹脂が(メタ)アクリル系粘着性樹脂、シリコーン系粘着性樹脂、ウレタン系粘着性樹脂、オレフィン系粘着性樹脂およびスチレン系粘着性樹脂から選択される一種または二種以上を含む電子装置の製造方法。