JP6681601B2 - 光学部材、照明カバー及び照明器具 - Google Patents
光学部材、照明カバー及び照明器具 Download PDFInfo
- Publication number
- JP6681601B2 JP6681601B2 JP2016044254A JP2016044254A JP6681601B2 JP 6681601 B2 JP6681601 B2 JP 6681601B2 JP 2016044254 A JP2016044254 A JP 2016044254A JP 2016044254 A JP2016044254 A JP 2016044254A JP 6681601 B2 JP6681601 B2 JP 6681601B2
- Authority
- JP
- Japan
- Prior art keywords
- light
- optical member
- resin
- silicone
- refractive index
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
図1に本実施形態に係る光学部材の一例を示す。本実施形態に係る光学部材11は、透光性樹脂基材12と透光性樹脂基材12の表面に設けられる光拡散層17とを備える。光拡散層17は、屈折率が1.49以下の透光性樹脂13と、シリコーン14に複数の無機粒子15が内包された無機粒子内包シリコーン粒子16とを含有する。
次に、本実施形態の照明カバー40について説明する。本実施形態の照明カバー40は光学部材11を用いる。すなわち、本実施形態の照明カバー40は光学部材11を備える。
次に、本実施形態の照明器具100について説明する。本実施形態に係る照明器具100は光源部30と光源部30を覆う照明カバー40とを備える。照明器具100は、開口部21を有する器具本体20と、器具本体20に設けられる光源部30と、開口部21を覆う照明カバー40と、を備えることもできる。
透光性樹脂の固形分100質量部に対し、無機粒子内包シリコーン粒子を100質量部添加した。透光性樹脂として、関東電化工業株式会社製のエフクリア(登録商標)KD200を使用した。なお、エフクリア(登録商標)KD200はポリフルオロオレフィン共重合体を含有し、屈折率は1.42である。また、無機粒子内包シリコーン粒子として、日興リカ株式会社製のMSP−AS02を使用した。なお、MSP−AS02はアルミナ微粒子をシリコーンで内包しており、アルミナ微粒子の屈折率は1.76、アルミナ微粒子の平均粒子径は0.2〜0.7μmである。また、MSP−AS02の平均粒子径は2μmである。シリコーンの屈折率は1.42である。
透光性樹脂の固形分100質量部に対し、無機粒子内包シリコーン粒子を150質量部添加した以外は実施例1と同様の手順で照明器具を作成した。
実施例1で用いたMSP−AS02に代えて、日興リカ株式会社製のMSP−AS04を無機粒子内包シリコーン粒子として用いた。また、透光性樹脂の固形分100質量部に対し、無機粒子内包シリコーン粒子を150質量部添加した。それ以外は実施例1と同様の手順で照明器具を作成した。なお、MSP−AS04はアルミナ微粒子を内包しており、アルミナ微粒子の屈折率は1.76、アルミナ微粒子の平均粒子径は0.2〜0.7μmである。また、MSP−AS04の平均粒子径は4μmである。シリコーンの屈折率は1.42である。
実施例1で用いたMSP−AS02に代えて、日興リカ株式会社製のMSP−TS04を無機粒子内包シリコーン粒子として用いた。また、透光性樹脂の固形分100質量部に対し、無機粒子内包シリコーン粒子を80質量部添加した。それ以外は実施例1と同様の手順で照明器具を作成した。なお、MSP−TS04はチタニア微粒子を内包しており、チタニア微粒子の屈折率は2.4、チタニア微粒子の平均粒子径は0.2μmである。また、MSP−TS04の平均粒子径は4μmである。シリコーンの屈折率は1.42である。
実施例1で用いたKD200に代えて、DIC株式会社製のポリライト(登録商標)RX−4800Mと三井化学株式会社製のタケネート(登録商標)D−103Hの硬化物を透光性樹脂として用いた以外は実施例1と同様の手順で照明器具を作成した。なお、ポリライト(登録商標)RX−4800Mの主成分はポリエステルポリオールであり、タケネート(登録商標)D−103Hの主成分はトルエンジイソシアネートである。また、硬化後の透光性樹脂の屈折率は1.58であった。
実施例1で用いたMSP−AS02に代えて、モメンティブ・パフォーマンス・マテリアルズ社製のトスパール(登録商標)120を用いた以外は実施例1と同様の手順で照明器具を作成した。なお、トスパール(登録商標)120は無機粒子を内包しないシリコーン粒子である。なお、トスパール(登録商標)120の平均粒子径は2μmであり、屈折率は1.42である。
実施例1で用いたMSP−AS02に代えて、日興リカ株式会社製のMSP−TS04を無機粒子内包シリコーン粒子として用いた。また、実施例1で用いたKD200に代えて、DIC株式会社製のポリライト(登録商標)RX−4800Mと三井化学株式会社製のタケネート(登録商標)D−103Hの硬化物を透光性樹脂として用いた。それ以外は実施例1と同様の手順で照明器具を作成した。なお、MSP−TS04はチタニア微粒子を内包しており、チタニア微粒子の屈折率は2.4、チタニア微粒子の平均粒子径は0.2μmである。また、MSP−TS04の平均粒子径は4μmである。なお、ポリライト(登録商標)RX−4800Mの主成分はポリエステルポリオールであり、タケネート(登録商標)D−103Hの主成分はトルエンジイソシアネートである。また、硬化後の透光性樹脂の屈折率は1.58であった。
実施例1で用いたMSP−AS02に代えて、住友化学株式会社製のAA−1.5を用いた以外は実施例1と同様の手順で照明器具を作成した。なお、AA−1.5の主成分はアルミナであり、屈折率は1.76、平均粒子径は1.6μmである。また、AA−1.5のアルミナは、シリコーンに内包されない。
実施例1で用いたMSP−AS02に代えて、チタン工業株式会社製のST−750ECを用いた以外は実施例1と同様の手順で照明器具を作成した。なお、ST−750ECの主成分はチタニアであり、屈折率は2.4、平均粒子径は1.0μmである。また、ST−750ECのチタニアは、シリコーンに内包されない。
実施例1乃至4、及び比較例1乃至5で得られた照明器具について、次の項目の評価を行った。各例の詳細と評価結果を表1に示す。
各例で得られた照明器具の全光束を測定し、基準照明器具の全光束を100とした場合の各例の全光束比を算出した。なお、全光束はラブスフェア社製の165cm積分球により、同社製の測定システムを用いて測定した。また、基準照明器具の全光束は1800lmである。また、判定基準は以下の通りとした。
・判定基準
103%以上:○
100%以上103%未満:△
100%未満:×
上述したLEDベースライトXL553PFV LE9は、LED光源間の距離が小さく、光均一性を測定するのに適していなかったため、3cm離して配置した2つのLEDを各例で得られた照明カバーで覆った場合の光均一性を評価した。LEDは日亜化学工業株式会社製のNSSW157Dを用いた。また、LEDより3cm離れた位置に、光拡散層がLED側となるように照明カバーを配置した。また、照明カバーよりさらに30cm離れた位置に株式会社トプコンテクノハウス社製の色彩輝度計BM−7を配置した。そして、2つのLEDを結ぶ線分上において、輝度が最大と最小になる値をそれぞれ測定した。光均一性は、{(輝度の最小値)/(輝度の最大値)}×100として算出している。また、判定基準は以下の通りとした。
・判定基準
70%以上:○
60以上70未満:△
60%未満:×
12 透光性樹脂基材
13 透光性樹脂
14 シリコーン
15 無機粒子
16 無機粒子内包シリコーン粒子
17 光拡散層
30 光源部
40 照明カバー
100 照明器具
Claims (7)
- 透光性樹脂基材と、
屈折率が1.49以下の透光性樹脂と、シリコーンに複数の無機粒子が内包された無機粒子内包シリコーン粒子とを含有し、前記透光性樹脂基材の表面に設けられる光拡散層と、
を備え、
前記透光性樹脂はフッ素樹脂を含有する光学部材。 - 前記無機粒子の屈折率が1.7〜2.5である請求項1に記載の光学部材。
- 前記無機粒子が酸化アルミニウム及び酸化チタンの少なくともいずれか一方を含有する請求項1又は2に記載の光学部材。
- 前記光拡散層において、前記無機粒子内包シリコーン粒子の含有量は、100質量部の前記透光性樹脂に対して66〜150質量部である請求項1〜3のいずれか一項に記載の光学部材。
- 請求項1〜4のいずれか一項に記載の光学部材を用いた照明カバー。
- 光源部と、
前記光源部を覆う請求項5に記載の照明カバーと、
を備える照明器具。 - 前記光拡散層は前記透光性樹脂基材よりも前記光源部側に配置される請求項6に記載の照明器具。