JP6645820B2 - 水中不分離性モルタル組成物 - Google Patents
水中不分離性モルタル組成物 Download PDFInfo
- Publication number
- JP6645820B2 JP6645820B2 JP2015248464A JP2015248464A JP6645820B2 JP 6645820 B2 JP6645820 B2 JP 6645820B2 JP 2015248464 A JP2015248464 A JP 2015248464A JP 2015248464 A JP2015248464 A JP 2015248464A JP 6645820 B2 JP6645820 B2 JP 6645820B2
- Authority
- JP
- Japan
- Prior art keywords
- water
- mass
- parts
- mortar composition
- reducing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
水中不分離モルタル・コンクリートとしては、水中不分離混和剤をベースとなるモルタル又はコンクリートに添加し練混ぜたものが知られている。この水中不分離混和剤としては、水溶性セルロースエーテル系の高分子材料が用いられている(特許文献1)。
また、ベースコンクリートに水中不分離混和剤を海水に添加したスラリーを混合して練混ぜ、亜硝酸塩系混和剤を添加し、凝結時間を短縮した水中不分離性コンクリートも提案されている(特許文献2)。
セメントとして、普通ポルトランドセメント及び早強ポルトランドセメントを含み、早強ポルトランドセメントに対する普通ポルトランドセメントの質量比が15/85〜85/15であり、
ポリカルボン酸系減水剤が、化学成分として、アルカリ金属及びカルシウムを含むアルカリ土類金属からそれぞれ1種類以上の成分を含有することを特徴とする水中不分離性モルタル組成物。
〔2〕さらにメラミン系減水剤を含有する〔1〕に記載の水中不分離性モルタル組成物。
〔3〕セメント100質量部に対して、細骨材30〜125質量部、メラミン系減水剤0.5〜1.5質量部、ポリカルボン酸系減水剤0.5〜1.3質量部及び増粘剤0.3〜0.6質量部含有する〔2〕に記載の水中不分離性モルタル組成物。
〔4〕さらに膨張材を含有する〔1〕〜〔3〕のいずれかに記載の水中不分離性モルタル組成物。
〔5〕さらに消泡剤を含有する〔1〕〜〔4〕のいずれかに記載の水中不分離性モルタル組成物。
〔6〕さらに発泡剤を含有する〔1〕〜〔5〕のいずれかに記載の水中不分離性モルタル組成物。
〔7〕凝結時間の終結が16時間以内となる〔1〕〜〔6〕のいずれかに記載の水中不分離性グラウトモルタル組成物。
また、ポリカルボン酸系減水剤の使用量は、適正な流動性を得る点及び凝結時間の遅延や強度低下を防止する点から、セメント100質量部に対して、0.5〜1.3質量部が好ましい。より好ましくは、0.55〜1.1質量部である。
本発明で使用するメラミン系減水剤の形態は、液状、粉末状何れのものも使用できる。また、メラミン系減水剤の使用量は、適正な流動性を得る点及び凝結時間の遅延や強度低下を防止する点から、セメント100質量部に対して、0.5〜1.5質量部が好ましい。より好ましくは、0.65〜1.3質量部である。
また、普通ポルトランドセメントと早強ポルトランドセメントを併用することがより好ましく、普通ポルトランドセメントと早強ポルトランドセメントの質量比は、良好な水中不分離性を得る点、凝結時間の遅延防止、初期強度発現性の点から15/85〜85/15が好ましい。より好ましくは質量比が20/80〜80/20である。
上記増粘剤の使用量は、適正な水中不分離性を得る点、粘性保持、良好な流動性を維持する点からセメント100質量部に対して、0.3〜0.6質量部が好ましい。より好ましくは、0.35〜0.5質量部である。
細骨材の使用量は、大量打設した際に良好な水中不分離性を得る点、熱ひび割れの発生を防止する点、充分な圧縮強度を得る点から、セメント100質量部に対して、30〜125質量部が好ましい。より好ましくは、50〜100質量部である。
膨張材の粉末度は、流動性を確保する点から、ブレーン比表面積(以下、ブレーン値という)で2000〜6000cm2/gが好ましく、2500〜5000cm2/gがより好ましい。
膨張材の使用量は、適性な膨張性状を得る点から、セメント100質量部に対して、0.5〜3.5質量部が好ましい。より好ましくは、0.7〜3.2質量部である。
消泡剤の使用量は、セメント100質量部に対して、0.05〜0.3質量部が好ましい。
発泡剤の使用量は、セメント100質量部に対して、0.005〜0.015質量部が好ましい。
本発明の水中不分離性モルタル組成物を用いたモルタルは、凝結時間の終結が16時間以内となるのが好ましい。
[使用材料]
使用材料を表1に示した。水以外の材料はいずれも固体成分である。また、使用したポリカルボン酸系減水剤(PC−1〜PC−8)を表2に示した。ポリカルボン酸系減水剤中の含有成分については、蛍光X線分析により評価した。但し、アルカリ金属及びアルカリ土類金属成分について0.01mol/g(アルカリ金属及びアルカリ土類金属酸化物としてmol換算)未満の場合、含有成分と見なさないものとした。
セメント100質量部に対して、膨張材2質量部、消泡剤0.1質量部、発泡剤0.007質量部とし、それ以外の使用材料を表3に示す配合割合となるように配合設計した。
20℃条件下において、配合設計し混合した(水は除く)モルタル組成物を水の入ったステンレス製円筒容器に投入し、ハンドミキサで120秒撹拌し、モルタルを作製した。なお、水固体比を25.5%とした。
作製したモルタルを以下に示す評価試験方法により、20℃条件下で評価した。
JIS R 5201「セメントの物理試験方法」11.「フロー試験」(ただし、15打の落下運動は行わず、引き抜きフローとする)に準じて、テーブルフロー値を測定した。流動性の指標は、練り上り直後のテーブルフロー値が200mm以上とした。また、テーブルフロー値の測定は、フローコーンを引き抜き後、5分経過後のテーブルフロー値とした。
土木学会「水中不分離性コンクリート設計施工指針(案)」付属書2「水中不分離性コンクリートの水中不分離度試験方法(案)」に準じて、懸濁物質量を測定した。水中不分離度の指標は、土木学会規準コンクリート用水中不分離性混和剤品質規格(案)に示されている懸濁物質量50mg/L以下とした。
JIS A 1147「コンクリートの凝結時間試験方法」に準じ、凝結時間を測定した。
[圧縮強度試験]
JSCE−G−541「充填モルタルの圧縮強度試験」に準じ、水中作製供試体の作り方は、JSCE−F−504に準じ、材齢24時間における圧縮強度を測定した。なお、供試体の寸法は、直径50mm、高さ100mmとした。
セメント100質量部に対して、膨張材2質量部、消泡剤0.1質量部、発泡剤0.007質量部とし、それ以外の使用材料を表5に示す配合割合となるように配合設計した。また、上記同様の評価試験を行った。
Claims (7)
- セメント、細骨材、ポリカルボン酸系減水剤及び増粘剤を含有する水中不分離性モルタル組成物であって、
セメントとして、普通ポルトランドセメント及び早強ポルトランドセメントを含み、早強ポルトランドセメントに対する普通ポルトランドセメントの質量比が15/85〜85/15であり、
ポリカルボン酸系減水剤が、化学成分として、アルカリ金属及びカルシウムを含むアルカリ土類金属からそれぞれ1種類以上の成分を含有することを特徴とする水中不分離性モルタル組成物。 - さらにメラミン系減水剤を含有する請求項1に記載の水中不分離性モルタル組成物。
- セメント100質量部に対して、細骨材30〜125質量部、メラミン系減水剤0.5〜1.5質量部、ポリカルボン酸系減水剤0.5〜1.3質量部及び増粘剤0.3〜0.6質量部含有する請求項2に記載の水中不分離性モルタル組成物。
- さらに膨張材を含有する請求項1〜3のいずれか1項に記載の水中不分離性モルタル組成物。
- さらに消泡剤を含有する請求項1〜4のいずれか1項に記載の水中不分離性モルタル組成物。
- さらに発泡剤を含有する請求項1〜5のいずれか1項に記載の水中不分離性モルタル組成物。
- 凝結時間の終結が16時間以内となる請求項1〜6のいずれか1項に記載の水中不分離性グラウトモルタル組成物。