JP6580824B2 - Waterproof sheet and its construction method - Google Patents
Waterproof sheet and its construction method Download PDFInfo
- Publication number
- JP6580824B2 JP6580824B2 JP2014245234A JP2014245234A JP6580824B2 JP 6580824 B2 JP6580824 B2 JP 6580824B2 JP 2014245234 A JP2014245234 A JP 2014245234A JP 2014245234 A JP2014245234 A JP 2014245234A JP 6580824 B2 JP6580824 B2 JP 6580824B2
- Authority
- JP
- Japan
- Prior art keywords
- waterproof sheet
- nonwoven fabric
- sheet
- tunnel
- water shielding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、トンネル用、特にトンネルのカーブ箇所の施工に適した防水シート及びその施工方法を提供する。 The present invention provides a waterproof sheet suitable for construction of a tunnel, in particular, a curved portion of the tunnel, and a construction method thereof.
従来から、地山にトンネルを建設する場合、トンネルの吹付けコンクリートと覆工コンクリートの間に防水シートを配し、吹付けコンクリート側からの湧水(地中からトンネル内への湧水)が覆工コンクリート側へ漏水することを防止することが行われていた。例えば、特許文献1には、不透水シートと透水マットを、両側縁に沿って貼合せ、その貼合せ面のうち約半分の面の接着力を弱小にしたトンネル覆工用止水シートが記載されている。特許文献1では、トンネル覆工用止水シートを地山又は吹付けコンクリートの面に固定する際に、シートの表面に穴を開けないでシートの中間部を確実に固定するために、不透水シートと透水マット間の接着力を弱小にした部分を設けている。
Conventionally, when constructing a tunnel in a natural ground, a waterproof sheet is placed between the shotcrete and lining concrete of the tunnel, and spring water from the shotcrete side (spring water from the underground into the tunnel) Prevention of water leakage to the lining concrete side was performed. For example,
最近では、吹付けコンクリートの凹凸部と型枠に設置した防水シートの間に充填材を充填することによって、覆工コンクリート背面を滑らかな形状に仕上げ、防水シートを全面接着する背面平滑型トンネルライニング工法が用いられている。該工法では、ロックボルトは充填材で止められていること及び施工の見栄えの見地から、側縁部以外は、不透水シートと透水マットを全面接着した長方形の防水シートが用いられていた。しかし、トンネルカーブ箇所に周方向に沿って配設する場合、防水シートをカーブの外周部に合わせて配設すると、内周部で防水シートがだぶつき、防水シートをカーブの外周部に合わせて配設すると、外周部で防水シートが不足するという問題があった。 Recently, the back surface of the tunnel lining has a smooth finish on the back of the lining concrete, and the waterproof sheet is adhered to the entire surface by filling the gap between the unevenness of the shotcrete and the waterproof sheet installed on the formwork. The construction method is used. In this construction method, a rectangular waterproof sheet in which a water-impermeable sheet and a water-permeable mat are bonded together is used except for the side edges from the viewpoint that the lock bolt is fixed with a filler and the appearance of construction. However, when installing along the circumferential direction at the tunnel curve location, if the waterproof sheet is installed along the outer periphery of the curve, the waterproof sheet will bump around the inner periphery, and the waterproof sheet will be aligned with the outer periphery of the curve. When disposed, there is a problem that the waterproof sheet is insufficient at the outer peripheral portion.
特許文献2には、トンネルのカーブ箇所に周方向に沿って張設される防水シートであって、長さ方向一端縁が長さ方向他端縁より幅広で、少なくとも長さ方向他端縁側が先細になるように形成された形状を有する不透水性シートを備えた防水シートが記載されている。しかし、防水シートの作製において、トンネルの周長及びカーブの長さに応じて、事前に長方形の不透水性シートを台形形状等に加工する必要があった。
本発明は、上記従来の問題を解決するため、特に背面平滑型トンネルライニング工法の施工現場において、トンネルのカーブ箇所の周方向に沿って適切に施工することができる防水シート及びその施工方法を提供する。 In order to solve the above-described conventional problems, the present invention provides a waterproof sheet that can be appropriately constructed along the circumferential direction of a curved portion of a tunnel, and a construction method thereof, particularly at the construction site of a back smooth tunnel lining method. To do.
本発明は、不織布と、上記不織布の一方の表面に配置されている遮水シートを含む防水シートであって、上記防水シートの両側縁部において、上記不織布と上記遮水シートは互いに離間しており、その他の部位においては、上記不織布と上記遮水シートは面接着及び点接着により接着されており、上記点接着部分は、上記防水シートの一方又は両方の側縁部に近接する部分に存在することを特徴とする防水シートに関する。 The present invention is a waterproof sheet including a nonwoven fabric and a water shielding sheet disposed on one surface of the nonwoven fabric, wherein the nonwoven fabric and the water shielding sheet are separated from each other at both side edges of the waterproof sheet. In other parts, the non-woven fabric and the water shielding sheet are bonded by surface bonding and point bonding, and the point bonding part is present in a part close to one or both side edges of the waterproof sheet. The present invention relates to a waterproof sheet.
上記防水シートにおいて、上記点接着部分の最大幅は、防水シートの全体幅の12.5%〜30%であることが好ましく、長さ方向における隣接する接着点間の距離は、200mm〜500mmであることが好ましい。 In the waterproof sheet, the maximum width of the point adhesion portion is preferably 12.5% to 30% of the entire width of the waterproof sheet, and the distance between adjacent adhesion points in the length direction is 200 mm to 500 mm. Preferably there is.
本発明は、また、上記の防水シートをトンネルのカーブ箇所の外周部に合致するようにしてトンネルの周方向に沿って配設した後、上記トンネルのカーブ箇所の内周部において、上記防水シートの点接着部分の一部を切り捨てることで、上記防水シートをトンネルのカーブ箇所の内周部にも合致させることを特徴とする防水シートの施工方法に関する。 In the present invention, the waterproof sheet is disposed along the circumferential direction of the tunnel so as to match the outer peripheral portion of the curved portion of the tunnel, and then the waterproof sheet is disposed on the inner peripheral portion of the curved portion of the tunnel. It is related with the construction method of the waterproof sheet characterized by making the said waterproof sheet match also the inner peripheral part of the curve location of a tunnel by discarding a part of point adhesion part of this.
本発明は、不織布と、上記不織布の一方の表面に配置されている遮水シートからなる防水シートにおいて、面接着部分と点接着部分を設け、点接着部分を防水シートの一方又は両方の側縁部に近接する部分に存在させることにより、特に背面平滑型トンネルライニング工法の施工現場において、内周部においてだぶついたりすることなく、トンネルのカーブ箇所の周方向に沿って適切に施工することができる防水シート及びその施工方法を提供する。 The present invention provides a waterproof sheet comprising a nonwoven fabric and a water shielding sheet disposed on one surface of the nonwoven fabric, wherein a surface-bonding portion and a point-bonding portion are provided, and the point-bonding portion is provided on one or both side edges of the waterproof sheet. By making it exist in the part close to the part, it can be properly constructed along the circumferential direction of the curve part of the tunnel without causing bumps in the inner peripheral part, especially at the construction site of the back smooth tunnel lining method A waterproof sheet and a construction method thereof are provided.
本発明の防水シートは、不織布と、上記不織布の一方の表面に配置されている遮水シートで構成されている。上記防水シートの両側縁部において、上記不織布と上記遮水シートは互いに離間して側縁自由端部となっており、該側縁自由端部により、他の防水シートの側縁自由端部と必要箇所で接合される。上記側縁自由端部の幅は防水シートの全体幅の5%〜20%であることが好ましく、より好ましくは7%〜15%である。上記防水シートの両側縁部以外の部位において、上記不織布と上記遮水シートは面接着及び点接着により接着されており、上記点接着部分は、上記防水シートの一方又は両方の側縁部に近接する部分に存在する。側縁部(側縁自由端部)に近接する部分に点接着部分を設けることにより、トンネルのカーブ箇所において、内周部においてだぶつくことや外周部において不足することなく、周方向に沿って適切に施工することができる。 The waterproof sheet of the present invention is composed of a nonwoven fabric and a water shielding sheet disposed on one surface of the nonwoven fabric. In the both side edges of the waterproof sheet, the nonwoven fabric and the water shielding sheet are separated from each other to form a side edge free end, and the side edge free end allows the side edge free end of another waterproof sheet to Joined at the necessary place. The width of the side edge free end is preferably 5% to 20% of the entire width of the waterproof sheet, and more preferably 7% to 15%. The non-woven fabric and the water-proof sheet are bonded by surface bonding and point bonding at portions other than both side edge portions of the waterproof sheet, and the point bonding portion is close to one or both side edge portions of the waterproof sheet. It exists in the part to be. By providing a point adhesion part in the part close to the side edge (side edge free end), along the circumferential direction without bumping in the inner peripheral part and lacking in the outer peripheral part in the curved part of the tunnel It can be constructed properly.
上記不織布と上記遮水シートは、接着剤を介して接着されていてもよく、上記不織布又は上記遮水シートを構成する成分の熱溶着により接着されていてもよい。上記不織布と上記遮水シートは、ホットメルト系接着剤を介して接着されていることが好ましい。或いは、上記不織布又は上記遮水シートを構成する成分の熱溶着により接着されていることが好ましい。或いは、上記不織布と上記遮水シートは、面接着部分においては、上記不織布又は上記遮水シートを構成する成分の熱溶着により接着されており、点接着部分においては、ホットメルト系接着剤を介して点接着されていることが好ましい。これらの構成であると、有機溶剤を含まず、防水シートから有機溶剤に起因する物質が揮発することがない。 The nonwoven fabric and the water shielding sheet may be adhered via an adhesive, or may be adhered by thermal welding of components constituting the nonwoven fabric or the water shielding sheet. The nonwoven fabric and the water shielding sheet are preferably bonded via a hot melt adhesive. Or it is preferable to adhere | attach by the heat welding of the component which comprises the said nonwoven fabric or the said water shielding sheet. Alternatively, the non-woven fabric and the water shielding sheet are bonded to each other at the surface bonding portion by thermal welding of the components constituting the non-woven fabric or the water shielding sheet, and at the point bonding portion, a hot melt adhesive is used. It is preferable to be point-bonded. With these configurations, the organic solvent is not included, and the substance derived from the organic solvent does not volatilize from the waterproof sheet.
上記不織布と上記遮水シートが点接着している部分において、接着点の大きさは、1cm2〜100cm2であることが好ましい。接着点の大きさが1cm2以上であると、不織布と遮水シートとを強固に接着することができる。また、接着点の大きさが100cm2以下であると、トンネルのカーブ箇所において余剰の防水シートの点接着部分の切り捨て作業がしやすい。より好ましくは接着点の大きさは、5cm2〜50cm2である。 In the portion where the nonwoven fabric and the water shield sheets are spot gluing, the size of the point of attachment is preferably 1 cm 2 100 cm 2. A nonwoven fabric and a water shielding sheet can be firmly adhere | attached as the magnitude | size of an adhesion point is 1 cm < 2 > or more. In addition, when the size of the adhesion point is 100 cm 2 or less, it is easy to cut off the point adhesion portion of the excess waterproof sheet at the curved portion of the tunnel. More preferably the size of the point of attachment is 5 cm 2 to 50 cm 2.
上記防水シートにおいて、上記点接着部分の最大幅は、防水シートの全体幅の12.5%〜30%であることが好ましく、より好ましくは15%〜25%である。施工の見栄えを良好にしつつ、トンネルのカーブ箇所での作業性が向上する。 In the waterproof sheet, the maximum width of the point-bonded portion is preferably 12.5% to 30%, more preferably 15% to 25% of the entire width of the waterproof sheet. While improving the appearance of the construction, workability at the curve of the tunnel is improved.
上記防水シートにおいて、幅方向における隣接する接着点間の最小距離は、100mm〜300mmであることが好ましく、より好ましくは100mm〜160mmである。幅方向における隣接する接着点の最大距離は、100mm〜800mmであることが好ましく、より好ましくは100mm〜500mmである。さらに好ましくは160mm〜300mmである。幅方向における隣接する接着点の最小距離及び最大距離が上記の範囲内であると、施工の見栄えを良好にしつつ、トンネルのカーブ箇所での作業性が向上する。本発明において、「接着点間の距離」は、接着点の中心点間の距離である。幅方向において、複数の接着点が同間隔で配置されている場合は、隣接する接着点間の最小距離と隣接する接着点の最大距離は同じである。 In the waterproof sheet, the minimum distance between adjacent adhesion points in the width direction is preferably 100 mm to 300 mm, and more preferably 100 mm to 160 mm. The maximum distance between adjacent adhesion points in the width direction is preferably 100 mm to 800 mm, more preferably 100 mm to 500 mm. More preferably, it is 160 mm-300 mm. When the minimum distance and the maximum distance between adjacent adhesion points in the width direction are within the above range, the workability at the curved portion of the tunnel is improved while improving the appearance of the construction. In the present invention, the “distance between adhesion points” is the distance between the center points of the adhesion points. In the width direction, when a plurality of adhesion points are arranged at the same interval, the minimum distance between adjacent adhesion points and the maximum distance between adjacent adhesion points are the same.
上記防水シートにおいて、長さ方向における隣接する接着点間の距離は、200mm〜500mmであることが好ましく、より好ましくは250mm〜350mmである。長さ方向においてこの距離であると不織布と遮水シートの接着強度を高め、剥離を防止する。 In the waterproof sheet, the distance between adjacent adhesion points in the length direction is preferably 200 mm to 500 mm, more preferably 250 mm to 350 mm. When the distance is in the length direction, the adhesive strength between the nonwoven fabric and the water-impervious sheet is increased and peeling is prevented.
上記防水シートは、単位面積当たりの質量が2kg/m2以下であることが好ましく、1.5kg/m2以下であることがより好ましい。防水シートの単位面積当たりの質量が2kg/m2以下であると、防水シートが軽く、施工が容易となる。特に限定されないが、好ましい下限は、0.5kg/m2である。 The waterproof sheet preferably has a mass per unit area of 2 kg / m 2 or less, and more preferably 1.5 kg / m 2 or less. When the mass per unit area of the waterproof sheet is 2 kg / m 2 or less, the waterproof sheet is light and construction is easy. Although not particularly limited, a preferable lower limit is 0.5 kg / m 2 .
上記不織布を構成する繊維は、特に限定されないが、例えば、ポリエチレン、ポリプロピレン、ポリブテンなどのポリオレフィン樹脂、ポリエチレンテレフタレート、ポリブチレンテレフタレートなどのポリエステル樹脂、ナイロン6、ナイロン66などのポリアミド樹脂などの合成樹脂で構成されている繊維が挙げられる。中でも、上記不織布を構成する繊維は、耐アルカリ性と耐候性に優れる観点からポリオレフィン樹脂を含むことが好ましい。また、アラミド繊維や炭素繊維からなる不織布を用いることで、防水シートに引裂強度を与えることもできる。 The fibers constituting the nonwoven fabric are not particularly limited. For example, polyolefin resins such as polyethylene, polypropylene, and polybutene, polyester resins such as polyethylene terephthalate and polybutylene terephthalate, and synthetic resins such as polyamide resins such as nylon 6 and nylon 66 are used. Examples include fibers that are constructed. Especially, it is preferable that the fiber which comprises the said nonwoven fabric contains polyolefin resin from a viewpoint excellent in alkali resistance and a weather resistance. Moreover, tear strength can also be given to a waterproof sheet by using the nonwoven fabric which consists of an aramid fiber and carbon fiber.
上記不織布は、目付が80g/m2〜500g/m2であることが好ましい。不織布の目付が80g/m2以上であると、引張強度が高く、破断しにくい。また、不織布の目付が500g/m2以下であると、重くなりすぎず、施工が容易である。より好ましくは不織布の目付は200g/m2〜400g/m2である。 Non-woven fabric is preferably the basis weight is 80g / m 2 ~500g / m 2 . When the basis weight of the nonwoven fabric is 80 g / m 2 or more, the tensile strength is high and it is difficult to break. Further, if the basis weight of the nonwoven fabric is 500 g / m 2 or less, it is not too heavy and construction is easy. More preferably the basis weight of the nonwoven fabric is 200g / m 2 ~400g / m 2 .
上記不織布は、厚みが0.5mm〜20mmであることが好ましい。不織布の厚みが0.5mm以上であると、突起物により遮水シートが損傷することを防止する効果がより高い。不織布の厚みが20mm以下であると、不織布が厚み方向に破断又は剥離し難い。より好ましくは不織布の厚みは1mm〜10mmであり、さらに好ましくは2mm〜8mmである。なお、不織布の厚みは、JIS L 1096 8.5に準じて、1cm2あたり2.94cNの荷重を加えた状態で測定する。 The nonwoven fabric preferably has a thickness of 0.5 mm to 20 mm. When the thickness of the nonwoven fabric is 0.5 mm or more, the effect of preventing the water shielding sheet from being damaged by the protrusions is higher. When the thickness of the nonwoven fabric is 20 mm or less, the nonwoven fabric is difficult to break or peel in the thickness direction. More preferably, the nonwoven fabric has a thickness of 1 mm to 10 mm, and more preferably 2 mm to 8 mm. In addition, the thickness of a nonwoven fabric is measured in the state which applied the load of 2.94 cN per cm < 2 > according to JISL10968.5.
上記不織布は、スパンボンド不織布、メルトブローン不織布などの長繊維不織布であってもよく、ニードルパンチ不織布、スパンレース不織布、サーマルボンド不織布などの短繊維不織布であってもよい。なかでも、安価である観点から、不織布はスパンボンド不織布をニードルパンチ処理で交絡させた不織布であることが好ましい。 The nonwoven fabric may be a long fiber nonwoven fabric such as a spunbond nonwoven fabric or a melt blown nonwoven fabric, or a short fiber nonwoven fabric such as a needle punch nonwoven fabric, a spunlace nonwoven fabric, or a thermal bond nonwoven fabric. Especially, from a cheap viewpoint, it is preferable that a nonwoven fabric is the nonwoven fabric which made the spun bond nonwoven fabric entangled by the needle punch process.
上記不織布を構成する繊維は、特に限定されないが、単繊維繊度が1dtex〜100dtexであってよい。繊度が1dtex〜100dtexである繊維を用いると、不織布の引張強度や引裂強度を高めることができる。 Although the fiber which comprises the said nonwoven fabric is not specifically limited, Single fiber fineness may be 1 dtex-100 dtex. When fibers having a fineness of 1 dtex to 100 dtex are used, the tensile strength and tear strength of the nonwoven fabric can be increased.
上記不織布が短繊維不織布である場合、不織布を構成する繊維は、特に限定されないが、繊維長が10mm〜200mmであることが好ましい。繊維長が10mm〜200mmであると、不織布の引張強度や引裂強度を高めることができる。 When the said nonwoven fabric is a short fiber nonwoven fabric, the fiber which comprises a nonwoven fabric is although it does not specifically limit, It is preferable that fiber length is 10 mm-200 mm. When the fiber length is 10 mm to 200 mm, the tensile strength and tear strength of the nonwoven fabric can be increased.
上記不織布は、1種の繊維から構成されていてもよく、2以上の繊維が混綿された不織布であってもよい。また、上記不織布は、1層のウェブからなる単層不織布であってもよく、2層以上のウェブが積層されてなる積層不織布であってもよい。さらに、上記不織布は単一成分の樹脂からなる繊維で構成されていてもよく、2以上の樹脂を用いた複合繊維で構成されていてもよい。上記繊維の断面形状は、特に限定されず、丸型断面であってもよく、同心円型、楔状分割型、スリット状分割型、中空型、三角型、Y型、四角型などの異型断面であってもよい。 The said nonwoven fabric may be comprised from 1 type of fiber, and the nonwoven fabric by which two or more fibers were mixed may be sufficient as it. Moreover, the said nonwoven fabric may be a single layer nonwoven fabric which consists of a 1 layer web, and may be a laminated nonwoven fabric by which 2 or more layers of webs are laminated | stacked. Furthermore, the nonwoven fabric may be composed of fibers made of a single component resin, or may be composed of composite fibers using two or more resins. The cross-sectional shape of the fiber is not particularly limited, and may be a round cross-section, such as a concentric circular shape, a wedge-shaped divided type, a slit-shaped divided type, a hollow shape, a triangular shape, a Y shape, a square shape, or the like. May be.
上記不織布は、遮水シートと向き合う表面に凹凸を有することが好ましい。凸部の高さは、0.5mm〜10mmであることが好ましく、1mm〜7mmであることがより好ましい。不織布の遮水シートと向き合う表面が凹凸部を有すると、不織布と遮水シートの間において、湧水が通過する空間が大きくなり、排水効率が向上する。 The nonwoven fabric preferably has irregularities on the surface facing the water-impervious sheet. The height of the convex portion is preferably 0.5 mm to 10 mm, and more preferably 1 mm to 7 mm. When the surface facing the nonwoven fabric water-impervious sheet has an uneven portion, a space through which spring water passes increases between the nonwoven fabric and the water-impervious sheet, thereby improving drainage efficiency.
上記不織布は、JIS L 1096に準じて測定される引張強度が、500N/5cm以上であることが好ましく、700N/5cm以上であることがより好ましい。引張強度が500N/5cm以上であると、不織布が破断しにくい。引張強度の好ましい上限は3000N/5cm以下である。 The nonwoven fabric preferably has a tensile strength measured according to JIS L 1096 of 500 N / 5 cm or more, and more preferably 700 N / 5 cm or more. If the tensile strength is 500 N / 5 cm or more, the nonwoven fabric is difficult to break. The upper limit with preferable tensile strength is 3000 N / 5cm or less.
上記不織布は、JIS L 1096に準じて測定される伸びが、20%以上であることが好ましく、50%以上であることがより好ましい。伸びが20%以上であると、遮水シートの伸びに追従しやすくなり、トンネルの円弧面や地山の曲斜面に沿って施工しやすい。伸びの好ましい上限は500%である。 The non-woven fabric has an elongation measured according to JIS L 1096 of preferably 20% or more, and more preferably 50% or more. When the elongation is 20% or more, it is easy to follow the elongation of the water shielding sheet, and it is easy to construct along the arc surface of the tunnel or the curved slope of the natural ground. A preferable upper limit of elongation is 500%.
上記不織布は、JIS L 1096(シングルタンク法)に準じて測定される引裂強度が、80N以上であることが好ましく、140N以上であることがより好ましい。引裂強度が80N以上であると、不織布が裂けにくい。引裂強度の好ましい上限は、500N以下である。 The nonwoven fabric preferably has a tear strength measured according to JIS L 1096 (single tank method) of 80 N or more, and more preferably 140 N or more. If the tear strength is 80 N or more, the nonwoven fabric is difficult to tear. The upper limit with preferable tear strength is 500 N or less.
上記遮水シートは、水を透過しないシートであればよく、特に限定されない。例えば、上記遮水シートは、遮水シートの全体質量に対して、エチレン−酢酸ビニル共重合体を20質量%〜80質量%含み、ポリエチレンを20質量%〜80質量%含むことが好ましい。遮水シート中のエチレン−酢酸ビニル共重合体の含有量が20質量%以上であると、エチレン−酢酸ビニル共重合体の樹脂特性に起因して良好な遮水性を有する。さらには、エチレン−酢酸ビニル共重合体の樹脂特性に起因して、例えば10℃以下の低温環境下に於いても遮水シートが固くならず、施工面に対する追従性が保たれる。かかる効果をより顕著に得る観点から、遮水シートは、エチレン−酢酸ビニル共重合体を40質量%以上含むことが好ましい。遮水シート中のポリエチレンの含有量が20質量%以上であると、不織布との接着力に優れた遮水シートを得ることができる。不織布と遮水シートとの接着力が高く、不織布と強固に接着された遮水シートは、防水シートの施工中や施工後に不織布と遮水シートとが剥離することがない又は少ない。かかる効果をより顕著に得る観点から、遮水シートは、ポリエチレンを40質量%以上含むことが好ましい。また、遮水シートのしなやかさや引張強度を低下させない観点から、遮水シートは、ポリエチレンを60質量%以下含むことが好ましい。 The water shielding sheet is not particularly limited as long as it is a sheet that does not transmit water. For example, it is preferable that the said water shielding sheet contains 20 mass%-80 mass% of ethylene-vinyl acetate copolymers, and contains 20 mass%-80 mass% of polyethylene with respect to the whole mass of a water shielding sheet. When the content of the ethylene-vinyl acetate copolymer in the water-impervious sheet is 20% by mass or more, the water-impervious sheet has good water shielding properties due to the resin characteristics of the ethylene-vinyl acetate copolymer. Furthermore, due to the resin characteristics of the ethylene-vinyl acetate copolymer, the water shielding sheet does not become hard even in a low temperature environment of, for example, 10 ° C. or less, and the followability to the construction surface is maintained. From the viewpoint of more prominently obtaining such effects, the water shielding sheet preferably contains 40% by mass or more of an ethylene-vinyl acetate copolymer. When the polyethylene content in the water-impervious sheet is 20% by mass or more, a water-impervious sheet excellent in adhesive strength with the nonwoven fabric can be obtained. The waterproof sheet firmly bonded to the nonwoven fabric has a high adhesive force between the nonwoven fabric and the waterproof sheet, and the nonwoven fabric and the waterproof sheet are not peeled off during or after the waterproof sheet is applied. From the viewpoint of more prominently obtaining such effects, the water shielding sheet preferably contains 40% by mass or more of polyethylene. Moreover, it is preferable that a water shielding sheet contains 60 mass% or less of polyethylene from a viewpoint which does not reduce the flexibility and tensile strength of a water shielding sheet.
上記エチレン−酢酸ビニル共重合体は、酢酸ビニル含有量が、3mol%〜50mol%であることが好ましい。エチレン−酢酸ビニル共重合体中の酢酸ビニル含有量が3mol%以上であると、柔軟性に優れたシートを得ることができる。また、酢酸ビニル含有量が50mol%以下であると、防水シートを30℃以上の環境下で保管する場合であっても、遮水シート同士がくっついて一体化(ブロッキング)してしまうことが少ない。かかる効果をより顕著に得る観点から、酢酸ビニル含有量は、5mol%〜40mol%であることがより好ましく、10mol%〜30mol%であることがさらに好ましい。 The ethylene-vinyl acetate copolymer preferably has a vinyl acetate content of 3 mol% to 50 mol%. When the vinyl acetate content in the ethylene-vinyl acetate copolymer is 3 mol% or more, a sheet having excellent flexibility can be obtained. Further, when the content of vinyl acetate is 50 mol% or less, even when the waterproof sheet is stored in an environment of 30 ° C. or higher, the water shielding sheets are less likely to stick together and be integrated (blocked). . From the viewpoint of obtaining such effects more remarkably, the vinyl acetate content is more preferably 5 mol% to 40 mol%, and still more preferably 10 mol% to 30 mol%.
上記ポリエチレンは、高密度ポリエチレン、低密度ポリエチレン、及び線状低密度ポリエチレンからなる群から1以上を選択して用いることができる。高密度ポリエチレンを用いるとその樹脂特性に起因して、耐衝撃性に優れた遮水シートを得ることができる。また、低密度ポリエチレンを用いるとその樹脂特性に起因して、熱溶着性に優れた遮水シートを得ることができる。なかでもポリエチレンは、線状低密度ポリエチレンであることが好ましい。線状低密度ポリエチレンを含む遮水シートは、特に優れた引張強度を有する。遮水シートが引張強度に優れると、遮水シートが破断し難くなる。 The polyethylene can be used by selecting one or more from the group consisting of high-density polyethylene, low-density polyethylene, and linear low-density polyethylene. When high density polyethylene is used, a water shielding sheet excellent in impact resistance can be obtained due to its resin characteristics. Moreover, when low density polyethylene is used, a water shielding sheet excellent in heat weldability can be obtained due to its resin characteristics. Especially, it is preferable that polyethylene is a linear low density polyethylene. The water shielding sheet containing linear low density polyethylene has particularly excellent tensile strength. If the water shielding sheet is excellent in tensile strength, the water shielding sheet is difficult to break.
上記線状低密度ポリエチレンは、密度が0.86g/cm3〜0.93g/cm3であることが好ましい。かかる密度の線状低密度ポリエチレンは、低価格で加工性にも優れる。 The linear low density polyethylene is preferably a density of 0.86g / cm 3 ~0.93g / cm 3 . A linear low density polyethylene having such a density is low in price and excellent in processability.
上記ポリエチレンは230℃におけるメルトフローレートが1g/10分〜10g/10分であることが好ましい。ポリエチレンのMFRが1g/10分以上であると、遮水シートを生産しやすい。ポリエチレンのMFRが10g/10分以下であると、遮水シートの強力が低下するおそれが少ない。かかる効果をより顕著に得る観点から、ポリエチレンのMFRは、1.5g/10分〜7g/10分であることがより好ましい。 The polyethylene preferably has a melt flow rate at 230 ° C. of 1 g / 10 min to 10 g / 10 min. When the MFR of polyethylene is 1 g / 10 min or more, it is easy to produce a water shielding sheet. When the MFR of polyethylene is 10 g / 10 min or less, there is little possibility that the strength of the water shielding sheet is lowered. From the viewpoint of obtaining such effects more remarkably, the MFR of polyethylene is more preferably 1.5 g / 10 min to 7 g / 10 min.
上記遮水シートは、エチレン−酢酸ビニル共重合体及びポリエチレンに加えて、他の樹脂成分を含んでもよい。他の樹脂成分の含有量は、遮水シートの全体質量に対して、30質量%以下の範囲であることが好ましく、より好ましくは10質量%以下の範囲である。他の樹脂は、特に限定されないが、例えば、ポリプロピレン、ポリブテン、エチレン−プロピレン共重合体、エチレン−ビニルアルコール共重合体などのポリオレフィン系樹脂を用いることができる。また、遮水シートは、必要に応じて、遮水シートの全体質量に対して、酸化防止剤や熱安定剤などを10質量%以下の量で含んでもよい。 The water shielding sheet may contain other resin components in addition to the ethylene-vinyl acetate copolymer and polyethylene. The content of other resin components is preferably in the range of 30% by mass or less, more preferably in the range of 10% by mass or less, with respect to the total mass of the water shielding sheet. Other resins are not particularly limited, and for example, polyolefin resins such as polypropylene, polybutene, ethylene-propylene copolymer, and ethylene-vinyl alcohol copolymer can be used. Moreover, the water-impervious sheet may contain an antioxidant, a heat stabilizer, or the like in an amount of 10% by mass or less with respect to the entire mass of the water-impervious sheet as necessary.
上記遮水シートは、厚みが0.1mm〜3mmであることが好ましく、0.3mm〜2mmであることがより好ましい。遮水シートの厚みが0.1mm〜3mmであると、施工時の取り扱い性に優れた防水シートとなる。なお、遮水シートの厚みは、JIS K 6250 8.1(A法)に従って測定する。 The water shielding sheet preferably has a thickness of 0.1 mm to 3 mm, and more preferably 0.3 mm to 2 mm. If the thickness of the water-impervious sheet is 0.1 mm to 3 mm, the waterproof sheet is excellent in handleability during construction. The thickness of the water shielding sheet is measured according to JIS K 6250 8.1 (A method).
上記遮水シートは、JIS K 6773に準じて測定される20℃における引張強度が、10N/mm2以上であることが好ましく、16N/mm2以上であることがより好ましい。引張強度が10N/mm2以上であると、遮水シートが破断しにくい。引張強度の好ましい上限は、100N/mm2以下である。 Said water barrier sheet tensile strength at 20 ° C. as measured in accordance with JIS K 6773, is preferably 10 N / mm 2 or more, more preferably 16N / mm 2 or more. When the tensile strength is 10 N / mm 2 or more, the water shielding sheet is hardly broken. The upper limit with preferable tensile strength is 100 N / mm < 2 > or less.
上記遮水シートは、JIS K 6773に準じて測定される20℃における伸びが、500%以上であることが好ましく、600%以上であることがより好ましい。伸びが500%以上であると、防水シートをトンネルの円弧面や地山の曲斜面に沿って施工することが容易になる。伸びの好ましい上限は、1000%以下である。 The water shielding sheet preferably has an elongation at 20 ° C. measured according to JIS K 6773 of 500% or more, and more preferably 600% or more. When the elongation is 500% or more, it becomes easy to construct the waterproof sheet along the arcuate surface of the tunnel or the curved slope of the natural ground. A preferable upper limit of elongation is 1000% or less.
遮水シートは、JIS K 6301に準じて測定される引裂強度が、400N/cm以上であることが好ましく、500N/cm以上であることがより好ましい。引裂強度が400N/cm以上であると、遮水シートが裂けにくい。引裂強度の好ましい上限は、2000N/cm以下である。 The water shielding sheet preferably has a tear strength measured according to JIS K 6301 of 400 N / cm or more, and more preferably 500 N / cm or more. When the tear strength is 400 N / cm or more, the water shielding sheet is difficult to tear. The upper limit with preferable tear strength is 2000 N / cm or less.
上記防水シートは、不織布の他方の表面に、太さが0.1mm〜10mmの複数の連続フィラメントが不規則に交差してなるシート状網状体が一体化されていてもよい。なお、不織布の他方の表面とは、不織布において、遮水シートが接着されていない表面をいう。 The waterproof sheet, the other surface of the nonwoven fabric, a plurality of continuous filaments of thickness is 0.1mm~10mm may be integrated sheet-like meshwork formed by irregularly cross. In addition, the other surface of a nonwoven fabric means the surface in which the water-proof sheet | seat is not adhere | attached in a nonwoven fabric.
次に図面により説明する。図1は本発明の一実施例の防水シートの模式的断面図である。該実施例の防水シート10は、不織布1と、不織布1の一方の表面に配置されている遮水シート2からなり、防水シート10の両側縁部において、不織布1と遮水シート2は互いに離間しており、その他の部位においては、不織布1と遮水シート2は面接着3及び点接着4により接着されている。すなわち、防水シート10は、不織布1と遮水シート2の非接着部分21aと21b、面接着部分22、及び点接着部分23を含む。不織布1と遮水シート2の非接着部分21aと21bは、自由末端となる。
Next, a description will be given with reference to the drawings. FIG. 1 is a schematic cross-sectional view of a waterproof sheet according to an embodiment of the present invention. The
防水シート10をトンネルのカーブ箇所に施工する場合は、図3に示すように、トンネル30のカーブ箇所の外周部31に合致するようにしてトンネルの周方向に沿って配設する。この際、トンネル30のカーブ箇所においては、外周部が内周部より長いため、トンネル30のカーブ箇所の内周部において、防水シート10はだぶつくことになるが、点接着部分23を有することで柔軟性に優れるため、周方向に追随させて配設しやすい。その後、トンネル30のカーブ箇所の内周部32において、点接着部分23の一部を切り捨てることにより、防水シート10がトンネル30のカーブ箇所の内周部32に合致するようにする。非接着部分(自由端部)21bに近接する点接着部分23において、不織布と透水シートは点接着しているため、トンネルの周長及びカーブの長さに応じて、切り捨て作業がしやすい。
When constructing the
以下実施例により説明する。なお、本発明は下記の実施例によって限定されない。 Examples will be described below. In addition, this invention is not limited by the following Example.
(実施例1)
遮水シート:遮水シートの全体質量に対して、エチレン−酢酸ビニル共重合体(三井・デュポンポリケミカル社製、商品名:EV260)を75質量%と、線状低密度ポリエチレン(プライムポリマー社製、商品名:SP2040)25質量%を含み、厚み0.91 mm、引張強度20.5N/mm2、伸度890%、引裂強度510N/cmである遮水シートを用いた。遮水シートの引張強度及び伸度は、JIS K 6773に準じて、20℃で測定した。遮水シートの引裂強度は、JIS K 6301に準じて、20℃で測定した。
不織布:ポリプロピレン繊維100質量%で、目付が350g/m2、厚みが3mmのスパンボンド不織布を用いた。
Example 1
Water shielding sheet: 75% by mass of ethylene-vinyl acetate copolymer (Mitsui / Dupont Polychemical Co., Ltd., trade name: EV260) with respect to the total mass of the water shielding sheet, linear low density polyethylene (Prime Polymer Co., Ltd.) Manufactured, trade name: SP2040) including 25% by mass, thickness 0.91 A water shielding sheet having a thickness of mm, a tensile strength of 20.5 N / mm 2 , an elongation of 890%, and a tear strength of 510 N / cm was used. The tensile strength and elongation of the water shielding sheet were measured at 20 ° C. according to JIS K 6773. The tear strength of the water shielding sheet was measured at 20 ° C. according to JIS K 6301.
Non-woven fabric: A spunbonded non-woven fabric having a polypropylene fiber of 100% by mass, a basis weight of 350 g / m 2 and a thickness of 3 mm was used.
上記遮水シートと不織布を用い、図1に示す防水シートを得た。具体的には、遮水シート2上の所定箇所にエチレン−酢酸ビニル共重合体からなるホットメルト接着剤を面状に付着させた後、接着剤を面状に付着させた部分の片方の隣接する部分に接着剤エチレン−酢酸ビニル共重合体からなるホットメルト接着剤を点状に付着させた。次に、接着剤を付着させた遮水シート2に不織布1を貼り合せることにより、防水シート10を得た。防水シート10の両側縁部において、不織布1と遮水シート2は互いに離間しており、その他の部位においては、不織布1と遮水シート2は面接着3及び点接着4により接着された。すなわち、防水シート10は、不織布1と遮水シート2の非接着部分21aと21b、面接着部分22、及び点接着部分23からなる。該実施例において、不織布10の全体幅は6000mmであり、非接着部分21aの幅は250mmであり、非接着部分21bの幅は800mmであった。
The waterproof sheet shown in FIG. 1 was obtained using the above-mentioned water-impervious sheet and nonwoven fabric. Specifically, after a hot melt adhesive made of an ethylene-vinyl acetate copolymer is adhered to a predetermined location on the
図2に、防水シート10の点接着部分23における接着点の配置を示した。点接着部分23の全体幅Wa、即ち接着点101と接着点108間の距離は1160mmであった。点接着部分の最大幅は防水シートの全体幅の19.3%であった。点接着部分23において、長さ方向における隣接する接着点108と208間の距離Laは、250mmであった。幅方向における隣接する接着点の最短距離である、接着点101と102間の距離W1a、接着点103と104間の距離W1b、接着点105と106間の距離W1c、接着点107と108間の距離W1dは100mmであった。幅方向における隣接する接着点102と103間の距離W2、接着点104と105間の距離W3は、共に300mmであった。幅方向における接着点106と107間の距離W4は160mmであった。
In FIG. 2, arrangement | positioning of the adhesion point in the
(比較例1)
上記実施例1と同一の遮水シートと不織布を用いた。遮水シートの両側縁部を除き、エチレン−酢酸ビニル共重合体からなるホットメルト接着剤を面状に付着させた。次に、接着剤を付着させた遮水シートに不織布を貼り合せることにより、比較例1の防水シートを得た。
(Comparative Example 1)
The same water shielding sheet and nonwoven fabric as in Example 1 were used. A hot melt adhesive made of an ethylene-vinyl acetate copolymer was adhered in a planar shape except for both side edges of the water shielding sheet. Next, the waterproof sheet of the comparative example 1 was obtained by bonding a nonwoven fabric to the water shielding sheet to which the adhesive was adhered.
実施例1で得られた防水シート10をトンネルのカーブ箇所(R600)に、図3に示すように、トンネル30のカーブ箇所の外周部31に合致するようにしてトンネルの周方向に沿って配設した。この際、トンネル30のカーブ箇所にいては、外周部が内周部より長いため、トンネル30のカーブ箇所の内周部32において、防水シート10はだぶつくことになるが、点接着部分23を有することで防水シート10が柔軟性を有し、周方向に沿うように配設しやすかった。その後、トンネル30のカーブ箇所の内周部32において、点接着部分23の一部を切り捨てることにより、防水シート10をトンネル30のカーブ箇所の内周部32に合致させた。点接着部分23において、不織布1と遮水シート2が面接着しておらず、不織布1と遮水シート2が離間している部分が存在しているため、点接着部分23の一部を切り捨てる作業性が良好であった。
The
比較例1で得られた防水シートをトンネルのカーブ箇所(R600)に、実施例1と同様に図3に示すように、トンネル30のカーブ箇所の外周部31に合致するようにしてトンネルの周方向に沿って配設したところ、点接着部分を有しないため、周方向に沿うよう配設しにくかった。 As shown in FIG. 3, the waterproof sheet obtained in Comparative Example 1 is aligned with the curved portion (R600) of the tunnel, as shown in FIG. When arranged along the direction, it was difficult to arrange along the circumferential direction because there was no point adhesion portion.
1 不織布
2 遮水シート
3 面接着
4 点接着
10 防水シート
21aと21b 非接着部分
22 面接着部分
23 点接着部分
30 トンネル
31 トンネルのカーブ箇所の外周部
32 トンネルのカーブ箇所の内周部
101〜108、201〜208 接着点
DESCRIPTION OF
Claims (4)
前記防水シートの幅方向の両側縁部において、前記不織布と前記遮水シートは互いに離間しており、その他の部位においては、前記不織布と前記遮水シートは面接着及び点接着により接着されており、
前記点接着部分は、前記防水シートの一方又は両方の幅方向の側縁部に近接する部分に存在し、
前記点接着部分の最大幅は、防水シートの全体幅の12.5%〜30%であることを特徴とする防水シート。 A waterproof sheet comprising a nonwoven fabric and a water shielding sheet disposed on one surface of the nonwoven fabric,
At both side edges in the width direction of the waterproof sheet, the nonwoven fabric and the water shielding sheet are separated from each other, and at other portions, the nonwoven fabric and the water shielding sheet are bonded by surface bonding and point bonding. ,
The point adhesion portion is present in a portion adjacent to one or both side edges in the width direction of the waterproof sheet,
The waterproof sheet according to claim 1, wherein the maximum width of the point adhesion portion is 12.5% to 30% of the entire width of the waterproof sheet.