JP6555864B2 - 非偏光部を有する偏光子の製造方法 - Google Patents
非偏光部を有する偏光子の製造方法 Download PDFInfo
- Publication number
- JP6555864B2 JP6555864B2 JP2014186909A JP2014186909A JP6555864B2 JP 6555864 B2 JP6555864 B2 JP 6555864B2 JP 2014186909 A JP2014186909 A JP 2014186909A JP 2014186909 A JP2014186909 A JP 2014186909A JP 6555864 B2 JP6555864 B2 JP 6555864B2
- Authority
- JP
- Japan
- Prior art keywords
- polarizer
- polarizing
- basic solution
- film
- polarizing film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
1つの実施形態においては、上記浸漬工程での上記偏光フィルム積層体を液中に搬送する角度は0°〜90°である。
1つの実施形態においては、上記浸漬工程は、上記偏光フィルム積層体を傾斜搬送することにより行われる。
1つの実施形態においては、上記偏光フィルム積層体を傾斜搬送しながら塩基性溶液内に搬送させることを含む。
1つの実施形態においては、本発明の非偏光部を有する偏光子の製造方法は、塩基性溶液以外の処理液への浸漬工程をさらに含み、該他の処理液への浸漬工程は該偏光フィルム積層体を露出部が上向きになるよう搬送して処理液に浸漬することにより行われる。
1つの実施形態においては、上記他の処理液への浸漬処理は、上記偏光フィルム積層体を傾斜搬送して処理液に浸漬することにより行われる。
本発明の偏光子の製造方法では、偏光子と該偏光子の一方面側に配置された表面保護フィルムとを備え、該一方面側に偏光子が露出した露出部を有する偏光フィルム積層体を用いて塩基性溶液への浸漬を行う。この偏光フィルム積層体は、偏光子が露出した露出部を有するため、浸漬処理において、偏光子の露出した部分のみが塩基性溶液と接触することになる。
偏光フィルム積層体100に用いられる偏光子10としては、任意の適切な偏光子が採用され得る。偏光子は、代表的には樹脂フィルムで構成される。樹脂フィルムは、代表的には、ヨウ素や有機染料等の二色性物質を含むポリビニルアルコール系樹脂(以下、「PVA系樹脂」と言う)フィルムである。偏光子を構成する樹脂フィルム(代表的には、PVA系樹脂フィルム)は、単一のフィルムであってもよく、樹脂基材上に形成された樹脂層(代表的には、PVA系樹脂層)であってもよい。
表面保護フィルム50は、偏光子(偏光子中間体)の非偏光部が形成される位置に対応する貫通孔61が設けられる。1つの実施形態においては、表面保護フィルムは、任意の適切な樹脂フィルムと該樹脂フィルムの一方の面に設けられた粘着剤層とを有する積層体であり、該樹脂フィルムと該粘着剤層とを貫通する貫通孔を有する(図2の表面保護フィルム)。
本発明の非偏光部を有する偏光子の製造方法は、露出部を有する偏光フィルム積層体を塩基性溶液に浸漬する工程を含む。長尺状の偏光フィルム積層体を用いる場合、偏光フィルム積層体を搬送しながら浸漬することにより、脱色処理を行うことができるので、製造効率が顕著に高くなる。上記のとおり、本発明で用いる偏光フィルム積層体は、第1の表面保護フィルム(および、必要に応じて第2の表面保護フィルム)を用いる。そのため、偏光フィルム積層体の露出部以外の部分ではヨウ素濃度が低減しないため、浸漬により非偏光部を形成することが可能となる。具体的には、塩基性溶液に偏光フィルム積層体を浸漬することにより、偏光フィルム積層体における露出部のみが塩基性溶液と接触する。
本発明の非偏光部を有する偏光子の製造方法は、塩基性溶液以外の他の処理液への浸漬工程をさらに含んでいてもよい。上記他の処理液としては、例えば、偏光フィルム積層体の酸処理に用いられる酸性溶液や、洗浄に用いられる水等の洗浄液等が挙げられる。これらの他の処理液による浸漬工程においても、長尺状の偏光フィルム積層体を露出部が上向きになるよう搬送しながら、浸漬処理を行うことが好ましい。他の処理液を用いる場合であっても、塩基性溶液への浸漬工程と同様に、偏光フィルム積層体の露出部での気泡抱き込みが生じ得る。その結果、所望の処理液による浸漬を行う効果が十分に得られない場合がある。他の処理液による浸漬工程においても、気泡の抱き込みを抑制することにより、所望の処理液への浸漬を行う効果を十分に得ることができる。
酸性溶液を用いた浸漬工程は、上記塩基性溶液への浸漬工程と組合せて行われ、かつ、塩基性溶液の浸漬工程の後、酸性溶液を用いた浸漬工程が行われることが好ましい。塩基性溶液に浸した後、酸性溶液に浸漬(接触)させることにより、非偏光部に残存する塩基性溶液をさらに良好なレベルまで除去することができる。また、酸性溶液と接触させることにより、非偏光部の寸法安定性および耐久性が向上し得る。酸性溶液を用いた浸漬工程は、塩基性溶液の除去を行った後に行ってもよく、塩基性溶液を除去することなく行ってもよい。酸性溶液への浸漬工程が偏光フィルム積層体を傾斜搬送することを含む場合、露出部全体と酸性溶液とを十分に接触させることができ、酸性溶液と接触させることによる効果をより十分に得ることができる。
洗浄は、各工程で偏光フィルム積層体表面に付着した処理液や異物を除去するために行われ得る。例えば、本発明の製造方法においては、上記塩基性溶液への浸漬工程および/または酸性溶液への浸漬工程の後に行われ得る。洗浄工程に供する偏光フィルム積層体を傾斜搬送することにより、偏光フィルム積層体表面および露出部内と洗浄に使用する液体とを十分に接触させることができる。これにより、偏光フィルム積層体表面および露出部を洗浄することによる効果がより発揮され得る。
本発明の製造方法は、上記A項〜C項で挙げた以外の任意の適切な工程を含み得る。例えば、上記浸漬工程に用いた処理液の除去工程、乾燥工程等が挙げられる。
本発明の製造方法は、上記の通り、偏光フィルム積層体の露出部への気泡の抱き込みを防止し得るものである。そのため、本発明の製造方法により得られる偏光子では、非偏光部の脱色不良等の不具合が抑制され得る。したがって、本発明の製造方法により提供される偏光子は優れた品質を有し得る。本発明の非偏光部を有する偏光子はスマートフォン等の携帯電話、ノート型PC、タブレットPC等のカメラ付き画像表示装置(液晶表示装置、有機ELデバイス)に好適に用いられる。これらに適用される際に、非偏光部はこれらの機器のカメラホール部に対応し得る。非偏光部がカメラホール部に対応する場合、カメラホール部の透過性を確保するのみならず、撮影時の明るさおよび色味を最適化し、かつ、像の歪みを防止して、得られる画像表示装置のカメラ性能の向上に寄与することができる。また、本発明の非偏光部を有する偏光子は、映像やモニタ等の受信型電子デバイス(例えば、撮影光学系を有するカメラ装置)だけでなく、LEDライトや赤外線センサー等の発信型電子デバイスおよび肉眼に対しての透過性および光の直進性を確保する画像表示装置にも好適に用いることができる。
20 保護層
30 第2の表面保護フィルム
50 第1の表面保護フィルム
70 樹脂フィルム
80 粘着剤層
100 偏光フィルム積層体
Claims (6)
- 偏光子と該偏光子の一方面側に配置された表面保護フィルムとを備え、該一方面側に偏光子が露出した露出部を有する長尺状の偏光フィルム積層体を塩基性溶液に浸漬させる工程を含み、
該塩基性溶液への浸漬が、該偏光フィルム積層体を露出部が上向きになるよう塩基性溶液に搬送して行われる、非偏光部を有する偏光子の製造方法であって、
該表面保護フィルムが樹脂フィルムと該樹脂フィルムの一方の面に設けられた粘着剤層とを有する積層体であり、該粘着剤層の厚みが5μm〜60μmである、非偏光部を有する偏光子の製造方法。 - 前記塩基性溶液に浸漬させる工程での前記偏光フィルム積層体を液中に搬送する角度が0°〜90°である、請求項1に記載の非偏光部を有する偏光子の製造方法。
- 前記塩基性溶液に浸漬させる工程が、前記偏光フィルム積層体を傾斜搬送することを含む、請求項1または2に記載の非偏光部を有する偏光子の製造方法。
- 前記偏光フィルム積層体を傾斜搬送しながら塩基性溶液内に搬送させることを含む、請求項1から3のいずれかに記載の非偏光部を有する偏光子の製造方法。
- 塩基性溶液以外の処理液への浸漬工程をさらに含み、
該塩基性溶液以外の処理液への浸漬工程が該偏光フィルム積層体を露出部が上向きになるよう搬送して処理液に浸漬することにより行われる、請求項1から4のいずれかに記載の非偏光部を有する偏光子の製造方法。 - 前記塩基性溶液以外の処理液への浸漬工程が、前記偏光フィルム積層体を傾斜搬送して処理液に浸漬することにより行われる、請求項5に記載の非偏光部を有する偏光子の製造方法。