JP6507622B2 - スチレン系発泡シート及びこれを用いた成形体 - Google Patents
スチレン系発泡シート及びこれを用いた成形体 Download PDFInfo
- Publication number
- JP6507622B2 JP6507622B2 JP2014256150A JP2014256150A JP6507622B2 JP 6507622 B2 JP6507622 B2 JP 6507622B2 JP 2014256150 A JP2014256150 A JP 2014256150A JP 2014256150 A JP2014256150 A JP 2014256150A JP 6507622 B2 JP6507622 B2 JP 6507622B2
- Authority
- JP
- Japan
- Prior art keywords
- styrene
- resin
- styrenic
- foam sheet
- monomer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
〔スチレン系樹脂〕
本発明で用いるスチレン系樹脂は、複数の分岐を有し、且つ複数の重合性二重結合を有する多分岐状マクロモノマー(a1)と、スチレン系モノマー(a2)と、メタクリル酸(a3)とを必須成分とする単量体混合物(a)を共重合して得られるスチレン系樹脂であって、前記メタクリル酸(a3)との使用割合が、前記単量体混合物(a)中0.2〜3質量%の範囲で用いてなり、前記多分岐状マクロモノマー(a1)とスチレン系モノマー(a2)とメタクリル酸(a3)とを共重合させることにより得られる多分岐状共重合体(A1)を必須とし、共重合時に同時に生成するスチレン系モノマー(a2)とメタクリル酸(a3)とを共重合してなる線状樹脂である共重合体(A2)、更に、スチレン系モノマー(a2)の単独重合体や、メタクリル酸(a3)の単独重合体を含有していても良い。
本発明に使用される前記スチレン系樹脂(A)をGPC−MALLSにより分子量を測定すると、例えば、図1に示すクロマトグラフが得られる。図1中、低分子量側のピークがP1であり、高分子量側のピークがP2である。ピークP1には、線状の樹脂と、低分岐度の樹脂が含まれていると推測される。そして、ピークP2には主として多分岐状の高分岐度の樹脂が含まれていると推測される。なお、ピークP2の領域は、ピークP2の最高点からベースライン(図1中、volume軸にほぼ平行に引かれた点線)に降ろした垂線と、ベースラインと、該最高点から左側の分子量カーブとで囲まれた領域(1)と、該領域(1)を、前記垂線を対称軸として右側に折り返したときに形成される分子量カーブ(図1中、垂線の右側に点線で示した仮想の分子量カーブ)と、垂線と、ベースラインとで囲まれた領域(2)とにより形成される領域である。そして、ピークP1の領域は、分子量カーブと、ベースラインとで囲まれた領域から前記領域(1)と領域(2)からなるピークP1の領域を差し引いた部分である。
本発明に使用される前記スチレン系樹脂(A)のピークP1の領域中の樹脂とピークP2の領域中の樹脂の質量比は、得られるシートの強度と加工性とのバランスに優れる点で(ピークP2の領域中の樹脂)/(ピークP1の領域中の樹脂)=30/70〜70/30が好ましく、より好ましくは、40/60〜60/40である。この比率は、多分岐状マクロモノマー(a1)とスチレン系モノマー(a2)、メタクリル酸(a3)との使用割合の調整や、連鎖移動剤の種類及びその使用量によって、容易に制御可能である。
また、本発明に使用される前記スチレン系樹脂(A)のGPC−MALLSから求められる分子量を横軸、慣性半径を縦軸とした両対数グラフにおける分子量25万〜1000万の領域での傾きは、強度と成形加工性とを優れたバランスで発現させる点で、0.25〜0.55であることが最も好ましい。傾きが0.55よりも大きくなると、線状樹脂により近い物性となり、逆に0.25よりも小さくなると、分岐度増加に伴う分子量増大により流動性が低下することがある。
本発明で使用する複数の分岐を有し、且つ複数の重合性二重結合を有する多分岐状マクロモノマー(a1)としては、上記諸特性に優れたスチレン系樹脂を容易に得られる点、特にピークP2に含まれる多分岐状の樹脂の重量平均分子量を1000万以下に制御してゲル物発生を抑制し、流動性を確保する観点から、多分岐状マクロモノマー(a1)の重量平均分子量(Mw)が、好ましくは1,000〜15,000、より好ましくは3,000〜8,000の範囲のものを用いる。
前記多分岐状マクロモノマー(a1)とスチレン系モノマー(a2)とメタクリル酸(a3)を、必要に応じて併用されるその他のモノマーとを共重合させることにより、多分岐状の樹脂と、重合条件により同時に生成する線状の樹脂及び低分岐樹脂との混合物であるスチレン系樹脂(A)が得られる。この時、前述の多分岐状マクロモノマー(a1)をスチレン系モノマー(a2)とメタクリル酸(a3)との総量に対して好ましくは50ppm〜1%、より好ましくは100ppm〜3000ppm(質量基準)の比率で用いることにより、多分岐状の樹脂の生成が容易であり、本発明に使用されるスチレン系発泡シート用の樹脂の作製を容易にする。
重合工程では、多分岐状マクロモノマー(a1)、スチレン系モノマー(a2)、メタクリル酸をモノマー成分として用い、これらを共重合させることによって、これら3成分の共重合体である多分岐状の共重合体を含むスチレン系樹脂(A)を得ることができる。本発明における当該樹脂(A)を得るための重合装置の反応容器についての一例を図3に示す。すなわち、反応液はポンプ(1)によって攪拌式反応器(I)に送られ、次いでポンプ(2)によって循環重合ライン(II)に送られ、循環重合ライン(II)内をポンプ(3)によって循環し、循環後は非循環重合ライン(III)に送られる。ここで、循環重合ライン(II)は(4)〜(6)から成る3つの反応器から構成され、非循環重合ライン(III)は(7)〜(9)から成る3つの反応器から構成される。
重合工程の後に、未反応モノマーや溶剤分を揮発するための脱揮槽1及び脱揮槽2が連結される。脱揮槽1、脱揮槽2はそれぞれ4.0kPa、1.3kPaの減圧下状態に調整しておくことが好ましく、脱揮槽1、脱揮槽2を通過後ペレット化され、本発明に使用されるスチレン系樹脂(A)を得ることができる。
スチレン系樹脂組成物のGPC−MALS測定を、Shodex HPLC、検出器Wyatt Technology DAWN EOS、Shodex RI−101、カラムShodex KF−806L×2、溶媒THF、流量1.0ml/minの条件にて行った。また、GPC−MALLSの測定の解析は、Wyatt社の解析ソフトASTRAにより行い、スチレン系樹脂組成物について重量平均分子量を求めた他、GPC−MALLSから求められる該樹脂組成物の分子量を横軸、慣性半径を縦軸とした両対数グラフにおける分子量25万〜1000万の領域での傾き(当該分子量範囲で得られた直線状の部分のみの測定値を元に、前記ソフトにて自動計算される近似直線の傾き)を求めた。
JIS K7210に準拠して測定した。測定条件は、230℃、37Nである。
JIS K7206に準拠して測定した。
発泡シートを作製後、容器形状へと二次成形を行った。成形では深さ(H)と開口部(W)との比(H/W)が0.75となるような金型を用いた。成形条件は、発泡シートの予備加熱時間を13秒、加熱ヒーター温度を280〜300℃とした。
◎:容器の形が完全に再現している、
○:一部型が不再現、
△:容器底面の縁に小さな穴が発生、
×:容器底部に大きな穴が発生
発泡シートの二次成形品を、110℃に保ったオーブン内に10分間入れた後、容器外観を目視により下記4段階にて評価した。
◎:変化なし、
○:一部表面ヤケが見られるものの実用上問題なし、
△:容器がわずかに変形、
×:容器が大きく変形
発泡シートの二次成形品の天地圧縮テストを行った。
◎:問題なし、
○:実用上問題のないレベル、
△:難あり、
×:容易に破断する
<多分岐ポリエーテルポリオール1の合成>
攪拌機、温度計、滴下ロート及びコンデンサーを備えた2リットルフラスコに、室温下、エトキシ化ペンタエリスリトール(5モル−エチレンオキシド付加ペンタエリスリトール)50.5g、BF3ジエチルエーテル溶液(50%)1gを加え、110℃に加熱した。これに3−エチル−3−(ヒドロキシメチル)オキセタン450gを、反応による発熱を制御しつつ、25分間でゆっくり加えた。発熱が収まったところで、反応混合物をさらに120℃で3時間撹拌し、その後、室温に冷却した。得られた多分岐ポリエーテルポリオールの重量平均分子量は3,000、水酸基価は530であった。
攪拌機、温度計、コンデンサーを備えたディーンスタークデカンター及び気体導入管を備えた反応器に、上述の<多分岐ポリエーテルポリオール1の合成>で得られた多分岐ポリエーテルポリオール50g、メタアクリル酸13.8g、トルエン150g、ヒドロキノン0.06g、パラトルエンスルホン酸1gを加え、混合溶液中に3ミリリットル/分の速度で7%酸素含有窒素(v/v)を吹き込みながら、常圧下で撹拌し、加熱した。デカンターへの留出液量が1時間あたり30gになるように加熱量を調節し、脱水量が2.9gに到達するまで加熱を続けた。反応終了後、一度冷却し、無水酢酸36g、スルファミン酸5.7gを加え、60℃で10時間撹拌した。その後、残っている酢酸及びヒドロキノンを除去する為に5%水酸化ナトリウム水溶液50gで4回洗浄し、さらに1%硫酸水溶液50gで1回、水50gで2回洗浄した。得られた有機層にメトキノン0.02gを加え、減圧下、7%酸素含有窒素(v/v)を導入しながら溶媒を留去し、イソプロペニル基およびアセチル基を有する多分岐ポリエーテル60gを得た。得られた多分岐ポリエーテルの重量平均分子量は3,900であり、多分岐ポリエーテルポリオールへのイソプロペニル基およびアセチル基導入率は、それぞれ30モル%および62モル%であった。
<多分岐ポリエーテルポリオール2の合成>
窒素、空気リフラックスコンデンサー、マグネット式撹拌棒、温度計を接続した1000mLの3つ口フラスコ中で、三フッ化ホウ素ジエチルエーテル錯体1.24g(8.7mmol)を、乾燥かつ過酸化物を除去したメチル−t−ブチルエーテル273gで希釈した。別途容器にて、3−ヒドロキシメチル−3−エチルオキセタン140g(1.21mol)とプロピレンオキサイド70.0g(1.21mol)を混合し、上記3つ口フラスコへ、定量ポンプで5.5時間かけて滴下した。このとき、系内の温度を20℃に保つよう、随時アイスバスで冷却を行った。滴下終了後、さらにプロピレンオキサイド63.0g(1.08mol)を、同様に系内の温度を20℃に保ちつつ、3時間かけて滴下し、さらに4時間攪拌した。ここで、三フッ化ホウ素ジエチルエーテル錯体0.620g(4.4mmol)を添加し、さらに20℃で6時間攪拌した。反応混合物は、反応に使用した三フッ化ホウ素ジエチルエーテル錯体の10倍重量のハイドロタルサイトを加え、1時間還流させることにより吸着除去した。ハイドロタルサイトを濾別したのち、メチル−t−ブチルエーテルを除去し、透明で高粘性の多分岐ポリエーテルポリオール267gを得た。この多分岐ポリエーテルポリオールは、Mn=2,876g/mol、Mw=7,171g/mol、水酸基価=253mg・KOH/gであり、プロトンNMRから、モル基準で3−ヒドロキシメチル−3−エチルオキセタン:プロピレンオキサイド=1:1.9であった。
ディーン・スターク管、窒素及び空気導入管、撹拌装置、温度計を具備した500mLの4つ口フラスコ中に、上述の<多分岐ポリエーテルポリオール2の合成>で得られた多分岐ポリエーテルポリオールを155g、アクリル酸51g、シクロヘキサン200g、ハイドロキノンモノメチルエーテル0.21g、触媒としてドデシルベンゼンスルホン酸4g(12.3mmol)を仕込み、窒素と空気2対1の混合ガス流通下で、82℃まで昇温した。シクロヘキサンの還流が始まり、水の流出が徐々に始まった。その後、85℃まで昇温して18時間反応させると、理論脱水量の60%に達したので冷却を開始した。30℃付近まで冷却した後、5%水酸化ナトリウム水溶液及び15%NaCl水溶液を加えて洗浄を行った。得られた重合性不飽和基含有多分岐ポリエーテルの水酸基価は、70mg・KOH/gで、全水酸基のアクリル基導入率は、60%であった。
<スチリル基及びアセチル基を有する多分岐ポリエーテル1の合成>
攪拌機、乾燥管を備えたコンデンサー、滴下ロート及び温度計を備えた反応器に、上述の<多分岐ポリエーテルポリオール1の合成>で得られた多分岐ポリエーテルポリオール50g、テトラヒドロフラン100g及び水素化ナトリウム4.3gを加え、室温下、撹拌した。これに4−クロロメチルスチレン26.7gを1時間かけて滴下し、得られた反応混合物を50℃でさらに4時間撹拌した。反応終了後、一度冷却し、無水酢酸34g、スルファミン酸5.4gを加え、60℃で10時間撹拌した。その後、減圧下でテトラヒドロフランを留去し、得られた混合物をトルエン150gで溶解させ、残っている酢酸を除去する為に5%水酸化ナトリウム水溶液50gで4回洗浄し、さらに1%硫酸水溶液50gで1回、水50gで2回洗浄した。得られた有機層から減圧下で溶媒を留去し、スチリル基およびアセチル基を有する多分岐ポリエーテル70gを得た。得られた多分岐ポリエーテルの質量平均分子量は4,800であり、多分岐ポリエーテルポリオールへのスチリル基およびアセチル基導入率は、それぞれ38モル%および57モル%であった。
<メタクリロイル基及びアセチル基を有する多分岐状マクロモノマーの合成>
4口フラスコにスターラー、圧力計、冷却器及び受け皿を取り付け、これに308.9gのエトキシル化ペンタエリスリトールと0.46gの硫酸を加えた。その後、140℃まで加温し、460.5gの2,2−ジ(ヒドロキシメチル)プロピオン酸を10分間で加えた。2,2−ジ(ヒドロキシメチル)プロピオン酸が完全に溶解して、透明溶液になってから、30〜40mmHgに減圧し、攪拌しながら、酸価が7.0mgKOH/gになるまで4時間反応させた。その後、この反応液に921gの2,2−ジ(ヒドロキシメチル)プロピオン酸と0.92gの硫酸を15分かけて加え、透明溶液になってから、30〜40mmHgに減圧し、攪拌しながら3時間反応させて、ポリエステルポリオールを得た。7%酸素導入管、温度計、コンデンサーを備えたディーンスタークデカンター、および攪拌機を備えた反応容器に、上記で生成したポリエステルポリオールを10g、ジブチル錫オキシド1.25g、イソプロペニル基を有するメチルメタクリレート100g、およびヒドロキノン0.05gを加え、混合溶液中に3ml/分の速度で7%酸素を吹き込みながら、撹拌下に加熱した。デカンターへの留出液量が1時間あたり15〜20gになるように加熱量を調節し、1時間ごとにデカンター内の留出液を取り出し、これに相当する量のメチルメタクリレートを加えながら4時間反応させた。反応終了後、メチルメタクリレートを減圧下で留去し、残っているヒドロキシ基をキャッピングするために無水酢酸10g、スルファミン酸2gを加えて室温下、10時間撹拌した。濾過でスルファミン酸を除去し、減圧下で無水酢酸および酢酸を留去した後に、残留物を酢酸エチル70gに溶解し、ヒドロキノンを除去する為に5%水酸化ナトリウム水溶液20gで4回洗浄した。さらに7%硫酸水溶液20gで2回、水20gで2回洗浄した。得られた有機層にメトキノン0.0045gを加え、減圧下、7%酸素を導入しながら溶媒を留去し、イソプロペニル基およびアセチル基を有する多分岐状マクロモノマー(Mm−3)11gを得た。得られた多分岐状マクロモノマー(Mm−3)の重量平均分子量は3,000、数平均分子量は2,100、二重結合導入量は2.00mmol/gであり、イソプロペニル基およびアセチル基導入率は、それぞれ55モル%および36モル%であった。
<スチリル基を有するPAMAMデンドリマーの合成>
攪拌機、乾燥管を備えたコンデンサー、滴下ロート及び温度計を備えた反応器にPAMAMデンドリマー(ゼネレーション2.0:Dentritech社製)のメタノール溶液(20%)50gを加え、減圧下、撹拌しながらメタノールを留去した。続いて、テトラヒドロフラン50g及び微粉化した水酸化カリウム3.0gを加え、室温下、撹拌した。これに4−クロロメチルスチレン7.0gを10分間かけて滴下し、得られた反応混合物を50℃でさらに3時間撹拌した。反応終了後、冷却し、固体を濾過した後に、テトラヒドロフランを減圧下、留去し、スチリル基を有するPAMAMデンドリマー13gを得た。得られたデンドリマーのスチリル基含有率は2.7ミリモル/グラムであった。
<スチリル基及びアセチル基を有する多分岐ポリエーテルポリオール2>
攪拌機、コンデンサー、遮光性滴下ロート及び温度計を備え、窒素シールが可能な遮光性反応容器に、窒素気流下、無水1,3,5−トリヒドロキシベンゼン0.5g、炭酸カリウム29g、18−クラウン−6 2.7g及びアセトン180gを加え、撹拌しながら、5−(ブロモメチル)−1,3−ジヒドロキシベンゼン21.7gとアセトン180gからなる溶液を2時間かけて滴下、加えた。その後、5−(ブロモメチル)−1,3−ジヒドロキシベンゼンが消失するまで、撹拌下、加熱、還流させた。その後、4−クロロメチルスチレン9.0gを加え、これが消失するまで、さらに撹拌下、加熱、還流させた。その後、反応混合物に無水酢酸4g、スルファミン酸0.6gを加え、室温下、一晩撹拌した。冷却後、反応混合物中の固体を濾過で除き、溶媒を減圧下で留去した。得られた混合物をジクロロメタンに溶解し、水で3回洗浄した後、ジクロロメタン溶液をヘキサンに滴下し、多分岐ポリエーテルを沈殿させた。これを濾過し、乾燥させて、スチリル基及びアセチル基を有する多分岐ポリエーテルポリオール12gを得た。質量平均分子量は3,200で、スチリル基の含有率は3.5ミリモル/グラムであった。
<メタクリロイル基及びアセチル基を有する多分岐ポリエステルポリオールの合成>
7%酸素導入管、温度計、コンデンサーを備えたディーンスタークデカンター、および攪拌機を備えた反応容器に、「Boltorn H20」10g、ジブチル錫オキシド1.25g、官能基としてイソプロペニル基を有するメチルメタクリレート100g、およびヒドロキノン0.05gを加え、混合溶液中に3ml/分の速度で7%酸素を吹き込みながら、撹拌下に加熱した。デカンターへの留出液量が1時間あたり15〜20gになるように加熱量を調節し、1時間ごとにデカンター内の留出液を取り出し、これに相当する量のメチルメタクリレートを加えながら6時間反応させた。
スチレンモノマー98部、メタクリル酸モノマーを2部、参考例1で得られた多分岐状マクロモノマー(Mm−1)をスチレンモノマーとメタクリル酸モノマーの合計量に対し1000ppm、トルエン8部からなる混合溶液を調製し、更に、有機過酸化物としてt−ブチルパーオキシベンゾエートをスチレンモノマーとメタクリル酸モノマーの合計量に対し150ppm加え、図3に示す装置を用いて下記条件で連続的に塊状重合させた。攪拌式反応器(I)は110〜130℃、循環重合ライン(II)、非循環重合ライン(III)は、それぞれ115〜170℃とした。反応液からは、最終反応器である非循環重合ライン(III)後に設置され脱揮槽1及び脱揮槽2において、未反応モノマー及び溶剤分が回収される。脱揮槽1及び脱揮槽2は、240〜280℃とした。その後単管を通過しストランド化及びペレタイザーにてペレット化を行い、スチレン系樹脂(A−1)を得た。
マクロモノマーを参考例2で得られたMm−2に変更しスチレン系樹脂(A−2)を得た以外は、実施例1と全て同一とした。
マクロモノマーを参考例3で得られたMm−3に変更しスチレン系樹脂(A−3)を得た以外は、実施例1と全て同一とした。
マクロモノマーを参考例4で得られたMm−4に変更しスチレン系樹脂(A−4)を得た以外は、実施例1と全て同一とした。
マクロモノマーを参考例5で得られたMm−5に変更しスチレン系樹脂(A−5)を得た以外は、実施例1と全て同一とした。
マクロモノマーを参考例6で得られたMm−6に変更しスチレン系樹脂(A−6)を得た以外は、実施例1と全て同一とした。
マクロモノマーを参考例7で得られたMm−7に変更しスチレン系樹脂(A−7)を得た以外は、実施例1と全て同一とした。
単量体としてスチレンモノマー97部、メタクリル酸モノマーを3部用いてスチレン系樹脂(A−8)を得たこと以外は、実施例1と全て同一とした。
マクロモノマーを2000ppmとしスチレン系樹脂(A−9)を得たこと以外は、実施例1と全て同一とした。
マクロモノマーを200ppmとしスチレン系樹脂(A−10)を得たこと以外は、実施例1と全て同一とした。
スチレンモノマー96部、メタクリル酸モノマーを3部、共重合可能なモノマーとしてアクリル酸ブチルを1部用いてスチレン系樹脂(A−11)を得たこと以外は、実施例1と全て同一とした。
実施例8と同様にして得たスチレン系樹脂(A−8)を90部、その他のスチレン系樹脂としてゴム変性スチレン系樹脂(B−1、DIC株式会社製ディックスチレンGH−8300−5)を10部用いて発泡シートを作製した以外は、実施例1と全て同一とした。
スチレンモノマー98部、アクリル酸ブチルを2部、マクロモノマーを0ppmとした以外は実施例1と同様にしてスチレン系共重合体(B−2)を得た。実施例8と同様にして得たスチレン系樹脂(A−8)を95部、その他のスチレン系樹脂としてスチレン系共重合体(B−2)を5部用いて発泡シートを作製した以外は、実施例1と全て同一とした。
実施例8と同様にして得たスチレン系樹脂(A−8)を97部、その他のスチレン系樹脂としてスチレン−ブタジエン共重合樹脂(B−3−1、旭化成ケミカルズ株式会社製タフプレン125)を3部用いて発泡シートを作製した以外は、実施例1と全て同一とした。
実施例8と同様にして得たスチレン系樹脂(A−8)を97部、その他のスチレン系樹脂としてスチレン−ブタジエン共重合樹脂(B−3−2、旭化成ケミカルズ株式会社製タフテックH1041)を3部用いて発泡シートを作製した以外は、実施例1と全て同一とした。
実施例8と同様にして得たスチレン系樹脂(A−8)を97部、その他のスチレン系樹脂としてメタクリル酸メチル−ブタジエン−スチレン共重合樹脂(B−3−3、ブタジエン80質量%)を3部用いて発泡シートを作製した以外は、実施例1と全て同一とした。
スチレンモノマーを100部、メタクリル酸モノマーを0部としたこと、マクロモノマーを0ppmとした以外は、実施例1と全て同一とした。
マクロモノマーを0ppmとした以外は、実施例1と全て同一とした。
スチレンモノマーを94部、メタクリル酸モノマーを6部としたこと、マクロモノマーを0ppmとした以外は、実施例1と全て同一とした。
スチレンモノマーを97部、メタクリル酸モノマーを3部、マクロモノマーを0ppmとした以外は、実施例1と同様にスチレン系樹脂を得た。このスチレン系樹脂70質量部とゴム変性スチレン系樹脂(B−1)30質量部を用いて発泡シートを作製した以外は、実施例1と全て同一とした。
比較例4と同様にして得たスチレン系樹脂80質量部とスチレン系共重合体(B−2)20質量部を用いて発泡シートを作製した以外は、実施例1と全て同一とした。
比較例4と同様にして得たスチレン系樹脂90質量部とスチレン−ブタジエン共重合樹脂(B−3−1)10質量部を用いて発泡シートを作製した以外は、実施例1と全て同一とした。
比較例4と同様にして得たスチレン系樹脂90質量部とスチレン−ブタジエン共重合樹脂(B−3−2)10質量部を用いて発泡シートを作製した以外は、実施例1と全て同一とした。
比較例4と同様にして得たスチレン系樹脂90質量部とメタクリル酸メチル−ブタジエン−スチレン共重合樹脂(B−3−3)10質量部を用いて発泡シートを作製した以外は、実施例1と全て同一とした。
Claims (10)
- 複数の分岐を有し、且つ複数の重合性二重結合を有する多分岐状マクロモノマー(a1)と、スチレン系モノマー(a2)と、メタクリル酸(a3)とを必須成分とする単量体混合物(a)を共重合して得られるスチレン系樹脂であって、前記メタクリル酸(a3)の使用割合が、前記単量体混合物(a)中0.2〜3質量%の範囲であるスチレン系樹脂(A)を発泡してなることを特徴とするスチレン系発泡シート。
- 前記スチレン系樹脂(A)のGPC−MALLSで求められる重量平均分子量が15万〜70万の範囲である請求項1記載のスチレン系発泡シート。
- 前記多分岐状マクロモノマー(a1)における分岐構造が、電子吸引基と、該電子吸引基に結合する結合手以外の3つの結合手すべてが炭素原子に結合している4級炭素原子によって枝分かれしているもの、または、エーテル結合、エステル結合若しくはアミド結合を有する構造単位の繰り返しによって分岐構造を形成するものである請求項1又は2記載のスチレン系発泡シート。
- 前記単量体混合物(a)中に、更に(メタ)アクリル酸エステルを含有するものである請求項1〜3の何れか1項記載のスチレン系発泡シート。
- 前記スチレン系樹脂(A)にゴム変性スチレン系樹脂(B−1)を混合しスチレン系樹脂組成物にした後、これを発泡してなるものであり、
前記ゴム変性スチレン系樹脂(B−1)の使用割合が、前記スチレン系樹脂(A)と前記ゴム変性スチレン系樹脂(B−1)の合計量に対して、前記ゴム変性スチレン系樹脂(B−1)が0.1〜20質量%の範囲である、請求項1〜4の何れか1項記載のスチレン系発泡シート。 - 前記スチレン系樹脂(A)に、スチレン系モノマーと(メタ)アクリル酸エステルとの共重合体(B−2)を混合しスチレン系樹脂組成物にした後、これを発泡してなるものであり、
前記スチレン系モノマーと(メタ)アクリル酸エステルとの共重合体(B−2)の使用割合が、前記スチレン系樹脂(A)と前記共重合体(B−2)の合計量に対して、前記共重合体(B−2)が0.1〜10質量%の範囲である、請求項1〜4の何れか1項記載のスチレン系発泡シート。 - 前記スチレン系樹脂(A)にスチレン系熱可塑性エラストマー(B−3)を混合しスチレン系樹脂組成物にした後、これを発泡してなるものであり、
前記スチレン系熱可塑性エラストマー(B−3)の使用割合が、前記スチレン系樹脂(A)と前記スチレン系熱可塑性エラストマー(B−3)の合計量に対して、前記スチレン系熱可塑性エラストマー(B−3)が0.1〜5質量%の範囲である、請求項1〜4の何れか1項記載のスチレン系発泡シート。 - 厚さが0.5〜6.0mmであり、かさ密度が0.02〜0.25g/cm3である請求項1〜7の何れか1項記載のスチレン系発泡シート。
- 請求項1〜8の何れか1項記載のスチレン系発泡シートを熱成形法によって成形してなるものであることを特徴とする成形体。
- 食品包装用途である請求項9記載の成形体。