JP6496102B2 - タイヤ - Google Patents
タイヤ Download PDFInfo
- Publication number
- JP6496102B2 JP6496102B2 JP2013264091A JP2013264091A JP6496102B2 JP 6496102 B2 JP6496102 B2 JP 6496102B2 JP 2013264091 A JP2013264091 A JP 2013264091A JP 2013264091 A JP2013264091 A JP 2013264091A JP 6496102 B2 JP6496102 B2 JP 6496102B2
- Authority
- JP
- Japan
- Prior art keywords
- mass
- parts
- bis
- rubber
- carbon black
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
スズ変性BR:日本ゼオン(株)製のBR1250(開始剤としてリチウムを用いて重合、ビニル結合量:10〜13質量%、Mw/Mn:1.5、スズ原子の含有率:250ppm、ポリスチレン換算分子量で105以下の成分の含有率:2〜3質量%、スズ末端変性BR)
NR:RSS#3
カーボンブラック:三菱化学(株)製のダイアブラックN330(N2SA:79m2/g、DBP吸油量:105cm3/100g)
スルフィド化合物1:四国化成工業(株)製の2EBZ(2,2’−ビス(ベンズイミダゾリル−2)エチルジスルフィド、式(I)中のR1が水素原子、AがNH、nが2、xが2、N2SA:10.5m2/g、油展なし)
スルフィド化合物2:100質量部のスルフィド化合物1にオイルを30質量部添加した油展物(添加したオイル:(株)ジャパンエナジー製のプロセスオイルX−40)
酸化亜鉛:三井金属鉱業(株)製の亜鉛華1号
ステアリン酸:日油(株)製のステアリン酸「椿」
アロマオイル:(株)ジャパンエナジー製のプロセスオイルX−140
ワックス:大内新興化学工業(株)製のサンノック
老化防止剤:大内新興化学工業(株)製のノクラック6C(N−(1,3−ジメチルブチル)−N’−フェニル−p−フェニレンジアミン)
硫黄:軽井沢硫黄(株)製の粉末硫黄
加硫促進剤:大内新興化学工業(株)製のノクセラーNS(N−tert−ブチル−2−ベンゾチアゾリルスルフェンアミド(TBBS))
表1に示す配合処方にしたがい、1.7Lの密閉型バンバリーミキサーを用いて、硫黄および加硫促進剤以外の薬品を150℃の条件下で4分間混練して、混練物を得た。次に、オープンロールを用いて、得られた混練物に硫黄および加硫促進剤を添加し、80℃の条件下で3分間練り込み、未加硫ゴム組成物を得た。さらに、得られた未加硫ゴム組成物を160℃の条件下で20分間プレス加硫し、加硫ゴム組成物(シート)を得た。
各未加硫ゴム組成物について、JIS K 6300−1の「未加硫ゴム−物理特性−第1部:ムーニー粘度計による粘度およびスコーチタイムの求め方」に準じたムーニー粘度の測定方法に従い、130℃の温度条件にて、ムーニー粘度(ML1+4)を測定した。結果は比較例1のムーニー粘度を100とし、下記計算式による指数で示す。加工性指数が大きいほどムーニー粘度が低く、加工性に優れることを示す。
(加工性指数)=(比較例1のML1+4)/(各配合のML1+4)×100
加硫ゴム組成物について、JIS K 6251に準じて引張試験を行い、破断伸びを測定した。結果は比較例1の破断伸びを100とし、下記計算式による指数で示す。ゴム強度指数が大きいほど、ゴム強度に優れることを示す。
(ゴム強度指数)=(各配合の破断伸び)/(比較例1の破断伸び)×100
(株)岩本製作所製の粘弾性スペクトロメーターを用いて、初期歪10%、動的歪振幅1%および周波数10Hzの条件下で、70℃における加硫ゴム組成物のヒステリシスロス(tanδ)、複素弾性率(E*)を測定した。
低燃費性指数
結果は比較例1のtanδを100とし、下記計算式による指数で示す。低燃費性指数が大きいほど転がり抵抗特性(低燃費性)に優れることを示す。
(低燃費性指数)=(比較例1のtanδ)/(各配合のtanδ)×100
操縦安定性指数
結果は比較例1のE*を100とし、下記計算式による指数で示す。操縦安定性指数が大きいほどゴム剛性が高く、操縦安定性に優れることを示す。
(操縦安定性指数)=(各配合のE*)/(比較例1のE*)×100
Claims (3)
- ゴム成分、カーボンブラックおよび下記式(I)
で示される窒素官能基を有するスルフィド化合物を含有し、
前記ゴム成分が、天然ゴムを50質量%以上、およびリチウム開始剤により重合され、スズ原子の含有量が50〜3000ppm、ビニル結合量が5〜50質量%、分子量分布(Mw/Mn)が2.0以下であるスズ変性ポリブタジエンゴムを5〜50質量%含み、
前記窒素官能基を有するスルフィド化合物の窒素吸着比表面積が2.0m 2 /g以上であり、
ゴム成分100質量部に対する前記カーボンブラックの含有量が15〜50質量部であり、カーボンブラック100質量部に対する前記窒素官能基を有するスルフィド化合物の含有量が0.05〜15質量部であるゴム組成物で構成されるベーストレッドを備えるタイヤ。 - 前記カーボンブラックの窒素吸着比表面積が50〜125m2/gであり、ジブチルフタレート吸油量が70〜155cm3/100gである請求項1記載のタイヤ。
- 前記窒素官能基を有するスルフィド化合物を、該化合物100質量部に対して5〜40質量部のオイルを添加した油展物として含有する請求項1または2に記載のタイヤ。