JP6478806B2 - ゴルフクラブ用グリップ、ゴルフクラブおよびゴルフクラブ用グリップの製造方法 - Google Patents
ゴルフクラブ用グリップ、ゴルフクラブおよびゴルフクラブ用グリップの製造方法 Download PDFInfo
- Publication number
- JP6478806B2 JP6478806B2 JP2015104821A JP2015104821A JP6478806B2 JP 6478806 B2 JP6478806 B2 JP 6478806B2 JP 2015104821 A JP2015104821 A JP 2015104821A JP 2015104821 A JP2015104821 A JP 2015104821A JP 6478806 B2 JP6478806 B2 JP 6478806B2
- Authority
- JP
- Japan
- Prior art keywords
- grip
- inner layer
- cylindrical
- rubber
- golf club
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
以下、図面を参照しつつ、本発明のゴルフクラブ用グリップの構造について説明するが、本発明は、図面に示された態様に限定されるものではない。
以下、本発明のゴルフクラブ用グリップに使用される材料について説明する。本発明のゴルフクラブ用グリップは、上記構造を有するものであれば、特に限定されない。本発明のゴルフクラブ用グリップは、円筒状外層とグリップエンドとを親和性の高い材料から形成することが好ましい。円筒状外層とグリップエンドとを親和性の高い材料から形成しておくことにより、グリップ本体とグリップエンドとの接着性が高くなるからである。具体的には、円筒状外層に使用される組成物と、グリップエンドに使用される組成物が、同じ基材ゴムを含有することが好ましい。また、円筒状外層とグリップエンドとが、同じ組成物から形成されていることも好ましい。
本発明のゴルフクラブ用グリップの円筒状外層およびグリップエンドは、基材ゴムとしてアクリロニトリル−ブタジエン系ゴムを含有する第一ゴム組成物から成形されていることが好ましい。外層がアクリロニトリル−ブタジエン系ゴムを含有することにより、グリップの引張強さが向上し、かつ、ウェット時のグリップ性能が良好となる。
前記内層は、基材ゴムまたは基材樹脂を含有する内層用組成物から成形されることが好ましい。前記基材ゴムとしては、天然ゴム(NR)、エチレン−プロピレン−ジエンゴム(EPDM)、ブチルゴム(IIR)、アクリロニトリル−ブタジエンゴム(NBR)、水素添加アクリロニトリル−ブタジエンゴム(HNBR)、カルボキシ変性アクリロニトリル−ブタジエンゴム(XNBR)、ブタジエンゴム(BR)、スチレン−ブタジエンゴム(SBR)、ポリウレタンゴム(PU)、イソプレンゴム(IR)、クロロプレンゴム(CR)、エチレン−プロピレンゴム(EPM)などが挙げられる。これらの中でも、前記基材ゴムとしては、NR、EPDM、IIR、NBR、HNBR、XNBR、BR、SBR、PUが好ましい。
前記ゴルフクラブ用グリップは、円筒状内層および円筒状外層の層間に接着剤層を有していてもよい。なお、接着剤層はその厚さが、約30μm以下の非常に薄い層であることが好ましい。接着剤層を構成する接着剤としては、加硫接着剤(架橋接着剤)、ゴムのりが挙げられる。接着剤層を有することで、円筒状内層と円筒状外層との剥離強度が高くなる。
本発明のゴルフクラブ用グリップは、例えば、前記第一ゴム組成物から形成した未加硫のゴムシートと、前記第二ゴム組成物から形成した未加硫のゴムシートまたは前記内層用樹脂組成物から形成した樹脂シートとの積層物、および、第一ゴム組成物から形成したグリップエンドを、金型内でプレス成形することで得られる。前記第一ゴム組成物または内層用組成物からシートを作製する方法は、プレス成型、射出成型のいずれも採用できる。また、グリップエンドは、未加硫、半加硫、完全加硫のいずれの状態でもよい。積層物をプレス成形する際、金型温度は140℃〜200℃が好ましく、成形時間は5分間〜45分間が好ましく、成形圧力は0.1MPa〜150MPaが好ましい。なお、バルーン発泡法を用いて発泡層を作製する場合、外層のシートおよび内層のシートを作製する際にはバルーンを膨張させず、外層のシートと内層のシートとの積層物をプレス成型する際にバルーンを膨張させることが好ましい。
本発明には、前記ゴルフクラブ用グリップを用いたゴルフクラブも含まれる。前記ゴルフクラブは、シャフトと、前記シャフトの一端に取り付けられたヘッドと、前記シャフトの他端に取り付けられたグリップとを備え、前記グリップが前記ゴルフクラブ用グリップである。前記シャフトは、ステンレス鋼製や炭素繊維強化樹脂製が使用できる。前記ヘッドとしては、ウッド型、ユーティリティ型、アイアン型が挙げられる。前記ヘッドを構成する材料は、特に限定されるものではなく、例えばチタン、チタン合金、炭素繊維強化プラスチック、ステンレス鋼、マルエージング鋼、軟鉄などが挙げられる。
(1)アクリロニトリル含有率
アクリロニトリル含有率は、水素添加前のアクリルニトリル−ブタジエンゴムについて、ISO 24698−1(2008)により測定した。
二重結合含有量は、共重合体中のブタジエン含有率(質量%)と残存二重結合量(%)から算出した。前記残存二重結合量とは、水素添加前の共重合体中の二重結合と水素添加後の共重合体中の二重結合との質量比(水素添加後の二重結合量/水素添加前の二重結合量)であり、赤外分光法により測定できる。アクリロニトリル−ブタジエンゴムが、アクリロニトリル−ブタジエン2元共重合体の場合、共重合体中のブタジエン含有率は100からアクリロニトリル含有率(質量%)を減ずることで求められる。
二重結合量={ブタジエン含有率/54}×残存二重結合量×10
水素添加アクリロニトリル−ブタジエンゴムを1g量りとり、クロロホルム50mlに溶解させ、ここにチモールブルー指示薬を滴下した。この溶液を攪拌しながら、水酸化ナトリウムの0.05mol/Lメタノール溶液を滴下し、最初に変色するまでの滴下量(Vml)を記録した。ブランクとして水素添加アクリロニトリル−ブタジエンゴムを含有しないクロロホルム50mlについても、チモールブルーを指示薬として、水酸化ナトリウムの0.05mol/Lメタノール溶液を滴下し、最初に変色するまでの滴下量(Bml)を記録した。下記式により、カルボキシ基含有率を算出した。
カルボキシ基含有単量体含有率={0.05×(V−B)×PM}/(10×X)
(式中、V:試験溶液の水酸化ナトリウム溶液滴下量(ml)、B:ブランクの水酸化ナトリウム溶液滴下量(ml)、PM:カルボキシ基含有単量体の分子量、X:カルボキシ基含有単量体の価数)
ゴム組成物を用いて、160℃で8〜20分間プレスして、厚み2mmのシートを作製した。なお、ゴム組成物がマイクロバルーンを含有する場合は、グリップを形成した際と同様の発泡倍率となるようにマイクロバルーンを膨張させてシートを作製した。このシートを、23℃で2週間保存し、測定基板などの影響が出ないように、3枚重ねた状態で、JIS K6253−3(2012)に規定するタイプAデュロメータを備えた高分子計器社製自動ゴム硬度計P1型を用いて測定した。
グリップから測定対象となる発泡層を切り出し、発泡層の密度(d1)を測定した。また、この発泡層の形成に使用されたゴム組成物を用いて未発泡のゴムシートを作製し、このゴムシートの密度(d2)を測定した。前記未発泡シートの密度を発泡層の密度で除することで発泡倍率(d2/d1)を算出した。なお、密度は、自動比重計(エムエステック社製、SP−GR1、アルキメデスの原理)を用いて測定した。
引張強さはJIS K 6251(2010)に準拠して測定した。ゴム組成物を用いて、160℃で8〜20分間プレスして、厚み2mmのシートを作製し、これをダンベル形状(ダンベル状3号形)に打ち抜いて試験片を作製した。なお、ゴム組成物がマイクロバルーンを含有する場合は、グリップを形成した際と同様の発泡倍率となるようにマイクロバルーンを膨張させてシートを作製した。各試験片について、引張試験測定装置(島津製作所社製、オートグラフAGS−D)を用いて物性を測定した(測定温度23℃、引張速度500mm/分)。そして、試験片を切断するまで引っ張ったときに記録される最大の引張力を試験片の初期断面積で除することで引張強さを算出した。
各グリップの質量を測定した。なお、質量は、グリップNo.1の質量を100として、指数化した値で示した。
成形後のゴルフクラブ用グリップのチップ側開口のシーム径と、ポール径とをそれぞれ測定して、以下の式で算出した。楕円率が0に近いほど、チップ側開口の形状が円形に近くなる。
楕円率={1−(ポール径/シーム径)}×100
グリップを取り付けたゴルフクラブを作製し、このゴルフクラブを用いて2万回の実打を行い、グリップの耐久性を評価した。評価基準は、2万回の実打後でもグリップが無傷の場合を「優」、1万回の実打後は無傷であるが、2万回の実打後に傷が生じている場合を「良」、1万回の実打後に傷が生じている場合を「不可」とした。
表1に示す配合で各原料をバンバリーミキサー(材料温度80〜150℃)で混練し、第一ゴム組成物および第二ゴム組成物を調製した。
NR(天然ゴム):TSR20
EPDM(エチレン−プロピレン−ジエンゴム):住友化学社製、エスプレン(登録商標)505A
HXNBR:水素添加カルボキシ変性アクリロニトリル−ブタジエンゴム(ランクセス社製、Therban XT VPKA 8889(残存二重結合量3.5%、アクリロニトリル含有率33.0質量%、カルボキシ基含有単量体含有率5.0質量%、二重結合含有量0.40mmol/g))
硫黄:鶴見化学工業社製、5%油入微粉硫黄(200メッシュ)
ノクセラーCZ:大内新興化学工業社製、N−シクロヘキシル−2−ベンゾチアゾリルスルフェンアミド
ノクセラーNS:大内新興化学工業社製、N−t−ブチル−2−ベンゾチアゾリルスルフェンアミド
ソクシノールD:住友化学社製、1,3−ジフェニルグアニジン
ノクセラーTBzTD:大内新興化学工業社製、テトラベンジルチウラムジスルフィド
酸化亜鉛:PT.INDO LYSAGHT社製、ホワイトシール
過酸化亜鉛:struktol社製、struktol ZP 1014(過酸化亜鉛含有量29質量%)
ステアリン酸:日油社製、ビーズステアリン酸つばき
シリカ:EVONIK社製、ウルトラジルVN3
カーボンブラック(1):三菱化学社製、ダイヤブラックN220
カーボンブラック(2):東海カーボン社製、シーストSO(FEF)
MBMBP:2,2’−メチレンビス(4−メチル−6−t−ブチルフェノール)(大内新興化学工業社製、ノクラック(登録商標)NS−6)
NiBDC:ジブチルジチオカルバミン酸ニッケル(大内新興化学工業社製、ノクラック NBC)
サントガードPVI:三新化学工業社製、N−シクロヘキシルチオフタルイミド
安息香酸:シグマアルドリッチ社製
ダイアナプロセスオイルPA32:出光興産社製
マイクロバルーン:Akzo Nobel社製、「エクスパンセル909−80」(熱可塑性樹脂の殻に低沸点炭化水素が内包された樹脂カプセル、体積平均粒子径18μm〜24μm、膨張開始温度120℃〜130℃)
第一ゴム組成物を用いて、扇台形状の未加硫の外層用ゴムシートを作製した。外層用ゴムシートは一定の厚さとなるように成形した。また、第一ゴム組成物から、厚み4mm、直径28mmの円盤状のグリップエンド(未加硫)を成形した。第二ゴム組成物を用いて、長方形状の未加硫の内層(第1内層および第2内層)用ゴムシートを作製した。なお、内層用ゴムシートは、一方端から他方端に向かって徐々に厚くなるように成形した。
Claims (11)
- 円筒状内層と、前記円筒状内層を被覆する円筒状外層とを有する円筒状グリップ本体と、前記円筒状グリップ本体のバット側端に設けられたグリップエンドとを有するゴルフクラブ用グリップであって、
前記円筒状内層のバット側端縁と前記グリップエンドとの間の少なくとも一部に、前記円筒状外層が介在しており、
前記円筒状外層とグリップエンドとが、基材ゴムとして、カルボキシル変性アクリロニトリルブタジエンゴム、水素添加アクリロニトリル−ブタジエンゴム、および、カルボキシル変性水素添加アクリロニトリル−ブタジエンゴムよりなる群から選択される少なくとも1種のアクリロニトリル−ブタジエン系ゴムを有するゴム組成物から形成されていることを特徴するゴルフクラブ用グリップ。 - 前記円筒状内層のバット側端縁とグリップエンドとの間に介在している前記円筒状外層のグリップ径方向の長さ(L1)と、前記円筒状内層のバット側端縁の厚さ(T)との比(L1/T)が、0.15以上である請求項1に記載のゴルフクラブ用グリップ。
- 前記円筒状外層のバット側端部が、前記円筒状内層のバット側端縁と円筒状内層バット側内面とを被覆するように折り返されている請求項1または2に記載のゴルフクラブ用グリップ。
- 前記円筒状内層が、基材ゴムとして、天然ゴムを含有するゴム組成物から形成されている請求項1〜3のいずれか一項に記載のゴルフクラブ用グリップ。
- 前記円筒状内層は、多孔質ゴム層である請求項4に記載のゴルフクラブ用グリップ。
- 前記多孔質ゴム層は、発泡倍率が1.2〜5.0である発泡層である請求項5に記載のグルフクラブ用グリップ。
- 前記円筒状外層が、中実層である請求項1〜6のいずれか一項に記載のゴルフクラブ用グリップ。
- シャフトと、前記シャフトの一端に取り付けられたヘッドと、前記シャフトの他端に取り付けられたグリップとを備え、
前記グリップが、請求項1〜7のいずれか1項に記載のゴルフクラブ用グリップであることを特徴とするゴルフクラブ。 - 円筒状内層と、前記円筒状内層を被覆する円筒状外層とを有する円筒状グリップ本体と、前記円筒状グリップ本体のバット側端に設けられたグリップエンドとを有するゴルフクラブ用グリップの製造方法であって、
第一ゴム組成物および内層用組成物を調製する工程、
前記内層用組成物を用いて内層シートを作製する工程、
前記第一ゴム組成物を用いて未加硫の外層シートを作製する工程、
前記第一ゴム組成物を用いてグリップエンドを作製する工程、
前記内層シートと前記外層シートとを積層し、積層物を作製する工程、
前記外層シートのバット側端部の少なくとも一部を内層シート側に折返し、内層シートのバット側端縁を外層シートで被覆する工程、および、
前記外層シートのバット側端部を折返した積層物とグリップエンドとを金型内でプレス成型する工程を含むことを特徴とするゴルフクラブ用グリップの製造方法。 - 前記内層用組成物がマイクロバルーンを含有しており、
前記外層シートのバット側端部を折り返す長さ(L0)と、発泡後の内層のバット側端部の厚さ(T)との比(L0/T)が、0.2〜3.3である請求項9に記載のゴルフクラブ用グリップの製造方法。 - 前記内層用組成物が、基材ゴムとして、天然ゴムを含有するゴム組成物であり、
前記第一ゴム組成物が、基材ゴムとしてアクリロニトリル−ブタジエン系ゴムを有するゴム組成物である請求項9または10に記載のゴルフクラブ用グリップの製造方法。