JP6468924B2 - セラミックグリーンシート製造工程用剥離フィルムおよびセラミックグリーンシート製造方法 - Google Patents
セラミックグリーンシート製造工程用剥離フィルムおよびセラミックグリーンシート製造方法 Download PDFInfo
- Publication number
- JP6468924B2 JP6468924B2 JP2015074172A JP2015074172A JP6468924B2 JP 6468924 B2 JP6468924 B2 JP 6468924B2 JP 2015074172 A JP2015074172 A JP 2015074172A JP 2015074172 A JP2015074172 A JP 2015074172A JP 6468924 B2 JP6468924 B2 JP 6468924B2
- Authority
- JP
- Japan
- Prior art keywords
- green sheet
- ceramic green
- release
- release film
- release agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
〔セラミックグリーンシート製造工程用剥離フィルム〕
本実施形態に係るセラミックグリーンシート製造工程用剥離フィルム(以下単に「剥離フィルム」という場合がある。)は、長尺の基材と、当該基材の片面側に設けられた剥離剤層とを備える。そして、剥離フィルムは、平面視において、幅方向中央部の領域にセラミックグリーンシート成形部を有し、且つ、幅方向両側部の領域に凸部を1つずつ有する。
剥離フィルム1Aにおいて、セラミックグリーンシート成形部15に位置する剥離剤層12Aの基材11とは反対側の面、すなわち剥離面の算術平均粗さRaは、8nm未満であり、5nm未満であることが好ましく、特に3nm未満であることが好ましい。なお、剥離面の算術平均粗さRaの下限値は特に限定されないものの、例えば1nm以上である。また、剥離面の最大突起高さRpは、50nm未満であり、40nm未満であることが好ましく、特に30nm未満であることが好ましい。なお、剥離面の最大突起高さRpの下限値は特に限定されないものの、例えば5nm以上である。剥離面における算術平均粗さRaが8nm以上であるか、または最大突起高さRpが50nm以上である場合、剥離面に成形したセラミックグリーンシートにおいて、ピンホールや厚みムラ等の欠陥が発生し易くなる。なお、本明細書における算術平均粗さRaおよび最大突起高さRpの測定方法は、後述する試験例に示すとおりである。
剥離フィルム1Aは剥離剤層12Aを備えることで、剥離面に成形されたセラミックグリーンシートから剥離フィルム1Aを剥離する際の剥離力を適度に低下させることができる。
剥離フィルム1Aは、基材11の両側部に樹脂層13Aを1つずつ備える。剥離フィルム1Aに樹脂層13Aを設けることで、凸部14を容易に形成することができる。
剥離フィルム1Aの基材11の材料としては、剥離剤層12Aおよび樹脂層13Aを積層することができ、さらに、剥離フィルム1Aの裏面における上述した平滑性を達成できるものであれば特に限定されない。かかる材料としては、例えば、ポリエチレンテレフタレートやポリエチレンナフタレート等のポリエステル、ポリプロピレンやポリメチルペンテン等のポリオレフィン、ポリカーボネート、ポリ酢酸ビニルなどのプラスチックからなるフィルムが挙げられ、単層であってもよいし、同種又は異種の2層以上の多層であってもよい。これらの中でもポリエステルフィルムが好ましく、特にポリエチレンテレフタレートフィルムが好ましく、さらには二軸延伸ポリエチレンテレフタレートフィルムが好ましい。ポリエチレンテレフタレートフィルムは、加工時、使用時等において、埃等が発生しにくいため、例えば、埃等によるセラミックスラリー塗工不良等を効果的に防止することができる。さらに、ポリエチレンテレフタレートフィルムに帯電防止処理を行うことで、有機溶剤を使用するセラミックスラリーを塗工する際の静電気による発火を防止したり、塗工不良等を防止する効果を高めることができる。
剥離フィルム1Aは、例えば次のように製造することができる。すなわち、基材11の一方の面の両端部に、樹脂層13Aを構成する材料および所望により有機溶剤を含有する塗工液を塗工した後、乾燥および硬化させることで樹脂層13Aを形成する。基材11としては、長尺のものを使用することが好ましい。さらに、剥離剤層12Aを構成する材料および所望により有機溶剤を含有する塗工液を、基材11における樹脂層13Aを形成した面に塗工する。このとき、当該塗工液は、樹脂層13A上にも塗工する。当該塗工液を乾燥および硬化させることで剥離剤層12Aを形成する。以上によって、剥離フィルム1Aが得られる。
本実施形態に係る剥離フィルムは、図1に示される剥離フィルム1Aに限定されず、例えば、図2に示すような第2の実施形態に係るセラミックグリーンシート製造工程用剥離フィルム1B(以下単に「剥離フィルム1B」という場合がある。)であってもよい。剥離フィルム1Bは、基材11と、基材11の一方の面(図2では上面)に積層された剥離剤層12Bと、剥離剤層12Bにおける基材11とは反対側の面であって剥離剤層12Bの幅方向両側部(図2では横方向両端部)に1つずつ設けられた樹脂層13Bとを備えて構成される。剥離フィルム1Bでは、セラミックグリーンシート成形部15の位置の層構成は、基材11および剥離剤層12Bからなり、凸部14の位置の層構成は、基材11、樹脂層13Bおよび剥離剤層12Bの順の構成からなる。
本実施形態に係る剥離フィルム1A,1B,1Cは、セラミックグリーンシートを製造するために使用することができる。具体的には、セラミックグリーンシート成形部15に対し、チタン酸バリウムや酸化チタンなどのセラミック材料を含有するセラミックスラリーを塗工した後、当該セラミックスラリーを乾燥させることでセラミックグリーンシートを得ることができる。塗工は、例えば、スロットダイ塗工方式やドクターブレード方式等を用いて行うことができる。セラミックスラリーにはバインダー成分を含有させることができ、その例としては、ブチラール系樹脂、アクリル系樹脂等が挙げられる。また、セラミックスラリーを調製するための溶媒の例としては、有機溶媒、水系溶媒等が挙げられる。
活性エネルギー線硬化性化合物としてのジペンタエリスリトールヘキサアクリレート(固形分100質量%)95質量部と、α−アミノアルキルフェノン系光重合開始剤(BASF社製,商品名:IRGACURE907,2-メチル−1[4−(メチルチオ)フェニル]−2−モリフォリノプロパン−1−オン,固形分100質量%)5質量部とを、イソプロピルアルコールとメチルエチルケトンとを質量比3:1で混合した溶剤にて混合して、固形分20質量%の樹脂層形成用塗布液を得た。
樹脂層形成用塗布液および剥離剤層形成用塗布液に含まれる活性エネルギー線硬化性化合物を、ペンタエリスリトールテトラアクリレート(新中村化学工業社製,商品名:A-TMMT,固形分100質量%)に変更した以外は、実施例1と同様にして剥離フィルムを得た。
基材を、二軸延伸ポリエチレンテレフタレートフィルム(幅:320mm,長さ:3000m,厚さ:31μm,第1面の算術平均粗さRa:18nm,第1面の最大突起高さRp:202nm,第2面の算術平均粗さRa:3nm,第2面の最大突起高さRp:29nm)に変更した以外は、実施例1と同様にして剥離フィルムを得た。
基材を、二軸延伸ポリエチレンテレフタレートフィルム(幅:320mm,長さ:3000m,厚さ:50μm,第1面の算術平均粗さRa:4nm,第1面の最大突起高さRp:40nm,第2面の算術平均粗さRa:3nm,第2面の最大突起高さRp:23nm)に変更した以外は、実施例1と同様にして剥離フィルムを得た。
樹脂層を設けないこと以外は、実施例1と同様にして剥離フィルムを得た。
基材を、二軸延伸ポリエチレンテレフタレートフィルム(幅:320mm,長さ:3000m,厚さ:31μm,第1面の算術平均粗さRa:21nm,第1面の最大突起高さRp:509nm,第2面の算術平均粗さRa:21nm,第2面の最大突起高さRp:509nm)に変更した以外は、実施例1と同様にして剥離フィルムを得た。
基材を、二軸延伸ポリエチレンテレフタレートフィルム(幅:320mm,長さ:3000m,厚さ:31μm、第1面の算術平均粗さRa:18nm,第1面の最大突起高さRp:264nm,第2面の算術平均粗さRa:18nm,第2面の最大突起高さRp:264nm)に変更した以外は、実施例1と同様にして剥離フィルムを得た。
ガラス板に両面テープを貼付し、実施例および比較例で得られた剥離フィルムを、測定する側の面の反対面がガラス板側となるように上記両面テープを介してガラス板に固定した。その剥離フィルムの剥離面および裏面について、算術平均粗さ(Ra;nm)および最大突起高さ(Rp;nm)を、光干渉式表面形状観察装置(ブルカー・エイエックスエス社製,製品名:WYKO−1100)を使用し、PSIモードにて50倍率で観察し、得られた91.2×119.8μmの範囲における表面形状画像に基づいて測定した。結果を表1に示す。
実施例および比較例で得られた剥離フィルムをロール状にする際のハンドリング性について評価した。具体的には、ロール状にする際の空気抜けの良さ、および剥離フィルムの巻きズレの生じ難さについて、以下の判断基準により評価した。結果を表1に示す。
A…剥離フィルムをロール状にするときの空気抜けが良く、剥離フィルムの巻きズレおよびシワを防止できた
B…剥離フィルムをロール状に巻いたときの空気の抜けが若干悪く、巻きズレが若干生じるものシワは発生せず支障はなかった
C…剥離フィルムをロール状に巻いたときの空気の抜けが悪く、巻きズレおよびシワが顕著に生じた
実施例及び比較例で得られた剥離フィルム(幅320mm,長さ3000m)をロール状に巻き上げた。この剥離フィルムロールを40℃、湿度50%以下の環境下に30日間保管し、剥離フィルムロールそのままの状態での外観を目視にて観察し、以下の判断基準によりブロッキング性を評価した。結果を表1に示す。
A…ロール状に巻き上げたときから変化がなかった(ブロッキング無し)
B…部分的にフィルム同士の密着に起因する色目の変化が見られた(ブロッキング傾向にあるものの使用可能)
C…広範な領域にわたってフィルム同士の密着に起因する色目の変化が見られた(ブロッキング有り)
なお、上記評価Cのように表裏の密着によるブロッキングが発生してロールの広範な領域にわたって色目が変化した場合、正常に巻き出すことができない場合がある。
トルエンおよびエタノールの混合溶剤(質量比60:40)にて、ポリビニルブチラール樹脂(積水化学社製,製品名:エスレックB・K BL−S,粉末状)を固形分濃度20質量%に溶解し、ポリビニルブチラール樹脂溶液を得た。得られたポリビニルブチラール樹脂溶液を、実施例および比較例で得られた剥離フィルムの剥離面にオフロール方式のダイコーターにて塗布した。このとき、凸部との間隔を1.5mmあけて塗布した。その後、塗布した樹脂溶液を80℃で1分間乾燥させて厚さ3μmのポリビニルブチラール樹脂層を成形した。そして、そのポリビニルブチラール樹脂層の表面にポリエステル粘着テープを貼付した。
A…凹みの数が0個
B…凹みの数が1〜5個
C…凹みの数が6個以上
なお、上記評価Cの凹みが存在するセラミックグリーンシートでコンデンサを製造した場合、得られるコンデンサは、耐電圧低下によるショートが発生し易いものとなる。
トルエン及びエタノールの混合溶剤(質量比60:40)にて、ポリビニルブチラール樹脂(積水化学社製,製品名:エスレックB・K BL−S,粉末状)を固形分濃度20質量%に溶解し、ポリビニルブチラール樹脂溶液を得た。得られたポリビニルブチラール樹脂溶液を、実施例および比較例で得られた剥離フィルムの長さ1000mの範囲において、オフロール方式のダイコーターを用いて剥離面に塗布し、80℃で1分間乾燥させて厚さ2μmのポリビニルブチラール樹脂層を成形した。成形後、剥離フィルムをポリビニルブチラール樹脂層とともに巻き上げた。
A…凹みの数および損傷部の数の合計が0個
B…凹みの数および損傷部の数の合計が1〜3個
C…凹みの数および損傷部の数の合計が4個以上
なお、上記評価Cの凹みが存在するセラミックグリーンシートでコンデンサを製造した場合、得られるコンデンサは、耐電圧低下によるショートが発生し易いものとなる。
11…基材
12A,12B…剥離剤層
13A,13B…樹脂層
14…凸部
15…セラミックグリーンシート成形部
2…セラミックグリーンシート
G…間隙
Claims (5)
- 長尺の基材と、前記基材の片面側に設けられた剥離剤層とを備えたセラミックグリーンシート製造工程用剥離フィルムであって、
前記剥離フィルムが、平面視において、幅方向中央部の領域にセラミックグリーンシート成形部を有し、且つ、幅方向両側部の領域に凸部を1つずつ有し、
前記剥離フィルムが、前記基材と前記剥離剤層との間であって前記基材の幅方向両側部に1つずつ設けられた樹脂層を備え、もって、前記凸部の位置に、前記樹脂層と前記剥離剤層とを含み、
前記凸部の高さが、前記セラミックグリーンシート成形部に位置する前記剥離剤層の前記基材とは反対側の面の高さを基準として0.1〜3μmであり、
前記セラミックグリーンシート成形部に位置する前記剥離剤層の前記基材とは反対側の面の算術平均粗さRaおよび最大突起高さRpが、それぞれ8nm未満および50nm未満であり、
前記基材における前記剥離剤層とは反対側の面の算術平均粗さRaおよび最大突起高さRpが、それぞれ10nm未満および100nm未満である
ことを特徴とするセラミックグリーンシート製造工程用剥離フィルム。 - 前記凸部の幅方向の長さは、5〜50mmであることを特徴とする請求項1に記載のセラミックグリーンシート製造工程用剥離フィルム。
- 前記セラミックグリーンシート成形部の幅方向の長さは、100〜500mmであることを特徴とする請求項1または2に記載のセラミックグリーンシート製造工程用剥離フィルム。
- 請求項1〜3の何れか一項に記載のセラミックグリーンシート製造工程用剥離フィルムの前記セラミックグリーンシート成形部にセラミックスラリーを塗工し、乾燥させる工程を含むことを特徴とするセラミックグリーンシート製造方法。
- 前記凸部の高さの値以下の厚さを有するセラミックグリーンシートを形成することを特徴とする請求項4に記載のセラミックグリーンシート製造方法。