JP6461453B2 - Red colored curable resin composition - Google Patents

Red colored curable resin composition Download PDF

Info

Publication number
JP6461453B2
JP6461453B2 JP2012266916A JP2012266916A JP6461453B2 JP 6461453 B2 JP6461453 B2 JP 6461453B2 JP 2012266916 A JP2012266916 A JP 2012266916A JP 2012266916 A JP2012266916 A JP 2012266916A JP 6461453 B2 JP6461453 B2 JP 6461453B2
Authority
JP
Japan
Prior art keywords
group
hydrocarbon group
pigment
carbon atoms
meth
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2012266916A
Other languages
Japanese (ja)
Other versions
JP2013140348A (en
Inventor
昭妍 朴
昭妍 朴
鈴木　智也
智也 鈴木
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dongwoo Fine Chem Co Ltd
Original Assignee
Dongwoo Fine Chem Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dongwoo Fine Chem Co Ltd filed Critical Dongwoo Fine Chem Co Ltd
Priority to JP2012266916A priority Critical patent/JP6461453B2/en
Publication of JP2013140348A publication Critical patent/JP2013140348A/en
Application granted granted Critical
Publication of JP6461453B2 publication Critical patent/JP6461453B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Description

本発明は、赤色着色硬化性樹脂組成物に関する。   The present invention relates to a red colored curable resin composition.

着色硬化性樹脂組成物は、液晶表示パネル、エレクトロルミネッセンスパネル、プラズマディスプレイパネルなどのディスプレイ装置に使用されるカラーフィルタの製造用に用いられている。この着色硬化性樹脂組成物には、着色剤として、顔料又は染料を用いることが知られている（非特許文献１）。   Colored curable resin compositions are used for the production of color filters used in display devices such as liquid crystal display panels, electroluminescence panels, and plasma display panels. In this colored curable resin composition, it is known to use a pigment or a dye as a colorant (Non-Patent Document 1).

鈴木八十二著、「よくわかる液晶ディスプレイのできるまで」、初版、日刊工業新聞社、２００５年３月、１１２頁Hachiji Suzuki, “Until the creation of a well-known liquid crystal display”, first edition, Nikkan Kogyo Shimbun, March 2005, p. 112

赤色着色硬化性樹脂組成物には、高明度な赤色カラーフィルタを製造しうることが求められている。   The red colored curable resin composition is required to produce a high-brightness red color filter.

本発明は、以下の発明を含む。
［１］ 着色剤、樹脂、重合性化合物及び重合開始剤を含み、
着色剤が、式（１ａ）で表される化合物と、黄色顔料、オレンジ色顔料及び赤色顔料からなる群から選ばれる少なくとも１種の顔料とを含む着色剤である赤色着色硬化性樹脂組成物。

Figure 0006461453
［式（１ａ）中、Ｒ1〜Ｒ4は、互いに独立に、水素原子、炭素数１〜２０の１価の飽和炭化水素基又は置換基を有していてもよい炭素数６〜１０の１価の芳香族炭化水素基を表し、該飽和炭化水素基に含まれる水素原子は、炭素数６〜１０の芳香族炭化水素基又はハロゲン原子で置換されていてもよく、該芳香族炭化水素基に含まれる水素原子は、炭素数１〜３のアルコキシ基で置換されていてもよく、前記飽和炭化水素基に含まれる−ＣＨ2−は、−Ｏ−、−ＣＯ−又は−ＮＲ11−で置き換わっていてもよい。Ｒ1及びＲ2は互いに結合して、それらが結合する窒素原子と一緒になって窒素原子を含む環を形成してもよく、Ｒ3及びＲ4は互いに結合して、それらが結合する窒素原子と一緒になって窒素原子を含む環を形成してもよい。
Ｒ5は、−ＯＨ、−ＳＯ3 -、−ＳＯ3Ｈ、−ＳＯ3 -Ｚ+、−ＣＯ2Ｈ、−ＣＯ2 -Ｚ+、−ＣＯ2Ｒ8、又は−ＳＯ3Ｒ 8 を表す。
Ｒ6及びＲ7は、それぞれ独立に、水素原子又は炭素数１〜６のアルキル基を表す。
ｍは、０〜５の整数を表す。ｍが２以上のとき、複数のＲ5は同一でも異なってもよい。
ａは、０又は１の整数を表す。
Ｘは、ハロゲン原子を表す。
Ｚ+は、+Ｎ（Ｒ11）4、Ｎａ+又はＫ+を表す。
Ｒ8は、炭素数１〜２０の１価の飽和炭化水素基を表し、該飽和炭化水素基に含まれる水素原子は、ハロゲン原子で置換されていてもよい。
Ｒ9及びＲ10は、互いに独立に、水素原子又は置換基を有していてもよい炭素数１〜２０の１価の飽和炭化水素基を表し、該飽和脂肪族炭化水素基に含まれる−ＣＨ2−は、−Ｏ−、−ＣＯ−、−ＮＨ−又は−ＮＲ8−で置き換っていてもよく、Ｒ9及びＲ10は互いに結合して、それらが結合する窒素原子と一緒になって３〜１０員窒素含有複素環を形成していてもよい。
Ｒ11は、互いに独立に、水素原子、炭素数１〜２０の１価の飽和炭化水素基又は炭素数７〜１０のアラルキル基を表す。］
［２］ 顔料が、Ｃ．Ｉ．ピグメントイエロー１３８、Ｃ．Ｉ．ピグメントイエロー１３９、Ｃ．Ｉ．ピグメントイエロー１５０、Ｃ．Ｉ．ピグメントレッド１７７、Ｃ．Ｉ．ピグメントレッド２４２及びＣ．Ｉ．ピグメントレッド２５４からなる群から選ばれる少なくとも１種である［１］記載の赤色着色硬化性樹脂組成物。
［３］ ［１］又は［２］記載の赤色着色硬化性樹脂組成物により形成される赤色カラーフィルタ。
［４］ ［３］記載の赤色カラーフィルタを含む表示装置。 The present invention includes the following inventions.
[1] including a colorant, a resin, a polymerizable compound, and a polymerization initiator,
A red colored curable resin composition, wherein the colorant comprises a compound represented by the formula (1a) and at least one pigment selected from the group consisting of a yellow pigment, an orange pigment, and a red pigment.
Figure 0006461453
[In Formula (1a), R 1 to R 4 are each independently a hydrogen atom, a monovalent saturated hydrocarbon group having 1 to 20 carbon atoms, or a substituent having 6 to 10 carbon atoms. Represents a monovalent aromatic hydrocarbon group, and the hydrogen atom contained in the saturated hydrocarbon group may be substituted with an aromatic hydrocarbon group having 6 to 10 carbon atoms or a halogen atom, and the aromatic hydrocarbon The hydrogen atom contained in the group may be substituted with an alkoxy group having 1 to 3 carbon atoms, and —CH 2 — contained in the saturated hydrocarbon group is —O—, —CO— or —NR 11 —. It may be replaced with. R 1 and R 2 may be bonded to each other to form a ring containing a nitrogen atom together with the nitrogen atom to which they are bonded, and R 3 and R 4 are bonded to each other to form a nitrogen to which they are bonded. A ring containing a nitrogen atom may be formed together with the atom.
R 5 is, -OH, -SO 3 - represents a Z +, -CO 2 R 8, or -SO 3 R 8 -, -SO 3 H, -SO 3 - Z +, -CO 2 H, -CO 2 .
R 6 and R 7 each independently represents a hydrogen atom or an alkyl group having 1 to 6 carbon atoms.
m represents an integer of 0 to 5. When m is 2 or more, the plurality of R 5 may be the same or different.
a represents an integer of 0 or 1.
X represents a halogen atom.
Z + represents + N (R 11 ) 4 , Na + or K + .
R 8 represents a monovalent saturated hydrocarbon group having 1 to 20 carbon atoms, and the hydrogen atom contained in the saturated hydrocarbon group may be substituted with a halogen atom.
R 9 and R 10 each independently represent a hydrogen atom or a monovalent saturated hydrocarbon group having 1 to 20 carbon atoms which may have a substituent, and is contained in the saturated aliphatic hydrocarbon group − CH 2 — may be replaced by —O—, —CO—, —NH— or —NR 8 —, and R 9 and R 10 are bonded to each other together with the nitrogen atom to which they are bonded. And may form a 3 to 10-membered nitrogen-containing heterocycle.
R 11 independently represents a hydrogen atom, a monovalent saturated hydrocarbon group having 1 to 20 carbon atoms, or an aralkyl group having 7 to 10 carbon atoms. ]
[2] The pigment is C.I. I. Pigment yellow 138, C.I. I. Pigment yellow 139, C.I. I. Pigment yellow 150, C.I. I. Pigment red 177, C.I. I. Pigment red 242 and C.I. I. The red colored curable resin composition according to [1], which is at least one selected from the group consisting of CI Pigment Red 254.
[3] A red color filter formed by the red colored curable resin composition according to [1] or [2].
[4] A display device including the red color filter according to [3].

本発明の赤色着色硬化性樹脂組成物によれば、高明度な赤色カラーフィルタを製造することができる。   According to the red colored curable resin composition of the present invention, a high brightness red color filter can be produced.

本発明の赤色着色硬化性樹脂組成物は、着色剤（Ａ）、樹脂（Ｂ）、重合性化合物（Ｃ）及び重合開始剤（Ｄ）を含む。
着色剤（Ａ）は、式（１ａ）で表される化合物（以下「化合物（１ａ）」）と顔料（Ａ２）とを含む。さらに、着色剤（Ａ）は、染料（ただし、化合物（１ａ）とは異なる）（以下「染料（Ａ３）」という場合がある）を含んでもよい。
本発明の赤色着色硬化性樹脂組成物は、さらに、溶剤（Ｅ）を含むことが好ましい。
また、本発明の赤色着色硬化性樹脂組成物は、必要に応じて、重合開始助剤（Ｄ１）及び界面活性剤（Ｆ）からなる群から選ばれる少なくとも１種を含んでもよい。
尚、本明細書において、各成分として例示する化合物は、特に断りのない限り、単独で又は複数種を組合せて使用することができる。 The red colored curable resin composition of the present invention includes a colorant (A), a resin (B), a polymerizable compound (C), and a polymerization initiator (D).
The colorant (A) includes a compound represented by the formula (1a) (hereinafter “compound (1a)”) and a pigment (A2). Furthermore, the colorant (A) may contain a dye (however, different from the compound (1a)) (hereinafter sometimes referred to as “dye (A3)”).
It is preferable that the red colored curable resin composition of the present invention further contains a solvent (E).
Moreover, the red coloring curable resin composition of this invention may contain at least 1 sort (s) chosen from the group which consists of a polymerization start adjuvant (D1) and surfactant (F) as needed.
In addition, in this specification, unless otherwise indicated, the compound illustrated as each component can be used individually or in combination of multiple types.

＜着色剤（Ａ）＞
化合物（１ａ）は、式（１ａ）で表される。

Figure 0006461453
［式（１ａ）中、Ｒ1〜Ｒ4は、互いに独立に、水素原子、炭素数１〜２０の１価の飽和炭化水素基又は置換基を有していてもよい炭素数６〜１０の１価の芳香族炭化水素基を表し、該飽和炭化水素基に含まれる水素原子は、炭素数６〜１０の芳香族炭化水素基又はハロゲン原子で置換されていてもよく、該芳香族炭化水素基に含まれる水素原子は、炭素数１〜３のアルコキシ基で置換されていてもよく、前記飽和炭化水素基に含まれる−ＣＨ２−は、−Ｏ−、−ＣＯ−又は−ＮＲ１１−で置き換わっていてもよい。Ｒ1及びＲ２は互いに結合して、それらが結合する窒素原子と一緒になって窒素原子を含む環を形成してもよく、Ｒ３及びＲ４は互いに結合して、それらが結合する窒素原子と一緒になって窒素原子を含む環を形成してもよい。
Ｒ5は、−ＯＨ、−ＳＯ3 -、−ＳＯ3Ｈ、−ＳＯ3 -Ｚ+、−ＣＯ2Ｈ、−ＣＯ2 -Ｚ+、−ＣＯ2Ｒ8、−ＳＯ3Ｒ8又は−ＳＯ2ＮＲ9Ｒ10を表す。
Ｒ6及びＲ7は、それぞれ独立に、水素原子又は炭素数１〜６のアルキル基を表す。
ｍは、０〜５の整数を表す。ｍが２以上のとき、複数のＲ5は同一でも異なってもよい。
ａは、０又は１の整数を表す。
Ｘは、ハロゲン原子を表す。
Ｚ+は、+Ｎ（Ｒ11）4、Ｎａ+又はＫ+を表す。
Ｒ8は、炭素数１〜２０の１価の飽和炭化水素基を表し、該飽和炭化水素基に含まれる水素原子は、ハロゲン原子で置換されていてもよい。
Ｒ9及びＲ10は、互いに独立に、水素原子又は置換基を有していてもよい炭素数１〜２０の１価の飽和炭化水素基を表し、該飽和脂肪族炭化水素基に含まれる−ＣＨ２−は、−Ｏ−、−ＣＯ−、−ＮＨ−又は−ＮＲ８−で置き換っていてもよく、Ｒ9及びＲ10は、互いに結合して、それらが結合する窒素原子と一緒になって３〜１０員窒素含有複素環を形成していてもよい。
Ｒ11は、互いに独立に、水素原子、炭素数１〜２０の１価の飽和炭化水素基又は炭素数７〜１０のアラルキル基を表す。］ <Colorant (A)>
Compound (1a) is represented by formula (1a).
Figure 0006461453
[In Formula (1a), R 1 to R 4 are each independently a hydrogen atom, a monovalent saturated hydrocarbon group having 1 to 20 carbon atoms, or a substituent having 6 to 10 carbon atoms. Represents a monovalent aromatic hydrocarbon group, and the hydrogen atom contained in the saturated hydrocarbon group may be substituted with an aromatic hydrocarbon group having 6 to 10 carbon atoms or a halogen atom, and the aromatic hydrocarbon The hydrogen atom contained in the group may be substituted with an alkoxy group having 1 to 3 carbon atoms, and —CH 2 — contained in the saturated hydrocarbon group is —O—, —CO— or —NR 11 —. It may be replaced with. R 1 and R 2 may be bonded to each other to form a ring containing a nitrogen atom together with the nitrogen atom to which they are bonded, and R 3 and R 4 are bonded to each other to form a nitrogen to which they are bonded. A ring containing a nitrogen atom may be formed together with the atom.
R 5 is, -OH, -SO 3 -, -SO 3 H, -SO 3 - Z +, -CO 2 H, -CO 2 - Z +, -CO 2 R 8, -SO 3 R 8 or -SO 2 represents NR 9 R 10
R 6 and R 7 each independently represents a hydrogen atom or an alkyl group having 1 to 6 carbon atoms.
m represents an integer of 0 to 5. When m is 2 or more, the plurality of R 5 may be the same or different.
a represents an integer of 0 or 1.
X represents a halogen atom.
Z + represents + N (R 11 ) 4 , Na + or K + .
R 8 represents a monovalent saturated hydrocarbon group having 1 to 20 carbon atoms, and the hydrogen atom contained in the saturated hydrocarbon group may be substituted with a halogen atom.
R 9 and R 10 each independently represent a hydrogen atom or a monovalent saturated hydrocarbon group having 1 to 20 carbon atoms which may have a substituent, and is contained in the saturated aliphatic hydrocarbon group − CH 2 — may be replaced by —O—, —CO—, —NH— or —NR 8 —, and R 9 and R 10 are bonded together and together with the nitrogen atom to which they are bonded. To form a 3- to 10-membered nitrogen-containing heterocycle.
R 11 independently represents a hydrogen atom, a monovalent saturated hydrocarbon group having 1 to 20 carbon atoms, or an aralkyl group having 7 to 10 carbon atoms. ]

Ｒ1〜Ｒ4における炭素数６〜１０の１価の芳香族炭化水素基としては、フェニル基、トルイル基、キシリル基、メシチル基、プロピルフェニル基及びブチルフェニル基が挙げられる。
該芳香族炭化水素基が有していてもよい置換基としては、ハロゲン原子、−Ｒ8、−ＯＨ、−ＯＲ8、−ＳＯ3 -、−ＳＯ3Ｈ、−ＳＯ3 -Ｚ+、−ＣＯ2Ｈ、−ＣＯ2Ｒ8、−ＳＲ8、−ＳＯ2Ｒ8、−ＳＯ3Ｒ8及び−ＳＯ2ＮＲ9Ｒ10が挙げられる。これらの中でも、置換基としては、−ＳＯ3 -、−ＳＯ3Ｈ、−ＳＯ3 -Ｚ+及び−ＳＯ2ＮＲ9Ｒ10が好ましく、−ＳＯ3 -Ｚ+及び−ＳＯ2ＮＲ9Ｒ10がより好ましい。この場合の−ＳＯ3 -Ｚ+としては、−ＳＯ3 - +Ｎ（Ｒ11）4が好ましい。Ｒ1〜Ｒ4がこれらの基であると、化合物（１ａ）を含む本発明の赤色着色硬化性樹脂組成物からは、異物の発生が少なく、且つ耐熱性に優れるカラーフィルタを形成できる。 Examples of the monovalent aromatic hydrocarbon group having 6 to 10 carbon atoms in R 1 to R 4 include a phenyl group, a toluyl group, a xylyl group, a mesityl group, a propylphenyl group, and a butylphenyl group.
The aromatic hydrocarbon group substituent which may have a halogen atom, -R 8, -OH, -OR 8 , -SO 3 -, -SO 3 H, -SO 3 - Z +, - CO 2 H, —CO 2 R 8 , —SR 8 , —SO 2 R 8 , —SO 3 R 8 and —SO 2 NR 9 R 10 may be mentioned. Among them, as the substituent, -SO 3 -, -SO 3 H , -SO 3 - Z + and preferably -SO 2 NR 9 R 10, -SO 3 - Z + and -SO 2 NR 9 R 10 Is more preferable. In this case, —SO 3 − + N (R 11 ) 4 is preferable as —SO 3 − Z + . When R 1 to R 4 are these groups, a color filter having less generation of foreign matters and excellent heat resistance can be formed from the red colored curable resin composition of the present invention containing the compound (1a).

Ｒ1及びＲ２が互いに結合して、それらが結合する窒素原子と一緒になって形成する環、並びにＲ３及びＲ４が互いに結合して、それらが結合する窒素原子と一緒になって形成する環としては、以下のものが挙げられる。

Figure 0006461453
R 1 and R 2 are bonded together to form a ring together with the nitrogen atom to which they are bonded, and R 3 and R 4 are bonded together to form together with the nitrogen atom to which they are bonded. Examples of the ring include the following.
Figure 0006461453

Ｒ8〜Ｒ11における炭素数１〜２０の１価の飽和炭化水素基としては、メチル基、エチル基、プロピル基、ブチル基、ペンチル基、ヘキシル基、ヘプチル基、オクチル基、ノニル基、デシル基、ドデシル基、ヘキサデシル基、イコシル基等の直鎖状アルキル基；イソプロピル基、イソブチル基、イソペンチル基、ネオペンチル基、２−エチルヘキシル基等の分岐鎖状アルキル基；シクロプロピル基、シクロペンチル基、シクロヘキシル基、シクロヘプチル基、シクロオクチル基、トリシクロデシル基等の炭素数３〜２０の脂環式飽和炭化水素基が挙げられる。 Examples of the monovalent saturated hydrocarbon group having 1 to 20 carbon atoms in R 8 to R 11 include methyl group, ethyl group, propyl group, butyl group, pentyl group, hexyl group, heptyl group, octyl group, nonyl group, decyl group. Group, dodecyl group, hexadecyl group, icosyl group and other linear alkyl groups; isopropyl group, isobutyl group, isopentyl group, neopentyl group, 2-ethylhexyl group and other branched chain alkyl groups; cyclopropyl group, cyclopentyl group, cyclohexyl Alicyclic saturated hydrocarbon groups having 3 to 20 carbon atoms such as a group, cycloheptyl group, cyclooctyl group, tricyclodecyl group and the like.

−ＯＲ8としては、メトキシ基、エトキシ基、プロポキシ基、ブトキシ基、ペンチルオキシ基、ヘキシルオキシ基、ヘプチルオキシ基、オクチルオキシ基、２−エチルヘキシルオキシ基及びイコシルオキシ基が挙げられる。 Examples of —OR 8 include methoxy group, ethoxy group, propoxy group, butoxy group, pentyloxy group, hexyloxy group, heptyloxy group, octyloxy group, 2-ethylhexyloxy group and icosyloxy group.

−ＣＯ2Ｒ8としては、メトキシカルボニル基、エトキシカルボニル基、プロポキシカルボニル基、ｔｅｒｔ−ブトキシカルボニル基、ヘキシルオキシカルボニル基及びイコシルオキシカルボニル基が挙げられる。 Examples of —CO 2 R 8 include a methoxycarbonyl group, an ethoxycarbonyl group, a propoxycarbonyl group, a tert-butoxycarbonyl group, a hexyloxycarbonyl group, and an icosyloxycarbonyl group.

−ＳＲ8としては、メチルスルファニル基、エチルスルファニル基、ブチルスルファニル基、ヘキシルスルファニル基、デシルスルファニル基及びイコシルスルファニル基が挙げられる。
−ＳＯ2Ｒ8としては、メチルスルホニル基、エチルスルホニル基、ブチルスルホニル基、ヘキシルスルホニル基、デシルスルホニル基及びイコシルスルホニル基が挙げられる。
−ＳＯ3Ｒ8としては、メトキシスルホニル基、エトキシスルホニル基、プロポキシスルホニル基、ｔｅｒｔ−ブトキシスルホニル基、ヘキシルオキシスルホニル基及びイコシルオキシスルホニル基が挙げられる。 Examples of —SR 8 include a methylsulfanyl group, an ethylsulfanyl group, a butylsulfanyl group, a hexylsulfanyl group, a decylsulfanyl group, and an icosylsulfanyl group.
Examples of —SO 2 R 8 include a methylsulfonyl group, an ethylsulfonyl group, a butylsulfonyl group, a hexylsulfonyl group, a decylsulfonyl group, and an icosylsulfonyl group.
Examples of —SO 3 R 8 include a methoxysulfonyl group, an ethoxysulfonyl group, a propoxysulfonyl group, a tert-butoxysulfonyl group, a hexyloxysulfonyl group, and an icosyloxysulfonyl group.

−ＳＯ2ＮＲ9Ｒ10としては、スルファモイル基；
Ｎ−メチルスルファモイル基、Ｎ−エチルスルファモイル基、Ｎ−プロピルスルファモイル基、Ｎ−イソプロピルスルファモイル基、Ｎ−ブチルスルファモイル基、Ｎ−イソブチルスルファモイル基、Ｎ−ｓｅｃ−ブチルスルファモイル基、Ｎ−ｔｅｒｔ−ブチルスルファモイル基、Ｎ−ペンチルスルファモイル基、Ｎ−（１−エチルプロピル）スルファモイル基、Ｎ−（１，１−ジメチルプロピル）スルファモイル基、Ｎ−（１，２−ジメチルプロピル）スルファモイル基、Ｎ−（２，２−ジメチルプロピル）スルファモイル基、Ｎ−（１−メチルブチル）スルファモイル基、Ｎ−（２−メチルブチル）スルファモイル基、Ｎ−（３−メチルブチル）スルファモイル基、Ｎ−シクロペンチルスルファモイル基、Ｎ−ヘキシルスルファモイル基、Ｎ−（１，３−ジメチルブチル）スルファモイル基、Ｎ−（３，３−ジメチルブチル）スルファモイル基、Ｎ−ヘプチルスルファモイル基、Ｎ−（１−メチルヘキシル）スルファモイル基、Ｎ−（１，４−ジメチルペンチル）スルファモイル基、Ｎ−オクチルスルファモイル基、Ｎ−（２−エチルヘキシル）スルファモイル基、Ｎ−（１，５−ジメチル）ヘキシルスルファモイル基、Ｎ−（１，１，２，２−テトラメチルブチル）スルファモイル基等のＮ−１置換スルファモイル基；
Ｎ，Ｎ−ジメチルスルファモイル基、Ｎ，Ｎ−エチルメチルスルファモイル基、Ｎ，Ｎ−ジエチルスルファモイル基、Ｎ，Ｎ−プロピルメチルスルファモイル基、Ｎ，Ｎ−イソプロピルメチルスルファモイル基、Ｎ，Ｎ−ｔｅｒｔ−ブチルメチルスルファモイル基、Ｎ，Ｎ−ブチルエチルスルファモイル基、Ｎ，Ｎ−ビス（１−メチルプロピル）スルファモイル基、Ｎ，Ｎ−ヘプチルメチルスルファモイル基等のＮ，Ｎ−２置換スルファモイル基が挙げられる。 —SO 2 NR 9 R 10 includes a sulfamoyl group;
N-methylsulfamoyl group, N-ethylsulfamoyl group, N-propylsulfamoyl group, N-isopropylsulfamoyl group, N-butylsulfamoyl group, N-isobutylsulfamoyl group, N- sec-butylsulfamoyl group, N-tert-butylsulfamoyl group, N-pentylsulfamoyl group, N- (1-ethylpropyl) sulfamoyl group, N- (1,1-dimethylpropyl) sulfamoyl group, N- (1,2-dimethylpropyl) sulfamoyl group, N- (2,2-dimethylpropyl) sulfamoyl group, N- (1-methylbutyl) sulfamoyl group, N- (2-methylbutyl) sulfamoyl group, N- (3 -Methylbutyl) sulfamoyl group, N-cyclopentylsulfamoyl group, N-hexylsulfamoyl N- (1,3-dimethylbutyl) sulfamoyl group, N- (3,3-dimethylbutyl) sulfamoyl group, N-heptylsulfamoyl group, N- (1-methylhexyl) sulfamoyl group, N- (1 , 4-Dimethylpentyl) sulfamoyl group, N-octylsulfamoyl group, N- (2-ethylhexyl) sulfamoyl group, N- (1,5-dimethyl) hexylsulfamoyl group, N- (1,1,2, , 2-tetramethylbutyl) sulfamoyl group and the like N-1 substituted sulfamoyl group;
N, N-dimethylsulfamoyl group, N, N-ethylmethylsulfamoyl group, N, N-diethylsulfamoyl group, N, N-propylmethylsulfamoyl group, N, N-isopropylmethylsulfa Moyl group, N, N-tert-butylmethylsulfamoyl group, N, N-butylethylsulfamoyl group, N, N-bis (1-methylpropyl) sulfamoyl group, N, N-heptylmethylsulfamoyl And N, N-2 substituted sulfamoyl groups such as a group.

Ｒ9及びＲ10における炭素数１〜２０の１価の飽和炭化水素基は、置換基を有していてもよい。該置換基としては、ヒドロキシ基及びハロゲン原子が挙げられる。 The monovalent saturated hydrocarbon group having 1 to 20 carbon atoms in R 9 and R 10 may have a substituent. Examples of the substituent include a hydroxy group and a halogen atom.

Ｒ9及びＲ10は、互いに結合して窒素原子と一緒になって３〜１０員窒素含有複素環（窒素原子を環内に１個以上含む複素環）を形成していてもよい。該複素環としては、例えば、以下のものが挙げられる。

Figure 0006461453
R 9 and R 10 may be bonded together to form a 3 to 10-membered nitrogen-containing heterocycle (a heterocycle containing one or more nitrogen atoms in the ring) together with the nitrogen atom. Examples of the heterocyclic ring include the following.
Figure 0006461453

Ｒ５としては、−ＣＯ２Ｈ、−ＣＯ2 -Ｚ+、−ＣＯ２Ｒ８、−ＳＯ３ −、−ＳＯ３ −Ｚ＋、−ＳＯ３Ｈ及び−ＳＯ２ＮＨＲ９が好ましく、−ＳＯ３ −、−ＳＯ３ −Ｚ＋、−ＳＯ３Ｈ及び−ＳＯ２ＮＨＲ９がより好ましい。
ｍとしては、１〜４の整数が好ましく、１及び２がより好ましい。 The R 5, -CO 2 H, -CO 2 - Z +, -CO 2 R 8, -SO 3 -, -SO 3 - Z +, -SO 3 H and -SO 2 NHR 9 are preferred, -SO 3 -, -SO 3 - Z + , -SO 3 H and -SO 2 NHR 9 is more preferable.
As m, the integer of 1-4 is preferable and 1 and 2 are more preferable.

Ｒ6及びＲ7における炭素数１〜６のアルキル基としては、上記で挙げたアルキル基のうち、炭素数１〜６のものが挙げられる。 The alkyl group having 1 to 6 carbon atoms in R 6 and R 7, among the alkyl groups listed above, include those having 1 to 6 carbon atoms.

Ｒ8及びＲ11における炭素数７〜１０のアラルキル基としては、ベンジル基、フェニルエチル基及びフェニルブチル基が挙げられる。 Examples of the aralkyl group having 7 to 10 carbon atoms in R 8 and R 11 include a benzyl group, a phenylethyl group, and a phenylbutyl group.

Ｚ+は、+Ｎ（Ｒ11）4、Ｎａ+又はＫ+であり、好ましくは+Ｎ（Ｒ11）4である。
前記+Ｎ（Ｒ11）4としては、４つのＲ11のうち、少なくとも２つが炭素数５〜２０の１価の飽和炭化水素基であることが好ましい。また、４つのＲ11の合計炭素数は２０〜８０であることが好ましく、２０〜６０であることがより好ましい。化合物（１ａ）中に＋Ｎ（Ｒ１１）４が存在する場合、Ｒ11がこれらの基であると、化合物（１ａ）を含む本発明の赤色着色硬化性樹脂組成物から、異物が少ないカラーフィルタを形成できる。 Z + is + N (R 11 ) 4 , Na + or K + , preferably + N (R 11 ) 4 .
As the + N (R 11 ) 4 , at least two of the four R 11 are preferably monovalent saturated hydrocarbon groups having 5 to 20 carbon atoms. It is preferable that the total number of carbon atoms of the four R 11 is 20 to 80, and more preferably from 20 to 60. When + N (R 11 ) 4 is present in the compound (1a), when R 11 is any of these groups, the color of the present invention containing the compound (1a) is reduced from the colored red curable resin composition of the present invention. A filter can be formed.

化合物（１ａ）としては、式（２ａ）で表される化合物（以下「化合物（２ａ）」という場合がある）がより好ましい。化合物（２ａ）は、その互変異性体であってもよい。   As the compound (1a), a compound represented by the formula (2a) (hereinafter sometimes referred to as “compound (2a)”) is more preferable. Compound (2a) may be a tautomer thereof.

Figure 0006461453
［式（２ａ）中、Ｒ21〜Ｒ24は、それぞれ独立に、水素原子、−Ｒ26又は置換基を有していてもよい炭素数６〜１０の１価の芳香族炭化水素基を表す。Ｒ21及びＲ22は互いに結合して、それらが結合する窒素原子と一緒になって窒素原子を含む環を形成してもよく、Ｒ23及びＲ24は互いに結合して、それらが結合する窒素原子と一緒になって窒素原子を含む環を形成してもよい。
Ｒ25は、−ＳＯ3 -、−ＳＯ3Ｈ、−ＳＯ3 -Ｚ１+又は−ＳＯ2ＮＨＲ26を表す。
ｍ１は、０〜５の整数を表す。ｍ１が２以上のとき、複数のＲ25は同一でも異なってもよい。
ａ１は、０又は１の整数を表す。
Ｘ１は、ハロゲン原子を表す。
Ｒ26は、炭素数１〜２０の１価の飽和炭化水素基を表す。
Ｚ１+は、+Ｎ（Ｒ27）4、Ｎａ+又はＫ+を表す。
Ｒ27は、それぞれ独立に、炭素数１〜２０の１価の飽和炭化水素基又はベンジル基を表す。］
Figure 0006461453
[In Formula (2a), R 21 to R 24 each independently represents a hydrogen atom, —R 26 or a monovalent aromatic hydrocarbon group having 6 to 10 carbon atoms which may have a substituent. . R 21 and R 22 may be bonded together to form a ring containing a nitrogen atom together with the nitrogen atom to which they are bonded, and R 23 and R 24 are bonded to each other to form a nitrogen to which they are bonded. A ring containing a nitrogen atom may be formed together with the atom.
R 25 is, -SO 3 - represents a Z1 + or -SO 2 NHR 26 -, -SO 3 H, -SO 3.
m1 represents the integer of 0-5. When m1 is 2 or more, the plurality of R 25 may be the same or different.
a1 represents an integer of 0 or 1.
X1 represents a halogen atom.
R 26 represents a monovalent saturated hydrocarbon group having 1 to 20 carbon atoms.
Z1 + represents + N (R 27 ) 4 , Na + or K + .
R 27 each independently represents a monovalent saturated hydrocarbon group having 1 to 20 carbon atoms or a benzyl group. ]

Ｒ21〜Ｒ24における炭素数６〜１０の１価の芳香族炭化水素基としては、前記Ｒ1〜Ｒ4で芳香族炭化水素基として挙げたものと同様の基が挙げられる。該芳香族炭化水素基に含まれる水素原子は、−ＳＯ3 -、−ＳＯ3Ｈ、−ＳＯ3 -Ｚ１+、−ＳＯ3Ｒ26又は−ＳＯ2ＮＨＲ26で置換されていてもよい。
Ｒ21〜Ｒ24の組合せとしては、Ｒ21及びＲ23が水素原子であり、Ｒ22及びＲ24が炭素数６〜１０の１価の芳香族炭化水素基であって、該芳香族炭化水素基に含まれる水素原子が、−ＳＯ3 -、−ＳＯ3Ｈ、−ＳＯ3 -Ｚ１+、−ＳＯ3Ｒ26又は−ＳＯ2ＮＨＲ26で置換されているものが好ましい。さらに好ましい組合せは、Ｒ21及びＲ23が水素原子であり、Ｒ22及びＲ24が炭素数６〜１０の１価の芳香族炭化水素基であって、該芳香族炭化水素基に含まれる水素原子が、−ＳＯ3 -Ｚ１+又は−ＳＯ2ＮＨＲ26で置換されていているものである。
Ｒ21〜Ｒ24がこれらの基であると、化合物（２ａ）を含む本発明の赤色着色硬化性樹脂組成物から、耐熱性に優れるカラーフィルタを形成できる。 Examples of the monovalent aromatic hydrocarbon group having 6 to 10 carbon atoms in R 21 to R 24 include the same groups as those exemplified as the aromatic hydrocarbon group in R 1 to R 4 . Hydrogen atoms contained in the aromatic hydrocarbon group, -SO 3 -, -SO 3 H , -SO 3 - Z1 +, may be substituted by -SO 3 R 26 or -SO 2 NHR 26.
As a combination of R 21 to R 24 , R 21 and R 23 are hydrogen atoms, R 22 and R 24 are monovalent aromatic hydrocarbon groups having 6 to 10 carbon atoms, and the aromatic hydrocarbons hydrogen atoms contained in the groups, -SO 3 -, -SO 3 H , -SO 3 - Z1 +, those substituted by -SO 3 R 26 or -SO 2 NHR 26 preferred. A more preferred combination is that R 21 and R 23 are hydrogen atoms, R 22 and R 24 are monovalent aromatic hydrocarbon groups having 6 to 10 carbon atoms, and hydrogen contained in the aromatic hydrocarbon group atom, -SO 3 - in which are substituted with Z1 + or -SO 2 NHR 26.
When R 21 to R 24 are these groups, a color filter having excellent heat resistance can be formed from the red colored curable resin composition of the present invention containing the compound (2a).

Ｒ21及びＲ22が互いに結合して、それらが結合する窒素原子と一緒になって形成する窒素原子を含む環、並びに、Ｒ23及びＲ24が互いに結合して、それらが結合する窒素原子と一緒になって形成する窒素原子を含む環としては、Ｒ1及びＲ２が互いに結合して、それらが結合する窒素原子と一緒になって形成する環と同様のものが挙げられる。中でも、脂肪族複素環が好ましい。該脂肪族複素環としては、例えば、下記のものが挙げられる。

Figure 0006461453
A ring containing a nitrogen atom formed by combining R 21 and R 22 together with the nitrogen atom to which they are bonded; and a nitrogen atom to which R 23 and R 24 are bonded together and to which they are bonded; Examples of the ring containing a nitrogen atom formed together include those similar to the ring formed by combining R 1 and R 2 together with the nitrogen atom to which they are bonded. Among these, an aliphatic heterocyclic ring is preferable. Examples of the aliphatic heterocycle include the following.
Figure 0006461453

Ｒ26及びＲ27における炭素数１〜２０の１価の飽和炭化水素基としては、Ｒ8〜Ｒ11で飽和炭化水素基として挙げたものと同様の基が挙げられる。
Ｒ21〜Ｒ24が−Ｒ２６である場合、−Ｒ26は、それぞれ独立に、メチル基又はエチル基であることが好ましい。また、−ＳＯ3Ｒ26及び−ＳＯ2ＮＨＲ26におけるＲ26としては、炭素数３〜２０の分枝鎖状アルキル基が好ましく、炭素数６〜１２の分枝鎖状アルキル基がより好ましく、２−エチルヘキシル基がさらに好ましい。Ｒ26がこれらの基であると、化合物（２ａ）を含む本発明の赤色着色硬化性樹脂組成物から、異物の発生が少ないカラーフィルタを形成できる。 Examples of the monovalent saturated hydrocarbon group having 1 to 20 carbon atoms in R 26 and R 27 include the same groups as those exemplified as the saturated hydrocarbon group in R 8 to R 11 .
When R 21 to R 24 is -R 26, -R 26 each independently is preferably a methyl group or an ethyl group. As the R 26 in -SO 3 R 26 and -SO 2 NHR 26, preferably branched alkyl group having 3 to 20 carbon atoms, more preferably a branched alkyl group having 6 to 12 carbon atoms, A 2-ethylhexyl group is more preferred. When R 26 is any of these groups, a color filter with less foreign matter can be formed from the red colored curable resin composition of the present invention containing the compound (2a).

Ｚ１+は、+Ｎ（Ｒ27）4、Ｎａ+又はＫ+であり、好ましくは+Ｎ（Ｒ27）4である。
前記+Ｎ（Ｒ27）4としては、４つのＲ27のうち、少なくとも２つが炭素数５〜２０の１価の飽和炭化水素基であることが好ましい。また、４つのＲ27の合計炭素数は２０〜８０であることが好ましく、２０〜６０であることがより好ましい。化合物（２ａ）中に＋Ｎ（Ｒ２７）４が存在する場合、Ｒ27がこれらの基である化合物（２ａ）を含む赤色着色硬化性樹脂組成物は、異物の発生が少ないカラーフィルタを形成できる。 Z1 + is + N (R 27 ) 4 , Na + or K + , preferably + N (R 27 ) 4 .
As the + N (R 27 ) 4 , at least two of the four R 27 are preferably monovalent saturated hydrocarbon groups having 5 to 20 carbon atoms. It is preferable that the total number of carbon atoms of the four R 27 is 20 to 80, and more preferably from 20 to 60. When + N (R 27 ) 4 is present in the compound (2a), the red colored curable resin composition containing the compound (2a) in which R 27 is any of these groups forms a color filter with less generation of foreign matters. it can.

ｍ１としては、１〜４の整数が好ましく、１及び２がより好ましい。   As m1, the integer of 1-4 is preferable and 1 and 2 are more preferable.

化合物（１ａ）としては、式（３ａ）で表される化合物（以下「化合物（３ａ）」という場合がある。）がより好ましい。化合物（３ａ）は、その互変異性体であってもよい。   As the compound (1a), a compound represented by the formula (3a) (hereinafter sometimes referred to as “compound (3a)”) is more preferable. Compound (3a) may be a tautomer thereof.

Figure 0006461453
［式（３ａ）中、Ｒ31及びＲ32は、互いに独立に、炭素数１〜１０の１価の飽和炭化水素基を表し、該飽和炭化水素基に含まれる水素原子は、炭素数６〜１０の芳香族炭化水素基又はハロゲン原子で置換されていてもよく、該芳香族炭化水素基に含まれる水素原子は、炭素数１〜３のアルコキシ基で置換されていてもよく、前記飽和炭化水素基に含まれる−ＣＨ２−は、−Ｏ−、−ＣＯ−又は−ＮＲ１１−で置き換わっていてもよい。
Ｒ33及びＲ34は、互いに独立に、炭素数１〜４のアルキル基、炭素数１〜４のアルキルスルファニル基又は炭素数１〜４のアルキルスルホニル基を表す。
Ｒ31及びＲ33は互いに結合して、窒素原子と一緒になって窒素原子を含む環を形成してもよく、Ｒ32及びＲ34は互いに結合して、窒素原子と一緒になって窒素原子を含む環を形成してもよい。
ｐ及びｑは、互いに独立に、０〜５の整数を表す。ｐが２以上のとき、複数のＲ33は同一でも異なってもよく、ｑが２以上のとき、複数のＲ34は同一でも異なってもよい。
Ｒ１１は、上記と同じ意味を表す。］
Figure 0006461453
[In the formula (3a), R 31 and R 32 independently represent a monovalent saturated hydrocarbon group having 1 to 10 carbon atoms, and the hydrogen atom contained in the saturated hydrocarbon group has 6 to 6 carbon atoms. May be substituted with 10 aromatic hydrocarbon groups or a halogen atom, and the hydrogen atom contained in the aromatic hydrocarbon group may be substituted with an alkoxy group having 1 to 3 carbon atoms, —CH 2 — contained in the hydrogen group may be replaced by —O—, —CO— or —NR 11 —.
R <33> and R <34 > represent a C1-C4 alkyl group, a C1-C4 alkylsulfanyl group, or a C1-C4 alkylsulfonyl group mutually independently.
R 31 and R 33 may be bonded together to form a ring containing a nitrogen atom together with the nitrogen atom, and R 32 and R 34 may be bonded together to form a nitrogen atom together with the nitrogen atom. A ring containing may be formed.
p and q represent the integer of 0-5 mutually independently. When p is 2 or more, the plurality of R 33 may be the same or different, and when q is 2 or more, the plurality of R 34 may be the same or different.
R 11 represents the same meaning as described above. ]

Ｒ31及びＲ32における炭素数１〜１０の１価の飽和炭化水素基としては、Ｒ8におけるもののうち炭素数１〜１０の基が挙げられる。
置換基として有していてもよい炭素数６〜１０の芳香族炭化水素基としては、Ｒ１におけるものと同じ基が挙げられる。
炭素数１〜３のアルコキシ基としては、メトキシ基、エトキシ基及びプロポキシ基が挙げられる。
Ｒ31及びＲ32は、互いに独立に、炭素数１〜３の１価の飽和炭化水素基であることが好ましい。 Examples of the monovalent saturated hydrocarbon group having 1 to 10 carbon atoms in R 31 and R 32 include those having 1 to 10 carbon atoms among those in R 8 .
Examples of the aromatic hydrocarbon group having 6 to 10 carbon atoms which may be present as a substituent include the same groups as those in R 1 .
Examples of the alkoxy group having 1 to 3 carbon atoms include a methoxy group, an ethoxy group, and a propoxy group.
R 31 and R 32 are preferably each independently a monovalent saturated hydrocarbon group having 1 to 3 carbon atoms.

Ｒ33及びＲ34における炭素数１〜４のアルキル基としては、メチル基、エチル基、プロピル基、ブチル基、イソプロピル基、イソブチル基、ｓｅｃ−ブチル基及びｔｅｒｔ−ブチル基が挙げられる。
Ｒ33及びＲ34における炭素数１〜４のアルキルスルファニル基としては、メチルスルファニル基、エチルスルファニル基、プロピルスルファニル基、ブチルスルファニル基及びイソプロピルスルファニル基が挙げられる。
Ｒ33及びＲ34における炭素数１〜４のアルキルスルホニル基としては、メチルスルホニル基、エチルスルホニル基、プロピルスルホニル基、ブチルスルホニル基及びイソプロピルスルホニル基が挙げられる。
Ｒ33及びＲ34は、炭素数１〜４のアルキル基であることが好ましく、メチル基であることがより好ましい。 Examples of the alkyl group having 1 to 4 carbon atoms in R 33 and R 34 include a methyl group, an ethyl group, a propyl group, a butyl group, an isopropyl group, an isobutyl group, a sec-butyl group, and a tert-butyl group.
Examples of the alkylsulfanyl group having 1 to 4 carbon atoms in R 33 and R 34 include a methylsulfanyl group, an ethylsulfanyl group, a propylsulfanyl group, a butylsulfanyl group, and an isopropylsulfanyl group.
The alkylsulfonyl group of 1 to 4 carbon atoms in R 33 and R 34, methylsulfonyl group, ethylsulfonyl group, propylsulfonyl group and a butylsulfonyl group and isopropylsulfonyl group.
R 33 and R 34 are preferably an alkyl group having 1 to 4 carbon atoms, and more preferably a methyl group.

ｐ及びｑとしては、０〜２の整数が好ましく、０及び１がより好ましい。   As p and q, the integer of 0-2 is preferable and 0 and 1 are more preferable.

化合物（１ａ）としては、例えば、式（１−１）〜式（１−４２）で表される化合物が挙げられる。なお、式中、Ｒ40は、炭素数１〜２０の１価の飽和炭化水素基を表し、好ましくは炭素数６〜１２の分枝鎖状アルキル基、さらに好ましくは２−エチルヘキシル基である。 Examples of compound (1a) include compounds represented by formula (1-1) to formula (1-42). In the formula, R 40 represents a monovalent saturated hydrocarbon group having 1 to 20 carbon atoms, preferably a branched alkyl group having 6 to 12 carbon atoms, and more preferably a 2-ethylhexyl group.

Figure 0006461453
Figure 0006461453

Figure 0006461453
Figure 0006461453

Figure 0006461453
Figure 0006461453

Figure 0006461453
Figure 0006461453

Figure 0006461453
Figure 0006461453

Figure 0006461453
Figure 0006461453

Figure 0006461453
Figure 0006461453

Figure 0006461453
Figure 0006461453

Figure 0006461453
Figure 0006461453

Figure 0006461453
Figure 0006461453

Figure 0006461453
Figure 0006461453

Figure 0006461453
Figure 0006461453

Figure 0006461453
Figure 0006461453

Figure 0006461453
Figure 0006461453

Figure 0006461453
Figure 0006461453

Figure 0006461453
Figure 0006461453

Figure 0006461453
Figure 0006461453

Figure 0006461453
Figure 0006461453

Figure 0006461453
Figure 0006461453

Figure 0006461453
Figure 0006461453

Figure 0006461453
Figure 0006461453

Figure 0006461453
Figure 0006461453

Figure 0006461453
Figure 0006461453

Figure 0006461453
Figure 0006461453

Figure 0006461453
Figure 0006461453

Figure 0006461453
Figure 0006461453

Figure 0006461453
Figure 0006461453

Figure 0006461453
Figure 0006461453

Figure 0006461453
Figure 0006461453

Figure 0006461453
Figure 0006461453

Figure 0006461453
Figure 0006461453

Figure 0006461453
Figure 0006461453

Figure 0006461453
Figure 0006461453

化合物（１ａ）は、市販されているキサンテン染料（例えば、中外化成（株）製の「Chugai Aminol Fast Pink R-H/C」、田岡化学工業（株）製の「Rhodamin 6G」）を用いることができる。また、市販されているキサンテン染料を出発原料として、特開２０１０−３２９９９号公報を参考に合成することもできる。   As the compound (1a), a commercially available xanthene dye (for example, “Chugai Aminol Fast Pink RH / C” manufactured by Chugai Kasei Co., Ltd., “Rhodamin 6G” manufactured by Taoka Chemical Industry Co., Ltd.) can be used. . Moreover, it can also synthesize | combine with reference to Unexamined-Japanese-Patent No. 2010-32999 using the commercially available xanthene dye as a starting material.

顔料（Ａ２）は、カラーインデックス（The Society of Dyers and Colourists出版）でピグメントに分類されている、黄色顔料、オレンジ色顔料及び赤色顔料からなる群から選ばれる少なくとも１種の顔料である。
例えば、Ｃ．Ｉ．ピグメントイエロー１、３、１２、１３、１４、１５、１６、１７、２０、２４、３１、５３、８３、８６、９３、９４、１０９、１１０、１１７、１２５、１２８、１３７、１３８、１３９、１４７、１４８、１５０、１５３、１５４、１６６、１７３、１９４、２１４などの黄色顔料；
Ｃ．Ｉ．ピグメントオレンジ１３、３１、３６、３８、４０、４２、４３、５１、５５、５９、６１、６４、６５、７１、７３などのオレンジ色顔料；
Ｃ．Ｉ．ピグメントレッド９、９７、１０５、１２２、１２３、１４４、１４９、１６６、１６８、１７６、１７７、１８０、１９２、２０９、２１５、２１６、２２４、２４２、２５４、２５５、２６４、２６５などの赤色顔料が挙げられる。その他、Ｃ．Ｉ．ピグメントブルー１５、１５：３、１５：４、１５：６、６０などの青色顔料；Ｃ．Ｉ．ピグメントバイオレット１、１９、２３、２９、３２、３６、３８などのバイオレット色顔料；
Ｃ．Ｉ．ピグメントグリーン７、３６、５８などの緑色顔料；
Ｃ．Ｉ．ピグメントブラウン２３、２５などのブラウン色顔料；
Ｃ．Ｉ．ピグメントブラック１、７などの黒色顔料等を含むこともできる。 The pigment (A2) is at least one pigment selected from the group consisting of a yellow pigment, an orange pigment, and a red pigment, which is classified as a pigment by a color index (published by The Society of Dyers and Colorists).
For example, C.I. I. Pigment Yellow 1, 3, 12, 13, 14, 15, 16, 17, 20, 24, 31, 53, 83, 86, 93, 94, 109, 110, 117, 125, 128, 137, 138, 139, Yellow pigments such as 147, 148, 150, 153, 154, 166, 173, 194, 214;
C. I. Orange pigments such as CI Pigment Orange 13, 31, 36, 38, 40, 42, 43, 51, 55, 59, 61, 64, 65, 71, 73;
C. I. Red pigments such as CI Pigment Red 9, 97, 105, 122, 123, 144, 149, 166, 168, 176, 177, 180, 192, 209, 215, 216, 224, 242, 254, 255, 264, 265 Can be mentioned. In addition, C.I. I. Blue pigments such as CI Pigment Blue 15, 15: 3, 15: 4, 15: 6, 60; I. Violet color pigments such as CI Pigment Violet 1, 19, 23, 29, 32, 36, 38;
C. I. Green pigments such as CI Pigment Green 7, 36, 58;
C. I. Brown pigments such as CI Pigment Brown 23 and 25;
C. I. Black pigments such as CI pigment black 1 and 7 can also be included.

顔料は、Ｃ．Ｉ．ピグメントイエロー１３８、Ｃ．Ｉ．ピグメントイエロー１３９、Ｃ．Ｉ．ピグメントイエロー１５０、Ｃ．Ｉ．ピグメントレッド１７７、Ｃ．Ｉ．ピグメントレッド２４２及びＣ．Ｉ．ピグメントレッド２５４からなる群から選ばれる少なくとも１種が好ましく、Ｃ．Ｉ．ピグメントレッド１７７、Ｃ．Ｉ．ピグメントレッド２４２及びＣ．Ｉ．ピグメントレッド２５４からなる群から選ばれる少なくとも１種がより好ましい。前記の顔料を含むことで、赤色カラーフィルタとしての透過スペクトルの最適化が容易であり、カラーフィルタの耐光性及び耐薬品性が良好になる。   The pigment is C.I. I. Pigment yellow 138, C.I. I. Pigment yellow 139, C.I. I. Pigment yellow 150, C.I. I. Pigment red 177, C.I. I. Pigment red 242 and C.I. I. Preferably at least one selected from the group consisting of CI Pigment Red 254; I. Pigment red 177, C.I. I. Pigment red 242 and C.I. I. More preferred is at least one selected from the group consisting of CI Pigment Red 254. By including the pigment, it is easy to optimize the transmission spectrum of the red color filter, and the light resistance and chemical resistance of the color filter are improved.

顔料は、必要に応じて、ロジン処理、酸性基又は塩基性基が導入された顔料誘導体等を用いた表面処理、高分子化合物等による顔料表面へのグラフト処理、硫酸微粒化法等による微粒化処理、又は不純物を除去するための有機溶剤や水等による洗浄処理、イオン性不純物のイオン交換法等による除去処理等が施されていてもよい。
顔料は、粒径が均一であることが好ましい。顔料分散剤を含有させて分散処理を行うことで、顔料が溶液中で均一に分散した状態の顔料分散液を得ることができる。 If necessary, the pigment can be atomized by rosin treatment, surface treatment using a pigment derivative having an acidic group or basic group introduced, graft treatment on the pigment surface with a polymer compound, sulfuric acid atomization method, etc. A treatment, a cleaning treatment with an organic solvent or water for removing impurities, a removal treatment with an ion exchange method of ionic impurities, or the like may be performed.
The pigment preferably has a uniform particle size. By carrying out a dispersion treatment by containing a pigment dispersant, a pigment dispersion in which the pigment is uniformly dispersed in the solution can be obtained.

前記の顔料分散剤としては、例えば、カチオン系、アニオン系、ノニオン系、両性、ポリエステル系、ポリアミン系、アクリル系等の顔料分散剤等が挙げられる。これらの顔料分散剤は、単独でも２種以上を組み合わせて用いてもよい。顔料分散剤としては、商品名でＫＰ（信越化学工業（株）製）、フローレン（共栄社化学（株）製）、ソルスパース（ゼネカ（株）製）、ＥＦＫＡ（ＣＩＢＡ社製）、アジスパー（味の素ファインテクノ（株）製）、Ｄｉｓｐｅｒｂｙｋ（ビックケミー社製）などが挙げられる。
顔料分散剤を用いる場合、その使用量は、顔料（Ａ２）の総量に対して、好ましくは１質量％以上１００質量％以下であり、より好ましくは５質量％以上５０質量％以下である。顔料分散剤の使用量が前記の範囲にあると、均一な分散状態の顔料分散液が得られる傾向がある。 Examples of the pigment dispersant include cationic dispersants such as cationic, anionic, nonionic, amphoteric, polyester, polyamine, and acrylic pigments. These pigment dispersants may be used alone or in combination of two or more. As the pigment dispersant, KP (manufactured by Shin-Etsu Chemical Co., Ltd.), Floren (manufactured by Kyoeisha Chemical Co., Ltd.), Solsperse (manufactured by Geneca Co., Ltd.), EFKA (manufactured by CIBA), Ajispur (Ajinomoto Fine) (Techno Co., Ltd.), Disperbyk (Bic Chemie) and the like.
When the pigment dispersant is used, the amount used is preferably 1% by mass or more and 100% by mass or less, more preferably 5% by mass or more and 50% by mass or less, based on the total amount of the pigment (A2). When the amount of the pigment dispersant used is in the above range, there is a tendency that a pigment dispersion in a uniform dispersion state is obtained.

染料（Ａ１）は、特に限定されず、公知の染料を使用することができ、例えば、溶剤染料、酸性染料、直接染料、媒染染料等が挙げられ、有機溶剤に溶解可な染料が好ましい。
染料（Ａ１）としては、例えば、カラーインデックス（The Society of Dyers and Colourists出版）で染料に分類されている化合物や、染色ノート（色染社）に記載されている公知の染料が挙げられる。また、化学構造によれば、アゾ染料、シアニン染料、トリフェニルメタン染料、フタロシアニン染料、アントラキノン染料、ナフトキノン染料、キノンイミン染料、メチン染料、アゾメチン染料、スクワリリウム染料、アクリジン染料、スチリル染料、クマリン染料、キノリン染料及びニトロ染料等が挙げられる。これらのうち、有機溶剤可溶性染料が好ましい。 The dye (A1) is not particularly limited, and a known dye can be used. Examples thereof include a solvent dye, an acid dye, a direct dye, a mordant dye, and the like, and a dye that is soluble in an organic solvent is preferable.
Examples of the dye (A1) include compounds classified as dyes by the Color Index (published by The Society of Dyers and Colorists) and known dyes described in dyeing notes (Color Dyeing). Also, according to chemical structure, azo dye, cyanine dye, triphenylmethane dye, phthalocyanine dye, anthraquinone dye, naphthoquinone dye, quinoneimine dye, methine dye, azomethine dye, squarylium dye, acridine dye, styryl dye, coumarin dye, quinoline And dyes and nitro dyes. Of these, organic solvent-soluble dyes are preferred.

具体的には、Ｃ．Ｉ．ソルベントイエロー４、１４、１５、２３、２４、３８、６２、６３、６８、８２、９４、９８、９９、１１７、１６２、１６３、１６７、１８９；
Ｃ．Ｉ．ソルベントレッド４５、４９、１１１、１２５、１３０、１４３、１４５、１４６、１５０、１５１、１５５、１６８、１６９、１７２、１７５、１８１、２０７、２２２、２２７、２３０、２４５、２４７；
Ｃ．Ｉ．ソルベントオレンジ２、７、１１、１５、２６、５６、７７、８６；
Ｃ．Ｉ．ソルベントバイオレット１１、１３、１４、２６、３１、３６、３７、３８、４５、４７、４８、５１、５９、６０等のＣ．Ｉ．ソルベント染料、
Ｃ．Ｉ．アシッドイエロー１、３、７、９、１１、１７、２３、２５、２９、３４、３６、３８、４０、４２、５４、６５、７２、７３、７６、７９、９８、９９、１１１、１１２、１１３、１１４、１１６、１１９、１２３、１２８、１３４、１３５、１３８、１３９、１４０、１４４、１５０、１５５、１５７、１６０、１６１、１６３、１６８、１６９、１７２、１７７、１７８、１７９、１８４、１９０、１９３、１９６、１９７、１９９、２０２、２０３、２０４、２０５、２０７、２１２、２１４、２２０、２２１、２２８、２３０、２３２、２３５、２３８、２４０、２４２、２４３、２５１；
Ｃ．Ｉ．アシッドレッド１、４、８、１４、１７、１８、２６、２７、２９、３１、３３、３４、３５、３７、４０、４２、４４、５７、６６、７３、７６、８０、８８、９７、１０３、１０６、１１１、１１４、１２９、１３３、１３４、１３８、１４３、１４５、１５０、１５１、１５５、１５８、１６０、１７２、１７６、１８２、１８３、１９５、１９８、２０６、２１１、２１５、２１６、２１７、２２７、２２８、２４９、２５２、２５７、２５８、２６０、２６１、２６６、２６８、２７０、２７４、２７７、２８０、２８１、３０８、３１２、３１５、３１６、３３９、３４１、３４５、３４６、３４９、３８２、３８３、３９４、４０１、４１２、４１７、４１８、４２２、４２６；
Ｃ．Ｉ．アシッドオレンジ６、７、８、１０、１２、２６、５０、５１、５２、５６、６２、６３、６４、７４、７５、９４、９５、１０７、１０８、１６９、１７３；
Ｃ．Ｉ．アシッドバイオレット６Ｂ、７、１７、１９、３４等のＣ．Ｉ．アシッド染料、 Specifically, C.I. I. Solvent Yellow 4, 14, 15, 23, 24, 38, 62, 63, 68, 82, 94, 98, 99, 117, 162, 163, 167, 189;
C. I. Solvent Red 45, 49, 111, 125, 130, 143, 145, 146, 150, 151, 155, 168, 169, 172, 175, 181, 207, 222, 227, 230, 245, 247;
C. I. Solvent Orange 2, 7, 11, 15, 26, 56, 77, 86;
C. I. Solvent Violet 11, 13, 14, 26, 31, 36, 37, 38, 45, 47, 48, 51, 59, 60, etc. I. Solvent dyes,
C. I. Acid Yellow 1, 3, 7, 9, 11, 17, 23, 25, 29, 34, 36, 38, 40, 42, 54, 65, 72, 73, 76, 79, 98, 99, 111, 112, 113, 114, 116, 119, 123, 128, 134, 135, 138, 139, 140, 144, 150, 155, 157, 160, 161, 163, 168, 169, 172, 177, 178, 179, 184, 190, 193, 196, 197, 199, 202, 203, 204, 205, 207, 212, 214, 220, 221, 228, 230, 232, 235, 238, 240, 242, 243, 251;
C. I. Acid Red 1, 4, 8, 14, 17, 18, 26, 27, 29, 31, 33, 34, 35, 37, 40, 42, 44, 57, 66, 73, 76, 80, 88, 97, 103, 106, 111, 114, 129, 133, 134, 138, 143, 145, 150, 151, 155, 158, 160, 172, 176, 182, 183, 195, 198, 206, 211, 215, 216, 217, 227, 228, 249, 252, 257, 258, 260, 261, 266, 268, 270, 274, 277, 280, 281, 308, 312, 315, 316, 339, 341, 345, 346, 349, 382, 383, 394, 401, 412, 417, 418, 422, 426;
C. I. Acid Orange 6, 7, 8, 10, 12, 26, 50, 51, 52, 56, 62, 63, 64, 74, 75, 94, 95, 107, 108, 169, 173;
C. I. Acid Violet 6B, 7, 17, 19, 34, etc. I. Acid dyes,

Ｃ．Ｉ．ダイレクトイエロー２、３３、３４、３５、３８、３９、４３、４７、５０、５４、５８、６８、６９、７０、７１、８６、９３、９４、９５、９８、１０２、１０８、１０９、１２９、１３６、１３８、１４１；
Ｃ．Ｉ．ダイレクトレッド７９、８２、８３、８４、９１、９２、９６、９７、９８、９９、１０５、１０６、１０７、１７２、１７３、１７６、１７７、１７９、１８１、１８２、１８４、２０４、２０７、２１１、２１３、２１８、２２０、２２１、２２２、２３２、２３３、２３４、２４１、２４３、２４６、２５０；
Ｃ．Ｉ．ダイレクトオレンジ２６、３４、３９、４１、４６、５０、５２、５６、５７、６１、６４、６５、６８、７０、９６、９７、１０６、１０７；
Ｃ．Ｉ．ダイレクトバイオレット４７、５２、５４、５９、６０、６５、６６、７９、８０、８１、８２、８４、８９、９０、９３、９５、９６、１０３、１０４等のＣ．Ｉ．ダイレクト染料、
Ｃ．Ｉ．ディスパースイエロー５１、５４，７６；
Ｃ．Ｉ．ディスパースバイオレット２６、２７等のＣ．Ｉ．ディスパース染料、
Ｃ．Ｉ．リアクティブイエロー２，７６，１１６；
Ｃ．Ｉ．リアクティブオレンジ１６；等のＣ．Ｉ．リアクティブ染料
Ｃ．Ｉ．モーダントイエロー５、８、１０、１６、２０、２６、３０、３１、３３、４２、４３、４５、５６、６１、６２、６５；
Ｃ．Ｉ．モーダントレッド１、２、３、４、９、１１、１２、１４、１７、１８、１９、２２、２３、２４、２５、２６、３０、３２、３３、３６、３７、３８、３９、４１、４３、４５、４６、４８、５３、５６、６３、７１、７４、８５、８６、８８、９０、９４、９５；
Ｃ．Ｉ．モーダントオレンジ３、４、５、８、１２、１３、１４、２０、２１、２３、２４、２８、２９、３２、３４、３５、３６、３７、４２、４３、４７、４８；
Ｃ．Ｉ．モーダントバイオレット１、２、４、５、７、１４、２２、２４、３０、３１、３２、３７、４０、４１、４４、４５、４７、４８、５３、５８
等が挙げられる。
これらの染料は、所望するカラーフィルタの分光スペクトルに合わせて適宜選択すればよい。 C. I. Direct Yellow 2, 33, 34, 35, 38, 39, 43, 47, 50, 54, 58, 68, 69, 70, 71, 86, 93, 94, 95, 98, 102, 108, 109, 129, 136, 138, 141;
C. I. Direct Red 79, 82, 83, 84, 91, 92, 96, 97, 98, 99, 105, 106, 107, 172, 173, 176, 177, 179, 181, 182, 184, 204, 207, 211, 213, 218, 220, 221, 222, 232, 233, 234, 241, 243, 246, 250;
C. I. Direct Orange 26, 34, 39, 41, 46, 50, 52, 56, 57, 61, 64, 65, 68, 70, 96, 97, 106, 107;
C. I. Direct violet 47, 52, 54, 59, 60, 65, 66, 79, 80, 81, 82, 84, 89, 90, 93, 95, 96, 103, 104, etc. I. Direct dyes,
C. I. Disperse Yellow 51, 54, 76;
C. I. Disperse Violet 26, 27 etc. C.I. I. Disperse dyes,
C. I. Reactive Yellow 2, 76, 116;
C. I. Reactive Orange 16; I. Reactive dyes C.I. I. Modern yellow 5, 8, 10, 16, 20, 26, 30, 31, 33, 42, 43, 45, 56, 61, 62, 65;
C. I. Modern Red 1, 2, 3, 4, 9, 11, 12, 14, 17, 18, 19, 22, 23, 24, 25, 26, 30, 32, 33, 36, 37, 38, 39, 41 43, 45, 46, 48, 53, 56, 63, 71, 74, 85, 86, 88, 90, 94, 95;
C. I. Modern orange 3, 4, 5, 8, 12, 13, 14, 20, 21, 23, 24, 28, 29, 32, 34, 35, 36, 37, 42, 43, 47, 48;
C. I. Modern violet 1, 2, 4, 5, 7, 14, 22, 24, 30, 31, 32, 37, 40, 41, 44, 45, 47, 48, 53, 58
Etc.
These dyes may be appropriately selected according to the desired spectral spectrum of the color filter.

着色剤（Ａ）が染料（Ａ３）を含む場合、染料（Ａ３）の含有量は、着色剤（Ａ）の総量に対して、１〜９０質量％が好ましく、１〜５０質量％がより好ましい。   When the colorant (A) contains the dye (A3), the content of the dye (A3) is preferably 1 to 90% by mass, and more preferably 1 to 50% by mass with respect to the total amount of the colorant (A). .

化合物（１ａ）と顔料（Ａ２）との含有比率は質量基準で、１：９９〜９９：１が好ましく、２：９８〜５０：５０がより好ましく、５：９５〜３０：７０がさらに好ましい。
このような比率とすることにより、透過スペクトルの最適化が容易となり、得られるカラーフィルタは、コントラスト、明度、耐熱性及び耐薬品性に優れる傾向がある。 The content ratio of the compound (1a) and the pigment (A2) is, on a mass basis, preferably from 1:99 to 99: 1, more preferably from 2:98 to 50:50, and further preferably from 5:95 to 30:70.
By setting such a ratio, the transmission spectrum can be easily optimized, and the resulting color filter tends to be excellent in contrast, brightness, heat resistance, and chemical resistance.

着色剤（Ａ）の含有量は、固形分の総量に対して、好ましくは５〜６０質量％であり、より好ましくは８〜５０質量％であり、さらに好ましくは１０〜４０質量％である。着色剤（Ａ）の含有量が前記の範囲内にあると、カラーフィルタとしたときの色濃度が十分であり、かつ組成物中に樹脂（Ｂ）や重合性化合物（Ｃ）を必要量含有させることができるので、機械的強度が十分なカラーフィルタを形成することができる。
ここで、本明細書における「固形分の総量」とは、赤色着色硬化性樹脂組成物の総量から溶剤の含有量を除いた量のことをいう。固形分の総量及びこれに対する各成分の含有量は、例えば、液体クロマトグラフィー又はガスクロマトグラフィーなどの公知の分析手段で測定することができる。 The content of the colorant (A) is preferably 5 to 60% by mass, more preferably 8 to 50% by mass, and further preferably 10 to 40% by mass with respect to the total amount of the solid content. When the content of the colorant (A) is within the above range, the color density when it is used as a color filter is sufficient, and the resin (B) and the polymerizable compound (C) are contained in a necessary amount in the composition. Therefore, a color filter having sufficient mechanical strength can be formed.
Here, the “total amount of solids” in this specification refers to an amount obtained by removing the content of the solvent from the total amount of the red colored curable resin composition. The total amount of solids and the content of each component relative thereto can be measured by known analytical means such as liquid chromatography or gas chromatography, for example.

＜樹脂（Ｂ）＞
樹脂（Ｂ）は、特に限定されないが、アルカリ可溶性樹脂であることが好ましい。樹脂（Ｂ）としては、例えば、以下の樹脂［Ｋ１］〜［Ｋ６］等が挙げられる。
樹脂［Ｋ１］不飽和カルボン酸及び不飽和カルボン酸無水物からなる群から選ばれる少なくとも１種（ａ）（以下「（ａ）」という場合がある）と、炭素数２〜４の環状エーテル構造とエチレン性不飽和結合とを有する単量体（ｂ）（以下「（ｂ）」という場合がある）との共重合体；
樹脂［Ｋ２］（ａ）と（ｂ）と、（ａ）と共重合可能な単量体（ｃ）（ただし、（ａ）及び（ｂ）とは異なる。）（以下「（ｃ）」という場合がある）との共重合体；
樹脂［Ｋ３］（ａ）と（ｃ）との共重合体；
樹脂［Ｋ４］（ａ）と（ｃ）との共重合体に（ｂ）を反応させた樹脂；
樹脂［Ｋ５］（ｂ）と（ｃ）との共重合体に（ａ）を反応させた樹脂；
樹脂［Ｋ６］（ｂ）と（ｃ）との共重合体に（ａ）を反応させ、さらにカルボン酸無水物を反応させた樹脂。 <Resin (B)>
The resin (B) is not particularly limited, but is preferably an alkali-soluble resin. Examples of the resin (B) include the following resins [K1] to [K6].
Resin [K1] At least one (a) selected from the group consisting of an unsaturated carboxylic acid and an unsaturated carboxylic acid anhydride (hereinafter sometimes referred to as “(a)”), and a cyclic ether structure having 2 to 4 carbon atoms And a copolymer of a monomer (b) having an ethylenically unsaturated bond (hereinafter sometimes referred to as “(b)”);
Resin [K2] (a) and (b), monomer (c) copolymerizable with (a) (however, different from (a) and (b)) (hereinafter referred to as “(c)”) In some cases)
Resin [K3] Copolymer of (a) and (c);
Resin [K4] A resin obtained by reacting (b) with a copolymer of (a) and (c);
Resin [K5] A resin obtained by reacting (a) with a copolymer of (b) and (c);
Resin [K6] A resin obtained by reacting (a) with a copolymer of (b) and (c) and further reacting with a carboxylic acid anhydride.

（ａ）としては、具体的には、アクリル酸、メタクリル酸、クロトン酸、ｏ−、ｍ−、ｐ−ビニル安息香酸等の不飽和モノカルボン酸類；
マレイン酸、フマル酸、シトラコン酸、メサコン酸、イタコン酸、３−ビニルフタル酸、４−ビニルフタル酸、３，４，５，６−テトラヒドロフタル酸、１，２，３，６−テトラヒドロフタル酸、ジメチルテトラヒドロフタル酸、１、４−シクロヘキセンジカルボン酸等の不飽和ジカルボン酸類；
メチル−５−ノルボルネン−２，３−ジカルボン酸、５−カルボキシビシクロ［２．２．１］ヘプト−２−エン、５，６−ジカルボキシビシクロ［２．２．１］ヘプト−２−エン、５−カルボキシ−５−メチルビシクロ［２．２．１］ヘプト−２−エン、５−カルボキシ−５−エチルビシクロ［２．２．１］ヘプト−２−エン、５−カルボキシ−６−メチルビシクロ［２．２．１］ヘプト−２−エン、５−カルボキシ−６−エチルビシクロ［２．２．１］ヘプト−２−エン等のカルボキシ基を含有するビシクロ不飽和化合物類；
無水マレイン酸、シトラコン酸無水物、イタコン酸無水物、３−ビニルフタル酸無水物、４−ビニルフタル酸無水物、３，４，５，６−テトラヒドロフタル酸無水物、１，２，３，６−テトラヒドロフタル酸無水物、ジメチルテトラヒドロフタル酸無水物、５，６−ジカルボキシビシクロ［２．２．１］ヘプト−２−エン無水物等の不飽和ジカルボン酸類無水物；
こはく酸モノ〔２−（メタ）アクリロイルオキシエチル〕、フタル酸モノ〔２−（メタ）アクリロイルオキシエチル〕等の２価以上の多価カルボン酸の不飽和モノ〔（メタ）アクリロイルオキシアルキル〕エステル類；
α−（ヒドロキシメチル）アクリル酸のような、同一分子中にヒドロキシ基及びカルボキシ基を含有する不飽和アクリル酸類等が挙げられる。 As (a), specifically, unsaturated monocarboxylic acids such as acrylic acid, methacrylic acid, crotonic acid, o-, m-, and p-vinylbenzoic acid;
Maleic acid, fumaric acid, citraconic acid, mesaconic acid, itaconic acid, 3-vinylphthalic acid, 4-vinylphthalic acid, 3,4,5,6-tetrahydrophthalic acid, 1,2,3,6-tetrahydrophthalic acid, dimethyl Unsaturated dicarboxylic acids such as tetrahydrophthalic acid and 1,4-cyclohexene dicarboxylic acid;
Methyl-5-norbornene-2,3-dicarboxylic acid, 5-carboxybicyclo [2.2.1] hept-2-ene, 5,6-dicarboxybicyclo [2.2.1] hept-2-ene, 5-carboxy-5-methylbicyclo [2.2.1] hept-2-ene, 5-carboxy-5-ethylbicyclo [2.2.1] hept-2-ene, 5-carboxy-6-methylbicyclo Bicyclounsaturated compounds containing a carboxy group such as [2.2.1] hept-2-ene, 5-carboxy-6-ethylbicyclo [2.2.1] hept-2-ene;
Maleic anhydride, citraconic anhydride, itaconic anhydride, 3-vinylphthalic anhydride, 4-vinylphthalic anhydride, 3,4,5,6-tetrahydrophthalic anhydride, 1,2,3,6- Unsaturated dicarboxylic acid anhydrides such as tetrahydrophthalic anhydride, dimethyltetrahydrophthalic anhydride, 5,6-dicarboxybicyclo [2.2.1] hept-2-ene anhydride;
Unsaturated mono [(meth) acryloyloxyalkyl] esters of polyvalent carboxylic acids such as succinic acid mono [2- (meth) acryloyloxyethyl] and phthalic acid mono [2- (meth) acryloyloxyethyl] Kind;
Examples thereof include unsaturated acrylic acids containing a hydroxy group and a carboxy group in the same molecule, such as α- (hydroxymethyl) acrylic acid.

これらのうち、共重合反応性の点や得られる樹脂のアルカリ水溶液への溶解性の点から、アクリル酸、メタクリル酸、無水マレイン酸等が好ましい。
尚、本明細書において、「（メタ）アクリロイル」とは、アクリロイル及びメタクリロイルよりなる群から選ばれる少なくとも１種を表す。「（メタ）アクリル酸」及び「（メタ）アクリレート」等の表記も、同様の意味を有する。 Of these, acrylic acid, methacrylic acid, maleic anhydride and the like are preferable from the viewpoint of copolymerization reactivity and the solubility of the resulting resin in an alkaline aqueous solution.
In the present specification, “(meth) acryloyl” represents at least one selected from the group consisting of acryloyl and methacryloyl. Notations such as “(meth) acrylic acid” and “(meth) acrylate” have the same meaning.

（ｂ）は、例えば、炭素数２〜４の環状エーテル構造（例えば、オキシラン環、オキセタン環及びテトラヒドロフラン環からなる群から選ばれる少なくとも１種）とエチレン性不飽和結合とを有する重合性化合物である。（ｂ）は、炭素数２〜４の環状エーテル構造と（メタ）アクリロイルオキシ基とを有する単量体が好ましい。
。 (B) is a polymerizable compound having, for example, a C2-C4 cyclic ether structure (for example, at least one selected from the group consisting of an oxirane ring, an oxetane ring and a tetrahydrofuran ring) and an ethylenically unsaturated bond. is there. (B) is preferably a monomer having a C2-C4 cyclic ether structure and a (meth) acryloyloxy group.
.

（ｂ）としては、例えば、オキシラニル基とエチレン性不飽和結合とを有する単量体（ｂ１）（以下「（ｂ１）」という場合がある）、オキセタニル基とエチレン性不飽和結合とを有する単量体（ｂ２）（以下「（ｂ２）」という場合がある）、テトラヒドロフリル基とエチレン性不飽和結合とを有する単量体（ｂ３）（以下「（ｂ３）」という場合がある）等が挙げられる。   Examples of (b) include a monomer (b1) having an oxiranyl group and an ethylenically unsaturated bond (hereinafter sometimes referred to as “(b1)”), and a single monomer having an oxetanyl group and an ethylenically unsaturated bond. Monomer (b2) (hereinafter sometimes referred to as “(b2)”), monomer (b3) having a tetrahydrofuryl group and an ethylenically unsaturated bond (hereinafter sometimes referred to as “(b3)”), etc. Can be mentioned.

（ｂ１）としては、直鎖状又は分枝鎖状の不飽和脂肪族炭化水素がエポキシ化された構造を有する単量体（ｂ１−１）（以下「（ｂ１−１）」という場合がある）及び不飽和脂環式炭化水素がエポキシ化された構造を有する単量体（ｂ１−２）（以下「（ｂ１−２）」という場合がある）が挙げられる。   As (b1), a monomer (b1-1) having a structure in which a linear or branched unsaturated aliphatic hydrocarbon is epoxidized (hereinafter referred to as “(b1-1)”) ) And a monomer (b1-2) having a structure in which an unsaturated alicyclic hydrocarbon is epoxidized (hereinafter sometimes referred to as “(b1-2)”).

（ｂ１−１）としては、グリシジル（メタ）アクリレート、β−メチルグリシジル（メタ）アクリレート、β−エチルグリシジル（メタ）アクリレート、グリシジルビニルエーテル、ｏ−ビニルベンジルグリシジルエーテル、ｍ−ビニルベンジルグリシジルエーテル、ｐ−ビニルベンジルグリシジルエーテル、α−メチル−ｏ−ビニルベンジルグリシジルエーテル、α−メチル−ｍ−ビニルベンジルグリシジルエーテル、α−メチル−ｐ−ビニルベンジルグリシジルエーテル、２，３−ビス（グリシジルオキシメチル）スチレン、２，４−ビス（グリシジルオキシメチル）スチレン、２，５−ビス（グリシジルオキシメチル）スチレン、２，６−ビス（グリシジルオキシメチル）スチレン、２，３，４−トリス（グリシジルオキシメチル）スチレン、２，３，５−トリス（グリシジルオキシメチル）スチレン、２，３，６−トリス（グリシジルオキシメチル）スチレン、３，４，５−トリス（グリシジルオキシメチル）スチレン及び２，４，６−トリス（グリシジルオキシメチル）スチレンが挙げられる。   As (b1-1), glycidyl (meth) acrylate, β-methylglycidyl (meth) acrylate, β-ethylglycidyl (meth) acrylate, glycidyl vinyl ether, o-vinylbenzyl glycidyl ether, m-vinylbenzyl glycidyl ether, p -Vinylbenzyl glycidyl ether, α-methyl-o-vinylbenzyl glycidyl ether, α-methyl-m-vinylbenzyl glycidyl ether, α-methyl-p-vinylbenzyl glycidyl ether, 2,3-bis (glycidyloxymethyl) styrene 2,4-bis (glycidyloxymethyl) styrene, 2,5-bis (glycidyloxymethyl) styrene, 2,6-bis (glycidyloxymethyl) styrene, 2,3,4-tris (glycidyloxymethyl) styrene 2,3,5-tris (glycidyloxymethyl) styrene, 2,3,6-tris (glycidyloxymethyl) styrene, 3,4,5-tris (glycidyloxymethyl) styrene and 2,4,6- An example is tris (glycidyloxymethyl) styrene.

（ｂ１−２）としては、ビニルシクロヘキセンモノオキサイド、１，２−エポキシ−４−ビニルシクロヘキサン（例えば、セロキサイド２０００；（株）ダイセル製）、３，４−エポキシシクロヘキシルメチル（メタ）アクリレート（例えば、サイクロマーＡ４００；（株）ダイセル製）、３，４−エポキシシクロヘキシルメチル（メタ）アクリレート（例えば、サイクロマーＭ１００；（株）ダイセル製）、式（Ｉ）で表される化合物及び式（ＩＩ）で表される化合物が挙げられる。   Examples of (b1-2) include vinylcyclohexene monooxide, 1,2-epoxy-4-vinylcyclohexane (for example, Celoxide 2000; manufactured by Daicel Corporation), 3,4-epoxycyclohexylmethyl (meth) acrylate (for example, Cyclomer A400; manufactured by Daicel Corporation), 3,4-epoxycyclohexylmethyl (meth) acrylate (for example, Cyclomer M100; manufactured by Daicel Corporation), a compound represented by Formula (I), and Formula (II) The compound represented by these is mentioned.

Figure 0006461453
Figure 0006461453

［式（Ｉ）及び式（ＩＩ）中、Ｒb1及びＲb2は、水素原子又は炭素数１〜４のアルキル基を表し、該アルキル基に含まれる水素原子は、ヒドロキシ基で置換されていてもよい。
Ｘb1及びＸb2は、単結合、−Ｒb3−、＊−Ｒb3−Ｏ−、＊−Ｒb3−Ｓ−又は＊−Ｒb3−ＮＨ−を表す。
Ｒb3は、炭素数１〜６のアルカンジイル基を表す。
＊は、Ｏとの結合手を表す。］ [In Formula (I) and Formula (II), R b1 and R b2 represent a hydrogen atom or an alkyl group having 1 to 4 carbon atoms, and the hydrogen atom contained in the alkyl group is substituted with a hydroxy group. Also good.
X b1 and X b2 represents a single bond, -R b3 -, * - R b3 -O -, * - R b3 -S- or * -R b3 represents a -NH-.
R b3 represents an alkanediyl group having 1 to 6 carbon atoms.
* Represents a bond with O. ]

炭素数１〜４のアルキル基としては、メチル基、エチル基、ｎ−プロピル基、イソプロピル基、ｎ−ブチル基、ｓｅｃ−ブチル基及びｔｅｒｔ−ブチル基が挙げられる。
水素原子がヒドロキシで置換されたアルキル基としては、ヒドロキシメチル基、１−ヒドロキシエチル基、２−ヒドロキシエチル基、１−ヒドロキシプロピル基、２−ヒドロキシプロピル基、３−ヒドロキシプロピル基、１−ヒドロキシ−１−メチルエチル基、２−ヒドロキシ−１−メチルエチル基、１−ヒドロキシブチル基、２−ヒドロキシブチル基、３−ヒドロキシブチル基及び４−ヒドロキシブチル基が挙げられる。
Ｒb1及びＲb2は、好ましくは水素原子、メチル基、ヒドロキシメチル基、１−ヒドロキシエチル基又は２−ヒドロキシエチル基であり、より好ましくは水素原子又はメチル基である。 Examples of the alkyl group having 1 to 4 carbon atoms include methyl group, ethyl group, n-propyl group, isopropyl group, n-butyl group, sec-butyl group and tert-butyl group.
Examples of the alkyl group in which a hydrogen atom is substituted with hydroxy include hydroxymethyl group, 1-hydroxyethyl group, 2-hydroxyethyl group, 1-hydroxypropyl group, 2-hydroxypropyl group, 3-hydroxypropyl group, 1-hydroxy Examples include -1-methylethyl group, 2-hydroxy-1-methylethyl group, 1-hydroxybutyl group, 2-hydroxybutyl group, 3-hydroxybutyl group, and 4-hydroxybutyl group.
R b1 and R b2 are preferably a hydrogen atom, a methyl group, a hydroxymethyl group, a 1-hydroxyethyl group or a 2-hydroxyethyl group, and more preferably a hydrogen atom or a methyl group.

アルカンジイル基としては、メチレン基、エチレン基、プロパン−１，２−ジイル基、プロパン−１，３−ジイル基、ブタン−１，４−ジイル基、ペンタン−１，５−ジイル基及びヘキサン−１，６−ジイル基が挙げられる。
Ｘb1及びＸb2としては、好ましくは単結合、メチレン基、エチレン基、＊−ＣＨ２−Ｏ−又は＊−ＣＨ２ＣＨ２−Ｏ−であり、より好ましくは単結合又は＊−ＣＨ２ＣＨ２−Ｏ−である（＊はＯとの結合手を表す）。 Examples of the alkanediyl group include methylene group, ethylene group, propane-1,2-diyl group, propane-1,3-diyl group, butane-1,4-diyl group, pentane-1,5-diyl group and hexane- A 1,6-diyl group may be mentioned.
X b1 and X b2 are preferably a single bond, a methylene group, an ethylene group, * —CH 2 —O— or * —CH 2 CH 2 —O—, more preferably a single bond or * —CH 2 CH. 2 -O- (* represents a bond with O).

式（Ｉ）で表される化合物としては、式（Ｉ−１）〜式（Ｉ−１５）のいずれかで表される化合物が挙げられる。中でも、式（Ｉ−１）、式（Ｉ−３）、式（Ｉ−５）、式（Ｉ−７）、式（Ｉ−９）又は式（Ｉ−１１）〜式（Ｉ−１５）で表される化合物が好ましく、式（Ｉ−１）、式（Ｉ−７）、式（Ｉ−９）又は式（Ｉ−１５）で表される化合物がより好ましい。   Examples of the compound represented by the formula (I) include compounds represented by any one of the formulas (I-1) to (I-15). Among them, formula (I-1), formula (I-3), formula (I-5), formula (I-7), formula (I-9), or formula (I-11) to formula (I-15) A compound represented by formula (I-1), formula (I-7), formula (I-9) or formula (I-15) is more preferred.

Figure 0006461453
Figure 0006461453

Figure 0006461453
Figure 0006461453

式（ＩＩ）で表される化合物としては、式（ＩＩ−１）〜式（ＩＩ−１５）のいずれかで表される化合物等が挙げられる。中でも、式（ＩＩ−１）、式（ＩＩ−３）、式（ＩＩ−５）、式（ＩＩ−７）、式（ＩＩ−９）又は式（ＩＩ−１１）〜式（ＩＩ−１５）で表される化合物が好ましく、式（ＩＩ−１）、式（ＩＩ−７）、式（ＩＩ−９）又は式（ＩＩ−１５）で表される化合物がより好ましい。   Examples of the compound represented by the formula (II) include compounds represented by any one of the formulas (II-1) to (II-15). Among them, formula (II-1), formula (II-3), formula (II-5), formula (II-7), formula (II-9) or formula (II-11) to formula (II-15) A compound represented by formula (II-1), formula (II-7), formula (II-9) or formula (II-15) is more preferred.

Figure 0006461453
Figure 0006461453

Figure 0006461453
Figure 0006461453

式（Ｉ）で表される化合物及び式（ＩＩ）で表される化合物は、それぞれ単独で用いても、任意の比率で混合して用いてもよい。混合して用いる場合、式（Ｉ）で表される化合物及び式（ＩＩ）で表される化合物の含有比率はモル基準で、好ましくは５：９５〜９５：５、より好ましくは１０：９０〜９０：１０、さらに好ましくは２０：８０〜８０：２０である。   The compound represented by the formula (I) and the compound represented by the formula (II) may be used singly or as a mixture in any ratio. When used as a mixture, the content ratio of the compound represented by the formula (I) and the compound represented by the formula (II) is preferably 5:95 to 95: 5, more preferably 10:90 to 5 on a molar basis. 90:10, more preferably 20:80 to 80:20.

（ｂ２）としては、オキセタニル基と（メタ）アクリロイルオキシ基とを有する単量体がより好ましい。（ｂ２）としては、３−メチル−３−メタクリルロイルオキシメチルオキセタン、３−メチル−３−アクリロイルオキシメチルオキセタン、３−エチル−３−メタクリロイルオキシメチルオキセタン、３−エチル−３−アクリロイルオキシメチルオキセタン、３−メチル−３−メタクリロイルオキシエチルオキセタン、３−メチル−３−アクリロイルオキシエチルオキセタン、３−エチル−３−メタクリロイルオキシエチルオキセタン及び３−エチル−３−アクリロイルオキシエチルオキセタンが挙げられる。   (B2) is more preferably a monomer having an oxetanyl group and a (meth) acryloyloxy group. (B2) includes 3-methyl-3-methacryloyloxymethyloxetane, 3-methyl-3-acryloyloxymethyloxetane, 3-ethyl-3-methacryloyloxymethyloxetane, 3-ethyl-3-acryloyloxymethyloxetane 3-methyl-3-methacryloyloxyethyl oxetane, 3-methyl-3-acryloyloxyethyl oxetane, 3-ethyl-3-methacryloyloxyethyl oxetane and 3-ethyl-3-acryloyloxyethyl oxetane.

（ｂ３）としては、テトラヒドロフリル基と（メタ）アクリロイルオキシ基とを有する単量体がより好ましい。（ｂ３）としては、具体的には、テトラヒドロフルフリルアクリレート（例えば、ビスコートＶ＃１５０、大阪有機化学工業（株）製）及びテトラヒドロフルフリルメタクリレートが挙げられる。   (B3) is more preferably a monomer having a tetrahydrofuryl group and a (meth) acryloyloxy group. Specific examples of (b3) include tetrahydrofurfuryl acrylate (for example, Biscoat V # 150, manufactured by Osaka Organic Chemical Industry Co., Ltd.) and tetrahydrofurfuryl methacrylate.

得られるカラーフィルタの耐熱性、耐薬品性等の信頼性をより高くすることができる点で、（ｂ）は、（ｂ１）であることが好ましい。さらに、赤色着色硬化性樹脂組成物の保存安定性が優れるという点で、（ｂ１−２）がより好ましい。   (B) is preferably (b1) in that the color filter obtained can have higher reliability such as heat resistance and chemical resistance. Furthermore, (b1-2) is more preferable in that the storage stability of the red colored curable resin composition is excellent.

（ｃ）としては、例えば、メチル（メタ）アクリレート、エチル（メタ）アクリレート、ｎ−ブチル（メタ）アクリレート、ｓｅｃ−ブチル（メタ）アクリレート、ｔｅｒｔ−ブチル（メタ）アクリレート、２−エチルヘキシル（メタ）アクリレート、ドデシル（メタ）アクリレート、ラウリル（メタ）アクリレート、ステアリル（メタ）アクリレート、シクロペンチル（メタ）アクリレート、シクロヘキシル（メタ）アクリレート、２−メチルシクロヘキシル（メタ）アクリレート、トリシクロ［５．２．１．０2,6］デカン−８−イル（メタ）アクリレート（当該技術分野では、慣用名として「ジシクロペンタニル（メタ）アクリレート」といわれている。また、「トリシクロデシル（メタ）アクリレート」という場合がある。）、トリシクロ［５．２．１．０2,6］デセン−８−イル（メタ）アクリレート（当該技術分野では、慣用名として「ジシクロペンテニル（メタ）アクリレート」といわれている。）、ジシクロペンタニルオキシエチル（メタ）アクリレート、イソボルニル（メタ）アクリレート、アダマンチル（メタ）アクリレート、アリル（メタ）アクリレート、プロパルギル（メタ）アクリレート、フェニル（メタ）アクリレート、ナフチル（メタ）アクリレート、ベンジル（メタ）アクリレート等の（メタ）アクリル酸エステル類；
２−ヒドロキシエチル（メタ）アクリレート、２−ヒドロキシプロピル（メタ）アクリレート等のヒドロキシ基含有（メタ）アクリル酸エステル類；
マレイン酸ジエチル、フマル酸ジエチル、イタコン酸ジエチル等のジカルボン酸ジエステル；
ビシクロ［２．２．１］ヘプト−２−エン、５−メチルビシクロ［２．２．１］ヘプト−２−エン、５−エチルビシクロ［２．２．１］ヘプト−２−エン、５−ヒドロキシビシクロ［２．２．１］ヘプト−２−エン、５−ヒドロキシメチルビシクロ［２．２．１］ヘプト−２−エン、５−（２’−ヒドロキシエチル）ビシクロ［２．２．１］ヘプト−２−エン、５−メトキシビシクロ［２．２．１］ヘプト−２−エン、５−エトキシビシクロ［２．２．１］ヘプト−２−エン、５，６−ジヒドロキシビシクロ［２．２．１］ヘプト−２−エン、５，６−ジ（ヒドロキシメチル）ビシクロ［２．２．１］ヘプト−２−エン、５，６−ジ（２’−ヒドロキシエチル）ビシクロ［２．２．１］ヘプト−２−エン、５，６−ジメトキシビシクロ［２．２．１］ヘプト−２−エン、５，６−ジエトキシビシクロ［２．２．１］ヘプト−２−エン、５−ヒドロキシ−５−メチルビシクロ［２．２．１］ヘプト−２−エン、５−ヒドロキシ−５−エチルビシクロ［２．２．１］ヘプト−２−エン、５−ヒドロキシメチル−５−メチルビシクロ［２．２．１］ヘプト−２−エン、５−ｔｅｒｔ−ブトキシカルボニルビシクロ［２．２．１］ヘプト−２−エン、５−シクロヘキシルオキシカルボニルビシクロ［２．２．１］ヘプト−２−エン、５−フェノキシカルボニルビシクロ［２．２．１］ヘプト−２−エン、５，６−ビス（ｔｅｒｔ−ブトキシカルボニル）ビシクロ［２．２．１］ヘプト−２−エン、５，６−ビス（シクロヘキシルオキシカルボニル）ビシクロ［２．２．１］ヘプト−２−エン等のビシクロ不飽和化合物類；
Ｎ−フェニルマレイミド、Ｎ−シクロヘキシルマレイミド、Ｎ−ベンジルマレイミド、Ｎ−スクシンイミジル−３−マレイミドベンゾエート、Ｎ−スクシンイミジル−４−マレイミドブチレート、Ｎ−スクシンイミジル−６−マレイミドカプロエート、Ｎ−スクシンイミジル−３−マレイミドプロピオネート、Ｎ−（９−アクリジニル）マレイミド等のジカルボニルイミド誘導体類；
スチレン、α−メチルスチレン、ｍ−メチルスチレン、ｐ−メチルスチレン、ビニルトルエン、ｐ−メトキシスチレン、アクリロニトリル、メタクリロニトリル、塩化ビニル、塩化ビニリデン、アクリルアミド、メタクリルアミド、酢酸ビニル、１，３−ブタジエン、イソプレン及び２，３−ジメチル−１，３−ブタジエンが挙げられる。
これらのうち、共重合反応性及び耐熱性の点から、スチレン、ビニルトルエン、Ｎ−フェニルマレイミド、Ｎ−シクロヘキシルマレイミド及びＮ−ベンジルマレイミドが好ましい。 Examples of (c) include methyl (meth) acrylate, ethyl (meth) acrylate, n-butyl (meth) acrylate, sec-butyl (meth) acrylate, tert-butyl (meth) acrylate, and 2-ethylhexyl (meth). Acrylate, dodecyl (meth) acrylate, lauryl (meth) acrylate, stearyl (meth) acrylate, cyclopentyl (meth) acrylate, cyclohexyl (meth) acrylate, 2-methylcyclohexyl (meth) acrylate, tricyclo [5.2.1.0 2,6 ] decan-8-yl (meth) acrylate (in this technical field, it is called “dicyclopentanyl (meth) acrylate” as a common name. In the case of “tricyclodecyl (meth) acrylate”) There is a bird) Black (in the art, it is said that "dicyclopentenyl (meth) acrylate" as trivial name.) [5.2.1.0 2,6] decene-8-yl (meth) acrylate, dicyclopenta Nyloxyethyl (meth) acrylate, isobornyl (meth) acrylate, adamantyl (meth) acrylate, allyl (meth) acrylate, propargyl (meth) acrylate, phenyl (meth) acrylate, naphthyl (meth) acrylate, benzyl (meth) acrylate, etc. (Meth) acrylic acid esters of
Hydroxy group-containing (meth) acrylic acid esters such as 2-hydroxyethyl (meth) acrylate and 2-hydroxypropyl (meth) acrylate;
Dicarboxylic acid diesters such as diethyl maleate, diethyl fumarate, diethyl itaconate;
Bicyclo [2.2.1] hept-2-ene, 5-methylbicyclo [2.2.1] hept-2-ene, 5-ethylbicyclo [2.2.1] hept-2-ene, 5- Hydroxybicyclo [2.2.1] hept-2-ene, 5-hydroxymethylbicyclo [2.2.1] hept-2-ene, 5- (2′-hydroxyethyl) bicyclo [2.2.1] Hept-2-ene, 5-methoxybicyclo [2.2.1] hept-2-ene, 5-ethoxybicyclo [2.2.1] hept-2-ene, 5,6-dihydroxybicyclo [2.2 .1] Hept-2-ene, 5,6-di (hydroxymethyl) bicyclo [2.2.1] hept-2-ene, 5,6-di (2′-hydroxyethyl) bicyclo [2.2. 1] hept-2-ene, 5,6-dimethoxybicyclo [2.2 1] hept-2-ene, 5,6-diethoxybicyclo [2.2.1] hept-2-ene, 5-hydroxy-5-methylbicyclo [2.2.1] hept-2-ene, 5 -Hydroxy-5-ethylbicyclo [2.2.1] hept-2-ene, 5-hydroxymethyl-5-methylbicyclo [2.2.1] hept-2-ene, 5-tert-butoxycarbonylbicyclo [ 2.2.1] Hept-2-ene, 5-cyclohexyloxycarbonylbicyclo [2.2.1] hept-2-ene, 5-phenoxycarbonylbicyclo [2.2.1] hept-2-ene, 5 , 6-bis (tert-butoxycarbonyl) bicyclo [2.2.1] hept-2-ene, 5,6-bis (cyclohexyloxycarbonyl) bicyclo [2.2.1] hept-2-ene, etc. Bicyclounsaturated compounds;
N-phenylmaleimide, N-cyclohexylmaleimide, N-benzylmaleimide, N-succinimidyl-3-maleimidobenzoate, N-succinimidyl-4-maleimidobutyrate, N-succinimidyl-6-maleimidocaproate, N-succinimidyl-3 -Dicarbonylimide derivatives such as maleimide propionate, N- (9-acridinyl) maleimide;
Styrene, α-methylstyrene, m-methylstyrene, p-methylstyrene, vinyl toluene, p-methoxystyrene, acrylonitrile, methacrylonitrile, vinyl chloride, vinylidene chloride, acrylamide, methacrylamide, vinyl acetate, 1,3-butadiene , Isoprene and 2,3-dimethyl-1,3-butadiene.
Of these, styrene, vinyltoluene, N-phenylmaleimide, N-cyclohexylmaleimide and N-benzylmaleimide are preferable from the viewpoint of copolymerization reactivity and heat resistance.

樹脂［Ｋ１］において、それぞれに由来する構造単位の比率は、樹脂［Ｋ１］を構成する全構造単位中、
（ａ）に由来する構造単位；２〜６０モル％
（ｂ）に由来する構造単位；４０〜９８モル％
であることが好ましく、
（ａ）に由来する構造単位；１０〜５０モル％
（ｂ）に由来する構造単位；５０〜９０モル％
であることがより好ましい。
樹脂［Ｋ１］の構造単位の比率が、上記の範囲にあると、赤色着色硬化性樹脂組成物の保存安定性、着色パターンを形成する際の現像性、及び得られる着色パターンの耐溶剤性に優れる傾向がある。 In the resin [K1], the ratio of the structural unit derived from each is the total structural unit constituting the resin [K1]
Structural unit derived from (a); 2 to 60 mol%
Structural unit derived from (b); 40-98 mol%
It is preferable that
Structural unit derived from (a); 10-50 mol%
Structural unit derived from (b); 50-90 mol%
It is more preferable that
When the ratio of the structural unit of the resin [K1] is in the above range, the storage stability of the red colored curable resin composition, the developability when forming a colored pattern, and the solvent resistance of the resulting colored pattern are improved. There is a tendency to excel.

樹脂［Ｋ１］は、例えば、文献「高分子合成の実験法」（大津隆行著 発行所（株）化学同人 第１版第１刷 １９７２年３月１日発行）に記載された方法及び当該文献に記載された引用文献を参考にして製造することができる。   The resin [K1] is, for example, a method described in the document “Experimental Method for Polymer Synthesis” (Takayuki Otsu, published by Kagaku Dojin Co., Ltd., First Edition, First Edition, issued March 1, 1972) and the document Can be produced with reference to the cited references described in 1.

具体的には、（ａ）及び（ｂ）の所定量、重合開始剤及び溶剤等を反応容器中に入れて、例えば、窒素により酸素を置換することにより、脱酸素雰囲気にし、攪拌しながら、加熱及び保温する方法が挙げられる。なお、ここで用いられる重合開始剤及び溶剤等は、特に限定されず、当該分野で通常使用されているものを使用することができる。例えば、重合開始剤としては、アゾ化合物（２，２′−アゾビスイソブチロニトリル、２，２′−アゾビス（２，４−ジメチルバレロニトリル）等）や有機過酸化物（ベンゾイルペルオキシド等）が挙げられ、溶剤としては、各モノマーを溶解するものであればよく、本発明の赤色着色硬化性樹脂組成物の溶剤（Ｅ）として後述する溶剤等が挙げられる。   Specifically, a predetermined amount of (a) and (b), a polymerization initiator, a solvent, and the like are placed in a reaction vessel, for example, by substituting oxygen with nitrogen to create a deoxygenated atmosphere, with stirring, The method of heating and heat retention is mentioned. In addition, the polymerization initiator, the solvent, and the like used here are not particularly limited, and those usually used in the field can be used. For example, as polymerization initiators, azo compounds (2,2'-azobisisobutyronitrile, 2,2'-azobis (2,4-dimethylvaleronitrile), etc.) and organic peroxides (benzoyl peroxide, etc.) Any solvent may be used as long as it dissolves each monomer. Examples of the solvent (E) for the red colored curable resin composition of the present invention include the solvents described later.

なお、得られた共重合体は、反応後の溶液をそのまま使用してもよいし、濃縮あるいは希釈した溶液を使用してもよいし、再沈殿等の方法で固体（粉体）として取り出したものを使用してもよい。特に、この重合の際に溶剤として、本発明の赤色着色硬化性樹脂組成物に含まれる溶剤を使用することにより、反応後の溶液をそのまま本発明の赤色着色硬化性樹脂組成物の調製に使用することができるため、本発明の赤色着色硬化性樹脂組成物の製造工程を簡略化することができる。   In addition, the obtained copolymer may use the solution after reaction as it is, a concentrated or diluted solution may be used, and it took out as solid (powder) by methods, such as reprecipitation. Things may be used. In particular, by using the solvent contained in the red colored curable resin composition of the present invention as a solvent during the polymerization, the solution after the reaction is used as it is for the preparation of the red colored curable resin composition of the present invention. Therefore, the manufacturing process of the red colored curable resin composition of the present invention can be simplified.

樹脂［Ｋ２］において、それぞれに由来する構造単位の比率は、樹脂［Ｋ２］を構成する全構造単位中、
（ａ）に由来する構造単位；２〜４５モル％
（ｂ）に由来する構造単位；２〜９５モル％
（ｃ）に由来する構造単位；１〜６５モル％
であることが好ましく、
（ａ）に由来する構造単位；５〜４０モル％
（ｂ）に由来する構造単位；５〜８０モル％
（ｃ）に由来する構造単位；５〜６０モル％
であることがより好ましい。
樹脂［Ｋ２］の構造単位の比率が、上記の範囲にあると、赤色着色硬化性樹脂組成物の保存安定性、着色パターンを形成する際の現像性、並びに、得られる着色パターンの耐溶剤性、耐熱性及び機械強度に優れる傾向がある。 In the resin [K2], the ratio of the structural units derived from each of the structural units constituting the resin [K2]
Structural unit derived from (a); 2-45 mol%
Structural unit derived from (b); 2 to 95 mol%
Structural unit derived from (c); 1 to 65 mol%
It is preferable that
Structural unit derived from (a); 5 to 40 mol%
Structural unit derived from (b); 5 to 80 mol%
Structural unit derived from (c); 5 to 60 mol%
It is more preferable that
When the ratio of the structural unit of the resin [K2] is in the above range, the storage stability of the red colored curable resin composition, the developability when forming a colored pattern, and the solvent resistance of the resulting colored pattern , Tend to be excellent in heat resistance and mechanical strength.

樹脂［Ｋ２］は、例えば、樹脂［Ｋ１］の製造方法として記載した方法と同様に製造することができる。   Resin [K2] can be produced, for example, in the same manner as the method described as the production method of resin [K1].

樹脂［Ｋ３］において、それぞれに由来する構造単位の比率は、樹脂［Ｋ３］を構成する全構造単位中、
（ａ）に由来する構造単位；２〜６０モル％
（ｃ）に由来する構造単位；４０〜９８モル％
であることが好ましく、
（ａ）に由来する構造単位；１０〜５０モル％
（ｃ）に由来する構造単位；５０〜９０モル％
であることがより好ましい。
樹脂［Ｋ３］は、例えば、樹脂［Ｋ１］の製造方法として記載した方法と同様に製造することができる。 In the resin [K3], the proportion of structural units derived from each of the structural units constituting the resin [K3]
Structural unit derived from (a); 2 to 60 mol%
Structural unit derived from (c); 40 to 98 mol%
It is preferable that
Structural unit derived from (a); 10-50 mol%
Structural unit derived from (c); 50-90 mol%
It is more preferable that
Resin [K3] can be produced, for example, in the same manner as described for the production method of resin [K1].

樹脂［Ｋ４］は、（ａ）と（ｃ）との共重合体を得て、（ｂ）が有する炭素数２〜４の環状エーテルを（ａ）が有するカルボン酸及び／又はカルボン酸無水物に付加させることにより製造することができる。
まず（ａ）と（ｃ）との共重合体を、樹脂［Ｋ１］の製造方法として記載した方法と同様に製造する。この場合、それぞれに由来する構造単位の比率は、樹脂［Ｋ３］で挙げたもの同様の比率であることが好ましい。 Resin [K4] obtains a copolymer of (a) and (c), and (a) has a carboxylic acid and / or carboxylic acid anhydride having (a) a cyclic ether having 2 to 4 carbon atoms that (b) has It can manufacture by adding to.
First, a copolymer of (a) and (c) is produced in the same manner as described in the method for producing resin [K1]. In this case, the ratio of the structural units derived from each is preferably the same as that described for the resin [K3].

次に、前記共重合体中の（ａ）に由来するカルボン酸及び／又はカルボン酸無水物の一部に、（ｂ）が有する炭素数２〜４の環状エーテルを反応させる。
（ａ）と（ｃ）との共重合体の製造に引き続き、フラスコ内雰囲気を窒素から空気に置換し、（ｂ）、カルボン酸又はカルボン酸無水物と環状エーテルとの反応触媒（例えばトリス（ジメチルアミノメチル）フェノール等）及び重合禁止剤（例えばハイドロキノン等）等をフラスコ内に入れて、例えば、６０〜１３０℃で、１〜１０時間反応することにより、樹脂［Ｋ４］を製造することができる。
（ｂ）の使用量は、（ａ）１００モルに対して、５〜８０モルが好ましく、より好ましくは１０〜７５モルである。この範囲にすることにより、赤色着色硬化性樹脂組成物の保存安定性、パターンを形成する際の現像性、並びに、得られるパターンの耐溶剤性、耐熱性、機械強度及び感度のバランスが良好になる傾向がある。環状エーテルの反応性が高く、未反応の（ｂ）が残存しにくいことから、樹脂［Ｋ４］に用いる（ｂ）としては（ｂ１）が好ましく、さらに（ｂ１−１）が好ましい。
前記反応触媒の使用量は、（ａ）、（ｂ）及び（ｃ）の合計量１００質量部に対して０．００１〜５質量部が好ましい。前記重合禁止剤の使用量は、（ａ）、（ｂ）及び（ｃ）の合計量１００質量部に対して０．００１〜５質量部が好ましい。
仕込方法、反応温度及び時間等の反応条件は、製造設備や重合による発熱量等を考慮して適宜調整することができる。なお、重合条件と同様に、製造設備や重合による発熱量等を考慮し、仕込方法や反応温度を適宜調整することができる。 Next, the C2-C4 cyclic ether which (b) has is reacted with a part of the carboxylic acid and / or carboxylic anhydride derived from (a) in the copolymer.
Subsequent to the production of the copolymer of (a) and (c), the atmosphere in the flask is replaced from nitrogen to air, and (b) a reaction catalyst of carboxylic acid or carboxylic anhydride and cyclic ether (for example, tris ( Dimethylaminomethyl) phenol, etc.) and a polymerization inhibitor (eg, hydroquinone, etc.) are placed in a flask and reacted, for example, at 60-130 ° C. for 1-10 hours to produce resin [K4]. it can.
The amount of (b) used is preferably 5 to 80 mol, more preferably 10 to 75 mol, per 100 mol of (a). By making this range, the storage stability of the red colored curable resin composition, the developability when forming the pattern, and the balance of the solvent resistance, heat resistance, mechanical strength and sensitivity of the resulting pattern are good. Tend to be. Since the reactivity of the cyclic ether is high and unreacted (b) hardly remains, (b1) is preferable as (b) used for the resin [K4], and (b1-1) is more preferable.
The amount of the reaction catalyst used is preferably 0.001 to 5 parts by mass with respect to 100 parts by mass of the total amount of (a), (b) and (c). The amount of the polymerization inhibitor used is preferably 0.001 to 5 parts by mass with respect to 100 parts by mass of the total amount of (a), (b) and (c).
The reaction conditions such as the charging method, reaction temperature, and time can be appropriately adjusted in consideration of the production equipment and the amount of heat generated by polymerization. In addition, like the polymerization conditions, the charging method and the reaction temperature can be appropriately adjusted in consideration of the production equipment, the amount of heat generated by the polymerization, and the like.

樹脂［Ｋ５］は、第一段階として、上述した樹脂［Ｋ１］の製造方法と同様にして、（ｂ）と（ｃ）との共重合体を得る。上記と同様に、得られた共重合体は、反応後の溶液をそのまま使用してもよいし、濃縮あるいは希釈した溶液を使用してもよいし、再沈殿等の方法で固体（粉体）として取り出したものを使用してもよい。
（ｂ）及び（ｃ）に由来する構造単位の比率は、前記の共重合体を構成する全構造単位の合計モル数に対して、以下の範囲にあることが好ましい。
（ｂ）に由来する構造単位；５〜９５モル％
（ｃ）に由来する構造単位；５〜９５モル％
であることが好ましく、
（ｂ）に由来する構造単位；１０〜９０モル％
（ｃ）に由来する構造単位；１０〜９０モル％
であることがより好ましい。 Resin [K5] obtains a copolymer of (b) and (c) as a first step in the same manner as in the method for producing resin [K1] described above. Similarly to the above, the obtained copolymer may be used as it is after the reaction, or may be a concentrated or diluted solution, or may be solid (powder) by a method such as reprecipitation. You may use what was taken out as.
The ratio of the structural units derived from (b) and (c) is preferably in the following range with respect to the total number of moles of all structural units constituting the copolymer.
Structural unit derived from (b); 5-95 mol%
Structural unit derived from (c); 5-95 mol%
It is preferable that
Structural unit derived from (b); 10-90 mol%
Structural unit derived from (c); 10 to 90 mol%
It is more preferable that

さらに、樹脂［Ｋ４］の製造方法と同様の条件で、（ｂ）と（ｃ）との共重合体が有する（ｂ）に由来する環状エーテルに、（ａ）が有するカルボン酸又はカルボン酸無水物を反応させることにより、樹脂［Ｋ５］を得ることができる。
前記の共重合体に反応させる（ａ）の使用量は、（ｂ）１００モルに対して、５〜８０モルが好ましい。環状エーテルの反応性が高く、未反応の（ｂ）が残存しにくいことから、樹脂［Ｋ５］に用いる（ｂ）としては（ｂ１）が好ましく、さらに（ｂ１−１）が好ましい。 Further, under the same conditions as in the method for producing the resin [K4], the cyclic ether derived from (b) of the copolymer of (b) and (c) is added to the carboxylic acid or carboxylic acid anhydride of (a). Resin [K5] can be obtained by reacting the product.
As for the usage-amount of (a) made to react with the said copolymer, 5-80 mol is preferable with respect to 100 mol of (b). Since the reactivity of the cyclic ether is high and unreacted (b) hardly remains, (b1) is preferable as (b) used for the resin [K5], and (b1-1) is more preferable.

樹脂［Ｋ６］は、樹脂［Ｋ５］に、さらにカルボン酸無水物を反応させた樹脂である。
環状エーテルとカルボン酸又はカルボン酸無水物との反応により発生するヒドロキシ基に、カルボン酸無水物を反応させる。
カルボン酸無水物としては、無水マレイン酸、シトラコン酸無水物、イタコン酸無水物、３−ビニルフタル酸無水物、４−ビニルフタル酸無水物、３，４，５，６−テトラヒドロフタル酸無水物、１，２，３，６−テトラヒドロフタル酸無水物、ジメチルテトラヒドロフタル酸無水物、５，６−ジカルボキシビシクロ［２．２．１］ヘプト−２−エン無水物（ハイミック酸無水物）等が挙げられる。カルボン酸無水物の使用量は、（ａ）の使用量１モルに対して、０．５〜１モルが好ましい。 Resin [K6] is a resin obtained by further reacting carboxylic anhydride with resin [K5].
Carboxylic anhydride is reacted with a hydroxy group generated by reaction of cyclic ether with carboxylic acid or carboxylic anhydride.
Carboxylic anhydrides include maleic anhydride, citraconic anhydride, itaconic anhydride, 3-vinylphthalic anhydride, 4-vinylphthalic anhydride, 3,4,5,6-tetrahydrophthalic anhydride, 1 2,3,6-tetrahydrophthalic anhydride, dimethyltetrahydrophthalic anhydride, 5,6-dicarboxybicyclo [2.2.1] hept-2-ene anhydride (highmic acid anhydride) and the like. It is done. As for the usage-amount of carboxylic acid anhydride, 0.5-1 mol is preferable with respect to 1 mol of usage-amount of (a).

樹脂（Ｂ）としては、具体的に、３，４−エポキシシクロヘキシルメチル（メタ）アクリレート／（メタ）アクリル酸共重合体、３，４−エポキシトリシクロ［５．２．１．０２．６］デシルアクリレート／（メタ）アクリル酸共重合体等の樹脂［Ｋ１］；グリシジル（メタ）アクリレート／ベンジル（メタ）アクリレート／（メタ）アクリル酸共重合体、グリシジル（メタ）アクリレート／スチレン／（メタ）アクリル酸共重合体、３，４−エポキシトリシクロ［５．２．１．０２．６］デシルアクリレート／（メタ）アクリル酸／Ｎ−シクロヘキシルマレイミド共重合体、３，４−エポキシトリシクロ［５．２．１．０２．６］デシルアクリレート／（メタ）アクリル酸／ビニルトルエン／ジシクロペンテニル（メタ）アクリレート共重合体、３−メチル−３−（メタ）アクリルロイルオキシメチルオキセタン／（メタ）アクリル酸／スチレン共重合体等の樹脂［Ｋ２］；ベンジル（メタ）アクリレート／（メタ）アクリル酸共重合体、スチレン／（メタ）アクリル酸共重合体等の樹脂［Ｋ３］；ベンジル（メタ）アクリレート／（メタ）アクリル酸共重合体にグリシジル（メタ）アクリレートを付加させた樹脂、トリシクロデシル（メタ）アクリレート／スチレン／（メタ）アクリル酸共重合体にグリシジル（メタ）アクリレートを付加させた樹脂、トリシクロデシル（メタ）アクリレート／ベンジル（メタ）アクリレート／（メタ）アクリル酸共重合体にグリシジル（メタ）アクリレートを付加させた樹脂等の樹脂［Ｋ４］；トリシクロデシル（メタ）アクリレート/グリシジル（メタ）アクリレートの共重合体に（メタ）アクリル酸を反応させた樹脂、トリシクロデシル（メタ）アクリレート/スチレン/グリシジル（メタ）アクリレートの共重合体に（メタ）アクリル酸を反応させた樹脂等の樹脂［Ｋ５］；トリシクロデシル（メタ）アクリレート/グリシジル（メタ）アクリレートの共重合体に（メタ）アクリル酸を反応させた樹脂にさらにテトラヒドロフタル酸無水物を反応させた樹脂等の樹脂［Ｋ６］等が挙げられる。 Specific examples of the resin (B) include 3,4-epoxycyclohexylmethyl (meth) acrylate / (meth) acrylic acid copolymer, 3,4-epoxytricyclo [5.2.1.0 2.6. ] Resin such as decyl acrylate / (meth) acrylic acid copolymer [K1]; glycidyl (meth) acrylate / benzyl (meth) acrylate / (meth) acrylic acid copolymer, glycidyl (meth) acrylate / styrene / (meta ) Acrylic acid copolymer, 3,4-epoxytricyclo [5.2.1.0 2.6 ] decyl acrylate / (meth) acrylic acid / N-cyclohexylmaleimide copolymer, 3,4-epoxytricyclo [5.2.1.0 2.6] decyl acrylate / (meth) acrylic acid / vinyl toluene / dicyclopentenyl (meth) acrylate Polymer, resin such as 3-methyl-3- (meth) acryloyloxymethyloxetane / (meth) acrylic acid / styrene copolymer [K2]; benzyl (meth) acrylate / (meth) acrylic acid copolymer, Resin [K3] such as styrene / (meth) acrylic acid copolymer; resin obtained by adding glycidyl (meth) acrylate to benzyl (meth) acrylate / (meth) acrylic acid copolymer, tricyclodecyl (meth) acrylate / Styrene / (meth) acrylic acid copolymer added with glycidyl (meth) acrylate, tricyclodecyl (meth) acrylate / benzyl (meth) acrylate / (meth) acrylic acid copolymer with glycidyl (meth) Resin such as acrylate-added resin [K4]; Tricyclodecyl (meth) acrylate / g Residue obtained by reacting (meth) acrylic acid with a copolymer of sidyl (meth) acrylate, and (meth) acrylic acid reacted with a copolymer of tricyclodecyl (meth) acrylate / styrene / glycidyl (meth) acrylate Resins such as resin [K5]; resins obtained by reacting a copolymer of tricyclodecyl (meth) acrylate / glycidyl (meth) acrylate with (meth) acrylic acid and further reacting with tetrahydrophthalic anhydride Resin [K6] etc. are mentioned.

中でも、樹脂（Ｂ）としては、樹脂［Ｋ１］、樹脂［Ｋ２］及び樹脂［Ｋ３］が好ましい。   Especially, as resin (B), resin [K1], resin [K2], and resin [K3] are preferable.

樹脂（Ｂ）のポリスチレン換算の重量平均分子量は、好ましくは３，０００〜１００，０００であり、より好ましくは５，０００〜５０，０００であり、さらに好ましくは５，０００〜３０，０００である。分子量が前記の範囲内にあると、塗膜硬度が向上し、残膜率も高く、未露光部の現像液に対する溶解性が良好で、解像度が向上する傾向がある。
樹脂（Ｂ）の分子量分布［重量平均分子量（Ｍｗ）／数平均分子量（Ｍｎ）］は、好ましくは１．１〜６であり、より好ましくは１．２〜４である。 The polystyrene equivalent weight average molecular weight of the resin (B) is preferably 3,000 to 100,000, more preferably 5,000 to 50,000, and further preferably 5,000 to 30,000. . When the molecular weight is within the above range, the coating film hardness is improved, the residual film ratio is high, the solubility of the unexposed portion in the developer is good, and the resolution tends to be improved.
The molecular weight distribution [weight average molecular weight (Mw) / number average molecular weight (Mn)] of the resin (B) is preferably 1.1 to 6, and more preferably 1.2 to 4.

樹脂（Ｂ）の酸価は、好ましくは５０〜１７０ｍｇ−ＫＯＨ／ｇであり、より好ましくは６０〜１５０−ＫＯＨ／ｇ、さらに好ましくは７０〜１３５ｍｇ−ＫＯＨ／ｇである。ここで酸価は樹脂１ｇを中和するに必要な水酸化カリウムの量（ｍｇ）として測定される値であり、例えば水酸化カリウム水溶液を用いて滴定することにより求めることができる。   The acid value of the resin (B) is preferably 50 to 170 mg-KOH / g, more preferably 60 to 150-KOH / g, and still more preferably 70 to 135 mg-KOH / g. Here, the acid value is a value measured as the amount (mg) of potassium hydroxide necessary to neutralize 1 g of the resin, and can be determined by titration using, for example, an aqueous potassium hydroxide solution.

樹脂（Ｂ）の含有量は、赤色着色硬化性樹脂組成物の固形分に対して、好ましくは７〜６５質量％であり、より好ましくは１３〜６０質量％であり、さらに好ましくは１７〜５５質量％である。樹脂（Ｂ）の含有量が、前記の範囲にあると、未露光部の現像液に対する溶解性が高い傾向がある。   Content of resin (B) becomes like this. Preferably it is 7-65 mass% with respect to solid content of a red coloring curable resin composition, More preferably, it is 13-60 mass%, More preferably, it is 17-55. % By mass. When content of resin (B) exists in the said range, there exists a tendency for the solubility with respect to the developing solution of an unexposed part to be high.

＜重合性化合物（Ｃ）＞
重合性化合物（Ｃ）は、光や熱の作用により重合開始剤（Ｄ）から発生した活性ラジカル及び／又は酸等によって重合し得る化合物であって、例えば、重合性のエチレン性不飽和結合を有する化合物等が挙げられ、好ましくは（メタ）アクリル酸エステル化合物が挙げられる。 <Polymerizable compound (C)>
The polymerizable compound (C) is a compound that can be polymerized by active radicals and / or acids generated from the polymerization initiator (D) by the action of light or heat, and includes, for example, a polymerizable ethylenically unsaturated bond. The compound etc. which have are mentioned, Preferably a (meth) acrylic acid ester compound is mentioned.

前記重合性化合物（Ｃ）としては、エチレン性不飽和結合を３つ以上有する重合性化合物が好ましい。このような重合性化合物としては、トリメチロールプロパントリ（メタ）アクリレート、ペンタエリスリトールテトラ（メタ）アクリレート、ジペンタエリスリトールペンタ（メタ）アクリレート、ジペンタエリスリトールヘキサ（メタ）アクリレート、トリペンタエリスリトールオクタ（メタ）アクリレート、トリペンタエリスリトールヘプタ（メタ）アクリレート、テトラペンタエリスリトールデカ（メタ）アクリレート、テトラペンタエリスリトールノナ（メタ）アクリレート、トリス（２−（メタ）アクリロイルオキシエチル）イソシアヌレート、エチレングリコール変性ペンタエリスリトールテトラ（メタ）アクリレート、エチレングリコール変性ジペンタエリスリトールヘキサ（メタ）アクリレート、プロピレングリコール変性ペンタエリスリトールテトラ（メタ）アクリレート、プロピレングリコール変性ジペンタエリスリトールヘキサ（メタ）アクリレート、カプロラクトン変性ペンタエリスリトールテトラ（メタ）アクリレート及びカプロラクトン変性ジペンタエリスリトールヘキサ（メタ）アクリレートが挙げられる。中でも、ジペンタエリスリトールペンタ（メタ）アクリレート及びジペンタエリスリトールヘキサ（メタ）アクリレートが好ましい。   As the polymerizable compound (C), a polymerizable compound having three or more ethylenically unsaturated bonds is preferable. Such polymerizable compounds include trimethylolpropane tri (meth) acrylate, pentaerythritol tetra (meth) acrylate, dipentaerythritol penta (meth) acrylate, dipentaerythritol hexa (meth) acrylate, tripentaerythritol octa (meth) ) Acrylate, tripentaerythritol hepta (meth) acrylate, tetrapentaerythritol deca (meth) acrylate, tetrapentaerythritol nona (meth) acrylate, tris (2- (meth) acryloyloxyethyl) isocyanurate, ethylene glycol modified pentaerythritol tetra (Meth) acrylate, ethylene glycol modified dipentaerythritol hexa (meth) acrylate, propylene glycol modified Pentaerythritol tetra (meth) acrylate, propylene glycol-modified dipentaerythritol hexa (meth) acrylate, caprolactone-modified pentaerythritol tetra (meth) acrylate and caprolactone-modified dipentaerythritol hexa (meth) acrylate. Of these, dipentaerythritol penta (meth) acrylate and dipentaerythritol hexa (meth) acrylate are preferable.

重合性化合物（Ｃ）の含有量は、固形分の総量に対して、７〜６５質量％であることが好ましく、より好ましくは１３〜６０質量％であり、さらに好ましくは１７〜５５質量％である。重合性化合物（Ｃ）の含有量が、前記の範囲にあると、着色パターンの残膜率及び耐薬品性が向上する傾向がある。   The content of the polymerizable compound (C) is preferably 7 to 65% by mass, more preferably 13 to 60% by mass, and further preferably 17 to 55% by mass with respect to the total amount of the solid content. is there. When the content of the polymerizable compound (C) is in the above range, the remaining film ratio and chemical resistance of the colored pattern tend to be improved.

＜重合開始剤（Ｄ）＞
重合開始剤（Ｄ）は、光や熱の作用により活性ラジカル、酸等を発生し、重合を開始しうる化合物であれば特に限定されることなく、公知の重合開始剤を用いることができる。
重合開始剤（Ｄ）としては、アルキルフェノン化合物、トリアジン化合物、アシルホスフィンオキサイド化合物、Ｏ−アシルオキシム化合物及びビイミダゾール化合物が挙げられる。 <Polymerization initiator (D)>
The polymerization initiator (D) is not particularly limited as long as it is a compound capable of generating an active radical, an acid or the like by the action of light or heat and initiating polymerization, and a known polymerization initiator can be used.
Examples of the polymerization initiator (D) include alkylphenone compounds, triazine compounds, acylphosphine oxide compounds, O-acyloxime compounds, and biimidazole compounds.

Ｏ−アシルオキシム化合物は、式（ｄ１）で表される部分構造を有する化合物である。
以下、＊は結合手を表す。

Figure 0006461453
Ｏ−アシルオキシム化合物としては、Ｎ−ベンゾイルオキシ−１−（４−フェニルスルファニルフェニル）ブタン−１−オン−２−イミン、Ｎ−ベンゾイルオキシ−１−（４−フェニルスルファニルフェニル）オクタン−１−オン−２−イミン、Ｎ−ベンゾイルオキシ−１−（４−フェニルスルファニルフェニル）−３−シクロペンチルプロパン−１−オン−２−イミン、Ｎ−アセトキシ−１−［９−エチル−６−（２−メチルベンゾイル）−９Ｈ−カルバゾール−３−イル］エタン−１−イミン、Ｎ−アセトキシ−１−［９−エチル−６−｛２−メチル−４−（３，３−ジメチル−２，４−ジオキサシクロペンタニルメチルオキシ）ベンゾイル｝−９Ｈ−カルバゾール−３−イル］エタン−１−イミン、Ｎ−アセトキシ−１−［９−エチル−６−（２−メチルベンゾイル）−９Ｈ−カルバゾール−３−イル］−３−シクロペンチルプロパン−１−イミン及びＮ−ベンゾイルオキシ−１−［９−エチル−６−（２−メチルベンゾイル）−９Ｈ−カルバゾール−３−イル］−３−シクロペンチルプロパン−１−オン−２−イミンが挙げられる。イルガキュア（登録商標）ＯＸＥ０１、ＯＸＥ０２（以上、ＢＡＳＦ社製）、Ｎ−１９１９（ＡＤＥＫＡ社製）等の市販品を用いてもよい。 The O-acyl oxime compound is a compound having a partial structure represented by the formula (d1).
Hereinafter, * represents a bond.
Figure 0006461453
Examples of O-acyloxime compounds include N-benzoyloxy-1- (4-phenylsulfanylphenyl) butan-1-one-2-imine, N-benzoyloxy-1- (4-phenylsulfanylphenyl) octane-1- On-2-imine, N-benzoyloxy-1- (4-phenylsulfanylphenyl) -3-cyclopentylpropane-1-one-2-imine, N-acetoxy-1- [9-ethyl-6- (2- Methylbenzoyl) -9H-carbazol-3-yl] ethane-1-imine, N-acetoxy-1- [9-ethyl-6- {2-methyl-4- (3,3-dimethyl-2,4-di) Oxacyclopentanylmethyloxy) benzoyl} -9H-carbazol-3-yl] ethane-1-imine, N-acetoxy-1- [9-ethyl 6- (2-Methylbenzoyl) -9H-carbazol-3-yl] -3-cyclopentylpropane-1-imine and N-benzoyloxy-1- [9-ethyl-6- (2-methylbenzoyl) -9H- Carbazol-3-yl] -3-cyclopentylpropan-1-one-2-imine. Commercial products such as Irgacure (registered trademark) OXE01, OXE02 (above, manufactured by BASF), N-1919 (manufactured by ADEKA) may be used.

アルキルフェノン化合物は、式（ｄ２）で表される部分構造又は式（ｄ３）で表される部分構造を有する化合物である。これらの部分構造におけるベンゼン環は置換基を有していてもよい。

Figure 0006461453
The alkylphenone compound is a compound having a partial structure represented by the formula (d2) or a partial structure represented by the formula (d3). The benzene ring in these partial structures may have a substituent.
Figure 0006461453

式（ｄ２）で表される部分構造を有する化合物としては、２−メチル−２−モルホリノ−１−（４−メチルスルファニルフェニル）プロパン−１−オン、２−ジメチルアミノ−１−（４−モルホリノフェニル）−２−ベンジルブタン−１−オン及び２−（ジメチルアミノ）−２−［（４−メチルフェニル）メチル］−１−［４−（４−モルホリニル）フェニル］ブタン−１−オンが挙げられる。イルガキュア（登録商標）３６９、９０７及び３７９（以上、ＢＡＳＦ社製）等の市販品を用いてもよい。
式（ｄ３）で表される部分構造を有する化合物としては、２−ヒドロキシ−２−メチル−１−フェニルプロパン−１−オン、２−ヒドロキシ−２−メチル−１−〔４−（２−ヒドロキシエトキシ）フェニル〕プロパン−１−オン、１−ヒドロキシシクロヘキシルフェニルケトン、２−ヒドロキシ−２−メチル−１−（４−イソプロペニルフェニル）プロパン−１−オンのオリゴマー、α，α−ジエトキシアセトフェノン及びベンジルジメチルケタールが挙げられる。
感度の点で、アルキルフェノン化合物としては、式（ｄ２）で表される部分構造を有する化合物が好ましい。 Examples of the compound having a partial structure represented by the formula (d2) include 2-methyl-2-morpholino-1- (4-methylsulfanylphenyl) propan-1-one, 2-dimethylamino-1- (4-morpholino Phenyl) -2-benzylbutan-1-one and 2- (dimethylamino) -2-[(4-methylphenyl) methyl] -1- [4- (4-morpholinyl) phenyl] butan-1-one. It is done. Commercial products such as Irgacure (registered trademark) 369, 907 and 379 (manufactured by BASF) may be used.
Examples of the compound having a partial structure represented by the formula (d3) include 2-hydroxy-2-methyl-1-phenylpropan-1-one, 2-hydroxy-2-methyl-1- [4- (2-hydroxy Ethoxy) phenyl] propan-1-one, 1-hydroxycyclohexyl phenyl ketone, oligomers of 2-hydroxy-2-methyl-1- (4-isopropenylphenyl) propan-1-one, α, α-diethoxyacetophenone and A benzyl dimethyl ketal is mentioned.
In terms of sensitivity, the alkylphenone compound is preferably a compound having a partial structure represented by the formula (d2).

トリアジン化合物としては、２，４−ビス（トリクロロメチル）−６−（４−メトキシフェニル）−１，３，５−トリアジン、２，４−ビス（トリクロロメチル）−６−（４−メトキシナフチル）−１，３，５−トリアジン、２，４−ビス（トリクロロメチル）−６−ピペロニル−１，３，５−トリアジン、２，４−ビス（トリクロロメチル）−６−(４−メトキシスチリル)−１，３，５−トリアジン、２，４−ビス（トリクロロメチル）−６−〔２−（５−メチルフラン−２−イル）エテニル〕−１，３，５−トリアジン、２，４−ビス（トリクロロメチル）−６−〔２−（フラン−２−イル）エテニル〕−１，３，５−トリアジン、２，４−ビス（トリクロロメチル）−６−〔２−（４−ジエチルアミノ−２−メチルフェニル）エテニル〕−１，３，５−トリアジン及び２，４−ビス（トリクロロメチル）−６−〔２−（３，４−ジメトキシフェニル）エテニル〕−１，３，５−トリアジンが挙げられる。   As triazine compounds, 2,4-bis (trichloromethyl) -6- (4-methoxyphenyl) -1,3,5-triazine, 2,4-bis (trichloromethyl) -6- (4-methoxynaphthyl) -1,3,5-triazine, 2,4-bis (trichloromethyl) -6-piperonyl-1,3,5-triazine, 2,4-bis (trichloromethyl) -6- (4-methoxystyryl)- 1,3,5-triazine, 2,4-bis (trichloromethyl) -6- [2- (5-methylfuran-2-yl) ethenyl] -1,3,5-triazine, 2,4-bis ( Trichloromethyl) -6- [2- (furan-2-yl) ethenyl] -1,3,5-triazine, 2,4-bis (trichloromethyl) -6- [2- (4-diethylamino-2-methyl) Phenyl) ethenyl -1,3,5-triazine and 2,4-bis (trichloromethyl) -6- [2- (3,4-dimethoxyphenyl) ethenyl] -1,3,5-triazine.

アシルホスフィンオキサイド化合物としては、２，４，６−トリメチルベンゾイルジフェニルホスフィンオキサイドが挙げられる。イルガキュア（登録商標）８１９（ＢＡＳＦ社製）等の市販品を用いてもよい。   Examples of the acyl phosphine oxide compound include 2,4,6-trimethylbenzoyldiphenylphosphine oxide. Commercial products such as Irgacure (registered trademark) 819 (manufactured by BASF) may be used.

ビイミダゾール化合物としては、２，２’−ビス（２−クロロフェニル）−４，４’，５，５’−テトラフェニルビイミダゾール、２，２’−ビス（２，３−ジクロロフェニル）−４，４’，５，５’−テトラフェニルビイミダゾール（例えば、特開平６−７５３７２号公報、特開平６−７５３７３号公報等参照。）、２，２’−ビス（２−クロロフェニル）−４，４’，５，５’−テトラフェニルビイミダゾール、２，２’−ビス（２−クロロフェニル）−４，４’，５，５’−テトラ（アルコキシフェニル）ビイミダゾール、２，２’−ビス（２−クロロフェニル）−４，４’，５，５’−テトラ（ジアルコキシフェニル）ビイミダゾール、２，２’−ビス（２−クロロフェニル）−４，４’，５，５’−テトラ（トリアルコキシフェニル）ビイミダゾール（例えば、特公昭４８−３８４０３号公報、特開昭６２−１７４２０４号公報等参照。）及び４，４’５，５’−位のフェニル基がカルボアルコキシ基により置換されているイミダゾール化合物（例えば、特開平７−１０９１３号公報等参照）が挙げられる。   Examples of the biimidazole compound include 2,2′-bis (2-chlorophenyl) -4,4 ′, 5,5′-tetraphenylbiimidazole and 2,2′-bis (2,3-dichlorophenyl) -4,4. ', 5,5'-tetraphenylbiimidazole (see, for example, JP-A-6-75372 and JP-A-6-75373), 2,2'-bis (2-chlorophenyl) -4,4' , 5,5′-tetraphenylbiimidazole, 2,2′-bis (2-chlorophenyl) -4,4 ′, 5,5′-tetra (alkoxyphenyl) biimidazole, 2,2′-bis (2- Chlorophenyl) -4,4 ′, 5,5′-tetra (dialkoxyphenyl) biimidazole, 2,2′-bis (2-chlorophenyl) -4,4 ′, 5,5′-tetra (trialkoxypheny ) Biimidazole (see, for example, JP-B-48-38403, JP-A-62-174204, etc.) and imidazole in which the phenyl group at the 4,4′5,5′-position is substituted with a carboalkoxy group Compounds (for example, see JP-A-7-10913).

さらに重合開始剤（Ｄ）としては、ベンゾイン、ベンゾインメチルエーテル、ベンゾインエチルエーテル、ベンゾインイソプロピルエーテル、ベンゾインイソブチルエーテル等のベンゾイン化合物；ベンゾフェノン、ｏ−ベンゾイル安息香酸メチル、４−フェニルベンゾフェノン、４−ベンゾイル−４’−メチルジフェニルサルファイド、３，３’，４，４’−テトラ（ｔｅｒｔ−ブチルパーオキシカルボニル）ベンゾフェノン、２，４，６−トリメチルベンゾフェノン等のベンゾフェノン化合物；９，１０−フェナンスレンキノン、２−エチルアントラキノン、カンファーキノン等のキノン化合物；１０−ブチル−２−クロロアクリドン、ベンジル、フェニルグリオキシル酸メチル及びチタノセン化合物が挙げられる。これらは、後述の重合開始助剤（Ｄ１）（特にアミン類）と組み合わせて用いることが好ましい。   Furthermore, as the polymerization initiator (D), benzoin compounds such as benzoin, benzoin methyl ether, benzoin ethyl ether, benzoin isopropyl ether, benzoin isobutyl ether; benzophenone, methyl o-benzoylbenzoate, 4-phenylbenzophenone, 4-benzoyl- Benzophenone compounds such as 4′-methyldiphenyl sulfide, 3,3 ′, 4,4′-tetra (tert-butylperoxycarbonyl) benzophenone, 2,4,6-trimethylbenzophenone; 9,10-phenanthrenequinone, Examples include quinone compounds such as 2-ethylanthraquinone and camphorquinone; 10-butyl-2-chloroacridone, benzyl, methyl phenylglyoxylate, and titanocene compounds. These are preferably used in combination with a polymerization initiation assistant (D1) (particularly amines) described later.

酸発生剤としては、４−ヒドロキシフェニルジメチルスルホニウムｐ−トルエンスルホナート、４−ヒドロキシフェニルジメチルスルホニウムヘキサフルオロアンチモネート、４−アセトキシフェニルジメチルスルホニウムｐ−トルエンスルホナート、４−アセトキシフェニル・メチル・ベンジルスルホニウムヘキサフルオロアンチモネート、トリフェニルスルホニウムｐ−トルエンスルホナート、トリフェニルスルホニウムヘキサフルオロアンチモネート、ジフェニルヨードニウムｐ−トルエンスルホナート、ジフェニルヨードニウムヘキサフルオロアンチモネート等のオニウム塩類や、ニトロベンジルトシレート類及びベンゾイントシレート類が挙げられる。   Examples of acid generators include 4-hydroxyphenyldimethylsulfonium p-toluenesulfonate, 4-hydroxyphenyldimethylsulfonium hexafluoroantimonate, 4-acetoxyphenyldimethylsulfonium p-toluenesulfonate, 4-acetoxyphenyl methyl benzylsulfonium. Onium salts such as hexafluoroantimonate, triphenylsulfonium p-toluenesulfonate, triphenylsulfonium hexafluoroantimonate, diphenyliodonium p-toluenesulfonate, diphenyliodonium hexafluoroantimonate, nitrobenzyl tosylate and benzoin tosylate Rates.

重合開始剤（Ｄ）としては、アルキルフェノン化合物、トリアジン化合物、アシルホスフィンオキサイド化合物、Ｏ−アシルオキシム化合物及びビイミダゾール化合物からなる群から選ばれる少なくとも１種を含む重合開始剤が好ましく、Ｏ−アシルオキシム化合物を含む重合開始剤がより好ましく、Ｏ−アシルオキシム化合物及びアルキルフェノン化合物を含む重合開始剤がさらに好ましい。   The polymerization initiator (D) is preferably a polymerization initiator containing at least one selected from the group consisting of alkylphenone compounds, triazine compounds, acylphosphine oxide compounds, O-acyloxime compounds and biimidazole compounds, and O-acyloxy compounds. More preferred is a polymerization initiator containing an oxime compound, and more preferred is a polymerization initiator containing an O-acyloxime compound and an alkylphenone compound.

重合開始剤（Ｄ）の含有量は、樹脂（Ｂ）及び重合性化合物（Ｃ）の合計量１００質量部に対して、好ましくは０．１〜３０質量部であり、より好ましくは１〜２０質量部である。重合開始剤（Ｄ）の含有量が、前記の範囲にあると、高感度化して露光時間が短縮される傾向があるため生産性が向上する。   The content of the polymerization initiator (D) is preferably 0.1 to 30 parts by mass, more preferably 1 to 20 parts per 100 parts by mass of the total amount of the resin (B) and the polymerizable compound (C). Part by mass. When the content of the polymerization initiator (D) is in the above range, the sensitivity is increased and the exposure time tends to be shortened, so that productivity is improved.

＜重合開始助剤（Ｄ１）＞
重合開始助剤（Ｄ１）は、重合開始剤によって重合が開始された光重合性化合物の重合を促進するために用いられる化合物、もしくは増感剤である。重合開始助剤（Ｄ１）を含む場合、通常、重合開始剤（Ｄ）と組み合わせて用いられる。
重合開始助剤（Ｄ１）としては、アミン化合物、アルコキシアントラセン化合物、チオキサントン化合物及びカルボン酸化合物が挙げられる。 <Polymerization initiation aid (D1)>
The polymerization initiation assistant (D1) is a compound or a sensitizer used for accelerating the polymerization of the photopolymerizable compound that has been polymerized by the polymerization initiator. When the polymerization initiation assistant (D1) is included, it is usually used in combination with the polymerization initiator (D).
Examples of the polymerization initiation assistant (D1) include amine compounds, alkoxyanthracene compounds, thioxanthone compounds, and carboxylic acid compounds.

アミン化合物としては、トリエタノールアミン、メチルジエタノールアミン、トリイソプロパノールアミン、４−ジメチルアミノ安息香酸メチル、４−ジメチルアミノ安息香酸エチル、４−ジメチルアミノ安息香酸イソアミル、安息香酸２−ジメチルアミノエチル、４−ジメチルアミノ安息香酸２−エチルヘキシル、Ｎ，Ｎ−ジメチルパラトルイジン、４，４’−ビス（ジメチルアミノ）ベンゾフェノン（通称ミヒラーズケトン）、４，４’−ビス（ジエチルアミノ）ベンゾフェノン及び４，４’−ビス（エチルメチルアミノ）ベンゾフェノンが挙げられ、中でも４，４’−ビス（ジエチルアミノ）ベンゾフェノンが好ましい。ＥＡＢ−Ｆ（保土谷化学工業（株）製）等の市販品を用いてもよい。   Examples of amine compounds include triethanolamine, methyldiethanolamine, triisopropanolamine, methyl 4-dimethylaminobenzoate, ethyl 4-dimethylaminobenzoate, isoamyl 4-dimethylaminobenzoate, 2-dimethylaminoethyl benzoate, 4- 2-ethylhexyl dimethylaminobenzoate, N, N-dimethylparatoluidine, 4,4′-bis (dimethylamino) benzophenone (commonly known as Michler's ketone), 4,4′-bis (diethylamino) benzophenone and 4,4′-bis ( Ethylmethylamino) benzophenone, and 4,4′-bis (diethylamino) benzophenone is preferred. Commercial products such as EAB-F (Hodogaya Chemical Co., Ltd.) may be used.

アルコキシアントラセン化合物としては、９，１０−ジメトキシアントラセン、２−エチル−９，１０−ジメトキシアントラセン、９，１０−ジエトキシアントラセン、２−エチル−９，１０−ジエトキシアントラセン、９，１０−ジブトキシアントラセン及び２−エチル−９，１０−ジブトキシアントラセンが挙げられる。   Examples of the alkoxyanthracene compound include 9,10-dimethoxyanthracene, 2-ethyl-9,10-dimethoxyanthracene, 9,10-diethoxyanthracene, 2-ethyl-9,10-diethoxyanthracene, and 9,10-dibutoxy. Anthracene and 2-ethyl-9,10-dibutoxyanthracene are mentioned.

チオキサントン化合物としては、２−イソプロピルチオキサントン、４−イソプロピルチオキサントン、２，４−ジエチルチオキサントン、２，４−ジクロロチオキサントン及び１−クロロ−４−プロポキシチオキサントンが挙げられる。   Examples of the thioxanthone compound include 2-isopropylthioxanthone, 4-isopropylthioxanthone, 2,4-diethylthioxanthone, 2,4-dichlorothioxanthone, and 1-chloro-4-propoxythioxanthone.

カルボン酸化合物としては、フェニルスルファニル酢酸、メチルフェニルスルファニル酢酸、エチルフェニルスルファニル酢酸、メチルエチルフェニルスルファニル酢酸、ジメチルフェニルスルファニル酢酸、メトキシフェニルスルファニル酢酸、ジメトキシフェニルスルファニル酢酸、クロロフェニルスルファニル酢酸、ジクロロフェニルスルファニル酢酸、Ｎ−フェニルグリシン、フェノキシ酢酸、ナフチルチオ酢酸、Ｎ−ナフチルグリシン及びナフトキシ酢酸が挙げられる。   Carboxylic acid compounds include phenylsulfanyl acetic acid, methylphenylsulfanyl acetic acid, ethylphenylsulfanyl acetic acid, methylethylphenylsulfanyl acetic acid, dimethylphenylsulfanyl acetic acid, methoxyphenylsulfanyl acetic acid, dimethoxyphenylsulfanyl acetic acid, chlorophenylsulfanyl acetic acid, dichlorophenylsulfanyl acetic acid, N -Phenylglycine, phenoxyacetic acid, naphthylthioacetic acid, N-naphthylglycine and naphthoxyacetic acid.

重合開始助剤（Ｄ１）としては、チオキサントン化合物が好ましい。
また、重合開始助剤（Ｄ１）を用いる場合、その使用量は、樹脂（Ｂ）及び重合性化合物（Ｃ）の合計量１００質量部に対して、好ましくは０．１〜３０質量部、より好ましくは１〜２０質量部である。また、重合開始剤（Ｄ）の含有量１００質量部に対して、好ましくは２０〜１００質量部、より好ましくは３０〜８０質量部である。重合開始助剤（Ｄ１）の量がこの範囲にあると、高感度でパターンを形成することができ、さらに高明度なカラーフィルタが得られる傾向がある。 As the polymerization initiation assistant (D1), a thioxanthone compound is preferable.
Moreover, when using a polymerization start adjuvant (D1), the usage-amount is preferably 0.1-30 mass parts with respect to 100 mass parts of total amounts of resin (B) and polymeric compound (C), and more. Preferably it is 1-20 mass parts. Moreover, Preferably it is 20-100 mass parts with respect to 100 mass parts of content of a polymerization initiator (D), More preferably, it is 30-80 mass parts. When the amount of the polymerization initiation assistant (D1) is within this range, a pattern can be formed with high sensitivity, and a color filter with higher brightness tends to be obtained.

＜溶剤（Ｅ）＞
溶剤（Ｅ）は、特に限定されず、当該分野で通常使用される溶剤を用いることができる。例えば、エステル溶剤（分子内に−ＣＯＯ−を含み、−Ｏ−を含まない溶剤）、エーテル溶剤（分子内に−Ｏ−を含み、−ＣＯＯ−を含まない溶剤）、エーテルエステル溶剤（分子内に−ＣＯＯ−と−Ｏ−とを含む溶剤）、ケトン溶剤（分子内に−ＣＯ−を含み、−ＣＯＯ−を含まない溶剤）、アルコール溶剤（分子内にＯＨを含み、−Ｏ−、−ＣＯ−及び−ＣＯＯ−を含まない溶剤）、芳香族炭化水素溶剤、アミド溶剤及びジメチルスルホキシドが挙げられる。 <Solvent (E)>
A solvent (E) is not specifically limited, The solvent normally used in the said field | area can be used. For example, an ester solvent (a solvent containing —COO— in the molecule and not containing —O—), an ether solvent (a solvent containing —O— in the molecule and not containing —COO—), an ether ester solvent (intramolecular) Solvent containing -COO- and -O-), ketone solvent (solvent containing -CO- in the molecule and not containing -COO-), alcohol solvent (containing OH in the molecule, -O-,- CO- and -COO- free solvents), aromatic hydrocarbon solvents, amide solvents and dimethyl sulfoxide.

前記エステル溶剤としては、乳酸メチル、乳酸エチル、乳酸ブチル、２−ヒドロキシイソブタン酸メチル、酢酸エチル、酢酸ｎ−ブチル、酢酸イソブチル、ギ酸ペンチル、酢酸イソペンチル、プロピオン酸ブチル、酪酸イソプロピル、酪酸エチル、酪酸ブチル、ピルビン酸メチル、ピルビン酸エチル、ピルビン酸プロピル、アセト酢酸メチル、アセト酢酸エチル、シクロヘキサノールアセテート及びγ−ブチロラクトンが挙げられる。   Examples of the ester solvent include methyl lactate, ethyl lactate, butyl lactate, methyl 2-hydroxyisobutanoate, ethyl acetate, n-butyl acetate, isobutyl acetate, pentyl formate, isopentyl acetate, butyl propionate, isopropyl butyrate, ethyl butyrate, butyric acid Examples include butyl, methyl pyruvate, ethyl pyruvate, propyl pyruvate, methyl acetoacetate, ethyl acetoacetate, cyclohexanol acetate and γ-butyrolactone.

前記エーテル溶剤としては、エチレングリコールモノメチルエーテル、エチレングリコールモノエチルエーテル、エチレングリコールモノプロピルエーテル、エチレングリコールモノブチルエーテル、ジエチレングリコールモノメチルエーテル、ジエチレングリコールモノエチルエーテル、ジエチレングリコールモノブチルエーテル、プロピレングリコールモノメチルエーテル、プロピレングリコールモノエチルエーテル、プロピレングリコールモノプロピルエーテル、プロピレングリコールモノブチルエーテル、３−メトキシ−１−ブタノール、３−メトキシ−３−メチルブタノール、テトラヒドロフラン、テトラヒドロピラン、１，４−ジオキサン、ジエチレングリコールジメチルエーテル、ジエチレングリコールジエチルエーテル、ジエチレングリコールメチルエチルエーテル、ジエチレングリコールジプロピルエーテル、ジエチレングリコールジブチルエーテル、アニソール、フェネトール及びメチルアニソールが挙げられる。   Examples of the ether solvent include ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, ethylene glycol monopropyl ether, ethylene glycol monobutyl ether, diethylene glycol monomethyl ether, diethylene glycol monoethyl ether, diethylene glycol monobutyl ether, propylene glycol monomethyl ether, propylene glycol monoethyl. Ether, propylene glycol monopropyl ether, propylene glycol monobutyl ether, 3-methoxy-1-butanol, 3-methoxy-3-methylbutanol, tetrahydrofuran, tetrahydropyran, 1,4-dioxane, diethylene glycol dimethyl ether, diethylene glycol diethyl ether, di Chi glycol methyl ethyl ether, diethylene glycol dipropyl ether, diethylene glycol dibutyl ether, anisole, include phenetol and methyl anisole.

前記エーテルエステル溶剤としては、メトキシ酢酸メチル、メトキシ酢酸エチル、メトキシ酢酸ブチル、エトキシ酢酸メチル、エトキシ酢酸エチル、３−メトキシプロピオン酸メチル、３−メトキシプロピオン酸エチル、３−エトキシプロピオン酸メチル、３−エトキシプロピオン酸エチル、２−メトキシプロピオン酸メチル、２−メトキシプロピオン酸エチル、２−メトキシプロピオン酸プロピル、２−エトキシプロピオン酸メチル、２−エトキシプロピオン酸エチル、２−メトキシ−２−メチルプロピオン酸メチル、２−エトキシ−２−メチルプロピオン酸エチル、３−メトキシブチルアセテート、３−メチル−３−メトキシブチルアセテート、プロピレングリコールモノメチルエーテルアセテート、プロピレングリコールモノエチルエーテルアセテート、プロピレングリコールモノプロピルエーテルアセテート、エチレングリコールモノメチルエーテルアセテート、エチレングリコールモノエチルエーテルアセテート、ジエチレングリコールモノエチルエーテルアセテート及びジエチレングリコールモノブチルエーテルアセテートが挙げられる。   Examples of the ether ester solvent include methyl methoxyacetate, ethyl methoxyacetate, butyl methoxyacetate, methyl ethoxyacetate, ethyl ethoxyacetate, methyl 3-methoxypropionate, ethyl 3-methoxypropionate, methyl 3-ethoxypropionate, 3- Ethyl ethoxypropionate, methyl 2-methoxypropionate, ethyl 2-methoxypropionate, propyl 2-methoxypropionate, methyl 2-ethoxypropionate, ethyl 2-ethoxypropionate, methyl 2-methoxy-2-methylpropionate , Ethyl 2-ethoxy-2-methylpropionate, 3-methoxybutyl acetate, 3-methyl-3-methoxybutyl acetate, propylene glycol monomethyl ether acetate, propylene glycol monoethyl ester Ether acetate, propylene glycol monopropyl ether acetate, ethylene glycol monomethyl ether acetate, ethylene glycol monoethyl ether acetate, diethylene glycol monoethyl ether acetate and diethylene glycol monobutyl ether acetate.

前記ケトン溶剤としては、４−ヒドロキシ−４−メチル−２−ペンタノン、アセトン、２−ブタノン、２−ヘプタノン、３−ヘプタノン、４−ヘプタノン、４−メチル−２−ペンタノン、シクロペンタノン、シクロヘキサノン及びイソホロンが挙げられる。   Examples of the ketone solvent include 4-hydroxy-4-methyl-2-pentanone, acetone, 2-butanone, 2-heptanone, 3-heptanone, 4-heptanone, 4-methyl-2-pentanone, cyclopentanone, cyclohexanone and Examples include isophorone.

前記アルコール溶剤としては、メタノール、エタノール、プロパノール、ブタノール、ヘキサノール、シクロヘキサノール、エチレングリコール、プロピレングリコール及びグリセリンが挙げられる。   Examples of the alcohol solvent include methanol, ethanol, propanol, butanol, hexanol, cyclohexanol, ethylene glycol, propylene glycol, and glycerin.

前記芳香族炭化水素溶剤としては、ベンゼン、トルエン、キシレン及びメシチレンが挙げられる。   Examples of the aromatic hydrocarbon solvent include benzene, toluene, xylene, and mesitylene.

前記アミド溶剤としては、Ｎ，Ｎ−ジメチルホルムアミド、Ｎ，Ｎ−ジメチルアセトアミド及びＮ−メチルピロリドンが挙げられる。   Examples of the amide solvent include N, N-dimethylformamide, N, N-dimethylacetamide and N-methylpyrrolidone.

上記の溶剤のうち、塗布性、乾燥性の点から、１ａｔｍ（１０１．３２５ｋＰａ）における沸点が１２０℃以上１８０℃以下である有機溶剤が好ましい。中でも、プロピレングリコールモノメチルエーテルアセテート、乳酸エチル、プロピレングリコールモノメチルエーテル、３−エトキシプロピオン酸エチル、エチレングリコールモノメチルエーテル、ジエチレングリコールモノメチルエーテル、ジエチレングリコールモノエチルエーテル、３−メトキシブチルアセテート、３−メトキシ−１−ブタノール、４−ヒドロキシ−４−メチル−２−ペンタノン及びＮ，Ｎ−ジメチルホルムアミドが好ましく、プロピレングリコールモノメチルエーテルアセテート、プロピレングリコールモノメチルエーテル、ジプロピレングリコールメチルエーテルアセテート、乳酸エチル、３−メトキシブチルアセテート、３−メトキシ−１−ブタノール及び３−エトキシプロピオン酸エチルがより好ましい。   Among the above-mentioned solvents, an organic solvent having a boiling point of 120 ° C. or more and 180 ° C. or less at 1 atm (101.325 kPa) is preferable from the viewpoints of coating properties and drying properties. Among them, propylene glycol monomethyl ether acetate, ethyl lactate, propylene glycol monomethyl ether, ethyl 3-ethoxypropionate, ethylene glycol monomethyl ether, diethylene glycol monomethyl ether, diethylene glycol monoethyl ether, 3-methoxybutyl acetate, 3-methoxy-1-butanol 4-hydroxy-4-methyl-2-pentanone and N, N-dimethylformamide are preferred, propylene glycol monomethyl ether acetate, propylene glycol monomethyl ether, dipropylene glycol methyl ether acetate, ethyl lactate, 3-methoxybutyl acetate, 3 More preferred are -methoxy-1-butanol and ethyl 3-ethoxypropionate.

赤色着色硬化性樹脂組成物における溶剤（Ｅ）の含有量は、赤色着色硬化性樹脂組成物に対して、好ましくは７０〜９５質量％であり、より好ましくは７５〜９２質量％である。言い換えると、赤色着色硬化性樹脂組成物の固形分は、好ましくは５〜３０質量％、より好ましくは８〜２５質量％である。溶剤（Ｅ）の含有量が前記の範囲にあると、塗布時の平坦性が良好になり、またカラーフィルタを形成した際に色濃度が不足しないために表示特性が良好となる傾向がある。   The content of the solvent (E) in the red colored curable resin composition is preferably 70 to 95% by mass and more preferably 75 to 92% by mass with respect to the red colored curable resin composition. In other words, the solid content of the red colored curable resin composition is preferably 5 to 30% by mass, more preferably 8 to 25% by mass. When the content of the solvent (E) is in the above range, the flatness at the time of coating is good, and when the color filter is formed, the color density does not become insufficient and the display characteristics tend to be good.

＜界面活性剤（Ｆ）＞
界面活性剤（Ｆ）としては、シリコーン系界面活性剤、フッ素系界面活性剤及びフッ素原子を有するシリコーン系界面活性剤が挙げられる。これらは、側鎖に重合性基を有していてもよい。 <Surfactant (F)>
Examples of the surfactant (F) include silicone surfactants, fluorine surfactants, and silicone surfactants having a fluorine atom. These may have a polymerizable group in the side chain.

前記シリコーン系界面活性剤としては、シロキサン結合を有する界面活性剤が挙げられる。具体的には、トーレシリコーンＤＣ３ＰＡ、同ＳＨ７ＰＡ、同ＤＣ１１ＰＡ、同ＳＨ２１ＰＡ、同ＳＨ２８ＰＡ、同ＳＨ２９ＰＡ、同ＳＨ３０ＰＡ、同ＳＨ８４００（東レ・ダウコーニング（株）製）、ＫＰ３２１、ＫＰ３２２、ＫＰ３２３、ＫＰ３２４、ＫＰ３２６、ＫＰ３４０、ＫＰ３４１（信越化学工業（株）製）、ＴＳＦ４００、ＴＳＦ４０１、ＴＳＦ４１０、ＴＳＦ４３００、ＴＳＦ４４４０、ＴＳＦ４４４５、ＴＳＦ−４４４６、ＴＳＦ４４５２、ＴＳＦ４４６０（モメンティブ・パフォーマンス・マテリアルズ・ジャパン合同会社製）等が挙げられる。   Examples of the silicone surfactant include surfactants having a siloxane bond. Specifically, Torre Silicone DC3PA, SH7PA, DC11PA, SH21PA, SH28PA, SH29PA, SH29PA, SH30PA, SH8400 (manufactured by Toray Dow Corning Co., Ltd.), KP321, KP322, KP323, KP324, KP326, KP340, KP341 (made by Shin-Etsu Chemical Co., Ltd.), TSF400, TSF401, TSF410, TSF4300, TSF4440, TSF4445, TSF-4446, TSF4452, TSF4460 (made by Momentive Performance Materials Japan GK), etc. are mentioned.

前記のフッ素系界面活性剤としては、フルオロカーボン鎖を有する界面活性剤が挙げられる。具体的には、フロラード（商品名）ＦＣ４３０、同ＦＣ４３１（住友スリーエム（株）製）、メガファック（登録商標）Ｆ１４２Ｄ、同Ｆ１７１、同Ｆ１７２、同Ｆ１７３、同Ｆ１７７、同Ｆ１８３、同Ｆ５５４、同Ｒ３０、同ＲＳ−７１８−Ｋ（ＤＩＣ（株）製）、エフトップ（登録商標）ＥＦ３０１、同ＥＦ３０３、同ＥＦ３５１、同ＥＦ３５２（三菱マテリアル電子化成（株）製）、サーフロン（登録商標）Ｓ３８１、同Ｓ３８２、同ＳＣ１０１、同ＳＣ１０５（旭硝子（株）製）、Ｅ５８４４（（株）ダイキンファインケミカル研究所製）等が挙げられる。   Examples of the fluorine-based surfactant include surfactants having a fluorocarbon chain. Specifically, Florard (trade name) FC430, FC431 (manufactured by Sumitomo 3M Co., Ltd.), Megafuck (registered trademark) F142D, F171, F172, F173, F177, F183, F183, F554, R30, RS-718-K (manufactured by DIC Corporation), Ftop (registered trademark) EF301, EF303, EF351, EF352 (manufactured by Mitsubishi Materials Electronic Chemicals), Surflon (registered trademark) S381, S382, SC101, SC105 (Asahi Glass Co., Ltd.), E5844 (Daikin Fine Chemical Laboratory Co., Ltd.) and the like.

前記のフッ素原子を有するシリコーン系界面活性剤としては、シロキサン結合及びフルオロカーボン鎖を有する界面活性剤が挙げられる。具体的には、メガファック（登録商標）Ｒ０８、同ＢＬ２０、同Ｆ４７５、同Ｆ４７７、同Ｆ４４３（ＤＩＣ（株）製）等が挙げられる。   Examples of the silicone-based surfactant having a fluorine atom include surfactants having a siloxane bond and a fluorocarbon chain. Specifically, Megafac (registered trademark) R08, BL20, F475, F477, F443 (manufactured by DIC Corporation) and the like can be mentioned.

界面活性剤（Ｆ）の含有量は、赤色着色硬化性樹脂組成物に対し、好ましくは０．００１質量％以上０.２質量％以下であり、より好ましくは０.００２質量％以上０．１質量％以下、さらに好ましくは０.０１質量％以上０．０５質量％以下である。ただし、前記界面活性剤（Ｆ）の含有量に、前記顔料分散剤の含有量は含まれない。界面活性剤（Ｆ）の含有量が前記の範囲にあると、塗膜の平坦性を良好にすることができる。   The content of the surfactant (F) is preferably 0.001% by mass or more and 0.2% by mass or less, more preferably 0.002% by mass or more and 0.1% by mass or more with respect to the red colored curable resin composition. It is not more than mass%, more preferably not less than 0.01 mass% and not more than 0.05 mass%. However, the content of the pigment dispersant is not included in the content of the surfactant (F). When the content of the surfactant (F) is in the above range, the flatness of the coating film can be improved.

＜その他の成分＞
本発明の赤色着色硬化性樹脂組成物は、必要に応じて、充填剤、他の高分子化合物、密着促進剤、酸化防止剤、紫外線吸収剤、光安定剤、連鎖移動剤等、当該技術分野で公知の添加剤を含んでもよい。 <Other ingredients>
The red colored curable resin composition of the present invention includes a filler, other polymer compound, an adhesion promoter, an antioxidant, an ultraviolet absorber, a light stabilizer, a chain transfer agent, and the like as necessary. And may contain known additives.

＜赤色着色硬化性樹脂組成物の製造方法＞
本発明の赤色着色硬化性樹脂組成物は、例えば、化合物（１ａ）、顔料（Ａ２）、樹脂（Ｂ）、重合性化合物（Ｃ）及び重合開始剤（Ｄ）、並びに必要に応じて用いられる染料（Ａ３）、重合開始助剤（Ｄ１）、溶剤（Ｅ）、界面活性剤（Ｆ）及びその他成分を混合することにより調製できる。
顔料（Ａ２）は、予め溶剤（Ｅ）の一部又は全部と混合し、顔料の平均粒子径が０．２μｍ以下程度となるまで、ビーズミル等を用いて分散させることが好ましい。この際、必要に応じて前記顔料分散剤、樹脂（Ｂ）の一部又は全部を配合してもよい。得られた顔料分散液に、化合物（１ａ）、樹脂（Ｂ）の残り、重合性化合物（Ｃ）及び重合開始剤（Ｄ）、溶剤（Ｅ）の残り、並びに、必要に応じて使用される染料（Ａ３）、重合開始剤（Ｄ）、重合開始助剤（Ｄ１）、界面活性剤（Ｆ）及びその他の成分等を、所定の濃度となるように混合することにより、目的の赤色着色硬化性樹脂組成物を調製できる。
染料（Ａ３）を含む場合の染料（Ａ３）及び化合物（１ａ）は、予め溶剤（Ｅ）の一部又は全部にそれぞれ溶解させて溶液を調製してもよい。該溶液を、孔径０．０１〜１μｍ程度のフィルタでろ過することが好ましい。
上記のとおり混合して調製された赤色着色硬化性樹脂組成物を、孔径０．１〜１０μｍ程度のフィルタでろ過することが好ましい。 <Method for producing red colored curable resin composition>
The red colored curable resin composition of the present invention is used, for example, as necessary, compound (1a), pigment (A2), resin (B), polymerizable compound (C) and polymerization initiator (D). It can be prepared by mixing the dye (A3), the polymerization initiation assistant (D1), the solvent (E), the surfactant (F) and other components.
The pigment (A2) is preferably mixed with a part or all of the solvent (E) in advance and dispersed using a bead mill or the like until the average particle diameter of the pigment is about 0.2 μm or less. Under the present circumstances, you may mix | blend a part or all of the said pigment dispersant and resin (B) as needed. In the obtained pigment dispersion, the compound (1a), the remainder of the resin (B), the polymerizable compound (C) and the polymerization initiator (D), the remainder of the solvent (E), and used as necessary. By mixing the dye (A3), the polymerization initiator (D), the polymerization initiation assistant (D1), the surfactant (F), and other components so as to have a predetermined concentration, the desired red colored curing is achieved. Resin composition can be prepared.
When the dye (A3) is contained, the dye (A3) and the compound (1a) may be previously dissolved in part or all of the solvent (E) to prepare a solution. The solution is preferably filtered with a filter having a pore size of about 0.01 to 1 μm.
It is preferable to filter the red colored curable resin composition prepared by mixing as described above with a filter having a pore size of about 0.1 to 10 μm.

＜赤色カラーフィルタの製造方法＞
本発明の赤色着色硬化性樹脂組成物から赤色カラーフィルタの着色パターンを製造する方法としては、フォトリソグラフ法、インクジェット法、印刷法等が挙げられる。中でも、フォトリソグラフ法が好ましい。フォトリソグラフ法は、前記赤色着色硬化性樹脂組成物を基板に塗布し、乾燥させて組成物層を形成し、フォトマスクを介して該組成物層を露光して、現像する方法である。フォトリソグラフ法において、露光の際にフォトマスクを用いないこと、及び／又は現像しないことにより、上記組成物層の硬化物である着色塗膜を形成することができる。
作製する赤色カラーフィルタの膜厚は、特に限定されず、目的や用途等に応じて適宜調整することができ、例えば、０．１〜３０μｍ、好ましくは０．１〜２０μｍ、さらに好ましくは０．５〜６μｍである。 <Method for producing red color filter>
Examples of a method for producing a colored pattern of a red color filter from the red colored curable resin composition of the present invention include a photolithographic method, an ink jet method, and a printing method. Of these, the photolithographic method is preferable. The photolithographic method is a method in which the red colored curable resin composition is applied to a substrate, dried to form a composition layer, and the composition layer is exposed through a photomask and developed. In the photolithography method, a colored coating film that is a cured product of the composition layer can be formed by not using a photomask and / or not developing during exposure.
The film thickness of the red color filter to be produced is not particularly limited, and can be appropriately adjusted according to the purpose and application, for example, 0.1 to 30 μm, preferably 0.1 to 20 μm, and more preferably 0.8. 5 to 6 μm.

基板としては、石英ガラス、ホウケイ酸ガラス、アルミナケイ酸塩ガラス、表面をシリカコートしたソーダライムガラスなどのガラス板や、ポリカーボネート、ポリメタクリル酸メチル、ポリエチレンテレフタレートなどの樹脂板、シリコン、前記基板上にアルミニウム、銀、銀／銅／パラジウム合金薄膜などを形成したものが用いられる。これらの基板上には、別のカラーフィルタ層、樹脂層、トランジスタ、回路等が形成されていてもよい。   As the substrate, quartz glass, borosilicate glass, alumina silicate glass, glass plate such as soda lime glass coated with silica on the surface, resin plate such as polycarbonate, polymethyl methacrylate, polyethylene terephthalate, silicon, on the substrate In addition, aluminum, silver, or a silver / copper / palladium alloy thin film is used. On these substrates, another color filter layer, a resin layer, a transistor, a circuit, and the like may be formed.

フォトリソグラフ法による各色画素の形成は、公知又は慣用の装置や条件で行うことができる。例えば、下記のようにして作製することができる。
まず、赤色着色硬化性樹脂組成物を基板上に塗布し、加熱乾燥（プリベーク）及び／又は減圧乾燥することにより溶剤等の揮発成分を除去して乾燥させ、平滑な組成物層を得る。
塗布方法としては、スピンコート法、スリットコート法、スリット アンド スピンコート法等が挙げられる。
加熱乾燥を行う場合の温度は、３０〜１２０℃が好ましく、５０〜１１０℃がより好ましい。また加熱時間としては、１０秒間〜６０分間であることが好ましく、３０秒間〜３０分間であることがより好ましい。
減圧乾燥を行う場合は、５０〜１５０Ｐａの圧力下、２０〜２５℃の温度範囲で行うことが好ましい。
組成物層の膜厚は、特に限定されず、目的とする赤色カラーフィルタの膜厚に応じて適宜選択すればよい。 Formation of each color pixel by the photolithographic method can be performed by a known or commonly used apparatus and conditions. For example, it can be produced as follows.
First, a red colored curable resin composition is applied onto a substrate, dried by heating (pre-baking) and / or drying under reduced pressure to remove volatile components such as a solvent, and a smooth composition layer is obtained.
Examples of the coating method include spin coating, slit coating, and slit and spin coating.
30-120 degreeC is preferable and the temperature in the case of performing heat drying has more preferable 50-110 degreeC. In addition, the heating time is preferably 10 seconds to 60 minutes, and more preferably 30 seconds to 30 minutes.
When performing vacuum drying, it is preferable to carry out in the temperature range of 20-25 degreeC under the pressure of 50-150 Pa.
The film thickness of the composition layer is not particularly limited, and may be appropriately selected according to the film thickness of the target red color filter.

次に、組成物層は、目的の着色パターンを形成するためのフォトマスクを介して露光される。該フォトマスク上のパターンは特に限定されず、目的とする用途に応じたパターンが用いられる。
露光に用いられる光源としては、２５０〜４５０ｎｍの波長の光を発生する光源が好ましい。例えば、３５０ｎｍ未満の光を、この波長域をカットするフィルタを用いてカットしたり、４３６ｎｍ付近、４０８ｎｍ付近、３６５ｎｍ付近の光を、これらの波長域を取り出すバンドパスフィルタを用いて選択的に取り出したりしてもよい。具体的には、水銀灯、発光ダイオード、メタルハライドランプ、ハロゲンランプ等が挙げられる。
露光面全体に均一に平行光線を照射したり、フォトマスクと基材との正確な位置合わせを行うことができるため、マスクアライナ及びステッパ等の露光装置を使用することが好ましい。 Next, the composition layer is exposed through a photomask for forming a target coloring pattern. The pattern on the photomask is not particularly limited, and a pattern according to the intended use is used.
The light source used for exposure is preferably a light source that generates light having a wavelength of 250 to 450 nm. For example, light less than 350 nm can be cut using a filter that cuts this wavelength range, or light near 436 nm, 408 nm, and 365 nm can be selectively extracted using a bandpass filter that extracts these wavelength ranges. Or you may. Specific examples include mercury lamps, light emitting diodes, metal halide lamps, halogen lamps, and the like.
It is preferable to use an exposure apparatus such as a mask aligner and a stepper because the entire exposure surface can be irradiated with parallel rays uniformly and accurate alignment between the photomask and the substrate can be performed.

露光後の組成物層を現像液に接触させて現像することにより、基板上に着色パターンが形成される。現像により、組成物層の未露光部が現像液に溶解して除去される。現像液としては、例えば、水酸化カリウム、炭酸水素ナトリウム、炭酸ナトリウム、水酸化テトラメチルアンモニウム等のアルカリ性化合物の水溶液が好ましい。これらのアルカリ性化合物の水溶液中の濃度は、好ましくは０．０１〜１０質量％であり、より好ましくは０．０３〜５質量％である。さらに、現像液は、界面活性剤を含んでいてもよい。
現像方法は、パドル法、ディッピング法及びスプレー法等のいずれでもよい。さらに現像時に基板を任意の角度に傾けてもよい。
現像後は、水洗することが好ましい。 By developing the exposed composition layer in contact with a developer, a colored pattern is formed on the substrate. By the development, the unexposed portion of the composition layer is dissolved and removed in the developer. As the developer, for example, an aqueous solution of an alkaline compound such as potassium hydroxide, sodium hydrogen carbonate, sodium carbonate, tetramethylammonium hydroxide is preferable. The concentration of these alkaline compounds in the aqueous solution is preferably 0.01 to 10% by mass, more preferably 0.03 to 5% by mass. Further, the developer may contain a surfactant.
The developing method may be any of paddle method, dipping method, spray method and the like. Further, the substrate may be tilted at an arbitrary angle during development.
After development, it is preferable to wash with water.

さらに、得られた着色パターンに、ポストベークを行うことが好ましい。ポストベーク温度は、１５０〜２５０℃が好ましく、１６０〜２３５℃がより好ましい。ポストベーク時間は、１〜１２０分間が好ましく、１０〜６０分間がより好ましい。   Furthermore, it is preferable to post-bake the obtained colored pattern. The post-bake temperature is preferably 150 to 250 ° C, more preferably 160 to 235 ° C. The post-bake time is preferably 1 to 120 minutes, more preferably 10 to 60 minutes.

かくして得られた着色パターン及び着色塗膜は、赤色カラーフィルタとして有用である。本発明の赤色着色硬化性樹脂組成物によれば、特に高明度な赤色カラーフィルタを作製することができるため、該赤色カラーフィルタは、表示装置（例えば、液晶表示装置、有機ＥＬ装置等）、電子ペーパー、固体撮像素子等に用いられる赤色カラーフィルタとして有用である。   The colored pattern and the colored coating film thus obtained are useful as a red color filter. According to the red colored curable resin composition of the present invention, since a particularly high-brightness red color filter can be produced, the red color filter includes a display device (for example, a liquid crystal display device, an organic EL device, etc.), It is useful as a red color filter used for electronic paper, solid-state imaging devices and the like.

次に実施例を挙げて、本発明をさらに具体的に説明する。例中、含有量ないし使用量を表す％及び部は、特記ない限り、質量基準である。
以下において、化合物の構造は質量分析（ＬＣ；Ａｇｉｌｅｎｔ製１２００型、ＭＡＳＳ；Ａｇｉｌｅｎｔ製ＬＣ／ＭＳＤ型）で確認した。 Next, the present invention will be described more specifically with reference to examples. In the examples, “%” and “part” representing the content or amount used are based on mass unless otherwise specified.
In the following, the structure of the compound was confirmed by mass spectrometry (LC; Agilent 1200 type, MASS; Agilent LC / MSD type).

〔合成例１〕
式（１ｘ）で表される化合物１２部とＮ−メチル−２−ピロリドン６０部とピペリジン（東京化成工業（株）製）１２．６部とを混合し、得られた混合物を６０℃で５時間攪拌した。上記の反応液を室温まで冷却後、水６００部、３５％塩酸１００部の混合液中に添加し室温で１時間攪拌した。析出した結晶を吸引濾過の残渣として取得後乾燥し、式（１−４７）で表される化合物１２．４部を得た。収率は８３％であった。

Figure 0006461453
[Synthesis Example 1]
12 parts of the compound represented by the formula (1x), 60 parts of N-methyl-2-pyrrolidone, and 12.6 parts of piperidine (manufactured by Tokyo Chemical Industry Co., Ltd.) are mixed, and the resulting mixture is mixed at 60 ° C. with 5 parts. Stir for hours. The reaction solution was cooled to room temperature, added to a mixed solution of 600 parts of water and 100 parts of 35% hydrochloric acid, and stirred at room temperature for 1 hour. The precipitated crystals were obtained as a suction filtration residue and dried to obtain 12.4 parts of a compound represented by the formula (1-47). The yield was 83%.
Figure 0006461453

式（１−４７）で表される化合物の同定
（質量分析）イオン化モード＝ＥＳＩ＋： ｍ／ｚ＝ ［Ｍ＋Ｈ］＋ ５０３．４
Ｅｘａｃｔ Ｍａｓｓ： ５０２．２ Identification of compound represented by formula (1-47) (mass spectrometry) ionization mode = ESI +: m / z = [M + H] + 503.4
Exact Mass: 502.2

〔合成例２〕
式（１ｘ）で表される化合物１５部とＮ−メチル−２−ピロリドン７５部とデカヒドロキノリン（東京化成工業（株）製）２５．８部とを混合し、得られた混合物を１１０℃で２４時間攪拌した。上記の反応液を室温まで冷却後、水６００部、３５％塩酸１００部の混合液中に添加し室温で１時間攪拌した。析出した結晶を吸引濾過の残渣として取得後乾燥し、式（１−４９）で表される化合物１９．５部を得た。収率は８６％であった。

Figure 0006461453
[Synthesis Example 2]
15 parts of the compound represented by the formula (1x), 75 parts of N-methyl-2-pyrrolidone and 25.8 parts of decahydroquinoline (manufactured by Tokyo Chemical Industry Co., Ltd.) are mixed, and the resulting mixture is 110 ° C. For 24 hours. The reaction solution was cooled to room temperature, added to a mixed solution of 600 parts of water and 100 parts of 35% hydrochloric acid, and stirred at room temperature for 1 hour. The precipitated crystals were obtained as a suction filtration residue and dried to obtain 19.5 parts of a compound represented by the formula (1-49). The yield was 86%.
Figure 0006461453

式（１−４９）で表される化合物の同定
（質量分析）イオン化モード＝ＥＳＩ＋： ｍ／ｚ＝ ［Ｍ＋Ｈ］＋ ６１１．４
Ｅｘａｃｔ Ｍａｓｓ： ６１０．３ Identification of compound represented by formula (1-49) (mass spectrometry) ionization mode = ESI +: m / z = [M + H] + 611.4
Exact Mass: 610.3

〔合成例３〕
式（１ｘ）で表される化合物２０部とＮ−エチル−ｏ−トルイジン（和光純薬工業（株）製）２００部とを遮光条件下混合し、得られた溶液を１１０℃で６時間攪拌した。得られた反応液を室温まで冷却後、水８００部、３５％塩酸５０部の混合液中に添加し室温で１時間攪拌したところ、結晶が析出した。析出した結晶を吸引濾過の残渣として取得後乾燥し、式（１−５０）で表される化合物２４部を得た。収率は８０％であった。

Figure 0006461453
[Synthesis Example 3]
20 parts of the compound represented by the formula (1x) and 200 parts of N-ethyl-o-toluidine (manufactured by Wako Pure Chemical Industries, Ltd.) were mixed under shading conditions, and the resulting solution was stirred at 110 ° C. for 6 hours. did. The obtained reaction solution was cooled to room temperature, then added to a mixed solution of 800 parts of water and 50 parts of 35% hydrochloric acid, and stirred at room temperature for 1 hour, whereby crystals were precipitated. The precipitated crystals were obtained as a suction filtration residue and dried to obtain 24 parts of a compound represented by the formula (1-50). The yield was 80%.
Figure 0006461453

式（１−５０）で表される化合物の同定
（質量分析）イオン化モード＝ＥＳＩ＋： ｍ／ｚ＝［Ｍ＋Ｈ］＋６０３．４
Ｅｘａｃｔ Ｍａｓｓ：６０２．２ Identification of compound represented by formula (1-50) (mass spectrometry) ionization mode = ESI +: m / z = [M + H] + 603.4
Exact Mass: 602.2

〔合成例４〕
式（１ｘ）で表される化合物１２部とＮ−メチル−２−ピロリドン６０部と１−メチルピペリジン（東京化成工業（株）製）１４．７部とを混合し、得られた混合物を６０℃で５時間攪拌した。上記の反応液を室温まで冷却後、水６００部、３５％塩酸１００部の混合液中に添加し室温で１時間攪拌した。析出した結晶を吸引濾過の残渣として取得後乾燥し、式（１−４８）で表される化合物１３．８部を得た。収率は８８％であった。

Figure 0006461453
[Synthesis Example 4]
12 parts of the compound represented by the formula (1x), 60 parts of N-methyl-2-pyrrolidone and 14.7 parts of 1-methylpiperidine (manufactured by Tokyo Chemical Industry Co., Ltd.) are mixed, and the resulting mixture is mixed with 60 parts. Stir at 5 ° C. for 5 hours. The reaction solution was cooled to room temperature, added to a mixed solution of 600 parts of water and 100 parts of 35% hydrochloric acid, and stirred at room temperature for 1 hour. The precipitated crystals were obtained as a suction filtration residue and then dried to obtain 13.8 parts of a compound represented by the formula (1-48). The yield was 88%.
Figure 0006461453

式（１−４８）で表される化合物の同定
（質量分析）イオン化モード＝ＥＳＩ＋： ｍ／ｚ＝ ［Ｍ＋Ｈ］＋５３１．２
Ｅｘａｃｔ Ｍａｓｓ： ５３０．２ Identification of compound represented by formula (1-48) (mass spectrometry) ionization mode = ESI +: m / z = [M + H] + 531.2
Exact Mass: 530.2

〔合成例５〕
冷却管及び攪拌装置を備えたフラスコに、式（Ａ１−１ａ）で表される化合物及び式（Ａ１−１ｂ）表される化合物の混合物（商品名Chugai Aminol Fast Pink R；中外化成製）を１５部、クロロホルム１５０部及びＮ，Ｎ−ジメチルホルムアミド８．９部を投入し、攪拌下２０℃以下を維持しながら、塩化チオニル１０．９部を滴下して加えた。滴下終了後、５０℃に昇温し、同温度で５時間維持して反応させ、その後２０℃に冷却した。冷却後の反応溶液を、攪拌下２０℃以下に維持しながら、２−エチルヘキシルアミン１２．５部及びトリエチルアミン２２．１部の混合液を滴下して加えた。その後、同温度で５時間攪拌して反応させた。次いで得られた反応混合物をロータリーエバポレーターで溶媒留去した後、メタノールを少量加えて激しく攪拌した。この混合物を、イオン交換水３７５部の混合液中に攪拌しながら加えて、結晶を析出させた。析出した結晶を濾別し、イオン交換水でよく洗浄し、６０℃で減圧乾燥して、染料（ア）（式（Ａ１−１−１）〜式（Ａ１−１−８）で表される化合物の混合物）１１．３部を得た。

Figure 0006461453
[Synthesis Example 5]
A mixture of a compound represented by the formula (A1-1a) and a compound represented by the formula (A1-1b) (trade name Chugai Aminol Fast Pink R; manufactured by Chugai Kasei Co., Ltd.) 15 in a flask equipped with a condenser and a stirrer. Part, 150 parts of chloroform and 8.9 parts of N, N-dimethylformamide were added dropwise and 10.9 parts of thionyl chloride was added dropwise while maintaining at 20 ° C. or lower with stirring. After completion of the dropwise addition, the temperature was raised to 50 ° C., the reaction was continued for 5 hours at the same temperature, and then cooled to 20 ° C. While maintaining the reaction solution after cooling at 20 ° C. or lower with stirring, a mixed solution of 12.5 parts of 2-ethylhexylamine and 22.1 parts of triethylamine was added dropwise. Then, it was made to react by stirring at the same temperature for 5 hours. Next, after the solvent of the obtained reaction mixture was distilled off with a rotary evaporator, a small amount of methanol was added and stirred vigorously. This mixture was added to a mixture of 375 parts of ion exchange water with stirring to precipitate crystals. The precipitated crystals are separated by filtration, washed well with ion-exchanged water, dried under reduced pressure at 60 ° C., and represented by dye (a) (formula (A1-1-1) to formula (A1-1-8)). Compound mixture) 11.3 parts were obtained.
Figure 0006461453

Figure 0006461453
Figure 0006461453

〔合成例６〕
撹拌機、温度計、還流冷却器及び、滴下ロートを備えたフラスコ内に窒素を０．０２Ｌ／分で流して窒素雰囲気とし、プロピレングリコールモノメチルエーテルアセテート３０５部を入れ、撹拌しながら７０℃まで加熱した。次いで、アクリル酸６０部、３，４−エポキシトリシクロ［５．２．１．０２．６］デシルアクリレート（式（Ｉ−１）で表される化合物及び式（ＩＩ−１）で表される化合物を、モル比で、５０：５０で混合。）４４０部を、プロピレングリコールモノメチルエーテルアセテート１４０部に溶解して溶液を調製し、該溶解液を、滴下ロートを用いて４時間かけて、７０℃に保温したフラスコ内に滴下した。

Figure 0006461453
一方、重合開始剤２，２’−アゾビス（２，４−ジメチルバレロニトリル）３０部をプロピレングリコールモノメチルエーテルアセテート２２５部に溶解した溶液を、別の滴下ロートを用いて４時間かけてフラスコ内に滴下した。重合開始剤の溶液の滴下が終了した後、４時間、７０℃に保持し、その後室温まで冷却して、重量平均分子量（Ｍｗ）は、９．１×１０３、分子量分布が２．１６、固形分３４．８％、固形分換算の酸価は８１ｍｇＫＯＨ／ｇの樹脂Ｂ１溶液を得た。樹脂Ｂ１は下記に示す構造単位を有する。
Figure 0006461453
[Synthesis Example 6]
Nitrogen was flowed at 0.02 L / min into a flask equipped with a stirrer, thermometer, reflux condenser and dropping funnel to form a nitrogen atmosphere, 305 parts of propylene glycol monomethyl ether acetate was added, and the mixture was heated to 70 ° C. with stirring. did. Next, 60 parts of acrylic acid, 3,4-epoxytricyclo [5.2.1.0 2.6 ] decyl acrylate (a compound represented by the formula (I-1) and a formula (II-1) 440 parts are dissolved in 140 parts of propylene glycol monomethyl ether acetate to prepare a solution, and the solution is added using a dropping funnel over 4 hours. It was dripped in the flask kept at 70 degreeC.
Figure 0006461453
On the other hand, a solution prepared by dissolving 30 parts of a polymerization initiator 2,2′-azobis (2,4-dimethylvaleronitrile) in 225 parts of propylene glycol monomethyl ether acetate was placed in a flask using another dropping funnel over 4 hours. It was dripped. After completion of the dropwise addition of the polymerization initiator solution, the mixture was kept at 70 ° C. for 4 hours, and then cooled to room temperature. The weight average molecular weight (Mw) was 9.1 × 10 3 , the molecular weight distribution was 2.16, A resin B1 solution having a solid content of 34.8% and an acid value in terms of solid content of 81 mgKOH / g was obtained. Resin B1 has the structural units shown below.
Figure 0006461453

合成例で得られた樹脂の重量平均分子量（Ｍｗ）及び数平均分子量（Ｍｎ）の測定は、ＧＰＣ法を用いて、以下の条件で行った。
装置；Ｋ２４７９（（株）島津製作所製）
カラム；ＳＨＩＭＡＤＺＵ Ｓｈｉｍ−ｐａｃｋ ＧＰＣ−８０Ｍ
カラム温度；４０℃
溶媒；ＴＨＦ（テトラヒドロフラン）
流速；１．０ｍＬ／ｍｉｎ
検出器；ＲＩ
校正用標準物質 ；ＴＳＫ ＳＴＡＮＤＡＲＤ ＰＯＬＹＳＴＹＲＥＮＥ Ｆ−４０、Ｆ−４、Ｆ−２８８、Ａ−２５００、Ａ−５００（東ソー（株）製）
上記で得られたポリスチレン換算の重量平均分子量及び数平均分子量の比（Ｍｗ／Ｍｎ）を分子量分布とした。 The weight average molecular weight (Mw) and the number average molecular weight (Mn) of the resin obtained in the synthesis example were measured using the GPC method under the following conditions.
Apparatus; K2479 (manufactured by Shimadzu Corporation)
Column; SHIMADZU Shim-pack GPC-80M
Column temperature: 40 ° C
Solvent; THF (tetrahydrofuran)
Flow rate: 1.0 mL / min
Detector; RI
Standard material for calibration: TSK STANDARD POLYSTYRENE F-40, F-4, F-288, A-2500, A-500 (manufactured by Tosoh Corporation)
The polystyrene-converted weight average molecular weight and number average molecular weight ratio (Mw / Mn) obtained above was defined as molecular weight distribution.

実施例１〜１２
表１及び表２に示す組成となるように各成分を混合して赤色着色硬化性樹脂組成物を得た。 Examples 1-12
Each component was mixed so that it might become a composition shown in Table 1 and Table 2, and the red colored curable resin composition was obtained.

Figure 0006461453
１） 顔料は、顔料分散剤及びE-12)欄記載の量のプロピレングリコールモノメチルエーテルアセテートと混合し、予め分散させた。
２） E-12)は、プロピレングリコールモノメチルエーテルアセテート含有量の合計を表す。
Figure 0006461453
 1) The pigment was mixed with a pigment dispersant and propylene glycol monomethyl ether acetate in the amount described in the column E-1 2) and dispersed in advance.
2) E-1 2) represents the total content of propylene glycol monomethyl ether acetate.

Figure 0006461453
１） 顔料は、顔料分散剤及びE-12)欄記載の量のプロピレングリコールモノメチルエーテルアセテートと混合し、予め分散させた。
２） E-12)は、プロピレングリコールモノメチルエーテルアセテート含有量の合計を表す。
Figure 0006461453
 1) The pigment was mixed with a pigment dispersant and propylene glycol monomethyl ether acetate in the amount described in the column E-1 2) and dispersed in advance.
2) E-1 2) represents the total content of propylene glycol monomethyl ether acetate.

なお、表１及び表２中、各成分は以下のものを表す。また、樹脂（Ｂ）は、固形分換算の質量部を示した。
化合物（１ａ）：Ａ１−１：式（１−４７）で表される化合物
化合物（１ａ）：Ａ１−２：式（１−４９）で表される化合物
化合物（１ａ）：Ａ１−３：式（１−５０）で表される化合物
化合物（１ａ）：Ａ１−４：式（１−４８）で表される化合物
化合物（１ａ）：Ａ１−５：式（１−４１）で表される化合物
化合物（１ａ）：Ａ１−６：式（１−３７）で表される化合物
顔料（Ａ２）：Ａ２−１：Ｃ．Ｉ．ピグメントレッド２５４
顔料（Ａ２）：Ａ２−２：Ｃ．Ｉ．ピグメントレッド２４２
顔料（Ａ２）：Ａ２−３：Ｃ．Ｉ．ピグメントレッド１７７
樹脂（Ｂ）：樹脂Ｂ１
重合性化合物（Ｃ）：ジペンタエリスリトールヘキサアクリレート（ＫＡＹＡＲＡＤ（登録商標） ＤＰＨＡ；日本化薬（株）製）
重合開始剤（Ｄ）：Ｎ−１９１９（ＡＤＥＫＡ社製；Ｏ−アシルオキシム化合物）
重合開始助剤（Ｄ１）：２，４−ジエチルチオキサントン（ＫＡＹＡＣＵＲＥ（登録商標） ＤＥＴＸ−Ｓ；日本化薬（株）製）
重合開始剤（Ｄ２）： ＯＸＥ０１（チバスペシャリティケミカルズ）
溶剤（Ｅ）：Ｅ−１：プロピレングリコールモノメチルエーテルアセテート
溶剤（Ｅ）：Ｅ−２：プロピレングリコールモノメチルエーテル
溶剤（Ｅ）：Ｅ−３：ダイアセトンアルコール
界面活性剤（Ｆ）：フッ素系界面活性剤（メガファック（登録商標）Ｆ５５４；ＤＩＣ（株）製） In Tables 1 and 2, each component represents the following. Moreover, resin (B) showed the mass part of solid content conversion.
Compound (1a): A1-1: Compound represented by formula (1-47) Compound (1a): A1-2: Compound represented by formula (1-49) Compound (1a): A1-3: Formula Compound represented by (1-50) Compound (1a): A1-4: Compound represented by formula (1-48) Compound (1a): A1-5: Compound represented by formula (1-41) Compound (1a): A1-6: Compound represented by formula (1-37) Pigment (A2): A2-1: C.I. I. Pigment Red 254
Pigment (A2): A2-2: C.I. I. Pigment Red 242
Pigment (A2): A2-3: C.I. I. Pigment Red 177
Resin (B): Resin B1
Polymerizable compound (C): dipentaerythritol hexaacrylate (KAYARAD (registered trademark) DPHA; manufactured by Nippon Kayaku Co., Ltd.)
Polymerization initiator (D): N-1919 (manufactured by ADEKA; O-acyloxime compound)
Polymerization initiation aid (D1): 2,4-diethylthioxanthone (KAYACURE (registered trademark) DETX-S; manufactured by Nippon Kayaku Co., Ltd.)
Polymerization initiator (D2): OXE01 (Ciba Specialty Chemicals)
Solvent (E): E-1: Propylene glycol monomethyl ether acetate Solvent (E): E-2: Propylene glycol monomethyl ether Solvent (E): E-3: Diacetone alcohol Surfactant (F): Fluorine-based surfactant Agent (Megafuck (registered trademark) F554; manufactured by DIC Corporation)

〔着色パターンの作製〕
２インチ角のガラス基板（イーグルＸＧ；コーニング社製）上に、赤色着色硬化性樹脂組成物をスピンコート法で塗布したのち、１００℃で３分間プリベークして組成物層を形成した。放冷後、基板上の組成物層とパターンを有する石英ガラス製フォトマスクとの間隔を１００μｍとして、露光機（ＴＭＥ−１５０ＲＳＫ；トプコン（株）製）を用いて、大気雰囲気下、１５０ｍＪ／ｃｍ２の露光量（３６５ｎｍ基準）で光照射した。尚、フォトマスクとしては、１００μｍラインアンドスペースパターンが形成されたマスクを使用した。光照射後、上記塗膜を、非イオン系界面活性剤０．１２％と炭酸ナトリウム２％を含む水系現像液に２３℃で８０秒間浸漬現像し、水洗後、オーブン中、２３０℃で２０分間ポストベークを行い、着色パターンを得た。 [Preparation of colored pattern]
A red colored curable resin composition was applied by spin coating on a 2-inch square glass substrate (Eagle XG; manufactured by Corning), and then pre-baked at 100 ° C. for 3 minutes to form a composition layer. After allowing to cool, the distance between the composition layer on the substrate and the quartz glass photomask having a pattern is set to 100 μm, and an exposure machine (TME-150RSK; manufactured by Topcon Co., Ltd.) is used in an air atmosphere at 150 mJ / cm. Light was irradiated with an exposure amount of 2 (based on 365 nm). As a photomask, a mask on which a 100 μm line and space pattern was formed was used. After the light irradiation, the coating film was immersed and developed in an aqueous developer containing 0.12% nonionic surfactant and 2% sodium carbonate at 23 ° C. for 80 seconds, washed with water, and then in an oven at 230 ° C. for 20 minutes. Post-baking was performed to obtain a colored pattern.

〔膜厚測定〕
得られた着色パターンについて、膜厚測定装置（ＤＥＫＴＡＫ３；日本真空技術（株）製））を用いて膜厚を測定した。結果を表３に示す。 [Film thickness measurement]
About the obtained coloring pattern, the film thickness was measured using the film thickness measuring apparatus (DEKTAK3; Nippon Vacuum Technology Co., Ltd. product). The results are shown in Table 3.

〔色度評価〕
得られたガラス基板上の着色パターンについて、測色機（ＯＳＰ−ＳＰ−２００；オリンパス（株）製）を用いて分光を測定し、Ｃ光源の等色関数を用いてＣＩＥのＸＹＺ表色系におけるｘｙ色度座標（ｘ、ｙ）及び三刺激値Ｙを測定した。Ｙの値が大きいほど明度が高いことを表す。結果を表３に示す。 [Chromaticity evaluation]
About the coloring pattern on the obtained glass substrate, the spectrum was measured using a colorimeter (OSP-SP-200; manufactured by Olympus Corporation), and the CIE XYZ color system using the color matching function of the C light source. Xy chromaticity coordinates (x, y) and tristimulus value Y were measured. The larger the value of Y, the higher the brightness. The results are shown in Table 3.

〔コントラスト評価〕
フォトマスクを使用せずに露光し、現像を行わない以外は着色パターンの形成と同様の操作を行い、ガラス基板上の着色塗膜を作製した。該得られたガラス基板上の着色塗膜について、コントラスト測色機（ＣＴ−１；壺坂電機社製、検出器；ＢＭ−５Ａ、光源；Ｆ−１０）を用いて、ブランク値を３００００としてコントラストを測定した。ガラス基板上の着色塗膜を、偏光フィルム（ＰＯＬＡＸ−３８Ｓ；ルケオ社製）ではさんだものを測定サンプルとした。結果を表３に示す。 [Contrast evaluation]
A colored coating film on a glass substrate was prepared by performing the same operation as that for forming a colored pattern except that the exposure was performed without using a photomask and development was not performed. About the obtained color coating film on the glass substrate, a blank value is set to 30000 using a contrast colorimeter (CT-1; manufactured by Aisaka Electric Co., Ltd .; detector; BM-5A, light source; F-10). Contrast was measured. A sample coated with a polarizing film (POLAX-38S; manufactured by Luceo Co., Ltd.) was used as a measurement sample. The results are shown in Table 3.

Figure 0006461453
Figure 0006461453

実施例１４
式（１−４７）で表される化合物をＣ．Ｉ．アシッドレッド５２に代える以外は実施例１の同様にして赤色着色硬化性樹脂組成物を調製する。該赤色着色硬化性樹脂組成物について、実施例１と同様の操作を行い、高明度な着色パターンを得る。 Example 14
The compound represented by formula (1-47) is represented by C.I. I. A red colored curable resin composition is prepared in the same manner as in Example 1 except that the acid red 52 is used. About this red colored curable resin composition, operation similar to Example 1 is performed and a highly light colored pattern is obtained.

本発明の赤色着色硬化性樹脂組成物によれば、高明度な赤色カラーフィルタを製造することができる。   According to the red colored curable resin composition of the present invention, a high brightness red color filter can be produced.

Claims (4)

着色剤、樹脂、重合性化合物及び重合開始剤を含み、
着色剤が、式（１ａ）で表される化合物と、黄色顔料、オレンジ色顔料及び赤色顔料からなる群から選ばれる少なくとも１種の顔料とを含む着色剤である赤色着色硬化性樹脂組成物。
Figure 0006461453
［式（１ａ）中、Ｒ1及びＲ2の組み合わせは、飽和炭化水素基と飽和炭化水素基との組み合わせ、又は飽和炭化水素基と芳香族炭化水素基（１）との組み合わせであり、
Ｒ3及びＲ4の組み合わせは、飽和炭化水素基と飽和炭化水素基との組み合わせ、又は飽和炭化水素基と芳香族炭化水素基（１）との組み合わせであり、
前記飽和炭化水素基は、炭素数１〜２０の１価の飽和炭化水素基であり、
前記芳香族炭化水素基（１）は、置換基を有していてもよい炭素数６〜１０の１価の芳香族炭化水素基であり、
前記飽和炭化水素基に含まれる水素原子は、炭素数６〜１０の芳香族炭化水素基（２）又はハロゲン原子で置換されていてもよく、前記芳香族炭化水素基（２）に含まれる水素原子は、炭素数１〜３のアルコキシ基で置換されていてもよく、前記飽和炭化水素基に含まれる−ＣＨ2−は、−Ｏ−、−ＣＯ−又は−ＮＲ11−で置き換わっていてもよい。Ｒ1及びＲ2 の組み合わせと、Ｒ 3 及びＲ 4 の組み合わせが、それぞれ飽和炭化水素基と飽和炭化水素基との組み合わせである場合、Ｒ 1 及びＲ 2 と、Ｒ 3 及びＲ 4 は、それぞれ互いに結合して、それらが結合する窒素原子と一緒になって窒素原子を含む環を形成している。
Ｒ5は、−ＳＯ3 -、−ＳＯ3Ｈ、又は−ＳＯ3 -Ｚ+を表す。
Ｒ6及びＲ7は、それぞれ独立に、水素原子又は炭素数１〜６のアルキル基を表す。
ｍは、０〜５の整数を表す。ｍが２以上のとき、複数のＲ5は同一でも異なってもよい。
ａは、０又は１の整数を表す。
Ｘは、ハロゲン原子を表す。
Ｚ+は、+Ｎ（Ｒ11）4、Ｎａ+又はＫ+を表す。
Ｒ11は、互いに独立に、水素原子、炭素数１〜２０の１価の飽和炭化水素基又は炭素数７〜１０のアラルキル基を表す。］ Including a colorant, a resin, a polymerizable compound and a polymerization initiator,
A red colored curable resin composition, wherein the colorant comprises a compound represented by the formula (1a) and at least one pigment selected from the group consisting of a yellow pigment, an orange pigment, and a red pigment.
Figure 0006461453
[In the formula (1a), the combination of R 1 and R 2 is a combination of a saturated hydrocarbon group and a saturated hydrocarbon group, or a combination of a saturated hydrocarbon group and an aromatic hydrocarbon group (1) ,
The combination of R 3 and R 4 is a combination of a saturated hydrocarbon group and a saturated hydrocarbon group, or a combination of a saturated hydrocarbon group and an aromatic hydrocarbon group (1) ,
The saturated hydrocarbon group is a monovalent saturated hydrocarbon group having 1 to 20 carbon atoms,
The aromatic hydrocarbon group (1) is a monovalent aromatic hydrocarbon group having 6 to 10 carbon atoms which may have a substituent,
Hydrogen atoms contained in the saturated hydrocarbon group, hydrogen contained in may be substituted by an aromatic hydrocarbon group (2) or a halogen atom having 6 to 10 carbon atoms, the aromatic hydrocarbon group (2) The atom may be substituted with an alkoxy group having 1 to 3 carbon atoms, and —CH 2 — contained in the saturated hydrocarbon group may be replaced with —O—, —CO— or —NR 11 —. Good. When the combination of R 1 and R 2 and the combination of R 3 and R 4 are each a combination of a saturated hydrocarbon group and a saturated hydrocarbon group, R 1 and R 2 , R 3 and R 4 are respectively bonded to each other, they form a ring containing a nitrogen atom together with the nitrogen atom bonded.
R 5 represents —SO 3 − , —SO 3 H, or —SO 3 − Z + .
R 6 and R 7 each independently represents a hydrogen atom or an alkyl group having 1 to 6 carbon atoms.
m represents an integer of 0 to 5. When m is 2 or more, the plurality of R 5 may be the same or different.
a represents an integer of 0 or 1.
X represents a halogen atom.
Z + represents + N (R 11 ) 4 , Na + or K + .
R 11 independently represents a hydrogen atom, a monovalent saturated hydrocarbon group having 1 to 20 carbon atoms, or an aralkyl group having 7 to 10 carbon atoms. ] 顔料が、Ｃ．Ｉ．ピグメントイエロー１３８、Ｃ．Ｉ．ピグメントイエロー１３９、Ｃ．Ｉ．ピグメントイエロー１５０、Ｃ．Ｉ．ピグメントレッド１７７、Ｃ．Ｉ．ピグメントレッド２４２及びＣ．Ｉ．ピグメントレッド２５４からなる群から選ばれる少なくとも１種である請求項１記載の赤色着色硬化性樹脂組成物。   The pigment is C.I. I. Pigment yellow 138, C.I. I. Pigment yellow 139, C.I. I. Pigment yellow 150, C.I. I. Pigment red 177, C.I. I. Pigment red 242 and C.I. I. The red colored curable resin composition according to claim 1, which is at least one selected from the group consisting of CI Pigment Red 254. 請求項１又は２記載の赤色着色硬化性樹脂組成物により形成される赤色カラーフィルタ。   A red color filter formed by the red colored curable resin composition according to claim 1. 請求項３記載の赤色カラーフィルタを含む表示装置。   A display device comprising the red color filter according to claim 3.
JP2012266916A 2011-12-09 2012-12-06 Red colored curable resin composition Active JP6461453B2 (en)