JP6450582B2 - Powder cosmetics - Google Patents
Powder cosmetics Download PDFInfo
- Publication number
- JP6450582B2 JP6450582B2 JP2014256290A JP2014256290A JP6450582B2 JP 6450582 B2 JP6450582 B2 JP 6450582B2 JP 2014256290 A JP2014256290 A JP 2014256290A JP 2014256290 A JP2014256290 A JP 2014256290A JP 6450582 B2 JP6450582 B2 JP 6450582B2
- Authority
- JP
- Japan
- Prior art keywords
- powder
- mass
- component
- preferable
- less
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、粉末化粧料に関する。 The present invention relates to a powder cosmetic.
微粒子酸化亜鉛は、皮脂を固定する効果などを有することが知られており、種々の粉体と組み合わせて、粉末化粧料に配合されている。
例えば、特許文献１には、微粒子酸化亜鉛、シリコーン処理粉体及び複合シリコーンエラストマー粉体を含有する粉末固型化粧料が、化粧持ちに優れ、なめらかでしっとりした感触を有し、肌へのフィット感に優れることが記載されている。
特許文献２には、微粒子酸化亜鉛と高分子球状弾性粉体を含有する粉末化粧料が、高いスキンケア効果、なめらかで肌当たりが良いことが記載されている。
特許文献３には、微粒子酸化亜鉛と弾性樹脂粉体を含有する粉末化粧料が、カバー効果が得られ、自然な仕上りで使用感に優れることが記載されている。
Fine particulate zinc oxide is known to have an effect of fixing sebum and is incorporated into powder cosmetics in combination with various powders.
For example, Patent Document 1 discloses that a powder solid cosmetic containing fine zinc oxide, silicone-treated powder, and composite silicone elastomer powder has excellent makeup, has a smooth and moist feel, and fits to the skin. It is described that the feeling is excellent.
Patent Document 2 describes that a powder cosmetic containing fine zinc oxide and a polymer spherical elastic powder has a high skin care effect, smoothness and good skin contact.
Patent Document 3 describes that a powder cosmetic containing fine zinc oxide and elastic resin powder has a cover effect and has a natural finish and excellent usability.
微粒子酸化亜鉛と球状粉体を多く含有する粉末化粧料は、白く粉浮きし、厚ぼったく見えてしまうため、従来は、有色の着色顔料を多く配合して、仕上がりを調整していた。
本発明者らは、有色の着色顔料を多く配合すると、肌がくすみやすく、明るく見えないという課題を見出した。
A powder cosmetic containing a large amount of fine zinc oxide and spherical powder floats white and looks thick, so conventionally, many colored pigments are blended to adjust the finish.
The present inventors have found that when a large amount of colored pigments are blended, the skin is dull and does not appear bright.
本発明者らは、微粒子酸化亜鉛とともに、特定の板状粉体、少量の有色の着色顔料を組合わせて用いることにより、粉浮きを抑えつつ、明るく、透明感のある肌に仕上げることができる粉末化粧料が得られることを見出した。 The inventors of the present invention can finish a bright and transparent skin while suppressing powder floating by using a specific plate-like powder and a small amount of colored pigment in combination with fine zinc oxide. It has been found that a powder cosmetic can be obtained.
本発明は、次の成分（Ａ）、（Ｂ）、（Ｃ）、（Ｄ）及び（Ｅ）：
（Ａ）比表面積１０〜１００ｍ2／ｇ、粒子径５〜１００ｎｍの微粒子酸化亜鉛 １〜２０質量％、
（Ｂ）有色の着色顔料 ０．０１〜０．５質量％、
（Ｃ）粒子径が１〜５０μｍの板状粉体であって、該粉体を黒色の人工皮革に８mg／１００cm2となるように均一に塗布し、その正反射（入射光角４５°、受光角−４５°）において測色したとき、ＣＩＥ１９７６ Ｌ*ａ*ｂ*表色系で規定する彩度Ｃが１５以上である板状粉体 １〜１０質量％、
（Ｄ）オルガノポリシロキサンエラストマー、シリカ、ナイロン及びウレタンから選ばれる、粒子径４〜５０μｍの球状粉体 １０〜６０質量％、
（Ｅ）ポリメチルシルセスキオキサン及びポリ（メタ）アクリル酸エステルから選ばれる、粒子径０．１〜３μｍの球状粉体 １〜２５質量％
を含有する粉末化粧料に関する。
The present invention includes the following components (A), (B), (C), (D) and (E):
(A) 1 to 20% by mass of fine particle zinc oxide having a specific surface area of 10 to 100 m 2 / g and a particle size of 5 to 100 nm,
(B) 0.01 to 0.5% by mass of a colored pigment,
(C) A plate-like powder having a particle diameter of 1 to 50 μm, and the powder was uniformly applied to black artificial leather so as to be 8 mg / 100 cm 2, and its regular reflection (incident light angle 45 °, 1 to 10% by mass of a plate-like powder having a saturation C defined by CIE1976 L * a * b * color system of 15 or more when measured at a light receiving angle of −45 °)
(D) 10-60 mass% of spherical powder having a particle size of 4-50 μm selected from organopolysiloxane elastomer, silica, nylon and urethane,
(E) Spherical powder having a particle size of 0.1 to 3 μm, selected from polymethylsilsesquioxane and poly (meth) acrylate, 1 to 25% by mass
The present invention relates to a powder cosmetic containing
本発明の粉末化粧料は、塗布後の粉浮き、厚ぼったさを抑えつつ、明るく、透明感のある仕上がりが得られる。また、５時間後においても、その明るさ、透明感が持続し、化粧持ちにも優れている。 The powder cosmetic of the present invention can provide a bright and transparent finish while suppressing powder float and thickness after application. Further, even after 5 hours, the brightness and transparency persist and the makeup is excellent.
本発明で用いる成分（Ａ）の微粒子酸化亜鉛は、比表面積１０〜１００ｍ2／ｇのものであって、比表面積１５〜６０ｍ2／ｇのものが好ましい。このような比表面積の微粒子酸化亜鉛を用いることにより、化粧持ちに優れ、白浮きを防止し、良好な使用感を得ることができる。
また、成分（Ａ）の微粒子酸化亜鉛は、粒子径５〜１００ｎｍであり、５〜４０ｎｍが好ましく、１０〜３０ｎｍがより好ましい。このような粒子径の微粒子酸化亜鉛を用いることにより、化粧持ちに優れ、良好な使用感を得ることができる。
Zinc oxide fine particles of the component (A) used in the present invention are those having a specific surface area of 10 to 100 m 2 / g, as a specific surface area of 15 to 60 2 / g are preferred. By using the fine particle zinc oxide having such a specific surface area, the cosmetic durability is excellent, whitening is prevented, and a good feeling of use can be obtained.
The fine particle zinc oxide of component (A) has a particle diameter of 5 to 100 nm, preferably 5 to 40 nm, and more preferably 10 to 30 nm. By using finely divided zinc oxide having such a particle size, the cosmetic durability is excellent and a good feeling of use can be obtained.
成分（Ａ）の比表面積は、ＢＥＴ法により測定される。
また、粒子径は、レーザー回折／散乱法による粒度分布測定機によって、測定される。具体的には、エタノールを分散媒として、レーザー回折散乱式粒度分布測定器（例えば、堀場製作所製、ＬＡ−９２０）により測定される。
The specific surface area of the component (A) is measured by the BET method.
Further, the particle diameter is measured by a particle size distribution measuring device using a laser diffraction / scattering method. Specifically, it is measured by a laser diffraction / scattering particle size distribution analyzer (for example, LA-920, manufactured by Horiba, Ltd.) using ethanol as a dispersion medium.
成分（Ａ）の微粒子酸化亜鉛は、そのまま使用することができるが、必要に応じて、これらの１種又は２種以上が疎水化処理されたものを用いることもできる。
疎水化処理としては、通常の化粧料用粉体に施されている処理であれば制限されず、シリコーン処理、脂肪酸処理、ラウロイルリジン処理、レシチン処理、Ｎ−アシルアミノ酸処理、金属石鹸処理、フッ素化合物処理等が挙げられる。これらのうち、化粧崩れを防ぎ、化粧料中の微粒子酸化亜鉛の分散性を向上させる点から、シリコーン処理が好ましい。
これらの疎水化処理は、通常の方法により行うことができる。
The fine particle zinc oxide of the component (A) can be used as it is, but if necessary, one obtained by hydrophobizing one or more of these can also be used.
The hydrophobizing treatment is not limited as long as it is a treatment applied to normal cosmetic powders. Silicone treatment, fatty acid treatment, lauroyllysine treatment, lecithin treatment, N-acylamino acid treatment, metal soap treatment, fluorine Compound treatment and the like can be mentioned. Among these, silicone treatment is preferable from the viewpoint of preventing makeup collapse and improving the dispersibility of fine zinc oxide in the cosmetic.
These hydrophobizing treatments can be performed by ordinary methods.
成分（Ａ）の微粒子酸化亜鉛の含有量は、化粧崩れを防ぐ点から、全組成中に１質量％以上であり、３質量％以上が好ましく、５質量％以上がより好ましく、２０質量％以下であり、１５質量％以下が好ましく、１３質量％以下がより好ましい。また、成分（Ａ）の含有量は、全組成中に１〜２０質量％であり、３〜１５質量％が好ましく、５〜１３質量％がより好ましい。 The content of the fine particle zinc oxide of the component (A) is 1% by mass or more in the total composition, preferably 3% by mass or more, more preferably 5% by mass or more, and 20% by mass or less from the viewpoint of preventing makeup collapse. 15 mass% or less is preferable and 13 mass% or less is more preferable. Moreover, content of a component (A) is 1-20 mass% in all the compositions, 3-15 mass% is preferable, and 5-13 mass% is more preferable.
成分（Ｂ）の有色の着色顔料において、有色とは、白色以外の着色力のある顔料であり、赤、黄、青、黒、茶から肌色等まで広い色調の幅を持った着色力のある顔料である。
成分（Ｂ）の有色の着色顔料としては、通常の化粧料に用いられるものであればいずれでも良く、例えば、ベンガラ、黄酸化鉄、黒酸化鉄、紺青、群青等の金属酸化物；マンガンバイオレット、チタン酸コバルト等の金属錯体；更にカーボンブラック等の無機顔料、タール系色素、レーキ顔料等の有機顔料、カルミン等の天然色素などが挙げられる。
これらのうち、ベンガラ、黄酸化鉄、黒酸化鉄が好ましい。
In the colored coloring pigment of component (B), colored is a pigment having a coloring power other than white, and has a coloring power with a wide range of tones from red, yellow, blue, black, brown to skin color, etc. Pigment.
The colored pigment of component (B) may be any color pigment used in ordinary cosmetics, for example, metal oxides such as bengara, yellow iron oxide, black iron oxide, bitumen, ultramarine, etc .; manganese violet Metal complexes such as cobalt titanate; inorganic pigments such as carbon black; organic pigments such as tar dyes and lake pigments; and natural dyes such as carmine.
Among these, bengara, yellow iron oxide, and black iron oxide are preferable.
成分（Ｂ）は、成分（Ａ）と同様、必要に応じて、これらの１種又は２種以上が疎水化処理されたものを用いることもできる。 As in the case of the component (A), the component (B) may be one obtained by hydrophobizing one or more of these as necessary.
成分（Ｂ）の着色顔料は、１種又は２種以上組合わせて用いることができ、白く粉浮きするのを抑制し、肌を明るく見せる点から、含有量は、全組成中に０．０１質量％以上であり、０．０５質量％以上が好ましく、０．１質量％以上がより好ましく、０．５質量％以下であり、０．４質量％以下が好ましく、０．３質量％以下がより好ましい。また、成分（Ｂ）の含有量は、全組成中に０．０１〜０．５質量％であり、０．０５〜０．４質量％が好ましく、０．１〜０．３質量％がより好ましい。 The color pigment of component (B) can be used alone or in combination of two or more, and the content is 0.01% in the total composition from the point that white powder is suppressed and the skin is brightened. % By mass or more, preferably 0.05% by mass or more, more preferably 0.1% by mass or more, 0.5% by mass or less, preferably 0.4% by mass or less, and 0.3% by mass or less. More preferred. Moreover, content of a component (B) is 0.01-0.5 mass% in the whole composition, 0.05-0.4 mass% is preferable, and 0.1-0.3 mass% is more. preferable.
本発明において、成分（Ａ）に対する成分（Ｂ）の質量割合（Ｂ）／（Ａ）は、塗布後のくすみを抑え、肌を明るく、透明感のある仕上がりに優れている点から、０．００１以上が好ましく、０．００５以上がより好ましく、０．０１以上がさらに好ましく、０．０６以下が好ましく、０．０５以下がより好ましく、０．０３以下がさらに好ましい。また、成分（Ａ）に対する成分（Ｂ）の質量割合（Ｂ）／（Ａ）は、０．００１〜０．０６が好ましく、０．００５〜０．０５がより好ましく、０．０１〜０．０３がさらに好ましい。 In the present invention, the mass ratio (B) / (A) of the component (B) to the component (A) suppresses dullness after coating, brightens the skin, and is excellent in a transparent finish. 001 or more is preferable, 0.005 or more is more preferable, 0.01 or more is more preferable, 0.06 or less is preferable, 0.05 or less is more preferable, and 0.03 or less is more preferable. Moreover, 0.001-0.06 is preferable, as for the mass ratio (B) / (A) of the component (B) with respect to a component (A), 0.005-0.05 is more preferable, 0.01-0. 03 is more preferable.
成分（Ｃ）の板状粉体は、粒子径が１〜５０μｍであり、好ましくは、２〜３０μｍのものである。また、アスペクト比は、１０〜１５０のものが好ましく、２０〜１００のものがより好ましい。
ここで、板状とは、形状が狭義の板状の他、薄片状、鱗状等の形状の粉体も含まれる。
また、粒子径は、電子顕微鏡観察、レーザー回折／散乱法による粒度分布測定機によって、測定される。具体的には、レーザー回折／散乱法の場合、エタノールを分散媒として、レーザー回折散乱式粒度分布測定器（例えば、堀場製作所製、ＬＡ−９２０）で測定する。厚さは、原子間力顕微鏡により基準面との差を測定し、相加平均したものを平均厚さとする。
さらに、アスペクト比は、粒子径と平均厚さとの比により計算されるものであり、アスペクト比＝（粒子径／平均厚さ）で定義される。
The plate-like powder of the component (C) has a particle diameter of 1 to 50 μm, preferably 2 to 30 μm. The aspect ratio is preferably 10 to 150, more preferably 20 to 100.
Here, the plate shape includes a plate shape having a narrow shape, as well as a powder having a flake shape, a scale shape, or the like.
The particle diameter is measured with an electron microscope observation and a particle size distribution measuring device using a laser diffraction / scattering method. Specifically, in the case of the laser diffraction / scattering method, measurement is performed with a laser diffraction / scattering particle size distribution analyzer (for example, LA-920, manufactured by Horiba, Ltd.) using ethanol as a dispersion medium. The thickness is determined by measuring the difference from the reference plane with an atomic force microscope, and calculating the arithmetic mean to obtain the average thickness.
Furthermore, the aspect ratio is calculated by the ratio between the particle diameter and the average thickness, and is defined as aspect ratio = (particle diameter / average thickness).
成分（Ｃ）の板状粉体は、該粉体を黒色の人工皮革に８mg／１００cm2となるように均一に塗布し、その正反射（入射光角４５°、受光角−４５°）において測色したとき、ＣＩＥ１９７６ Ｌ＊ａ＊ｂ＊表色系で規定する彩度Ｃが１５以上であり、塗布後の粉浮きや厚ぼったさを抑制し、明るく、透明感のある仕上がりが得られる点から、２５以上が好ましく、３８以上がより好ましい。
ここで、彩度Ｃは、以下の方法により求められる。
黒色の人工皮革（オカモト化成品、セラヌバック＃０１０）に、市販の化粧料用スポンジ（ファンデーション用）を用いて、各粉体を８mg／１００cm2となるよう均一に塗布する。得られた試料を、測色計（Ｇｏｎｉｏ Ｓｐｅｃｔｒｏｐｈｏｔｏｍｅｔｅｒ ＧＳＰ−２、村上色彩技術研究所製）を用いて、入射角４５°受光角−４５°の条件で測色する。なお表色系は、ＣＩＥ１９７６Ｌ＊ａ＊ｂ＊表色系を用い、彩度Ｃを測色する。
In the plate-like powder of component (C), the powder is uniformly applied to black artificial leather so as to be 8 mg / 100 cm 2, and in its regular reflection (incident light angle 45 °, light-receiving angle −45 °). When colorimetry is performed, the saturation C specified by the CIE 1976 L * a * b * color system is 15 or more, and it suppresses powder floating and thickness after application, resulting in a bright and transparent finish. Therefore, 25 or more is preferable, and 38 or more is more preferable.
Here, the saturation C is obtained by the following method.
Each powder is uniformly applied to black artificial leather (Okamoto Chemicals, Seranubak # 010) using a commercially available sponge for cosmetics (for foundation) to 8 mg / 100 cm 2 . The obtained sample is measured using a colorimeter (Gonio Spectrophotometer GSP-2, manufactured by Murakami Color Research Laboratory) under the condition of an incident angle of 45 ° and a light receiving angle of −45 °. The CIE 1976 L * a * b * color system is used as the color system, and the chroma C is measured.
また、成分（Ｃ）の板状粉体は、該粉体を黒色の人工皮革に８mg／１００cm2となるように均一に塗布し、その正反射（入射光角４５°、受光角−４５°）において測色したとき、ＣＩＥ１９７６ Ｌ＊ａ＊ｂ＊表色系で規定する明度Ｌが、粉浮きや厚ぼったさを抑制し、明るく、透明感のある仕上がりが得られる点から、６５以上であるのが好ましく、８０以上がより好ましく、９５以上がさらに好ましい。
ここで、明度Ｌは、以下の方法により求められる。
黒色の人工皮革（オカモト化成品、セラヌバック＃０１０）に、市販の化粧料用スポンジ（ファンデーション用）を用いて、各組成物を８mg／１００cm2となるよう均一に塗布する。得られた試料を、測色計（Ｇｏｎｉｏ Ｓｐｅｃｔｒｏｐｈｏｔｏｍｅｔｅｒ ＧＳＰ−２（村上色彩技術研究所製））を用いて、入射角４５°受光角−４５°の条件で測色する。なお表色系は、ＣＩＥ１９７６Ｌ＊ａ＊ｂ＊表色系を用い、明度Ｌを測色する。
Further, the plate-like powder of component (C) was uniformly applied to black artificial leather so as to be 8 mg / 100 cm 2, and its regular reflection (incident light angle 45 °, light receiving angle −45 °). ), The lightness L specified in the CIE1976 L * a * b * color system suppresses powder floating and thickness, and a bright and transparent finish can be obtained. Preferably, 80 or more is more preferable, and 95 or more is more preferable.
Here, the lightness L is obtained by the following method.
Each composition is uniformly applied to black artificial leather (Okamoto Chemicals, Seranubak # 010) using a commercial cosmetic sponge (for foundation) to 8 mg / 100 cm 2 . The obtained sample is measured using a colorimeter (Gonio Spectrophotometer GSP-2 (manufactured by Murakami Color Research Laboratory)) under the conditions of an incident angle of 45 ° and a light receiving angle of −45 °. The CIE 1976 L * a * b * color system is used as the color system, and the lightness L is measured.
成分（Ｃ）の板状粉体としては、薄片状基材の上に屈折率の異なる光学透過性材料を被覆したパール光沢を有するものが好ましい。薄片状基材としては、雲母、合成雲母、シリカフレーク、アルミニウムフレーク、酸化アルミニウムフレーク、酸化鉄フレーク、ガラスフレーク等が挙げられ、透明性が高いことから、雲母、合成雲母、ガラスフレークが好ましく、雲母、ガラスフレークがより好ましく、雲母がさらに好ましい。また、薄片状基材を被覆する光学透過性材料としては、酸化チタン、酸化ジルコニウム、酸化亜鉛、酸化スズ、酸化鉄、酸化クロム、シリカ、クロム、窒化チタン、チタン、フッ化マグネシウムアルミナ、ベーマイト、酸化ホウ素、これらの混合物などが挙げられ、発色の点から、酸化チタン、酸化スズ、酸化鉄、これらの混合物が好ましい。なかでも、酸化チタン、酸化鉄が好ましく、酸化チタンがより好ましい。 As the plate-like powder of component (C), those having a pearly luster in which an optically transparent material having a different refractive index is coated on a flaky substrate are preferable. Examples of the flaky substrate include mica, synthetic mica, silica flakes, aluminum flakes, aluminum oxide flakes, iron oxide flakes, glass flakes and the like, and because of high transparency, mica, synthetic mica, and glass flakes are preferable. Mica and glass flakes are more preferable, and mica is more preferable. Moreover, as an optically transparent material for coating the flaky substrate, titanium oxide, zirconium oxide, zinc oxide, tin oxide, iron oxide, chromium oxide, silica, chromium, titanium nitride, titanium, magnesium fluoride alumina, boehmite, Examples thereof include boron oxide and a mixture thereof. From the viewpoint of color development, titanium oxide, tin oxide, iron oxide, and a mixture thereof are preferable. Of these, titanium oxide and iron oxide are preferable, and titanium oxide is more preferable.
より具体的には、酸化チタン及び／又は酸化鉄で被覆された雲母又はガラスが好ましい。例えば、雲母の表面を酸化チタンで被覆したもの、例えば、BASF社製のFlamenco Silkシリーズ、雲母の表面を酸化チタン及び酸化鉄で被覆したもの、例えば、BASF社製のFlamenco Satinシリーズ、ガラスフレークの表面を酸化チタンで被覆したもの、例えば、日本板硝子社製のメタシャインシリーズを好適に用いることができる。
ここで用いる板状粉体は、その干渉色がゴールド系、グリーン系、パープル系のものが好ましい。
More specifically, mica or glass coated with titanium oxide and / or iron oxide is preferable. For example, the surface of mica coated with titanium oxide, such as Flamenco Silk series manufactured by BASF, the surface of mica coated with titanium oxide and iron oxide, such as Flamenco Satin series manufactured by BASF, glass flakes, etc. The surface of which is coated with titanium oxide, for example, Metashine series manufactured by Nippon Sheet Glass Co., Ltd. can be suitably used.
The plate-like powder used here preferably has a gold, green or purple interference color.
成分（Ｃ）は、成分（Ａ）と同様、必要に応じて、これらの１種又は２種以上が疎水化処理されたものを用いることもできる。 As in the case of the component (A), the component (C) may be one obtained by hydrophobizing one or more of these as necessary.
成分（Ｃ）の板状粉体は、１種又は２種以上組合わせて用いることができ、塗布後にくすみのない、明るく、透明感のある仕上がりが持続する点から、含有量は、全組成中に１質量％以上であり、１．５質量％以上が好ましく、２質量％以上がより好ましく、１０質量％以下であり、７質量％以下が好ましく、５質量％以下がより好ましい。また、成分（Ｃ）の含有量は、全組成中に１〜１０質量％であり、１．５〜７質量％が好ましく、２〜５質量％がより好ましい。 The plate-like powder of component (C) can be used alone or in combination of two or more, and the content is the total composition from the point that a dull, bright and transparent finish lasts after application. It is 1 mass% or more, 1.5 mass% or more is preferable, 2 mass% or more is more preferable, 10 mass% or less is preferable, 7 mass% or less is preferable, and 5 mass% or less is more preferable. Moreover, content of a component (C) is 1-10 mass% in the whole composition, 1.5-7 mass% is preferable, and 2-5 mass% is more preferable.
本発明において、成分（Ｂ）に対する成分（Ｃ）の質量割合（Ｃ）／（Ｂ）は、塗布後のくすみを抑え、明るく、透明感のある仕上がりが得られ、時間が経過しても、その明るさ、透明感が持続する点から、３以上が好ましく、５以上がより好ましく、１４以上がさらに好ましく、２００以下が好ましく、１００以下がより好ましく、５０以下がさらに好ましい。また、成分（Ｂ）に対する成分（Ｃ）の質量割合（Ｃ）／（Ｂ）は、３〜２００が好ましく、５〜１００がより好ましく、１４〜５０がさらに好ましい。 In the present invention, the mass ratio (C) / (B) of the component (C) to the component (B) suppresses dullness after coating, and a bright and transparent finish is obtained. 3 or more are preferable, 5 or more are more preferable, 14 or more are more preferable, 200 or less are preferable, 100 or less are more preferable, and 50 or less are more preferable from the point that the brightness and a transparent feeling continue. Moreover, 3-200 are preferable, as for the mass ratio (C) / (B) of the component (C) with respect to a component (B), 5-100 are more preferable, and 14-50 are more preferable.
本発明において、成分（Ｃ）に対する成分（Ａ）の質量割合（Ａ）／（Ｃ）は、塗布後の粉浮き、厚ぼったさを抑え、明るく、透明感のある仕上がりが得られる点から、０．２以上が好ましく、０．５以上がより好ましく、１以上がさらに好ましく、１５以下が好ましく、８以下がより好ましく、６以下がさらに好ましい。また、成分（Ｃ）に対する成分（Ａ）の質量割合（Ａ）／（Ｃ）は、０．２〜１５が好ましく、０．５〜８がより好ましく、１〜６がさらに好ましい。 In the present invention, the mass ratio (A) / (C) of the component (A) to the component (C) suppresses powder floating and thickness after application, and a bright and transparent finish can be obtained. 0.2 or more, 0.5 or more is more preferable, 1 or more is more preferable, 15 or less is preferable, 8 or less is more preferable, and 6 or less is more preferable. Moreover, 0.2-15 are preferable, as for the mass ratio (A) / (C) of the component (A) with respect to a component (C), 0.5-8 are more preferable, and 1-6 are more preferable.
成分（Ｄ）の球状粉体は、塗布中の滑り性に優れる点から、オルガノポリシロキサンエラストマー、シリカ、ナイロン及びウレタンから選ばれるものである。本発明において、球状とは、真球、略球状、回転楕円体を含み、表面に凹凸がある球状粉体等であっても良い。球状粉体の短径／長径の比、すなわち楕円率は、１．５以下が好ましく、１．２以下がより好ましく、１．１以下がさらに好ましい。
オルガノポリシロキサンエラストマーとしては、ゴム弾性を有する球状粉体が好ましく、ゴム弾性５〜８０の球状粉体がより好ましく、ゴム弾性２０〜７５のものが更に好ましい。ここで、ゴム弾性は、ＪＩＳ Ｋ ７２１５に従い、デュロメータＡにより測定されるものである。球状シリコーンエラストマーとしては、シリコーンＫＳＰ−１００（信越化学工業社；粒子径４〜７μｍ、ゴム弾性３０）、シリコーンＫＳＰ−１０１（信越化学工業社；粒子径７〜２０μｍ、ゴム弾性３０）、シリコーンＫＳＰ−１０２（信越化学工業社；粒子径１０〜５０μｍ、ゴム弾性３０）等の市販品を用いることができる。
The spherical powder of component (D) is selected from organopolysiloxane elastomer, silica, nylon and urethane from the viewpoint of excellent slipperiness during coating. In the present invention, the spherical shape may be a spherical powder including a true sphere, a substantially spherical shape, and a spheroid and having irregularities on the surface. The ratio of the minor axis / major axis of the spherical powder, that is, the ellipticity, is preferably 1.5 or less, more preferably 1.2 or less, and even more preferably 1.1 or less.
As the organopolysiloxane elastomer, spherical powder having rubber elasticity is preferable, spherical powder having rubber elasticity of 5 to 80 is more preferable, and rubber powder having rubber elasticity of 20 to 75 is more preferable. Here, the rubber elasticity is measured by the durometer A according to JIS K 7215. Examples of the spherical silicone elastomer include silicone KSP-100 (Shin-Etsu Chemical Co., Ltd .; particle size 4-7 μm, rubber elasticity 30), silicone KSP-101 (Shin-Etsu Chemical Co., Ltd .; particle size 7-20 μm, rubber elasticity 30), silicone KSP. Commercially available products such as −102 (Shin-Etsu Chemical Co., Ltd .; particle diameter 10 to 50 μm, rubber elasticity 30) can be used.
シリカとしては、無水ケイ酸の球状粉体が挙げられ、サンスフェアＮＰ−１００（ＡＧＣエスアイテック；真球状、粒子径５〜２５μｍ）等の市販品を用いることができる。
ナイロンとしては、球状ナイロンパウダーとして、ナイロンＳＰ−１０（東レ社：粒子径７〜１２μｍ）、ナイロンパウダーＨＫ−５０００（シオノケミカル社：粒子径５〜２０μｍ）等の市販品を用いることができる。
ウレタンとしては、球状ウレタンパウダーとして、ダイミックビーズＵＣＮ−８１５０ＣＭクリヤー（大日精化工業社；粒子径１０〜２０μｍ、ゴム弾性７４）等の市販品を用いることができる。
Examples of silica include spherical powders of silicic anhydride, and commercially available products such as Sunsphere NP-100 (AGC S-Tech; true sphere, particle size 5 to 25 μm) can be used.
As nylon, commercially available products such as nylon SP-10 (Toray Industries, Inc .: particle diameter 7 to 12 μm), nylon powder HK-5000 (Shiono Chemical Co., Ltd .: particle diameter 5 to 20 μm) can be used as spherical nylon powder.
As urethane, commercially available products such as dimic beads UCN-8150CM clear (Daiichi Seika Kogyo Co., Ltd .; particle diameter 10 to 20 μm, rubber elasticity 74) can be used as spherical urethane powder.
成分（Ｄ）の球状粉体は、塗布中の滑り性に優れる点から、粒子径４〜５０μｍのものであり、５〜３０μｍが好ましく、５〜２０μｍがより好ましい。
粉体の粒子径は、レーザー回折／散乱法による粒度分布測定機によって、測定される。具体的には、エタノールを分散媒として、レーザー回折散乱式粒度分布測定器（例えば、堀場製作所製、ＬＡ−９２０）で測定する。
The spherical powder of component (D) has a particle diameter of 4 to 50 μm, preferably 5 to 30 μm, more preferably 5 to 20 μm, from the viewpoint of excellent slipperiness during coating.
The particle diameter of the powder is measured by a particle size distribution measuring machine using a laser diffraction / scattering method. Specifically, measurement is performed with a laser diffraction / scattering particle size distribution analyzer (for example, LA-920, manufactured by Horiba, Ltd.) using ethanol as a dispersion medium.
成分（Ｄ）の球状粉体は、１種又は２種以上組合わせて用いることができ、使用感の持続性に優れる点から、含有量は、全組成中に１０質量％以上であり、２０質量％以上が好ましく、２５質量％以上がより好ましく、６０質量％以下であり、５０質量％以下が好ましく、４５質量％以下がより好ましい。また、成分（Ｄ）の含有量は、全組成中に１０〜６０質量％であり、２０〜５０質量％が好ましく、２５〜４５質量％がより好ましい。 The spherical powder of component (D) can be used singly or in combination of two or more, and the content is 10% by mass or more in the total composition from the viewpoint of excellent sustainability, 20 % By mass or more is preferable, 25% by mass or more is more preferable, 60% by mass or less is preferable, 50% by mass or less is preferable, and 45% by mass or less is more preferable. Moreover, content of a component (D) is 10-60 mass% in the whole composition, 20-50 mass% is preferable, and 25-45 mass% is more preferable.
成分（Ｅ）の球状粉体は、ポリメチルシルセスキオキサン及びポリ（メタ）アクリル酸エステルから選ばれるものであり、使用感の持続性に優れるものである。
ポリメチルシルセスキオキサンは、メチルトリメトキシシロキサンをアルカリ水溶液中で乳化重合させた球状粉体であり、シリコーンＫＭＰ−５９０（信越化学社製；粒子径１〜３μｍ）等の市販品を用いることができる。
ポリ（メタ）アクリル酸エステルとしては、ポリ（メタ）アクリル酸、ポリ（メタ）アクリル酸ナトリウム、ポリ（メタ）アクリル酸エステル、ポリ（メタ）アクリル酸アルキレングリコールから選ばれる１種または２種以上の重合体または共重合体のパウダー等の架橋型あるいは非架橋型の有機球状粉体が挙げられる。なかでも、ポリ（メタ）アクリル酸エステルが好ましく、ポリメタクリル酸メチル（ＰＭＭＡ）がより好ましい。具体的には、ＭＰ−２２００（綜研化学社製；粒子径０．３〜０．４μｍ）等の市販品を用いることができる。
The spherical powder of component (E) is selected from polymethylsilsesquioxane and poly (meth) acrylic acid ester, and is excellent in durability of use.
Polymethylsilsesquioxane is a spherical powder obtained by emulsion polymerization of methyltrimethoxysiloxane in an alkaline aqueous solution, and a commercially available product such as silicone KMP-590 (manufactured by Shin-Etsu Chemical Co., Ltd .; particle size 1 to 3 μm) is used. Can do.
The poly (meth) acrylic acid ester is one or more selected from poly (meth) acrylic acid, poly (meth) acrylic acid sodium, poly (meth) acrylic acid ester, and poly (meth) acrylic acid alkylene glycol. And a crosslinked or non-crosslinked organic spherical powder such as a polymer or copolymer powder. Especially, poly (meth) acrylic acid ester is preferable and polymethyl methacrylate (PMMA) is more preferable. Specifically, commercially available products such as MP-2200 (manufactured by Soken Chemical Co., Ltd .; particle size: 0.3 to 0.4 μm) can be used.
成分（Ｅ）の球状粉体は、使用感の持続性、成型性を確保する点から、粒子径０．１〜３μｍのものであり、０．２〜２μｍが好ましく、０．３〜１μｍがより好ましい。
粒子径は、成分（Ｄ）と同様に測定される。
The spherical powder of the component (E) has a particle size of 0.1 to 3 μm, preferably 0.2 to 2 μm, and preferably 0.3 to 1 μm from the viewpoint of ensuring the durability of use and moldability. More preferred.
The particle diameter is measured in the same manner as in the component (D).
成分（Ｅ）の球状粉体は、１種又は２種以上組合わせて用いることができ、使用感の持続性、成型性を確保する点から、含有量は、全組成中に１質量％以上であり、２質量％以上が好ましく、４質量％以上がより好ましく、２５質量％以下であり、２０質量％以下が好ましく、１５質量％以下がより好ましい。また、成分（Ｅ）の含有量は、全組成中に１〜２５質量％であり、２〜２０質量％が好ましく、４〜１５質量％がより好ましい。 The spherical powder of component (E) can be used singly or in combination of two or more, and the content is 1% by mass or more in the total composition from the viewpoint of ensuring the durability of use and moldability. 2 mass% or more is preferable, 4 mass% or more is more preferable, 25 mass% or less is preferable, 20 mass% or less is preferable, and 15 mass% or less is more preferable. Moreover, content of a component (E) is 1-25 mass% in the whole composition, 2-20 mass% is preferable, and 4-15 mass% is more preferable.
本発明において、成分（Ｄ）及び（Ｅ）の合計質量に対する成分（Ｃ）の質量割合（Ｃ）／（（Ｄ）＋（Ｅ））は、塗布後の粉浮き、厚ぼったさを抑えつつ、明るく、透明感のある仕上がりが得られる点から、０．０２以上が好ましく、０．０３以上がより好ましく、０．０４以上がさらに好ましく、０．４以下が好ましく、０．２以下がより好ましく、０．１２以下がさらに好ましい。また、成分（Ｄ）及び（Ｅ）の合計質量に対する成分（Ｃ）の質量割合（Ｃ）／（（Ｄ）＋（Ｅ））は、０．０２〜０．４が好ましく、０．０３〜０．２がより好ましく、０．０４〜０．１２がさらに好ましい。 In the present invention, the mass ratio (C) / ((D) + (E)) of the component (C) to the total mass of the components (D) and (E) suppresses powder floating and thickness after application. On the other hand, 0.02 or more is preferable, 0.03 or more is more preferable, 0.04 or more is further preferable, 0.4 or less is preferable, and 0.2 or less is preferable in that a bright and transparent finish is obtained. More preferred is 0.12 or less. Further, the mass ratio (C) / ((D) + (E)) of the component (C) to the total mass of the components (D) and (E) is preferably 0.02 to 0.4, preferably 0.03 to 0.03. 0.2 is more preferable, and 0.04 to 0.12 is still more preferable.
さらに、本発明の粉末化粧料は、２５℃で液体の油剤を含有することができる。ここで、２５℃で液体とは、２５℃における粘度が１００００ｍＰａ・ｓ以下であることをいう。具体的には、Ｂ型粘度計、ローターＮｏ．４、１２ｒｐｍ、１分で測定される。
かかる油剤としては、通常の化粧料に用いられるものであれば良く、例えば、流動パラフィン、軽質イソパラフィン、流動イソパラフィン、スクワラン、スクワレン等の直鎖又は分岐の炭化水素油；ホホバ油、オリーブ油等の植物油；液状ラノリン等の動物油；脂肪酸エステル、多価カルボン酸エステル、脂肪酸多価アルコールエステル、ヒドロキシ脂肪酸エステル、その他、メトキシケイ皮酸オクチル、パラジメチルアミノ安息香酸オクチル、dl−α−トコフェロール、ニコチン酸dl−α−トコフェロール等のエステル油；ジメチルポリシロキサン、ジメチルシクロポリシロキサン、メチルフェニルポリシロキサン、メチルハイドロジェンポリシロキサン、高級アルコール変性オルガノポリシロキサン等のシリコーン油；フルオロポリエーテル、パーフルオロアルキルエーテルシリコーン等のフッ素油などが挙げられる。
なかでも、粉体とのなじみが良く、粉っぽさを抑制する点から、ジメチルポリシロキサン、ジメチルシクロポリシロキサン、メチルフェニルポリシロキサン、メチルハイドロジェンポリシロキサン、高級アルコール変性オルガノポリシロキサン等のシリコーン油；フルオロポリエーテル、パーフルオロアルキルエーテルシリコーン等のフッ素油が好ましく、ジメチルポリシロキサン、ジメチルシクロポリシロキサンがより好ましい。
Furthermore, the powder cosmetic of the present invention can contain an oil agent that is liquid at 25 ° C. Here, the liquid at 25 ° C. means that the viscosity at 25 ° C. is 10000 mPa · s or less. Specifically, B-type viscometer, rotor No. Measured at 4, 12 rpm for 1 minute.
Such oil agents may be those used in normal cosmetics, for example, straight or branched hydrocarbon oils such as liquid paraffin, light isoparaffin, liquid isoparaffin, squalane and squalene; vegetable oils such as jojoba oil and olive oil. Animal oil such as liquid lanolin; fatty acid ester, polycarboxylic acid ester, fatty acid polyhydric alcohol ester, hydroxy fatty acid ester, octyl methoxycinnamate, octyl paradimethylaminobenzoate, dl-α-tocopherol, dl nicotinate Ester oil such as α-tocopherol; silicone oil such as dimethylpolysiloxane, dimethylcyclopolysiloxane, methylphenylpolysiloxane, methylhydrogenpolysiloxane, higher alcohol-modified organopolysiloxane; fluoropolyether , Fluorine oils such as perfluoroalkyl ether silicone.
Of these, silicones such as dimethylpolysiloxane, dimethylcyclopolysiloxane, methylphenylpolysiloxane, methylhydrogenpolysiloxane, and higher alcohol-modified organopolysiloxane have good compatibility with powder and suppress powderiness. Oil: Fluorine oil such as fluoropolyether and perfluoroalkylether silicone is preferred, and dimethylpolysiloxane and dimethylcyclopolysiloxane are more preferred.
２５℃で液体の油剤は、１種又は２種以上を用いることができ、ケーキングの抑制、粉っぽさの抑制、使用感が良好である点から、含有量は、全組成中に０．１質量％以上が好ましく、１質量％以上がより好ましく、３質量％以上がさらに好ましく、１５質量％以下が好ましく、１０質量％以下がより好ましく、７質量％以下がさらに好ましい。また、２５℃で液体の油剤の含有量は、全組成中に０．１〜１５質量％が好ましく、１〜１０質量％がより好ましく、３〜７質量％がさらに好ましい。 The oil agent that is liquid at 25 ° C. can be used singly or in combination of two or more. The content of the oil agent is 0. 1 mass% or more is preferable, 1 mass% or more is more preferable, 3 mass% or more is more preferable, 15 mass% or less is preferable, 10 mass% or less is more preferable, and 7 mass% or less is further more preferable. Moreover, 0.1-15 mass% is preferable in the whole composition, as for content of a liquid oil agent at 25 degreeC, 1-10 mass% is more preferable, and 3-7 mass% is further more preferable.
本発明の粉末化粧料は、前記以外に、通常の化粧料に用いられる粉体を含有することができる。
本発明で用いる粉体は、いずれも、そのまま使用することができ、更に、これらの１種又は２種以上が疎水化処理されたものを用いることもできる。
疎水化処理としては、通常の化粧料用粉体に施されている処理であれば制限されず、シリコーン処理、脂肪酸処理、ラウロイルリジン処理、レシチン処理、Ｎ−アシルアミノ酸処理、金属石鹸処理、フッ素化合物処理等が挙げられる。これらのうち、シリコーン処理が好ましい。
In addition to the above, the powder cosmetic of the present invention can contain powders used in ordinary cosmetics.
Any of the powders used in the present invention can be used as it is, and further, one or two or more of these powders which have been subjected to a hydrophobic treatment can be used.
The hydrophobizing treatment is not limited as long as it is a treatment applied to normal cosmetic powders. Silicone treatment, fatty acid treatment, lauroyllysine treatment, lecithin treatment, N-acylamino acid treatment, metal soap treatment, fluorine Compound treatment and the like can be mentioned. Of these, silicone treatment is preferred.
疎水化処理の処理量は粉体によって異なるが、粉体１００質量％に対して、下限は、２質量％以上が好ましく、３質量％以上がより好ましい。また、上限は、７質量％以下が好ましく、５質量％以下がより好ましい。これらの観点を総合すると、２〜７質量％であるのが好ましく、３〜５質量％処理されるのがより好ましい。この処理量であれば、撥水性及び撥油性が付与され、化粧持続性が確保できるので好ましい。 The treatment amount of the hydrophobizing treatment varies depending on the powder, but the lower limit is preferably 2% by mass or more and more preferably 3% by mass or more with respect to 100% by mass of the powder. Further, the upper limit is preferably 7% by mass or less, and more preferably 5% by mass or less. If these viewpoints are put together, it is preferable that it is 2-7 mass%, and it is more preferable to process 3-5 mass%. If it is this processing amount, since water repellency and oil repellency are provided and makeup sustainability can be ensured, it is preferable.
本発明の粉末化粧料は、前記成分のほか、通常の化粧料に用いられる成分、例えば、前記以外の油性成分、界面活性剤、水溶性及び油溶性ポリマー、エタノール、多価アルコール、防腐剤、酸化防止剤、色素、増粘剤、pH調整剤、香料、紫外線吸収剤、保湿剤、血行促進剤、冷感剤、制汗剤、殺菌剤、皮膚賦活剤などを含有することができる。 In addition to the above components, the powder cosmetic of the present invention is a component used in ordinary cosmetics, for example, other oil components, surfactants, water-soluble and oil-soluble polymers, ethanol, polyhydric alcohols, preservatives, An antioxidant, a pigment | dye, a thickener, a pH adjuster, a fragrance | flavor, an ultraviolet absorber, a moisturizer, a blood circulation promoter, a cooling agent, an antiperspirant, a disinfectant, a skin activator, etc. can be contained.
本発明の粉末化粧料は、通常の方法に従って製造することができる。フェイスパウダー、白粉、ファンデーション、ほほ紅、アイシャドウ等のメイクアップ化粧料；ボディパウダー、ベビーパウダー等のボディパウダーなどとして適用することができる。成型工程を伴わない粉末状とするのが好ましく、中でも、フェイスパウダーが好ましい。
上述した実施形態に関し、本発明は、更に以下の組成物を開示する。
The powder cosmetic of the present invention can be produced according to a usual method. It can be applied as makeup cosmetics such as face powder, white powder, foundation, cheek red, and eye shadow; body powder such as body powder and baby powder. It is preferable to use a powder without a molding step, and among these, face powder is preferable.
This invention discloses the following compositions further regarding embodiment mentioned above.
＜１＞次の成分（Ａ）、（Ｂ）、（Ｃ）、（Ｄ）及び（Ｅ）：
（Ａ）比表面積１０〜１００ｍ2／ｇ、粒子径５〜１００ｎｍの微粒子酸化亜鉛 １〜２０質量％、
（Ｂ）有色の着色顔料 ０．０１〜０．５質量％、
（Ｃ）粒子径が１〜５０μｍの板状粉体であって、該粉体を黒色の人工皮革に８mg／１００cm2となるように均一に塗布し、その正反射（入射光角４５°、受光角−４５°）において測色したとき、ＣＩＥ１９７６ Ｌ＊ａ＊ｂ＊表色系で規定する彩度Ｃが１５以上である板状粉体 １〜１０質量％、
（Ｄ）オルガノポリシロキサンエラストマー、シリカ、ナイロン及びウレタンから選ばれる、粒子径４〜５０μｍの球状粉体 １０〜６０質量％、
（Ｅ）ポリメチルシルセスキオキサン及びポリ（メタ）アクリル酸エステルから選ばれる、粒子径０．１〜３μｍの球状粉体 １〜２５質量％
を含有する粉末化粧料。
<1> The following components (A), (B), (C), (D) and (E):
(A) 1 to 20% by mass of fine zinc oxide particles having a specific surface area of 10 to 100 m 2 / g and a particle size of 5 to 100 nm
(B) 0.01 to 0.5% by mass of a colored pigment,
(C) A plate-like powder having a particle diameter of 1 to 50 μm, and the powder was uniformly applied to black artificial leather so as to be 8 mg / 100 cm 2, and its regular reflection (incident light angle 45 °, 1 to 10% by mass of a plate-like powder having a saturation C defined by CIE1976 L * a * b * color system of 15 or more when measured at a light receiving angle of −45 °)
(D) 10-60 mass% of spherical powder having a particle size of 4-50 μm selected from organopolysiloxane elastomer, silica, nylon and urethane,
(E) Spherical powder having a particle size of 0.1 to 3 μm, selected from polymethylsilsesquioxane and poly (meth) acrylate, 1 to 25% by mass
Containing powder cosmetics.
＜２＞成分（Ａ）の微粒子酸化亜鉛が、好ましくは、比表面積１５〜６０ｍ2／ｇのものである前記＜１＞記載の粉末化粧料。
＜３＞成分（Ａ）の微粒子酸化亜鉛が、好ましくは、粒子径５〜４０ｎｍであって、１０〜３０ｎｍがより好ましい前記＜１＞又は＜２＞記載の粉末化粧料。
＜４＞成分（Ａ）の微粒子酸化亜鉛が、好ましくは、疎水化処理されたものであって、シリコーン処理されたものがより好ましい前記＜１＞〜＜３＞のいずれか１記載の粉末化粧料。
＜５＞成分（Ａ）の含有量が、好ましくは、全組成中に３質量％以上であって、５質量％以上がより好ましく、１５質量％以下が好ましく、１３質量％以下がより好ましい前記＜１＞〜＜４＞のいずれか１記載の粉末化粧料。
<2> The powder cosmetic according to <1>, wherein the particulate zinc oxide of the component (A) is preferably one having a specific surface area of 15 to 60 m 2 / g.
<3> The powder cosmetic according to the above <1> or <2>, wherein the fine particle zinc oxide of the component (A) is preferably a particle diameter of 5 to 40 nm and more preferably 10 to 30 nm.
<4> The powder cosmetic according to any one of <1> to <3>, wherein the particulate zinc oxide of component (A) is preferably hydrophobized and more preferably siliconized Fee.
The content of <5> component (A) is preferably 3% by mass or more, more preferably 5% by mass or more, preferably 15% by mass or less, more preferably 13% by mass or less in the total composition. The powder cosmetic according to any one of <1> to <4>.
＜６＞成分（Ｂ）の有色の着色顔料が、好ましくは、金属酸化物であって、ベンガラ、黄酸化鉄、黒酸化鉄がより好ましい前記＜１＞〜＜５＞のいずれか１記載の粉末化粧料。
＜７＞成分（Ｂ）の着色顔料が、好ましくは、疎水化処理されたものであって、シリコーン処理されたものがより好ましい前記＜１＞〜＜６＞のいずれか１記載の粉末化粧料。
＜８＞成分（Ｂ）の含有量が、好ましくは、全組成中に０．０５質量％以上であって、０．１質量％以上がより好ましく、０．４質量％以下が好ましく、０．３質量％以下がより好ましい前記＜１＞〜＜７＞のいずれか１記載の粉末化粧料。
＜９＞成分（Ａ）に対する成分（Ｂ）の質量割合（Ｂ）／（Ａ）が、好ましくは、０．００１以上であって、０．００５以上がより好ましく、０．０１以上がさらに好ましく、０．０６以下が好ましく、０．０５以下がより好ましく、０．０３以下がさらに好ましい前記＜１＞〜＜８＞のいずれか１記載の粉末化粧料。
<6> The colored pigment of component (B) is preferably a metal oxide, and more preferably bengara, yellow iron oxide, or black iron oxide. Powder cosmetic.
<7> The powder cosmetic according to any one of <1> to <6>, wherein the colored pigment of component (B) is preferably hydrophobized and more preferably silicone-treated .
The content of <8> component (B) is preferably 0.05% by mass or more, more preferably 0.1% by mass or more, and preferably 0.4% by mass or less in the total composition. The powder cosmetic according to any one of <1> to <7>, more preferably 3% by mass or less.
<9> The mass ratio (B) / (A) of the component (B) to the component (A) is preferably 0.001 or more, more preferably 0.005 or more, and further preferably 0.01 or more. 0.06 or less is preferable, 0.05 or less is more preferable, and 0.03 or less is still more preferable, The powder cosmetics in any one of said <1>-<8>.
＜１０＞成分（Ｃ）の板状粉体が、好ましくは、粒子径２〜３０μｍのものである前記＜１＞〜＜９＞のいずれか１記載の粉末化粧料。
＜１１＞成分（Ｃ）の板状粉体が、好ましくは、アスペクト比１０〜１５０のものであって、２０〜１００のものがより好ましい前記＜１＞〜＜１０＞のいずれか１記載の粉末化粧料。
＜１２＞成分（Ｃ）の板状粉体が、該粉体を黒色の人工皮革に８mg／１００cm2となるように均一に塗布し、その正反射（入射光角４５°、受光角−４５°）において測色したとき、ＣＩＥ１９７６ Ｌ＊ａ＊ｂ＊表色系で規定する彩度Ｃが、好ましくは、２５以上であって、３８以上がより好ましい前記＜１＞〜＜１１＞のいずれか１記載の粉末化粧料。
＜１３＞成分（Ｃ）の板状粉体が、該粉体を黒色の人工皮革に８mg／１００cm2となるように均一に塗布し、その正反射（入射光角４５°、受光角−４５°）において測色したとき、ＣＩＥ１９７６ Ｌ＊ａ＊ｂ＊表色系で規定する明度Ｌが、好ましくは、６５以上であって、８０以上がより好ましく、９５以上がさらに好ましい前記＜１＞〜＜１２＞のいずれか１記載の粉末化粧料。
<10> The powder cosmetic according to any one of <1> to <9>, wherein the plate-like powder of component (C) is preferably one having a particle diameter of 2 to 30 μm.
<11> The plate-like powder of component (C) is preferably one having an aspect ratio of 10 to 150, and more preferably 20 to 100. Powder cosmetic.
The plate-like powder of <12> component (C) is uniformly applied to black artificial leather so as to be 8 mg / 100 cm 2, and its regular reflection (incident light angle 45 °, light receiving angle −45). When the color is measured at °), the saturation C defined by the CIE 1976 L * a * b * color system is preferably 25 or more, and more preferably 38 or more, any of the above <1> to <11> The powder cosmetic according to claim 1.
The plate-like powder of <13> component (C) is uniformly applied to black artificial leather so as to be 8 mg / 100 cm 2, and its regular reflection (incident light angle 45 °, light receiving angle −45). When the color is measured at °), the lightness L defined by the CIE 1976 L * a * b * color system is preferably 65 or more, more preferably 80 or more, and even more preferably 95 or more. The powder cosmetic according to any one of <12>.
＜１４＞成分（Ｃ）の板状粉体が、好ましくは、薄片状基材の上に屈折率の異なる光学透過性材料を被覆したパール光沢を有するものであって、酸化チタン及び／又は酸化鉄で被覆された雲母又はガラスがより好ましく、雲母の表面を酸化チタンで被覆したもの、雲母の表面を酸化チタン及び酸化鉄で被覆したもの、ガラスフレークの表面を酸化チタンで被覆したものがさらに好ましい前記＜１＞〜＜１３＞のいずれか１記載の粉末化粧料。
＜１５＞成分（Ｃ）の板状粉体が、好ましくは、疎水化処理されたものであって、シリコーン処理されたものがより好ましい前記＜１＞〜＜１４＞のいずれか１記載の粉末化粧料。
＜１６＞成分（Ｃ）の含有量が、好ましくは、全組成中に１．５質量％以上であって、２質量％以上がより好ましく、７質量％以下が好ましく、５質量％以下がより好ましい前記＜１＞〜＜１５＞のいずれか１記載の粉末化粧料。
<14> The plate-like powder of component (C) preferably has a pearly luster in which an optically transparent material having a different refractive index is coated on a flaky substrate, and has titanium oxide and / or oxidation Mica or glass coated with iron is more preferable, and the mica surface is coated with titanium oxide, the mica surface is coated with titanium oxide and iron oxide, and the glass flake surface is coated with titanium oxide. The powder cosmetic according to any one of <1> to <13>, which is preferable.
<15> The powder according to any one of <1> to <14>, wherein the plate-like powder of component (C) is preferably hydrophobized and more preferably siliconized Cosmetics.
The content of <16> component (C) is preferably 1.5% by mass or more, more preferably 2% by mass or more, preferably 7% by mass or less, more preferably 5% by mass or less in the total composition. The powder cosmetic according to any one of <1> to <15>, preferably.
＜１７＞成分（Ｂ）に対する成分（Ｃ）の質量割合（Ｃ）／（Ｂ）が、好ましくは、３以上であって、５以上がより好ましく、１４以上がさらに好ましく、２００以下が好ましく、１００以下がより好ましく、５０以下がさらに好ましい前記＜１＞〜＜１６＞のいずれか１記載の粉末化粧料。
＜１８＞成分（Ｃ）に対する成分（Ａ）の質量割合（Ａ）／（Ｃ）が、好ましくは、０．２以上であって、０．５以上がより好ましく、１以上がさらに好ましく、１５以下が好ましく、８以下がより好ましく、６以下がさらに好ましい前記＜１＞〜＜１７＞のいずれか１記載の粉末化粧料。
<17> The mass ratio (C) / (B) of the component (C) to the component (B) is preferably 3 or more, more preferably 5 or more, further preferably 14 or more, and preferably 200 or less, The powder cosmetic according to any one of <1> to <16>, more preferably 100 or less, and still more preferably 50 or less.
<18> The mass ratio (A) / (C) of the component (A) to the component (C) is preferably 0.2 or more, more preferably 0.5 or more, and even more preferably 1 or more, 15 The powder cosmetic according to any one of <1> to <17>, wherein the following is preferable, 8 or less is more preferable, and 6 or less is more preferable.
＜１９＞成分（Ｄ）の球状粉体が、好ましくは、粒子径５〜３０μｍであって、５〜２０μｍがより好ましい前記＜１＞〜＜１８＞のいずれか１記載の粉末化粧料。
＜２０＞成分（Ｄ）の含有量が、好ましくは、全組成中に２０質量％以上であって、２５質量％以上がより好ましく、５０質量％以下が好ましく、４５質量％以下がより好ましい前記＜１＞〜＜１９＞のいずれか１記載の粉末化粧料。
＜２１＞成分（Ｅ）の球状粉体が、好ましくは、粒子径０．２〜２μｍであって、０．３〜１μｍがより好ましい前記＜１＞〜＜２０＞のいずれか１記載の粉末化粧料。
＜２２＞成分（Ｅ）の含有量が、好ましくは、全組成中に２質量％以上であって、４質量％以上がより好ましく、２０質量％以下が好ましく、１５質量％以下がより好ましい前記＜１＞〜＜２１＞のいずれか１記載の粉末化粧料。
<19> The powder cosmetic according to any one of <1> to <18>, wherein the spherical powder of component (D) preferably has a particle diameter of 5 to 30 μm, and more preferably 5 to 20 μm.
The content of <20> component (D) is preferably 20% by mass or more, more preferably 25% by mass or more, preferably 50% by mass or less, and more preferably 45% by mass or less in the total composition. The powder cosmetic according to any one of <1> to <19>.
<21> The powder according to any one of <1> to <20>, wherein the spherical powder of component (E) preferably has a particle diameter of 0.2 to 2 μm, and more preferably 0.3 to 1 μm. Cosmetics.
The content of <22> component (E) is preferably 2% by mass or more in the total composition, more preferably 4% by mass or more, preferably 20% by mass or less, and more preferably 15% by mass or less. The powder cosmetic according to any one of <1> to <21>.
＜２３＞成分（Ｄ）及び（Ｅ）の合計質量に対する成分（Ｃ）の質量割合（Ｃ）／（（Ｄ）＋（Ｅ））が、好ましくは、０．０２以上であって、０．０３以上がより好ましく、０．０４以上がさらに好ましく、０．４以下が好ましく、０．２以下がより好ましく、０．１２以下がさらに好ましい前記＜１＞〜＜２２＞のいずれか１記載の粉末化粧料。
＜２４＞さらに、２５℃で液体の油剤を含有することができ、２５℃で液体の油剤が、好ましくは、シリコーン油、フッ素油であって、ジメチルポリシロキサン、ジメチルシクロポリシロキサンがより好ましい前記＜１＞〜＜２３＞のいずれか１記載の粉末化粧料。
＜２５＞２５℃で液体の油剤の含有量が、好ましくは、全組成中に０．１質量％以上であって、１質量％以上がより好ましく、３質量％以上がさらに好ましく、１５質量％以下が好ましく、１０質量％以下がより好ましく、７質量％以下がさらに好ましい前記＜２４＞記載の粉末化粧料。
＜２６＞好ましくは、メイクアップ化粧料であって、フェイスパウダーがより好ましい前記＜１＞〜＜２５＞のいずれか１記載の粉末化粧料。
<23> The mass ratio (C) / ((D) + (E)) of the component (C) to the total mass of the components (D) and (E) is preferably 0.02 or more, and 03 or more is more preferable, 0.04 or more is further preferable, 0.4 or less is preferable, 0.2 or less is more preferable, and 0.12 or less is more preferable. <1> to <22> Powder cosmetic.
<24> Furthermore, an oil agent that is liquid at 25 ° C. can be contained, and the oil agent that is liquid at 25 ° C. is preferably silicone oil or fluorine oil, and dimethylpolysiloxane and dimethylcyclopolysiloxane are more preferable. The powder cosmetic according to any one of <1> to <23>.
<25> The content of the liquid oil at 25 ° C. is preferably 0.1% by mass or more, more preferably 1% by mass or more, further preferably 3% by mass or more, and 15% by mass in the total composition. The powder cosmetic according to the above <24>, preferably 10% by mass or less, more preferably 7% by mass or less.
<26> The powder cosmetic according to any one of <1> to <25>, preferably a makeup cosmetic, and more preferably a face powder.
実施例１〜９及び比較例１〜４
表２に示す組成の粉末化粧料（フェイスパウダー）を製造し、粉っぽさのなさ、厚ぼったさのなさ、明るい仕上がり、透明感、５時間後の明るさ、５時間後の透明感、化粧持ちを評価した。結果を表２に併せて示す。なお、実施例及び比較例で用いた成分（Ｃ）の粒子径、彩度Ｃ、明度Ｌは、表１に示すとおりである。
Examples 1-9 and Comparative Examples 1-4
A powder cosmetic (face powder) having the composition shown in Table 2 was produced, and it had no powderiness, no thickness, bright finish, transparency, brightness after 5 hours, and transparency after 5 hours. , Evaluated makeup holding. The results are also shown in Table 2. In addition, the particle diameter, the chroma C, and the lightness L of the component (C) used in Examples and Comparative Examples are as shown in Table 1.
（製法）
表２に示す組成の粉体成分を、ヘンシェルミキサーを用いて均一混合し、これに油性成分を加えて更に混合した後、ふるいを通してフェイスパウダーを得た。
(Manufacturing method)
The powder component having the composition shown in Table 2 was uniformly mixed using a Henschel mixer, and after adding an oily component to this, the powder was further passed through a sieve to obtain a face powder.
（評価方法）
（１）粉っぽさのなさ、厚ぼったさのなさ、明るい仕上がり、透明感：
１０名の専門パネラーが、各フェイスパウダーをスポンジで顔に塗布した直後の、「粉っぽさのなさ」、「厚ぼったさのなさ」、「明るい仕上がり」、「透明感」を、以下の基準で評価した。結果を１０名の積算値で示す。
(Evaluation method)
(1) No powderiness, no thickness, bright finish, transparency:
10 expert panelists immediately apply each face powder to their faces with a sponge, “no powderiness”, “no thickness”, “bright finish”, “transparency” Evaluation based on the criteria. A result is shown by the integrated value of 10 persons.
（１−１）粉っぽさのなさ：
５；粉っぽさが全くない。
４；粉っぽさがない。
３；粉っぽさがあまりない。
２；粉っぽさがややある。
１；粉っぽさがかなりある。
(1-1) No powderiness:
5: There is no powderiness.
4; There is no powderiness.
3; Not very powdery.
2; Slightly powdery.
1; There is considerable powderiness.
（１−２）厚ぼったさのなさ：
５；厚ぼったさを全く感じない。
４；厚ぼったさを感じない。
３；厚ぼったさをあまり感じない。
２；厚ぼったさをやや感じる
１；厚ぼったさを感じる。
(1-2) Thickness:
5; I don't feel thick at all.
4; I don't feel thick.
3; I don't feel much thickness.
2; I feel a little thick 1; I feel thick.
（１−３）明るい仕上がり：
５；仕上がりが非常に明るい。
４；仕上がりが明るい。
３；仕上がりがやや明るい。
２；仕上がりがあまり明るくない。
１；仕上がりが明るくない。
(1-3) Bright finish:
5: The finish is very bright.
4; The finish is bright.
3; The finish is slightly bright.
2; The finish is not so bright.
1: The finish is not bright.
（１−４）透明感：
５；かなり透明感がある。
４；透明感がある。
３；やや透明感がある。
２；あまり透明感がない。
１；透明感がない。
(1-4) Transparency:
5: There is a considerable transparency.
4; There is a feeling of transparency.
3; Somewhat transparent.
2; Not very transparent.
1: There is no sense of transparency.
（２）５時間後の明るさ、５時間後の透明感、化粧持ち：
１０名の専門パネラーが、各フェイスパウダーをスポンジで顔に塗布し、５時間経過した後の「５時間後の明るさ」、「５時間後の透明感」、「化粧持ち」を、以下の基準で評価した。結果を１０名の積算値で示す。
(2) Brightness after 5 hours, transparency after 5 hours, makeup lasting:
Ten professional panelists applied each face powder to their face with a sponge, and after 5 hours, “brightness after 5 hours”, “transparency after 5 hours”, “long-lasting makeup” Evaluated by criteria. A result is shown by the integrated value of 10 persons.
（２−１）５時間後の明るさ：
５；仕上がりが非常に明るい。
４；仕上がりが明るい。
３；仕上がりがやや明るい。
２；仕上がりがあまり明るくない。
１；仕上がりが明るくない。
(2-1) Brightness after 5 hours:
5: The finish is very bright.
4; The finish is bright.
3; The finish is slightly bright.
2; The finish is not so bright.
1: The finish is not bright.
（２−２）５時間後の透明感：
５；かなり透明感がある。
４；透明感がある。
３；やや透明感がある。
２；あまり透明感がない。
１；透明感がない。
(2-2) Transparency after 5 hours:
5: There is a considerable transparency.
4; There is a feeling of transparency.
3; Somewhat transparent.
2; Not very transparent.
1: There is no sense of transparency.
（３）化粧持ち：
５；非常に化粧持ちが良い。
４；化粧持ちが良い。
３；やや化粧持ちが良い。
２；あまり化粧持ちが良くない
１；化粧持ちが良くない
(3) Makeup:
5; Very good makeup.
4; Good makeup.
3; Good makeup is good.
2; Long-lasting makeup is not good 1; Long-lasting makeup is not good
実施例１０〜１１
実施例１〜９と同様にして、表３及び表４に示す組成の粉末化粧料を製造した。
得られた粉末化粧料はいずれも、粉っぽさや厚ぼったさがなく、明るく、透明感のある仕上がりが得られ、５時間後においても、明るく、透明感があり、化粧持ちに優れていた。
Examples 10-11
In the same manner as in Examples 1 to 9, powder cosmetics having the compositions shown in Tables 3 and 4 were produced.
Each of the obtained powder cosmetics has no powderiness or thickness, and a bright and transparent finish is obtained. Even after 5 hours, it is bright and transparent, and has excellent makeup. It was.
Claims (7)
（Ａ）比表面積１０〜１００ｍ2／ｇ、粒子径５〜１００ｎｍの微粒子酸化亜鉛 １〜２０質量％、
（Ｂ）有色の着色顔料 ０．０１〜０．５質量％、
（Ｃ）粒子径が１〜５０μｍの板状粉体であって、該粉体を黒色の人工皮革に８mg／１００cm2となるように均一に塗布し、その正反射（入射光角４５°、受光角−４５°）において測色したとき、ＣＩＥ１９７６ Ｌ＊ａ＊ｂ＊表色系で規定する彩度Ｃが１５以上である板状粉体 １．５〜７質量％、
（Ｄ）オルガノポリシロキサンエラストマー、シリカ、ナイロン及びウレタンから選ばれる、粒子径４〜５０μｍの球状粉体 １０〜６０質量％、
（Ｅ）ポリメチルシルセスキオキサン及びポリ（メタ）アクリル酸エステルから選ばれる、粒子径０．１〜３μｍの球状粉体 １〜１５質量％
を含有する粉末化粧料。 The following components (A), (B), (C), (D) and (E):
(A) 1 to 20% by mass of fine zinc oxide particles having a specific surface area of 10 to 100 m 2 / g and a particle size of 5 to 100 nm
(B) 0.01 to 0.5% by mass of a colored pigment,
(C) A plate-like powder having a particle diameter of 1 to 50 μm, and the powder was uniformly applied to black artificial leather so as to be 8 mg / 100 cm 2, and its regular reflection (incident light angle 45 °, When the color is measured at a light receiving angle of −45 °), 1.5 to 7 % by mass of a plate-like powder having a saturation C defined by CIE1976 L * a * b * color system of 15 or more,
(D) 10-60 mass% of spherical powder having a particle size of 4-50 μm selected from organopolysiloxane elastomer, silica, nylon and urethane,
(E) Spherical powder having a particle size of 0.1 to 3 μm, selected from polymethylsilsesquioxane and poly (meth) acrylic ester 1 to 15 % by mass
Containing powder cosmetics.